JPH02124182A - ゴルフクラブヘツド - Google Patents
ゴルフクラブヘツドInfo
- Publication number
- JPH02124182A JPH02124182A JP63277429A JP27742988A JPH02124182A JP H02124182 A JPH02124182 A JP H02124182A JP 63277429 A JP63277429 A JP 63277429A JP 27742988 A JP27742988 A JP 27742988A JP H02124182 A JPH02124182 A JP H02124182A
- Authority
- JP
- Japan
- Prior art keywords
- club head
- whisker
- syntactic foam
- matrix resin
- golf club
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、ゴルフクラブヘッドに係わり、更に詳しく
はウッドゴルフクラブのヘッドを構成する芯体の耐破壊
強度を向上させるとともにクラブヘッド本体の耐久性を
高めたゴルフクラブヘッドに関するものである。
はウッドゴルフクラブのヘッドを構成する芯体の耐破壊
強度を向上させるとともにクラブヘッド本体の耐久性を
高めたゴルフクラブヘッドに関するものである。
従来、ウッドゴルフクラブのヘッドにおいて、特にその
芯体として、金型成形の中空芯体や、硬質ポリウレタン
フォームが使用されてきたが、これらは圧縮強度が小さ
いため、高い圧縮成形圧下で成形することが困難で、成
形後の殼部の繊維強化プラスチック(FRP)層にボイ
ドが発生し易く、品質の向上を図ることができなかった
。
芯体として、金型成形の中空芯体や、硬質ポリウレタン
フォームが使用されてきたが、これらは圧縮強度が小さ
いため、高い圧縮成形圧下で成形することが困難で、成
形後の殼部の繊維強化プラスチック(FRP)層にボイ
ドが発生し易く、品質の向上を図ることができなかった
。
そこで上記硬質ポリウレタンフォームに代えて、軽量で
圧縮強度に優れたシンタクチックフオームを芯体とする
クラブヘッドが提案されている。
圧縮強度に優れたシンタクチックフオームを芯体とする
クラブヘッドが提案されている。
然しなから、上記シンタクチックフオーム、即ち、ガラ
ス、フェノール樹脂、エポキシ樹脂などからなる微小中
空球をエポキシ樹脂、不飽和ポリエステル樹脂などの熱
硬化性樹脂中に均一に分散させ、固化させたフオームは
、高い圧縮強度を有するが、特に比重を下げて軽量化を
図る場合に衝撃破壊強度において、物性の低下がみられ
、それが打球によるクラブヘッドの割れを生じせしめる
等、クラブヘッドとしての耐久性低下の大きな原因にな
る恐れがあった。
ス、フェノール樹脂、エポキシ樹脂などからなる微小中
空球をエポキシ樹脂、不飽和ポリエステル樹脂などの熱
硬化性樹脂中に均一に分散させ、固化させたフオームは
、高い圧縮強度を有するが、特に比重を下げて軽量化を
図る場合に衝撃破壊強度において、物性の低下がみられ
、それが打球によるクラブヘッドの割れを生じせしめる
等、クラブヘッドとしての耐久性低下の大きな原因にな
る恐れがあった。
この考案は、かかる従来の問題点に着目して案出された
もので、本発明者らは、先にこのゴルフクラブヘッド用
芯体としてのシンタクチックフオームについて、特開昭
60−68873号および特開昭60−122580号
公報により、特定のエポキシ樹脂とガラス質微小中空球
とを配合した組成物からなるシンタクチックフオームを
提案したが、本発明はさらにシンタクチックフオームを
主材とする芯体の耐衝撃破壊強度を向上させ、クラブヘ
ッド本体の耐久性を高めたゴルフクラブヘッドを提供す
ることを目的とするものである。
もので、本発明者らは、先にこのゴルフクラブヘッド用
芯体としてのシンタクチックフオームについて、特開昭
60−68873号および特開昭60−122580号
公報により、特定のエポキシ樹脂とガラス質微小中空球
とを配合した組成物からなるシンタクチックフオームを
提案したが、本発明はさらにシンタクチックフオームを
主材とする芯体の耐衝撃破壊強度を向上させ、クラブヘ
ッド本体の耐久性を高めたゴルフクラブヘッドを提供す
ることを目的とするものである。
この発明は上記目的を達成するため、主として繊維強化
プラスチックからなる股部とマトリックス樹脂とガラス
質微小中空球から成るシンタクチックフオーム芯体とに
よって構成されたゴルフクラブヘッドにおいて、前記シ
ンタクチックフオーム芯体を、マトリックス樹脂とガラ
ス質微小中空球とを必須成分とする組成物に、ホイスカ
を混入して構成したことを要旨とするもので、前記ホイ
スカを、マトリックス樹脂とガラス質微小中空球、硬化
剤などを含むシンタクチックフオーム混合物に対し、3
重量パーセントから8重量パーセント混入したことを特
徴とするものである。
プラスチックからなる股部とマトリックス樹脂とガラス
質微小中空球から成るシンタクチックフオーム芯体とに
よって構成されたゴルフクラブヘッドにおいて、前記シ
ンタクチックフオーム芯体を、マトリックス樹脂とガラ
ス質微小中空球とを必須成分とする組成物に、ホイスカ
を混入して構成したことを要旨とするもので、前記ホイ
スカを、マトリックス樹脂とガラス質微小中空球、硬化
剤などを含むシンタクチックフオーム混合物に対し、3
重量パーセントから8重量パーセント混入したことを特
徴とするものである。
この発明は、上記のように構成され、マトリックス樹脂
とガラス質微小中空球とを必須成分とする組成物に、ホ
イスカを混入した芯体を構成するシンタクチックフオー
ムとすることで、芯体の耐衝撃破壊強度を向上させるこ
とが出来る一方、クラブヘッド本体の耐久性を高めるこ
とが出来、また芯体の強度向上により比重を下げること
が可能となり、これによってクラブヘッドの大きさを従
来のものより大きく設計でき、打球の際のゴルファ−の
心理的向上を図ることが出来ることを特徴としている。
とガラス質微小中空球とを必須成分とする組成物に、ホ
イスカを混入した芯体を構成するシンタクチックフオー
ムとすることで、芯体の耐衝撃破壊強度を向上させるこ
とが出来る一方、クラブヘッド本体の耐久性を高めるこ
とが出来、また芯体の強度向上により比重を下げること
が可能となり、これによってクラブヘッドの大きさを従
来のものより大きく設計でき、打球の際のゴルファ−の
心理的向上を図ることが出来ることを特徴としている。
以下添付図面に基いて、この発明の詳細な説明する。
第1図および第2図は、この発明を実施したウッドゴル
フクラブヘッドの正面図と、■−■矢視断面図を示し、
1はクラブヘッド本体、2は炭素繊維強化プラスチック
により構成された外殻、3はシンタクチックフオームか
ら成る芯体、4はソールプレートを示し、前記芯体3の
シンタクチックフオームは、マトリックス樹脂とガラス
質微小中空球とを必須成分とする組成物に、ホイスカを
混入して一体的に構成されている。
フクラブヘッドの正面図と、■−■矢視断面図を示し、
1はクラブヘッド本体、2は炭素繊維強化プラスチック
により構成された外殻、3はシンタクチックフオームか
ら成る芯体、4はソールプレートを示し、前記芯体3の
シンタクチックフオームは、マトリックス樹脂とガラス
質微小中空球とを必須成分とする組成物に、ホイスカを
混入して一体的に構成されている。
前記、マトリックス樹脂は、エポキシアクリレート系樹
脂を主成分とする反応性樹脂を用い、またホイスカとし
ては、チタン酸カリウム系ホイスカを使用している。ま
た、チタン酸カリウム系ホイスカの混入量としては、後
述する実施例から明らかなように、破壊強度、圧縮強度
及び成形作業性等の点からマトリックス樹脂とガラス質
微小中空球、硬化剤などを含むシンタクチックフオーム
混合物に対し、3重量パーセントから8重量パーセント
混入するのが好ましい。
脂を主成分とする反応性樹脂を用い、またホイスカとし
ては、チタン酸カリウム系ホイスカを使用している。ま
た、チタン酸カリウム系ホイスカの混入量としては、後
述する実施例から明らかなように、破壊強度、圧縮強度
及び成形作業性等の点からマトリックス樹脂とガラス質
微小中空球、硬化剤などを含むシンタクチックフオーム
混合物に対し、3重量パーセントから8重量パーセント
混入するのが好ましい。
なお、補強材としてのホイスカとしては、チタン酸カリ
ウム系ホイスカに限定されるものではなく、シリコンカ
ーバイト系ホイスカも用いることが出来る。
ウム系ホイスカに限定されるものではなく、シリコンカ
ーバイト系ホイスカも用いることが出来る。
また使用するホイスカは、混合・分散の向上、更にはマ
トリックス繊維とのヌレ性を改良する為に、表面処理し
たホイスカを用いることも出来、これにより、均一分散
が容易となり、また、シンタクチックフオームの芯体の
破壊強度を更に高めることが出来る。
トリックス繊維とのヌレ性を改良する為に、表面処理し
たホイスカを用いることも出来、これにより、均一分散
が容易となり、また、シンタクチックフオームの芯体の
破壊強度を更に高めることが出来る。
次に、この発明の各実施例と、比較例により、この発明
の効果について、具体的に説明する。
の効果について、具体的に説明する。
「比較例IJ
ビニルエステル樹脂(エポキシM7020:昭和高分子
)100重量パーセント(硬化剤を含む)とガラス質微
小中空球(ガラスマイクロバルーンrc15/250J
:スリーエム)を32重量部を撹拌機を用いてバルー
ンを破損しないようにしながら均一に混合し、ペースト
状の未硬化のシンタクチックフオームの組成物を得た。
)100重量パーセント(硬化剤を含む)とガラス質微
小中空球(ガラスマイクロバルーンrc15/250J
:スリーエム)を32重量部を撹拌機を用いてバルー
ンを破損しないようにしながら均一に混合し、ペースト
状の未硬化のシンタクチックフオームの組成物を得た。
それをゴルフクラブヘッド芯体成形用金型に充填し、1
30℃で30分間ギヤーオープンに入れて反応硬化させ
た。脱型後、150℃で2時間アフターキュアし、比重
0.41g/adのシンタクチックフオームの芯体を得
た。
30℃で30分間ギヤーオープンに入れて反応硬化させ
た。脱型後、150℃で2時間アフターキュアし、比重
0.41g/adのシンタクチックフオームの芯体を得
た。
芯体のパリの除去等、表面を部分修正した後、この芯体
を適量のビニルエステル樹脂をあらかじめ含浸させたカ
ーボン繊維のSMC(シート・モールディング・コンパ
ウンド)及ヒクロス状プリプレグ(繊維強化プラスチツ
ク層の構成部材)とソールプレート等とを一緒にクラブ
ヘッド圧縮成形用金型内に挿入して加圧・加熱硬化させ
てクラブヘッドを一体的に成形した。
を適量のビニルエステル樹脂をあらかじめ含浸させたカ
ーボン繊維のSMC(シート・モールディング・コンパ
ウンド)及ヒクロス状プリプレグ(繊維強化プラスチツ
ク層の構成部材)とソールプレート等とを一緒にクラブ
ヘッド圧縮成形用金型内に挿入して加圧・加熱硬化させ
てクラブヘッドを一体的に成形した。
「実施例1」
比較例1のビニルエステル樹脂とガラス質微小中空球と
の混合物に、ホイスカとしてチタン酸カリウムホイスカ
(ティスモD:大塚化学)を上記混合物に対して3重量
パーセント混入させて均一に分散させ、比較例1と同様
に加工し、0.43g/crAの芯体を得た。
の混合物に、ホイスカとしてチタン酸カリウムホイスカ
(ティスモD:大塚化学)を上記混合物に対して3重量
パーセント混入させて均一に分散させ、比較例1と同様
に加工し、0.43g/crAの芯体を得た。
「実施例2,3.4及び比較例4」
実施例1のチタン酸カリウムホイスカの混入量を、実施
例2.3及び4についてはそれぞれ5重量パーセント、
7重量パーセント及び10重量パーセント、また、比較
例4については15重量パーセントとし、実施例1と同
様に、それぞれシンタクチックフオームの芯体を得た。
例2.3及び4についてはそれぞれ5重量パーセント、
7重量パーセント及び10重量パーセント、また、比較
例4については15重量パーセントとし、実施例1と同
様に、それぞれシンタクチックフオームの芯体を得た。
「比較例2J
ビニルエステル樹脂100重量パーセントにガラス質微
小中空球を37重量パーセントを比較例工と同様に混入
し、成形・加工してシンタクチックフオームの芯体を得
た。
小中空球を37重量パーセントを比較例工と同様に混入
し、成形・加工してシンタクチックフオームの芯体を得
た。
「実施例5及び比較例5」
比較例2のビニルエステル樹脂とガラス質微小中空球と
の混合物に、ホイスカとしてチタン酸カリウムホイスカ
を上記混合物100に対して、実施例5については7重
量パーセントを、また比較例5については10重量パー
セントを、比較例2と同様にそれぞれ混入し、成形・加
工してシンタクチックフオームの芯体をそれぞれ得た。
の混合物に、ホイスカとしてチタン酸カリウムホイスカ
を上記混合物100に対して、実施例5については7重
量パーセントを、また比較例5については10重量パー
セントを、比較例2と同様にそれぞれ混入し、成形・加
工してシンタクチックフオームの芯体をそれぞれ得た。
r比較例3」
ビニルエステル樹脂100重量パーセントにガラス質微
小中空球を40重量パーセントを比較例1と同様に混入
し、成形・加工してシンタクチックフオームの芯体を得
た。
小中空球を40重量パーセントを比較例1と同様に混入
し、成形・加工してシンタクチックフオームの芯体を得
た。
「実施例6及び実施例7」
比較例3のビニルエステル樹脂とガラス質微小中空球と
の混合物にホイスカとしてチタン酸カリウムホイスカを
上記混合物100に対して実施例6については3重量パ
ーセントを、また実施例7については8重量パーセント
を、比較例3と同様にそれぞれ混入し、成形・加工して
シンタクチックフオーム芯体をそれぞれ得た。
の混合物にホイスカとしてチタン酸カリウムホイスカを
上記混合物100に対して実施例6については3重量パ
ーセントを、また実施例7については8重量パーセント
を、比較例3と同様にそれぞれ混入し、成形・加工して
シンタクチックフオーム芯体をそれぞれ得た。
以上のようにして成形したこの発明のシンタクチックフ
オームの材質の比重、圧縮強度、破壊強度及び成形作業
性、更には該シンタクチックフオームからなる芯体を有
するゴルフクラブの破壊強度を、それぞれ第1表に示し
た。
オームの材質の比重、圧縮強度、破壊強度及び成形作業
性、更には該シンタクチックフオームからなる芯体を有
するゴルフクラブの破壊強度を、それぞれ第1表に示し
た。
(以下余白)
第1表から明らかなように、成形されたシンタクチック
フオームの材質の比重、圧縮強度、破壊強度及び成形作
業性を比較検討すると、チタン酸カリウムホイスカを、
上記混合物100に対して3重量バーセントル8重量パ
ーセントを混入した時が一番良いことが判明した。
フオームの材質の比重、圧縮強度、破壊強度及び成形作
業性を比較検討すると、チタン酸カリウムホイスカを、
上記混合物100に対して3重量バーセントル8重量パ
ーセントを混入した時が一番良いことが判明した。
この発明は、上記のように芯体を構成するシンタクチッ
クフオームを、マトリックス樹脂とガラス質微小中空球
とを必須成分とする組成物に、ホイスカを混入して構成
し、特にホイスカを、マトリックス樹脂とガラス質微小
中空球、硬化剤などを含むシンタクチックフオーム混合
物に対し、3重量パーセントから8重量パーセント混入
することにより、以下のような優れた効果を奏するもの
である。
クフオームを、マトリックス樹脂とガラス質微小中空球
とを必須成分とする組成物に、ホイスカを混入して構成
し、特にホイスカを、マトリックス樹脂とガラス質微小
中空球、硬化剤などを含むシンタクチックフオーム混合
物に対し、3重量パーセントから8重量パーセント混入
することにより、以下のような優れた効果を奏するもの
である。
(a)、芯体の衝撃破壊強度を向上させて、クラブヘッ
ド本体の耐久性を高めることが出来る。
ド本体の耐久性を高めることが出来る。
(b)、クラブヘッドの芯体として強度的に下限とされ
ていたシンタクチックフオームの比重を、芯体の強度向
上により、更に下げることが可能となり、それによって
クラブヘッドの大きさを従来よりも大きく設計すること
が出来、打球の際のゴルファ−の心理的向上を図ること
が出来る。
ていたシンタクチックフオームの比重を、芯体の強度向
上により、更に下げることが可能となり、それによって
クラブヘッドの大きさを従来よりも大きく設計すること
が出来、打球の際のゴルファ−の心理的向上を図ること
が出来る。
第1図は、この発明を実施したウッドゴルフクラブヘッ
ドの正面図、第2図は第1図の■−■矢視断面図である
。 1・・・クラブヘッド本体、2・・・外殻、3・・・シ
ンタクチックフオームから成る芯体、4・・・ソールプ
レート。
ドの正面図、第2図は第1図の■−■矢視断面図である
。 1・・・クラブヘッド本体、2・・・外殻、3・・・シ
ンタクチックフオームから成る芯体、4・・・ソールプ
レート。
Claims (1)
- 【特許請求の範囲】 1、主として繊維強化プラスチックからなる殼部とマト
リックス樹脂とガラス質微小中空球から成るシンタクチ
ックフォーム芯体とによって構成されたゴルフクラブヘ
ッドにおいて、前記シンタクチックフォーム芯体を、マ
トリックス樹脂とガラス質微小中空球とを必須成分とす
る組成物に、ホイスカを混入して構成したことを特徴と
するゴルフクラブヘッド。 2、前記ホイスカを、マトリックス樹脂とガラス質微小
中空球、硬化剤などを含むシンタクチックフォーム混合
物に対し、3重量パーセントから8重量パーセント混入
したことを特徴とする請求項1に記載のゴルフクラブヘ
ッド。