JP7456091B2 - A low-solvent odor, easy-to-open gas barrier laminate using a solvent-free adhesive, and a low-solvent odor gas barrier packaging material and packaging bag made of the laminate. - Google Patents
A low-solvent odor, easy-to-open gas barrier laminate using a solvent-free adhesive, and a low-solvent odor gas barrier packaging material and packaging bag made of the laminate. Download PDFInfo
- Publication number
- JP7456091B2 JP7456091B2 JP2019055902A JP2019055902A JP7456091B2 JP 7456091 B2 JP7456091 B2 JP 7456091B2 JP 2019055902 A JP2019055902 A JP 2019055902A JP 2019055902 A JP2019055902 A JP 2019055902A JP 7456091 B2 JP7456091 B2 JP 7456091B2
- Authority
- JP
- Japan
- Prior art keywords
- gas barrier
- layer
- low
- solvent
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、易開封性と、ガスバリア性と、耐屈曲性と、低溶剤臭性に優れた積層体、及び該積層体からなる包装材料、該包装材料を用いた包装袋、特にピロー包装袋に関するものである。
また、本発明の包装材料は、各種包装用袋やレトルト用袋に最適である。
The present invention relates to a laminate with excellent ease of opening, gas barrier properties, bending resistance, and low solvent odor, a packaging material made of the laminate, and a packaging bag using the packaging material, particularly a pillow packaging bag. It is related to.
Furthermore, the packaging material of the present invention is most suitable for various packaging bags and retort bags.
一般に、ガスバリア性を有する包装材料は、少なくとも、基材層、ガスバリア層、接着剤層、及びシーラント層を有する積層体からなり、特に、酸素バリア性を向上させるためのガスバリア層として、金属箔、金属あるいは金属酸化物の蒸着膜等が使用されている。 In general, packaging materials having gas barrier properties are composed of a laminate having at least a base layer, a gas barrier layer, an adhesive layer, and a sealant layer. In particular, as a gas barrier layer for improving oxygen barrier properties, metal foil, A vapor-deposited film of metal or metal oxide is used.
しかし、ガスバリア層としての金属箔は、高い酸素バリア性を達成することができるが、蒸着膜などに比べて厚く、その結果、金属箔を使用した包装材料も厚くなり、耐折り曲げ性に劣ることが知られている。 However, although metal foil as a gas barrier layer can achieve high oxygen barrier properties, it is thicker than vapor-deposited films, etc., and as a result, packaging materials using metal foil are also thicker and have poor bending resistance. It has been known.
これに対し、金属あるいは金属酸化物の蒸着膜等を使用すると膜厚を薄くすることができ、折り曲げ性等に優れているが、蒸着膜表面は凹凸を有することからか、十分な酸素バリア性を達成することが困難であるという問題を有していた。 On the other hand, if a vapor-deposited film of metal or metal oxide is used, the film thickness can be made thinner and it has excellent bendability. The problem was that it was difficult to achieve.
更に、特許文献１には、酸素バリア材として、活性水素含有化合物（Ａ）および有機ポリイソシアネート化合物（Ｂ）を反応させてなる樹脂硬化物を含む熱硬化型ガス（酸素）バリア性ポリウレタン樹脂が記載されている。
Further,
該樹脂硬化物中には、メタキシレンジイソシアネート由来の骨格構造が２０％質量以上含有され、かつ前記（Ａ）および（Ｂ）の内、３官能以上の化合物の占める割合が、（Ａ）と（Ｂ）の総量に対して７質量％以上であることを特徴とする熱硬化型酸素バリア性ポリウレタン樹脂を使用したガス（酸素）バリア性複合フィルム（基材フィルム層と熱硬化型ガスバリア性ポリウレタン樹脂を含む層とを有する）が記載されている。 The resin cured product contains 20% or more by mass of a skeleton structure derived from meta-xylene diisocyanate, and the proportion of trifunctional or higher functional compounds among (A) and (B) is the same as that of (A) and ( A gas (oxygen) barrier composite film (base film layer and thermosetting gas barrier polyurethane resin) using a thermosetting oxygen barrier polyurethane resin characterized by an amount of 7% by mass or more based on the total amount of B) and a layer containing the same.
更にまた、特許文献２には、高分子フィルム基材の少なくとも片面に、酸化珪素または酸化アルミニウムの薄膜層を形成した透明性を有する被覆フィルムの該薄膜層面と、ヒートシール性樹脂フィルムとを、無機の酸化珪素及び酸化アルミニウムの材料から選ばれる一種以上の粒子とポリエステルポリオールとイソシアネート化合物を含有するバリア性接着剤を介してドライラミネート法により接着させたことを特徴とするバリア性積層体、及びこれを用いた包装材料が記載されている。
Furthermore,
しかしながら、特許文献１においては、該組成物は極性が高い溶剤を使用しなければならないため、作業性に乏しい。例えばアセトンのような溶解性の高い溶剤を使用した場合には、沸点が低く且つ外気の水を取り込みやすいため、水とイソシアネートとの反応によって調整粘度が上昇しやすいといった問題がある。
However, in
また、特許文献２においては、接着剤に含有されている無機化合物の粒径がナノオーダーの球状ないしは不定形の無機化合物であるため、接着剤自体の酸素バリア性、特に屈曲の負荷を与えた場合の酸素バリア性は高くないという問題点がある。
In addition, in
本発明は、上記の問題点を解決して、総構成層数が少なく、積層体生産時の作業性に優れ、易開封性とガスバリア性と耐屈曲性と低溶剤臭性に優れた積層体および該積層体からなる包装材料とピロー包装袋を提供することを目的とする。 The present invention solves the above problems and provides a laminate with a small total number of constituent layers, excellent workability during laminate production, and excellent ease of opening, gas barrier properties, bending resistance, and low solvent odor. The present invention also aims to provide a packaging material and a pillow packaging bag made of the laminate.
本発明者は、種々研究の結果、少なくとも、基材層（Ａ）と、ガスバリア性有機接着剤層（Ｂ）と、ガスバリア無機蒸着層（Ｃ）と、易開封性シーラント層（Ｄ）と、印刷層（Ｆ）とを有する低溶剤臭易開封性ガスバリア積層体であって、ガスバリア無機蒸着層（Ｃ）とガスバリア性有機接着剤層（Ｂ）とが隣接した構成を有し、ガスバリア性有機接着剤層（Ｂ）は、無溶剤型接着剤樹脂組成物が塗布され、硬化されて形成された層であり、印刷層（Ｆ）は、水性フレキソ印刷層および／または水性グラビア印刷層を含み、積層体の溶剤含有率はゼロまたは６ｍｇ／ｍ2以下である、低溶剤臭易開封性ガスバリア積層体、
更には、ガスバリア塗布膜層（Ｅ）を有する低溶剤臭易開封性ガスバリア積層体、および該低溶剤臭易開封性ガスバリア積層体からなる低溶剤臭ガスバリア包装材料が、上記の目的を達成することを見出した。
As a result of various studies, the present inventor has determined that at least a base material layer (A), a gas barrier organic adhesive layer (B), a gas barrier inorganic vapor deposition layer (C), an easy-open sealant layer (D), A low solvent odor, easy-to-open gas barrier laminate having a printed layer (F), which has a structure in which a gas barrier inorganic vapor deposited layer (C) and a gas barrier organic adhesive layer (B) are adjacent to each other, and has a gas barrier organic The adhesive layer (B) is a layer formed by applying and curing a solvent-free adhesive resin composition, and the printing layer (F) includes an aqueous flexographic printing layer and/or an aqueous gravure printing layer. , a low solvent odor, easy-to-open gas barrier laminate, in which the laminate has a solvent content of zero or 6 mg/m 2 or less;
Furthermore, a low-solvent-odor, easy-to-open gas barrier laminate having a gas barrier coating layer (E), and a low-solvent-odor, easy-to-open gas barrier packaging material comprising the low-solvent, easy-to-open gas barrier laminate achieve the above objects. I found out.
そして、本発明は、以下の点を特徴とする。
１．少なくとも、基材層（Ａ）と、ガスバリア性有機接着剤層（Ｂ）と、ガスバリア無機蒸着層（Ｃ）と、易開封性シーラント層（Ｄ）と印刷層（Ｆ）とを有する低溶剤臭易開封性ガスバリア積層体であって、
ガスバリア無機蒸着層（Ｃ）とガスバリア性有機接着剤層（Ｂ）とは隣接して積層されており、
ガスバリア性有機接着剤層（Ｂ）は、無溶剤接着剤組成物が塗布され、更に硬化されて形成された層であり、
印刷層（Ｆ）は、水性フレキソ印刷層および／または水性グラビア印刷層を含み、
前記低溶剤臭易開封性ガスバリア積層体の溶剤含有量は、ゼロまたは６ｍｇ／ｍ2以下で
ある、
低溶剤臭易開封性ガスバリア積層体。
２．印刷層（Ｆ）は、ガスバリア性有機接着剤層（Ｂ）と隣接して設けられている、
上記１に記載の低溶剤臭易開封性ガスバリア積層体。
３．基材層（Ａ）は、ポリプロピレン系樹脂を含む二軸延伸フィルムからなる、
上記１または２に記載の低溶剤臭易開封性ガスバリア積層体。
４．基材層（Ａ）は、ポリエチレンテレフタレート系樹脂を含む二軸延伸フィルムからなる、
上記１～３の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
５．更に、基材層（Ａ）とガスバリア性有機接着剤層（Ｂ）との間に、ガスバリア塗布膜層（Ｅ）を有する低溶剤臭易開封性ガスバリア積層体であって、
ガスバリア塗布膜層（Ｅ）は、金属アルコキシドと水溶性高分子とを含む樹脂組成物から生成された、ゾルゲル法加水分解重縮合物を含有する、
上記１～４の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
６．ガスバリア無機蒸着層（Ｃ）は、アルミニウム蒸着層、アルミナ蒸着層、及び、シリカ蒸着層、からなる群から選ばれる１種または２種以上を有する層である、
上記１～５の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
７．ガスバリア無機蒸着層（Ｃ）が、アルミニウム蒸着層を有する層である、上記１～５
の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
８．ガスバリア無機蒸着層（Ｃ）の厚みが、１～１００ｎｍである、
上記１～７の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
９．前記無溶剤接着剤組成物が、２液硬化型無溶剤接着剤組成物である、上記１～８の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
１０．ガスバリア性有機接着剤層（Ｂ）は、厚みが０．６～６．０μｍである、
上記１～９の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
The present invention is characterized by the following points.
1. A low solvent odor comprising at least a base material layer (A), a gas barrier organic adhesive layer (B), a gas barrier inorganic vapor deposited layer (C), an easy-to-open sealant layer (D), and a printed layer (F). An easily openable gas barrier laminate,
The gas barrier inorganic vapor deposited layer (C) and the gas barrier organic adhesive layer (B) are laminated adjacent to each other,
The gas barrier organic adhesive layer (B) is a layer formed by applying a solvent-free adhesive composition and further curing it,
The printing layer (F) includes an aqueous flexographic printing layer and/or an aqueous gravure printing layer,
The solvent content of the low solvent odor easy-to-open gas barrier laminate is zero or 6 mg/m 2 or less,
Easy-to-open gas barrier laminate with low solvent odor.
2. The printing layer (F) is provided adjacent to the gas barrier organic adhesive layer (B),
The low solvent odor, easy-to-open gas barrier laminate according to 1 above.
3. The base layer (A) is made of a biaxially stretched film containing a polypropylene resin.
The low solvent odor, easy-to-open gas barrier laminate according to 1 or 2 above.
4. The base layer (A) is made of a biaxially stretched film containing a polyethylene terephthalate resin.
The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 3 above.
5. Furthermore, a low solvent odor easy-to-open gas barrier laminate having a gas barrier coating layer (E) between the base material layer (A) and the gas barrier organic adhesive layer (B),
The gas barrier coating layer (E) contains a sol-gel hydrolysis polycondensate produced from a resin composition containing a metal alkoxide and a water-soluble polymer.
The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 4 above.
6. The gas barrier inorganic vapor deposited layer (C) is a layer having one or more selected from the group consisting of an aluminum vapor deposited layer, an alumina vapor deposited layer, and a silica vapor deposited layer.
The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 5 above.
7. 1 to 5 above, wherein the gas barrier inorganic vapor deposited layer (C) is a layer having an aluminum vapor deposited layer.
The low solvent odor, easy-to-open gas barrier laminate according to any one of the above.
8. The thickness of the gas barrier inorganic vapor deposited layer (C) is 1 to 100 nm.
8. The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 7 above.
9. 9. The low-solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 8 above, wherein the solvent-free adhesive composition is a two-component curable solvent-free adhesive composition.
10. The gas barrier organic adhesive layer (B) has a thickness of 0.6 to 6.0 μm,
The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 9 above.
１１．２３℃９０％ＲＨ環境下における酸素透過度が、０．０５～２ｃｃ／ｍ2／ｄａｙ／ａｔｍであり、
４０℃９０％ＲＨ環境下における水蒸気透過度が、０．０１～２ｇ／ｍ2／ｄａｙである、
酸素バリア用及び水蒸気バリア用の、
上記１～１０の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
１２．ゲルボフレックステスターで５回の屈曲負荷を与えた後の、２３℃９０％ＲＨ環境下における酸素透過度の、前記屈曲負荷を与える前からの増加値が、ゼロまたは２０ｃｃ／ｍ2／ｄａｙ／ａｔｍ以下である、
上記１～１１の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
１３．総構成層数が６以下である、上記１～１２の何れかに記載の低溶剤臭易開封性ガスバリア積層体。
１４．上記１～１３の何れかに記載の低溶剤臭易開封性ガスバリア積層体を用いた、低溶剤臭ガスバリア包装材料。
１５．上記１４に記載の低溶剤臭ガスバリア包装材料を用いた、低溶剤臭ガスバリア包装袋。
１６．上記１４に記載の低溶剤臭ガスバリア包装材料を用いた、低溶剤臭ガスバリアピロー包装袋。
11. The oxygen permeability in a 23°C 90% RH environment is 0.05 to 2 cc/m 2 /day/atm,
The water vapor permeability in an environment of 40° C. and 90% RH is 0.01 to 2 g/m 2 /day.
For oxygen barrier and water vapor barrier,
The low solvent odor, easy-to-open gas barrier laminate according to any one of
12. After applying a
The low solvent odor, easy-to-open gas barrier laminate according to any one of
13. 13. The low solvent odor, easy-to-open gas barrier laminate according to any one of 1 to 12 above, wherein the total number of constituent layers is 6 or less.
14. A low-solvent-odor gas barrier packaging material using the low-solvent-odor, easy-to-open gas barrier laminate according to any one of 1 to 13 above.
15. A low-solvent odor gas barrier packaging bag using the low-solvent odor gas barrier packaging material described in 14 above.
16. A low-solvent odor gas barrier pillow packaging bag using the low-solvent odor gas barrier packaging material described in 14 above.
本発明に係る積層体及び該積層体からなる包装材料は、ガスバリア無機蒸着層（Ｃ）とガスバリア性有機接着剤層（Ｂ）とを隣接して組み合わせることで、ガスバリア無機蒸着層（Ｃ）表面に生じている凹凸の凹部が、ガスバリア性有機接着剤層（Ｂ）により埋められて平坦化されて面方向のガスバリア性が均一化され、ガスバリア無機蒸着層（Ｃ）の層厚を薄くして耐屈曲性を保持しつつ、少ない総構成層数で、従来と同等以上のガスバリア性を発揮することができる。 The laminate according to the present invention and the packaging material made of the laminate can be obtained by combining a gas barrier inorganic vapor deposited layer (C) and a gas barrier organic adhesive layer (B) adjacently, so that the surface of the gas barrier inorganic vapor deposited layer (C) is The concavities and convexities occurring in the surface are filled and flattened by the gas barrier organic adhesive layer (B), and the gas barrier properties in the plane direction are made uniform, and the layer thickness of the gas barrier inorganic vapor deposited layer (C) is reduced. While maintaining bending resistance, it is possible to exhibit gas barrier properties equivalent to or better than conventional ones with a small total number of constituent layers.
さらに、ガスバリア性有機接着剤層（Ｂ）の溶剤含有率が低いことと、印刷層（Ｆ）が水性フレキソ印刷層および／または水性グラビア印刷層からなり、印刷層（Ｆ）に残留する溶剤も低減できることから、内容物への溶剤臭転移を低減化することができる。 Furthermore, the solvent content of the gas barrier organic adhesive layer (B) is low, and the printing layer (F) is composed of an aqueous flexographic printing layer and/or an aqueous gravure printing layer, and the solvent remaining in the printing layer (F) is also low. Since it is possible to reduce the transfer of solvent odor to the contents, it is possible to reduce the transfer of solvent odor to the contents.
本発明に係る積層体および該積層体からなる包装材料とピロー包装袋について、図面を参照しながら以下に詳しく説明する。 The laminate according to the present invention and the packaging material and pillow packaging bag made of the laminate are described in detail below with reference to the drawings.
本発明における、総構成層数とは、積層体を構成する、基材層、ガスバリア層、接着剤層、及びシーラント層等の層の詳細な数であり、各層における蒸着層やＡＣコート等の特殊処理コート層をも含む層数のことである。例えば、アルミニウム蒸着層付きＰＥＴフィ
ルム層は、２層として数える。
In the present invention, the total number of constituent layers refers to the detailed number of layers such as a base material layer, gas barrier layer, adhesive layer, and sealant layer that make up the laminate, and the number of layers such as a vapor deposited layer, AC coat, etc. in each layer. This refers to the number of layers including the special treatment coat layer. For example, a PET film layer with an aluminum vapor deposited layer counts as two layers.
図１～２は、本発明の低溶剤臭易開封性ガスバリア積層体の層構成の一例を示す概略的断面図である。 1 and 2 are schematic cross-sectional views showing an example of the layer structure of the low-solvent odor, easy-to-open gas barrier laminate of the present invention.
本発明の低溶剤臭易開封性ガスバリア積層体は、図１に示すように、基材層（Ａ）と、ガスバリア性有機接着剤層（Ｂ）と、ガスバリア無機蒸着層（Ｃ）と、易開封性シーラント層（Ｄ）、印刷層（Ｆ）とを、積層してなる構成を基本構造とするものである。 As shown in FIG. 1, the low-solvent odor, easy-to-open gas barrier laminate of the present invention includes a base layer (A), a gas barrier organic adhesive layer (B), and an easily opened gas barrier inorganic vapor deposited layer (C). The basic structure is a structure in which an unsealable sealant layer (D) and a printed layer (F) are laminated.
本発明の低溶剤臭易開封性ガスバリア積層体の他の態様としては、図２に示すように、基材層（Ａ）とガスバリア性有機接着剤層（Ｂ）との間に、更に、ガスバリア無機蒸着層（Ｃ）とは別個のガスバリア無機蒸着層と、ガスバリア塗布膜層（Ｅ）とを積層した構成であってもよい。 As another embodiment of the low-solvent odor, easy-to-open gas barrier laminate of the present invention, as shown in FIG. A structure in which a gas barrier inorganic vapor deposited layer separate from the inorganic vapor deposited layer (C) and a gas barrier coating film layer (E) are laminated may be used.
上記の例は、本発明の低溶剤臭易開封性ガスバリア積層体の一例であり、本発明はこれに限定されるものではない。
次に、 本発明に係る積層体および該積層体からなる包装材料とピロー包装袋の材料、それらの製造法等について説明する。
本発明において使用される樹脂名は、業界において慣用されるものを用いることとする。また、本発明は、以降の列記された諸々の具体例に限定されるものでは無い。
The above example is an example of the low-solvent odor, easy-to-open gas barrier laminate of the present invention, and the present invention is not limited thereto.
Next, the laminate according to the present invention, the packaging material made of the laminate, the material of the pillow packaging bag, the manufacturing method thereof, etc. will be explained.
The resin names used in the present invention are those commonly used in the industry. Further, the present invention is not limited to the various specific examples listed below.
［基材層（Ａ）］
基材層（Ａ）としては、化学的ないし物理的強度に優れ、無機蒸着膜を形成する条件等に耐え、それら無機蒸着膜等の特性を損なうことなく良好に保持し得ることができる金属、金属酸化物等の無機材料や樹脂等の有機材料を例えばフィルムやシートとして使用することができる。
[Base layer (A)]
As the base layer (A), inorganic materials such as metals and metal oxides, and organic materials such as resins, which have excellent chemical and physical strength, can withstand the conditions for forming an inorganic vapor deposition film, and can well maintain the properties of the inorganic vapor deposition film without impairing the properties, can be used in the form of, for example, a film or sheet.
基材層（Ａ）としては、単層フィルムまたは多層積層フィルムが用いられるが、特に限定されず、各種包装材料に用いられる任意のフィルムを使用することができる。これらの中から、包装する内容物の種類や充填後の加熱処理の有無等の使用条件に応じて、適するものを自由に選択して使用する。 As the base material layer (A), a single layer film or a multilayer laminated film is used, but it is not particularly limited, and any film used for various packaging materials can be used. From these, a suitable one is freely selected and used depending on the usage conditions such as the type of contents to be packaged and the presence or absence of heat treatment after filling.
基材層（Ａ）として好ましく使用されるフィルムの具体例としては、紙、アルミニウム箔、セロファン、ポリアミド系樹脂フィルム、ポリエステル系樹脂フィルム、オレフィン系樹脂フィルム、酸変性ポリオレフィン系樹脂フィルム、ポリスチレン系樹脂フィルム、ポリウレタン系樹脂フィルム、アセタール系樹脂フィルム、これらを一軸または二軸延伸したフィルム、Ｋコートフィルム、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、線状低密度ポリエチレン、ポリプロピレン、ポリブテン、ポリビニルアルコール、エチレン－酢酸ビニル共重合体、アイオノマー、エチレン－（メタ）アクリル酸共重合体、エチレン－（メタ）アクリル酸エステル共重合体、エチレン－プロピレン共重合体、メチルペンテン、ポリアクリロニトリル、アクリロニトリル－スチレン共重合体、アクリロニトリル－ブタジエン－スチレン共重合体、ポリカーボネート、ポリ塩化ビニル（ＰＶＣ）、ポリ塩化ビニリデン（ＰＶＤＣ）、ポリフッ化ビニリデン（ＰＶＤＦ）、エチレン－テトラフルオロエチレン共重合体（ＥＴＦＥ）、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート、ポリエチレンナフタレート等からなる樹脂フィルム、Ｋコート延伸ポリプロピレンフィルム、Ｋコート延伸ナイロンフィルム、これらの２以上のフィルムを積層した複合フィルム等が挙げられる。 Specific examples of films preferably used as the base layer (A) include paper, aluminum foil, cellophane, polyamide resin film, polyester resin film, olefin resin film, acid-modified polyolefin resin film, and polystyrene resin. Films, polyurethane resin films, acetal resin films, uniaxially or biaxially stretched films of these, K coated films, such as low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, polypropylene, polybutene, Polyvinyl alcohol, ethylene-vinyl acetate copolymer, ionomer, ethylene-(meth)acrylic acid copolymer, ethylene-(meth)acrylic acid ester copolymer, ethylene-propylene copolymer, methylpentene, polyacrylonitrile, acrylonitrile -Styrene copolymer, acrylonitrile-butadiene-styrene copolymer, polycarbonate, polyvinyl chloride (PVC), polyvinylidene chloride (PVDC), polyvinylidene fluoride (PVDF), ethylene-tetrafluoroethylene copolymer (ETFE), Resin films made of polytetrafluoroethylene (PTFE), polyethylene terephthalate (PET), polybutylene terephthalate, polyethylene naphthalate, etc., K-coated stretched polypropylene films, K-coated stretched nylon films, and composite films made by laminating two or more of these films. etc.
なかでも、ポリエチレンテレフタレート、ポリエチレンナフタレートなどの一軸または
二軸延伸ポリエステルフィルム、ナイロン６、ナイロン６６、ＭＸＤ６（ポリメタキシリレンアジパミド）などのポリアミドの一軸または二軸延伸ポリアミドフィルム、そして、二軸延伸ポリプロピレンフィルム（ＯＰＰ）等を好適に使用することができる。また、シリカ蒸着ＰＥＴ、アルミナ蒸着ＰＥＴなどの透明蒸着ＰＥＴ、アルミニウム蒸着二軸延伸ポリプロピレンフィルム（ＯＰＰ）等も好適である。
Among them, uniaxially or biaxially oriented polyester films such as polyethylene terephthalate and polyethylene naphthalate, uniaxially or biaxially oriented polyamide films such as
（厚さ）
基材層（Ａ）の厚さは、成形性、透明性、屈曲後のガスバリア性維持の観点から、好ましくは５μｍ以上、５０μｍ以下であり、より好ましくは１５μｍ以上、４０μｍ以下である。上記範囲よりも薄いと、積層体の剛性が低すぎる為に屈曲時にガスバリア性に寄与する層が破壊され易く、また、積層体の強度が不足し易い。またこれより厚いと、積層体の剛性が高くなりすぎる為に屈曲時にガスバリア性に寄与する層が破壊され易く、また、積層体の加工が困難になり易い。
基材層（Ａ）の厚みは、基材層（Ａ）がポリプロピレン系樹脂を含む二軸延伸フィルムからなる場合には１８～４０μｍが好ましく、基材層（Ａ）がポリエチレンテレフタレート系樹脂を含む二軸延伸フィルムからなる場合には５～４０μｍが好ましい。
(thickness)
The thickness of the base layer (A) is preferably 5 μm or more and 50 μm or less, more preferably 15 μm or more and 40 μm or less, from the viewpoint of moldability, transparency, and maintaining gas barrier properties after bending. If it is thinner than the above range, the rigidity of the laminate is too low, so that the layer contributing to gas barrier properties is likely to be destroyed when bent, and the strength of the laminate is likely to be insufficient. Moreover, if it is thicker than this, the rigidity of the laminate becomes too high, so that the layer contributing to gas barrier properties is likely to be destroyed when bent, and processing of the laminate is likely to be difficult.
The thickness of the base layer (A) is preferably 18 to 40 μm when the base layer (A) is made of a biaxially stretched film containing a polypropylene resin, and the base layer (A) contains a polyethylene terephthalate resin. In the case of a biaxially stretched film, the thickness is preferably 5 to 40 μm.
（表面処理）
また、基材層（Ａ）及び基材層（Ａ）を構成するフィルム又はシートは、ガスバリア性有機接着剤層（Ｂ）等の各接着剤層あるいはガスバリア無機蒸着層（Ｃ）等の各無機蒸着層との密着性を向上させるために、ラミネートあるいは蒸着前に基材層（Ａ）及び基材層（Ａ）を構成するフィルム又はシートの密着させる表面に、必要に応じて、前もって、コロナ放電処理、オゾン処理、酸素ガス若しくは窒素ガス等を用いた低温プラズマ処理、グロー放電処理などの物理的な処理や、化学薬品を用いた酸化処理などの化学的な処理や、接着剤層、プライマーコート剤層、アンダーコート層、あるいは、蒸着アンカーコート剤層等を形成する処理、及びその他処理を施してもよく、該表面処理後に無機蒸着層を設け、さらに、該無機蒸着層上に、後述のガスバリア塗布膜層（Ｅ）等のバリアコート層を設けた構成としてもよい。
(surface treatment)
[0043] In order to improve adhesion between the base layer (A) and each adhesive layer such as the gas barrier organic adhesive layer (B) or each inorganic vapor deposition layer such as the gas barrier inorganic vapor deposition layer (C), the surfaces of the base layer (A) and the film or sheet constituting the base layer (A) to be adhered thereto may be previously subjected to physical treatments such as corona discharge treatment, ozone treatment, low-temperature plasma treatment using oxygen gas or nitrogen gas or the like, glow discharge treatment, chemical treatments such as oxidation treatment using chemicals, treatments to form an adhesive layer, a primer coating agent layer, an undercoat layer, a vapor deposition anchor coating agent layer, or the like, and other treatments, as necessary, before lamination or vapor deposition. It is also possible to provide an inorganic vapor deposition layer after the surface treatment, and further provide a barrier coat layer such as a gas barrier coating film layer (E) described below on the inorganic vapor deposition layer.
（フィルムの成形法）
基材層（Ａ）に用いる樹脂のフィルム又はシートとしては、例えば、前記の樹脂の群から選ばれる１種又は２種以上の樹脂を使用し、押し出し法、キャスト成形法、Ｔダイ法、切削法、インフレーション法等従来から使用されている製膜化法により、又は、２種以上の樹脂を使用して多層共押し出し製膜化法により製造することができる。さらに、フィルムの強度、寸法安定性、耐熱性の観点から、例えば、テンター方式、あるいは、チューブラー方式等を利用して１軸ないし２軸方向に延伸することができる。
(Film forming method)
As the resin film or sheet used for the base material layer (A), for example, one or more resins selected from the group of resins mentioned above may be used, and extrusion method, cast molding method, T-die method, cutting can be used. It can be manufactured by a conventionally used film forming method such as a method or an inflation method, or by a multilayer coextrusion film forming method using two or more types of resins. Furthermore, from the viewpoint of the strength, dimensional stability, and heat resistance of the film, it is possible to stretch the film in uniaxial or biaxial directions using, for example, a tenter method or a tubular method.
（添加剤）
基材層（Ａ）に用いる樹脂のフィルム又はシートは、必要に応じて、加工性、耐熱性、耐候性、機械的性質、寸法安定性、抗酸化性、滑り性、離形性、難燃性、抗カビ性、電気的特性、強度等を改良、改質する目的で、滑剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、充填剤、補強剤、帯電防止剤、顔料等のプラスチック配合剤や添加剤等を添加することができ、その添加量としては、他の性能に悪影響を与えない範囲で目的に応じて、任意に添加することができる。
(Additive)
The resin film or sheet used for the base layer (A) may have properties such as processability, heat resistance, weather resistance, mechanical properties, dimensional stability, antioxidant properties, slipperiness, mold releasability, and flame retardancy, as required. lubricants, crosslinking agents, antioxidants, ultraviolet absorbers, light stabilizers, fillers, reinforcing agents, antistatic agents, pigments, etc. for the purpose of improving and modifying properties, anti-fungal properties, electrical properties, strength, etc. Plastic compounding agents, additives, etc. can be added, and the amount thereof can be arbitrarily added depending on the purpose as long as it does not adversely affect other performances.
［ガスバリア性有機接着剤層（Ｂ）］
本発明におけるガスバリア性有機接着剤層（Ｂ）は、無溶剤接着剤組成物が塗布され、更に硬化されて形成された層であり、積層体中でガスバリア無機蒸着層（Ｃ）と隣接して積層されており、ガスバリア性、特に酸素と水蒸気に対するバリア性を有する。
[Gas barrier organic adhesive layer (B)]
The gas barrier organic adhesive layer (B) in the present invention is a layer formed by applying and further curing a solvent-free adhesive composition, and is adjacent to the gas barrier inorganic vapor deposited layer (C) in the laminate. It is laminated and has gas barrier properties, especially against oxygen and water vapor.
ガスバリア性有機接着剤層（Ｂ）の厚みは、好ましくは０．６～６．０μｍであり、より好ましくは０．８～５．０μｍであり、更に好ましくは１．０～４．５μｍである。上記範囲よりも薄いとガスバリア性が不十分になりやすく、上記範囲よりも厚いと耐折り曲げ性に劣りやすく、折り曲げ後のガスバリア性が低下することにつながりやすい。 The thickness of the gas barrier organic adhesive layer (B) is preferably 0.6 to 6.0 μm, more preferably 0.8 to 5.0 μm, and even more preferably 1.0 to 4.5 μm. . If it is thinner than the above range, the gas barrier properties tend to be insufficient, and if it is thicker than the above range, the bending resistance tends to be poor, which tends to lead to a decrease in the gas barrier properties after bending.
ガスバリア性有機接着剤層（Ｂ）のガラス転移温度は、好ましくは－３０℃～８０℃の範囲であり、より好ましくは０℃～７０℃であり、更に好ましくは２５℃～７０℃である。上記範囲よりも高い場合は、室温付近での硬化塗膜の柔軟性が低下して基材への密着性が劣ることで接着力が低下するおそれがある。上記範囲よりも低い場合は、常温付近での硬化塗膜の分子運動が大きくなり得ることによって十分な酸素バリア性が発揮され難いおそれや、凝集力不足による接着力低下のおそれがある。 The glass transition temperature of the gas barrier organic adhesive layer (B) is preferably in the range of -30°C to 80°C, more preferably in the range of 0°C to 70°C, even more preferably in the range of 25°C to 70°C. If it is higher than the above range, the flexibility of the cured coating film at around room temperature may decrease, resulting in poor adhesion to the substrate, which may lead to a decrease in adhesive strength. If it is lower than the above range, the molecular movement of the cured coating film may become large at around room temperature, which may make it difficult to exhibit sufficient oxygen barrier properties, and there is a risk that adhesive strength may decrease due to insufficient cohesive force.
ガスバリア性有機接着剤層（Ｂ）を形成する接着剤樹脂組成物としては、例えば、１分子内に水酸基を２個以上有するポリオール（Ｊ）と、１分子内にイソシアネート基を２個以上有するイソシアネート化合物（Ｋ）と、リン酸変性化合物（Ｌ）とを含有する接着剤樹脂組成物が挙げられる。 Examples of the adhesive resin composition forming the gas barrier organic adhesive layer (B) include a polyol (J) having two or more hydroxyl groups in one molecule, and an isocyanate having two or more isocyanate groups in one molecule. Examples include adhesive resin compositions containing the compound (K) and the phosphoric acid-modified compound (L).
また、接着剤樹脂組成物は、更に、板状無機化合物（Ｍ）、１分子内に２個以上の水酸基を有するポリエステルポリオール（Ｐ）、１分子内に１個または２個以上のカルボキシル基と２個以上の水酸基とを有する多価カルボン酸変性ポリエステルポリオール（Ｎ）からなる群の１種または２種以上を含有していても良い。 The adhesive resin composition further contains a plate-like inorganic compound (M), a polyester polyol (P) having two or more hydroxyl groups in one molecule, and one or more carboxyl groups in one molecule. It may contain one or more of the group consisting of polyhydric carboxylic acid-modified polyester polyols (N) having two or more hydroxyl groups.
特に、多価カルボン酸変性ポリエステルポリオール（Ｎ）と、１分子内にイソシアネート基を２個以上有するイソシアネート化合物（Ｋ）とを含有し、酸価が２０ｍｇＫＯＨ／ｇ以上であることが好ましい。 In particular, it is preferable that it contains a polycarboxylic acid-modified polyester polyol (N) and an isocyanate compound (K) having two or more isocyanate groups in one molecule, and has an acid value of 20 mgKOH/g or more.
接着剤樹脂組成物は、２液硬化型接着剤組成物が好ましく、２液硬化型無溶剤型接着剤樹脂組成物組成物がより好ましい。
接着剤樹脂組成物は、ラミネート時に、例えば、無溶剤のまま、加熱して低粘度化して用いられる。
ここで、本発明において無溶剤とは、溶剤を積極的には含有しないことを意味し、原材料中に残存する溶剤に由来する微量分を、形成された積層体中の溶剤含有量をゼロまたは６ｍｇ／ｍ2以下にし得る範囲内で含有していてもよい。
The adhesive resin composition is preferably a two-component curable adhesive composition, more preferably a two-component curable solvent-free adhesive resin composition.
At the time of lamination, the adhesive resin composition is used, for example, without a solvent, by heating to lower the viscosity.
Here, in the present invention, "solvent-free" means not actively containing a solvent, and the trace amount derived from the solvent remaining in the raw materials is reduced to zero or no solvent content in the formed laminate. The content may be within the range of 6 mg/m 2 or less.
或いは、形成されたガスバリア性有機接着剤層（Ｂ）の溶剤含有量を上記範囲にし得る溶剤を含んでいてもよい。 Alternatively, it may contain a solvent that can bring the solvent content of the formed gas barrier organic adhesive layer (B) within the above range.
（ポリオール（Ｊ））
ポリオール（Ｊ）は、１分子内に水酸基を２個以上有し、主骨格がポリエステル構造、ポリエステルポリウレタン構造、ポリエーテル構造、及びポリエーテルポリウレタン構造からなる群から選ばれる１種または２種以上を有するものである。前記ポリエステル構造は、例えば、多価カルボン酸類と多価アルコールとを公知慣用の方法で重縮合反応させて得ることができるが、合成ルートはこれに限定されない。
(Polyol (J))
The polyol (J) has two or more hydroxyl groups in one molecule, and has one or more main skeletons selected from the group consisting of a polyester structure, a polyester polyurethane structure, a polyether structure, and a polyether polyurethane structure. It is something that you have. The polyester structure can be obtained, for example, by subjecting a polycarboxylic acid and a polyhydric alcohol to a polycondensation reaction by a known and commonly used method, but the synthetic route is not limited thereto.
該ポリエステル構造又は該ポリエステルポリウレタン構造における多価カルボン酸類由来構造部分の７０～１００質量％が、オルト配向芳香族ジカルボン酸類由来であることが好ましい。該オルト配向芳香族ジカルボン酸類とは、オルト配向芳香族ジカルボン酸及びその無水物やエステル形成性誘導体を指す。 It is preferable that 70 to 100% by mass of the polycarboxylic acid-derived structural portion in the polyester structure or the polyester polyurethane structure is derived from ortho-oriented aromatic dicarboxylic acids. The ortho-oriented aromatic dicarboxylic acids refer to ortho-oriented aromatic dicarboxylic acids and their anhydrides and ester-forming derivatives.
多価カルボン酸類とは、多価カルボン酸及びその無水物やエステル形成性誘導体を指し
、例えば、脂肪族多価カルボン酸類と芳香族多価カルボン酸類が挙げられる。
Polyvalent carboxylic acids refer to polyvalent carboxylic acids and their anhydrides and ester-forming derivatives, and include, for example, aliphatic polyvalent carboxylic acids and aromatic polyvalent carboxylic acids.
具体的な脂肪族多価カルボン酸類としては、コハク酸、アジピン酸、アゼライン酸、セバシン酸、ドデカンジカルボン酸、１，４－シクロヘキサンジカルボン酸等が挙げられる。 Specific examples of aliphatic polycarboxylic acids include succinic acid, adipic acid, azelaic acid, sebacic acid, dodecanedicarboxylic acid, and 1,4-cyclohexanedicarboxylic acid.
具体的な芳香族多価カルボン酸類としては、オルトフタル酸、テレフタル酸、イソフタル酸、ピロメリット酸、トリメリット酸、１，２－ナフタレンジカルボン酸、１，８－ナフタレンジカルボン酸、２，３－ナフタレンジカルボン酸、１，４－ナフタレンジカルボン酸、２，５－ナフタレンジカルボン酸、２，６－ナフタレンジカルボン酸、ナフタル酸、ビフェニルジカルボン酸、１，２－ビス（フェノキシ）エタン－ｐ，ｐ‘－ジカルボン酸及びこれらジカルボン酸の無水物あるいはエステル形成性誘導体；ｐ－ヒドロキシ安息香酸、ｐ－（２－ヒドロキシエトキシ）安息香酸及びこれらのジヒドロキシカルボン酸のエステル形成性誘導体等の多塩基酸等が挙げられる。 Specific aromatic polycarboxylic acids include orthophthalic acid, terephthalic acid, isophthalic acid, pyromellitic acid, trimellitic acid, 1,2-naphthalene dicarboxylic acid, 1,8-naphthalene dicarboxylic acid, and 2,3-naphthalene. Dicarboxylic acid, 1,4-naphthalene dicarboxylic acid, 2,5-naphthalene dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, naphthalic acid, biphenyl dicarboxylic acid, 1,2-bis(phenoxy)ethane-p,p'-dicarboxylic acid Acids and anhydrides or ester-forming derivatives of these dicarboxylic acids; examples include polybasic acids such as p-hydroxybenzoic acid, p-(2-hydroxyethoxy)benzoic acid, and ester-forming derivatives of these dihydroxycarboxylic acids. .
具体的なオルト配向芳香族ジカルボン酸類としては、オルトフタル酸、１，２－ナフタレンジカルボン酸、１，８－ナフタレンジカルボン酸、２，３－ナフタレンジカルボン酸、及びこれらジカルボン酸の無水物あるいはエステル形成性誘導体等が挙げられる。 Specific ortho-oriented aromatic dicarboxylic acids include orthophthalic acid, 1,2-naphthalene dicarboxylic acid, 1,8-naphthalene dicarboxylic acid, 2,3-naphthalene dicarboxylic acid, and anhydrides or esters of these dicarboxylic acids. Examples include derivatives.
多価カルボン酸類としては、これらを単独で或いは２種以上を併用することができる。
多価アルコールとしては、脂肪族多価アルコールと芳香族多価フェノールが挙げられる。
The polyvalent carboxylic acids may be used alone or in combination of two or more kinds.
The polyhydric alcohols include aliphatic polyhydric alcohols and aromatic polyhydric phenols.
脂肪族多価アルコールとしては、具体的には、エチレングリコール、プロピレングリコール、ブチレングリコール、ネオペンチルグリコール、シクロヘキサンジメタノール、１，５－ペンタンジオール、３－メチル－１，５－ペンタンジオール、１，６－ヘキサンジオール、メチルペンタンジオール、ジメチルブタンジオール、ブチルエチルプロパンジオール、ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、ジプロピレングリコール、トリプロピレングリコール等を例示することができる。 Specifically, the aliphatic polyhydric alcohols include ethylene glycol, propylene glycol, butylene glycol, neopentyl glycol, cyclohexanedimethanol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 1, Examples include 6-hexanediol, methylpentanediol, dimethylbutanediol, butylethylpropanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, and tripropylene glycol.
芳香族多価フェノールとしては、具体的には、ヒドロキノン、レゾルシノール、カテコール、ナフタレンジオール、ビフェノール、ビスフェノールＡ、ヒスフェノールＦ、テトラメチルビフェノールや、これらの、エチレンオキサイド伸長物、水添化脂環族等を例示することができる。 Specific examples of aromatic polyhydric phenols include hydroquinone, resorcinol, catechol, naphthalene diol, biphenol, bisphenol A, hisphenol F, tetramethylbiphenol, ethylene oxide extension products, and hydrogenated alicyclic compounds. etc. can be exemplified.
（イソシアネート化合物（Ｋ））
イソシアネート化合物（Ｋ）は、分子内にイソシアネート基を２個以上有し、芳香族または脂肪族のどちらでもよく、低分子化合物または高分子化合物のどちらでもよく、イソシアネート基が２個のジイソシアネート化合物や、３個以上のポリイソシアネート化合物等の公知の化合物が使用できる。イソシアネート化合物（Ｋ）としては、公知のイソシアネートブロック化剤を用いて公知慣用の適宜の方法より付加反応させて得られたブロック化イソシアネート化合物であってもよい。
(Isocyanate compound (K))
The isocyanate compound (K) has two or more isocyanate groups in the molecule, and may be either aromatic or aliphatic, and may be either a low-molecular compound or a high-molecular compound, and may include a diisocyanate compound having two isocyanate groups, , three or more polyisocyanate compounds, and other known compounds can be used. The isocyanate compound (K) may be a blocked isocyanate compound obtained by addition reaction using a known isocyanate blocking agent by a known and commonly used method.
中でも、接着性や耐レトルト性の観点から、ポリイソシアネート化合物が好まれ、酸素バリア性付与という点では、芳香族環を有するものが好ましく、特に、メタキシレン骨格を含むイソシアネート化合物が、ウレタン基の水素結合だけでなく芳香環同士のπ－πスタッキングによって酸素バリア性を向上させることが出来るという理由から好ましい。 Among these, polyisocyanate compounds are preferred from the viewpoint of adhesiveness and retort resistance, and those having an aromatic ring are preferred from the viewpoint of imparting oxygen barrier properties.In particular, isocyanate compounds containing a meta-xylene skeleton are preferred because they have a urethane group. This is preferable because oxygen barrier properties can be improved not only by hydrogen bonding but also by π-π stacking between aromatic rings.
イソシアネート化合物（Ｋ）の具体的な化合物としては、たとえば、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トルエンジイソシアネート、ジフェ
ニルメタンジイソシアネート、水素化ジフェニルメタンジイソシアネート、メタキシリレンジイソシアネート、水素化キシリレンジイソシアネート、イソホロンジイソシアネート或いはこれらのイソシアネート化合物の３量体、およびこれらのイソシアネート化合物の過剰量と、たとえばエチレングリコール、プロピレングリコール、メタキシリレンアルコール、１，３－ビスヒドロキシエチルベンゼン、１，４－ビスヒドロキシエチルベンゼン、トリメチロールプロパン、グリセロール、ペンタエリスリトール、エリスリトール、ソルビトール、エチレンジアミン、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、メタキシリレンジアミンなどの低分子活性水素化合物およびそのアルキレンオキシド付加物、各種ポリエステル樹脂類、ポリエーテルポリオール類、ポリアミド類の高分子活性水素化合物などと反応させて得られるアダクト体、ビュレット体、アロファネート体等が挙げられる。
Specific compounds of the isocyanate compound (K) include, for example, tetramethylene diisocyanate, hexamethylene diisocyanate, toluene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate, metaxylylene diisocyanate, hydrogenated xylylene diisocyanate, isophorone diisocyanate, or these. Trimers of isocyanate compounds, and excess amounts of these isocyanate compounds, such as ethylene glycol, propylene glycol, metaxylylene alcohol, 1,3-bishydroxyethylbenzene, 1,4-bishydroxyethylbenzene, trimethylolpropane, glycerol , low-molecular active hydrogen compounds such as pentaerythritol, erythritol, sorbitol, ethylene diamine, monoethanolamine, diethanolamine, triethanolamine, metaxylylene diamine, and their alkylene oxide adducts, various polyester resins, polyether polyols, polyamides Examples include adducts, bullets, allophanates, etc. obtained by reacting with polymeric active hydrogen compounds.
（リン酸変性化合物（Ｌ））
リン酸変性化合物（Ｌ）は、無機系部材に対する接着強度を向上させる効果を有するものであり、公知慣用のものを用いることができる。
(Phosphoric acid modified compound (L))
The phosphoric acid-modified compound (L) has the effect of improving the adhesive strength to inorganic members, and any known and commonly used compounds can be used.
具体的には、リン酸、ピロリン酸、トリリン酸、メチルアシッドホスフェート、エチルアシッドホスフェート、ブチルアシッドホスフェート、ジブチルホスフェート、２－エチルヘキシルアシッドホスフェート、ビス（２－エチルヘキシル）ホスフェート、イソドデシルアシッドホスフェート、ブトキシエチルアシッドホスフェート、オレイルアシッドホスフェート、テトラコシルアシッドホスフェート、２－ヒドロキシエチルメタクリレートアシッドホスフェート、ポリオキシエチレンアルキルエーテルリン酸、等が挙げられ、これらの１種または２種以上を用いることができる。 Specifically, phosphoric acid, pyrophosphoric acid, triphosphoric acid, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl) phosphate, isododecyl acid phosphate, butoxyethyl Examples include acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate, polyoxyethylene alkyl ether phosphate, and one or more of these can be used.
（溶剤）
溶剤は、ポリオール（Ｊ）とイソシアネート化合物（Ｋ）とを溶解し、リン酸変性化合物（Ｌ）や板状無機化合物（Ｍ）を均一に分散可能で、積層体の製造工程上の適切な沸点や揮発性を有し、形成された積層体の溶剤含有量をゼロまたは６ｍｇ／ｍ2以下にし得る
ものならば、特に制限は無い。
(solvent)
The solvent can dissolve the polyol (J) and the isocyanate compound (K), can uniformly disperse the phosphoric acid-modified compound (L) and the plate-like inorganic compound (M), and has an appropriate boiling point for the manufacturing process of the laminate. There are no particular limitations as long as the solvent is volatile and can reduce the solvent content of the formed laminate to zero or 6 mg/m 2 or less.
該接着剤樹脂組成物に、例えば極性が高い溶剤を使用している場合には、作業性に乏しくなりやすい。例えばアセトンのような溶解性の高い溶剤を使用した場合には、沸点が低く且つ外気の水を取り込みやすいため、水とイソシアネートとの反応によって該接着剤樹脂組成物の粘度が上昇しやすいといった問題が発生することがある。 For example, when a highly polar solvent is used in the adhesive resin composition, workability tends to be poor. For example, when a highly soluble solvent such as acetone is used, the problem is that the viscosity of the adhesive resin composition tends to increase due to the reaction between water and isocyanate because it has a low boiling point and easily incorporates water from the outside air. may occur.
また、ガスバリア性有機接着剤層（Ｂ）に溶剤が多量に含有されていると、溶剤によって積層体の層間の接着が弱まることが懸念され、更には、得られた積層体を用いた包装材料で作製した包装体において、内容物に溶剤臭が移ることが懸念される。また更には、乾燥時の体積収縮の為に、ガスバリア無機蒸着層（Ｃ）表面に生じている凹凸の凹部に埋め込まれているガスバリア性有機接着剤層（Ｂ）が剥離して欠陥が生じることでガスバリア性の低下を生じ易く、積層体を折り曲げた際にも凹部からの剥離が大きくなり、ガスバリア性が劣化することにつながりやすい。
よって、本発明においては、溶剤を用いないことが好ましい。
Furthermore, if the gas barrier organic adhesive layer (B) contains a large amount of solvent, there is a concern that the solvent may weaken the adhesion between the layers of the laminate, and furthermore, packaging materials using the obtained laminate may There is a concern that the solvent odor may transfer to the contents of the package made with. Furthermore, due to volumetric shrinkage during drying, the gas barrier organic adhesive layer (B) embedded in the uneven concavities occurring on the surface of the gas barrier inorganic vapor deposited layer (C) may peel off, resulting in defects. This tends to cause a decrease in gas barrier properties, and even when the laminate is folded, peeling from the recesses increases, which tends to lead to deterioration of gas barrier properties.
Therefore, in the present invention, it is preferable not to use a solvent.
（板状無機化合物（Ｍ））
板状無機化合物（Ｍ）は、ガスバリア性有機接着剤層（Ｂ）のラミネート強度とガスバリア性を向上させる効果を有する。
板状無機化合物（Ｍ）としては、具体的には、カオリナイト－蛇紋族粘土鉱物（ハロイサイト、カオリナイト、エンデライト、ディッカイト、ナクライト等、アンチゴライト、クリソタイル等）、パイロフィライト－タルク族（パイロフィライト、タルク、ケロライ
等）等が挙げられ、これらの１種または２種以上を用いることができる。
(Plate-shaped inorganic compound (M))
The plate-like inorganic compound (M) has the effect of improving the lamination strength and gas barrier properties of the gas barrier organic adhesive layer (B).
Specifically, the platy inorganic compound (M) includes kaolinite-serpentine clay minerals (halloysite, kaolinite, endellite, dickite, nacrite, etc., antigorite, chrysotile, etc.), pyrophyllite-talc group (pyrophyllite, talc, kerolae, etc.), and one or more of these can be used.
（多価カルボン酸変性ポリエステルポリオール（Ｎ））
多価カルボン酸変性ポリエステルポリオール（Ｎ）は、１分子内に１個または２個以上のカルボキシル基と２個以上の水酸基を有する化合物である。
多価カルボン酸変性ポリエステルポリオール（Ｎ）は、例えば、１分子内に３個以上の水酸基を有するポリエステルポリオールの水酸基の一部に、多価カルボン酸類を反応させることにより得ることができる。
(Polycarboxylic acid-modified polyester polyol (N))
The polycarboxylic acid-modified polyester polyol (N) is a compound having one or more carboxyl groups and two or more hydroxyl groups in one molecule.
The polycarboxylic acid-modified polyester polyol (N) can be obtained, for example, by reacting a part of the hydroxyl groups of a polyester polyol having three or more hydroxyl groups in one molecule with a polycarboxylic acid.
［ガスバリア無機蒸着層（Ｃ）］
ガスバリア無機蒸着層（Ｃ）は、酸素ガスおよび水蒸気等の透過を防ぐガスバリア性を有するバリア膜であり、無機物または無機酸化物からなる蒸着膜が挙げられる。
[Gas barrier inorganic vapor deposited layer (C)]
The gas barrier inorganic vapor deposited layer (C) is a barrier film having gas barrier properties that prevents permeation of oxygen gas, water vapor, etc., and includes a vapor deposited film made of an inorganic substance or an inorganic oxide.
一般的に、無機蒸着層表面には超微細な凹凸が生じており、超微細レベルでは、無機蒸着層の厚みは均一では無く、薄い部分は面方向のガスバリア性が弱い。 Generally, the surface of an inorganic vapor deposition layer has ultra-fine irregularities, and at the ultra-fine level, the thickness of the inorganic vapor deposition layer is not uniform, and the thinner parts have poor gas barrier properties in the surface direction.
しかし、本発明の積層体は、ガスバリア無機蒸着層（Ｃ）とガスバリア性有機接着剤層（Ｂ）とが隣接した構成を有することで、ガスバリア無機蒸着層（Ｃ）表面に生じている超微細な凹凸の凹部がガスバリア性を有するガスバリア性有機接着剤層（Ｂ）により埋められて平坦化された構造を有することで、面方向のガスバリア性が均一化され、ガスバリア無機蒸着層（Ｃ）の層厚を薄くして耐屈曲性を保持しつつ、従来以上の高いガスバリア性を発揮することができる。 However, the laminate of the present invention has a structure in which the gas barrier inorganic vapor deposited layer (C) and the gas barrier organic adhesive layer (B) are adjacent to each other. By having a structure in which the uneven concave portions are filled and flattened by the gas barrier organic adhesive layer (B) having gas barrier properties, the gas barrier property in the plane direction is made uniform, and the gas barrier inorganic vapor deposited layer (C) has a flat structure. By reducing the layer thickness, it is possible to maintain bending resistance while exhibiting higher gas barrier properties than before.
ガスバリア無機蒸着層（Ｃ）は、アルミニウム蒸着層、アルミナ蒸着層、及び、シリカ蒸着層、からなる群から選ばれる１種または２種以上を有する層であることが好ましく、特に、アルミニウム蒸着層を有することが好ましい。 The gas barrier inorganic vapor deposited layer (C) is preferably a layer having one or more selected from the group consisting of an aluminum vapor deposited layer, an alumina vapor deposited layer, and a silica vapor deposited layer. It is preferable to have.
ガスバリア無機蒸着層（Ｃ）は、易開封性シーラント層（Ｄ）上に直接、ガスバリア性有機接着剤層（Ｂ）等の接着層を介さずに設けることができる。 The gas barrier inorganic vapor deposited layer (C) can be provided directly on the easily openable sealant layer (D) without intervening an adhesive layer such as the gas barrier organic adhesive layer (B).
更に、必要に応じて、可視光および紫外線等の透過を阻止する遮光性を付与することもできる。また、ガスバリア無機蒸着層（Ｃ）は１層または２層以上で構成されていてもよい。２層以上で構成される場合は、それぞれが同一の組成であってもよいし、異なる組成であってもよい。 Furthermore, if necessary, light-shielding properties that block the transmission of visible light, ultraviolet rays, etc. can also be provided. Further, the gas barrier inorganic vapor deposited layer (C) may be composed of one layer or two or more layers. When composed of two or more layers, each layer may have the same composition or different compositions.
ガスバリア無機蒸着層（Ｃ）の厚さは、好ましくは１～２００ｎｍであり、更に好ましい厚みは蒸着種によって異なるが、アルミニウム蒸着膜の場合には、更に好ましくは１～１００ｎｍであり、また更に好ましくは１５～６０ｎｍであり、特に好ましくは１０～４０ｎｍである。ケイ素酸化物またはアルミナ蒸着膜の場合には、更に好ましくは１～１００ｎｍであり、また更に好ましくは１０～５０ｎｍであり、特に好ましくは２０～３０ｎｍである。 The thickness of the gas barrier inorganic vapor deposition layer (C) is preferably 1 to 200 nm, and the more preferred thickness varies depending on the type of vapor deposition. In the case of an aluminum vapor deposition film, the more preferred thickness is 1 to 100 nm, more preferably 15 to 60 nm, and particularly preferably 10 to 40 nm. In the case of a silicon oxide or alumina vapor deposition film, the more preferred thickness is 1 to 100 nm, more preferably 10 to 50 nm, and particularly preferably 20 to 30 nm.
ガスバリア無機蒸着層（Ｃ）は、従来公知の無機物または無機酸化物を用いて、従来公知の方法により形成することができ、その組成および形成方法は特に限定されない。 The gas barrier inorganic vapor deposition layer (C) can be formed by a conventionally known method using a conventionally known inorganic substance or inorganic oxide, and its composition and formation method are not particularly limited.
形成方法としては、例えば、真空蒸着法、スパッタリング法、およびイオンプレーティング法等の物理気相成長法（ＰｈｙｓｉｃａｌＶａｐｏｒＤｅｐｏｓｉｔｉｏｎ法、ＰＶＤ法）、あるいは、プラズマ化学気相成長法、熱化学気相成長法、および光化学気相成長法等の化学気相成長法（ＣｈｅｍｉｃａｌＶａｐｏｒＤｅｐｏｓｉｔｉｏｎ法、ＣＶＤ法）等を挙げることができる。 Examples of the formation method include a physical vapor deposition method (PVD method) such as a vacuum evaporation method, a sputtering method, and an ion plating method, or a plasma chemical vapor deposition method, a thermochemical vapor deposition method, and a chemical vapor deposition method (CVD method) such as a photochemical vapor deposition method.
本発明において、ガスバリア無機蒸着層（Ｃ）は、易開封性シーラント層（Ｄ）の、ガスバリア性有機接着剤層（Ｂ）側の表面に設けることができる。 In the present invention, the gas barrier inorganic vapor deposited layer (C) can be provided on the surface of the easily openable sealant layer (D) on the gas barrier organic adhesive layer (B) side.
また、その際に、易開封性シーラント層（Ｄ）表面に必要に応じて前処理が可能であり、具体的には、コロナ放電処理、オゾン処理、酸素ガス若しくは窒素ガス等を用いた低温プラズマ処理、グロー放電処理などの物理的な処理や、化学薬品などを用いて処理する酸化処理などの化学的な処理を施してもよい。 In addition, at that time, the surface of the easy-open sealant layer (D) can be pretreated if necessary, and specifically, corona discharge treatment, ozone treatment, low-temperature plasma using oxygen gas or nitrogen gas, etc. A physical treatment such as a glow discharge treatment or a chemical treatment such as an oxidation treatment using chemicals or the like may be performed.
また更に、酸素ガスおよび水蒸気等に対するガスバリア性を更に高めるために、ガスバリア無機蒸着層（Ｃ）と同様なガスバリア無機蒸着層を、基材層（Ａ）の、ガスバリア性有機接着剤層（Ｂ）と接する側にも設けることができる。前処理、蒸着種、蒸着膜形成方法等は、ガスバリア無機蒸着層（Ｃ）と同様である。 Furthermore, in order to further improve the gas barrier properties against oxygen gas, water vapor, etc., a gas barrier inorganic vapor deposition layer similar to the gas barrier inorganic vapor deposition layer (C) can also be provided on the side of the base layer (A) that contacts the gas barrier organic adhesive layer (B). The pretreatment, vapor deposition species, vapor deposition film formation method, etc. are the same as for the gas barrier inorganic vapor deposition layer (C).
［易開封性シーラント層（Ｄ）（ヒートシール層）］
易開封性シーラント層（Ｄ）は、本発明に係る積層体及び該積層体からなる包装材料にヒートシール性と耐屈曲性、耐衝撃性等の機能を付与するものであり、特に耐屈曲性を付与することで屈曲後のガスバリア性の低下を抑制することができるものが望ましい。
そして更に、本発明においては、易開封性シーラント層（Ｄ）には、易開封性を付与するために、イージーピールフィルムが用いられる。
[Easy-open sealant layer (D) (heat seal layer)]
The easy-open sealant layer (D) imparts functions such as heat-sealability, bending resistance, and impact resistance to the laminate according to the present invention and the packaging material made of the laminate. It is desirable to be able to suppress the deterioration of gas barrier properties after bending by adding .
Furthermore, in the present invention, an easy-peel film is used in the easy-open sealant layer (D) in order to impart easy-openability.
イージーピールフィルムとしては、界面剥離タイプ、凝集剥離タイプ、層間剥離タイプの何れでも適用可能であり、包装体の種類や要求特性に応じて適宜選択して用いることができる。 As the easy-peel film, any of interfacial peeling type, cohesive peeling type, and interlayer peeling type can be used, and can be appropriately selected and used depending on the type of package and required characteristics.
易開封性の指標としては、該包装体のシール強度は２～２０Ｎ／１５ｍｍの範囲であることが好ましく、該範囲のシール強度を与えることが可能なイージーピールフィルムが用いられる。 As an indicator of ease of opening, the seal strength of the package is preferably in the range of 2 to 20 N/15 mm, and an easy-peel film that can provide the seal strength within this range is used.
本発明においては、易開封性シーラント層（Ｄ）は、ヒートシール性の樹脂層を有することが望ましい。ヒートシール性の樹脂層は、熱によって溶融し相互に融着し得るものであればよい。 In the present invention, it is desirable that the easy-open sealant layer (D) has a heat-sealable resin layer. The heat-sealable resin layer may be any material as long as it can be melted by heat and fused to each other.
易開封性シーラント層（Ｄ）に好適な樹脂としては、例えば、ポリエチレン、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖状（線状）低密度ポリエチレン、メタロセンポリエチレン、ポリプロピレン、エチレン－酢酸ビニル共重合体、アイオノマー樹脂、エチレン－（メタ）アクリル酸エチル共重合体、エチレン－（メタ）アクリル酸共重合体、エチレン－プロピレン共重合体、メチルペンテンポリマー、ポリエチレンまたはポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタクリル酸、無水マレイン酸、フマル酸その他等の不飽和カルボン酸で変性したポリオレフィン系樹脂、エチレン－（メタ）アクリル酸エステル－不飽和カルボン酸の三元共重合体樹脂、環状ポリオレフィン樹脂、環状オレフィンコポリマー、ポリエチレンテレフタレート（ＰＥＴ）、ポリアクリロニトリル（ＰＡＮ）などが挙げられ、これらの樹脂の１種または２種以上からなる樹脂のフィルムないしシートあるいはその他塗布膜等を使用することができる。 Examples of resins suitable for the easy-open sealant layer (D) include polyethylene, low-density polyethylene, medium-density polyethylene, high-density polyethylene, linear low-density polyethylene, metallocene polyethylene, polypropylene, and ethylene-acetic acid. Polyolefin resins such as vinyl copolymers, ionomer resins, ethylene-ethyl (meth)acrylate copolymers, ethylene-(meth)acrylic acid copolymers, ethylene-propylene copolymers, methylpentene polymers, polyethylene or polypropylene polyolefin resins modified with unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, etc., terpolymer resins of ethylene-(meth)acrylic acid ester-unsaturated carboxylic acids, and cyclic polyolefins. Examples include resins, cyclic olefin copolymers, polyethylene terephthalate (PET), polyacrylonitrile (PAN), etc., and resin films or sheets or other coating films made of one or more of these resins can be used. .
上記の樹脂層を形成するフィルムないしシートとしては、未延伸フィルムないしシート、あるいは１軸方向または２軸方向に延伸した延伸フィルムないしシート等のいずれのものでも使用することができる。 As the film or sheet forming the above-mentioned resin layer, any one of unstretched film or sheet, uniaxially or biaxially stretched stretched film or sheet, etc. can be used.
２軸方向に延伸した延伸フィルムは、例えば５０～１００℃のロール延伸機により２～
４倍に縦延伸し、更に９０～１５０℃の雰囲気のテンター延伸機により３～５倍に横延伸せしめ、引き続いて同テンターにより１００～２４０℃雰囲気中で熱処理して得ることができる。また、延伸フィルムは、同時二軸延伸、逐次二軸延伸をしても良い。
The stretched film stretched in two axial directions is, for example, 2 to 100°C by a roll stretching machine at 50 to 100°C.
It can be obtained by longitudinally stretching 4 times, further horizontally stretching 3 to 5 times in a tenter stretching machine in an atmosphere of 90 to 150°C, and then heat-treating in the same tenter in an atmosphere of 100 to 240°C. Further, the stretched film may be subjected to simultaneous biaxial stretching or sequential biaxial stretching.
易開封性シーラント層（Ｄ）の層構成としては、ポリエチレン／ポリプロピレン＆ポリエチレンの混合物／ポリプロピレンの多層フィルムが好適である。また、アルミニウム膜をヒートシール可能な無延伸ポリプロピレン（ＣＰＰ）、低密度ポリエチレン、直鎖状低密度ポリエチレンに蒸着したフィルムを用いることもできる。
上記の樹脂には、必要に応じて、公知の耐屈曲性改良剤、無機又は有機添加剤等を配合することができる。
本発明においては、上記のような諸条件を充足する材料を任意に使用することができる。
The layer structure of the easily openable sealant layer (D) is preferably a multilayer film of polyethylene/a mixture of polypropylene and polyethylene/polypropylene. Alternatively, a film in which an aluminum film is deposited on heat-sealable unstretched polypropylene (CPP), low-density polyethylene, or linear low-density polyethylene can also be used.
The above-mentioned resin may be blended with a known flex resistance improver, inorganic or organic additives, etc., if necessary.
In the present invention, any material that satisfies the above conditions can be used.
（易開封性シーラント層（Ｄ）の膜厚）
易開封性シーラント層（Ｄ）の厚さは、任意に選択し得るが、包装材料としての強度等の観点から、５～５００μｍ位の範囲から選択して使用することができ、好ましくは１０～２５０μｍ、更に好ましくは１５～１００μｍの範囲である。これより薄いとヒートシールしても充分なラミネート強度が得られず、包装材料としては機能しないし耐突き刺し性等が抵下する。また、これより厚いと、コスト上昇を招くと共にフィルムが硬くなり作業性が悪くなる。
(Thickness of easy-open sealant layer (D))
The thickness of the easy-open sealant layer (D) can be selected arbitrarily, but from the viewpoint of strength as a packaging material, it can be selected from the range of about 5 to 500 μm, preferably 10 to 250 μm, more preferably 15 to 100 μm. If it is thinner than this, sufficient laminate strength cannot be obtained even if it is heat sealed, it does not function as a packaging material, and puncture resistance etc. is reduced. Moreover, if it is thicker than this, it will lead to an increase in cost and the film will become hard, resulting in poor workability.
［ガスバリア塗布膜層（Ｅ）］
本発明においては、基材層（Ａ）とガスバリア性有機接着剤層（Ｂ）との間に、酸素ガスおよび水蒸気等のガスへのバリア性を高めるために、更に、ガスバリア塗布膜層（Ｅ）を設けることができる。ガスバリア塗布膜層（Ｅ）は、基材層（Ａ）に積層されたガスバリア無機蒸着層の上に設けられてもよい。
ガスバリア塗布膜層（Ｅ）は、金属アルコキシドと水溶性高分子とを含む樹脂組成物から、ゾルゲル法触媒、水及び有機溶剤等の存在下で生成された、ゾルゲル法加水分解重縮合物を含有する層であることが好ましい。
[Gas barrier coating layer (E)]
In the present invention, a gas barrier coating layer (E ) can be provided. The gas barrier coating layer (E) may be provided on the gas barrier inorganic vapor deposited layer laminated on the base layer (A).
The gas barrier coating layer (E) contains a sol-gel hydrolysis polycondensate produced from a resin composition containing a metal alkoxide and a water-soluble polymer in the presence of a sol-gel catalyst, water, an organic solvent, etc. It is preferable that the layer is
金属アルコキシドとしては、下記一般式で表される、１種または２種以上を好ましく用いることができる。
Ｒ1
nＭ（ＯＲ2）m
（ただし、式中、Ｒ1、Ｒ2は、炭素数１～８の有機基を表し、Ｍは金属原子を表し、ｎは０以上の整数を表し、ｍは１以上の整数を表し、ｎ＋ｍはＭの原子価を表す。）
ここで、金属原子Ｍとしては、珪素、ジルコニウム、チタン、アルミニウムその他を使用することができる。また、Ｒ1及びＲ2で表される有機基の具体例としては、例えば、メチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基等のアルキル基を挙げることができる。同一分子中において、これらのアルキル基は同一であっても、異なってもよい。
As the metal alkoxide, one or more kinds represented by the following general formula can be preferably used.
R 1 n M (OR 2 ) m
(However, in the formula, R 1 and R 2 represent an organic group having 1 to 8 carbon atoms, M represents a metal atom, n represents an integer of 0 or more, m represents an integer of 1 or more, and n+m represents the valence of M.)
Here, as the metal atom M, silicon, zirconium, titanium, aluminum, or the like can be used. Further, specific examples of the organic groups represented by R 1 and R 2 include alkyl groups such as methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, and i-butyl group. can be mentioned. In the same molecule, these alkyl groups may be the same or different.
このような金属アルコキシドとしては、例えば、テトラメトキシシランＳｉ（ＯＣＨ3）4、テトラエトキシシランＳｉ（ＯＣ2Ｈ5）4、テトラプロポキシシランＳｉ（ＯＣ3Ｈ7）4、テトラブトキシシランＳｉ（ＯＣ4Ｈ9）4等、及び、有機物と結合する官能基を有するシランカップリング剤が挙げられる。
金属アルコキシドは、１種ないし２種以上を混合して用いてもよい。
Examples of such metal alkoxides include tetramethoxysilane Si(OCH 3 ) 4 , tetraethoxysilane Si(OC 2 H 5 ) 4 , tetrapropoxysilane Si(OC 3 H 7 ) 4 , and tetrabutoxysilane Si(OC 4H9 ) 4 , etc., and silane coupling agents having a functional group that binds to an organic substance.
The metal alkoxides may be used alone or in combination of two or more.
シランカップリング剤としては、既知の有機反応性基含有オルガノアルコキシシランを用いることができるが、特に、エポキシ基を有するオルガノアルコキシシランが好適であり、例えば、γ－グリシドキシプロピルトリメトキシシラン、γ－グリシドキシプロピル
メチルジエトキシシラン、あるいは、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等を用いることができる。
As the silane coupling agent, known organoalkoxysilanes containing organic reactive groups can be used, but organoalkoxysilanes having epoxy groups are particularly suitable, such as γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, etc. can be used.
上記のようなシランカップリング剤は、１種ないし２種以上を混合して用いてもよい。本発明において、上記のようなシランカップリング剤は、上記のアルコキシドの合計量１００質量部に対して１～２０質量部程度の範囲内で含有することができる。 The above silane coupling agents may be used alone or in combination of two or more. In the present invention, the above-mentioned silane coupling agent can be contained within a range of about 1 to 20 parts by mass based on 100 parts by mass of the total amount of the alkoxides.
水溶性高分子としては、ポリビニルアルコール系樹脂若しくはエチレン・ビニルアルコール共重合体のいずれか又はその両方を好ましく用いることができる。これら樹脂は市販のものを用いてもよく、例えばエチレン・ビニルアルコール共重合体としては、株式会社クラレ製、エバールＥＰ－Ｆ１０１（エチレン含量；３２モル％）、日本合成化学工業株式会社製、ソアノールＤ２９０８（エチレン含量；２９モル％）等を用いることができる。 As the water-soluble polymer, polyvinyl alcohol resin, ethylene-vinyl alcohol copolymer, or both can preferably be used. Commercially available resins may be used as these resins. For example, examples of the ethylene/vinyl alcohol copolymer include Eval EP-F101 (ethylene content: 32 mol%) manufactured by Kuraray Co., Ltd., and Soarnol manufactured by Nippon Gosei Kagaku Kogyo Co., Ltd. D2908 (ethylene content: 29 mol%) and the like can be used.
また、ポリビニルアルコール系樹脂としては、株式会社クラレ製のＲＳポリマーであるＲＳ－１１０（ケン化度＝９９％、重合度＝１，０００）、同社製のクラレポバールＬＭ－２０ＳＯ（ケン化度＝４０％、重合度＝２，０００）、日本合成化学工業株式会社製のゴーセノールＮＭ－１４（ケン化度＝９９％、重合度＝１，４００）等を用いることができる。 As polyvinyl alcohol-based resins, RS polymer RS-110 (saponification degree = 99%, polymerization degree = 1,000) manufactured by Kuraray Co., Ltd., Kuraray Poval LM-20SO (saponification degree = 40%, polymerization degree = 2,000) manufactured by the same company, and Gohsenol NM-14 (saponification degree = 99%, polymerization degree = 1,400) manufactured by Nippon Synthetic Chemical Industry Co., Ltd. can be used.
水溶性高分子の含有量は、金属アルコキシド１００質量部に対して５～５００質量部の範囲であることが好ましい。５質量部より少ないと、ガスバリア塗布膜層（Ｅ）の製膜性が劣って脆性が大きくなり、耐侯性等も低下する傾向になり、５００質量部を越えると、ガスバリア性向上効果が低くなる傾向になる。 The content of the water-soluble polymer is preferably in the range of 5 to 500 parts by weight per 100 parts by weight of the metal alkoxide. If it is less than 5 parts by mass, the gas barrier coating layer (E) will have poor film formability and become brittle, and its weather resistance will tend to decrease, and if it exceeds 500 parts by mass, the effect of improving gas barrier properties will decrease. become a trend.
ゾルゲル法触媒としては、酸またはアミン系化合物が好適である。
アミン系化合物としては、水に実質的に不溶であり、且つ有機溶媒に可溶な第３級アミンが好適である。具体的には、例えば、Ｎ，Ｎ－ジメチルベンジルアミン、トリプロピルアミン、トリブチルアミン、トリペンチルアミン等を使用することができる。特に、Ｎ，Ｎ－ジメチルべンジルアミンが好適であり、金属アルコキシド１００質量部当り、例えば０．０１～１．０質量部、特に０．０３～０．３質量部を含有することが好ましい。０．０１質量部よりも少ないと触媒効果が小さすぎ、１．０質量部よりも多いと触媒効果が強すぎて反応速度が速くなり過ぎ、不均一になり易い傾向になる。
As the sol-gel method catalyst, acid or amine compounds are suitable.
As the amine compound, tertiary amines that are substantially insoluble in water and soluble in organic solvents are preferred. Specifically, for example, N,N-dimethylbenzylamine, tripropylamine, tributylamine, tripentylamine, etc. can be used. Particularly suitable is N,N-dimethylbenzylamine, and it is preferably contained in an amount of, for example, 0.01 to 1.0 parts by weight, particularly 0.03 to 0.3 parts by weight, per 100 parts by weight of metal alkoxide. If it is less than 0.01 parts by mass, the catalytic effect will be too small, and if it is more than 1.0 parts by mass, the catalytic effect will be too strong and the reaction rate will be too fast, tending to become non-uniform.
酸としては、例えば、硫酸、塩酸、硝酸などの鉱酸、ならびに、酢酸、酒石酸な等の有機酸等を用いることができる。酸の含有量は、金属アルコキシドのアルコキシ基の総モル量に対して、好ましくは０．００１～０．０５モルであり、より好ましくは０．０１～０．０３モルである。０．００１モルよりも少ないと触媒効果が小さすぎ、０．０５モル部よりも多いと触媒効果が強すぎて反応速度が速くなり過ぎ、不均一になり易い傾向になる。 As the acid, for example, mineral acids such as sulfuric acid, hydrochloric acid, and nitric acid, and organic acids such as acetic acid and tartaric acid can be used. The acid content is preferably 0.001 to 0.05 mol, more preferably 0.01 to 0.03 mol, based on the total molar amount of alkoxy groups in the metal alkoxide. If it is less than 0.001 mole, the catalytic effect will be too small, and if it is more than 0.05 mole part, the catalytic effect will be too strong and the reaction rate will be too fast, tending to become non-uniform.
有機溶媒としては、メチルアルコール、エチルアルコール、ｎ－プロピルアルコール、イソプロピルアルコール、ｎ－ブタノール等を用いることができる。 As the organic solvent, methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butanol, etc. can be used.
ガスバリア塗布膜層（Ｅ）は、該樹脂組成物からなる塗工液を、通常用いられる、グラビアロールコーターなどのロールコート、スプレーコート、スピンコート、ディッピング、刷毛、バーコード、アプリケータ等の従来公知の手段により、１回あるいは複数回塗布して形成される。 The gas barrier coating layer (E) is coated with a coating liquid made of the resin composition using a conventional method such as roll coating such as a gravure roll coater, spray coating, spin coating, dipping, brush coating, barcode coating, applicator, etc. It is formed by coating once or multiple times by known means.
ガスバリア塗布膜層（Ｅ）の形成方法の具体例について以下に説明する。 A specific example of the method for forming the gas barrier coating layer (E) will be described below.
まず、金属アルコキシド、水溶性高分子、ゾルゲル法触媒、水、有機溶媒、および、必要に応じてシランカップリング剤等を混合して、樹脂組成物から成る塗工液を調製する。該塗工液中では次第に重縮合反応が進行する。 First, a coating liquid consisting of a resin composition is prepared by mixing a metal alkoxide, a water-soluble polymer, a sol-gel method catalyst, water, an organic solvent, and, if necessary, a silane coupling agent. A polycondensation reaction gradually proceeds in the coating liquid.
次いで、基材層（Ａ）に積層されたガスバリア無機蒸着層の上に、常法により、該塗工液を通常の方法で塗布し、乾燥する。乾燥により、上記アルコキシドおよびビニルアルコールポリマー（およびシランカップリング剤）の重縮合がさらに進行し、複合ポリマーの層が形成される。好適には、上記の操作を繰り返して、複数の複合ポリマー層を積層することもできる。 Next, the coating liquid is applied in a conventional manner onto the gas barrier inorganic vapor-deposited layer laminated on the base layer (A) and dried. By drying, the polycondensation of the alkoxide and vinyl alcohol polymer (and silane coupling agent) further proceeds to form a composite polymer layer. Preferably, a plurality of composite polymer layers can be laminated by repeating the above operation.
最後に、該塗工液を塗布した積層体を２０～２５０℃、好ましくは５０～２２０℃の温度で、１秒～１０分間加熱する。これにより、ガスバリア無機蒸着層上にガスバリア塗布膜層（Ｅ）を形成することができる。 Finally, the laminate coated with the coating liquid is heated at a temperature of 20 to 250°C, preferably 50 to 220°C, for 1 second to 10 minutes. Thereby, a gas barrier coating layer (E) can be formed on the gas barrier inorganic vapor deposited layer.
ガスバリア塗布膜層（Ｅ）は、１層または２層以上を重層した複合ポリマー層であってよい。また、乾燥後のガスバリア塗布膜層（Ｅ）の厚さは０．０１～１００μｍの範囲が好ましく、更に好ましくは０．１～５０μｍである。乾燥後の厚さが０．０１μｍより小さいとガスバリア性の向上は小さすぎ、１００μｍより大きいと、クラックが発生しやすくなる。 The gas barrier coating layer (E) may be one layer or a composite polymer layer consisting of two or more layers. Further, the thickness of the gas barrier coating layer (E) after drying is preferably in the range of 0.01 to 100 μm, more preferably 0.1 to 50 μm. If the thickness after drying is smaller than 0.01 μm, the improvement in gas barrier properties is too small, and if it is larger than 100 μm, cracks are likely to occur.
［印刷層（Ｆ）］
印刷層（Ｆ）は、水性フレキソ印刷層および／または水性グラビア印刷層を含むことができ、印刷絵柄としては、文字、図形、記号、その他の所望の絵柄を、任意に形成することができる。
[Printing layer (F)]
The printing layer (F) can include an aqueous flexographic printing layer and/or an aqueous gravure printing layer, and as the printed pattern, letters, figures, symbols, and other desired patterns can be arbitrarily formed.
水性フレキソ印刷層および／または水性グラビア印刷層を含むことによって、油性フレキソ印刷層や油性グラビア印刷層を含む場合よりも、印刷層（Ｆ）中の溶剤残存量を低減することで積層体の溶剤含有量を低減でき、包装体内容物への溶剤臭転移を低く抑えることができる。 By including an aqueous flexographic printing layer and/or an aqueous gravure printing layer, the amount of solvent remaining in the printing layer (F) is reduced compared to when an oil-based flexographic printing layer or an oil-based gravure printing layer is included. The content can be reduced, and the transfer of solvent odor to the contents of the package can be suppressed to a low level.
水性グラビア印刷とは、一般的に凹版印刷に区分される印刷方式である。先ず、版に水性インキを転移し、ドクターブレードで版の表面の水性インキをそぎ落とした後に、印刷する印刷対象フィルムと版を接着させ、印刷対象フィルムの上から圧力をかけ凹版部分に残った水性インキを基材に転移させ、乾燥させることで印刷物が得られる。 Water-based gravure printing is a printing method that is generally classified as intaglio printing. First, water-based ink is transferred to the plate, and after scraping off the water-based ink on the surface of the plate with a doctor blade, the film to be printed and the plate are adhered, and pressure is applied from above the film to be printed so that the ink remaining on the intaglio area is removed. Printed matter is obtained by transferring the water-based ink to the substrate and drying it.
グラビア印刷の版は、凹版部の深さや形状の自由度が高く、水性インキの転移量を幅広く調節することが可能であり、細かい濃淡の表現を再現することに優れ、鮮やかな印刷絵柄を得ることに優れている。 Gravure printing plates have a high degree of freedom in the depth and shape of the intaglio area, making it possible to adjust the amount of water-based ink transfer over a wide range, and are excellent at reproducing fine shading to produce vivid printed patterns. Especially excellent.
印刷対象フィルムはロール巻き状のものを使用可能であり、印刷後もロール巻き状で保管でき、印刷変動要因が少なく、版の耐久性が高いことから、大ロットを安定稼働させて印刷できる。 Rolled film can be used for printing, and it can be stored in a rolled form even after printing, there are few printing fluctuation factors, and the plate is highly durable, making it possible to print large lots with stable operation.
水性グラビア印刷は希釈溶剤として水およびアルコールを用いる為、溶剤臭を低減した印刷層とすることができる。 Since water-based gravure printing uses water and alcohol as diluting solvents, it is possible to produce a printed layer with reduced solvent odor.
水性フレキソ印刷とは、凸版印刷の１種である。先ず、樹脂でできた版の凸部にアニロックスロールを介して水性インキを付着し、印刷対象フィルムに転移させることで印刷物が得られる。 Water-based flexographic printing is a type of letterpress printing. First, water-based ink is applied to the convex portions of a resin plate via an anilox roll and transferred to the film to be printed, thereby obtaining printed matter.
フレキソ印刷は凸版印刷であるため、グラビア印刷と比較して、細かい文字やシャープな表現を再現することに優れ、平滑性の低い印刷対象フィルムに印刷する事にも適している。さらに、インキの使用量が少なく、乾燥風量が少ないことから、エネルギー消費量が少なく、エコロジカルである。 Since flexographic printing is letterpress printing, it is superior to gravure printing in reproducing fine text and sharp expressions, and is also suitable for printing on films with low smoothness. Furthermore, since the amount of ink used is small and the amount of drying air is small, energy consumption is low and it is ecological.
フレキソ印刷はインキ使用量が少ない為、印刷層に残留する溶剤臭を低減することができる。また、水性フレキソインキを用いることで、さらに溶剤臭を低減することができる。 Since flexographic printing uses less ink, it is possible to reduce the odor of solvents remaining in the printed layer. Furthermore, by using water-based flexographic ink, solvent odor can be further reduced.
本発明に係る積層体の一態様として、印刷層（Ｆ）を、ガスバリア性有機接着剤層（Ｂ）と隣接して設けることも可能である。例えば、基材層（Ａ）とガスバリア性有機接着剤層（Ｂ）との間に、特に例えば、図２に示すように、ガスバリア塗布膜層（Ｅ）とガスバリア性有機接着剤層（Ｂ）との間に設けることができる。 As one embodiment of the laminate according to the present invention, it is also possible to provide the printed layer (F) adjacent to the gas barrier organic adhesive layer (B). For example, between the base material layer (A) and the gas barrier organic adhesive layer (B), for example, as shown in FIG. It can be provided between.
［積層体および該積層体からなる包装材料］
積層体中の溶剤含有量は、ゼロまたは６ｍｇ／ｍ2以下である。上記範囲よりも多量に含有されていると、該積層体を用いた包装材料で作製した包装体において、内容物に溶剤臭が移るおそれがある。
[Laminated body and packaging material made of the laminate]
The solvent content in the laminate is zero or less than 6 mg/m 2 . If the content is greater than the above range, there is a risk that a solvent odor will be transferred to the contents in a package made from a packaging material using the laminate.
さらには、溶剤によって積層体の層間の接着が弱まるおそれがあり、乾燥時の体積収縮の為に、ガスバリア無機蒸着層（Ｃ）表面に生じている凹凸の凹部に埋め込まれているガスバリア性有機接着剤層（Ｂ）が剥離して欠陥が生じることでガスバリア性の低下を生じ易く、積層体を折り曲げた際にも凹部からの剥離が大きくなり、ガスバリア性が劣化することにつながりやすい。 Furthermore, there is a risk that the adhesion between the layers of the laminate may be weakened by the solvent, and due to volumetric shrinkage during drying, the gas barrier organic adhesive is embedded in the uneven recesses that occur on the surface of the gas barrier inorganic vapor deposited layer (C). The agent layer (B) peels off and causes defects, which tends to cause a decrease in gas barrier properties, and when the laminate is bent, the peeling from the recesses increases, which tends to lead to deterioration of gas barrier properties.
従来の積層体においては、十分なガスバリア性を得る為には、ＡＣ（アンカーコート）層や金属蒸着層等を含めると、総構成層数に８層程度以上が必要であり、そのために製造工程が長く、複雑化していたが、本発明に係る積層体は、総構成層数を従来よりも少なくすることが可能であり、６層以下で従来と同等以上のガスバリア性を発現することが可能である。 In conventional laminates, in order to obtain sufficient gas barrier properties, the total number of constituent layers must be approximately 8 or more, including the AC (anchor coat) layer, metal vapor deposition layer, etc., and for this purpose, the manufacturing process However, the laminate according to the present invention can reduce the total number of constituent layers compared to the conventional one, and can exhibit gas barrier properties equivalent to or better than the conventional one with six or fewer layers. It is.
７層以上の構成にすることも可能であり、相対的に従来材よりも少ない総構成層数で同等以上のガスバリア性を発現することが可能である。また、総構成層数が少なく、無機蒸着層を薄くできることで、工程を短縮して簡略化でき、積層体を薄くすることが可能であり、積層体の柔軟性が向上して、耐屈曲性が向上する。 It is also possible to have a structure with seven or more layers, and it is possible to exhibit gas barrier properties of the same or better quality with a relatively smaller total number of constituent layers than conventional materials. In addition, since the total number of constituent layers is small and the inorganic vapor deposited layer can be made thinner, the process can be shortened and simplified, making it possible to make the laminate thinner, improving the flexibility of the laminate and improving its bending resistance. will improve.
本発明に係る積層体および該積層体からなる包装材料は、図１のように、印刷層（Ｆ）が設けられた基材層（Ａ）の印刷層（Ｆ）面と、隣接して積層されているガスバリア無機蒸着層（Ｃ）と易開封性シーラント層（Ｄ）のガスバリア無機蒸着層（Ｃ）面とを、ガスバリア性有機接着剤層（Ｂ）を介してラミネートされていることができる。また、図２のように、印刷層（Ｆ）は、ガスバリア塗布膜層（Ｅ）上に設けられていてもよい。 As shown in FIG. 1, the laminate according to the present invention and the packaging material made of the laminate are laminated adjacent to the printed layer (F) surface of the base layer (A) provided with the printed layer (F). The gas barrier inorganic vapor deposited layer (C) and the gas barrier inorganic vapor deposited layer (C) side of the easy-open sealant layer (D) can be laminated via a gas barrier organic adhesive layer (B). . Further, as shown in FIG. 2, the printed layer (F) may be provided on the gas barrier coating layer (E).
本発明に係る積層体は、積層体の構成に応じた温度と時間によるエージングを施してもよい。エージング処理によって、積層体の層界面の接着性を向上することができる。 The laminate according to the present invention may be subjected to aging at a temperature and time depending on the structure of the laminate. The aging treatment can improve the adhesion of the layer interfaces of the laminate.
エージングは、３０～５０℃で、１～３日が好ましい。上記範囲よりも低温又は短時間だと、エージングの効果が充分には発揮され難い場合が有り、上記範囲よりも高温または長時間だと、エネルギーまたは長時間を要する割にはエージングの効果がそれ以上には向上され難く、生産性が悪化し易い。 Aging is preferably performed at 30 to 50°C for 1 to 3 days. If the temperature is lower or for a shorter time than the above range, the aging effect may not be fully exhibited. If the temperature is higher than the range or for a long time, the aging effect may not be as effective as it requires energy or a long time. It is difficult to improve more than this, and productivity tends to deteriorate.
本発明に係る積層体及び該積層体からなる包装材料は、ガスバリア性に優れ、好ましくは、２３℃９０％ＲＨ環境下における酸素透過度が、０．０５～２ｃｃ／ｍ2／ｄａｙ／ａｔｍであり、４０℃９０％ＲＨ環境下における水蒸気透過度が、０．０１～２ｇ／ｍ2／ｄａｙである。 The laminate according to the present invention and the packaging material made of the laminate have excellent gas barrier properties, and preferably have an oxygen permeability of 0.05 to 2 cc/m 2 /day/atm in an environment of 23° C. and 90% RH. The water vapor permeability in an environment of 40°C and 90% RH is 0.01 to 2 g/m 2 /day.
更に、包装材料を用いて包装袋を作製して内容物を縦ピロー充填した際に、包装袋は熱や摩擦や圧力等によって物理的な負荷に曝される為に、一般的には、包装袋のガスバリア性は低下する。 Furthermore, when packaging bags are made using packaging materials and filled vertically with the contents, the packaging bags are exposed to physical loads due to heat, friction, pressure, etc. The gas barrier properties of the bag are reduced.
しかしながら、本発明に係る包装材料を用いて作製された包装袋は、縦ピロー充填後のガスバリア性の低下が少なく、好ましくは、ゲルボフレックステスターで５回の屈曲負荷を与えた後の、２３℃９０％ＲＨ環境下における酸素透過度の、前記屈曲負荷を与える前からの増加値がゼロまたは２０ｃｃ／ｍ2／ｄａｙ／ａｔｍ以下であり、４０℃９０％ＲＨ環境下における水蒸気透過度の、前記屈曲負荷を与える前からの増加値が、ゼロまたは２０ｇ／ｍ2／ｄａｙ以下であることができる。 However, the packaging bag produced using the packaging material according to the present invention has less deterioration in gas barrier properties after being filled with vertical pillows, and preferably has a The increase value of the oxygen permeability in a 90% RH environment at 90°C from before applying the bending load is zero or 20 cc/m 2 /day/atm or less, and the water vapor permeability in a 90% RH environment at 40°C. The increase value from before applying the bending load may be zero or 20 g/m 2 /day or less.
［包装体］
本発明に係る包装袋は、本発明に係る包装材料から作製されたものであり、易開封性とガスバリア性と低溶剤臭性と耐屈曲性に優れる。包装袋の具低例としては、例えば、ピロー包装袋等が挙げられる。
本発明について、実施例を挙げて具体的に説明する。
[Package]
The packaging bag according to the present invention is made from the packaging material according to the present invention, and is excellent in easy opening, gas barrier properties, low solvent odor, and bending resistance. Examples of packaging bags include pillow packaging bags and the like.
The present invention will be specifically described with reference to Examples.
＜原材料の準備＞
ＰＥＴフィルム１：東洋紡社製ＰＥＴフィルム、Ｔ４１００。片面コロナ処理。１０μｍ厚。
ＰＥＴフィルム２：東レフィルム加工（株）社製ＰＥＴフィルム、１３１０。片面アルミニウム蒸着処理（４０ｎｍ厚）。１２μｍ厚。
ＯＰＰフィルム１～６：東洋紡（株）社製ＯＰＰ（２軸延伸ポリプロピレン）フィルム、２１６１。片面コロナ処理。厚さ１８、２０、２５、３０、４０、６０μｍ。
ＡＣコート剤１：（株）日本触媒社製、エポミンＰ－１０００。
無溶剤ガスバリア性有機接着剤組成物１：下記で調製。
無溶剤ガスバリア性有機接着剤組成物２：ＤＩＣ（株）社製無溶剤型ＰＡＳＬＩＭ
含溶剤ガスバリア性有機接着剤組成物１：下記で調製。
２液硬化型ウレタン接着剤１：東洋モートン（株）社製、トモフレックスＴＭ－３４０／東洋モートン（株）社製ＣＡＴ－２９
低密度ポリエチレン１：日本ポリエチレン（株）製低密度ポリエチレン、ＬＣ６００Ａ。イージーピールＣＰＰフィルム１：下記で作製。
イージーピールＣＰＰフィルム２：下記で作製。
イージーピールＣＰＰフィルム３：下記で作製。
イージーピールＣＰＰフィルム４：下記で作製。
<Preparation of raw materials>
PET film 1: PET film manufactured by Toyobo Co., Ltd., T4100. Single side corona treatment. 10μm thick.
PET film 2: PET film manufactured by Toray Film Processing Co., Ltd., 1310. Single side aluminum vapor deposition treatment (40nm thickness). 12μm thick.
AC coating agent 1: Epomin P-1000 manufactured by Nippon Shokubai Co., Ltd.
Solvent-free gas barrier organic adhesive composition 1: Prepared as follows.
Solvent-free gas barrier organic adhesive composition 2: Solvent-free PASLIM manufactured by DIC Corporation
Solvent-containing gas barrier organic adhesive composition 1: Prepared as follows.
Two-part curable urethane adhesive 1: Tomoflex TM-340 manufactured by Toyo Morton Co., Ltd. / CAT-29 manufactured by Toyo Morton Co., Ltd.
Low density polyethylene 1: Low density polyethylene manufactured by Japan Polyethylene Co., Ltd., LC600A. Easy peel CPP film 1: Produced as follows.
Easy peel CPP film 2: Produced as follows.
Easy peel CPP film 3: Produced as follows.
Easy peel CPP film 4: Produced as follows.
［ガスバリア塗布膜用樹脂組成物１の調製］
下記の原料を混合して、ガスバリア塗布膜層（Ｅ）用の、ガスバリア塗布膜用樹脂組成物１を調製した。
テトラエトキシシラン １００質量部
エバールＥＰ－Ｆ１０１ ２０質量部
Ｎ，Ｎ－ジメチルべンジルアミン ０．２質量部
イソプロピルアルコール ３００質量部
[Preparation of
A gas barrier
Tetraethoxysilane 100 parts by mass EVAL EP-F101 20 parts by mass N,N-dimethylbenzylamine 0.2 parts by mass Isopropyl alcohol 300 parts by mass
［無溶剤ガスバリア性有機接着剤組成物１の調製］
下記のように操作して、ガスバリア性有機接着剤層（Ｂ）用の、無溶剤ガスバリア性有機接着剤組成物１を調製した。
先ず、精留管と水分分離器を備えたポリエステル反応容器に下記原料を投入して徐々に加熱し、窒素雰囲気下で、反応液の液温２２０℃、蒸気温１００℃を維持しながらエステル化反応を進行させ、反応液の酸価が１ｍｇＫＯＨ／ｇ以下になったところでエステル化反応を終了し、液温を１２０℃まで冷却した。
無水フタル酸 ２４１．９質量部
エチレングリコール １０５．４質量部
グリセリン ７５．２質量部
チタニウムテトライソプロポキシド ０．０４２質量部
[Preparation of solvent-free gas barrier organic adhesive composition 1]
A solvent-free gas barrier
First, the following raw materials were put into a polyester reaction vessel equipped with a rectification tube and a water separator, and gradually heated, and esterified while maintaining the liquid temperature of the reaction liquid at 220°C and the steam temperature at 100°C under a nitrogen atmosphere. The reaction was allowed to proceed, and when the acid value of the reaction solution became 1 mgKOH/g or less, the esterification reaction was terminated, and the solution temperature was cooled to 120°C.
Phthalic anhydride 241.9 parts by mass Ethylene glycol 105.4 parts by mass Glycerin 75.2 parts by mass Titanium tetraisopropoxide 0.042 parts by mass
次いで、反応液に下記原料を投入し、液温１２０℃を維持しつつ、多価カルボン酸変性化反応を進行させ、酸価が無水マレイン酸の仕込み量から計算した酸価の概ね半分になったところでエステル化反応を終了して、冷却して、多価カルボン酸変性ポリエステルポリオールＡを得た。
無水マレイン酸 ７７．５質量部
得られた多価カルボン酸変性ポリエステルポリオールＡの特徴は下記の通り。
数平均分子量：約５２０、
水酸基価：２１６．６ｍｇＫＯＨ／ｇ、
酸価：９６．２ｍｇＫＯＨ／ｇ
１分子当たりの水酸基数：２個 （設計値）
１分子当たりのカルボキシル基数：１個 （設計値）
Next, the following raw materials were added to the reaction solution, and while maintaining the solution temperature at 120°C, the polyhydric carboxylic acid modification reaction was allowed to proceed until the acid value became approximately half of the acid value calculated from the amount of maleic anhydride charged. At this point, the esterification reaction was completed and the mixture was cooled to obtain a polycarboxylic acid-modified polyester polyol A.
77.5 parts by mass of maleic anhydride The characteristics of the obtained polycarboxylic acid-modified polyester polyol A are as follows.
Number average molecular weight: about 520,
Hydroxyl value: 216.6mgKOH/g,
Acid value: 96.2mgKOH/g
Number of hydroxyl groups per molecule: 2 (designed value)
Number of carboxyl groups per molecule: 1 (designed value)
次いで、イソシアネート化合物として、住化バイエルウレタン製「デスモジュールＮ３２００」（ヘキサメチレンジイソシアネートのビウレット体。１分子当たりのイソシアネート基数：２個）と、三井化学製「タケネート５００」（メタキシリレンジイソシアネート。１分子当たりのイソシアネート基数：２個）とを用いて、上記で得た多価カルボン酸変性ポリエステルポリオールＡと、下記配合比で８０℃に加熱して均一に混合して、冷却し、無溶剤ガスバリア性有機接着剤組成物１を得た。
多価カルボン酸変性ポリエステルポリオールＡ １００質量部
デスモジュールＮ３２００ ４９．５質量部
タケネート５００ ２８．９質量部
Next, as isocyanate compounds, "Desmodur N3200" manufactured by Sumika Bayer Urethane (biuret form of hexamethylene diisocyanate. Number of isocyanate groups per molecule: 2) and "Takenate 500" manufactured by Mitsui Chemicals (methaxylylene diisocyanate. 1) The number of isocyanate groups per molecule: 2) is heated to 80° C. and mixed uniformly with the polycarboxylic acid-modified polyester polyol A obtained above at the following blending ratio, and then cooled to form a solvent-free gas barrier. Organic
Polycarboxylic acid-modified polyester polyol A 100 parts by mass Desmodur N3200 49.5 parts by mass Takenate 500 28.9 parts by mass
［含溶剤ガスバリア性有機接着剤組成物１の調製］
下記の接着剤と溶剤を混合して、含溶剤ガスバリア性有機接着剤組成物１を調製した。接着剤：ＰＡＳＬＩＭ ＶＭ００１／ＶＭ１０２ＣＰ（ＤＩＣ（株）社製） １９質量部溶剤：酢酸エチル １５質量部
[Preparation of solvent-containing gas barrier organic adhesive composition 1]
A solvent-containing gas barrier
［イージーピールＣＰＰフィルム１の作製］
ポリエチレン／ポリプロピレン＆ポリエチレンの混合物／ポリプロピレン、の３層フィルムを製膜し、厚み２５μｍのフィルムを得た。
更に、得られたフィルムに対して、巻取式真空蒸着機によって、アルミニウムを誘導加熱して、５×１０-4Ｔｏｒｒ下でアルミニウム蒸着処理を行い、ガスバリア無機蒸着層（Ｃ）として４０ｎｍ厚の片面アルミニウム蒸着層を有する、厚み２５μｍのイージーピールＣＰＰ（未延伸ポリプロピレン）フィルム１を得た。
[Preparation of Easy Peel CPP Film 1]
A three-layer film of polyethylene/polypropylene & a mixture of polyethylene/polypropylene was formed to a thickness of 25 μm.
Furthermore, the obtained film was subjected to an aluminum deposition process under 5 x 10-4 Torr by induction heating of aluminum using a winding vacuum deposition machine, to obtain an easy-peel CPP (unoriented polypropylene)
［イージーピールＣＰＰフィルム２の作製］
ポリエチレン／ポリプロピレン＆ポリエチレンの混合物／ポリプロピレン、の３層フィ
ルムを製膜し、厚み２５μｍのフィルムを得た。
更に、得られたフィルムに対して、下記条件でアルミナ蒸着膜（２０ｎｍ厚）を形成した。
真空チャンバ―内の真空度；２～６×１０-6ｍＢａｒ
蒸着チャンバ―内の真空度：２～５×１０-3ｍＢａｒ
冷却・電極ドラム供給電力：１０ｋＷ
ライン速度：１００ｍ／ｍｉｎ
[Production of easy peel CPP film 2]
A three-layer film of polyethylene/polypropylene and a mixture of polyethylene/polypropylene was formed to obtain a film with a thickness of 25 μm.
Furthermore, an alumina vapor deposition film (20 nm thick) was formed on the obtained film under the following conditions.
Vacuum degree inside the vacuum chamber: 2 to 6 x 10 -6 mBar
Vacuum degree inside the deposition chamber: 2 to 5 x 10 -3 mBar
Cooling/electrode drum supply power: 10kW
Line speed: 100m/min
次いで、アルミナ蒸着膜を形成した直後に、そのアルミナ蒸着膜面に、下記条件でプラズマ処理を行って、アルミナ蒸着膜面の表面張力を５４ｄｙｎｅ／ｃｍ以上向上させたプラズマ処理面を形成して、イージーピールＣＰＰフィルム２を得た。
プラズマ発生装置：グロー放電プラズマ発生装置
パワー：９ｋｗ
混合ガス流量：酸素ガス／アルゴンガス＝７．０／２．５（単位：ｓｌｍ）
混合ガス圧：６×１０-3Ｔｏｒｒ
Next, immediately after forming the alumina vapor deposited film, plasma treatment is performed on the alumina vapor deposited film surface under the following conditions to form a plasma treated surface in which the surface tension of the alumina vapor deposited film surface is improved by 54 dyne/cm or more, Easy
Plasma generator: Glow discharge plasma generator Power: 9kw
Mixed gas flow rate: oxygen gas/argon gas = 7.0/2.5 (unit: slm)
Mixed gas pressure: 6×10 -3 Torr
［イージーピールＣＰＰフィルム３の作製］
ポリエチレン／ポリプロピレン＆ポリエチレンの混合物／ポリプロピレン、の３層フィルムを製膜し、厚み２５μｍのフィルムを得た。
更に、得られたフィルムに対して、下記条件で酸化珪素蒸着膜（２０ｎｍ厚）を形成した。
導入ガス：ヘキサメチルジシロキサン／酸素ガス／ヘリウム＝１．０／３．０／３．０（単位：ｓ１ｍ）
真空チャンバ―内の真空度；２～６×１０-6ｍＢａｒ
蒸着チャンバ―内の真空度：２～５×１０-3ｍＢａｒ
冷却・電極ドラム供給電力：１０ｋＷ
ライン速度：１００ｍ／ｍｉｎ
[Production of easy peel CPP film 3]
A three-layer film of polyethylene/polypropylene and a mixture of polyethylene/polypropylene was formed to obtain a film with a thickness of 25 μm.
Furthermore, a silicon oxide vapor deposition film (20 nm thick) was formed on the obtained film under the following conditions.
Introduced gas: hexamethyldisiloxane/oxygen gas/helium = 1.0/3.0/3.0 (unit: s1m)
Vacuum degree inside the vacuum chamber: 2 to 6 x 10 -6 mBar
Vacuum degree inside the deposition chamber: 2 to 5 x 10 -3 mBar
Cooling/electrode drum supply power: 10kW
Line speed: 100m/min
次いで、酸化珪素蒸着膜を形成した直後に、その酸化珪素蒸着膜面に、下記条件でプラズマ処理を行って、酸化珪素蒸着膜面の表面張力を５４ｄｙｎｅ／ｃｍ以上向上させたプラズマ処理面を形成して、イージーピールＣＰＰフィルム３を得た。
プラズマ発生装置：グロー放電プラズマ発生装置
パワー：９ｋｗ
混合ガス流量：酸素ガス／アルゴンガス＝７．０／２．５（単位：ｓｌｍ）
混合ガス圧：６×１０-3Ｔｏｒｒで
Next, immediately after forming the silicon oxide vapor deposited film, plasma treatment is performed on the silicon oxide vapor deposited film surface under the following conditions to form a plasma treated surface in which the surface tension of the silicon oxide vapor deposited film surface is improved by 54 dyne/cm or more. As a result, Easy
Plasma generator: Glow discharge plasma generator Power: 9kw
Mixed gas flow rate: oxygen gas/argon gas = 7.0/2.5 (unit: slm)
Mixed gas pressure: 6×10 -3 Torr
［イージーピールＣＰＰフィルム４の作製］
ポリエチレン／ポリプロピレン＆ポリエチレンの混合物／ポリプロピレン、の３層フィルムを製膜し、厚み２５μｍのフィルムを得た。
[Preparation of Easy Peel CPP Film 4]
A three-layer film of polyethylene/polypropylene & a mixture of polyethylene/polypropylene was formed to a thickness of 25 μm.
［実施例１］
基材層（Ａ）としてＯＰＰフィルム４、ガスバリア性有機接着剤層（Ｂ）として無溶剤ガスバリア性有機接着剤組成物１、シーラント層（Ｄ）としてＣＰＰフィルム１を用いた。
[Example 1]
まず、ＯＰＰフィルム４のコロナ処理面に、水性フレキソ印刷層からなる印刷層（Ｆ）を設けた。
First, a printing layer (F) consisting of an aqueous flexographic printing layer was provided on the corona-treated surface of the
次に、印刷層（Ｆ）面と、イージーピールＣＰＰフィルム１のアルミニウム蒸着面とを、無溶剤ガスバリア性有機接着剤組成物１を介して、ラミネートし、次いで４０℃で２日
間エージング処理し、積層体を得た。
Next, the printed layer (F) surface and the aluminum vapor-deposited surface of the easy-
このときの無溶剤ガスバリア性有機接着剤組成物１の塗布量は、硬化後のガスバリア性有機接着剤層（Ｂ）の厚さが２μｍになる量とした。
The coating amount of the solvent-free gas barrier
得られた積層体について各種評価を実施した。結果を表１に示す。
層構成：ＯＰＰフィルム４（３０μｍ）／水性フレキソ印刷層（１μｍ）／無溶剤ガスバリア性有機接着剤組成物１硬化物（２μｍ）／アルミニウム蒸着膜（４０ｎｍ）／イージーピールＣＰＰフィルム１（２５μｍ）
Various evaluations were performed on the obtained laminate. The results are shown in Table 1.
Layer structure: OPP film 4 (30 μm) / water-based flexographic printing layer (1 μm) / cured product of solvent-free gas barrier organic adhesive composition 1 (2 μm) / aluminum vapor deposited film (40 nm) / easy peel CPP film 1 (25 μm)
［実施例２～４、６～１１］
各層の構成を表１に記載の内容に変えた以外は、実施例１と同様に操作して、同様に評価した。結果を表１、２に示す。
[Examples 2 to 4, 6 to 11]
The same procedures and evaluations were carried out as in Example 1, except that the constitution of each layer was changed to that shown in Table 1. The results are shown in Tables 1 and 2.
［実施例５］
基材層（Ａ）としてＯＰＰフィルム４、ガスバリア性有機接着剤層（Ｂ）として無溶剤ガスバリア性有機接着剤組成物１、シーラント層（Ｄ）としてイージーピールＣＰＰフィルム１、ガスバリア塗布膜層（Ｅ）としてガスバリア塗布膜用樹脂組成物１を用いた。
まず、ＯＰＰフィルム４のコロナ処理面に、水性フレキソ印刷層からなる印刷層（Ｆ）を設けた。
次に、印刷層（Ｆ）面に、ガスバリア塗布膜用樹脂組成物１を塗布、乾燥して、ガスバリア塗布膜層（Ｅ）を形成し、該ガスバリア塗布膜層（Ｅ）面と、イージーピールＣＰＰフィルム１のアルミニウム蒸着面とを、無溶剤ガスバリア性有機接着剤組成物１を介して、ラミネートし、次いで４０℃で２日間エージング処理し、積層体を得た。
[Example 5]
First, a printing layer (F) consisting of an aqueous flexographic printing layer was provided on the corona-treated surface of the
Next, the
このときの、ガスバリア塗布膜用樹脂組成物１の塗布量は、乾燥後のガスバリア塗布膜層（Ｅ）の厚さが２μｍになる量、無溶剤ガスバリア性有機接着剤組成物１の塗布量は、硬化後のガスバリア性有機接着剤層（Ｂ）の厚さが２μｍになる量とした。
得られた積層体について、実施例１と同様に評価した。結果を表１に示す。
At this time, the coating amount of the
The obtained laminate was evaluated in the same manner as in Example 1. The results are shown in Table 1.
［比較例１］
印刷層を油性グラビア印刷層によって形成した以外は実施例１と同様に操作して、積層体を得て、同様に評価した。結果を表３に示す。
[Comparative example 1]
A laminate was obtained in the same manner as in Example 1 except that the printing layer was formed by an oil-based gravure printing layer, and evaluated in the same manner. The results are shown in Table 3.
［比較例２］
ガスバリア性有機接着剤層（Ｂ）を無溶剤ガスバリア性有機接着剤組成物１を用いて形成する代わりに、含溶剤ガスバリア性有機接着剤組成物１を用いて接着層を形成し、エージング条件を４０℃３日に変えた以外は、比較例１と同様に操作して、積層体を得て、同様に評価した。結果を表３に示す。
[Comparative example 2]
Instead of forming the gas barrier organic adhesive layer (B) using the solvent-free gas barrier
［比較例３］
基材層（Ａ）にＰＥＴフィルム１を用いた以外は比較例２と同様に操作して、積層体を得て、同様に評価した。結果を表３に示す。
[Comparative example 3]
A laminate was obtained in the same manner as in Comparative Example 2 except that
［比較例４］
ガスバリア性有機接着剤層（Ｂ）に、２液硬化型ウレタン接着剤１を塗布、乾燥して接着層を形成してから、ドライラミネーションによってイージーピールＣＰＰフィルム１のアルミニウム蒸着面を接着して積層し、エージング条件を２５℃１日間に変えた以外は、比較例１と同様に操作して、積層体を得て、同様に評価した。結果を表３に示す。
[Comparative example 4]
A two-component curable urethane adhesive 1 is applied to the gas barrier organic adhesive layer (B), dried to form an adhesive layer, and then the aluminum-deposited surface of the easy-
［比較例５］
基材層（Ａ）としてＯＰＰフィルム２、シーラント層（Ｄ）としてイージーピールＣＰＰフィルム４を用いた。
まず、ＯＰＰフィルム２のコロナ処理面に、油性グラビア印刷層からなる印刷層を設けた。
次に、印刷層面に、ＡＣコート剤１を乾燥後の厚さが１μｍになるように塗布、乾燥して、次いで、厚さが１０μｍになるように溶融押出された低密度ポリエチレン１を介して、ＰＥＴフィルム２のアルミニウム蒸着層を接着して積層した。
[Comparative example 5]
First, a printing layer consisting of an oil-based gravure printing layer was provided on the corona-treated surface of the
Next,
次に、ＰＥＴフィルム面に、ＡＣコート剤１を乾燥後の厚さが１μｍになるように塗布、乾燥して、次いで、厚さが１０μｍになるように溶融押出された低密度ポリエチレン１を介して、イージーピールＣＰＰフィルム４を接着して積層して、積層体を得た。
得られた積層体について、実施例１と同様に評価した。結果を表３に示す。
Next,
The obtained laminate was evaluated in the same manner as in Example 1. The results are shown in Table 3.
＜評価＞
［ガスバリア性］
（１）酸素透過度
各積層体をＡ４サイズに裁断し、米国ＭＯＣＯＮ社製ＯＸＴＲＡＮ２／２０を使用し、２３℃、９０％ＲＨの条件下での酸素透過度（ｃｃ／ｍ2／ｄａｙ／ａｔｍ）を測定した。２ｃｃ／ｍ2／ｄａｙ／ａｔｍ以下を合格とした。
（２）水蒸気透過度
各積層体をＡ４サイズに裁断し、米国ＭＯＣＯＮ社製ＰＥＲＭＡＴＲＡＮ３／３１を使用し、４０℃、９０％ＲＨの条件下での水蒸気透過度（ｇ／ｍ2／ｄａｙ）を測定した。２ｇ／ｍ2／ｄａｙ以下を合格とした。
（３）屈曲負荷後
ゲルボフレックステスターで５回の屈曲負荷を与えた後に、酸素透過度と水蒸気透過度を、上記と同一の方法及び条件下で測定した。前記屈曲負荷を与える前からの増加値が、酸素透過度は２０ｃｃ／ｍ2／ｄａｙ／ａｔｍ以下、水蒸気透過度は２０ｇ／ｍ2／ｄａｙ以下を合格とした。
<Evaluation>
[Gas barrier properties]
(1) Oxygen permeability Each laminate was cut into A4 size, and oxygen permeability (cc/m 2 /day/atm ) was measured. A value of 2 cc/m 2 /day/atm or less was considered to be a pass.
(2) Water vapor permeability Cut each laminate into A4 size and measure the water vapor permeability (g/m 2 /day) under the conditions of 40°C and 90%
(3) After bending load After applying bending load five times using a Gelbo Flex tester, oxygen permeability and water vapor permeability were measured using the same method and conditions as above. An increase value from before applying the bending load of 20 cc/m 2 /day/atm or less for oxygen permeability and 20 g/m 2 /day or less for water vapor permeability was considered to be a pass.
［縦ピロー充填性］
下記条件で、内容物無しの空袋で、縦ピロー充填性を評価した。
充填機：ＫＢＦ－６１００（株式会社川島製作所社製）
包装袋サイズ：巾２００ｍｍ×高さ２４０ｍｍ
シール条件：縦シール１４０℃、横シール１５０℃
ショット数：３０個／分
[Vertical pillow filling properties]
Vertical pillow filling properties were evaluated using empty bags without contents under the following conditions.
Filling machine: KBF-6100 (manufactured by Kawashima Seisakusho Co., Ltd.)
Packaging bag size: width 200mm x height 240mm
Sealing conditions: vertical seal 140℃, horizontal seal 150℃
Number of shots: 30/min
［ラミネート強度］
積層体から、幅１５ｍｍの短冊状の試験片を切り出し、テンシロン引張試験機（（株）オリエンテック製ＲＴＣ－１３１０Ａ）を用いて、２５℃雰囲気下、Ｔ字剥離方式（引張速度５０ｍｍ／分）により、基材層とシーラント層間を剥離した際の最大荷重を測定し、ラミネート強度（Ｎ／１５ｍｍ）とした。更には、剥離界面部位を確認した。表１内の表記は下記の意味である。ラミネート強度は、１Ｎ／１５ｍｍ以上を合格とした。
蒸／シ：ガスバリア無機蒸着層（Ｃ）／シーラント層（Ｄ）の界面で剥離
接／蒸：ガスバリア性有機接着剤層（Ｂ）／ガスバリア無機蒸着層（Ｃ）の界面で剥離
蒸着膜＝アルミニウム、アルミナ、酸化珪素の蒸着膜。
接着剤＝無溶剤ガスバリア性有機接着剤組成物１、無溶剤ガスバリア性有機接着剤組成物２、含溶剤ガスバリア性有機接着剤組成物１、２液硬化型ウレタン接着剤１、低密度ポポリエチレン１。
シーラント部＝ＣＰＰフィルム１～４のＣＰＰ部。
[Lamination strength]
A strip-shaped test piece with a width of 15 mm was cut out from the laminate, and tested using a Tensilon tensile tester (RTC-1310A manufactured by Orientec Co., Ltd.) under a 25°C atmosphere using the T-shaped peeling method (tensile speed 50 mm/min). The maximum load when the base material layer and the sealant layer were peeled off was measured and defined as the laminate strength (N/15 mm). Furthermore, the peeling interface site was confirmed. The notations in Table 1 have the following meanings. A lamination strength of 1 N/15 mm or more was considered acceptable.
Vaporization/Si: Peeling off at the interface of gas barrier inorganic vapor deposition layer (C)/sealant layer (D) Contact/vaporization: Peeling off at the interface of gas barrier organic adhesive layer (B)/gas barrier inorganic vapor deposition layer (C) Vapor deposition film = Aluminum , alumina, and silicon oxide vapor deposited films.
Adhesive = Solvent-free gas barrier
Sealant portion = CPP portion of
［シール強度］
２枚の積層体をシーラント層が対向するように重ねてヒートシールした後に、幅１５ｍｍの短冊状に試験片を切り出し、テンシロン引張試験機（（株）オリエンテック製ＲＴＣ－１３１０Ａ）を用いて、２５℃雰囲気下、Ｔ字剥離方式（引張速度５０ｍｍ／分）により、シーラント層間を剥離した際の最大荷重を測定し、シール強度（Ｎ／１５ｍｍ）とした。２～２０Ｎ／１５ｍｍの場合を合格とした。
[Seal strength]
After the two laminates were stacked and heat-sealed so that the sealant layers faced each other, a test piece was cut into a strip with a width of 15 mm, and using a Tensilon tensile tester (RTC-1310A manufactured by Orientec Co., Ltd.), The maximum load when the sealant layers were peeled off using a T-peel method (pulling speed: 50 mm/min) in an atmosphere of 25°C was determined as the seal strength (N/15 mm). A case of 2 to 20 N/15 mm was considered to be a pass.
［積層体中の残留溶剤量］
ガスクロマトグラフィーにて積層体中の、トルエン、酢酸エチル、ＩＰＡ、メタノール、ＭＥＫの総量（ｍｇ／ｍ2）を測定した。総量がゼロまたは６ｍｇ／ｍ2以下を合格とした。
[Amount of residual solvent in the laminate]
The total amount (mg/m 2 ) of toluene, ethyl acetate, IPA, methanol, and MEK in the laminate was measured by gas chromatography. A total amount of zero or 6 mg/m 2 or less was considered to be a pass.
［結果まとめ］
実施例１～１１は、総構成層数が５～６層構成でありながらも、良好な、縦ピロー充填性と、屈曲負荷前後の酸素透過度と水蒸気透過度と、ラミネート性と、シール強度とのバランスを示し、従来のガスバリア積層体であり総構成層数が９層で多い比較例５よりも高いガスバリア性を示した。
[Result Summary]
Examples 1 to 11 have a total of 5 to 6 layers, but have good vertical pillow filling properties, oxygen permeability and water vapor permeability before and after bending load, lamination properties, and seal strength. It showed a higher gas barrier property than Comparative Example 5, which is a conventional gas barrier laminate and has a large total number of constituent layers, 9 layers.
しかし、油性グラビア印刷層や含溶剤ガスバリア性有機接着剤組成物、２液硬化型ウレタン接着剤、ＡＣコート剤等を含む比較例１～５は、総じて高い残留溶剤量を示した。 However, Comparative Examples 1 to 5, which included an oil-based gravure printing layer, a solvent-containing gas barrier organic adhesive composition, a two-component curable urethane adhesive, an AC coating agent, etc., generally showed a high amount of residual solvent.
比較例４は、屈曲負荷後の酸素透過度は、測定装置の測定可能範囲を超えた酸素透過度を示し、測定値を得ることはできなかった。 In Comparative Example 4, the oxygen permeability after bending load exceeded the measurable range of the measuring device, and no measurement value could be obtained.
１ 低溶剤臭易開封性ガスバリア積層体
２ 基材層（Ａ）
３ ガスバリア性有機接着剤層（Ｂ）
４ ガスバリア無機蒸着層（Ｃ）
５ 易開封性シーラント層（Ｄ）
６ ガスバリア無機蒸着層
７ ガスバリア塗布膜層（Ｅ）
８ 印刷層（Ｆ）
1 Low solvent odor, easy-to-open
3 Gas barrier organic adhesive layer (B)
4 Gas barrier inorganic vapor deposited layer (C)
5 Easy-open sealant layer (D)
6 Gas barrier inorganic vapor deposited
8 Printing layer (F)
Claims (13)
ガスバリア無機蒸着層（Ｃ）とガスバリア性有機接着剤層（Ｂ）とは隣接して積層されており、
ガスバリア性有機接着剤層（Ｂ）は、無溶剤接着剤組成物が塗布され、更に硬化されて形成された層であり、
該無溶剤接着剤組成物は、多価カルボン酸変性ポリエステルポリオール（Ｎ）と、１分子内にイソシアネート基を２個以上有するイソシアネート化合物（Ｋ）とを含有し、
ガスバリア性有機接着剤層（Ｂ）は、厚みが０．６～６．０μｍであり、
印刷層（Ｆ）は、水性フレキソ印刷層および／または水性グラビア印刷層を含み、
前記低溶剤臭易開封性ガスバリア積層体の溶剤含有量は、ゼロまたは６ｍｇ／ｍ2以下であり、
該低溶剤臭易開封性ガスバリア積層体の２３℃、９０％ＲＨの条件下での酸素透過度は０．７～１．０ｃｃ／ｍ2／ｄａｙ／ａｔｍであって、４０℃、９０％ＲＨの条件下での水蒸気透過度は０．１～０．２ｇ／ｍ2／ｄａｙ／ａｔｍであり、
該低溶剤臭易開封性ガスバリア積層体に、ゲルボフレックステスターで５回の屈曲負荷を与える前と後との増加値が、２３℃、９０％ＲＨの条件下で酸素透過度は０．６～１．１ｃｃ／ｍ2／ｄａｙ／ａｔｍであって、４０℃、９０％ＲＨの条件下での水蒸気透過度は０．１～０．５ｇ／ｍ2／ｄａｙ／ａｔｍである、
低溶剤臭易開封性ガスバリア積層体。 A low solvent odor comprising at least a base material layer (A), a gas barrier organic adhesive layer (B), a gas barrier inorganic vapor deposited layer (C), an easy-to-open sealant layer (D), and a printed layer (F). An easily openable gas barrier laminate,
The gas barrier inorganic vapor deposited layer (C) and the gas barrier organic adhesive layer (B) are laminated adjacent to each other,
The gas barrier organic adhesive layer (B) is a layer formed by applying a solvent-free adhesive composition and further curing it,
The solvent-free adhesive composition contains a polycarboxylic acid-modified polyester polyol (N) and an isocyanate compound (K) having two or more isocyanate groups in one molecule,
The gas barrier organic adhesive layer (B) has a thickness of 0.6 to 6.0 μm,
The printing layer (F) includes an aqueous flexographic printing layer and/or an aqueous gravure printing layer,
The solvent content of the low solvent odor easy-to-open gas barrier laminate is zero or 6 mg/m 2 or less,
The oxygen permeability of the low solvent odor, easy-to-open gas barrier laminate at 23° C. and 90% RH is 0.7 to 1.0 cc/m 2 /day/atm, and the oxygen permeability is 0.7 to 1.0 cc/m 2 /day/atm at 40° C. and 90% RH. The water vapor permeability under the conditions is 0.1 to 0.2 g/m 2 /day/atm,
The increase in oxygen permeability between before and after applying a bending load to the low-solvent odor, easy-to-open gas barrier laminate using a Gelboflex tester 5 times was 0.6 under the conditions of 23°C and 90% RH. ~1.1 cc/m 2 /day/atm, and the water vapor permeability under the conditions of 40°C and 90% RH is 0.1 to 0.5 g/m 2 /day/atm,
Easy-to-open gas barrier laminate with low solvent odor.
請求項１に記載の低溶剤臭易開封性ガスバリア積層体。 The printing layer (F) is provided adjacent to the gas barrier organic adhesive layer (B),
The low solvent odor, easy-to-open gas barrier laminate according to claim 1.
請求項１または２に記載の低溶剤臭易開封性ガスバリア積層体。 The base layer (A) is made of a biaxially stretched film containing a polypropylene resin.
The low solvent odor, easy-to-open gas barrier laminate according to claim 1 or 2.
、
請求項１～３の何れか１項に記載の低溶剤臭易開封性ガスバリア積層体。 The base layer (A) is made of a biaxially stretched film containing a polyethylene terephthalate resin.
The low solvent odor, easy-to-open gas barrier laminate according to any one of claims 1 to 3.
ガスバリア塗布膜層（Ｅ）は、金属アルコキシドと水溶性高分子とを含む樹脂組成物から生成された、ゾルゲル法加水分解重縮合物を含有する、
請求項１～４の何れか１項に記載の低溶剤臭易開封性ガスバリア積層体。 Furthermore, a low solvent odor easy-to-open gas barrier laminate having a gas barrier coating layer (E) between the base material layer (A) and the gas barrier organic adhesive layer (B),
The gas barrier coating layer (E) contains a sol-gel hydrolysis polycondensate produced from a resin composition containing a metal alkoxide and a water-soluble polymer.
The low solvent odor, easy-to-open gas barrier laminate according to any one of claims 1 to 4.
請求項１～５の何れか１項に記載の低溶剤臭易開封性ガスバリア積層体。 The gas barrier inorganic vapor deposited layer (C) is a layer having one or more types selected from the group consisting of an aluminum vapor deposited layer, an alumina vapor deposited layer, and a silica vapor deposited layer.
The low solvent odor, easy-to-open gas barrier laminate according to any one of claims 1 to 5.
請求項１～５の何れか１項に記載の低溶剤臭易開封性ガスバリア積層体。 The gas barrier inorganic vapor deposited layer (C) is a layer having an aluminum vapor deposited layer,
The low solvent odor, easy-to-open gas barrier laminate according to any one of claims 1 to 5.
請求項１～７の何れか１項に記載の低溶剤臭易開封性ガスバリア積層体。 The thickness of the gas barrier inorganic vapor deposited layer (C) is 1 to 100 nm.
The low solvent odor, easy-to-open gas barrier laminate according to any one of claims 1 to 7.