JPH0368091B2 - - Google Patents

Info

Publication number
JPH0368091B2
JPH0368091B2 JP4706285A JP4706285A JPH0368091B2 JP H0368091 B2 JPH0368091 B2 JP H0368091B2 JP 4706285 A JP4706285 A JP 4706285A JP 4706285 A JP4706285 A JP 4706285A JP H0368091 B2 JPH0368091 B2 JP H0368091B2
Authority
JP
Japan
Prior art keywords
weight
friction
coefficient
tin
graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP4706285A
Other languages
Japanese (ja)
Other versions
JPS61207549A (en
Inventor
Yoshitaka Tomyama
Kojiro Saito
Hideo Ooyabu
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NIPPON FUNMATSU GOKIN KK
Original Assignee
NIPPON FUNMATSU GOKIN KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NIPPON FUNMATSU GOKIN KK filed Critical NIPPON FUNMATSU GOKIN KK
Priority to JP4706285A priority Critical patent/JPS61207549A/en
Publication of JPS61207549A publication Critical patent/JPS61207549A/en
Publication of JPH0368091B2 publication Critical patent/JPH0368091B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】[Detailed description of the invention]

産業上の利用分野 本発明は、高摩擦係数を有する乾式焼結摩擦材
料に関し、更に詳しくは、二輪及び四輪自動車、
産業用車両、鉄道用車両等のブレーキライニング
材、デイスクブレーキパツド材、クラツチフエー
シング材等として有用な摩擦合金材料に関する。 従来の技術及びその問題点 従来車両用特に二輪乃至四輪自動車用の摩擦材
料としては、石綿を含有するレジンモールドが使
用されて来たが、現今の公害防止の要望に対処す
べく、金属繊維を含有するセミメタリツクタイプ
の材料が広く使用される様になつている。しかし
ながら、このセミメタリツクタイプの摩擦材料に
も、降雨時に摩擦係数が低下する、高負荷等の苛
酷な条件下ではレジンの炭化によりやはり摩擦係
数が低下する等の欠点がある。従つて、最近では
焼結合金系の摩擦材料が次第に使用される様にな
つて来たが、これについしても更に性能向上が求
められている。即ち、自動車においては、省エネ
ルギーの為の小型化及び計量化が急速に進行して
おり、デイスクブレーキ機構等に対しても小型化
が要求されている。そして、デイスクブレーキ機
構等の小型化を実現する為には、摩擦係数が高
く、摩耗量の少ない新しい焼結合金摩擦材料が必
要となつている。 問題点を解決するための手段 本発明は、上記の如き要求に応えるべくなされ
たものであり、(1)銅30〜70重量%、(2)錫又は錫と
亜鉛の合計量4〜20重量%、(3)黒鉛5〜15重量
%、(4)硫化物固体潤滑剤の少なくとも1種0.3〜
7重量%、(5)金属酸化物の少なくとも1種0.5〜
10重量%及び(6)硬質窒化物の少なくとも1種21〜
50重量%からなることを特徴とする焼結合金摩擦
材料に係る。 本発明によれば、耐摩耗性に優れ、摩擦係数が
高く、操作性に優れ、降雨時にも摩擦係数の低下
を実質的に生じない焼結合金摩擦材料が得られ
る。 以下本発明の焼結合金摩擦材料の各成分につい
て説明する。これ等の各成分は、相互に関連しつ
つ摩擦材料としての物性に影響するので、夫々の
限定理由を個別に論ずることは必ずしも妥当では
ないが、一応の限定理由を併せて示す。 (1) 銅及び(2)錫又は錫と亜鉛 これ等は、合金摩擦材料の素地をなすもので
あり、焼結によつて合金化して、いわゆる青銅
地を形成し、素地の強度を高める。特に強度の
観点から、銅30〜70重量%に対し錫又は錫及び
亜鉛4〜20重量%とする。錫又は錫及び亜鉛が
4重量%未満の場合には、黒鉛その他の非金属
を保持するに充分な強度が得られず、一方20重
量%を上回る場合には、摩擦材料を脆化させ、
強度を低下させる。 (3) 黒鉛 黒鉛の添加は、主として摩擦係数を安定させ
る。即ち、一般に相互に摺動する摩擦材料の二
面間に発生する摩擦力は、(イ)二面間の一部に生
ずる凝着を剪断するに要する力、及び(ロ)硬質粒
子による相手材への掘りおこし力によるといわ
れている。黒鉛は、この様な二面間に存在する
ことにより、二面間に生ずる凝着を制御する。
従つて適当量の黒鉛の存在により、摩擦材料の
摩擦係数が向上するとともに安定化され、併せ
て耐摩耗性も向上する。 黒鉛の量が5重量%未満では、上記の効果が
十分に奏されないのに対し、15重量%を上回る
場合には、材料強度が低下するとともに摩擦係
数が低下する。 (4) 二硫化モリブデン、二硫化タングステン、硫
化マンガン等の硫化物固体潤滑剤の少なくとも
1種 二流化モリブデン等は、黒鉛と同様の効果を
奏するのみならず、いわゆる“鳴き”の防止及
び高荷重時の潤滑性付与という顕著な効果をも
発揮する。二硫化モリブデン等の使用量は、
0.3〜7重量%とする。これ等の使用量が、0.3
%未満の場合には、添加の効果が十分に発揮さ
れず、一方7重量%を上回る場合には、材料強
度及び摩擦係数が低下する。 (5) アルミナ、シリカ、ムライト等の金属酸化物
の少なくとも1種 アルミナ等は、0.5〜10重量%の使用範囲に
おいて、前記の掘りおこし効果を奏するととも
に、摩擦熱により相手側摺動面に生成する酸化
皮膜を除去することにより摩擦材料間の凝着を
安定的に発生させて、安定的な摩擦力を発揮さ
せる。使用量が0.5重量%未満の場合には、上
記の効果が十分に発揮されず、一方10重量%を
上回る場合には、相手側摺動面を荒損させる傾
向がある。 (6) Si3N4、AlN、BN、TiN等の硬質窒化物の
少なくとも1種 これ等は摩擦係数の改善に特に寄与する。こ
れ等の量が21重量%未満では、摩擦係数の向上
が充分に行なわれ得ず、一方50重量%を上回る
場合には、素地強度が低下するとともに、摩耗
量がかえつて増大する。 本発明材料を使用して所望の製品、例えばデ
イスクブレーキ用部品を製造するには、常法に
従つて各原料粉末を配合し、これを所定の形状
にプレス成形した後、中性又は還元性雰囲気中
3〜7Kg/cm2程度の加圧下に730〜880℃程度で
焼成すれば良い。 発明の効果 本発明による焼結合金摩擦材料の摩擦係数は、
従来品(0.3〜0.5程度)に比して高く、0.5〜0.8
程度にも達する。従つて、本発明材料を例えば二
輪及び四輪自動車用のデイスクブレーキのパツド
として使用する場合には、(イ)ブレーキ性能の向
上、(ロ)パツド及びデイスクの耐摩耗性の向上、(ハ)
ブレーキ機構の小型化、(ニ)パツドのインシユレー
ターの簡素化等の効果が奏される。 実施例 以下、実施例及び比較例により本発明の特徴と
するところをより一層明らかにする。 実施例1〜6及び比較例1〜2 第1表に示す割合の各原料と残余銅とからなる
配合物100重量部を4ton/cm2の圧力で成形した後、
成形物をCuメツキした鋼板上に載せ、N2雰囲気
中5Kg/mm2の荷重をかけて780℃で60分間焼成し
た。
INDUSTRIAL APPLICATION FIELD The present invention relates to a dry sintered friction material having a high coefficient of friction, and more particularly, to two-wheeled and four-wheeled vehicles,
This invention relates to friction alloy materials useful as brake lining materials, disc brake pad materials, clutch facing materials, etc. for industrial vehicles, railway vehicles, etc. Conventional technology and its problems Conventionally, resin molds containing asbestos have been used as friction materials for vehicles, especially two- and four-wheeled vehicles, but in order to meet the current demands for pollution prevention, metal fiber molds have been used. Semi-metallic type materials containing . However, this semi-metallic type friction material also has drawbacks, such as a decrease in the coefficient of friction during rain, and a decrease in the coefficient of friction due to carbonization of the resin under severe conditions such as high loads. Therefore, recently, sintered alloy friction materials have been increasingly used, but there is also a demand for further improvement in performance. That is, automobiles are rapidly becoming smaller and more compact in order to save energy, and disc brake mechanisms and the like are also required to be smaller. In order to realize the miniaturization of disc brake mechanisms and the like, new sintered alloy friction materials with a high coefficient of friction and low wear are required. Means for Solving the Problems The present invention was made in response to the above-mentioned demands, and includes (1) 30 to 70% by weight of copper, (2) 4 to 20% by weight of tin or tin and zinc in total. %, (3) graphite 5-15% by weight, (4) at least one sulfide solid lubricant 0.3-15%
7% by weight, (5) at least one metal oxide 0.5~
10% by weight and (6) at least one hard nitride21~
It pertains to a sintered alloy friction material characterized in that it consists of 50% by weight. According to the present invention, it is possible to obtain a sintered alloy friction material that has excellent wear resistance, a high coefficient of friction, excellent operability, and whose coefficient of friction does not substantially decrease even when it rains. Each component of the sintered alloy friction material of the present invention will be explained below. Since each of these components is mutually related and affects the physical properties of the friction material, it is not necessarily appropriate to discuss the reasons for each limitation individually, but the reasons for the limitations will be shown together. (1) Copper and (2) Tin or tin and zinc These make up the base of alloy friction materials, and are alloyed by sintering to form what is called a bronze base and increase the strength of the base. Particularly from the viewpoint of strength, the content of tin or tin and zinc is 4 to 20% by weight relative to 30 to 70% by weight of copper. If tin or tin and zinc is less than 4% by weight, it will not have sufficient strength to hold graphite and other non-metals, while if it exceeds 20% by weight, it will embrittle the friction material.
Reduce strength. (3) Graphite The addition of graphite mainly stabilizes the coefficient of friction. That is, in general, the frictional force generated between two surfaces of friction materials that slide against each other is (a) the force required to shear the adhesion that occurs in a part of the two surfaces, and (b) the force required to shear the adhesion that occurs on a part of the two surfaces, and (b) the force caused by the hard particles of the opposing material. It is said that this is due to the power of digging. By existing between these two surfaces, graphite controls adhesion that occurs between the two surfaces.
Therefore, the presence of an appropriate amount of graphite improves and stabilizes the friction coefficient of the friction material, and also improves the wear resistance. If the amount of graphite is less than 5% by weight, the above effects will not be sufficiently exhibited, whereas if it exceeds 15% by weight, the material strength will decrease and the coefficient of friction will decrease. (4) At least one type of sulfide solid lubricant such as molybdenum disulfide, tungsten disulfide, manganese sulfide, etc. Molybdenum disulfide not only has the same effect as graphite, but also prevents so-called "squeal" and under high loads. It also has the remarkable effect of imparting lubricity when used. The amount of molybdenum disulfide, etc. used is
The content should be 0.3 to 7% by weight. The usage of these is 0.3
If the amount is less than 7% by weight, the effect of addition will not be sufficiently exhibited, while if it exceeds 7% by weight, the material strength and coefficient of friction will decrease. (5) At least one metal oxide such as alumina, silica, mullite, etc. Alumina, etc., has the above-mentioned excavation effect when used in the range of 0.5 to 10% by weight, and also forms on the mating sliding surface due to frictional heat. By removing the oxide film, adhesion between friction materials is stably generated and stable frictional force is exerted. If the amount used is less than 0.5% by weight, the above effects will not be fully exhibited, while if it exceeds 10% by weight, there is a tendency for the mating sliding surface to become rough. (6) At least one hard nitride such as Si 3 N 4 , AlN, BN, TiN, etc. These particularly contribute to improving the coefficient of friction. If the amount is less than 21% by weight, the coefficient of friction cannot be sufficiently improved, while if it exceeds 50% by weight, the strength of the base material decreases and the amount of wear increases. In order to manufacture a desired product, such as parts for disc brakes, using the material of the present invention, each raw material powder is blended according to a conventional method, and after press-molding it into a predetermined shape, a neutral or reducing It may be fired at a temperature of about 730 to 880° C. under pressure of about 3 to 7 kg/cm 2 in an atmosphere. Effects of the invention The friction coefficient of the sintered alloy friction material according to the invention is as follows:
Higher than conventional products (about 0.3 to 0.5), 0.5 to 0.8
reach a certain extent. Therefore, when the present invention material is used, for example, as a disc brake pad for two-wheeled and four-wheeled vehicles, (a) improved braking performance, (b) improved wear resistance of pads and discs, and (c)
Effects such as miniaturization of the brake mechanism and simplification of the (d)pad insulator are produced. Examples Hereinafter, the features of the present invention will be further clarified by Examples and Comparative Examples. Examples 1 to 6 and Comparative Examples 1 to 2 After molding 100 parts by weight of a blend consisting of each raw material and residual copper in the proportions shown in Table 1 at a pressure of 4 ton/cm 2 ,
The molded product was placed on a Cu-plated steel plate and fired at 780° C. for 60 minutes under a load of 5 kg/mm 2 in an N 2 atmosphere.

【表】 かくして得た焼成品をパツド材として慣性力
1.25Kg・m・sec2、ブレーキ初速度50Km/hr、接
触面積20cm2、面圧20Kg/cm2の条件下に相手デイス
ク材(13クローム鋼)に対し60秒間隔で300回繰
返し制動接触させた。 平均摩擦係数並びにパツド材及びデイスク材の
摩耗量を第2表に示す。
[Table] Using the thus obtained fired product as a pad material, the inertia force
1.25Kg・m・sec 2 , initial braking speed 50Km/hr, contact area 20cm 2 , surface pressure 20Kg/cm 2 , and the brake was brought into repeated contact with the mating disc material (13 chrome steel) 300 times at 60 second intervals. Ta. Table 2 shows the average coefficient of friction and the amount of wear of the pad material and disk material.

【表】【table】

【表】 第2表に示す結果から明らかな如く、本発明に
よる焼結合金摩擦材料は、高い摩擦係数を有して
おり、耐摩耗性に優れ、且つ相手材の摩耗量も少
ない。
[Table] As is clear from the results shown in Table 2, the sintered alloy friction material according to the present invention has a high coefficient of friction, excellent wear resistance, and a small amount of wear on the mating material.

Claims (1)

【特許請求の範囲】 1 (1) 銅30〜70重量%、 (2) 錫又は錫と亜鉛の合計量4〜20重量%、 (3) 黒鉛5〜15重量%、 (4) 硫化物固体潤滑剤の少なくとも1種0.3〜7
重量%、 (5) 金属酸化物の少なくとも1種0.5〜10重量%、
及び (6) 硬質窒化物の少なくとも1種21〜50重量%、 からなることを特徴とする焼結合金摩擦材料。
[Claims] 1 (1) 30 to 70% by weight of copper, (2) 4 to 20% by weight of tin or a total amount of tin and zinc, (3) 5 to 15% by weight of graphite, (4) Sulfide solids At least one lubricant 0.3-7
(5) 0.5 to 10% by weight of at least one metal oxide;
and (6) 21 to 50% by weight of at least one hard nitride. A sintered alloy friction material.
JP4706285A 1985-03-08 1985-03-08 Sintered alloy friction material Granted JPS61207549A (en)