JPH02235914A - 水性エマルシヨン樹脂組成物 - Google Patents
水性エマルシヨン樹脂組成物Info
- Publication number
- JPH02235914A JPH02235914A JP5506989A JP5506989A JPH02235914A JP H02235914 A JPH02235914 A JP H02235914A JP 5506989 A JP5506989 A JP 5506989A JP 5506989 A JP5506989 A JP 5506989A JP H02235914 A JPH02235914 A JP H02235914A
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- aqueous emulsion
- emulsion resin
- methacrylic acid
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、防錆用塗料に用いる樹脂で、耐水性、低臭気
性に優れる水性エマルション樹脂組成物に関するもので
ある。
性に優れる水性エマルション樹脂組成物に関するもので
ある。
〔従来の技術及び発明が解決しようとする課題］従来、
防錆用のアクリルエマルションとしては、スチレン、メ
タクリル酸メチル、アクリル酸ブチル等の臭気の強い単
量体を用い、残留単量体から発生する臭気が作業時の問
題点として指摘されていた。また、防錆用塗料としての
耐候性を維持するためには、アクリル酸エステル（特に
メタクリル酸メチル、アクリル酸エチル等）を多量に用
いるために、水浸漬時に塗膜が白化し、塗膜の美観を損
ない、かつ、塗膜強度が著しく低下した。本発明は、か
かる塗装作業時の臭気、水浸漬時の塗膜の白化、塗膜強
度が著しく低下することを改良したものを提供すること
を目的としている。
防錆用のアクリルエマルションとしては、スチレン、メ
タクリル酸メチル、アクリル酸ブチル等の臭気の強い単
量体を用い、残留単量体から発生する臭気が作業時の問
題点として指摘されていた。また、防錆用塗料としての
耐候性を維持するためには、アクリル酸エステル（特に
メタクリル酸メチル、アクリル酸エチル等）を多量に用
いるために、水浸漬時に塗膜が白化し、塗膜の美観を損
ない、かつ、塗膜強度が著しく低下した。本発明は、か
かる塗装作業時の臭気、水浸漬時の塗膜の白化、塗膜強
度が著しく低下することを改良したものを提供すること
を目的としている。
本発明者らは、塗装作業時の臭気、水浸漬時の塗膜の白
化及び塗膜強度の低下を解決するために鋭意研究の結果
、メタクリル酸二量体ンメチルエステルとそれと共重合
可能なビニル基を有する単量体とからなる水性エマルシ
ョン樹脂組成物が、上記課題を解決するために極めて有
効であることを見出し本発明の完成に至った。
化及び塗膜強度の低下を解決するために鋭意研究の結果
、メタクリル酸二量体ンメチルエステルとそれと共重合
可能なビニル基を有する単量体とからなる水性エマルシ
ョン樹脂組成物が、上記課題を解決するために極めて有
効であることを見出し本発明の完成に至った。
すなわち、本発明は、メタクリル酸二量体ジメチルエス
テルを２０〜６０重量部とそれと共重合可能なビニル暴
を有する単量体を４０〜８０重量部とからなる水性エマ
ルション樹脂組成物に関するものである。
テルを２０〜６０重量部とそれと共重合可能なビニル暴
を有する単量体を４０〜８０重量部とからなる水性エマ
ルション樹脂組成物に関するものである。
以下、本発明を詳細に説明する。
本発明で用いるメククリル酸二量体ジメヂルエステルと
は、次式で示されるものである。
は、次式で示されるものである。
ＣＨ．
ＣＯＯＣ｝ｌｉ ＣＯＯＣＬ
このメタクリル酸二景体ジメチルエステルは、２０〜６
０重量部の範囲で用いるのが好ましく、２０重量部未満
では、耐水性の効果が十分に発揮されず、６０重量部を
越えると重合ができなかった。
０重量部の範囲で用いるのが好ましく、２０重量部未満
では、耐水性の効果が十分に発揮されず、６０重量部を
越えると重合ができなかった。
メタクリル酸二景体ジメチルエステルと共重合が可能な
ビニル基を有する単量体としては、スチレン、ビニル１
・ルエン、α−メチルスチレン等ノスチレン系単量体、
アクリル酸メチル、アクリル酸エチル、アクリル酸ブチ
ル、アクリル酸−２−エチルヘキシル等のアクリル酸エ
ステル類、メタクリル酸メチル、メタクリル酸エチル、
メタクリル酸ブチル等のメククリル酸エステル類、アク
リル酸、メタクリル酸、フマル酸、マレイン酸、イタコ
ン酸等の不飽和カルボン酸類、アクリル酸ヒドロキシエ
チル、メククリル酸−２−ヒドロキシエチル等の側鎖に
水酸基を有する（メタ）アクリル酸エステル化合物類、
（メク）アクリロニ１−リルおよびその誘導体類、（メ
タ）アクリルアミドおよびそのＴｆ＜Ｎ体類等がある。
ビニル基を有する単量体としては、スチレン、ビニル１
・ルエン、α−メチルスチレン等ノスチレン系単量体、
アクリル酸メチル、アクリル酸エチル、アクリル酸ブチ
ル、アクリル酸−２−エチルヘキシル等のアクリル酸エ
ステル類、メタクリル酸メチル、メタクリル酸エチル、
メタクリル酸ブチル等のメククリル酸エステル類、アク
リル酸、メタクリル酸、フマル酸、マレイン酸、イタコ
ン酸等の不飽和カルボン酸類、アクリル酸ヒドロキシエ
チル、メククリル酸−２−ヒドロキシエチル等の側鎖に
水酸基を有する（メタ）アクリル酸エステル化合物類、
（メク）アクリロニ１−リルおよびその誘導体類、（メ
タ）アクリルアミドおよびそのＴｆ＜Ｎ体類等がある。
また、架橋性単量体として、エチレングリコールジメタ
クリレート、プロピレングリコールジメタクリレート、
トリメチロールプロパントリメタクリレート等の多価ア
ルコールの（メタ）アクリル酸エステル誘導体、ジビニ
ルヘンゼン等の使用も可能である。
クリレート、プロピレングリコールジメタクリレート、
トリメチロールプロパントリメタクリレート等の多価ア
ルコールの（メタ）アクリル酸エステル誘導体、ジビニ
ルヘンゼン等の使用も可能である。
メタクリル酸二量体ジメチルエステルと他の単量体を共
重合させる場合には、ガラス転移温度（Ｔｇ値）を−４
０〜６０゜Ｃの間に設定することが必要である。
重合させる場合には、ガラス転移温度（Ｔｇ値）を−４
０〜６０゜Ｃの間に設定することが必要である。
ガラス転移温度が−４０゜Ｃ未満では耐水性、塗膜強度
が低下する。また、６０’Ｃを越えると造膜性が不十分
となり、結局、耐水性に著しい低下が認められ、実用に
供し得ない。
が低下する。また、６０’Ｃを越えると造膜性が不十分
となり、結局、耐水性に著しい低下が認められ、実用に
供し得ない。
水性エマルションの重合方法は、常法のエマルション重
合法、例えば、一括仕込み法、分割添加法、連続単量体
添加法等一般的に用いられているものでよく、特に限定
しない。
合法、例えば、一括仕込み法、分割添加法、連続単量体
添加法等一般的に用いられているものでよく、特に限定
しない。
〔実施例］
以下、実施例により本発明を具体的に説明する。
実施例１
攪拌機に付けた１！の三ツ口フラスコにイオン交換水３
００ｇと、乳化剤としてドデシルベンゼンスルホン酸ナ
１・リウムを８ｇ入れ、７０゜Ｃにした。その中に重合
開始剤として過硫酸カリウム２ｇを添加し、メタクリル
酸二量体ジメチルエステル８０ｇ、アクリル酸ブチル３
Ｎ２ｇおよびメタクリル酸８ｇをイオン交換水３２０ｇ
中で予め乳化させたものを３時間連続添加し、水性エマ
ルシコン樹脂組成物を得た。
００ｇと、乳化剤としてドデシルベンゼンスルホン酸ナ
１・リウムを８ｇ入れ、７０゜Ｃにした。その中に重合
開始剤として過硫酸カリウム２ｇを添加し、メタクリル
酸二量体ジメチルエステル８０ｇ、アクリル酸ブチル３
Ｎ２ｇおよびメタクリル酸８ｇをイオン交換水３２０ｇ
中で予め乳化させたものを３時間連続添加し、水性エマ
ルシコン樹脂組成物を得た。
実施例２、３および比較例１〜５
実施例１と同様の方法で第１表の水性エマルション樹脂
組成物（比較例３、４ではメタクリル酸二量体ジメチル
エステルの変わりに、Ｔｇ値がほぼ同等で、かつ、−ｉ
的防錆用の共重合単量体として用いられるメタクリル酸
イソブチルを、比較例５ではアクリル酸ブチルの変わり
にメタクリル酸一 ４ メチルを用いた。）を調製した。
組成物（比較例３、４ではメタクリル酸二量体ジメチル
エステルの変わりに、Ｔｇ値がほぼ同等で、かつ、−ｉ
的防錆用の共重合単量体として用いられるメタクリル酸
イソブチルを、比較例５ではアクリル酸ブチルの変わり
にメタクリル酸一 ４ メチルを用いた。）を調製した。
（評価方法）
塗料化は、エマルション１００ｇにカーボンブラック（
大日精化製：ＥＰ−５１０ＩＩＲ＞１０ｇ ，プチルセ
ロソルブ２．５ｇを入れて配合した。この塗料をガラス
板上にバーコーターＮｏ．６０で塗布した。
大日精化製：ＥＰ−５１０ＩＩＲ＞１０ｇ ，プチルセ
ロソルブ２．５ｇを入れて配合した。この塗料をガラス
板上にバーコーターＮｏ．６０で塗布した。
この塗装したガラス板を２４時間常温乾燥し、市水に２
４時間浸漬した後、評価した。
４時間浸漬した後、評価した。
耐水性、臭気の評価は、４段階評価（◎一非常に良い、
○−良い、△・一やや良い、×一悪い）で行った。その
結果を第１表に示す。
○−良い、△・一やや良い、×一悪い）で行った。その
結果を第１表に示す。
（以下、余白。）
〔発明の効果〕
本発明のメタクリル酸二量体ジメチルエステルを含有す
る水性エマルション樹脂組成物は、強い耐水性と塗膜強
度の高い、さらに低臭気性の優れた性能を有するもので
、特に防錆用塗料等に脊用である。
る水性エマルション樹脂組成物は、強い耐水性と塗膜強
度の高い、さらに低臭気性の優れた性能を有するもので
、特に防錆用塗料等に脊用である。
特許出願人 三井東圧化学株式会社
Claims (1)
- １ メタクリル酸二量体ジメチルエステルを２０〜６０
重量部とそれと共重合可能なビニル基を有する単量体を
４０〜８０重量部とからなることを特徴とする水性エマ
ルション樹脂組成物。