JP7538046B2 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JP7538046B2 JP7538046B2 JP2020566175A JP2020566175A JP7538046B2 JP 7538046 B2 JP7538046 B2 JP 7538046B2 JP 2020566175 A JP2020566175 A JP 2020566175A JP 2020566175 A JP2020566175 A JP 2020566175A JP 7538046 B2 JP7538046 B2 JP 7538046B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- adherend
- manufactured
- polyol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
粘着剤層を有する表面保護フィルムであって、
該表面保護フィルムの該粘着剤層をガラス板に貼り合わせて温度23℃で30分間放置した後に、温度23℃で該表面保護フィルムを該ガラス板から剥離角度180度、剥離速度300mm/分で剥がした際の剥離力を剥離力Aとしたときに、剥離力Aが0.005N/25mm~0.50N/25mmであり、
該表面保護フィルムの該粘着剤層をガラス板に貼り合わせて温度100℃で2日間放置した後に、温度23℃で該表面保護フィルムを該ガラス板から剥離角度180度、剥離速度300mm/分で剥がした際の剥離力を剥離力Bとしたときに、(剥離力B/剥離力A)×100で算出される剥離力経時上昇率P1が200%以下である。
本発明の表面保護フィルムは、粘着剤層を有する。本発明の表面保護フィルムは、粘着剤層を有していれば、本発明の効果を損なわない範囲で、任意の適切な他の部材を備えていてもよい。代表的には、本発明の表面保護フィルムは、基材層と粘着剤層を有する。
(1)粘着剤層の形成材料の溶液や熱溶融液を基材層上に塗布する方法、
(2)粘着剤層の形成材料の溶液や熱溶融液をセパレーター上に塗布して形成した粘着剤層を基材層上に移着する方法、
(3)粘着剤層の形成材料を基材層上に押出して形成塗布する方法、
(4)基材層と粘着剤層を二層または多層にて押出しする方法、
(5)基材層上に粘着剤層を単層ラミネートする方法またはラミネート層とともに粘着剤層を二層ラミネートする方法、
(6)粘着剤層とフィルムやラミネート層等の基材層形成材料とを二層または多層ラミネートする方法、
などの、任意の適切な製造方法に準じて行うことができる。
基材層は、1層のみであってもよいし、2層以上であってもよい。基材層は、延伸されたものであってもよい。
粘着剤層は、粘着剤から構成され得る。粘着剤は、粘着剤組成物から形成され得る。
ベースポリマーは、好ましくは、ウレタンプレポリマー、ポリオール、アクリル系樹脂、ゴム系樹脂、シリコーン系樹脂から選ばれる少なくとも1種である。ベースポリマーが、ウレタンプレポリマー、ポリオール、アクリル系樹脂、ゴム系樹脂、シリコーン系樹脂から選ばれる少なくとも1種であれば、本発明の表面保護フィルムは、被着体からより容易に剥がれることがなく、被着体に貼り付けた後の初期の剥離力が大きくても経時における重剥離化をより十分に抑制でき、被着体に貼り付けることによる該被着体表面の汚染性がより十分に低いという効果をより発現し得る。
ウレタンプレポリマーは、好ましくは、ポリウレタンポリオールであり、より好ましくは、ポリエステルポリオール(a1)またはポリエーテルポリオール(a2)を、それぞれ単独で、もしくは、(a1)と(a2)の混合物で、触媒存在下または無触媒下で、有機ポリイソシアネ-ト化合物(a3)と反応させてなるものである。
ポリオールとしては、例えば、好ましくは、ポリエステルポリオール、ポリエーテルポリオール、ポリカプロラクトンポリオール、ポリカーボネートポリオール、ひまし油系ポリオールが挙げられる。ポリオールとしては、より好ましくは、ポリエーテルポリオールである。
アクリル系樹脂としては、本発明の効果を損なわない範囲で、例えば、特開2013-241606号公報などに記載の公知のアクリル系粘着剤など、任意の適切なアクリル系粘着剤を採用し得る。
ゴム系樹脂としては、本発明の効果を損なわない範囲で、例えば、特開2015-074771号公報などに記載の公知のゴム系粘着剤など、任意の適切なゴム系粘着剤を採用し得る。これらは、1種のみであってもよいし、2種以上であってもよい。
シリコーン系樹脂としては、本発明の効果を損なわない範囲で、例えば、特開2014-047280号公報などに記載の公知のシリコーン系粘着剤など、任意の適切なシリコーン系粘着剤を採用し得る。これらは、1種のみであってもよいし、2種以上であってもよい。
低分子量ポリオールは、1種のみであってもよいし、2種以上であってもよい。
シリコーン系添加剤は、本発明の効果を損なわない範囲で、任意の適切なシリコーン系添加剤を採用し得る。このようなシリコーン系添加剤としては、好ましくは、シロキサン結合含有化合物、水酸基含有シリコーン系化合物、架橋性官能基含有シリコーン系化合物から選ばれる少なくとも1種が挙げられ、より好ましくは、水酸基含有シリコーン系化合物である。
フッ素系添加剤は、本発明の効果を損なわない範囲で、任意の適切なフッ素系添加剤を採用し得る。このようなフッ素系添加剤としては、好ましくは、フッ素含有化合物、水酸基含有フッ素系化合物、架橋性官能基含有フッ素系化合物から選ばれる少なくとも1種が挙げられる。本発明の効果をより発現させ得る点で、水酸基含有フッ素系化合物が好ましい。
上記のベースポリマーとしてのウレタンプレポリマーおよびポリオールは、それぞれ、多官能イソシアネート化合物(B)と組み合わせて、ウレタン系樹脂を形成するための組成物の成分となり得る。ウレタン系樹脂を形成するための組成物の成分として上記のようなものを採用することにより、本発明の表面保護フィルムは、被着体から容易に剥がれることがなく、被着体に貼り付けた後の初期の剥離力が大きくても経時における重剥離化を十分に抑制でき、被着体に貼り付けることによる該被着体表面の汚染性が十分に低いという効果をより発現し得る。
ウレタンプレポリマーと多官能イソシアネート化合物(B)を含有する組成物から形成されるウレタン系樹脂は、例えば、ウレタンプレポリマーとしてのポリウレタンポリオールと多官能イソシアネート化合物(B)を含有する組成物から形成されるウレタン系樹脂が挙げられる。
ポリオールと多官能イソシアネート化合物(B)を含有する組成物から形成されるウレタン系樹脂は、具体的には、好ましくは、ポリオールと多官能イソシアネート化合物(B)を含有する組成物を硬化させて得られるウレタン系樹脂である。
粘着剤組成物は、本発明の効果を損なわない範囲で、任意の適切な他の成分を含有し得る。このような他の成分としては、例えば、他の樹脂成分、粘着付与剤、無機充填剤、有機充填剤、金属粉、顔料、箔状物、軟化剤、老化防止剤、導電剤、紫外線吸収剤、酸化防止剤、光安定剤、表面潤滑剤、レベリング剤、腐食防止剤、重合禁止剤、滑剤、溶剤、触媒などが挙げられる。
本発明の表面保護フィルムは、被着体から容易に剥がれることがなく、被着体に貼り付けた後の初期の剥離力が大きくても経時における重剥離化を十分に抑制でき、被着体に貼り付けることによる該被着体表面の汚染性が十分に低いという効果を発現し得る。このため、光学部材や電子部材の表面保護に好適に用いることができる。本発明の光学部材は、本発明の表面保護フィルムが貼着されたものである。本発明の電子部材は、本発明の表面保護フィルムが貼着されたものである。
セパレーターを剥がした表面保護フィルム(幅25mm×長さ140mm)の粘着剤層側をガラス板(ソーダライムガラス、松浪硝子工業株式会社製)に2kgハンドローラー1往復にて貼り合わせ、23℃の環境温度下で30分間放置した。
上記のようにして得られた評価用試料を、引張試験機にて測定した。引張試験機としては、島津製作所社製の商品名「オートグラフAG-Xplus HS 6000mm/min高速モデル(AG-50NX plus)」を用いた。引張試験機に評価用試料をセットし、引張試験を開始した。具体的には、上記ガラス板から表面保護フィルムを剥離した時の荷重を測定し、その際の平均荷重を表面保護フィルムのガラス板からの剥離力Aとした。引張試験の条件は、試験環境温度:23℃、剥離角度:180度、剥離速度(引張速度):300mm/分とした。
セパレーターを剥がした表面保護フィルム(幅25mm×長さ140mm)の粘着剤層側をガラス板(ソーダライムガラス、松浪硝子工業株式会社製)に2kgハンドローラー1往復にて貼り合わせ、100℃の温度環境下で2日間放置した。
上記のようにして得られた評価用試料を、引張試験機にて測定した。引張試験機としては、島津製作所社製の商品名「オートグラフAG-Xplus HS 6000mm/min高速モデル(AG-50NX plus)」を用いた。引張試験機に評価用試料をセットし、引張試験を開始した。具体的には、上記ガラス板から表面保護フィルムを剥離した時の荷重を測定し、その際の平均荷重を表面保護フィルムのガラス板からの剥離力Bとした。引張試験の条件は、試験環境温度:23℃、剥離角度:180度、剥離速度(引張速度):300mm/分とした。
セパレーターを剥がした表面保護フィルム(幅25mm×長さ140mm)の粘着剤層側をガラス板(ソーダライムガラス、松浪硝子工業株式会社製)に2kgハンドローラー1往復にて貼り合わせ、23℃の温度環境下で7日間放置した。
上記のようにして得られた評価用試料を、引張試験機にて測定した。引張試験機としては、島津製作所社製の商品名「オートグラフAG-Xplus HS 6000mm/min高速モデル(AG-50NX plus)」を用いた。引張試験機に評価用試料をセットし、引張試験を開始した。具体的には、上記ガラス板から表面保護フィルムを剥離した時の荷重を測定し、その際の平均荷重を表面保護フィルムのガラス板からの剥離力Cとした。引張試験の条件は、試験環境温度:23℃、剥離角度:180度、剥離速度(引張速度):300mm/分とした。
ガラス板(松浪硝子製、1.35mm×10cm×10cm)に、セパレーターを剥がした表面保護フィルムの粘着剤層側を2kgハンドローラー1往復にて全面に貼り合せ、温度23℃、湿度55%RHの雰囲気下で、24時間保管した後、0.3m/minの速度で表面保護フィルムを剥離し、処理済みガラス板を準備した。
続いて、上記処理済みガラス板の表面保護フィルムが剥離された面に、長さ150mmに切断した19mm幅のNo.31Bテープ(日東電工(株)製、基材厚:25μm)を、温度23℃、湿度55%RHの雰囲気下で、2kgハンドローラー1往復により貼り付けた。温度23℃、湿度55%RHの雰囲気下で、30分間養生した後、引張試験機(島津製作所社製の商品名「オートグラフAG-Xplus HS 6000mm/min高速モデル(AG-50NX plus)」)を用い、剥離角度:180度、剥離速度:300mm/minで剥離し、粘着力aを測定した。
別途、上記のような表面保護フィルムの貼り合わせと剥離の処理を行っていないガラス板(松浪硝子製、1.35mm×10cm×10cm)に対しても、上記と同様に、19mm幅のNo.31Bテープの粘着力bを測定した。
下記の式によって残留接着率を算出した。
残留接着率(%)=(粘着力a/粘着力b)×100
この残留接着率は、表面保護フィルムの粘着剤層の成分が被着体に対してどの程度被着体の表面に転写して汚染しているかの指標となる。残留接着率の値が高いほど、被着体の表面を粘着剤層の成分で汚染しにくい表面保護フィルムであり、残留接着率の値が低いほど、被着体の表面を粘着剤層の成分で汚染しやすい表面保護フィルムである。
(サンプル作製方法)
粘着剤組成物を、片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:MRF、三菱ケミカル株式会社製)の剥離処理面にファウンテンロールで乾燥後の厚みが50μmとなるよう塗布し、乾燥温度130℃、乾燥時間3分の条件でキュアーして乾燥した。このようにして、基材上に粘着剤層を作製した。次いで、粘着剤層の表面に、片面をシリコーンで剥離処理した厚み38μmのポリエステルフィルム(商品名:MRF、三菱ケミカル株式会社製)を、該フィルムの剥離処理面が粘着剤層側になるようにして被覆した。このようにして、評価用表面保護フィルムを作製した。この評価用表面保護フィルムについて、温度23℃の環境下のものを貯蔵弾性率X1、X2の測定用とし、温度80℃で7日間放置した後に温度23℃の環境下としたものを貯蔵弾性率Y1、Y2の測定用とした。
(測定方法)
得られた評価用表面保護フィルムからから粘着剤層のみを取り出し、積層して約2mmの厚みとし、これをφ7.9mmに打ち抜き、円柱状のペレットを作製して測定用サンプルとした。測定サンプルをφ7.9mmパラレルプレートの治具に固定し、動的粘弾性測定装置(レオメトリックス社製、ARES)により、貯蔵弾性率G’を算出した。測定条件は下記の通りである。なお、表中に記載の「a E+b」は、一般によく知られるように、「a×10b」を意味する。
測定:せん断モード
温度範囲:-70℃~150℃
昇温速度:5℃/min
周波数:1Hz
1L丸底セパラブルフラスコ、セパラブルカバー、分液ロート、温度計、窒素導入管、リービッヒ冷却器、バキュームシール、攪拌棒、攪拌羽が装備された重合用実験装置に、ポリプロピレングリコール(製品名「サンニックスPP-2000」、Mn=2000、三洋化成工業社製)を150g、ポリエステルポリオール(製品名「クラレポリオールP-2010」、Mn=2000、クラレ社製)を150g、溶剤としてトルエン(東ソー社製)を110g、触媒としてジラウリン酸ジブチルすず(IV)(和光純薬工業社製)を0.041g、を投入し、撹拌しながら、常温で窒素置換を1時間実施した。その後、窒素流入下、攪拌しながら、ヘキサメチレンジイソシアネート(製品名「HDI」、東ソー社製)を33.5g投入し、ウォーターバスにて実験装置内溶液温度が90±2℃となるように制御しつつ、4時間保持した後、ポリプロピレングリコール(製品名「GP1000」、Mn=1000、三洋化成工業社製)を74.9g投入し、ウォーターバスにて実験装置内溶液温度が90±2℃となるように制御しつつ、2時間保持した後、ヘキサメチレンジイソシアネート(製品名「HDI」、東ソー社製)を25.4g投入し、ウォーターバスにて実験装置内溶液温度が90±2℃となるように制御しつつ、2時間保持し、ウレタンプレポリマー溶液Aを得た。なお、重合途中に、重合中の温度制御および粘度上昇による撹拌性低下防止のために、適宜トルエンを滴下した。滴下したトルエンの総量は320gであった。ウレタンプレポリマー溶液Aの固形分濃度は50重量%であった。
表1に示すように、得られたウレタンプレポリマー溶液Aをポリマー固形分換算で100重量部と、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)を固形分換算で20.0重量部と、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を固形分換算で4.0重量部と、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を固形分換算で3.0重量部と、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を固形分換算で0.05重量部を加えて、全体の固形分が45重量%となるように酢酸エチルで希釈し、粘着剤組成物(1)を得た。得られた粘着剤組成物(1)を、ポリエステル樹脂からなる基材(商品名「T100-75S」、厚み75μm、三菱ケミカル株式会社製)に乾燥後の厚みが75μmとなるよう塗布し、乾燥温度130℃、乾燥時間3分の条件でキュアーして乾燥した。このようにして、基材上に、粘着剤組成物(1)からなる粘着剤層を作製した。次いで、得られた粘着剤層の表面に、一方の面にシリコーン処理を施した厚さ25μmのポリエステル樹脂からなる剥離シート(商品名「MRF25」、厚み25μm、三菱ケミカル株式会社製)のシリコーン処理面を貼合せて、表面保護フィルム(1)を得た。得られた表面保護フィルム(1)は、常温で7日間エージングを行い、評価を行った。剥離シートは評価の直前に剥離した。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で6.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(2)からなる粘着剤層を作製し、表面保護フィルム(2)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で8.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(3)からなる粘着剤層を作製し、表面保護フィルム(3)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で10.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(4)からなる粘着剤層を作製し、表面保護フィルム(4)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で15.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(5)からなる粘着剤層を作製し、表面保護フィルム(5)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で2.0重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(6)からなる粘着剤層を作製し、表面保護フィルム(6)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(7)からなる粘着剤層を作製し、表面保護フィルム(7)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で8.0重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(8)からなる粘着剤層を作製し、表面保護フィルム(8)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で10.0重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(9)からなる粘着剤層を作製し、表面保護フィルム(9)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で15.0重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(10)からなる粘着剤層を作製し、表面保護フィルム(10)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用いた以外は、実施例1と同様に行い、粘着剤組成物(11)からなる粘着剤層を作製し、表面保護フィルム(11)を得た。結果を表2に示した。
表1に示すように、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用いた以外は、実施例1と同様に行い、粘着剤組成物(12)からなる粘着剤層を作製し、表面保護フィルム(12)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で18.8重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で2.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない以外は、実施例1と同様に行い、粘着剤組成物(13)からなる粘着剤層を作製し、表面保護フィルム(13)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で26.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で3.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない以外は、実施例1と同様に行い、粘着剤組成物(14)からなる粘着剤層を作製し、表面保護フィルム(14)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で33.2重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で4.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない以外は、実施例1と同様に行い、粘着剤組成物(15)からなる粘着剤層を作製し、表面保護フィルム(15)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で40.8重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で5.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない以外は、実施例1と同様に行い、粘着剤組成物(16)からなる粘着剤層を作製し、表面保護フィルム(16)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で18.8重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で2.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)の使用量を固形分換算で0.075重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(17)からなる粘着剤層を作製し、表面保護フィルム(17)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で26.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で3.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)の使用量を固形分換算で0.075重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(18)からなる粘着剤層を作製し、表面保護フィルム(18)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で33.2重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で4.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)の使用量を固形分換算で0.075重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(19)からなる粘着剤層を作製し、表面保護フィルム(19)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で40.6重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で4.0重量部として用い、耐熱安定剤(商品名「TINUVIN765」、BASF製)を固形分換算で4.0重量部を追加で用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)を用いない代わりに、トリメチロールプロパン(商品名「TMP」、Mn=134、三菱ガス化学株式会社製)を固形分換算で5.0重量部として用い、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)の使用量を固形分換算で0.075重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(20)からなる粘着剤層を作製し、表面保護フィルム(20)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で16.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)を用いない代わりに、耐熱安定剤(商品名「イルガノックス1135」、BASF製)を固形分換算で8.0重量部として用い、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で1.5重量部に変更し、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない代わりに、水酸基含有シリコーン(商品名「X-22-4015」、信越化学工業株式会社製)を固形分換算で0.05重量部として用い、実施例1と同様に行い、粘着剤組成物(21)からなる粘着剤層を作製し、表面保護フィルム(21)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で6.5重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で1.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(C1)からなる粘着剤層を作製し、表面保護フィルム(C1)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で13.2重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で3.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(C2)からなる粘着剤層を作製し、表面保護フィルム(C2)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で20.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で5.0重量部に変更した以外は、実施例1と同様に行い、粘着剤組成物(C3)からなる粘着剤層を作製し、表面保護フィルム(C3)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で6.5重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で1.0重量部に変更し、脂肪酸エステル(商品名「サラコス816」、日清オイリオ株式会社製)を固形分換算で1.0重量部を追加した以外は、実施例1と同様に行い、粘着剤組成物(C4)からなる粘着剤層を作製し、表面保護フィルム(C4)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で13.2重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で3.0重量部に変更し、脂肪酸エステル(商品名「サラコス816」、日清オイリオ株式会社製)を固形分換算で1.0重量部を追加した以外は、実施例1と同様に行い、粘着剤組成物(C5)からなる粘着剤層を作製し、表面保護フィルム(C5)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で20.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で5.0重量部に変更し、脂肪酸エステル(商品名「サラコス816」、日清オイリオ株式会社製)を固形分換算で1.0重量部を追加した以外は、実施例1と同様に行い、粘着剤組成物(C6)からなる粘着剤層を作製し、表面保護フィルム(C6)を得た。結果を表2に示した。
表1に示すように、イソシアネート系架橋剤(商品名「コロネートHL」、日本ポリウレタン株式会社製)の使用量を固形分換算で16.0重量部に変更し、耐熱安定剤(商品名「イルガノックス1010」、BASF製)の使用量を固形分換算で0.5重量部に変更し、ポリオール(商品名「サンニックスGP250」、Mn=250、三洋化成工業株式会社製)の使用量を固形分換算で1.5重量部に変更し、フッ素含有ポリマー(商品名「F-571」、DIC株式会社製)を用いない代わりに、水酸基含有シリコーン(商品名「X-22-4015」、信越化学工業株式会社製)を固形分換算で0.05重量部として用いた以外は、実施例1と同様に行い、粘着剤組成物(C7)からなる粘着剤層を作製し、表面保護フィルム(C7)を得た。結果を表2に示した。
実施例1~21で得られた表面保護フィルム(1)~(21)のそれぞれについて、セパレーターを剥離し、粘着剤層側を、光学部材である偏光板(日東電工株式会社製、商品名「TEG1465DUHC」)に貼着し、表面保護フィルムが貼着された光学部材を得た。
実施例1~21で得られた表面保護フィルム(1)~(21)のそれぞれについて、セパレーターを剥離し、粘着剤層側を、電子部材である導電性フィルム(日東電工株式会社製、商品名「エレクリスタV270L-TFMP」)に貼着し、表面保護フィルムが貼着された電子部材を得た。
2 粘着剤層
10 表面保護フィルム
Claims (9)
- 粘着剤層を有する表面保護フィルムであって、
該粘着剤層を構成する粘着剤が粘着剤組成物から形成され、該粘着剤組成物が、ベースポリマーとしてのウレタンプレポリマーと、多官能イソシアネート化合物と、数平均分子量Mnが50~1500である低分子量ポリオールと、耐熱安定剤を含み、
該耐熱安定剤は、ヒンダードフェノール構造を有する酸化防止剤、ヒンダードフェノール構造を有する光安定剤、ヒンダードフェノール構造を有する熱安定剤、ヒンダードフェノール構造を有する紫外線吸収剤からなる群から選択される少なくとも1種であり、
該ベースポリマーとしてのウレタンプレポリマー100重量部に対して、該耐熱安定剤の含有割合が1.5重量部~30重量部であり、
該表面保護フィルムの該粘着剤層をガラス板に貼り合わせて温度23℃で30分間放置した後に、温度23℃で該表面保護フィルムを該ガラス板から剥離角度180度、剥離速度300mm/分で剥がした際の剥離力を剥離力Aとしたときに、剥離力Aが0.005N/25mm~0.50N/25mmであり、
該表面保護フィルムの該粘着剤層をガラス板に貼り合わせて温度100℃で2日間放置した後に、温度23℃で該表面保護フィルムを該ガラス板から剥離角度180度、剥離速度300mm/分で剥がした際の剥離力を剥離力Bとしたときに、(剥離力B/剥離力A)×100で算出される剥離力経時上昇率P1が200%以下である、
表面保護フィルム。 - 前記粘着剤層の23℃における貯蔵弾性率を貯蔵弾性率X1とし、前記表面保護フィルムを温度80℃で7日間放置した後の温度23℃における貯蔵弾性率を貯蔵弾性率Y1としたときに、(貯蔵弾性率Y1/貯蔵弾性率X1)×100で算出される貯蔵弾性率変化率Q1が150%以下である、請求項1に記載の表面保護フィルム。
- 前記表面保護フィルムの前記粘着剤層をガラス板に貼り合わせて温度23℃で7日間放置した後に、温度23℃で該表面保護フィルムを該ガラス板から剥離角度180度、剥離速度300mm/分で剥がした際の剥離力を剥離力Cとしたときに、(剥離力C/剥離力A)×100で算出される剥離力経時上昇率P2が160%以下である、請求項1または2に記載の表面保護フィルム。
- 23℃におけるガラス板に対する残留接着率が50%以上である、請求項1から3までのいずれかに記載の表面保護フィルム。
- 前記粘着剤組成物が、シリコーン系添加剤および/またはフッ素系添加剤を含む、請求項1から4までのいずれかに記載の表面保護フィルム。
- 前記シリコーン系添加剤が、シロキサン結合含有化合物、水酸基含有シリコーン系化合物、架橋性官能基含有シリコーン系化合物から選ばれる少なくとも1種である、請求項5に記載の表面保護フィルム。
- 前記フッ素系添加剤が、フッ素含有化合物、水酸基含有フッ素系化合物、架橋性官能基含有フッ素系化合物から選ばれる少なくとも1種である、請求項5に記載の表面保護フィルム。
- 請求項1から7までのいずれかに記載の表面保護フィルムが貼着された光学部材。
- 請求項1から7までのいずれかに記載の表面保護フィルムが貼着された電子部材。