JPH05239434A - 成形された金属表面の表面調整方法及び表面調整剤 - Google Patents
成形された金属表面の表面調整方法及び表面調整剤Info
- Publication number
- JPH05239434A JPH05239434A JP3046781A JP4678191A JPH05239434A JP H05239434 A JPH05239434 A JP H05239434A JP 3046781 A JP3046781 A JP 3046781A JP 4678191 A JP4678191 A JP 4678191A JP H05239434 A JPH05239434 A JP H05239434A
- Authority
- JP
- Japan
- Prior art keywords
- group
- acid
- water
- formula
- hydrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 湿潤時に水滴跡の斑点が実質的にまたは完全
に消失する成形された金属表面に用いられる表面調質方
法およびその組成物を提供する。 【構成】 アルカリ洗浄されたアルミニウム表面、特に
缶を(i) エトキシフオスフェートエステル(ii)アルミニ
ウム、ジルコニウム、鉄、錫および/またはセリウムイ
オンおよび(iii) 金属食刻性成分と接触させることから
なるアルミニウム製品の表面調質方法およびその組成
物。 【効果】 アルミニウム製品の表面調質が行なわれ、後
で乾燥したときに処理表面の反射性または印刷性、又表
面へのラッカーの密着性を損うことなく、該表面に対し
て可動性、すなわち小さな静的表面摩擦係数を付与でき
る。
に消失する成形された金属表面に用いられる表面調質方
法およびその組成物を提供する。 【構成】 アルカリ洗浄されたアルミニウム表面、特に
缶を(i) エトキシフオスフェートエステル(ii)アルミニ
ウム、ジルコニウム、鉄、錫および/またはセリウムイ
オンおよび(iii) 金属食刻性成分と接触させることから
なるアルミニウム製品の表面調質方法およびその組成
物。 【効果】 アルミニウム製品の表面調質が行なわれ、後
で乾燥したときに処理表面の反射性または印刷性、又表
面へのラッカーの密着性を損うことなく、該表面に対し
て可動性、すなわち小さな静的表面摩擦係数を付与でき
る。
Description
【0001】本発明は、湿潤時に「水滴跡の斑点」が実
質的にまたは完全に消失する処理成形表面、換言すれ
ば、表面に存在する水が自動的に広がる表面を作り出す
組成物、及びこれら組成物を用いる方法に特に関する。
さらに本発明は、成形金属表面、特にアルミニウム缶、
スズメッキ缶等の表面に塗布するに好適な水性組成物
で、乾燥後には可動性強化潤滑フィルムが形成される水
性組成物にも関する。この組成物は、貯蔵時に微生物の
作用による劣化を受けないように、さらに/または使用
時に発泡することもないように保護されているものであ
る。
質的にまたは完全に消失する処理成形表面、換言すれ
ば、表面に存在する水が自動的に広がる表面を作り出す
組成物、及びこれら組成物を用いる方法に特に関する。
さらに本発明は、成形金属表面、特にアルミニウム缶、
スズメッキ缶等の表面に塗布するに好適な水性組成物
で、乾燥後には可動性強化潤滑フィルムが形成される水
性組成物にも関する。この組成物は、貯蔵時に微生物の
作用による劣化を受けないように、さらに/または使用
時に発泡することもないように保護されているものであ
る。
【0002】すでに登録されている米国特許第4,85
9,351(以下 '351号特許)技術に加えて、19
79年4月10日付けのケリー(Kelly)の米国特
許第4,148,670号明細書の教示するところによ
れば、ジルコニウム及び/又はチタニウムの化合物、弗
化物、及び燐酸塩を、また選択的にはポリヒドロキシ化
合物を、溶解した状態で、含有する、アルミニウム用の
転化被覆用溶液がある。この際に用いられる燐酸塩は、
従来的な無機燐酸塩であり、この処理によって得られる
可動性向上効果についてはなんら教示されていない。
9,351(以下 '351号特許)技術に加えて、19
79年4月10日付けのケリー(Kelly)の米国特
許第4,148,670号明細書の教示するところによ
れば、ジルコニウム及び/又はチタニウムの化合物、弗
化物、及び燐酸塩を、また選択的にはポリヒドロキシ化
合物を、溶解した状態で、含有する、アルミニウム用の
転化被覆用溶液がある。この際に用いられる燐酸塩は、
従来的な無機燐酸塩であり、この処理によって得られる
可動性向上効果についてはなんら教示されていない。
【0003】1976年6月22日付けのダス(Da
s)の米国特許第3,964,936号明細書の教示す
るところによれば、アルミニウム用の転化被覆用溶液が
あり、これを用いると、沸騰する水によって処理されて
も、光輝ある外観を維持し、変色に耐える表面が得られ
る。この被覆用溶液は、ジルコニウム及び弗素の化合物
を含有し、硼酸を含有しても差し支えない。これには、
燐酸塩含有成分を使用することは教示されていないし、
この処理によって得られる可動性の向上についても教示
されていない。
s)の米国特許第3,964,936号明細書の教示す
るところによれば、アルミニウム用の転化被覆用溶液が
あり、これを用いると、沸騰する水によって処理されて
も、光輝ある外観を維持し、変色に耐える表面が得られ
る。この被覆用溶液は、ジルコニウム及び弗素の化合物
を含有し、硼酸を含有しても差し支えない。これには、
燐酸塩含有成分を使用することは教示されていないし、
この処理によって得られる可動性の向上についても教示
されていない。
【0004】
【課題を解決するための手段】以下、本発明を説明す
る。本明細書の記載においては、特許請求の範囲および
実施例に記載の場合を除いて、又は特記なき限り、成分
の量又は反応条件を示す数字は、全て「約」という語で
修飾され、本発明の最も広い範囲で定義すると理解する
ものとする。操作は、記載の正確な数字範囲内で行われ
るのが一般に好ましい。また、特記なき限り、組成物の
ある特定の成分に対して一つ以上の物質が好適であると
記載されている場合には、記載されている二つ以上の物
質を含む混合物も同様に好適であると理解するものとす
る。
る。本明細書の記載においては、特許請求の範囲および
実施例に記載の場合を除いて、又は特記なき限り、成分
の量又は反応条件を示す数字は、全て「約」という語で
修飾され、本発明の最も広い範囲で定義すると理解する
ものとする。操作は、記載の正確な数字範囲内で行われ
るのが一般に好ましい。また、特記なき限り、組成物の
ある特定の成分に対して一つ以上の物質が好適であると
記載されている場合には、記載されている二つ以上の物
質を含む混合物も同様に好適であると理解するものとす
る。
【0005】さて、見出されたことによると、成形アル
ミニウム表面は、水性の酸またはアルカリ洗浄剤との十
分なる接触により、従来的に完全に洗浄、脱脂された場
合、水および以下の成分を包含し又は実質的にはこれら
から成る組成物とこの表面を接触することによって、効
果的かつ有利に表面調質が行われ、後で乾燥したときに
は、処理表面の反射性または印刷性、あるいは表面への
ラッカーの密着性を損なうことなく、該表面に対して可
動性、つまり小さな静的表面摩擦係数を付与することが
できる。上記成分とは、
ミニウム表面は、水性の酸またはアルカリ洗浄剤との十
分なる接触により、従来的に完全に洗浄、脱脂された場
合、水および以下の成分を包含し又は実質的にはこれら
から成る組成物とこの表面を接触することによって、効
果的かつ有利に表面調質が行われ、後で乾燥したときに
は、処理表面の反射性または印刷性、あるいは表面への
ラッカーの密着性を損なうことなく、該表面に対して可
動性、つまり小さな静的表面摩擦係数を付与することが
できる。上記成分とは、
【0006】(A) 化学一般式:
【化13】
【0007】(式中、R1 、R3 、及びR6 は、それぞ
れ水素および炭素数1〜4のアルキル基から、好ましく
は水素およびメチル基から独立的に選択され、最も好ま
しくは水素であり、x、y、及びzは、それぞれ整数
で、0〜25の範囲で独立的に選択され、R2 、R4 、
及びR5 は、それぞれ水素、一価のカチオン、多価カチ
オンの一価部分、炭素数1〜20のアルキル基、及び炭
素数1〜20のアリール及びアリールアルキル基から独
立的に選択されるが、但し、R2 、R4 、及び R 5 の
少なくとも一つは、(i) 水素ではなく(ii)これと式中の
燐原子との間にアルコキシ基を少なくとも一つは結合さ
せているものである)に適合する基から選択される水溶
性物質成分;
れ水素および炭素数1〜4のアルキル基から、好ましく
は水素およびメチル基から独立的に選択され、最も好ま
しくは水素であり、x、y、及びzは、それぞれ整数
で、0〜25の範囲で独立的に選択され、R2 、R4 、
及びR5 は、それぞれ水素、一価のカチオン、多価カチ
オンの一価部分、炭素数1〜20のアルキル基、及び炭
素数1〜20のアリール及びアリールアルキル基から独
立的に選択されるが、但し、R2 、R4 、及び R 5 の
少なくとも一つは、(i) 水素ではなく(ii)これと式中の
燐原子との間にアルコキシ基を少なくとも一つは結合さ
せているものである)に適合する基から選択される水溶
性物質成分;
【0008】(B) Fe,Zr,Sn,Al,及びC
eから成る群から選択される原子を包含するイオンを含
有する水溶性塩の群から選択される成分;及び
eから成る群から選択される原子を包含するイオンを含
有する水溶性塩の群から選択される成分;及び
【0009】(C) 金属を食刻する成分、好ましく
は、硝酸、硫酸、燐酸、弗化水素酸、塩化水素酸、臭化
水素酸、沃化水素酸;硫酸および燐酸との酸性塩;硝
酸、硫酸、燐酸、弗化水素酸、塩化水素酸、臭化水素
酸、および沃化水素酸と塩を生成する酸のイオン積定数
より小さいイオン積定数を有する塩基との塩;及びこれ
らの物質の混合物から成る群から選択される成分、さら
に選択的には
は、硝酸、硫酸、燐酸、弗化水素酸、塩化水素酸、臭化
水素酸、沃化水素酸;硫酸および燐酸との酸性塩;硝
酸、硫酸、燐酸、弗化水素酸、塩化水素酸、臭化水素
酸、および沃化水素酸と塩を生成する酸のイオン積定数
より小さいイオン積定数を有する塩基との塩;及びこれ
らの物質の混合物から成る群から選択される成分、さら
に選択的には
【0010】(D) 成分(B)のイオンを含有する金
属用のキレート剤から選択される成分、好ましくは各分
子が、アミノ基、置換アミノ基、カルボキシル基、燐酸
塩、スルフォン酸塩、及びカルボニル部分基から成る群
から選択される少なくとも二つの部分基を有する分子
(ポリマー分子を包含する)から成る群から選択される
成分;
属用のキレート剤から選択される成分、好ましくは各分
子が、アミノ基、置換アミノ基、カルボキシル基、燐酸
塩、スルフォン酸塩、及びカルボニル部分基から成る群
から選択される少なくとも二つの部分基を有する分子
(ポリマー分子を包含する)から成る群から選択される
成分;
【0011】(E) 一般式II:
【化14】
【0012】(式中、R7 は、線形、環式または分枝
状、飽和または不飽和一価脂肪族炭化水素部分基で、R
1 とxは、式Iと同じ意味を有する)に適合する分子か
ら選択される成分。または上記成分として次の成分が挙
げられる。
状、飽和または不飽和一価脂肪族炭化水素部分基で、R
1 とxは、式Iと同じ意味を有する)に適合する分子か
ら選択される成分。または上記成分として次の成分が挙
げられる。
【0013】(A) 化学一般式I:
【化15】
【0014】(式中、R1 、R3 、及びR6 は、それぞ
れ水素および炭素数1〜4のアルキル基から、好ましく
は水素およびメチル基から独立的に選択され、最も好ま
しくは水素であり、x、y、及びzは、それぞれ整数
で、0〜25の範囲で独立的に選択され、R2 、R4 、
及びR5 は、それぞれ水素、一価のカチオン、多価カチ
オンの一価部分、炭素数1〜20のアルキル基、及び炭
素数1〜20のアリール及びアリールアルキル基から独
立的に選択されるが、但し、R2 、R4 、及びR5 の少
なくとも一つは、(i) 水素ではなく(ii)これと式中の燐
原子との間にアルコキシ基を少なくとも一つは結合させ
ているものである)に適合する基から選択される水溶性
物質成分;
れ水素および炭素数1〜4のアルキル基から、好ましく
は水素およびメチル基から独立的に選択され、最も好ま
しくは水素であり、x、y、及びzは、それぞれ整数
で、0〜25の範囲で独立的に選択され、R2 、R4 、
及びR5 は、それぞれ水素、一価のカチオン、多価カチ
オンの一価部分、炭素数1〜20のアルキル基、及び炭
素数1〜20のアリール及びアリールアルキル基から独
立的に選択されるが、但し、R2 、R4 、及びR5 の少
なくとも一つは、(i) 水素ではなく(ii)これと式中の燐
原子との間にアルコキシ基を少なくとも一つは結合させ
ているものである)に適合する基から選択される水溶性
物質成分;
【0015】(B) Fe,Zr,Sn,Al,及びC
eから成る群から選択される原子を包含するイオンを含
有する水溶性塩の群から選択される成分;
eから成る群から選択される原子を包含するイオンを含
有する水溶性塩の群から選択される成分;
【0016】(C) 硝酸、硫酸、燐酸、弗化水素酸、
塩化水素酸、臭化水素酸、沃化水素酸;硫酸および燐酸
との酸性塩;硝酸、硫酸、燐酸、弗化水素酸、塩化水素
酸、臭化水素酸、および沃化水素酸と塩を生成する酸の
イオン積定数より小さいイオン積定数を有する塩基との
塩;及びこれらの物質の混合物、さらに選択的には、
塩化水素酸、臭化水素酸、沃化水素酸;硫酸および燐酸
との酸性塩;硝酸、硫酸、燐酸、弗化水素酸、塩化水素
酸、臭化水素酸、および沃化水素酸と塩を生成する酸の
イオン積定数より小さいイオン積定数を有する塩基との
塩;及びこれらの物質の混合物、さらに選択的には、
【0017】(D) 成分(B)のイオンを含有する金
属用のキレート剤から選択される成分、好ましくは各分
子が、アミノ基、置換アミノ基、カルボキシル基、燐酸
塩、スルフォン酸塩、及びカルボニル部分基から成る群
から選択される少なくとも二つの部分基を有する分子
(ポリマー分子を包含する)から成る群から選択される
成分;
属用のキレート剤から選択される成分、好ましくは各分
子が、アミノ基、置換アミノ基、カルボキシル基、燐酸
塩、スルフォン酸塩、及びカルボニル部分基から成る群
から選択される少なくとも二つの部分基を有する分子
(ポリマー分子を包含する)から成る群から選択される
成分;
【0018】(E) 一般式II′:
【化16】 (式中、R7 は、炭素数1〜25、好ましくは4〜20
の、線形、環式、または分枝状飽和一価脂肪族炭化水素
部分基で、Xは、水素、ハロゲン、フェニル及びR1 か
ら成る群から選択され、sは1〜50、好ましくは1〜
20の整数で、そしてR1 は式Iと同じ意味を有する)
に適合する分子から選択される成分;
の、線形、環式、または分枝状飽和一価脂肪族炭化水素
部分基で、Xは、水素、ハロゲン、フェニル及びR1 か
ら成る群から選択され、sは1〜50、好ましくは1〜
20の整数で、そしてR1 は式Iと同じ意味を有する)
に適合する分子から選択される成分;
【0019】(F) 一般式III :
【化17】 (式中、R8 は、炭素数4〜25、好ましくは8〜1
2、最も好ましくは9の、線形、環式、または分枝状飽
和一価脂肪族炭化水素部分基で、(C6 H4 )は、オル
ソ、メタ、又はパラフェニレン核で、そしてR1 及びs
は、式II′と同じ意味を有する)に適合する分子から選
択される成分;
2、最も好ましくは9の、線形、環式、または分枝状飽
和一価脂肪族炭化水素部分基で、(C6 H4 )は、オル
ソ、メタ、又はパラフェニレン核で、そしてR1 及びs
は、式II′と同じ意味を有する)に適合する分子から選
択される成分;
【0020】(G) 一般式IV:
【化18】
【0021】(式中、R10は、炭素数1〜25、好まし
くは4〜20の、線形または分枝状飽和または不飽和一
価脂肪族炭化水素部分基で、そしてR1 とXは、式Iと
同じ意味を有する)に適合する分子から選択される成
分。
くは4〜20の、線形または分枝状飽和または不飽和一
価脂肪族炭化水素部分基で、そしてR1 とXは、式Iと
同じ意味を有する)に適合する分子から選択される成
分。
【0022】留意すべきは、上記に特定した成分は、全
部が独立的な物質である必要はないということである。
例えば、フルオロジルコン酸(すなわち、H2 Zr
F6 )は、成分(B)と成分(C)との両方の機能を果
たす。
部が独立的な物質である必要はないということである。
例えば、フルオロジルコン酸(すなわち、H2 Zr
F6 )は、成分(B)と成分(C)との両方の機能を果
たす。
【0023】成分(A)は、x及びzが、それぞれ0
で、R2 及びR5 が、それぞれ水素またはカチオンまた
はカチオン部分である時の式Iに適合する分子から選択
されるのが好ましく、このような物質は、例えば、R2
が水素でR5 が( 1/3 )Fe+3の場合には、成分
(A)、(B)、及び(C)全部の機能を果たすことが
できる。
で、R2 及びR5 が、それぞれ水素またはカチオンまた
はカチオン部分である時の式Iに適合する分子から選択
されるのが好ましく、このような物質は、例えば、R2
が水素でR5 が( 1/3 )Fe+3の場合には、成分
(A)、(B)、及び(C)全部の機能を果たすことが
できる。
【0024】本発明のこの実施態様に従って行われる処
理に使用される溶液中の成分(A)の量は、1リットル
当たり燐0.00001〜0.0032グラム原子、又
はより好ましくは1リットル当たり燐0.0005〜
0.0015グラム原子の濃度となるようにすることが
好ましい。本発明のこの実施態様に従って行われる処理
に使用される溶液中の成分(B)の量は、成分(B)の
項に記載の金属原子すべての全量が、1リットル当たり
0.00001〜0.01グラム原子、又はより好まし
くは1リットル当たり0.0001〜0.003グラム
原子の濃度となるようにすることも、独立的に好まし
い。
理に使用される溶液中の成分(A)の量は、1リットル
当たり燐0.00001〜0.0032グラム原子、又
はより好ましくは1リットル当たり燐0.0005〜
0.0015グラム原子の濃度となるようにすることが
好ましい。本発明のこの実施態様に従って行われる処理
に使用される溶液中の成分(B)の量は、成分(B)の
項に記載の金属原子すべての全量が、1リットル当たり
0.00001〜0.01グラム原子、又はより好まし
くは1リットル当たり0.0001〜0.003グラム
原子の濃度となるようにすることも、独立的に好まし
い。
【0025】成分(A)を式Iに適合する分子から選択
する際に、(i) xがゼロか、R2 にある炭素の数の0.
5倍以上とし、(ii) yがゼロか、R4 にある炭素の数
の0.5倍以上とし、そして (iii)zがゼロか、R5 に
ある炭素の数の0.5倍以上とすることも、独立的に好
ましい。
する際に、(i) xがゼロか、R2 にある炭素の数の0.
5倍以上とし、(ii) yがゼロか、R4 にある炭素の数
の0.5倍以上とし、そして (iii)zがゼロか、R5 に
ある炭素の数の0.5倍以上とすることも、独立的に好
ましい。
【0026】成分(A)の少なくとも50%、少なくと
も75%、又は少なくとも90%が、モノ(ヘキシルト
リエトキシル)二酸燐酸塩、すなわち、
も75%、又は少なくとも90%が、モノ(ヘキシルト
リエトキシル)二酸燐酸塩、すなわち、
【化19】C6 H13−(O−CH2 −CH2 )3 −O−
PO(OH)2
PO(OH)2
【0027】およびその塩から選択されるならば、更に
好ましい。
好ましい。
【0028】詳細な組成とは無関係に、本発明のこの実
施態様の工程の間に成形アルミニウム表面と接触される
組成物には、上に記載の成分(A)、(B)及び(C)
が全部で0.001〜10重量%(「W%」)、より好
ましくは0.005〜0.05W%含有され、選択的成
分及び水が残りを占めるのが好ましい。ここに使用の水
は、脱イオンされる必要もなく、他のやり方で特に精製
される必要もなく、通常の水道水で満足すべき結果が得
られる。成形アルミニウム表面と接触される間の組成物
のpHは、1〜8の範囲が好ましく、より好ましくは2〜
5の範囲である。このpHは、使用中に好ましくは硝酸お
よび/または硫酸を用いて必要に応じて調整し、所望の
範囲にpHを維持することができる。
施態様の工程の間に成形アルミニウム表面と接触される
組成物には、上に記載の成分(A)、(B)及び(C)
が全部で0.001〜10重量%(「W%」)、より好
ましくは0.005〜0.05W%含有され、選択的成
分及び水が残りを占めるのが好ましい。ここに使用の水
は、脱イオンされる必要もなく、他のやり方で特に精製
される必要もなく、通常の水道水で満足すべき結果が得
られる。成形アルミニウム表面と接触される間の組成物
のpHは、1〜8の範囲が好ましく、より好ましくは2〜
5の範囲である。このpHは、使用中に好ましくは硝酸お
よび/または硫酸を用いて必要に応じて調整し、所望の
範囲にpHを維持することができる。
【0029】成形アルミニウム表面と接触される間の組
成物の温度は、10〜85℃が好ましく、より好ましく
は21〜54℃である。接触の方法は、噴霧、浸漬、ま
たは他の便利な方法またはこれらの方法をとりまぜた方
法でもよい。接触時間は、5〜60秒が好ましく、より
好ましくは20〜30秒である。また一般に好ましいの
は、本発明の処理を行った後と、乾燥、印刷、ラッカー
塗りなどの後工程の前に、最初に水で、次いで再び脱イ
オン水で、この処理された表面をゆすぐことである。
成物の温度は、10〜85℃が好ましく、より好ましく
は21〜54℃である。接触の方法は、噴霧、浸漬、ま
たは他の便利な方法またはこれらの方法をとりまぜた方
法でもよい。接触時間は、5〜60秒が好ましく、より
好ましくは20〜30秒である。また一般に好ましいの
は、本発明の処理を行った後と、乾燥、印刷、ラッカー
塗りなどの後工程の前に、最初に水で、次いで再び脱イ
オン水で、この処理された表面をゆすぐことである。
【0030】上記のような処理に直接使用される処理方
法および組成物に加えて、もう一つの実施態様がある
が、それは処理に用いられる組成物が水による希釈で得
られる濃厚液である。このような濃厚液は、金属表面処
理に直接的に使用される組成物に対して上記に定義のW
%の30〜200倍の量だけ上に記載の成分(A)、
(B)、(C)、更に選択的成分(D)、(E)、
(F)、及び/または(G)を含有しているのが好まし
い。
法および組成物に加えて、もう一つの実施態様がある
が、それは処理に用いられる組成物が水による希釈で得
られる濃厚液である。このような濃厚液は、金属表面処
理に直接的に使用される組成物に対して上記に定義のW
%の30〜200倍の量だけ上に記載の成分(A)、
(B)、(C)、更に選択的成分(D)、(E)、
(F)、及び/または(G)を含有しているのが好まし
い。
【0031】本発明のこの実施態様の組成物が、上に定
義の選択的成分(D)及び(E)を十分な量だけ含有す
ることは、他の全ての選択と独立に好ましいものであ
る。こうすることによって、この組成物がそれらを含有
しなければ起きるかも知れない濃厚さや、外見にも分か
る相分離の傾向を防止するか、少なくとも相当程度減少
することができる。上記に定義の成分(A)〜(C)及
び選択的組成(F)及び(G)のみを含有する組成物に
おいては、調液後組成物をしばらく使用した後では、金
属含有量が多い相が残りの組成物から分離する傾向があ
ることが知られている。成分(D):成分(E)の重量
比は、3:1〜1:3の範囲が好ましく、あるいはより
好ましくは1.7:1〜1:1.4の範囲である。以上
とは独立的ではあるが、成分(A)に対する成分(D)
及び(E)を併せたものの重量比は、 3.3:1〜
1:2の範囲が好ましく、あるいはより好ましくは1.
8:1〜 1:1.5の範囲である。
義の選択的成分(D)及び(E)を十分な量だけ含有す
ることは、他の全ての選択と独立に好ましいものであ
る。こうすることによって、この組成物がそれらを含有
しなければ起きるかも知れない濃厚さや、外見にも分か
る相分離の傾向を防止するか、少なくとも相当程度減少
することができる。上記に定義の成分(A)〜(C)及
び選択的組成(F)及び(G)のみを含有する組成物に
おいては、調液後組成物をしばらく使用した後では、金
属含有量が多い相が残りの組成物から分離する傾向があ
ることが知られている。成分(D):成分(E)の重量
比は、3:1〜1:3の範囲が好ましく、あるいはより
好ましくは1.7:1〜1:1.4の範囲である。以上
とは独立的ではあるが、成分(A)に対する成分(D)
及び(E)を併せたものの重量比は、 3.3:1〜
1:2の範囲が好ましく、あるいはより好ましくは1.
8:1〜 1:1.5の範囲である。
【0032】本発明のこの実施態様の組成物および方法
は、’351号特許に記載のものより優れた利点が幾つ
か存在する。すなわち、
は、’351号特許に記載のものより優れた利点が幾つ
か存在する。すなわち、
【0033】−本発明の処理後、改良された表面可動性
や他の利点を損なうことなく、’351号特許の実施例
に従って処理された表面よりも多くの回数水道水または
脱イオン水で処理表面をゆすぐことができる。
や他の利点を損なうことなく、’351号特許の実施例
に従って処理された表面よりも多くの回数水道水または
脱イオン水で処理表面をゆすぐことができる。
【0034】−処理される表面と洗浄組成物との間の接
触または洗浄後かつ本発明の組成物による処理以前のゆ
すぎ液との間の接触が長引いた場合(例えば、高速生産
ラインの予期せざる停止の結果として)、加水分解され
た酸化アルミニウムと信じられる薄茶から濃褐色の斑点
が処理された表面に現れることが時々あり、このような
斑点は、本発明の処理によって取り除かれるが、’35
1号特許の実施例に教示される方法を用いた後ではこの
ような斑点はなかなか取りきれない。
触または洗浄後かつ本発明の組成物による処理以前のゆ
すぎ液との間の接触が長引いた場合(例えば、高速生産
ラインの予期せざる停止の結果として)、加水分解され
た酸化アルミニウムと信じられる薄茶から濃褐色の斑点
が処理された表面に現れることが時々あり、このような
斑点は、本発明の処理によって取り除かれるが、’35
1号特許の実施例に教示される方法を用いた後ではこの
ような斑点はなかなか取りきれない。
【0035】−本発明の方法は、pHを十分に低くして操
作するのが容易なので、’351号特許の実施例の方法
よりも微生物の成長を防止することができる。
作するのが容易なので、’351号特許の実施例の方法
よりも微生物の成長を防止することができる。
【0036】−本発明の組成物の補給または希釈に対し
ては、容易に入手し得る工業用水や水道水ならほとんど
全てが使用可能であるが、’351号特許に教示のもの
は一般に脱イオン水を用いて初めて最良の結果が得られ
るという違いがある。
ては、容易に入手し得る工業用水や水道水ならほとんど
全てが使用可能であるが、’351号特許に教示のもの
は一般に脱イオン水を用いて初めて最良の結果が得られ
るという違いがある。
【0037】−本発明の方法によって得られた表面は、
水によって極めて容易に湿潤状態になるので「水滴跡の
斑点」が付かない状態になる。この斑点はアルミニウム
缶の製造業者にとっては好ましくないと考えられてい
る。’351号特許に従って製造された缶は、本発明の
それよりも、このような水滴跡の斑点を非常に形成し易
い。
水によって極めて容易に湿潤状態になるので「水滴跡の
斑点」が付かない状態になる。この斑点はアルミニウム
缶の製造業者にとっては好ましくないと考えられてい
る。’351号特許に従って製造された缶は、本発明の
それよりも、このような水滴跡の斑点を非常に形成し易
い。
【0038】本発明のもう一つ別の実施態様は、上記に
明快に記述された組成物およびその使用法、および上記
に引用された米国特許出願第395,620号及び米国
特許第4,859,351号に記載の組成物およびその
使用法を包含するが、これらは、貯蔵時および/または
使用時の微生物の作用による劣化を受けないように、さ
らに/または調整時および/または使用時に発泡するこ
ともないように保護されているものである。
明快に記述された組成物およびその使用法、および上記
に引用された米国特許出願第395,620号及び米国
特許第4,859,351号に記載の組成物およびその
使用法を包含するが、これらは、貯蔵時および/または
使用時の微生物の作用による劣化を受けないように、さ
らに/または調整時および/または使用時に発泡するこ
ともないように保護されているものである。
【0039】どんな抗菌剤や殺菌剤でも、組成物の可動
性強化特性や安定性に悪影響を与えるものを除いて、本
明細書に既に教示のように組成物に十分な量有利に添加
し、微生物の成長を防止することができる。過酸化水素
は、この目的のために一般に最も好ましい。水性濃厚組
成物は、既に記載のように、乾燥後に可動性を強化する
ために金属に直接使用する組成物とするにはその濃厚液
の約99倍の水で希釈することが適当であるが、この濃
厚液組成物の場合、過酸化水素の濃度は、0.375〜
3.75W%の範囲が好ましく、1.4〜2.2W%の
範囲の濃度が最も好ましい。より濃厚な組成物の場合
は、好ましい殺菌剤の濃度は、濃厚液の想定される希釈
度によって定めることになる。しかし、一般には、濃厚
過酸化水素は比較的安定性が低いので、この成分は、使
用される場合には、十分薄い濃厚液にのみ添加すること
が好ましく、この場合過酸化水素の濃度は、組成物を調
整する時点で約3%を超えることはない。
性強化特性や安定性に悪影響を与えるものを除いて、本
明細書に既に教示のように組成物に十分な量有利に添加
し、微生物の成長を防止することができる。過酸化水素
は、この目的のために一般に最も好ましい。水性濃厚組
成物は、既に記載のように、乾燥後に可動性を強化する
ために金属に直接使用する組成物とするにはその濃厚液
の約99倍の水で希釈することが適当であるが、この濃
厚液組成物の場合、過酸化水素の濃度は、0.375〜
3.75W%の範囲が好ましく、1.4〜2.2W%の
範囲の濃度が最も好ましい。より濃厚な組成物の場合
は、好ましい殺菌剤の濃度は、濃厚液の想定される希釈
度によって定めることになる。しかし、一般には、濃厚
過酸化水素は比較的安定性が低いので、この成分は、使
用される場合には、十分薄い濃厚液にのみ添加すること
が好ましく、この場合過酸化水素の濃度は、組成物を調
整する時点で約3%を超えることはない。
【0040】どんな発泡防止剤でも、組成物に対して既
に記載の可動性強化特性や安定性に悪影響を与えるもの
を除いて、本明細書に既に教示のように組成物に十分な
量有利に添加し、組成物の調整時および/または使用時
に認められる発泡現象の量を減少させることができる。
好ましい発泡防止剤は、ワックス、低揮発度液状パラフ
ィン炭化水素、および高分子量脂肪酸誘導体を組み合わ
せたものである。一般に、シリコーン発泡防止剤は、本
発明に使用するには望ましくはない。これは、水滴跡の
斑点を形成する傾向があるからである。0.05〜2W
%に相当する発泡防止剤が一般に好ましく、0.5〜1
W%が一般に最も好ましい。
に記載の可動性強化特性や安定性に悪影響を与えるもの
を除いて、本明細書に既に教示のように組成物に十分な
量有利に添加し、組成物の調整時および/または使用時
に認められる発泡現象の量を減少させることができる。
好ましい発泡防止剤は、ワックス、低揮発度液状パラフ
ィン炭化水素、および高分子量脂肪酸誘導体を組み合わ
せたものである。一般に、シリコーン発泡防止剤は、本
発明に使用するには望ましくはない。これは、水滴跡の
斑点を形成する傾向があるからである。0.05〜2W
%に相当する発泡防止剤が一般に好ましく、0.5〜1
W%が一般に最も好ましい。
【0041】本発明の処理方法は、’351号特許に教
示されるような改良された可動性、低表面摩擦係数、高
品質印刷性、およびラッカー類の良好な密着性などの利
点が全て備わっている。
示されるような改良された可動性、低表面摩擦係数、高
品質印刷性、およびラッカー類の良好な密着性などの利
点が全て備わっている。
【0042】本発明の実際は、以下の実施例を考慮する
ことによってさらに理解され得るであろうが、これら実
施例は本発明を限定するものではない。 実施例
ことによってさらに理解され得るであろうが、これら実
施例は本発明を限定するものではない。 実施例
【0043】実施例1〜7及び比較例に対する一般条件 これらの実施例において、処理された表面は、すでに最
終の形および寸法にある従来的アルミニウム製飲料缶の
表面であった。缶は、まずpH2を有する硫酸水溶液中
にて酸による予備洗浄を54℃にて30秒(「se
c」)行い、次にpH12.3のアルカリ性の、表面活性
剤含有洗浄剤で54℃にて60sec洗浄し、更に水道
水で30secゆすぎ、その後で以下の特定的実施例に
記載のように本発明の組成物で処理した。(特定的実施
例に記載の組成物は、本発明の濃厚物に対するもので、
処理に際しては、表1に記載の濃厚物の水道水中のW%
の溶液を使用した。)この処理後、缶は、先ず水道水で
30secゆすぎ、次に脱イオン水で90secゆす
ぎ、最後に210℃で乾燥した。乾燥後の缶の静的表面
摩擦係数は、’351号特許に記載のように測定した。
終の形および寸法にある従来的アルミニウム製飲料缶の
表面であった。缶は、まずpH2を有する硫酸水溶液中
にて酸による予備洗浄を54℃にて30秒(「se
c」)行い、次にpH12.3のアルカリ性の、表面活性
剤含有洗浄剤で54℃にて60sec洗浄し、更に水道
水で30secゆすぎ、その後で以下の特定的実施例に
記載のように本発明の組成物で処理した。(特定的実施
例に記載の組成物は、本発明の濃厚物に対するもので、
処理に際しては、表1に記載の濃厚物の水道水中のW%
の溶液を使用した。)この処理後、缶は、先ず水道水で
30secゆすぎ、次に脱イオン水で90secゆす
ぎ、最後に210℃で乾燥した。乾燥後の缶の静的表面
摩擦係数は、’351号特許に記載のように測定した。
【0044】実施例1 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 塩化スズ溶液、25重量%水溶液 300 ETHFACTM 136 400 ETHOXTM MI−14 100 二弗化アンモニウム溶液、25重量%水溶液 135 DEQUESTTM 2010 25 水 9040
【0045】実施例2 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 クエン酸アンモニウム第二鉄塩、25重量%水溶液 300 ETHFACTM 136 400 ETHOXTM MI−14 100 二弗化アンモニウム溶液、25重量%水溶液 135 DEQUESTTM 2010 25 水 9040
【0046】実施例3 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 硫酸アンモニウムセリウム 4 ETHFACTM 136 30 二弗化アンモニウム溶液、25重量%水溶液 16 DEQUESTTM 2010 2 硫酸 1 TRITONTM N 101 5 水 942
【0047】実施例4 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 塩化アルミニウム 10 ETHFACTM 136 50 二弗化アンモニウム溶液、25重量%水溶液 11 TRITONTM N 101 6 クエン酸 6 エトキシ化アルコール表面活性剤 11 水 906
【0048】実施例5 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 フルオロジルコン酸 15 モノ(ヘキシルトリエトキシ)燐酸塩 70 ポリ(オキシエチレン)イソステアリン酸塩 20 (イソステアリン酸塩一単位当たりオキシエチレン単位平均14個) 二弗化アンモニウム溶液、25重量%水溶液 19 アミノ酢酸 20 水 856
【0049】実施例6 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 フルオロジルコン酸 15 モノ(ヘキシルトリエトキシ)燐酸塩 30 ETHOXTM MI−14 20 二弗化アンモニウム溶液、25重量%水溶液 15 ブタン−2−フォスフォン酸トリカルボン酸塩 10 水 910
【0050】実施例7 この実施例の濃厚物は、次の組成を有した。成 分 組成物中の重量部 フルオロジルコン酸 10 ポリオキシエチレン イソステアリン酸塩 10 (イソステアリン酸塩一モル当たり-C2H4O- 基平均14個) TRITONTM H−66 80 DEQUESTTM 2010 2.5 二弗化アンモニウム溶液、25重量%水溶液 4 水 893.5
【0051】上記の組成物において、DEQUEST
2010は、主成分が1−ヒドロキシエチリデン−1−
ジフォフォン酸とされている物質に対する商標名であ
り、TORITON N 101は、主成分がノニルフ
ェノキシポリ(エトキシ)エタノール(単位分子当たり
エトキシ基平均9〜10個)とされている表面活性剤の
商標名である。
2010は、主成分が1−ヒドロキシエチリデン−1−
ジフォフォン酸とされている物質に対する商標名であ
り、TORITON N 101は、主成分がノニルフ
ェノキシポリ(エトキシ)エタノール(単位分子当たり
エトキシ基平均9〜10個)とされている表面活性剤の
商標名である。
【0052】表1は、使用濃厚物の特定量、処理条件、
および静的摩擦係数を示すが、該摩擦係数は、潤滑油と
これらの実施例に対する表面調質剤の吸着によって缶の
表面について得られたものである。
および静的摩擦係数を示すが、該摩擦係数は、潤滑油と
これらの実施例に対する表面調質剤の吸着によって缶の
表面について得られたものである。
【0053】
【表1】
【0054】実施例8 本例は、好ましい発泡防止剤および好ましい殺菌剤を含
有する組成物の実施例であるが、他の条件は '351号
特許の教示に従うものである。
有する組成物の実施例であるが、他の条件は '351号
特許の教示に従うものである。
【0055】一番目の濃厚物は、ETHOXTM MI−
14を880重量部(「PBW」)、OOLLOID
999TM(高分子量脂肪酸誘導体、コロイド社(Col
loids,Inc..394 Frelinghuy
sen Ave.,Newark,New Jerse
y 07114,U.S.A.)から市販のもの)を6
0 PBW、GP−295TM 消泡剤(白鉱油中に固体
ワックスを約10%懸濁させたもの、ジェネーズ ポリ
マー社(Genese Polymers Cor
p.,Flint,Michigan,48507,
U.S.A.)から市販)を60 PBW混合して調整
した。ETHOXTM MI−14は、最初混合タンク中
で27〜32℃にて融解した。次に、他の二つの物質を
記載の順序で添加し、混合し、濁ってはいるが目視では
均一な液体を作った。塊は存在しなかった。
14を880重量部(「PBW」)、OOLLOID
999TM(高分子量脂肪酸誘導体、コロイド社(Col
loids,Inc..394 Frelinghuy
sen Ave.,Newark,New Jerse
y 07114,U.S.A.)から市販のもの)を6
0 PBW、GP−295TM 消泡剤(白鉱油中に固体
ワックスを約10%懸濁させたもの、ジェネーズ ポリ
マー社(Genese Polymers Cor
p.,Flint,Michigan,48507,
U.S.A.)から市販)を60 PBW混合して調整
した。ETHOXTM MI−14は、最初混合タンク中
で27〜32℃にて融解した。次に、他の二つの物質を
記載の順序で添加し、混合し、濁ってはいるが目視では
均一な液体を作った。塊は存在しなかった。
【0056】二番目の濃厚物は、少なくとも数カ月の貯
蔵に適したもので、上記の一番目の濃厚物4747 P
BWを、水、好ましくは脱イオン水917 PBWと3
7.5過酸化水素37.5%水溶液40 PBWと一緒
に混合して調整した。この二番目の濃厚物は、次に所望
時に希釈して、’351号特許に一般に記載のようにア
ルミニウム表面を直接に処理する組成物とすることがで
きる。
蔵に適したもので、上記の一番目の濃厚物4747 P
BWを、水、好ましくは脱イオン水917 PBWと3
7.5過酸化水素37.5%水溶液40 PBWと一緒
に混合して調整した。この二番目の濃厚物は、次に所望
時に希釈して、’351号特許に一般に記載のようにア
ルミニウム表面を直接に処理する組成物とすることがで
きる。
【0057】実施例9及び10 これらの実施例では、金属含有塩およびエトキシ化燐酸
塩を含有する好ましい安定化組成物が示される。以下の
表2に記載の組成物は、濃厚物であるが、水道水で、例
えば自分の重量の50〜200倍希釈した後で金属容器
を処理するに好適なものである。
塩を含有する好ましい安定化組成物が示される。以下の
表2に記載の組成物は、濃厚物であるが、水道水で、例
えば自分の重量の50〜200倍希釈した後で金属容器
を処理するに好適なものである。
【0058】
【表2】
【0059】表2に示される成分の源および特性の中で
いままで明示しなかったものは、以下の通りである。E
THOXTM 2684は、エトックス ケミカル社(E
thox Chemicals,Inc.,Green
ville,South Carolina 2060
6,USA)から市販のもので、x及びzが0で独立的
に選択され、R2 、R3 、及びR5 が、すべて水素で、
R4 が、C8-10アルキル基で、そしてyが平均して15
である時の一般式Iに対応する。TRITON TMDF−
16は、ローム ハース社(Rohm & Haas,
Philadelphia,Pennsylvania
19105,USA)から市販のもので、修飾された
ポリエトキシ化直鎖アルコールとされている。TRYC
OLTMLF−1は、エメリー ケミカル社(the E
Mery ChemicalDivision of
Henkel Corporation,Cincin
ati,Ohio 45249,USA)から市販のも
ので、アルキル ポリエーテルとされている。IGEP
ALTM CO−880は、GAF社(GAFCorp,
Wayne,New Jersey 07470,US
A)から市販のもので、エトキシ化ノニルアルコールと
されている。
いままで明示しなかったものは、以下の通りである。E
THOXTM 2684は、エトックス ケミカル社(E
thox Chemicals,Inc.,Green
ville,South Carolina 2060
6,USA)から市販のもので、x及びzが0で独立的
に選択され、R2 、R3 、及びR5 が、すべて水素で、
R4 が、C8-10アルキル基で、そしてyが平均して15
である時の一般式Iに対応する。TRITON TMDF−
16は、ローム ハース社(Rohm & Haas,
Philadelphia,Pennsylvania
19105,USA)から市販のもので、修飾された
ポリエトキシ化直鎖アルコールとされている。TRYC
OLTMLF−1は、エメリー ケミカル社(the E
Mery ChemicalDivision of
Henkel Corporation,Cincin
ati,Ohio 45249,USA)から市販のも
ので、アルキル ポリエーテルとされている。IGEP
ALTM CO−880は、GAF社(GAFCorp,
Wayne,New Jersey 07470,US
A)から市販のもので、エトキシ化ノニルアルコールと
されている。
Claims (5)
- 【請求項1】 (a)成形された金属製品の表面を洗浄
剤水溶液で洗浄する工程、 (b)(i) 工程(a)に次いで水でゆすぐ工程 (b)(ii) ゆすいだ表面を乾燥する工程、および (c) 次いで該製品を移送する工程、 の諸工程を包含する方法において、前記b(i) の工程
後、b(ii)の工程前に該金属製品の表面を、水および以
下の成分: (A) 化学一般式I: 【化1】 (式中、R1 、R3 、及びR6 は、それぞれ水素および
炭素数1〜4のアルキル基から独立的に選択され、x、
y、及びzは、それぞれ整数で、0〜25の範囲で独立
的に選択され、R2 、R4 、及びR5 は、それぞれ水
素、一価のカチオン、多価カチオンの一価部分、炭素数
1〜20のアルキル基、及び炭素数1〜20のアリール
及びアリールアルキル基から独立的に選択されるが、た
だし、R2 、R4 、及びR5 の少なくとも一つは、水素
ではなくかつ式中のR2 、R4 、及びR5 の少なくとも
一つと燐原子との間にアルコキシ基を少なくとも一つは
結合させているものである)で示される化合物から選択
される水溶性成分; (B) Fe,Zr,Sn,Al,及びCeから成る群
から選択される原子を包含する水溶性塩の群から選択さ
れる成分; (C) 水溶性の金属エッチング剤、さらに選択的に
は、 (D) 成分(B)の金属イオンをキレートし得るキレ
ート剤から選択される成分、 (E) 一般式II: 【化2】 (式中、R7 は、直鎖状または分枝状、飽和または不飽
和脂肪族炭化水素部分基で、そしてR1 とxは、式Iに
おける場合と同様である)で示される化合物から選択さ
れる成分、を含有する液状組成物と接触させることを包
含し、かつ金属表面と前記液状組成物との接触は、この
ように処理された金属表面の静摩擦係数を1.5未満に
するに効果的な温度にて十分な時間行うことを特徴とす
る成形された金属表面の表面調整方法。 - 【請求項2】 水および次の成分: (A) 化学一般式I: 【化3】 (式中、R1 、R3 、及びR6 は、それぞれ水素および
炭素数1〜4のアルキル基から独立的に選択され、x、
y、及びzは、それぞれ整数で、0〜25の範囲で独立
的に選択され、R2 、R4 、及びR5 は、それぞれ水
素、一価のカチオン、多価カチオンの一価部分、炭素数
1〜20のアルキル基、及び炭素数1〜20のアリール
及びアリールアルキル基から独立的に選択されるが、た
だし、R2 、R4 、及びR5 の少なくとも一つは、水素
ではないものである)で示される化合物から選択される
水溶性成分; (B) Fe,Zr,Sn,Al,及びCeから成る群
から選択される原子を包含する水溶性塩の群から選択さ
れる成分、 (C) 金属をエッチングする成分として、硝酸、硫
酸、燐酸、弗化水素酸、塩化水素酸、臭化水素酸、沃化
水素酸;硫酸、弗化水素酸および燐酸の酸性塩;硝酸、
硫酸、燐酸、弗化水素酸、塩化水素酸、臭化水素酸、お
よび沃化水素酸とこれらの酸のイオン積定数より小さい
イオン積定数を有する塩基との塩;及びこれらの物質の
混合物から成る群から選択される1種又は2種以上の金
属をエッチングする成分、さらに選択的には、 (D) 成分(B)の金属イオンをキレートし得るキレ
ート剤から選択される成分、好ましくは、各分子が、ア
ミノ基、置換アミノ基、カルボキシル基、燐酸塩、スル
フォン酸塩、及びカルボニル部分基から成る群から選択
される少なくとも二つの部分基を有する分子(ポリマー
分子を包含する)から成る群から選択される成分;及び (E) 一般式II: 【化4】 (式中、R7 は、直鎖状または分枝状、飽和または不飽
和脂肪族炭化水素部分基で、そしてR1 とxは、式Iと
同じ意味を有する)で示される化合物から選択される成
分、を含有することを特徴とする表面調整剤。 - 【請求項3】 (a)成形された金属製品の表面を洗浄
剤水溶液で洗浄する工程、 (b)(i) 工程(a)に次いで水でゆすぐ工程 (b)(ii) ゆすいだ表面を乾燥する工程、および (c) 次いで該製品を移送する工程、 の諸工程を包含する方法において、前記b(i) の工程
後、b(ii)の工程前に該金属製品の表面を、水および以
下の成分: (A) 化学一般式I: 【化5】 (式中、R1 、R3 、及びR6 は、それぞれ水素および
炭素数1〜4のアルキル基から独立的に選択され、x、
y、及びzは、それぞれ整数で、0〜25の範囲で独立
的に選択され、R2 、R4 、及びR5 は、それぞれ水
素、一価のカチオン、多価カチオンの一価部分、炭素数
1〜20のアルキル基、及び炭素数1〜20のアリール
及びアリールアルキル基から独立的に選択されるが、但
し、R2 、R4 、及びR5 の少なくとも一つは、水素で
はなくかつ式中のR2 、R4 、及びR5 の少なくとも一
つと燐原子との間にアルコキシ基を少なくとも一つは結
合させているものである)で示される化合物から選択さ
れる水溶性成分; (B) Fe,Zr,Sn,Al,及びCeから成る群
から選択される原子を包含する水溶性塩の群から選択さ
れる成分; (C) 水溶性の金属エッチング剤、 (D) 成分(B)の金属イオンをキレートし得るキレ
ート剤から選択される成分、 (E) 一般式II′: 【化6】 (式中、R7 は、炭素数1〜25の、直鎖状、環状、ま
たは分枝状飽和一価脂肪族炭化水素部分基で、Xは、水
素、ハロゲン、フェニル及びR1 から成る群から選択さ
れ、sは、1〜50の整数で、そしてR1 は式Iにおけ
る場合と同様である)で示される化合物から選択される
成分; (F) 一般式III : 【化7】 (式中、R8 は、炭素数4〜25の、直鎖状、環状、ま
たは分枝状飽和一価脂肪族炭化水素部分基で、( C6 H
4 )は、オルソ、メタ、又はパラ フェニレン核で、そ
してR1 及びsは、式IIにおける場合と同様である)で
示される化合物から選択される成分;そして、選択的に
は (G) 一般式IV: 【化8】 (式中、R10は、炭素数1〜25の、直鎖状または分枝
状飽和または不飽和一価脂肪族炭化水素部分基で、そし
てR1 とxは、式Iにおける場合と同様である)で示さ
れる化合物から選択される成分、を含有する液状組成物
と接触させる工程を包含し、前記液状組成物に存在する
成分(D)及び(E)は、液状組成物を相分離させない
ために十分な量を含むものであってかつ金属表面と前記
液状組成物との接触は、このように処理された金属表面
の静摩擦係数を1.5未満にするに効果的な温度にて十
分な時間行うことを特徴とする成形された金属表面の表
面調整方法。 - 【請求項4】 水および次の成分: (A) 化学一般式I: 【化9】 (式中、R1 、R3 、及びR6 は、それぞれ水素および
炭素数1〜4のアルキル基から、好ましくは水素および
メチル基から独立的に選択され、最も好ましくは水素で
あり、x、y、及びzは、それぞれ整数で、0〜25の
範囲で独立的に選択され、R2 、R4 、及びR5 は、そ
れぞれ水素、一価のカチオン、多価カチオンの一価部
分、炭素数1〜20のアルキル基、及び炭素数1〜20
のアリール及びアリールアルキル基から独立的に選択さ
れるが、但し、R2 、R4 、及びR5 の少なくとも一つ
は、水素ではないものである)で示される化合物から選
択される水溶性成分; (B) Fe,Zr,Sn,Al,及びCeから成る群
から選択される原子を包含する水溶性塩の群から選択さ
れる成分; (C) 金属をエッチングする成分として、硝酸、硫
酸、燐酸、弗化水素酸、塩化水素酸、臭化水素酸、沃化
水素酸;硫酸、弗化水素酸および燐酸の酸性塩;硝酸、
硫酸、燐酸、弗化水素酸、塩化水素酸、臭化水素酸、お
よび沃化水素酸とこれらの酸のイオン積定数より小さい
イオン積定数を有する塩基との塩;及びこれらの物質の
混合物から成る群から選択される1種又は2種以上の金
属をエッチングする成分、さらに選択的には、 (D) 一般式II′: 【化10】 (式中、R7 は、炭素数1〜25の、直鎖状、環状、ま
たは分枝状飽和一価脂肪族炭化水素部分基で、Xは、水
素、ハロゲン、フェニル及びR1 から成る群から選択さ
れ、sは、1〜50の整数で、そしてR1 は式Iにおけ
る場合と同様である)で示される化合物から選択される
成分; (E) 一般式III : 【化11】 (式中、R8 は、炭素数4〜25の、線形、環式、また
は分枝状飽和一価脂肪族炭化水素部分基で、( C
6 H4 )は、オルソ、メタ、又はパラ フェニレン核
で、そしてR1 及びsは、式II′における場合と同様で
ある)で示される化合物から選択される成分;そして、
選択的には (F) 成分(B)の金属イオンをキレートしうるキレ
ート剤から選択される成分、 (G) 一般式IV: 【化12】 (式中、R10は、炭素数1〜25の、直鎖状または分枝
状飽和または不飽和一価脂肪族炭化水素部分基で、そし
てR1 とxは、式Iと同じ意味を有する)で示される化
合物から選択される成分、を含有することを特徴とする
表面調整剤。 - 【請求項5】 (A)エトキシル化脂肪酸、エトキシル
化脂肪酸の塩、炭素原子少なくとも4個を有しアルコー
ル単位モル当たり縮合エチレンオキサイドを最大約20
モル含有するエトキシル化アルコール、エトキシル化ア
ルキルアルコール燐酸エステル、及びこれらの混合物か
ら成る群から選択される水溶性エトキシル化有機物質、
(B) 微生物の作用による組成物の劣化を防止するの
に効果的な量の過酸化水素、 および水から実質的に成り、1〜6.5の間のpHを有
し、金属製缶の表面に塗布・乾燥されると缶の表面にフ
ィルムを形成し、前記表面の静摩擦係数を減少させるこ
とを特徴とする表面調整剤。