JP7238396B2 - ポリウレタンポリオール及び接着剤組成物 - Google Patents
ポリウレタンポリオール及び接着剤組成物 Download PDFInfo
- Publication number
- JP7238396B2 JP7238396B2 JP2018243701A JP2018243701A JP7238396B2 JP 7238396 B2 JP7238396 B2 JP 7238396B2 JP 2018243701 A JP2018243701 A JP 2018243701A JP 2018243701 A JP2018243701 A JP 2018243701A JP 7238396 B2 JP7238396 B2 JP 7238396B2
- Authority
- JP
- Japan
- Prior art keywords
- polyol
- derived
- polyurethane
- structural unit
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔1〕ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位のうち少なくとも一方を含むポリオール由来の構造単位と、ポリイソシアネート(b)由来の構造単位と、2個以上の水酸基を有し、ポリオレフィンポリオール(a1)は、脂環式構造を含まず、ポリエステルポリオール(a2)は、水添ダイマー酸由来の構造単位及び水添ダイマージオール由来の構造単位を有し、ポリイソシアネート(b)は、飽和架橋脂環式構造を有する、ポリウレタンポリオール。
〔2〕ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位の合計含有率は40質量%以上95質量%以下であり、ポリイソシアネート(b)由来の構造単位の含有率が5質量%以上60質量%以下である〔1〕に記載のポリウレタンポリオール。
〔3〕ポリオレフィンポリオール(a1)由来の構造単位を含み、ポリオレフィンポリオール(a1)に含まれる炭素原子間の結合は全て単結合である〔1〕または〔2〕に記載のポリウレタンポリオール。
〔4〕環式炭化水素構造及び2つ以上の水酸基を有する環式ポリオール(a3)由来の構造単位を含む〔1〕~〔3〕のいずれかに記載のポリウレタンポリオール。
〔5〕ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位のうち少なくとも一方と、環式ポリオール(a3)由来の構造単位とのみからなる〔4〕に記載のポリウレタンポリオール。
〔6〕環式ポリオール(a3)が、飽和架橋脂環式構造を含むポリオールである、〔4〕または〔5〕に記載のポリウレタンポリオール。
〔7〕環式ポリオール(a3)が、ビスフェノール化合物である、〔4〕または〔5〕に記載のポリウレタンポリオール。
〔8〕ポリオレフィンポリオール(a1)及びポリエステルポリオール(a2)の総量100質量部に対する環式ポリオール(a3)の含有量が5~60質量部である〔4〕~〔7〕のいずれかに記載のポリウレタンポリオール。
〔9〕〔1〕~〔8〕のいずれかに記載のポリウレタンポリオール(A)と、飽和脂肪族ポリイソシアネート、飽和脂環式ポリイソシアネート、及び芳香族ポリイソシアネートのうち、少なくともいずれかを含む硬化剤(B)と、を含む接着剤組成物。
〔10〕ポリウレタンポリオール(A)に含まれる水酸基量1モル当量に対する、硬化剤(B)に含まれるイソシアナト基量が、1~20モル当量である、〔9〕に記載の接着剤組成物。
〔11〕溶剤(C)をさらに含む、〔9〕または〔10〕に記載の接着剤組成物。
〔12〕第1の基材、第2の基材、及び第1の基材と第2の基材との間に設けられた接着剤層と、を備え、前記接着剤層は、〔9〕~〔11〕のいずれかに記載の接着剤組成物の硬化物を含むラミネート材。
〔13〕前記第1の基材が金属箔であり、前記第2の基材が樹脂フィルムである〔12〕に記載のラミネート材。
〔14〕〔13〕に記載のラミネート材からなる電池外装用包装材を備えるリチウムイオン二次電池。
本実施形態にかかるポリウレタンポリオール(A)は、ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位のうち少なくとも一方を含むポリオール由来の構造単位と、ポリイソシアネート(b)由来の構造単位と、2個以上の水酸基と、を含有する。さらに、ポリウレタンポリオール(A)は、環式ポリオール(a3)由来の構造単位を含有することが好ましい。
ポリオレフィンポリオール(a1)は、1種または2種以上のオレフィンの重合体または共重合体であるポリオレフィン骨格と、2つ以上の水酸基とを含有し、かつ脂環構造を有さない化合物である。具体例としては、ポリブタジエンポリオール、ポリイソプレンポリオール等のポリジエンポリオール、及びポリジエンポリオールとポリオレフィンとのグラフト共重合体等が挙げられる。これらの重合体は、1種のみが含まれるものでもよく、2種以上が含まれていてもよい。また、ポリウレタンポリオール(A)から得られる接着剤層の耐電解液性の観点から、ポリオレフィンポリオール(a1)は、構造中に不飽和炭化水素構造を含まないことが好ましい。すなわち、ポリオレフィンポリオール(a1)は、全ての炭素原子間の結合は単結合であることが好ましい。不飽和炭化水素構造を含まないポリオレフィンポリオール(a1)としては、例えば、上記に挙げたポリジエンポリオール水素添加物、及びポリジエンポリオールとポリオレフィンとのグラフト共重合体の水素添加物等が挙げられる。これらの市販品としては、例えば、GI-1000、GI-2000、GI-3000(いずれも日本曹達株式会社製)、及びエポール(登録商標、出光興産株式会社製)等が挙げられる。
ポリエステルポリオール(a2)は、水添ダイマー酸由来の構造単位と、水添ダイマージオール由来の構造単位とを有する。ポリウレタンポリオール(A)を金属箔と樹脂フィルムとのラミネート用接着剤として用いた場合、接着部の耐電解液性が向上するためである。
環式ポリオール(a3)は、環式炭化水素構造と2つ以上の水酸基とを有する化合物である。環式ポリオール(a3)は、単独の化合物からなるものでもよく、2種以上の化合物からなるものでもよい。環式炭化水素構造は、脂環式構造でも芳香環式構造でもよいが、脂環式構造であることが好ましく、飽和脂環式構造であることがより好ましい。ポリウレタンポリオール(A)を金属箔と樹脂フィルムとのラミネート用接着剤として用いた場合に、接着部の耐電解液性を高めるため、環式ポリオール(a3)は、不飽和または飽和脂環式炭化水素構造と2つ以上の水酸基を有し、その他の部分の構造が炭化水素からなる化合物であることが好ましい。
ポリイソシアネート(b)は、2つ以上のイソシアナト基及び飽和架橋脂環式構造を有する化合物である。ポリイソシアネート(b)として、例えば、1,3-ジイソシアナトアダマンタン、3(4),8(9)-ビス(イソシアナトメチル)トリシクロ[5.2.1.0(2,6)]デカン、ノルボルナンジイソシアネート、またこれらのアロファネート化多量体、イソシアヌレート化物、ビウレット変性物等が挙げられる。
ポリウレタンポリオール(A)における、ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位の合計含有率は40質量%以上であることが好ましく、50質量%以上であることがより好ましく、60質量%以上であることがさらに好ましい。ポリウレタンポリオール(A)における、ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位の合計含有率は、95質量%以下であることが好ましく、90質量%以下であることがより好ましく、80質量%以下であることがさらに好ましい。
ポリウレタンポリオール(A)の製造方法としては、特に限定されないが、例えば、ジブチルスズジラウレート、ジオクチルスズジラウレート、ビスマストリス2-エチルヘキサノエート、ジルコニウムテトラアセチルアセトネート等のウレタン化触媒の存在下または非存在下で、ポリオレフィンポリオール(a1)及びポリエステルポリオール(a2)のうち少なくとも1つと、ポリイソシアネート(b)と、を重付加反応させることにより行うことが挙げられる。また、重合される成分として、環式ポリオール(a3)、及びその他の共重合可能な化合物を含むことができる。ここで、「重合される成分」とは、重付加反応、すなわちウレタン化によりポリウレタンポリオール(A)の構造単位になりうる成分を指す。
本実施形態にかかる接着剤組成物は、ポリウレタンポリオール(A)と、硬化剤(B)とを含む。接着剤組成物は、溶剤(C)及びその他の成分を含んでもよい。ポリウレタンポリオール(A)の詳細については、上記の説明の通りである。
硬化剤(B)は、飽和脂肪族ポリイソシアネート、飽和脂環式ポリイソシアネート、及び芳香族ポリイソシアネートのうち、少なくともいずれかを含む。硬化剤(B)は、ポリウレタンポリオール(A)製造の際に用いられるポリイソシアネート(b)以外の成分である。
溶剤(C)は、ポリウレタンポリオール(A)及び硬化剤(B)を溶解または分散可能なものであれば特に限定されない。溶剤(C)としては、例えば、トルエン、キシレン等の芳香族系有機溶剤、シクロヘキサン、メチルシクロヘキサン、エチルシクロヘキサン等の脂環式系有機溶剤、n-ヘキサン、n-ヘプタン等の脂肪族系有機溶剤、酢酸エチル、酢酸プロピル、酢酸ブチル等のエステル系有機溶剤、アセトン、メチルエチルケトン、メチルブチルケトン等のケトン系有機溶剤等が挙げられる。これらは、単独または2種以上混合して使用することができる。
接着剤組成物は、必要に応じて、かつ本発明の効果が得られる範囲で、反応促進剤、粘着性付与剤、可塑剤、熱可塑性樹脂、熱可塑性エラストマー等を含有していてもよい。
本実施形態にかかるラミネート材は、第1の基材、第2の基材、及び第1の基材と第2の基材との間に設けられた接着剤層と、を備え、接着剤層は上記接着剤組成物の硬化物を含む。ここで接着剤組成物の硬化物には、樹脂成分の硬化物に限らず、含有する樹脂の合成に用いた開始剤、各種添加剤等、またはこれらの成分に由来する成分が含まれていてもよい。
本実施形態の電池外装用包装材は、上記ラミネート材が用いられる。本実施形態の電池外装用包装材に用いられるラミネート材の好ましい構成は、樹脂フィルム層と、接着剤層と、この接着剤層を挟んで樹脂フィルムに対向して設けられた金属箔層と、接着剤層と反対側の金属箔層の面と対向して設けられた外層を備える。
(2)外層/第1中間樹脂層/金属箔層/接着剤層/樹脂フィルム層
(3)外層/金属箔層/第2中間樹脂層/接着剤層/樹脂フィルム層
(4)外層/第1中間樹脂層/金属箔層/第2中間樹脂層/接着剤層/樹脂フィルム層
(5)コート層/外層/金属箔層/接着剤層/樹脂フィルム層
(6)コート層/外層/第1中間樹脂層/金属箔層/接着剤層/樹脂フィルム層
(7)コート層/外層/金属箔層/第2中間樹脂層/接着剤層/樹脂フィルム層
(8)コート層/外層/第1中間樹脂層/金属箔層/第2中間樹脂層/接着剤層/樹脂フィルム層
樹脂フィルム層は、ヒートシール性を有し、リチウムイオン二次電池の電解液等に対する電池外装用包装材の耐薬品性を向上させる。樹脂フィルム層を構成するフィルムとしては、ポリプロピレン、ポリエチレン、マレイン酸変性ポリプロピレン、エチレン-アクリレート共重合体またはアイオノマー樹脂などの熱融着性樹脂フィルムが好ましい。
接着剤層は、本実施形態にかかる接着剤組成物の硬化物を含む層であり、接着剤組成物の詳細な構成については上で説明したとおりである。
金属箔層は、酸素及び水分の包装内への浸入を防止するバリア層としての役割を担う。金属箔層の材質としては純アルミニウム(1000系)またはアルミニウム-鉄系合金のO材(軟質材)であることが好ましい。金属箔層の厚さは10μm以上であることが好ましい。ラミネート材の成形時における金属箔層の破断及びピンホールの発生を抑制するためである。この観点から、金属箔層の厚さは、30μm以上であることが好ましく、40μm以上であることがより好ましい。
外層は、樹脂フィルムを用いることが好ましい。外層として使用する樹脂フィルムは、耐熱性、成形性、絶縁性等に優れたものであることが好ましく、ポリアミド(ナイロン)樹脂またはポリエステル樹脂の延伸フィルムを用いることが好ましい。この外層の厚さは、9μm以上であることが好ましい。ラミネート材の成形を行うときに外層のネッキング、及びラミネート材の成形不良を抑制するためである。この観点から、外層の厚さは、10μm以上であることがより好ましく、20μm以上であることがさらに好ましい。
コート層としては、ガスバリア性を有するポリマーをコートしたもの、アルミニウム金属、酸化ケイ素・酸化アルミニウム等の無機酸化物を蒸着し、その上から金属及び無機物の薄膜をコートしたものなどがある。コート層を設けることにより、水蒸気及びその他のガスバリア性がより優れたラミネート材が得られる。
本実施形態にかかる電池ケースは、上記のラミネート材(電池外装用包装材)を成形することによって得られる。成型方法としては絞り成形、ブロー成型等が挙げられる。本実施形態にかかるラミネート材は耐電解液性、耐熱性、さらには、水蒸気及び酸素等に対するガスバリア性に優れており、非水系二次電池、特にリチウムイオン二次電池用の電池ケースとして好適に用いられる。また、本実施形態にかかるラミネート材は成形性が非常に良好であるため、深い凹凸、あるいは高い曲率等を有する様々な形状の電池ケースを得ることができる。成形の方法は特に限定されないが、深絞り成形または張り出し成形によって成形すると、複雑な形状を有し、かつ寸法精度が高い電池ケースを作製することができる。
カラム:昭和電工株式会社製、KF-806L
カラム温度:40℃
試料:試料ポリマーの0.2質量%テトラヒドロフラン溶液
流量:2ml/分
溶離液:テトラヒドロフラン
検出器:示差屈折率計(RI)
〔1-1.ポリイソシアネート(b-1)〕
1,3-ジアミノアダマンタンを原料として冷熱2段ホスゲン化法により、架橋構造を有する飽和脂環構造を含むポリイソシアネート(b-1)を得た。具体的な合成方法は以下のとおりである。
3(4),8(9)-ビス(アミノメチル)トリシクロ[5.2.1.0(2,6)]デカンを原料として冷熱2段ホスゲン化法により、架橋構造を有する飽和脂環構造を含むポリイソシアネートを得た。撹拌機、冷却器、温度計及び塩化水素ガス導入管を備えた四ツ口フラスコに、3(4),8(9)-ビス(アミノメチル)トリシクロ[5.2.1.0(2,6)]デカン(徐州徳威化学技術有限公司製)38.8gを、o-ジクロルベンゼン200mlに溶解した後、撹拌しながら、乾燥塩化水素ガスを導入した。その後130℃に昇温してホスゲンを1時間当たり、40gの割合で5時間導入し、次いで反応温度を180℃にしてホスゲンを1時間当たり20gの割合で5時間導入し、さらに同温度で1時間保持して反応を完結させた。得られた混合物からo-ジクロルベンゼンを減圧下に留去した後、沸点169~173℃/0.4mmHgの透明液体留分として、ポリイソシアネート(b-2)26.2g(NCO含量34.1質量%)を得た。
攪拌機、水分離器付き反応容器中に、水添ダイマージオールとして「Sovermol908」(BASF社製)を220g、水添ダイマー酸として「EMPOL1008」(BASF社製)を230g、触媒のブチルスズジラウレートとして「KS-1260」(堺化学工業製)を0.10g仕込み、240℃、大気圧下から始めて縮合水を流出させながら150mmHgまで60分で減圧し、150mmHgで60分保持して脱水エステル化反応を行い、ポリエステルポリオール(a2-1)を得た。
〔3-1.ポリウレタンポリイソシアネート(1)〕
攪拌装置、温度計およびコンデンサーを備えた反応容器中に、ビスフェノールA(新日鐵化学製、化合物名2,2-ビス(4-ヒドロキシフェニル)プロパン)を23.29g、「KS-1260」(堺化学工業製、ジブチルスズジラウレート)を0.01gおよび、「コスモネートNBDI」(三井化学製ノルボルナンジイソシアネートイソシアネート)を31.50g、メチルエチルケトンを113g投入し、撹拌しながら、オイルバスを用いて85~90℃に昇温した。その後、2.5時間撹拌しながら反応を継続して、ポリウレタンポリイソシアネート(1)のメチルエチルケトン溶液を得た。
ビスフェノールAの代わりにビスフェノールF(本州化学工業製)20gを用いたこと以外は、ポリウレタンポリイソシアネート(1)の合成方法と同様にして、ポリウレタンポリイソシアネート(2)のメチルエチルケトン溶液を得た。
攪拌装置、温度計およびコンデンサーを備えた反応容器中に、重合される成分、触媒、酸化防止剤を表1に示される量、及び表1に示される溶剤のうち70gを投入し、撹拌しながら、オイルバスを用いて85~90℃に昇温した。なお、ポリウレタンポリオール(A-5)及び(CA-2)で用いた溶剤はトルエンとメチルエチルケトンとの質量比1:1の混合溶剤であり、それ以外はトルエンを用いた。その後、2.5時間撹拌しながら反応を継続した。赤外吸収スペクトルを測定し、イソシアナト基の吸収が消失していることを確認して反応を終了し、さらに表1に示させる溶剤を、先に投入した70gと合わせて表1の量となるように投入して撹拌溶解し、ポリウレタンポリオール(A-1)~(A-10)及びポリウレタンポリオール(CA-1)~(CA-3)の溶液(固形分濃度18質量%)を得た。
各実施例及び比較例における組成は表2に示すとおりである。
〔5-1.ラミネート材の作製〕
実施例1~10及び比較例1~3で作製したそれぞれの接着剤組成物を用いて、以下のようにして外層/外層用接着剤層/金属箔層/接着剤層/樹脂フィルムの構造を有するラミネート材をドライラミネーション方式で製造した。
得られた電池ケース用包装材料について、常態T字剥離強度、電解液溶媒浸漬後のT字剥離強度および85℃雰囲気下でのT字剥離強度を測定した。測定の条件、方法は下記の(1)~(3)の通りである。各試験は、n=2で行い、その平均値をとった。また、結果を表2に示す。
JIS K 6854-2(1999)に基づいて測定した。作製されたラミネート材を長さ150mm×幅15mmで切り出し試験片とした。試験片の端部においてアルミニウム箔層と樹脂フィルムとを一部剥離し、剥離した部分を装置でつかんでオートグラフAG-X(株式会社島津製作所製)を用いて、23℃×50%RH雰囲気下に剥離速度100mm/minで剥離させ、金属箔層と樹脂フィルム層間の180°剥離強度を測定した。
長さ150mm×幅15mmの試験片を電解液溶媒(エチレンカーボネート/ジエチルカーボネート、質量比50/50)に浸漬し、85℃雰囲気下に1日放置した後に取り出し、その試験片を用いて上記(1)と同様にしてアルミニウム箔層と未延伸ポリプロピレンフィルム層間の180°剥離強度を測定した。測定方法は上記同様JIS K 6854-2(1999)に基づく。
長さ150mm×幅15mmの試験片を85℃雰囲気下に放置し、試験片の温度が85℃になった後に剥離速度100mm/minで剥離させ、アルミニウム箔層と未延伸ポリプロピレンフィルム層間の180°剥離強度を測定した。JIS K 6854-2(1999)に基づく。
表2の結果から、本発明の金属箔と樹脂フィルムのラミネート用接着剤(実施例1~10)は、常態T字剥離強度、電解液溶媒浸漬後のT字剥離強度および85℃雰囲気下でのT字剥離強度のいずれにおいても優れていることがわかる。
Claims (14)
- ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位のうち少なくとも一方を含むポリオール由来の構造単位と、
ポリイソシアネート(b)由来の構造単位と、
2個以上の水酸基を有し、
ポリオレフィンポリオール(a1)は、脂環式構造を含まず、
ポリエステルポリオール(a2)は、水添ダイマー酸由来の構造単位及び水添ダイマージオール由来の構造単位を有し、
ポリイソシアネート(b)は、飽和架橋脂環式構造を有する、
ポリウレタンポリオール。 - ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位の合計含有率は40質量%以上95質量%以下であり、ポリイソシアネート(b)由来の構造単位の含有率が5質量%以上60質量%以下である請求項1に記載のポリウレタンポリオール。
- ポリオレフィンポリオール(a1)由来の構造単位を含み、ポリオレフィンポリオール(a1)に含まれる炭素原子間の結合は全て単結合である請求項1または2に記載のポリウレタンポリオール。
- 環式炭化水素構造及び2つ以上の水酸基を有する環式ポリオール(a3)由来の構造単位を含む請求項1~3のいずれか1項に記載のポリウレタンポリオール。
- ポリオール由来の構造単位は、ポリオレフィンポリオール(a1)由来の構造単位及びポリエステルポリオール(a2)由来の構造単位のうち少なくとも一方と、環式ポリオール(a3)由来の構造単位とのみからなる請求項4に記載のポリウレタンポリオール。
- 環式ポリオール(a3)が、飽和架橋脂環式構造を含むポリオールである、請求項4または5に記載のポリウレタンポリオール。
- 環式ポリオール(a3)が、ビスフェノール化合物である、請求項4または5に記載のポリウレタンポリオール。
- ポリオレフィンポリオール(a1)及びポリエステルポリオール(a2)の総量100質量部に対する環式ポリオール(a3)の含有量が5~60質量部である請求項4~7のいずれか1項に記載のポリウレタンポリオール。
- 請求項1~8のいずれか1項に記載のポリウレタンポリオール(A)と、
飽和脂肪族ポリイソシアネート、飽和脂環式ポリイソシアネート、及び芳香族ポリイソシアネートのうち、少なくともいずれかを含む硬化剤(B)と、
を含む接着剤組成物。 - ポリウレタンポリオール(A)に含まれる水酸基量1モル当量に対する、硬化剤(B)に含まれるイソシアナト基量が、1~20モル当量である、請求項9に記載の接着剤組成物。
- 溶剤(C)をさらに含む、請求項9または10に記載の接着剤組成物。
- 第1の基材、第2の基材、及び第1の基材と第2の基材との間に設けられた接着剤層と、を備え、
前記接着剤層は、請求項9~11のいずれか1項に記載の接着剤組成物の硬化物を含むラミネート材。 - 前記第1の基材が金属箔であり、前記第2の基材が樹脂フィルムである請求項12に記載のラミネート材。
- 請求項13に記載のラミネート材からなる電池外装用包装材を備えるリチウムイオン二次電池。