JP7465658B2 - 口腔用組成物 - Google Patents
口腔用組成物 Download PDFInfo
- Publication number
- JP7465658B2 JP7465658B2 JP2019239657A JP2019239657A JP7465658B2 JP 7465658 B2 JP7465658 B2 JP 7465658B2 JP 2019239657 A JP2019239657 A JP 2019239657A JP 2019239657 A JP2019239657 A JP 2019239657A JP 7465658 B2 JP7465658 B2 JP 7465658B2
- Authority
- JP
- Japan
- Prior art keywords
- particles
- hydroxyapatite
- hydroxyapatite particles
- oral composition
- diffraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
項1.
ヒドロキシアパタイト粒子、
硝酸カリウム、
ポリオキシエチレン硬化ヒマシ油、並びに、
キサンタンガム及びアルギン酸若しくはその塩からなる群より選択される少なくとも1種、
を含有し、
前記ヒドロキシアパタイト粒子が、CuKα特性X線により測定される粉末X線回折パターンにおける2θ=26°付近の回折ピーク強度に対する2θ=32°付近の回折ピーク強度の比が0.8~1.6である、
口腔用組成物。
項2.
前記ヒドロキシアパタイト粒子のCa/Pモル比が1.67未満である、項1に記載の口腔用組成物。
項3.
前記ヒドロキシアパタイト粒子のメジアン径が5μm以下である、項1又は2に記載の口腔用組成物。
項4.
前記ヒドロキシアパタイト粒子の比表面積が30~200m2/gである、項1~3のいずれかに記載の口腔用組成物。
項5.
前記ヒドロキシアパタイト粒子が、CuKα特性X線により測定される粉末X線回折パターンにおける2θ=32°付近の回折ピーク強度に対する2θ=34°付近の回折ピーク強度の比が1以下である、項1~4のいずれかに記載の口腔用組成物。
項6.
前記ヒドロキシアパタイト粒子が、ヒドロキシアパタイト板状結晶の凝集体である、
項1~5のいずれかに記載の口腔用組成物。
項7.
さらに、乳酸アルミニウムを含有する、項1~6のいずれかに記載の口腔用組成物。
項8.
知覚過敏予防又は改善用である、項1~7のいずれかに記載の口腔用組成物。
測定条件1
ターゲット:Cu、管電圧40kV、管電流:30mA、サンプリング幅:0.02°、スキャンスピード:2.00°/min、発散スリット:1.0°、散乱スリット:1.0°、受光スリット:0.3mm。
測定条件2
ターゲット:Cu、管電圧40kV、管電流:15mA、サンプリング幅:0.02°、スキャンスピード:2.00°/min、発散スリット:1.25°、散乱スリット:1.25°、受光スリット:0.3mm。
シュウ酸反応性:5質量%の濃度に調製され、25±1℃に保たれた水酸化カルシウムスラリー50gに、25±1℃に保たれた0.5モル/リットルの濃度のシュウ酸水溶液40gを一気に添加し、添加後pH7.0になるまでの時間(分)。
・以下の表1に記載の歯磨剤(表中の配合量の単位「%」は質量%を示す。また、表中のヒドロキシアパタイトは、本開示の粒子を示す。)
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積:6.7m2/g シュウ酸反応性:15分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温し撹拌停止まで維持した。10%NaOH水溶液を添加してpHを5.5に調整した。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト粒子(粉末)を得た。
キャンスピード:2.00°/min、発散スリット:1.0°、散乱スリット:1.0°、受光スリット:0.3mm。結果を図1に示す。また、市販される試薬品であるヒドロキシアパタイト(試薬HAp)のX線回折パターンを図2に示す。2θ=26°付近の(002)面による回折ピーク強度比に対する、2θ=32°付近の(211)面による回折ピーク強度の比が1.1であり、試薬HApの同ピーク強度比2.7に比べ明確に低い結果となった。これより、得られたヒドロキシアパタイト粒子は、c面が比較的多く露出している板状結晶の凝集体であることが分かった。また、25°≦2θ≦35°の範囲内の全ての回折ピークの面積の総和100%に対して、25.5°≦2θ≦26.5°の範囲内の全ての回折ピークの面積と31.5°≦2θ≦32.5°の範囲内の全ての回折ピークの面積との総和は、37.2%であった。これは試薬HApが示した52.1%よりも明確に低い値を示しており、またX線回折パターンが比較的ブロードであることからも結晶性が低いことが示される。また、2θ=40°付近の(130)面による回折ピークから算出した結晶子サイズは7nmであり、試薬HApが示す52nmに比べて明確に小さく、この点からも結晶性が低いことが示される。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積:7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温し撹拌停止まで維持した。10%NaOH水溶液を添加してpHを6.0に調整した。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト粒子(粉体)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら40℃に加温し撹拌停止まで維持した。10%NaOH水溶液を添加してpHを5.5に調整した。そこに水酸化カルシウムスラリーを50分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト粒子(粉体)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム無水物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム無水物水溶液をステンレスビーカーに入れ、撹拌しながら80℃に加温した。pHは4.2のまま調整しなかった。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト粒子(粉体)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム無水物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム無水物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温した。pHは4.2のまま調整しなかった。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト微粒子(粉末)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム無水物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム無水物水溶液をステンレスビーカーに入れ、撹拌しながら80℃に加温した。pHは4.2のまま調整しなかった。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト微粒子(粉末)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積:6.7m2/g シュウ酸反応性:15分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温し撹拌停止まで維持した。10%NaOH水溶液を添加してpHを5.5に調整した。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させた後に40℃、75%RHの条件で6か月静置し、ヒドロキシアパタイト微粒子(粉末)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム無水物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。水酸化カルシウムスラリーをステンレスビーカーに入れ、撹拌しながら40℃に加温した。そこにリン酸二水素ナトリウム無水物水溶液(pH:4.2)を30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト得られたヒドロキシアパタイト粒子(粉体)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温し撹拌停止まで維持した。pHは4.2のまま調整しなかった。そこに水酸化カルシウムスラリーを45分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ試料を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%高純度水酸化カルシウムスラリー(BET比表面積:2.4m2/g、シュウ酸反応性:25秒 特開第2011-126772号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら60℃に加温し撹拌停止まで維持した。10%NaOH水溶液を添加してpHを5.5に調整した。そこに水酸化カルシウムスラリーを30分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ、試料を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(BET比表面積7.9m2/g シュウ酸反応性:12分30秒 特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、10%NaOH水溶液を添加してpHを5.5に調整した。そこに水酸化カルシウムスラリーを50分かけて添加した。添加終了後、更に1時間撹拌したあとに撹拌を停止し、9日間常温で静置後、ろ過、水洗、及び80℃にて乾燥させ、ヒドロキシアパタイト粒子(粉体)を得た。
Ca/Pモル比が0.5になるように、10.7質量%リン酸二水素ナトリウム・2水和物水溶液及び、固形分濃度8.6質量%磨砕処理水酸化カルシウムスラリー(特開第2017-036176号公報)を調製した。リン酸二水素ナトリウム・2水和物水溶液をステンレスビーカーに入れ、撹拌しながら80℃に加温し撹拌停止まで維持した。pHは4.2のまま調整しなかった。そこに水酸化カルシウムスラリーを50分かけて添加した。添加終了後、更に1時間撹拌したあとに、ろ過、水洗、及び80℃にて乾燥させ試料を得た。
[試験目的]
ヒドロキシアパタイト粒子の口腔内での反応性を評価するべく、人工唾液浸漬前後の結晶性の変化を粉末X線回折装置により測定した。
実施例1と同様にして得られたヒドロキシアパタイト粒子0.5gを人工唾液(CaCl2:1.5mM,KH2PO4:0.9mM,KCl:130mM,HEPES:20mM,pH7.0(KOH))200mLに7日間浸漬させた。吸引ろ過によりろ別した粉体を粉末X線回折装置により測定し、人工唾液浸漬前後での結晶性の変化を観測した。
・使用機種:Miniflex II (株式会社リガク)
・開始角度:20°
・終了角度:40°
・サンプリング幅:0.02°
・スキャンスピード:4.0°/min
・ターゲット:Cu、
・管電圧:30kV
・管電流:15mA
・発散スリット:1.25°
・散乱スリット:8.0mm
・受光スリット:0.3mm。
[試験目的]
ヒドロキシアパタイト粒子の象牙細管を封鎖する能力を評価するべく、ウシ象牙質表面をヒドロキシアパタイト粒子液でブラッシングし、象牙細管の封鎖度合いを電子顕微鏡(SEM)観察で調べた。
象牙質ブロック(サンプル)の作成
1. ウシ抜去歯根面部の象牙質を5×5mmのサイズに切り出した。
2. 切り出した歯片をレジン樹脂(ポリメチルメタクリレート)に埋没、ブロックを作成し、耐水研磨紙を用いて研磨し、表面出しを行った。
3. 当該象牙質ブロックを5%w/w EDTA水溶液(pH7.0)に2分間浸漬させた。
4. 蒸留水中で5分間超音波処理を行った。
5. 実施例1と同様にして得られたヒドロキシアパタイト粒子0.3gを粘性希釈液39.7gに懸濁させ、ヒドロキシアパタイト粒子を液得た。なお、当該粘性希釈液は、0.5w/w% カルボキシメチルセルロースナトリウム、10w/w% グリセリンを含む水溶液である。
6. ヒドロキシアパタイト粒子液(40g)中で、象牙質ブロックを30秒間歯ブラシ(GUM #211)でブラッシングした(ストローク:150rpm、荷重:160g)。
7. 象牙質ブロックを水洗したのち、人工唾液(CaCl2:1.5mM,KH2PO4:0.9mM,KCl:130mM,HEPES:20mM,pH7.0(KOH))に5分間浸漬させた。
8. 上記操作1と2を6回繰り返した。
9. 表面を蒸着処理した後、電子顕微鏡にて観察した。
{蒸着処理}
・使用機種:MCI1000(株式会社日立ハイテクノロジーズ)
・電流:20mA
・処理時間:120秒
{SEM観察}
・使用機種:S-3400N(株式会社日立ハイテクノロジーズ)
・検出器:SE(二次電子像)
・印加電圧:5kV
・プローブ電流:50mA
・倍率:25000倍。
[試験目的]
ヒドロキシアパタイト粒子の象牙細管内で固着する能力を評価するべく、ウシ象牙質表面をヒドロキシアパタイト粒子溶液でブラッシングした後、象牙質裏面から水圧をかけ、その水圧にヒドロキシアパタイト粒子の封鎖が耐えたかどうかを電子顕微鏡(SEM)観察で調べた。
象牙質ディスク(サンプル)の作成
1. ウシ抜去歯根面部の象牙質を5×5mmのサイズに切り出した。
2. 切り出した歯片を耐水研磨紙で研磨した。
3. 得られた象牙質ディスクを5%w/w EDTA水溶液(pH7.0)に2分間浸漬させた。
4. 蒸留水中で5分間超音波処理を行った。
5. 実施例1と同様にして得られたヒドロキシアパタイト粒子1gを粘性希釈液39gに懸濁させ、ヒドロキシアパタイト粒子液を得た。なお、当該粘性希釈液は、0.5w/w% カルボキシメチルセルロースナトリウム、10w/w% グリセリンを含む水溶液である。
6. ヒドロキシアパタイト粒子液(40g)中で、象牙質ディスクを30秒間歯ブラシ(GUM #211)でブラッシングした(ストローク:150rpm、荷重:160g)。
7. ディスクを水洗したのち、人工唾液(CaCl2:1.5mM,KH2PO4:0.9mM,KCl:130mM,HEPES:20mM,pH7.0(KOH))に5分間浸漬させた。
8. 上記操作1と2を6回繰り返した。
9. 人工唾液に7日間浸漬させた。
10. ブラッシング処理後の象牙質ディスクを、pashleyらの報告(Pashley DH, Galloway SE. The effects of oxalate treatment on the smear layer of ground surfaces of human dentin. Arch Oral Biol 1983; 30: 731-737.)を参考にした装置を用いて0.1MPaで30分加圧した。
11. 表面を蒸着処理した後、電子顕微鏡にて観察した。
{蒸着処理}
・使用機種:MCI1000(株式会社日立ハイテクノロジーズ)
・電流:20mA
・処理時間:120秒
{SEM観察}
・使用機種:S-3400N(株式会社日立ハイテクノロジーズ)
・検出器:SE(二次電子像)
・印加電圧:5kV
・プローブ電流:50mA
・倍率:25000倍。
[試験目的]
素材配合のハミガキ製剤の象牙細管を封鎖する能力を確認するべく、ウシ象牙質表面を素材溶液でブラッシングし、象牙細管の封鎖度合いを電子顕微鏡(SEM)で調べた。
[試験方法]
象牙質ブロック(サンプル)の作成
1. ウシ抜去歯根面部の象牙質を5×5 mmのサイズに切り出した。
2. 切り出した歯片をレジン樹脂(ポリメチルメタクリレート)に埋没、ブロックを作成し、耐水研磨紙を用いて研磨し、表面出しを行った。
3. 当該象牙質ブロックを5w/w% EDTA 水溶液(pH 7.0)に2分間浸漬させた。
4. 蒸留水中で5分間超音波処理を行った。
5. 実施例1と同様にして得られたヒドロキシアパタイト粒子を3w/w%配合した歯磨剤10 gを常法により調製した。当該歯磨剤の組成を次の表に示す。なお、以下、表中の配合量の単位「%」は質量%を示す。
6. 当該歯磨剤10gを蒸留水で4倍希釈し、歯磨剤溶液を得た。当該歯磨剤溶液(40 g)中で、象牙質ブロックを30秒間歯ブラシ(GUM #211)でブラッシングした (ストローク:150rpm、荷重:160g)。
7. 象牙質ブロックを水洗したのち、人工唾液(CaCl2: 1.5mM, KH2PO4:0.9mM, KCl: 130mM, HEPES: 20mM, pH 7.0(KOH))に5分間浸漬させた。
8. 上記操作1と2を6回繰り返した。
9. 表面を蒸着処理した後、電子顕微鏡にて観察した。
[観察測定条件]
{蒸着処理}
・使用機種: MCI1000 (株式会社日立ハイテクノロジーズ)
・電流: 20mA
・処理時間: 120秒
{SEM観察}
・使用機種: S-3400N (株式会社日立ハイテクノロジーズ)
・検出器:SE (二次電子像)
・印加電圧:5 kV
・プローブ電流 50mA
・倍率: 25000倍
[試験目的]
ヒドロキシアパタイト粒子配合のゲル製剤の象牙細管を封鎖する能力を確認するべく、ウシ象牙質表面にソフトピック(ゴム製の歯間ブラシ)を用いてゲル製剤を塗布し、象牙細管の封鎖度合いを電子顕微鏡(SEM)で調べた。
[試験方法]
象牙質ブロック(サンプル)の作成
1. ウシ抜去歯根面部の象牙質を5×5 mmのサイズに切り出した。
2. 切り出した歯片をレジン樹脂(ポリメチルメタクリレート)に埋没、ブロックを作成し、耐水研磨紙を用いて研磨し、表面出しを行った。
3. 当該象牙質ブロックを5w/w% EDTA 水溶液(pH 7.0)に2分間浸漬させた。
4. 蒸留水中で5分間超音波処理を行った。
5. 当該象牙質ブロック2つを、象牙質表面が間隔1.1 mmで向かい合うようにテープで固定し、疑似的歯間空隙とした。
6. ソフトピック(ガム・ソフトピック カーブ型:サンスター株式会社)のブラシ部分に、実施例1と同様にして得られたヒドロキシアパタイト粒子を含有する(あるいは含有しない)ゲル製剤を載せ、空隙に挿入して5往復させた。なお、当該ゲル製剤の組成を次の表に示す。
7. 象牙質ブロックを水洗した。
8. 表面を蒸着処理した後、電子顕微鏡にて観察した。
[観察測定条件]
{蒸着処理}
・使用機種: MCI1000 (株式会社日立ハイテクノロジーズ)
・電流: 20mA
・処理時間: 120秒
{SEM観察}
・使用機種: S-3400N (株式会社日立ハイテクノロジーズ)
・検出器:SE (二次電子像)
・印加電圧:5 kV
・プローブ電流 50mA
・倍率: 25000倍
[試験目的]
ヒドロキシアパタイト粒子配合のゲル製剤の抗知覚過敏に関する臨床効果を検討した。なお、当該検討において、ヒドロキシアパタイト粒子として実施例1と同様にして得られたヒドロキシアパタイト粒子を用いた。
[試験デザイン]
(i)ヒドロキシアパタイト粒子、乳酸アルミニウム、及び硝酸カリウムを含有するゲル製剤(HAp+Al+K)、(ii)乳酸アルミニウム及び硝酸カリウムを含有するゲル製剤(Al+K)、並びに(iii)硝酸カリウムを含有するゲル製剤(K)、の3製剤での比較を行った。これらのゲル製剤の組成を次の表に示す。
被験者にジェル製剤(試験品)を1日2回(朝・晩)(起床後や食事後、就寝前等の規定はせず、各自の口腔清掃習慣に合わせることとする。)使用させた。具体的には、まず、指定のハブラシ(ガム・プロズデンタルブラシ#3C:サンスター株式会社)と歯磨剤(コープ ノンフォームハミガキ N)でブラッシング後、約10 mlの水で20秒間洗口させ(ブラッシング時間の規定はしない。)、その後にジェル製剤を使用させた。ジェル製剤の使用は、具体的には、被験歯1歯に対し、ジェル製剤(試験品)約0.04 g(米粒大くらい)をタフトブラシ(バトラーシングルタフトブラシ#01F:サンスター株式会社)で被験部位に塗布し、被験部位とその両隣接歯を1歯につき5秒以上ブラッシングさせた。被験部位と両隣接歯との歯間に指定の歯間清掃具(ガム・ソフトピック カーブ型:サンスター株式会社)を挿入可能な場合は、当該歯間清掃具を被験部位と両隣接歯との歯間部に頬側から挿入し、5回往復させた。ジェル製剤(試験品)の使用後、約10 mlの水で20秒間洗口させた。
実施例1と同様にして得られたヒドロキシアパタイト粒子(実施例1手順製造HAp)又は市販ヒドロキシアパタイト粒子(市販HAp(富田製薬(株)製);上記試薬HApとは別の市販ヒドロキシアパタイト)、並びに各種界面活性剤及び各種粘結剤を用いて、口腔用組成物を調製した。具体的には、表7に示す各成分を混合して各口腔用組成物を調製した。なお、表7に示す各成分の数値は質量%を示す。また、実施例1手順製造HAp及び市販HApについて、上記実施例1と同様にしてX線結晶回折を行ったところ、2θ=26°付近の(002)面による回折ピーク強度比に対する、2θ=32°付近の(211)面による回折ピーク強度の比が、実施例1手順製造HApは1.44、市販HApでは2.72であった。また、用いたポリオキシエチレン硬化ヒマシ油の酸化エチレンの平均付加モル数は60である。
得られた各口腔用組成物を満注量83.5mL、胴径45.5mmの無色透明なガラス容器(柏洋硝子製)に60mL以上充填し、ペースト表面が平坦になるようにならした。プランジャーがペースト表面に接触してから8mm押し下げた後、1000mm/分のスピードで引き上げた時の糸を引いた高さ(mm)を曳糸性評価として以下の基準で評価した。なお、曳糸性が高すぎると、使用時に組成物の切れが悪くなるため、好ましくない。
〇:<10mm、△:10~20mm、×:≧20mm
得られた各口腔用組成物につき、3倍質量の水を加えて4倍希釈水スラリーを調製し、全長9.5cm、口径1.5cmのプラスチック製丸底チューブに5mLを測り取った。当該チューブに蓋をした後、上下に10往復浸透し、室温にて3分間静置した後の泡の高さを測定し、以下の基準で評価した。
〇:≧5mm、△:2mm~5mm、×:<2mm
得られた各口腔用組成物5gと蒸留水15gを口径4.5cmのガラスビーカーに秤取し、直径0.6cm、長さ3.0cmの攪拌子を用いて500rpmの速度で攪拌した。5分間の攪拌の後、分散できていない口腔用組成物の沈殿の有無を目視にて確認した。
〇:沈殿は確認できない ×:沈殿が確認できる
Claims (8)
- ヒドロキシアパタイト粒子、
硝酸カリウム、
ポリオキシエチレン硬化ヒマシ油、並びに、
アルギン酸若しくはその塩、
を含有し、
前記ヒドロキシアパタイト粒子が、CuKα特性X線により測定される粉末X線回折パターンにおける2θ=26°付近の回折ピーク強度に対する2θ=32°付近の回折ピーク強度の比が0.8~1.6である、
口腔用組成物。 - 前記ヒドロキシアパタイト粒子のCa/Pモル比が1.67未満である、請求項1に記載の口腔用組成物。
- 前記ヒドロキシアパタイト粒子のメジアン径が5μm以下である、請求項1又は2に記載の口腔用組成物。
- 前記ヒドロキシアパタイト粒子の比表面積が30~200m2/gである、請求項1~3のいずれかに記載の口腔用組成物。
- 前記ヒドロキシアパタイト粒子が、CuKα特性X線により測定される粉末X線回折パターンにおける2θ=32°付近の回折ピーク強度に対する2θ=34°付近の回折ピーク強度の比が1以下である、請求項1~4のいずれかに記載の口腔用組成物。
- 前記ヒドロキシアパタイト粒子が、ヒドロキシアパタイト板状結晶の凝集体である、
請求項1~5のいずれかに記載の口腔用組成物。 - さらに、乳酸アルミニウムを含有する、請求項1~6のいずれかに記載の口腔用組成物。
- 知覚過敏予防又は改善用である、請求項1~7のいずれかに記載の口腔用組成物。