JP7343117B1 - Heat shield adhesive film - Google Patents
Heat shield adhesive film Download PDFInfo
- Publication number
- JP7343117B1 JP7343117B1 JP2022084344A JP2022084344A JP7343117B1 JP 7343117 B1 JP7343117 B1 JP 7343117B1 JP 2022084344 A JP2022084344 A JP 2022084344A JP 2022084344 A JP2022084344 A JP 2022084344A JP 7343117 B1 JP7343117 B1 JP 7343117B1
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- film
- resin
- base material
- resin film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】紫外線と赤外線の両方の入射を抑え、良好な光学特性を有する遮熱用粘着フィルムを実現できるようにする。【解決手段】遮熱用粘着フィルムは、樹脂からなる基材１０１と、基材１０１の第１の面に形成された第１の粘着剤層１０３と、第１の粘着剤層１０３の基材１０１と反対側の面に形成された第２の粘着剤層１０４とを備えている。第１の粘着剤層１０３は赤外線吸収剤を含み、第２の粘着剤層１０４は紫外線吸収剤を含む。【選択図】図１An object of the present invention is to realize a heat-shielding adhesive film that suppresses the incidence of both ultraviolet rays and infrared rays and has good optical properties. A heat shielding adhesive film includes a base material 101 made of resin, a first adhesive layer 103 formed on a first surface of the base material 101, and a base material of the first adhesive layer 103. 101 and a second adhesive layer 104 formed on the opposite surface. The first adhesive layer 103 contains an infrared absorber, and the second adhesive layer 104 contains an ultraviolet absorber. [Selection diagram] Figure 1
Description
本開示は、遮熱用粘着フィルムに関する。 The present disclosure relates to a heat shielding adhesive film.
建物や自動車等の窓から入射する赤外線は、室内や車内の温度上昇の大きな要因である。また、窓から入射する紫外線は室内や車内におかれた様々なものを劣化させる原因となり、近年では癌を誘発する原因となることも指摘されている。このため、窓から入射する赤外線及び紫外線を低減することが求められている。 Infrared rays that enter through the windows of buildings, cars, etc. are a major cause of temperature increases inside rooms and cars. In addition, ultraviolet rays that enter through windows can cause deterioration of various things placed indoors and inside cars, and in recent years, it has been pointed out that they can also cause cancer. Therefore, there is a need to reduce infrared rays and ultraviolet rays that enter through windows.
窓の機能を向上させるために、窓に種々の機能を有する粘着フィルムを貼り付けることが行われている。紫外線及び赤外線を吸収する機能を有する粘着フィルムを窓に貼り付けることにより、窓から入射する赤外線及び紫外線の両方を低減することができる。紫外線及び赤外線を吸収する機能を有する粘着フィルムとして、赤外線吸収剤及び紫外線吸収剤を、コート層又は粘着剤層に添加した、遮熱フィルムが知られている（例えば、特許文献１を参照。）。 In order to improve the functionality of windows, adhesive films having various functions are attached to windows. By attaching an adhesive film that has the function of absorbing ultraviolet rays and infrared rays to a window, it is possible to reduce both infrared rays and ultraviolet rays incident from the window. As an adhesive film having the function of absorbing ultraviolet rays and infrared rays, a heat shielding film in which an infrared absorber and an ultraviolet absorber are added to a coating layer or an adhesive layer is known (see, for example, Patent Document 1). .
しかしながら、赤外線吸収剤をコート層に添加した遮熱フィルムは、フィルム基体とコート層との密着性が悪く、剥離やひび割れが生じるおそれがある。一方、赤外線吸収剤を粘着剤層に添加した遮熱フィルムは、透明性が低下するおそれがあることを本願発明者らは見いだした。 However, a heat shielding film in which an infrared absorber is added to the coating layer has poor adhesion between the film base and the coating layer, which may cause peeling or cracking. On the other hand, the inventors of the present invention have discovered that a heat shielding film in which an infrared absorber is added to the adhesive layer may have reduced transparency.
粘着フィルムを窓に貼り付ける際には、皺や気泡の発生を抑えるために、被着面及び粘着剤層を水で濡らした状態で施工するいわゆる水貼りが一般に行われる。しかし、赤外線吸収剤を粘着剤層に添加すると、水貼りの際に赤外線吸収剤が水分を吸収して透明性が低下してしまうことが明らかとなった。 When applying an adhesive film to a window, so-called water application is generally performed in which the adhesive film is wetted with water in order to suppress the generation of wrinkles and air bubbles. However, it has become clear that when an infrared absorber is added to the adhesive layer, the infrared absorber absorbs water during application with water, resulting in a decrease in transparency.
本発明の課題は、紫外線と赤外線の両方の入射を抑え、良好な光学特性を示す遮熱用粘着フィルムを実現できるようにすることである。 An object of the present invention is to suppress the incidence of both ultraviolet rays and infrared rays, and to make it possible to realize a heat-shielding adhesive film that exhibits good optical properties.
本開示の遮熱用粘着フィルムの一態様は、樹脂からなる基材と、基材の第１の面に形成され、赤外線吸収剤を含む第１の粘着剤層と、第１の粘着剤層の基材と反対側の面に形成され、紫外線吸収剤を含む第２の粘着剤層とを備えている。 One embodiment of the heat shielding adhesive film of the present disclosure includes a base material made of resin, a first adhesive layer formed on a first surface of the base material and containing an infrared absorber, and a first adhesive layer. A second adhesive layer containing an ultraviolet absorber is formed on the surface opposite to the base material.
遮熱用粘着フィルムの一態様は、赤外線吸収剤を含む第１の粘着剤層は、紫外線吸収剤を含む第２の粘着剤層と基材との間に形成されているため、赤外線吸収剤が貼り付けの際の水分の影響を受けにくい。このため、赤外線吸収剤が水分を吸収することによる白化を抑えることができる。また、第１の粘着剤層は、コート層と異なり厚くしても基材との密着性を確保することができるので、赤外線吸収能力の高い層を形成することができる。 One aspect of the heat shielding adhesive film is that the first adhesive layer containing an infrared absorber is formed between the base material and the second adhesive layer containing an ultraviolet absorber. is not easily affected by moisture during pasting. Therefore, whitening caused by the infrared absorbent absorbing moisture can be suppressed. Furthermore, unlike the coat layer, the first adhesive layer can ensure adhesion to the base material even if it is thick, so a layer with high infrared absorption ability can be formed.
遮熱用粘着フィルムの一態様は、基材の第１の面と反対側の第２の面に形成されたハードコート層をさらに備えていてもよい。このような構成とすることにより、遮熱用粘着フィルムが傷つきにくく良好な光学特性を維持することができる。 One embodiment of the heat shielding adhesive film may further include a hard coat layer formed on a second surface opposite to the first surface of the base material. With such a configuration, the heat shielding adhesive film is less likely to be damaged and can maintain good optical properties.
遮熱用粘着フィルムの一態様において、基材は、ポリエステルフィルム、熱可塑性エラストマーフィルム、ポリオレフィン系樹脂フィルム、ポリエステル系樹脂、ポリカーボネート系樹脂、ポリ塩化ビニル系樹脂フィルム、ポリフェニレンサルファイド系樹脂フィルム、ポリエーテルサルフォン系樹脂フィルム、ポリエチレンサルファイド系樹脂フィルム、ポリフェニレンエーテル系樹脂フィルム、スチレン系樹脂フィルム、アクリル系樹脂フィルム、ポリアミド系樹脂フィルム、ポリイミド系樹脂フィルム及びセルロース系樹脂フィルムから選ばれた１つ又は２つ以上からなる積層体とすることができる。 In one embodiment of the heat shielding adhesive film, the base material is a polyester film, a thermoplastic elastomer film, a polyolefin resin film, a polyester resin, a polycarbonate resin, a polyvinyl chloride resin film, a polyphenylene sulfide resin film, or a polyether. One or two selected from sulfone resin film, polyethylene sulfide resin film, polyphenylene ether resin film, styrene resin film, acrylic resin film, polyamide resin film, polyimide resin film, and cellulose resin film It can be a laminate consisting of two or more.
遮熱用粘着フィルムの一態様において、可視光線透過率が７０％以上であり、日射透過率（赤外線透過率）は８０％以下であり、紫外線透過率は５％以下とすることができる。 In one embodiment of the thermal barrier adhesive film, the visible light transmittance can be 70% or more, the solar transmittance (infrared transmittance) can be 80% or less, and the ultraviolet transmittance can be 5% or less.
遮熱用粘着フィルムの一態様において、第１の粘着剤層を構成する樹脂成分と、第２の粘着剤層を構成する樹脂成分とは、同一とすることができる。 In one embodiment of the heat-shielding adhesive film, the resin component that constitutes the first adhesive layer and the resin component that constitutes the second adhesive layer can be the same.
遮熱用粘着フィルムの一態様において、赤外線吸収剤は、アンチモン含有酸化スズ（ＡＴＯ）、インジウム含有酸化スズ（ＩＴＯ）及び複合タングステン酸化物から選ばれた少なくとも１種を含む微粒子とすることができる。 In one embodiment of the thermal barrier adhesive film, the infrared absorber can be fine particles containing at least one selected from antimony-containing tin oxide (ATO), indium-containing tin oxide (ITO), and composite tungsten oxide. .
遮熱用粘着フィルムの一態様において、第２の粘着剤層は、赤外線吸収剤の含有量が検出限界以下とすることができる。 In one embodiment of the heat-shielding adhesive film, the content of the infrared absorber in the second adhesive layer can be below the detection limit.
本開示の遮熱用粘着フィルムによれば、紫外線と赤外線の両方の入射を抑え、良好な光学特性を実現できる。 According to the heat shielding adhesive film of the present disclosure, it is possible to suppress the incidence of both ultraviolet rays and infrared rays, and achieve good optical properties.
一実施形態の遮熱用粘着フィルム１００は、シート状の樹脂からなる基材１０１と、基材１０１の第１の面に形成された、第１の粘着剤層１０３と、第１の粘着剤層１０３の基材１０１とは反対側の面に積層された第２の粘着剤層１０４と、基材１０１の第２の面に形成されたハードコート層１０５とを備えている。第１の粘着剤層１０３は、赤外線吸収剤を含む層であり、第２の粘着剤層１０４は、紫外線吸収剤を含む層である。ハードコート層１０５は、基材１０１及び被着体であるガラス等を保護するために形成されており、必要に応じて形成すればよく、形成しなくてもよい。 The heat shielding adhesive film 100 of one embodiment includes a base material 101 made of a sheet-like resin, a first adhesive layer 103 formed on a first surface of the base material 101, and a first adhesive layer 103 formed on a first surface of the base material 101. It includes a second adhesive layer 104 laminated on the surface of the layer 103 opposite to the base material 101, and a hard coat layer 105 formed on the second surface of the base material 101. The first adhesive layer 103 is a layer containing an infrared absorber, and the second adhesive layer 104 is a layer containing an ultraviolet absorber. The hard coat layer 105 is formed to protect the base material 101 and the adherend, such as glass, and may be formed as necessary or may not be formed.
第２の粘着剤層１０４の第１の粘着剤層１０３と反対側の面には、剥離ライナー１０７が設けられているが、これは、運搬時や施工時の取り扱いを容易にするためのものであり、ガラス等の被着体に貼り付ける際に剥離される。 A release liner 107 is provided on the surface of the second adhesive layer 104 opposite to the first adhesive layer 103, which is intended to facilitate handling during transportation and construction. It is peeled off when attached to an adherend such as glass.
コート層の様な比較的硬質の層は、あまり厚く形成しないのが一般的である。一方、赤外線吸収能力は層の厚さに大きく影響を受けるため、薄い層において十分な赤外線吸収機能を発揮させるためには、大量の赤外線吸収剤を添加する必要が生じる。このため、赤外線吸収剤の分散ムラが生じて透明性が低下したり、樹脂の物性に影響を与えたりするおそれがある。本実施形態の遮熱用粘着フィルム１００は、第１の粘着剤層１０３に赤外線吸収剤を添加している。コート層よりも厚く形成されることが多い粘着剤層であるため、赤外線吸収剤の含有濃度が低くても十分な赤外線吸収効果を得やすくなっている。粘着剤層であるため、基材１０１との密着性を確保することも容易である。 Generally, a relatively hard layer such as a coating layer is not formed very thick. On the other hand, since the infrared absorption ability is greatly affected by the thickness of the layer, it is necessary to add a large amount of infrared absorbing agent in order to exhibit sufficient infrared absorption function in a thin layer. For this reason, there is a risk that the infrared absorbent may be unevenly dispersed, which may reduce transparency or affect the physical properties of the resin. In the heat shielding adhesive film 100 of this embodiment, an infrared absorber is added to the first adhesive layer 103. Since the adhesive layer is often formed thicker than the coating layer, it is easy to obtain a sufficient infrared absorption effect even if the concentration of the infrared absorber is low. Since it is an adhesive layer, it is easy to ensure adhesion to the base material 101.
赤外線吸収剤を含む第１の粘着剤層１０３は、基材１０１と反対側の面が第２の粘着剤層１０４により覆われている。このため、遮熱用粘着フィルム１００をガラス等の被着体に貼り付ける際に、粘着剤層及び被着体の表面を水でぬらして行う水貼りを行っても第１の粘着剤層１０３に含まれる赤外線吸収剤が水分を吸収しにくく、赤外線吸収剤が水分を吸収することによる白化を抑えることができる。 The first adhesive layer 103 containing an infrared absorber has a surface opposite to the base material 101 covered with a second adhesive layer 104 . Therefore, when attaching the heat-shielding adhesive film 100 to an adherend such as glass, even if the adhesive layer and the surface of the adherend are wetted with water, the first adhesive layer 103 The infrared absorbing agent contained in the product is difficult to absorb moisture, and whitening caused by the infrared absorbing agent absorbing moisture can be suppressed.
第１の粘着剤層１０３に含まれる赤外線吸収剤は、公知の有機系赤外線吸収剤及び無機系赤外線吸収剤を使用できる。中でも、無機系微粒子からなる赤外線吸収剤は耐候性に優れるので好ましい。無機系微粒子からなる赤外線吸収剤は、例えばアンチモン含有酸化スズ（ＡＴＯ）、インジウム含有酸化スズ（ＩＴＯ）及び複合タングステン酸化物から選ばれた少なくとも１種を含む微粒子とすることができる。 As the infrared absorber contained in the first adhesive layer 103, known organic infrared absorbers and inorganic infrared absorbers can be used. Among these, infrared absorbers made of inorganic fine particles are preferred because they have excellent weather resistance. The infrared absorbing agent made of inorganic fine particles can be, for example, fine particles containing at least one selected from antimony-containing tin oxide (ATO), indium-containing tin oxide (ITO), and composite tungsten oxide.
第１の粘着剤層１０３を構成する第１の樹脂成分は、特に限定されず、アクリル系、ウレタン系、シリコーン系、及びゴム系等から選択することができる。また、溶剤型、水系、エマルション系、及び無溶剤型等のいずれの構成を用いることもできる。 The first resin component constituting the first adhesive layer 103 is not particularly limited, and can be selected from acrylic, urethane, silicone, rubber, and the like. Moreover, any structure such as a solvent type, a water type, an emulsion type, or a non-solvent type can be used.
赤外線吸収剤の第１の粘着剤層１０３の樹脂固形分当たりの含有量は、第１の粘着剤層１０３の厚さにもよるが、赤外線吸収機能を発揮させるために、好ましくは５質量％以上、より好ましくは１０質量％以上、さらに好ましくは３０質量％以上、よりさらに好ましくは５０質量％以上である。赤外線吸収剤を均一に分散させる観点及び可視光線透過率を確保する観点から、好ましくは１００質量％以下、より好ましくは８０質量％以下である。 The content of the infrared absorber per resin solid content of the first adhesive layer 103 depends on the thickness of the first adhesive layer 103, but is preferably 5% by mass in order to exhibit the infrared absorbing function. The content is more preferably 10% by mass or more, still more preferably 30% by mass or more, even more preferably 50% by mass or more. From the viewpoint of uniformly dispersing the infrared absorbent and ensuring visible light transmittance, the content is preferably 100% by mass or less, more preferably 80% by mass or less.
第１の粘着剤層１０３の厚さは、赤外線吸収剤の含有量にもよるが、日射透過率（ＩＲ透過率）を小さくする観点から、好ましくは３μｍ以上、より好ましくは５μ以上、さらに好ましくは１０μ以上であり、可視光線透過率を確保する観点から、好ましくは５０μｍ以下、より好ましくは４０μｍ以下である。 The thickness of the first adhesive layer 103 depends on the content of the infrared absorber, but from the viewpoint of reducing solar transmittance (IR transmittance), the thickness is preferably 3 μm or more, more preferably 5 μm or more, and even more preferably is 10 μm or more, and from the viewpoint of ensuring visible light transmittance, is preferably 50 μm or less, more preferably 40 μm or less.
第１の粘着剤層１０３は、赤外線吸収剤以外に、架橋剤、分散剤、反応促進剤、及び遅延剤等を含んでいてもよい。架橋剤として、公知のイソシアネート系架橋剤、エポキシ系架橋剤、及びキレート系架橋剤から選ばれた１種又は２種以上の混合物を使用できる。赤外線吸収剤が無機系微粒子である場合には、分散剤を添加することにより赤外線吸収剤を第１の粘着剤層１０３中における分散性を向上させて、透明性をより高くすることができる。分散剤の添加量は、種類にもよるが、分散性向上の観点から赤外線吸収剤に対して好ましくは０．５質量％以上、好ましくは１０質量％以下である。 The first adhesive layer 103 may contain a crosslinking agent, a dispersant, a reaction accelerator, a retarder, etc. in addition to the infrared absorbing agent. As the crosslinking agent, one or a mixture of two or more selected from known isocyanate crosslinking agents, epoxy crosslinking agents, and chelate crosslinking agents can be used. When the infrared absorber is inorganic fine particles, adding a dispersant can improve the dispersibility of the infrared absorber in the first adhesive layer 103, thereby increasing transparency. The amount of the dispersant added depends on the type, but from the viewpoint of improving dispersibility, it is preferably 0.5% by mass or more, preferably 10% by mass or less, based on the infrared absorber.
第２の粘着剤層１０４を構成する樹脂成分は、特に限定されず、例えば、第１の粘着剤層１０３を構成する樹脂成分と同一のものを用いることができる。第１の粘着剤層１０３と第２の粘着剤層１０４とにおいて樹脂成分を一致させることにより、第１の粘着剤層１０３と第２の粘着剤層１０４との密着性を向上させることができる。なお、樹脂成分が同一とは、樹脂の主要な構成単位（モノマー）が同一であることであり、樹脂の分子量や副成分まで完全に同一であることを要求しない。また、樹脂成分以外の配合成分が異なっている場合も含まれる。なお、第１の粘着剤層１０３と第２の粘着剤層１０４とを異なる樹脂成分により形成することもできる。例えば、第１の粘着剤層１０３を構成する樹脂成分として、赤外線吸収剤の分散性が良好なものを選択し、第２の粘着剤層１０４を構成する樹脂成分として、より強力な粘着力を発揮するものを選択することができる。 The resin component constituting the second adhesive layer 104 is not particularly limited, and for example, the same resin component as the resin component constituting the first adhesive layer 103 can be used. By matching the resin components in the first adhesive layer 103 and the second adhesive layer 104, the adhesion between the first adhesive layer 103 and the second adhesive layer 104 can be improved. . Note that the expression that the resin components are the same means that the main constituent units (monomers) of the resins are the same, and it does not require that the molecular weights and subcomponents of the resins be completely the same. It also includes cases where the ingredients other than the resin component are different. Note that the first adhesive layer 103 and the second adhesive layer 104 may be formed of different resin components. For example, as the resin component constituting the first adhesive layer 103, one with good dispersibility of the infrared absorber is selected, and as the resin component constituting the second adhesive layer 104, one with stronger adhesive strength is selected. You can choose what you want to perform.
第２の粘着剤層１０４に含まれる紫外線吸収剤は、特に限定されず、ベンゾフェノン系、ベンゾトリアゾール系、シアノアクリレート系、及びトリアジン系等の紫外線を選択的に吸収する公知の紫外線吸収剤から選ばれた１種又はそれらの混合物を使用できる。中でも、トリアジン系紫外線吸収剤は、耐候性が良好で、２８０ｎｍ～３５０ｎｍの波長の紫外線を吸収するので好ましい。 The ultraviolet absorber contained in the second adhesive layer 104 is not particularly limited, and is selected from known ultraviolet absorbers that selectively absorb ultraviolet rays such as benzophenone, benzotriazole, cyanoacrylate, and triazine. One type or a mixture thereof can be used. Among these, triazine-based ultraviolet absorbers are preferred because they have good weather resistance and absorb ultraviolet rays with wavelengths of 280 nm to 350 nm.
ベンゾトリアゾール系紫外線吸収剤としては、例えばＢＡＳＦ社製のTinuvin384-2を使用できる。シアノアクリレート系紫外線吸収剤としては、例えばＢＡＳＦ社製のユビナール３０３５、ユビナール３０３９、ユビナール３０３０ＦＦ等を使用できる。トリアジン系紫外線吸収剤としては、例えばＢＡＳＦ社製のTinuvin１６００等が使用できる。 As the benzotriazole ultraviolet absorber, for example, Tinuvin 384-2 manufactured by BASF can be used. As the cyanoacrylate ultraviolet absorber, for example, Uvinal 3035, Yuvinal 3039, and Yuvinal 3030FF manufactured by BASF can be used. As the triazine-based ultraviolet absorber, for example, Tinuvin 1600 manufactured by BASF, etc. can be used.
紫外線吸収剤の第２の粘着剤層１０４における含有量は、必要とする紫外線透過率に応じて調整することができる。なお、遮熱用粘着フィルム１００の紫外線透過率は、好ましくは５％以下であり、より好ましくは２％以下である。 The content of the ultraviolet absorber in the second adhesive layer 104 can be adjusted depending on the required ultraviolet transmittance. The ultraviolet transmittance of the heat shielding adhesive film 100 is preferably 5% or less, more preferably 2% or less.
第２の粘着剤層１０４の厚さは、ガラス等の被着体に対する十分な粘着力を発揮できると共に、十分な紫外線遮蔽効果を得られる範囲とすることができる。例えば５μｍ以上、５０μｍ以下とすることができる。 The thickness of the second adhesive layer 104 can be set within a range that can exhibit sufficient adhesion to an adherend such as glass and can also provide a sufficient ultraviolet shielding effect. For example, it can be set to 5 μm or more and 50 μm or less.
第２の粘着剤層１０４も、第１の粘着剤層１０３と同様に、紫外線吸収剤以外に、架橋剤、分散剤、反応促進剤、及び遅延剤等を含んでいてもよい。架橋剤として、公知のイソシアネート系架橋剤、エポキシ系架橋剤、及びキレート系架橋剤から選ばれた１種又は２種以上の混合物を使用できる。なお、白化を防ぐ観点からは、第２の粘着剤層１０４は、赤外線吸収剤を含まないことが好ましい。製造工程において微量の赤外線吸収剤が第２の粘着剤層に混入することがあり得るが、赤外線吸収剤の含有量は、痕跡量程度であることが好ましく、検出限界以下であることがより好ましい。 Like the first adhesive layer 103, the second adhesive layer 104 may also contain a crosslinking agent, a dispersant, a reaction accelerator, a retarder, etc. in addition to the ultraviolet absorber. As the crosslinking agent, one or a mixture of two or more selected from known isocyanate crosslinking agents, epoxy crosslinking agents, and chelate crosslinking agents can be used. Note that from the viewpoint of preventing whitening, the second adhesive layer 104 preferably does not contain an infrared absorber. Although a trace amount of the infrared absorber may be mixed into the second adhesive layer during the manufacturing process, the content of the infrared absorber is preferably about a trace amount, and more preferably below the detection limit. .
基材１０１は、透明な樹脂フィルムであれば特に限定されないが、用途に適した特性を持つ材料を適宜選択することができる。例えば、ポリエチレン、ポリプロピレン、ポリ４－メチルペンテン－１、及びポリブテン－１等からなるポリオレフィン系樹脂フィルム、ポリエチレンテレフタレート（ＰＥＴ）、及びポリエチレンナフタレート等からなるポリエステル系樹脂フィルム、ポリカーボネート系樹脂フィルム、ポリ塩化ビニル系樹脂フィルム、ポリフェニレンサルファイド系樹脂フィルム、ポリエーテルサルフォン系樹脂フィルム、ポリエチレンサルファイド系樹脂フィルム、ポリフェニレンエーテル系樹脂フィルム、スチレン系樹脂フィルム、アクリル系樹脂フィルム、ポリアミド系樹脂フィルム、ポリイミド系樹脂フィルム、セルロースアセテート等からなるセルロース系樹脂フィルム、並びにポリウレタン又はアクリルウレタン等の伸張性のある熱可塑性エラストマーからなるフィルムのいずれかを用いることができる。また、これらのフィルムを含む積層フィルムを用いることもできる。ＰＥＴフィルムは耐久性や寸法安定性のバランスが良く、取り扱いが容易であるという利点を有する。熱可塑性エラストマーからなるフィルムを基材１０１とすることにより、遮熱用粘着フィルム１００を水貼りする際にドライヤー等で加熱しなくても引き伸ばして容易に施工できるという利点が得られる。 The base material 101 is not particularly limited as long as it is a transparent resin film, but a material having characteristics suitable for the purpose can be appropriately selected. For example, polyolefin resin films made of polyethylene, polypropylene, poly4-methylpentene-1, polybutene-1, etc., polyester resin films made of polyethylene terephthalate (PET), polyethylene naphthalate, etc., polycarbonate resin films, Vinyl chloride resin film, polyphenylene sulfide resin film, polyether sulfone resin film, polyethylene sulfide resin film, polyphenylene ether resin film, styrene resin film, acrylic resin film, polyamide resin film, polyimide resin A film, a cellulose resin film made of cellulose acetate or the like, or a film made of a stretchable thermoplastic elastomer such as polyurethane or acrylic urethane can be used. Moreover, a laminated film containing these films can also be used. PET film has the advantage of having a good balance of durability and dimensional stability, and is easy to handle. By using a film made of thermoplastic elastomer as the base material 101, there is an advantage that when applying the heat shielding adhesive film 100 with water, it can be easily stretched and applied without heating with a dryer or the like.
基材１０１の厚さは、１０μｍ以上、５００μｍ以下程度とすることができる。基材１０１の厚さを５０μｍ以上、５００μｍ以下程度と比較的厚くすることにより、遮熱用粘着フィルム１００を建築物のガラス窓に貼り付けた際に、飛散防止効果や防犯効果を期待できる。一方、１０μｍ以上、２００μｍ以下程度とすることにより、自動車のガラス窓等、湾曲した窓に貼り付ける際に、曲面への追従性を向上させることができる。 The thickness of the base material 101 can be approximately 10 μm or more and 500 μm or less. By making the thickness of the base material 101 relatively thick, such as about 50 μm or more and 500 μm or less, it is possible to expect a scattering prevention effect and a crime prevention effect when the heat shielding adhesive film 100 is attached to a glass window of a building. On the other hand, by setting the thickness to about 10 μm or more and 200 μm or less, it is possible to improve the followability to a curved surface when pasting it on a curved window such as a glass window of an automobile.
ハードコート層１０５は必要に応じて形成すればよいが、例えば鉛筆硬度が２Ｈ以上のハードコート層１０５を形成することにより、遮熱用粘着フィルム１００の表面にキズが生じにくくすることができる。ハードコート層１０５の厚さは、２μｍ以上、１０μｍ以下程度とすることができる。ハードコート層１０５は、紫外線吸収剤を含む構成とすることもできる。紫外線吸収剤を含むハードコート層１０５を形成することにより、遮熱用粘着フィルム１００を窓の外側に貼り付けた場合に、遮熱用粘着フィルム１００の劣化を生じにくくすることができる。 The hard coat layer 105 may be formed as necessary, but by forming the hard coat layer 105 having a pencil hardness of 2H or more, for example, it is possible to make the surface of the heat shielding adhesive film 100 less likely to be scratched. The thickness of the hard coat layer 105 can be approximately 2 μm or more and 10 μm or less. The hard coat layer 105 may also include a UV absorber. By forming the hard coat layer 105 containing an ultraviolet absorber, it is possible to prevent the heat shielding adhesive film 100 from deteriorating when the heat shielding adhesive film 100 is attached to the outside of a window.
遮熱用粘着フィルム１００の全光線透過率及び可視光透過率は、例えば７０％以上とすることできる。可視光線透過率が７０％以上であれば、自動車のフロントガラスやサイドガラスに使用することができる。また、ヘイズ値は５％以下程度とすることができる。紫外線透過率は１０％以下とすることが好ましい。日射透過率（ＩＲ透過率）は８０％以下とすることが好ましい。１００－日射透過率（％）－日射反射率（％）である日射吸収率（ＩＲ吸収率）は、室内に入射する赤外線を大きく低減する観点から１０％以上とすることが好ましく、赤外線吸収による遮熱ウインドウフィルム自身の過熱を抑える観点から４０％以下とすることが好ましい。 The total light transmittance and visible light transmittance of the heat shielding adhesive film 100 can be, for example, 70% or more. If the visible light transmittance is 70% or more, it can be used for automobile windshields and side windows. Further, the haze value can be about 5% or less. The ultraviolet transmittance is preferably 10% or less. The solar transmittance (IR transmittance) is preferably 80% or less. The solar absorption rate (IR absorption rate), which is 100 - solar transmittance (%) - solar reflectance (%), is preferably set to 10% or more from the viewpoint of greatly reducing infrared rays entering the room. From the viewpoint of suppressing overheating of the heat shielding window film itself, it is preferably 40% or less.
本実施形態の遮熱用粘着フィルム１００は、水分吸収による赤外線吸収剤の白化が生じにくいため、水貼りをすることができる。本実施形態の遮熱用粘着フィルム１００を水貼りする場合には、まず、霧吹き等でフィルムを濡らし、水の表面張力を利用して窓に仮固定し、スクレーパーでスクイーズして気泡を抜く。その後、乾燥させることにより遮熱用粘着フィルム１００が窓に貼りつけられる。遮熱用粘着フィルム１００を窓の内側に貼り付けた場合には、紫外線吸収剤を含む第２の粘着剤層１０４が最も外側となる。このため、紫外線により劣化しやすいハードコート層１０５に入射する紫外線の量を低減して劣化を生じにくくすることができる。但し、遮熱用粘着フィルム１００は、窓の外側に貼り付けることもできる。遮熱用粘着フィルム１００は、赤外線吸収剤を含む層が露出していないので、窓の外側に貼る用途にも適している。 The heat shielding adhesive film 100 of this embodiment can be applied with water because the infrared absorber is less likely to whiten due to moisture absorption. When applying the heat shielding adhesive film 100 of this embodiment with water, first, the film is wetted with a sprayer, etc., temporarily fixed to a window using the surface tension of the water, and then squeezed with a scraper to remove air bubbles. Thereafter, the heat shielding adhesive film 100 is attached to the window by drying. When the heat-shielding adhesive film 100 is attached to the inside of a window, the second adhesive layer 104 containing an ultraviolet absorber is the outermost layer. Therefore, it is possible to reduce the amount of ultraviolet rays incident on the hard coat layer 105, which is easily deteriorated by ultraviolet rays, and to make it difficult to cause deterioration. However, the heat shielding adhesive film 100 can also be attached to the outside of the window. Since the layer containing the infrared absorber is not exposed in the heat shielding adhesive film 100, it is also suitable for application to the outside of a window.
以下に、実施例に基づいて本発明をより詳細に説明するが、これらの実施例は例示であり、本発明を限定することを意図するものではない。 The present invention will be described in more detail below based on Examples, but these Examples are merely illustrative and are not intended to limit the present invention.
＜光学特性の測定＞
全光線透過率及びヘイズ値は、積分球付分光光度計（日本分光製、V-770/ILN-925）を用い、JIS K7361-1に準拠して測定した。可視光線透過率、紫外線透過率、日射透過率、日射反射率、日射吸収率及び遮蔽係数は、積分球付分光光度計（日本分光製、V-770/ILN-925）を用い、JIS A 5759(2008)に準拠して測定した。測定は、粘着フィルムを厚さ３ｍｍのガラスに貼り合わせて、ガラス面側から光を入射させて行った。
<Measurement of optical properties>
The total light transmittance and haze value were measured in accordance with JIS K7361-1 using a spectrophotometer with an integrating sphere (manufactured by JASCO Corporation, V-770/ILN-925). Visible light transmittance, ultraviolet transmittance, solar transmittance, solar reflectance, solar absorption rate, and shielding coefficient were measured using a spectrophotometer with an integrating sphere (manufactured by JASCO Corporation, V-770/ILN-925), according to JIS A 5759. (2008). The measurement was carried out by attaching the adhesive film to glass with a thickness of 3 mm and allowing light to enter from the glass surface side.
＜密着性評価＞
ガラス製の被着体に貼り合わせた遮熱用粘着フィルムを、剥離角度１８０°、剥離速度３００ｍｍ／分で引き剥がした。基材と共に粘着剤層が剥離し、被着体に残存しなかった場合を良好、基材と粘着剤層との間で剥離が生じ、被着体の表面に粘着剤層が残存した場合を不良とした。
<Adhesion evaluation>
The heat shielding adhesive film bonded to the glass adherend was peeled off at a peeling angle of 180° and a peeling speed of 300 mm/min. Good when the adhesive layer peels off along with the base material and does not remain on the adherend; when peeling occurs between the base material and the adhesive layer and the adhesive layer remains on the surface of the adherend It was marked as defective.
＜水貼り施工時の外観評価＞
遮熱用粘着シートの粘着剤層の表面と、ガラス製の被着体とに霧吹きにより水を吹き付け、表面が濡れた状態の粘着剤層を被着体に貼り付け、粘着剤層と被着体との間の気泡を除去した。貼り付け後に、目視によりフィルムの白濁の有無を調べた。
<Appearance evaluation during water pasting construction>
Water is sprayed onto the surface of the adhesive layer of the heat shielding adhesive sheet and the glass adherend, and the adhesive layer with the wet surface is attached to the adherend, and the adhesive layer and adherend are bonded. Removed air bubbles between the body and the body. After pasting, the film was visually inspected for cloudiness.
（実施例１）
ハードコート層を片面に有する厚さ１００μｍの二軸延伸ＰＥＴフィルムを基材として準備した。第１の剥離ライナーの剥離面に、表１に示す組成物をコーターにより塗布した後乾燥して、赤外線吸収剤を含む厚さが１０μｍの第１の粘着剤層を形成した。第１の剥離ライナー上の第１の粘着剤層を、基材のハードコート層と反対側に面に貼り合わせた。第２の剥離ライナーの剥離面に、表２に示す組成物をコーターにより塗布した後乾燥して、紫外線吸収剤を含む厚さが１５μｍの第２の粘着剤層を形成した。第１の剥離ライナーを剥離した後、第２の剥離ライナー上の第２の粘着剤層を、第１の粘着剤層に貼り合わせて実施例１の遮熱用粘着フィルムを形成した。
(Example 1)
A biaxially stretched PET film having a thickness of 100 μm and having a hard coat layer on one side was prepared as a base material. The composition shown in Table 1 was applied to the release surface of the first release liner using a coater and then dried to form a first adhesive layer containing an infrared absorber and having a thickness of 10 μm. The first adhesive layer on the first release liner was attached to the opposite side of the substrate from the hard coat layer. The composition shown in Table 2 was applied to the release surface of the second release liner using a coater and then dried to form a second adhesive layer containing an ultraviolet absorber and having a thickness of 15 μm. After peeling off the first release liner, the second adhesive layer on the second release liner was bonded to the first adhesive layer to form the heat shielding adhesive film of Example 1.
赤外線吸収剤は、アンチモン含有酸化スズ（ＡＴＯ）微粒子を４０質量％含む分散液を使用し、組成物の固形分に対してＡＴＯ粒子が５３．６質量％となるように加えた。 As the infrared absorber, a dispersion containing 40% by mass of antimony-containing tin oxide (ATO) fine particles was used, and the amount of ATO particles was 53.6% by mass based on the solid content of the composition.
実施例１の遮熱用粘着フィルムの全光線透過率は８３．９％、ヘイズ値は０．７％、可視光線透過率は８２．１％、紫外線透過率は１．８％、日射透過率は６３．４％、日射反射率は６．７％、日射吸収率は２９．８％、遮蔽係数は０．８３であった。 The heat shielding adhesive film of Example 1 had a total light transmittance of 83.9%, a haze value of 0.7%, a visible light transmittance of 82.1%, an ultraviolet transmittance of 1.8%, and a solar transmittance. was 63.4%, solar reflectance was 6.7%, solar absorption was 29.8%, and shielding coefficient was 0.83.
密着性の試験において、被着体の表面に粘着剤層は残存せず、基材と粘着剤層との密着性は良好であった。 In the adhesion test, no adhesive layer remained on the surface of the adherend, and the adhesion between the base material and the adhesive layer was good.
遮熱用粘着フィルムを水貼りした場合にも白濁等は認められず、貼り付け後の外観は良好であった。 Even when the heat shielding adhesive film was applied with water, no clouding was observed, and the appearance after application was good.
（比較例１）
実施例１と同じ基材のハードコート層と反対側の面に、表３に示す組成物をコーターにより塗布した後乾燥して、赤外線吸収剤を含む厚さが５μｍのコート層を形成した。実施例１と同様にして、紫外線吸収剤を含む厚さが１５μｍの粘着剤層を形成し、コート層と貼り合わせて、比較例１の遮熱用粘着フィルムを形成した。
(Comparative example 1)
The composition shown in Table 3 was applied using a coater to the surface opposite to the hard coat layer of the same base material as in Example 1, and then dried to form a coat layer containing an infrared absorber and having a thickness of 5 μm. In the same manner as in Example 1, a 15 μm thick adhesive layer containing an ultraviolet absorber was formed and bonded to the coating layer to form a heat shielding adhesive film of Comparative Example 1.
赤外線吸収剤は、アンチモン含有酸化スズ（ＡＴＯ）微粒子を４０質量％含む分散液を使用し、組成物の固形分に対してＡＴＯ粒子が２５０質量％となるように加えた。 As the infrared absorber, a dispersion containing 40% by mass of antimony-containing tin oxide (ATO) fine particles was used, and the amount of ATO particles was 250% by mass based on the solid content of the composition.
比較例１の遮熱用粘着フィルムの全光線透過率は８１．７％、ヘイズ値は０．４％、可視光線透過率は８０．５％、紫外線透過率は１．６％、日射透過率は６０．９％、日射反射率は６．６％、日射吸収率は３２．６％、遮蔽係数は０．８２であった。 The heat shielding adhesive film of Comparative Example 1 had a total light transmittance of 81.7%, a haze value of 0.4%, a visible light transmittance of 80.5%, an ultraviolet transmittance of 1.6%, and a solar transmittance. was 60.9%, solar reflectance was 6.6%, solar absorption was 32.6%, and shielding coefficient was 0.82.
密着性の試験において、コート層と基材との間で剥離が生じ、被着体の表面に粘着剤層が残存し、密着性は不良であった。 In the adhesion test, peeling occurred between the coating layer and the base material, the adhesive layer remained on the surface of the adherend, and the adhesion was poor.
粘着剤層を形成する前のコート層に基材表面に至る切れ込みを入れ、１ｍｍ角の縦横１００マスのブロックを形成した。ブロックの表面に市販のセロハンテープを貼り付けて剥がしたところ、１００ブロック中９５ブロックが基材から剥離した。 A cut was made in the coat layer before forming the adhesive layer to reach the surface of the base material to form a 1 mm square block of 100 squares in length and width. When a commercially available cellophane tape was attached to the surface of the block and peeled off, 95 out of 100 blocks were detached from the base material.
遮熱用粘着フィルムを水貼りした場合にも白濁等は認められず、貼り付け後の外観は良好であった。 Even when the heat shielding adhesive film was applied with water, no clouding was observed, and the appearance after application was good.
（比較例２）
剥離ライナーの剥離面に、表４に示す組成物をコーターにより塗布した後乾燥して赤外線吸収剤及び紫外線吸収剤を含む厚さが１５μｍの混合粘着剤層を形成した。実施例１と同じ基材のハードコート層と反対側の面に、混合粘着剤層を貼り合わせて、比較例２の遮熱用粘着フィルムを形成した。
(Comparative example 2)
The composition shown in Table 4 was applied to the release surface of the release liner using a coater and then dried to form a mixed adhesive layer containing an infrared absorber and an ultraviolet absorber and having a thickness of 15 μm. A mixed adhesive layer was attached to the surface of the same base material as in Example 1 opposite to the hard coat layer to form a heat shielding adhesive film of Comparative Example 2.
赤外線吸収剤は、アンチモン含有酸化スズ（ＡＴＯ）微粒子を４０質量％含む分散液を使用し、組成物の固形分に対してＡＴＯ粒子が５３．６質量％となるように加えた。 As the infrared absorber, a dispersion containing 40% by mass of antimony-containing tin oxide (ATO) fine particles was used, and the amount of ATO particles was 53.6% by mass based on the solid content of the composition.
比較例２の遮熱用粘着フィルムの全光線透過率は８３．６％、ヘイズ値は０．９％、可視光線透過率は８２．１％、紫外線透過率は２．０％、日射透過率は６３．４％、日射反射率は６．８％、日射吸収率は２９．８％、遮蔽係数は０．８３であった。 The heat shielding adhesive film of Comparative Example 2 had a total light transmittance of 83.6%, a haze value of 0.9%, a visible light transmittance of 82.1%, an ultraviolet transmittance of 2.0%, and a solar transmittance. was 63.4%, solar reflectance was 6.8%, solar absorption was 29.8%, and shielding coefficient was 0.83.
密着性の試験において、被着体の表面に粘着剤層は残存せず、基材と粘着剤層との密着性は良好であった。 In the adhesion test, no adhesive layer remained on the surface of the adherend, and the adhesion between the base material and the adhesive layer was good.
遮熱用粘着フィルムを水貼りした場合に白濁が認められ、貼り付け後の外観は不良であった。 When the heat shielding adhesive film was applied with water, cloudiness was observed, and the appearance after application was poor.
表５に実施例及び比較例の評価結果をまとめて示す。 Table 5 summarizes the evaluation results of Examples and Comparative Examples.
本開示の遮熱用粘着フィルムは、紫外線と赤外線の両方の入射を抑え、良好な光学特性を実現でき、建物や車両の窓に貼り付ける遮熱用のフィルムとして有用である。 The heat-shielding adhesive film of the present disclosure can suppress the incidence of both ultraviolet rays and infrared rays and achieve good optical properties, and is useful as a heat-shielding film that is attached to windows of buildings and vehicles.
１００ 遮熱用粘着フィルム
１０１ 基材
１０３ 第１の粘着剤層
１０４ 第２の粘着剤層
１０５ ハードコート層
１０７ 剥離ライナー
100 Heat shielding adhesive film 101 Base material 103 First adhesive layer 104 Second adhesive layer 105 Hard coat layer 107 Release liner
Claims (7)
前記基材の第１の面に形成され、赤外線吸収剤を含む第１の粘着剤層と、
前記第１の粘着剤層の前記基材と反対側の面に形成され、紫外線吸収剤を含む第２の粘着剤層とを備えている、遮熱用粘着フィルム。 A base material made of resin,
a first adhesive layer formed on the first surface of the base material and containing an infrared absorber;
A heat-shielding adhesive film comprising: a second adhesive layer formed on a surface of the first adhesive layer opposite to the base material and containing an ultraviolet absorber.
The heat shielding adhesive film according to any one of claims 1 to 6, wherein the second adhesive layer has a content of the infrared absorbing agent below a detection limit.