JP7394808B2 - Gusset bag for miso storage - Google Patents
Gusset bag for miso storage Download PDFInfo
- Publication number
- JP7394808B2 JP7394808B2 JP2021087862A JP2021087862A JP7394808B2 JP 7394808 B2 JP7394808 B2 JP 7394808B2 JP 2021087862 A JP2021087862 A JP 2021087862A JP 2021087862 A JP2021087862 A JP 2021087862A JP 7394808 B2 JP7394808 B2 JP 7394808B2
- Authority
- JP
- Japan
- Prior art keywords
- miso
- film
- materials
- gusset bag
- folding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、粘度の高い半固形物である味噌を包装(収納)するための包装袋に関するものであり、詳しくは、左右両サイドにマチを設けた味噌収納用の包装袋(所謂ガゼット袋)に関するものである。 The present invention relates to a packaging bag for packaging (storing) miso, which is a semi-solid substance with high viscosity. Specifically, the present invention relates to a packaging bag (so-called gusset bag) for storing miso that has gussets on both left and right sides. It is related to.
粘度の高い半固形物である味噌を長期的に収納する容器としては、収納し易さと取り出し易さの観点から、合成樹脂製の蓋付きのケースが用いられることが多い。また、味噌の容器としては、中身の状態を確認できるように透明な合成樹脂によって形成されたケースが用いられることが多い(特許文献1)。 As a container for long-term storage of miso, which is a semi-solid substance with high viscosity, a synthetic resin case with a lid is often used from the viewpoint of ease of storage and removal. Furthermore, cases made of transparent synthetic resin are often used as containers for miso so that the state of the contents can be confirmed (Patent Document 1).
しかしながら、上記した特許文献1の如き従来の味噌用の収納容器は、内容物を充填して陳列するためには、ケース本体、蓋体の他に、ケース本体の開口部において内部を密封するためのシール部材が必要である。また、内容物の商品名や性状を表示するためには、別途、それらを表示したシール等を作成してケースに貼り付けなければならない。それゆえ、従来の味噌用の収納容器は、包装に要する部材点数が多くなってしまうため、安価に包装することが難しい。
However, in the conventional storage container for miso such as the one disclosed in
本発明の目的は、上記従来の収納容器が有する問題点を解消し、粘度の高い半固形物である味噌を容易に包装(収納)したり、取り出したりすることができ、味噌を安価に包装することが可能な上、味噌を収納した状態で安定して起立させることが可能で冷蔵庫の中で保管し易い味噌収納用のガゼット袋を提供することにある。 The purpose of the present invention is to solve the above-mentioned problems of the conventional storage container, to easily package (storage) and take out miso, which is a semi-solid substance with high viscosity, and to package miso at low cost. To provide a gusset bag for storing miso, which can be stably erected with miso stored therein, and is easy to store in a refrigerator.
本発明の内、請求項1に記載された発明は、合成樹脂フィルムによって、表裏2枚の胴材の左右両側および下側に折り込み材を挟み込んだ袋状に形成された味噌収納用ガゼット袋の内部に味噌を充填してなる味噌入りの味噌収納用ガゼット袋であって、下側の折り込み材の外周が、表裏の各胴材の下端際および左右の各折り込み材の下端際にヒートシールされており、かつ、表側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の前側の端縁際にヒートシールされているとともに、裏側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の後側の端縁際にヒートシールされており、表裏の胴材、左右両側および下側の折り込み材を構成する合成樹脂フィルムが、ナイロン層の外側にPET層を積層してなるベース層の片面に熱接着層を積層してなる多層フィルムであり、それらの厚みが、いずれも70μm以上140μm以下であるとともに、前記左右の各折り込み材が、前記多層フィルムを、熱接着層が外向きになるように二つ折りしたものであり、なおかつ、内部に味噌が充填された状態で、上端縁において、前記左右の折り込み材が、内向きの山折り状に二つ折りされた状態で表裏の胴材とともにヒートシールされることによって、一定の高さの帯状の頭シール部が形成されており、前記頭シール部が形成されていることによって、上端縁の中央においては、表裏の胴材が一定の高さで熱融着しており、かつ、上端際の左右においては、表裏の胴材が、上端縁の中央における熱融着部分と同じ一定の高さで、対向する左右の折り込み材の外面と熱融着しているとともに、左右の折り込み材の内面同士が、熱融着しておらず離れた状態になっているとともに、充填された味噌の上面より上側であって前記頭シール部の下側の所定の高さ位置に、開封すべき位置である開封予定位置が印刷されており、その開封予定位置が、表裏の胴材および左右の折り込み部を横断するように周状に印刷されたものであることを特徴とする。
The invention described in
請求項2に記載された発明は、請求項1に記載された発明において、表裏の胴材、左右両側および下側の折り込み材を構成する合成樹脂フィルムが、いずれもガスバリア性を有するものであることを特徴とするものである。
The invention set forth in claim 2 is the invention set forth in
請求項1に記載の味噌収納用ガゼット袋は、粘性の高い半固形物である味噌を収納(充填)する際に、上部において大きく開口する開口部から容易に収納することができる(味噌を吐出するノズル等を引っ掛かけたりすることなく収納することができる)。また、上端縁をヒートシールすることによって容易に密封することができる。その上、所定厚みの合成樹脂フィルムによって左右および底部に折り込み部を設けた袋状(ガゼット形状)に形成されているので、味噌を充填すると充填部分が略直方体状になって安定した状態で起立させることが可能となるため、店頭や冷蔵庫内の小さなスペースで効率良く収納することができる。さらに、味噌を充填した際に、底部の折り込み部が拡がって矩形の底面を形成するため、味噌を残さないように掻き出すことが可能となる。また、胴材や折り込み材の表面等に内容物の商品名や性状を印刷することができるため、少ない部材点数で安価に包装することができる。
The miso storage gusset bag according to
また、請求項1に記載の味噌収納用ガゼット袋は、胴材および折り込み材を構成する合成樹脂フィルムがPET層を含む積層フィルムであるため、胴材や折り込み材の強度が高く、耐水性にも優れているので、きわめて長期間に亘って味噌を保管することができる。その上、寸法安定性に優れているため、製袋機でロール状のフィルムから連続的に製袋する際に、歩留まり良く製袋することができる。
Further, in the miso storage gusset bag according to
請求項2に記載の味噌用収納容器は、胴材および折り込み材を構成する合成樹脂フィルムがガスバリア性を有するものであるため、長期間に亘って味噌の品質を保持することができる。
In the storage container for miso according to claim 2 , since the synthetic resin film constituting the body material and the insert material has gas barrier properties, the quality of the miso can be maintained for a long period of time.
以下、本発明に係る味噌収納用ガゼット袋の一実施形態について詳細に説明する。本発明に係る味噌収納用ガゼット袋は、柔軟な合成樹脂フィルムによって形成されたものである。ここでいう合成樹脂フィルムとは、合成樹脂フィルムを積層した積層フィルム、あるいは合成樹脂フィルムと紙やアルミ箔等とを積層した積層フィルム、共押出フィルム等のことである。味噌収納用ガゼット袋に用いられる合成樹脂フィルムは、少なくとも片面(内面)が熱接着性(熱融着性)を有している必要がある。また、当該味噌収納用ガゼット袋は、味噌の品質を保持するために、ガスバリア性を有していると好ましい。具体的には、20℃65%RHにおける酸素透過度が20cc/m2・day・atm以下であると好ましく、10cc/m2・day・atm以下であるとより好ましく、1cc/m2・day・atm以下であるとさらに好ましい。 Hereinafter, one embodiment of the miso storage gusset bag according to the present invention will be described in detail. The miso storage gusset bag according to the present invention is made of a flexible synthetic resin film. The synthetic resin film here refers to a laminated film made by laminating synthetic resin films, a laminated film made by laminating a synthetic resin film and paper, aluminum foil, etc., a coextruded film, and the like. The synthetic resin film used in the gusset bag for storing miso must have thermal adhesion (thermal fusibility) on at least one side (inner surface). Moreover, it is preferable that the miso storage gusset bag has gas barrier properties in order to maintain the quality of the miso. Specifically, the oxygen permeability at 20° C. and 65% RH is preferably 20 cc/m 2 ·day · atm or less, more preferably 10 cc/m 2 ·day · atm or less, and 1 cc/m 2 ·day - It is more preferable that it is below ATM.
そして、そのような合成樹脂フィルムとしては、たとえば、バリア層と熱接着層とを含む多層フィルムを用いることができる。バリア層としては、エチレン-ビニルアルコール共重合体フィルム、バリア層としては、エチレン-ビニルアルコール共重合体フィルム、あるいはエチレン-ビニルアルコール共重合体フィルムまたはポリメタキシリレンアジパミドフィルムのナイロン等との共押し出しフィルムを挙げることができる。また、酸化ケイ素(シリカ)や酸化アルミニウム(アルミナ)が蒸着されたポリエステル等のフィルム、アルミニウム箔やアルミニウムが蒸着されたポリエステルやナイロン等のフィルムを用いても良い。熱接着層としては、たとえば、ポリエチレンや無延伸ポリプロピレン等のフィルムを用いることができる。 As such a synthetic resin film, for example, a multilayer film including a barrier layer and a thermal adhesive layer can be used. The barrier layer is an ethylene-vinyl alcohol copolymer film, the barrier layer is an ethylene-vinyl alcohol copolymer film, or an ethylene-vinyl alcohol copolymer film or a polymethaxylylene adipamide film with nylon or the like. Mention may be made of coextruded films. Further, a film made of polyester or the like on which silicon oxide (silica) or aluminum oxide (alumina) is vapor-deposited, aluminum foil or a film made of polyester or nylon on which aluminum is vapor-deposited may be used. As the thermal adhesive layer, for example, a film of polyethylene, unstretched polypropylene, or the like can be used.
また、本発明に係る味噌収納用ガゼット袋は、構成部材(表裏の胴材、左右両側および下側の折り込み材)である合成樹脂フィルムが、いずれもPET層を含む積層フィルムであると好ましく、合成樹脂フィルムの熱接着性の層以外のベース層(あるいはベースフィルム)がナイロン層の外側にPET層を積層したものであると、ナイロンの強度とPETの防水性および寸法安定性とを同時に発現させることができ、味噌収納用ガゼット袋が味噌の収納に適したものとなるのでより好ましい。そのような合成樹脂フィルムのより好ましい具体的として、以下の積層フィルムを挙げることができる(なお、以下の積層フィルムには、必要に応じて、他の樹脂からなるフィルムを挟み込んだり積層したりすることも可能である)。
a.PETを積層した二軸延伸ナイロンフィルム、エチレン-ビニルアルコール共重合体フィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
b.PETフィルム、ナイロンとポリメタキシリレンアジパミドとの共押し出しフィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
c.PETフィルム、ナイロンとエチレンビニルアルコール共重合体との共押し出しフィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
d.酸化ケイ素蒸着PETフィルム、ナイロンフィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
e.酸化アルミニウム蒸着PETフィルム、ナイロンフィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
f.PETフィルム、エチレン-ビニルアルコール共重合体フィルム、直鎖状低密度ポリエチレンフィルムを積層してなる積層フィルム
Further, in the miso storage gusset bag according to the present invention, the synthetic resin films that are the constituent members (the front and back body materials, the left and right sides, and the lower folding materials) are preferably laminated films containing a PET layer, If the base layer (or base film) other than the thermoadhesive layer of the synthetic resin film is a PET layer laminated on the outside of a nylon layer, it will simultaneously exhibit the strength of nylon and the waterproofness and dimensional stability of PET. This is more preferable because the gusset bag for storing miso becomes suitable for storing miso. More preferable examples of such synthetic resin films include the following laminated films (in addition, films made of other resins may be sandwiched or laminated in the following laminated films as necessary). ).
a. A laminated film formed by laminating a biaxially stretched nylon film laminated with PET, an ethylene-vinyl alcohol copolymer film, and a linear low-density polyethylene film b. A laminated film formed by laminating a PET film, a coextruded film of nylon and polymethaxylylene adipamide, and a linear low-density polyethylene film c. A laminated film formed by laminating a PET film, a coextruded film of nylon and ethylene vinyl alcohol copolymer, and a linear low-density polyethylene film d. A laminated film formed by laminating a silicon oxide deposited PET film, a nylon film, and a linear low-density polyethylene film e. Laminated film formed by laminating aluminum oxide vapor-deposited PET film, nylon film, and linear low-density polyethylene filmf. Laminated film made by laminating PET film, ethylene-vinyl alcohol copolymer film, and linear low-density polyethylene film.
また、合成樹脂フィルムの厚み(総厚み)は、70μm以上140μm未満の範囲内であることが必要である。合成樹脂フィルムの厚みが70μmを下回ると、合成樹脂フィルムの強度が不十分となる。また、合成樹脂フィルムの“こし(スティフネス)”がなくなることで、味噌収納用ガゼット袋に味噌を充填したときに味噌収納用ガゼット袋が膨らみやすく、外周に若干のシワや弛みが生じて見栄えが悪くなり、店頭でのディスプレイ効果が低減するので好ましくない。反対に、合成樹脂フィルムの厚みが140μmを上回ると、マチの部分等において味噌収納用ガゼット袋をハサミで裁断することが難しくなるので好ましくない。なお、合成樹脂フィルムの厚みは、70μm以上110μm未満であるとより好ましい。 Further, the thickness (total thickness) of the synthetic resin film needs to be within the range of 70 μm or more and less than 140 μm. If the thickness of the synthetic resin film is less than 70 μm, the strength of the synthetic resin film will be insufficient. In addition, since the synthetic resin film loses its "stiffness", the miso storage gusset bag tends to swell when filled with miso, causing slight wrinkles and slack on the outer periphery, resulting in an unattractive appearance. This is undesirable because it reduces the display effect at stores. On the other hand, if the thickness of the synthetic resin film exceeds 140 μm, it is not preferable because it becomes difficult to cut the gusset bag for storing miso with scissors at the gusset part, etc. In addition, the thickness of the synthetic resin film is more preferably 70 μm or more and less than 110 μm.
加えて、上記したa~fの積層フィルム(第0017段落)を用いる場合には、各層の厚みを以下のように調整すると、フィルムの強度、“こし”の強さ、ハサミで裁断するときの裁断容易性が、ともに良好なものとなるので好ましい(なお、以下の記載における“数値”~“数値”μmは、“数値”μm以上“数値”μm以下を意味する)。
a.PETを積層した二軸延伸ナイロンフィルム(12~18μm)/エチレン-ビニルアルコール共重合体フィルム(9~15μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
b.PETフィルム(9~15μm)/ナイロンとポリメタキシリレンアジパミドとの共押し出しフィルム(12~18μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
c.PETフィルム(9~15μm)/ナイロンとエチレンビニルアルコール共重合体との共押し出しフィルム(12~18μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
d.酸化ケイ素蒸着PETフィルム(9~15μm)/ナイロンフィルム(12~18μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
e.酸化アルミニウム蒸着PETフィルム(9~15μm)/ナイロンフィルム(12~18μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
f.PETフィルム(9~15μm)/エチレン-ビニルアルコール共重合体フィルム(9~15μm)/直鎖状低密度ポリエチレンフィルム(75~85μm)
In addition, when using the laminated films a to f described above (paragraph 0017), adjusting the thickness of each layer as follows will improve the strength of the film, the strength of the strain, and the ease of cutting with scissors. This is preferable because both the ease of cutting becomes good (in the following description, "numerical value" to "numerical value" μm mean "numerical value" μm or more and "numerical value" μm or less).
a. Biaxially stretched nylon film laminated with PET (12-18 μm) / Ethylene-vinyl alcohol copolymer film (9-15 μm) / Linear low-density polyethylene film (75-85 μm)
b. PET film (9-15 μm) / Co-extruded film of nylon and polymethaxylylene adipamide (12-18 μm) / Linear low-density polyethylene film (75-85 μm)
c. PET film (9-15 μm) / coextruded film of nylon and ethylene vinyl alcohol copolymer (12-18 μm) / linear low-density polyethylene film (75-85 μm)
d. Silicon oxide vapor-deposited PET film (9-15 μm) / Nylon film (12-18 μm) / Linear low-density polyethylene film (75-85 μm)
e. Aluminum oxide vapor-deposited PET film (9-15 μm) / Nylon film (12-18 μm) / Linear low-density polyethylene film (75-85 μm)
f. PET film (9-15μm) / Ethylene-vinyl alcohol copolymer film (9-15μm) / Linear low-density polyethylene film (75-85μm)
また、本発明に係る味噌収納用ガゼット袋は、上記した合成樹脂フィルムをガゼット袋状にすることによって製造される。すなわち、表裏の胴材の左右の側部および下部(底部)に、それぞれ、二つ折りされた折り込み材を挟み込むという態様で積層し、その積層体の側部および下部をヒートシール(熱融着)することによって製造される。加えて、本発明に係る味噌収納用ガゼット袋は、表側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の前側の端縁際にヒートシールされているとともに、裏側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の後側の端縁際にヒートシールされていることが必要である。味噌収納用ガゼット袋をそのように構成することによって、上部の開口部を大きく開口させることが可能となり、内容物である味噌を収納(充填)する際や味噌を掻き出す際に、それらの作業を容易なものとすることが可能となる。 Moreover, the gusset bag for storing miso according to the present invention is manufactured by forming the above-described synthetic resin film into a gusset bag shape. That is, the left and right sides and lower part (bottom) of the front and back trunk materials are laminated with two-folded inserts sandwiched between them, and the sides and lower part of the laminate are heat-sealed (thermal fusion). Manufactured by In addition, in the miso storage gusset bag according to the present invention, substantially the entire left and right edges of the front body material are heat-sealed to the front edges of the left and right inserts, respectively, and It is necessary that substantially the entirety of the left and right edges of the backside body material be heat-sealed to the rear edges of the left and right folded pieces, respectively. By configuring the miso storage gusset bag in this way, the opening at the top can be opened wide, making it easier to store (fill) the miso contents and scrape out the miso. It becomes possible to make it easy.
各ヒートシール(側方シール部、底シール部の形成等)および裁断は、ガゼット製袋機を用いて、一連の加工として実施することも可能であるし、バッチ(非一連)の加工として実施することも可能である。なお、ヒートシールの温度は、特に限定されないが、ポリエチレン(直鎖状低密度ポリエチレン)フィルムを熱接着性フィルムとする合成樹脂フィルムを用いる場合には、170~210℃の範囲内にするのが好ましい。 Each heat seal (forming side seals, bottom seals, etc.) and cutting can be performed as a series of processes using a gusset bag making machine, or can be performed as a batch (non-series) process. It is also possible to do so. Note that the heat sealing temperature is not particularly limited, but when using a synthetic resin film made of polyethylene (linear low-density polyethylene) film as a heat-adhesive film, it is recommended that the temperature be within the range of 170 to 210°C. preferable.
また、本発明に係る味噌収納用ガゼット袋は、左右両側に折り込み部(所謂、マチ)を設けるとともに、下側(底部)にも折り込み部を設けたものであることが必要である。そのような味噌収納用ガゼット袋を用いることによって、味噌収納用ガゼット袋の自立性が高くなり、味噌収納用ガゼット袋のみで冷蔵庫内等へ収納したり、商品棚で陳列したりすることが可能となる。 Further, the miso storage gusset bag according to the present invention needs to be provided with fold-in portions (so-called gussets) on both left and right sides, and also with a fold-in portion on the lower side (bottom). By using such a miso storage gusset bag, the miso storage gusset bag becomes highly self-reliant and can be stored in a refrigerator or displayed on a product shelf with just the miso storage gusset bag. becomes.
また、味噌収納用ガゼット袋は、正面視で概ね矩形に形成されるが、その大きさは特に限定されず、高さ、幅ともに概ね50~350mmの範囲内で、必要に応じて調整することができる。また、味噌収納用ガゼット袋は、左右両側および下側(底部)に折り込み部(内向きに二つ折りに折り込んだ部分)を設けたものであるが、当該折り込み部の幅(二つ折り部分の幅)も、特に限定されず、概ね15~175mmの範囲内で必要に応じて調整することができる。 In addition, the miso storage gusset bag is generally rectangular in shape when viewed from the front, but its size is not particularly limited, and both the height and width may be adjusted as necessary within the range of approximately 50 to 350 mm. I can do it. In addition, the miso storage gusset bag has fold-in portions (parts folded inward in half) on both the left and right sides and the bottom (bottom); ) is also not particularly limited, and can be adjusted as necessary within the range of approximately 15 to 175 mm.
さらに、本発明に係る味噌収納用ガゼット袋は、表裏の胴材の幅(左右の幅)aに対する左右の各折り込み材の幅b(すなわち、折り込み部の幅の2倍)の割合(すなわち、b/a)が0.6以上1.0未満であると好ましい(図1~図3参照)。b/aの値が0.6を下回ると、味噌を充填した味噌収納用ガゼット袋の前後の厚みが左右の幅に比べて大幅に薄いものとなり、味噌が内部で左右前後に偏在した場合に倒れやすくなるので好ましくない。反対に、b/aの値が1.0を上回ると、左右の折り込み材が中央(幅方向の中央)で干渉することとなり、製袋が困難になるので好ましくない。また、味噌を充填したときの味噌の高さを「m」としたときに、表裏の胴材の幅(左右の幅)aに対する味噌の高さmの割合(すなわち、m/a)が0.7以上1.5以下であると、味噌を取り出すときに安定して起立させた状態を保持しやすいので好ましい。 Further, in the miso storage gusset bag according to the present invention, the ratio of the width b of each left and right folding material (that is, twice the width of the folded part) to the width a of the front and back body materials (left and right width) (i.e., b/a) is preferably 0.6 or more and less than 1.0 (see FIGS. 1 to 3). If the value of b/a is less than 0.6, the thickness of the front and back of the miso storage gusset bag filled with miso will be significantly thinner than the left and right width, and if the miso is unevenly distributed inside the bag, This is not desirable as it can easily fall down. On the other hand, if the value of b/a exceeds 1.0, the left and right folding materials will interfere at the center (the center in the width direction), making bag making difficult, which is not preferable. Also, when the height of miso when filled with miso is "m", the ratio of the height m of miso to the width (left and right width) a of the body material on the front and back (that is, m/a) is 0. If it is .7 or more and 1.5 or less, it is preferable because the miso can be stably maintained in an upright state when taken out.
加えて、味噌収納用ガゼット袋は、所定の高さ位置において水平方向に裁断して開封する開封予定位置が設定されていると好ましい。すなわち、破線やハサミのマーク等を印刷すること等によって裁断(開封)すべき位置が表示されていたり、側部の裁断すべき位置に水平方向への裁断のきっかけとなるノッチや切れ込みあるいは複数の細孔等の易開封手段が設けられていたり、手で裁断可能なように複数の切線、貫通あるいは未貫通の細孔やミシン目等が水平方向に直線状に連続的に設けられていたりすると好ましい。なお、開封予定位置は、内部に充填される味噌の上面より上側の任意の高さ位置に設定するのが好ましい。 In addition, it is preferable that the miso storage gusset bag has a scheduled opening position set at a predetermined height position where the bag is cut horizontally and opened. In other words, the position to be cut (opened) is indicated by printing dashed lines or scissor marks, etc., or there are notches, notches, or multiple cuts at the cutting position on the side that will trigger horizontal cutting. If an easy-to-open means such as a pore is provided, or if multiple cutting lines, through or non-through pores, perforations, etc. are provided continuously in a horizontal straight line so that it can be cut by hand. preferable. In addition, it is preferable that the planned opening position is set at an arbitrary height position above the top surface of the miso filled inside.
以下、本発明に係る味噌収納用ガゼット袋について実施例に基づいてより詳細に説明するが、本発明は、かかる実施例の態様に何ら限定されるものではなく、本発明の趣旨を逸脱しない範囲で、適宜変更することが可能である。また、実施例、比較例における物性、特性の評価方法は以下の通りである。 Hereinafter, the miso storage gusset bag according to the present invention will be described in more detail based on Examples, but the present invention is not limited to the embodiments of such Examples in any way, and the scope of the present invention does not depart from the spirit of the present invention. It is possible to change it as appropriate. In addition, the methods for evaluating physical properties and characteristics in Examples and Comparative Examples are as follows.
<味噌取り出し時の安定性>
約750gの味噌(マルコメ株式会社製 「料亭の味」)を常温にて収納(充填)して水平面に載置し、味噌をスプーン(15ccの計量スプーン)で3回繰り返しすくい出したときの味噌収納用ガゼット袋の安定感を、下記の3段階で官能評価した。
○:ぐらつくことなく鉛直方向に起立した状態を保持した
△:味噌の残量や偏りによって、わずかにぐらつくときがあるが、略鉛直方向に起立した状態を保持した
×:味噌の残量や偏りによって、ぐらついて安定して起立しないときが多かった
<Stability when removing miso>
Approximately 750g of miso (“Ryotei no Aji” manufactured by Marukome Co., Ltd.) was stored (filled) at room temperature, placed on a horizontal surface, and the miso was scooped out three times with a spoon (15cc measuring spoon). The stability of the storage gusset bag was sensory evaluated on the following three levels.
○: Maintained standing vertically without wobbling △: Occasionally it wobbled slightly depending on the remaining amount of miso or unevenness, but maintained an approximately vertical state ×: Remaining amount of miso or unevenness Due to this, I often found myself wobbling and unable to stand up stably.
<裁断容易性>
味噌を充填して密封した味噌収納用ガゼット袋の開封予定位置Cを、ハサミ(小型の工作用ハサミ)を利用して裁断したときの裁断のし易さを、下記の3段階で官能評価した。
○:大きな力を加えなくても裁断することができる
△:かなり大きな力を加えないと裁断することができない
×:手の力では裁断することができない
<Ease of cutting>
A sensory evaluation was conducted on the ease of cutting using scissors (small craft scissors) at the planned opening position C of a miso storage gusset bag filled with miso and sealed, using the following three levels. .
○: Can be cut without applying much force △: Cannot be cut without applying considerable force ×: Cannot be cut with hand force
[実施例1]
<味噌収納用ガゼット袋の製造>
ガゼット製袋機を利用して、下記a~cの工程によって、左右両側および下側に折り込み部を有する実施例1の味噌収納用ガゼット袋を形成した。
a.片面が熱接着性を有する長尺な2枚の合成樹脂フィルム(すなわち、表裏の胴材)を、その熱接着性の面が対向するように配置させる
b.配置させた2枚の合成樹脂フィルム(すなわち、表裏の胴材)の間に、左右の折り込み部を形成するための折り込み材(胴材と同様な合成樹脂フィルムを二つ折りしてなるもの)と、下側(底部)の折り込み部を形成するための折り込み材(胴材と同様な合成樹脂フィルムを二つ折りしてなるもの)とを連続的に挟み込んで積層する
c.上記の積層物を所定の大きさ(縦×横=220mm×105mm)に裁断するのと同時に、積層物の外周(左右の両側縁際および底縁際)を所定の温度(約190℃)でヒートシールする
[Example 1]
<Manufacture of gusset bags for storing miso>
Using a gusset bag-making machine, a gusset bag for storing miso according to Example 1 having folded portions on both left and right sides and on the bottom was formed by the following steps a to c.
a. Arranging two long synthetic resin films (i.e., front and back body materials) each having thermal adhesive properties on one side so that their thermal adhesive surfaces face each other b. A folding material (made by folding the same synthetic resin film as the body material in half) to form left and right folded parts between the two arranged synthetic resin films (i.e., the front and back body materials). , a folding material (made by folding the same synthetic resin film as the body material in half) for forming the lower (bottom) folding part is continuously sandwiched and laminated; c. At the same time as cutting the above laminate into a predetermined size (length x width = 220 mm x 105 mm), cut the outer periphery of the laminate (both left and right edges and bottom edge) at a predetermined temperature (approximately 190°C). heat seal
なお、上記の味噌収納用ガゼット袋の製造においては、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、総厚15μmのPETを積層した二軸延伸ナイロンフィルム(ベースフィルム)の上に、厚さ12μmのエチレン-ビニルアルコール共重合体フィルムを積層し、さらにその上に、厚さ80μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み107μmの多層フィルム)を使用した。なお、ベースフィルムにおいては、ナイロン層がPET層に比べて厚くなっている。 In the production of the above-mentioned miso storage gusset bag, a biaxially stretched nylon film laminated with PET with a total thickness of 15 μm (base A transparent film made by laminating an ethylene-vinyl alcohol copolymer film with a thickness of 12 μm on top of the film, and then a linear low-density polyethylene film (thermal adhesive film) with a thickness of 80 μm on top of that. A synthetic resin film (multilayer film with a total thickness of 107 μm) was used. Note that in the base film, the nylon layer is thicker than the PET layer.
<味噌収納用ガゼット袋の構成>
図1、図2は、製造された実施例1の味噌収納用ガゼット袋Pを示したものであり、味噌収納用ガゼット袋Pは、表裏2枚の略矩形の胴材2a,2b、それらの胴材2a,2bの左右の両端縁際に挟み込まれた折り込み材3a,3b、および、底部の折り込み材4によって、正面視が略矩形(縦長な長方形状)となるように形成されており、縦×横=220mm×105mmの大きさを有している。表裏の各胴材2a,2bは、直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)層を内側にした状態で配置されている。
<Configuration of miso storage gusset bag>
1 and 2 show the produced gusset bag P for storing miso of Example 1, and the gusset bag P for storing miso consists of two substantially
また、図3は、味噌収納用ガゼット袋Pにおける左右両サイドの折り込み材3a,3bおよび底部の折り込み材4を示したものである。左右の各折り込み材3a,3bは、上記した合成樹脂フィルムからなる幅95mmの縦長な帯状体を、直鎖状低密度ポリエチレンフィルム層が外向きになるように、所定の幅(約47.5mm幅)の二つ折りにした構造を有している。それらの折り込み材3a,3bは、直鎖状低密度ポリエチレンフィルム層を表裏の胴材2a,2bの裏面に対向させた状態で配置されている。
Moreover, FIG. 3 shows the
また、左右の各折り込み材3a,3bの下端際の部分は、それぞれ、断面(鉛直な断面)M字状になるように中側へ斜めに折り曲げられており、それらの屈曲部分F,Fの内部に、幅95mmの横長な帯状体を二つ折りにしてなる底部の折り込み材4の左右の両端際が挟み込まれている。なお、当該底部の折り込み材4は、直鎖状低密度ポリエチレンフィルム層が外向きになるように、所定の幅(約47.5mm幅)の二つ折りにした構造を有している。そして、それらの左右の折り込み材3a,3bおよび底部の折り込み材4の表裏の外側に、胴材2a,2bが重ねられている。
In addition, the lower end portions of the left and
そして、胴材2a,2bと折り込み材3a,3bとの積層部分の内の端縁際の部分をヒートシールすることによって幅約8mmの側方シール部5,5・・が形成されている。当該側方シール部5,5・・の上側の部分においては、表側の胴材2aの裏面と折り込み材3a,3bの裏面、および、裏側の胴材2bの裏面と折り込み材3a,3bの裏面が、それぞれ融着し合っている。一方、側方シール部5,5・・の下端際の部分においては、断面M字状の屈曲部分Fの外側では、表側の胴材2aの裏面と折り込み材3a,3bの裏面、および、裏側の胴材2bの裏面と折り込み材3a,3bの裏面が、それぞれ融着し合っており、屈曲部分Fの内側では、折り込み材3a,3bの裏面と底部の折り込み材4の裏面が融着し合っている。
また、底部の折り込み部(折り込み材4が挟み込まれた部分)の下端縁際の部分を一定の高さ(約8mm)の帯状にヒートシールすることによって底シール部15,15が形成されている。それらの底シール部15,15においては、表側の胴材2aの裏面と折り込み材4の裏面、および、裏側の胴材2bの裏面と折り込み材4の裏面が、それぞれ融着し合っている。
In addition,
そして、味噌収納用ガゼット袋Pにおいては、底部の折り込み材4の外周(周縁際)が、表裏の胴材2a,2bの下端際および左右の各折り込み材3a,3bの下端際にヒートシールされた状態になっている。また、表側の胴材2aの左右の端縁際全体が、それぞれ、左右の各折り込み材3a,3bの前側の端縁際にヒートシールされた状態になっているとともに、裏側の胴材2bの左右の端縁際全体が、それぞれ、左右の各折り込み材3a,3bの後側の端縁際にヒートシールされた状態になっている。
In the miso storage gusset bag P, the outer periphery (near the periphery) of the
また、上記の如く製袋された味噌収納用ガゼット袋Pの所定の高さ位置(上端縁から約30mm下側の位置)には、ハサミ等によって裁断(開封)すべき位置を示す破線C(開封予定位置)が印刷によって表示されている。なお、破線Cは、折り込み部3a,3bおよび胴材2a,2bを横断するように周状に印刷されている(図1、図2参照)。
Furthermore, at a predetermined height position (approximately 30 mm below the upper edge) of the miso storage gusset bag P made as described above, a broken line C ( The expected opening position) is displayed by printing. Note that the broken line C is printed in a circumferential manner so as to cross the folded
<味噌収納用ガゼット袋の評価>
上記した実施例1の味噌収納用ガゼット袋Pの上端縁の開口部O(左右の側方シール部5,5同士の間のヒートシールされていない部分)から味噌(750g)を充填した。充填は、味噌の表面が概ね平らになるように行った。充填後の味噌の高さ(m)は、約90mmであった。なお、味噌の充填時には、左右の各折り込み材3a,3bを拡げることで大きく開口したから開口部Oから非常に容易に充填することが可能であった。そして、味噌を充填した後に、上端縁の開口部Oにおいて、折り込み材3a,3bを畳んで元に戻してヒートシールすることにより、開口部Oの中央で胴材2a,2bを融着させとともに、その左右では胴材2a,2bと対向する折り込み材3a,3bとを融着させ、一定の高さで(約5mm~10mm)の帯状の頭シール部を形成することによって味噌収納用ガゼット袋Pを密封した。なお、頭シール部は、左右の側方シール部5,5と重なり合うように形成した。
<Evaluation of miso storage gusset bag>
Miso (750 g) was filled through the opening O (the part that was not heat-sealed between the left and right
味噌収納用ガゼット袋Pに上記の如く味噌を収納(充填)させると、折り込み材3a,3bが拡がって矩形状の側面を形成するとともに、底部付近において折り込み材4が拡がって矩形状の底面(左右幅=105mm×前後幅=95mm)を形成し、安定した状態で起立させることが可能であった。そして、その(味噌を収納した)味噌収納用ガゼット袋Pを用いて、上記した方法で「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋Pの性状とともに表1に示す。
When miso is stored (filled) in the miso storage gusset bag P as described above, the
[実施例2]
味噌収納用ガゼット袋の製造時に、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、実施例1と同じ総厚15μmのPETを積層した二軸延伸ナイロンフィルム(ベースフィルム)の上に、厚さ12μmのエチレン-ビニルアルコール共重合体フィルムを積層し、さらにその上に、厚さ50μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み77μmの多層フィルム)を使用した。それ以外は、実施例1と同様にして、実施例2の味噌収納用ガゼット袋を得た。そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Example 2]
When manufacturing the gusset bag for storing miso, a biaxially stretched nylon film (base) laminated with PET with a total thickness of 15 μm, the same as in Example 1, was used as the folding material for forming the front and back body materials, left and right folded parts, and the lower folded parts. A transparent film made by laminating a 12 μm thick ethylene-vinyl alcohol copolymer film on top of the 50 μm thick linear low density polyethylene film (thermal adhesive film). A synthetic resin film (multilayer film with a total thickness of 77 μm) was used. Other than that, a miso storage gusset bag of Example 2 was obtained in the same manner as in Example 1. Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
[実施例3]
味噌収納用ガゼット袋の製造時に、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、実施例1と同じ総厚15μmのPETを積層した二軸延伸ナイロンフィルム(ベースフィルム)の上に、厚さ12μmのエチレン-ビニルアルコール共重合体フィルムを積層し、さらにその上に、厚さ100μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み127μmの多層フィルム)を使用した。それ以外は、実施例1と同様にして、実施例3の味噌収納用ガゼット袋を得た。そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Example 3]
When manufacturing the gusset bag for storing miso, a biaxially stretched nylon film (base) laminated with PET with a total thickness of 15 μm, the same as in Example 1, was used as the folding material for forming the front and back body materials, left and right folded parts, and the lower folded parts. A transparent film made by laminating a 12 μm thick ethylene-vinyl alcohol copolymer film on top of the film, and then a 100 μm thick linear low-density polyethylene film (thermal adhesive film) on top of that. A synthetic resin film (multilayer film with a total thickness of 127 μm) was used. Other than that, a miso storage gusset bag of Example 3 was obtained in the same manner as in Example 1. Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
[実施例4,5]
味噌収納用ガゼット袋の製造時に、左右の折り込み材3a,3bの幅(拡げた幅)aおよび底部の折り込み材4の幅(拡げた幅)bを、それぞれ、50mm、70mmに変更し、それ以外は実施例1と同様にして、実施例4,5の味噌収納用ガゼット袋を得た。
そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。なお、味噌が充填された実施例4の味噌収納用ガゼット袋における味噌の高さは210mmであり(m/a=2.0)、味噌が充填された実施例5の味噌収納用ガゼット袋における味噌の高さは130mmであった(m/a=1.3)。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Example 4, 5]
When manufacturing the miso storage gusset bag, the width (expanded width) a of the left and
Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The height of miso in the miso storage gusset bag of Example 4 filled with miso was 210 mm (m/a = 2.0), and the height of the miso in the miso storage gusset bag of Example 5 filled with miso was 210 mm (m/a = 2.0). The height of the miso was 130 mm (m/a=1.3). The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
[実施例6]
味噌収納用ガゼット袋の製造時に、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、厚さ15μmのPETフィルム(ベースフィルム)の上に、厚さ12μmのポリメタキシリレンアジパミドとナイロンの共押し出しフィルムを積層し、さらにその上に、厚さ80μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み107μmの多層フィルム)を使用した。それ以外は、実施例1と同様にして、実施例6の味噌収納用ガゼット袋を得た。そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Example 6]
When manufacturing gusseted bags for storing miso, a 12 μm thick polymetal film was used as a folding material to form the front and back body materials, left and right folded parts, and the lower folded portions. A transparent synthetic resin film (total thickness: 107 μm) made by laminating a co-extruded film of silylene adipamide and nylon, and then laminating a linear low-density polyethylene film (thermal adhesive film) with a thickness of 80 μm on top of the co-extruded film of silylene adipamide and nylon. multilayer film) was used. Other than that, a miso storage gusset bag of Example 6 was obtained in the same manner as in Example 1. Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
[実施例7]
味噌収納用ガゼット袋の製造時に、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、厚さ15μmのナイロンフィルム(ベースフィルム)の上に、厚さ12μmのエチレン-ビニルアルコール共重合体フィルムを積層し、さらにその上に、厚さ80μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み107μmの多層フィルム)を使用した。それ以外は、実施例1と同様にして、実施例7の味噌収納用ガゼット袋を得た。そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Example 7]
When manufacturing gusseted bags for storing miso, 12 μm thick ethylene film was placed on a 15 μm thick nylon film (base film) as a folding material to form the front and back body materials, left and right folded parts, and bottom folded parts. A transparent synthetic resin film (multilayer film with a total thickness of 107 μm) made by laminating a vinyl alcohol copolymer film and further laminating a linear low-density polyethylene film (thermal adhesive film) with a thickness of 80 μm on top of the vinyl alcohol copolymer film. It was used. Other than that, a miso storage gusset bag of Example 7 was obtained in the same manner as in Example 1. Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
[比較例1]
味噌収納用ガゼット袋の製造時に、表裏の胴材、左右および下側の折り込み部を形成するための折り込み材として、実施例1と同じ総厚15μmのPETを積層した二軸延伸ナイロンフィルム(ベースフィルム)の上に、厚さ12μmのエチレン-ビニルアルコール共重合体フィルムを積層し、さらにその上に、厚さ150μmの直鎖状低密度ポリエチレンフィルム(熱接着性フィルム)を積層してなる透明な合成樹脂フィルム(総厚み177μmの多層フィルム)を使用した。それ以外は、実施例1と同様にして、比較例1の味噌収納用ガゼット袋を得た。そして、得られた味噌収納用ガゼット袋に味噌を収納し、その味噌収納後の味噌収納用ガゼット袋を用いて、実施例1と同様に「味噌取り出し時の安定性」および「裁断容易性」を評価した。評価結果を味噌収納用ガゼット袋の性状とともに表1に示す。
[Comparative example 1]
When manufacturing the gusset bag for storing miso, a biaxially stretched nylon film (base) laminated with PET with a total thickness of 15 μm, the same as in Example 1, was used as the folding material for forming the front and back body materials, left and right folded parts, and the lower folded parts. A transparent film made by laminating an ethylene-vinyl alcohol copolymer film with a thickness of 12 μm on top of the film, and then a linear low-density polyethylene film (thermal adhesive film) with a thickness of 150 μm on top of that. A synthetic resin film (multilayer film with a total thickness of 177 μm) was used. Other than that, a miso storage gusset bag of Comparative Example 1 was obtained in the same manner as in Example 1. Then, miso was stored in the obtained miso storage gusset bag, and the miso storage gusset bag after storing the miso was used to improve the "stability when taking out the miso" and the "ease of cutting" in the same manner as in Example 1. was evaluated. The evaluation results are shown in Table 1 along with the properties of the miso storage gusset bag.
表1から、実施例1~6の味噌収納用ガゼット袋は、何れも、味噌取り出し時の安定性、裁断容易性ともに良好であることが分かる。それに対して、合成樹脂フィルムの厚みが特許請求の範囲の上限よりも大きい比較例1の味噌収納用ガゼット袋は、裁断容易性が劣ることが分かる。 From Table 1, it can be seen that the miso storage gusset bags of Examples 1 to 6 were all good in both stability when taking out the miso and ease of cutting. On the other hand, it can be seen that the gusset bag for storing miso of Comparative Example 1, in which the thickness of the synthetic resin film is larger than the upper limit of the claimed range, is inferior in ease of cutting.
<味噌収納用ガゼット袋の変更例>
本発明に係る味噌収納用ガゼット袋の構成は、上記した各実施形態の態様に何ら限定されるものではなく、胴材や折り込み部を形成するための合成樹脂フィルムの材質、大きさ(高さ、幅、マチの幅、マチの構造等)等の構成を、本発明の趣旨を逸脱しない範囲で、必要に応じて適宜変更できる。
<Example of modification of miso storage gusset bag>
The configuration of the miso storage gusset bag according to the present invention is not limited to the aspects of each of the above-described embodiments, and may vary depending on the material, size (height, , width, gusset width, gusset structure, etc.) can be changed as necessary without departing from the spirit of the present invention.
たとえば、胴材や折り込み部を形成するための合成樹脂フィルムは、上記実施形態の如く、PETフィルムあるいはナイロンフィルムとエチレン-ビニルアルコール共重合体フィルムとポリエチレンフィルム(直鎖状低密度ポリエチレンフィルム)とを積層させたものに限定されず、他の材質の合成樹脂フィルムを積層させたものでも良いし、金属箔や金属蒸着フィルム等を積層させたものでも良い。なお、合成樹脂フィルムとして、上記実施形態の如く、PETを積層した二軸延伸ナイロンフィルムとエチレン-ビニルアルコール共重合体フィルムと直鎖状低密度ポリエチレンフィルム等のPETフィルムを含む積層フィルムを用いた場合には、胴材や折り込み材の強度が良好なものとなるとともに製造が容易なものとなる。また、酸素バリア性および寸法安定性に優れるため、味噌用の包装体として好適なものとなる。 For example, as in the above embodiment, the synthetic resin film for forming the body material and the folded portion is a PET film or a nylon film, an ethylene-vinyl alcohol copolymer film, and a polyethylene film (linear low-density polyethylene film). The material is not limited to a layered layer, but may be a layered layer of synthetic resin films made of other materials, or a layered layer of metal foil, metal-deposited film, or the like. As the synthetic resin film, as in the above embodiment, a laminated film including a biaxially stretched nylon film laminated with PET, an ethylene-vinyl alcohol copolymer film, and a PET film such as a linear low-density polyethylene film was used. In this case, the strength of the body material and folding material is good, and manufacturing is easy. Furthermore, since it has excellent oxygen barrier properties and dimensional stability, it is suitable as a package for miso.
また、下側(底部)の折り込み部の設置方法は、上記実施形態の如く、左右の折り込み材の下端縁際の部分を鉛直断面がM字状になるように中側へ斜めに折り曲げて、それらの屈曲部分の内部に、底部の折り込み材の左右の両端際を挟み込ませる方法に限定されず、図6の如く、長尺な帯状の合成樹脂フィルムを所定の態様で折り畳むことによって、左右の折り込み材と底部の折り込み材とを一緒に形成する(連ならせるように形成する)方法を採用することも可能である。 In addition, the method for installing the lower (bottom) folding part is as in the above embodiment, by bending the parts near the lower edges of the left and right folding members diagonally inward so that the vertical cross section becomes M-shaped. The method is not limited to the method of sandwiching the left and right ends of the bottom folding material inside those bent parts, but as shown in Figure 6, by folding a long belt-shaped synthetic resin film in a predetermined manner, it is possible to It is also possible to adopt a method of forming the folding material and the bottom folding material together (forming them in a continuous manner).
本発明の味噌収納用ガゼット袋は、上記の如く優れた効果を奏するものであるから、粘性の高い半固形物である味噌の包装用袋として好適に用いることができる。 Since the gusset bag for storing miso of the present invention exhibits the excellent effects as described above, it can be suitably used as a bag for packaging miso, which is a semi-solid substance with high viscosity.
P・・味噌収納用ガゼット袋
2a,2b・・胴材
3a,2b・・折り込み部(左右)
4・・折り込み部(底部)
5・・側方シール部
15・・底シール部
C・・開封予定位置
P... Gusset bag for storing
3a, 2b...folding part (left and right)
4. Fold-in part (bottom)
5...
Claims (2)
下側の折り込み材の外周が、表裏の各胴材の下端際および左右の各折り込み材の下端際にヒートシールされており、かつ、
表側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の前側の端縁際にヒートシールされているとともに、裏側の胴材の左右の端縁際の略全体が、それぞれ、左右の各折り込み材の後側の端縁際にヒートシールされており、
表裏の胴材、左右両側および下側の折り込み材を構成する合成樹脂フィルムが、ナイロン層の外側にPET層を積層してなるベース層の片面に熱接着層を積層してなる多層フィルムであり、それらの厚みが、いずれも70μm以上140μm以下であるとともに、
前記左右の各折り込み材が、前記多層フィルムを、熱接着層が外向きになるように二つ折りしたものであり、
なおかつ、内部に味噌が充填された状態で、上端縁において、前記左右の折り込み材が、内向きの山折り状に二つ折りされた状態で表裏の胴材とともにヒートシールされることによって、一定の高さの帯状の頭シール部が形成されており、
前記頭シール部が形成されていることによって、上端縁の中央においては、表裏の胴材が一定の高さで熱融着しており、かつ、上端際の左右においては、表裏の胴材が、上端縁の中央における熱融着部分と同じ一定の高さで、対向する左右の折り込み材の外面と熱融着しているとともに、左右の折り込み材の内面同士が、熱融着しておらず離れた状態になっているとともに、
充填された味噌の上面より上側であって前記頭シール部の下側の所定の高さ位置に、開封すべき位置である開封予定位置が印刷されており、その開封予定位置が、表裏の胴材および左右の折り込み部を横断するように周状に印刷されたものであることを特徴とする味噌入りの味噌収納用ガゼット袋。 A miso storage gusset containing miso, which is made by filling miso into a bag-shaped miso storage gusset bag made of synthetic resin film with inserts sandwiched between the left and right sides and the bottom of two body materials. It is a bag ,
The outer periphery of the lower folding material is heat-sealed to the bottom edge of each body material on the front and back sides and to the bottom edge of each left and right folding material, and
Almost the entire left and right edges of the front body material are heat-sealed to the front edges of the left and right folded pieces, respectively, and almost the entire right and left edges of the back body material are heat-sealed to , are heat-sealed near the rear edges of each left and right folding material, respectively.
The synthetic resin films that make up the front and back body materials, the left and right sides, and the lower folding material are multilayer films made by laminating a thermal adhesive layer on one side of a base layer made of a PET layer laminated on the outside of a nylon layer. , the thickness of each of them is 70 μm or more and 140 μm or less, and
Each of the left and right folding materials is obtained by folding the multilayer film in half so that the thermal adhesive layer faces outward,
In addition, with the inside filled with miso, the left and right folding materials are folded in half in an inward mountain-fold shape and heat-sealed together with the front and back body materials at the upper edge, so that a certain level of A high band-shaped head seal is formed,
Due to the formation of the head seal, the front and back shell materials are thermally fused at a constant height at the center of the upper edge, and the front and back shell materials are bonded to each other at a constant height at the center of the upper edge. , is thermally fused to the outer surfaces of the left and right folding materials facing each other at the same constant height as the heat fused portion at the center of the upper edge, and the inner surfaces of the left and right folding materials are not heat fused to each other. At the same time as being separated from each other,
A scheduled opening position is printed at a predetermined height position above the top surface of the filled miso and below the head seal part, and the scheduled opening position is printed on the front and back sides of the body. A gusset bag for storing miso containing miso, characterized in that it is printed in a circumferential manner across the material and the left and right folded parts.