JP7305547B2 - 炭素材料及びその製造方法、蓄電デバイス用電極材料、並びに蓄電デバイス - Google Patents
炭素材料及びその製造方法、蓄電デバイス用電極材料、並びに蓄電デバイス Download PDFInfo
- Publication number
- JP7305547B2 JP7305547B2 JP2019553592A JP2019553592A JP7305547B2 JP 7305547 B2 JP7305547 B2 JP 7305547B2 JP 2019553592 A JP2019553592 A JP 2019553592A JP 2019553592 A JP2019553592 A JP 2019553592A JP 7305547 B2 JP7305547 B2 JP 7305547B2
- Authority
- JP
- Japan
- Prior art keywords
- carbon material
- resin
- graphite
- material according
- storage device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の炭素材料は、グラフェン積層構造を有する炭素材料を含む。本発明の炭素材料のBET比表面積は、240m2/g以上である。また、本発明の炭素材料0.1gを、断面積が3.14cm2の容器に入れ、16kNの圧力で圧縮したときの粉体密度が、0.5g/cc以上である。より具体的に、粉体密度は、例えば、粉体抵抗測定装置(三菱化学アナリテック社製、品番「MCP-T700/PD51」)を用いて測定することができる。この方法においては、炭素材料の粉体0.1gを秤量し、断面積が3.14cm2の容器に入れ、油圧式ポンプにて、16kNまで圧力をかけて圧縮するのと同時に厚みを計測する。その際に算出される密度を粉体密度とすることができる。なお、断面積は、容器の深さ方向に直交する断面の面積であり、例えば、平面形状が略円状の場合は、直径20mmφの容器を用いることができる。
本発明の炭素材料は、グラフェン積層構造を有する炭素材料と、樹脂及び/又は樹脂炭化物の複合体に、例えば、賦活処理を施すことにより得ることができる。
本発明の蓄電デバイスとしては、特に限定されないが、非水電解質一次電池、水系電解質一次電池、非水電解質二次電池、水系電解質二次電池、コンデンサ、電気二重層キャパシタ、又はリチウムイオンキャパシタなどが例示される。本発明の蓄電デバイス用電極材料は、上記のような蓄電デバイスの電極に用いられる電極材料である。
膨張黒鉛(東洋炭素社製、商品名「PFパウダー8」、BET比表面積=22m2/g)1gと、ポリエチレングリコール(PEG、和光純薬工業社製)200gと、テレフタル酸4gと、溶媒としての水80gとを混合し、原料組成物を用意した。用意した原料組成物に、超音波処理装置(本多電子社製)を用い、100W、発振周波数:28kHzで6時間、超音波を照射した。超音波照射により、ポリエチレングリコールを膨張黒鉛に吸着させた。このようにして、ポリエチレングリコールが膨張黒鉛に吸着されている組成物を用意した。
ポリエチレングリコール(PEG)とテレフタル酸の代わりに、芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RLK087」)200gを用いたこと以外は、実施例1と同様にして炭素材料を得た。
ポリエチレングリコール(PEG)とテレフタル酸の代わりに、芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RLK035」)200gを用いたこと以外は、実施例1と同様にして炭素材料を得た。
ポリエチレングリコール(PEG)とテレフタル酸の代わりに、ポリエチレングリコール(PEG)と芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RFK509」)を重量比で、2:1で混合した樹脂200gを用いたこと以外は、実施例1と同様にして炭素材料を得た。
膨張黒鉛(東洋炭素社製、商品名「PFパウダー8」、BET比表面積=22m2/g)1gに対して、芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RLK087」)200gを混合した原料組成物を用いたこと以外は、実施例2と同様にして得られた部分剥離型薄片化黒鉛を得た。得られた部分剥離型薄片化黒鉛0.5gに、賦活剤としての炭酸カリウム0.1gを水5.0gに溶解させた炭酸カリウム水溶液に浸漬させた。それによって、炭酸カリウムの部分剥離型薄片化黒鉛に対する重量比を0.2倍とした(=含浸率0.2)。
ポリエチレングリコール(PEG)とテレフタル酸の代わりに、ポリエチレングリコール(PEG)と芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RFK556」)を重量比で、1:1で混合した樹脂200gを用いたこと以外は、実施例1と同様にして炭素材料を得た。
ポリエチレングリコール(PEG)とテレフタル酸の代わりに、ポリエチレングリコール(PEG)と芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RDK121」)を重量比で、2:1で混合した樹脂200gを用いたこと以外は、実施例1と同様にして炭素材料を得た。
炭素材料として、グラフェン積層構造を有さない活性炭(クラレケミカル社製、商品名「YP50F」)をそのまま用いた。
炭素材料として、グラフェン積層構造を有さない多孔質カーボン(東洋カーボン社製、商品名「MH」)をそのまま用いた。
炭素材料として、グラフェン積層構造を有さないグラフェン(XGサイエンス社製、商品名「C-1000」)をそのまま用いた。
実施例1において、炭酸カリウムを混合して、800℃の温度で、60分維持する加熱工程の代わりに、420℃の温度で、30分維持する加熱工程を行って得られた部分剥離型薄片化黒鉛に、賦活処理を施さずにそのまま炭素材料として用いた。
テレフタル酸を用いなかったこと以外は、実施例1と同様にして炭素材料を得た。
実施例1において、ポリエチレングリコール(PEG)とテレフタル酸の代わりに、芳香族系ポリエステルポリオール(川崎化成工業社製、商品名「RFK509」)を用いた。さらに、炭酸カリウムを浸漬させた部分剥離型薄片化黒鉛を、窒素雰囲気下において、温度(炭化・賦活温度)800℃で、240分間保持することにより、賦活処理を施した。その他の点は、実施例1と同様にして炭素材料を得た。賦活処理における保持時間が極端に長くなると、反応が過剰に進行することでメソ孔が著しく増加し、粉体密度が低下した。
実施例1~7及び比較例1~6で得られた炭素材料について、以下の評価を行った。結果を下記の表1に示す。
実施例1~7及び比較例1~6で得られた炭素材料のBET比表面積は、次のように算出した。高精度ガス吸着量測定装置(マイクロトラック・ベル社製、品番「BELSORP-MAX」、窒素ガス、1.0×10-6<相対圧P/P0<0.99)を用いて吸着等温線の測定を行った。この吸着等温線を解析ソフト(マイクロトラック・ベル社製、ソフト名「BELMaster」)にて、BET法からBET比表面積を算出した。
炭素材料のマイクロ孔の容積は、上記と同様に得られた吸着等温線を解析ソフト(マイクロトラック・ベル社製、ソフト名「BELMaster」)にて、MP法に準拠して算出した。
炭素材料の粉体密度の評価は、粉体抵抗測定装置(三菱化学アナリテック社製、品番「MCP-T700/PD51」)を用いて行った。具体的には、炭素材料0.1gを秤量し、断面積が3.14cm2の容器に入れ、油圧式ポンプにて16kNまで圧力をかけて圧縮するのと同時に厚みを計測した。その際に算出される密度を粉体密度とした。また、BET比表面積(m2/g)と粉体密度(g/cc)との積を求めた。
実施例1~7及び比較例1~5で得られた炭素材料を用いた電気二重層キャパシタの静電容量を測定した。
(式(1)中、Cは静電容量であり単位はF、Iは放電電流値で単位はAである。ΔVは、計算範囲における開始電圧値と終了電圧値との差であって単位はVであり、ここでは範囲が2Vから1Vまでであることから1である。Δtは開始電圧値から終了電圧値になるまで放電するのに要する時間であり単位は秒である。)
◎:20F/cc≦CV
〇:12.5F/cc≦CV<20F/cc
×:CV<12.5F/cc
Claims (19)
- グラフェン積層構造を有する炭素材料を含む炭素材料であって、
前記炭素材料のBET比表面積が、240m2/g以上であり、
前記炭素材料0.1gを、断面積が3.14cm2の容器に入れ、16kNの圧力で圧縮したときの粉体密度が、0.5g/cc以上であり、
前記炭素材料のBJH法に準拠して測定されたメソ孔の容積が、0.04mL/g以上である、炭素材料。 - 前記炭素材料のBET比表面積が、450m2/g以上である、請求項1に記載の炭素材料。
- 前記炭素材料のMP法に準拠して測定されたマイクロ孔の容積が、0.20mL/g以上である、請求項1又は2に記載の炭素材料。
- 前記炭素材料のMP法に準拠して測定されたマイクロ孔の容積をXmL/gとし、前記炭素材料のBJH法に準拠して測定されたメソ孔の容積をYmL/gとしたときに、0.3<X/Y<4である、請求項1~3のいずれか1項に記載の炭素材料。
- 前記グラフェン積層構造を有する炭素材料が、黒鉛又は薄片化黒鉛である、請求項1~4のいずれか1項に記載の炭素材料。
- 前記黒鉛又は薄片化黒鉛が、部分的にグラファイトが剥離されている、部分剥離型薄片化黒鉛である、請求項5に記載の炭素材料。
- 前記炭素材料が、さらに樹脂炭化物を含む、請求項1~6のいずれか1項に記載の炭素材料。
- 前記炭素材料中における前記樹脂炭化物の含有量が、1重量%以上、99.9重量%以下である、請求項7に記載の炭素材料。
- 前記樹脂炭化物が、芳香環を含有する、請求項7又は8に記載の炭素材料。
- 請求項1~9のいずれか1項に記載の炭素材料の製造方法であって、
黒鉛又は一次薄片化黒鉛と樹脂とを混合する混合工程と、
前記混合工程において又は前記混合工程の後に、さらに賦活剤を混合し、混合物を得る工程と、
前記混合物に賦活処理を施す工程と、
を備える、炭素材料の製造方法。 - 前記混合工程において、前記黒鉛又は前記一次薄片化黒鉛と前記樹脂とを含む組成物を200℃~500℃の温度で加熱する、請求項10に記載の炭素材料の製造方法。
- 前記混合工程において、前記黒鉛又は前記一次薄片化黒鉛と前記樹脂と前記賦活剤との混合物を200℃~500℃の温度で加熱する、請求項10又は11に記載の炭素材料の製造方法。
- 前記樹脂が、芳香環を有する樹脂である、請求項10~12のいずれか1項に記載の炭素材料の製造方法。
- 前記芳香環を有する樹脂が、芳香族系ポリエステル樹脂を含有する、請求項13に記載の炭素材料の製造方法。
- 前記芳香環を有する樹脂が、ヒドロキシル基を有する化合物と、カルボキシル基を有する化合物との反応物である、請求項13又は14に記載の炭素材料の製造方法。
- 前記ヒドロキシル基を有する化合物が、多価アルコールである、請求項15に記載の炭素材料の製造方法。
- 前記カルボキシル基を有する化合物が、芳香族多価カルボン酸誘導体である、請求項15又は16に記載の炭素材料の製造方法。
- 請求項1~9のいずれか1項に記載の炭素材料を含有する、蓄電デバイス用電極材料。
- 請求項18に記載の蓄電デバイス用電極材料により構成されている電極を備える、蓄電デバイス。