JP7221339B2 - 低放射率コーティングを使用する、レーザ溶接用の透明な板ガラス - Google Patents
低放射率コーティングを使用する、レーザ溶接用の透明な板ガラス Download PDFInfo
- Publication number
- JP7221339B2 JP7221339B2 JP2021121287A JP2021121287A JP7221339B2 JP 7221339 B2 JP7221339 B2 JP 7221339B2 JP 2021121287 A JP2021121287 A JP 2021121287A JP 2021121287 A JP2021121287 A JP 2021121287A JP 7221339 B2 JP7221339 B2 JP 7221339B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- low
- emissivity layer
- glass sheet
- bumps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
2つの板ガラスの各々の1つの試料を、板ガラス間の界面に、板ガラスと接触している低放射率コーティングとともに配置した。355nmの波長を有するUVレーザからのレーザビームを、2つの板ガラス間の界面に略直交して提供した。3ワットのレーザビームを、界面におけるビームスポット径が約100μmになるように、板ガラス間の界面を横切って導いた。レーザビームを、30mm/秒で板ガラスの界面を横切って平行移動させた。レーザエネルギーを吸収することによって、低放射率コーティングを加熱し、2つのソーダ石灰板ガラスをともに結合させて、端部封止30を生成した。2つの板ガラス間の結合の写真が図6に提示されている。図6における結合の幅WBは、約130μmである。
次の8つの試験については、上述の2つの板ガラス(1つのSLG板ガラスと、一方の表面に低-eコーティングを有する1つのSLG板ガラス)の各々の一方を使用した。すなわち、8対の板ガラス(各対の一方は低-eコーティングを有する)を次のように調製した。ガラスバンプスペーサを、8つのSLG板ガラス(すなわち、低-eコーティングを有しない板ガラス)の各々にレーザ誘起することによって形成した。具体的には、15ワットでの355nm波長のレーザビームを、板ガラスの各々に通し、その後ろに収束させて、150μmの高さ及び600μmの直径を有する、ガラスバンプスペーサを生成した。各ガラスバンプを、380℃で約3時間、プラズマ洗浄して(すなわち、イオン化ガス照射による)、ガラスバンプ表面から汚染物質(例えば、微粒子)を除去した。低-eコーティングを有する8つのSLG板ガラスの半分を、最初に380℃で約3時間、加熱処理して、有機物除去の間のVIG窓の加熱をシミュレートし、次に、410℃で約30分間、加熱処理して、VIG窓のフリット端部封止をシミュレートした。低-eコーティングを有する他の4つのSLG板ガラスは、試験前に加熱処理されなかった。
封止された物品であって、
第1のガラス材料、第1の外面と反対側の第1の内面、及び第1の外縁を含む、第1の板ガラスと、
第2のガラス材料、第2の外面と反対側の第2の内面、及び第2の外縁を含む、第2の板ガラスであって、
前記第1の板ガラスから離間され、かつ、前記第1及び第2の内面が互いに向き合うように、前記第1の板ガラスに略平行に配置されている、第2板ガラスと、
前記第1及び第2の板ガラスの対向する前記内面の間の低放射率層と
前記低放射率層に隣接する端部封止であって、前記第1及び第2の板ガラスの間に封止された内部領域を画成するように、前記第1及び第2の外縁の少なくとも一部の周りに形成され、かつ、それらを接続する、端部封止
を含む、封止された物品。
前記結合が、前記低放射率層によって予め決められた波長を有するレーザ光を少なくとも30%吸収することによって形成される、レーザ誘起された結合であることを特徴とする、実施形態1に記載の物品。
前記レーザ光の前記予め決められた波長が、100nm~400nmであることを特徴とする、実施形態2に記載の物品。
前記レーザ誘起された結合が、約10μm~約1,000μmの幅を有することを特徴とする、実施形態2に記載の物品。
前記第1の板ガラス、前記第2の板ガラス、及び前記低放射率層が、420nm~750nmにおいて透過性であることを特徴とする、実施形態1~4のいずれかに記載の物品。
前記低放射率コーティングが、約50nm~約500nmの厚さを有することを特徴とする、実施形態1~5のいずれかに記載の物品。
前記第1の板ガラス又は前記第2の板ガラスの前記内面上に形成された複数のガラスバンプをさらに含み、前記低放射率層が前記複数のガラスバンプと前記対向する内面との間にあることを特徴とする、実施形態1~6のいずれかに記載の物品。
前記低放射率層が、前記複数のガラスバンプと前記対向する内面との間の摩擦を低減することを特徴とする、実施形態1~7のいずれかに記載の物品。
前記低放射率層と前記複数のガラスバンプのうちの1つとの間の静止摩擦係数が、前記複数のガラスバンプのうちの1つにおける1N~200Nの負荷に対して約0.1~約0.4の範囲であり、前記負荷が前記第1の内面と略直交することを特徴とする、実施形態1~8のいずれかに記載の物品。
前記結合が、前記第1及び第2の板ガラスの前記内面間に、封止された内部領域を生成することを特徴とする、実施形態1~9のいずれかに記載の物品。
真空絶縁ガラス(VIG)窓であって、
第1のガラス材料、第1の外面と反対側の第1の内面、及び第1の外縁を含む、第1の板ガラスと、
第2のガラス材料、第2の外面と反対側の第2の内面、及び第2の外縁を含む、第2の板ガラスであって、
前記第1の板ガラスから離間され、かつ、前記第1の板ガラスに略平行に配置されている、第2の板ガラスと、
前記第2の板ガラスの前記第2の内面上の低放射率コーティングと、
前記第1の板ガラスの前記第1の内面上に前記第1のガラス材料で形成された、複数のガラスバンプと、
前記第1及び第2の板ガラスの間に封止された内部領域を画成するように、前記第1及び第2の外縁の少なくともそれぞれの一部分の周りに形成された、前記低放射率層に隣接した、レーザ誘起された端部封止と
を含み、
前記第1の板ガラスの前記第1の内面上の前記複数のレーザで形成されたガラスバンプが、前記第2の板ガラスの前記第2の内面上の前記低放射率コーティングと接している、
真空絶縁ガラス(VIG)窓。
前記低放射率コーティングが、SiO2、Al2O3、ZnO、TiO2、SnO2、及びそれらの組合せからなる群より選択される無機層を含むことを特徴とする、実施形態11に記載の窓。
前記低放射率コーティングが、金、銀、銅、及びそれらの組合せからなる群より選択される金属層を含むことを特徴とする、実施形態11又は12に記載の窓。
前記第1の板ガラスの前記第1の内面と対向する前記低放射率コーティングの上層が、SiO2、Al2O3、又はそれらの組合せを含むことを特徴とする、実施形態11~13のいずれかに記載の窓。
前記低放射率コーティングが、701nm~2,000nmの波長を有する太陽光を反射することを特徴とする、実施形態11~14のいずれかに記載の窓。
前記低放射率コーティングと前記複数のガラスバンプのうちの1つとの間の静止摩擦係数が、前記複数のガラスバンプのうちの1つにおける40N~160Nの負荷に対して0.1~0.4の範囲であり、前記負荷が前記第1の内面と略直交することを特徴とする、実施形態11~15のいずれかに記載の窓。
前記第1の板ガラス、前記第2の板ガラス、及び前記低放射率コーティングが、約450nm~約625nmの波長において、最大で70%の組合せ透過を有することを特徴とする、実施形態11~16のいずれかに記載の窓。
前記複数のガラスバンプが、約80μm~約300μmの高さを有することを特徴とする、実施形態11~17のいずれかに記載の窓。
前記第2の板ガラスが、構造体における外側の板ガラスであることを特徴とする、実施形態11~18のいずれかに記載の窓。
真空絶縁ガラス(VIG)窓の製造方法において、
第1の板ガラスにレーザ光を照射して、前記第1の板ガラスの第1の内面上に複数のガラスバンプを形成する工程であって、
前記第1の板ガラスが、第1のガラス材料、第1の外面と反対側の前記第1の内面、及び第1の外縁を含む、工程、
前記第1の板ガラスの前記第1の内面を、第2の板ガラスの第2の内面に隣接し、かつ、該第2の板ガラスと略平行に配置する工程であって、
前記第2の板ガラスが、第2のガラス材料、第2の外面と反対側の前記第2の内面、及び第2の外縁を含み、かつ
前記第2の内面が低放射率コーティングを含む、工程、及び
前記低放射率コーティングを、予め決められた波長を有するレーザ光と接触させることによって、前記第1及び第2の板ガラスを結合して、前記第1及び第2の板ガラスの前記第1及び第2の内面間に封止された内部領域を生成する工程であって、
前記第1の内面上の前記複数のガラスバンプが、前記封止された内部領域内の前記第2の板ガラスの前記第2の内面上の前記低放射率コーティングに接している、工程
を含む、方法。
前記封止された内部領域の内側に大気圧より低い圧力を生成する工程をさらに含むことを特徴とする、実施形態20に記載の方法。
前記低放射率コーティングを、予め決められた波長を有するレーザ光と接触させる工程が、約1mm/秒~約1000mm/秒の速度で前記レーザ光によって形成されるレーザスポットを移動させて、前記低放射率コーティングを加熱する工程をさらに含むことを特徴とする、実施形態20に記載の方法。
20 板ガラス
22 表面
23B本体部分
24 表面
25 低放射率層
28 ギャップ/封止された縁部
30 端部封止
40 封止された内部領域
50 ガラスバンプスペーサ
51 ガラスバンプの上部
100 レーザ
102 レーザビーム
Claims (7)
- 封止された物品であって、
(i)第1のガラス材料、第1の外面と反対側の第1の内面、及び第1の外縁を含む、第1の板ガラスと、
(ii)第2のガラス材料、第2の外面と反対側の第2の内面、及び第2の外縁を含む、第2の板ガラスであって、
前記第1の板ガラスから離間され、かつ、前記第1及び第2の内面が互いに向き合うように、前記第1の板ガラスに略平行に配置されている、第2の板ガラスと、
(iii)前記第1及び第2の板ガラスの対向する前記内面の間の低放射率層と、前記低放射率層が約50nm~約500nmの厚さを有し、
前記第1の板ガラス、前記第2の板ガラス、及び前記低放射率層が、420nm~750nmの可視光波長に対して透過性であり、
(iv)前記低放射率層に隣接するレーザ誘起された端部封止であって、溶解した低放射率層を有する前記第1及び第2の板ガラスの間に封止された内部領域を画成するように、前記第1及び第2の表面の少なくとも一部の周りに形成され、かつ、それらを接続する、端部封止と、
を含む、物品。 - 前記第1の板ガラス又は前記第2の板ガラスの前記内面上に形成された複数のガラスバンプをさらに含み、前記低放射率層が、前記複数のガラスバンプと前記対向する内面との間にあることを特徴とする、請求項1に記載の物品。
- 前記低放射率層が、前記複数のガラスバンプと前記対向する内面との間の摩擦を低減し、
前記低放射率層と前記複数のガラスバンプのうちの1つとの間の静止摩擦係数が、前記複数のガラスバンプのうちの1つにおける1N~200Nの負荷に対して約0.1~約0.4の範囲であり、前記負荷が前記第1の内面と略直交する
ことを特徴とする、請求項2に記載の物品。 - 請求項2又は3に記載の封止された物品からなり、
前記第1の板ガラスの前記第1の内面上の前記複数のガラスバンプが、前記第2の板ガラスの前記第2の内面上の前記低放射率層と接している真空絶縁ガラス(VIG)窓。 - 前記低放射率層が、SiO2、Al2O3、ZnO、TiO2、SnO2、及びそれらの組合せからなる群より選択される無機層を含み、かつ
前記低放射率層が、金、銀、銅、及びそれらの組合せからなる群より選択される金属層を含むことを特徴とする、請求項4に記載の窓。 - 前記低放射率層が、701nm~2,000nmの波長を有する赤外(IR)と近赤外(NIR)からなる太陽光を反射し、
前記第1の板ガラス、前記第2の板ガラス、及び前記低放射率層が、約450nm~約625nmの波長において、最大で70%の組合せ透過を有することを特徴とする、請求項4又は5に記載の窓。 - 前記低放射率層と前記複数のガラスバンプのうちの1つとの間の静止摩擦係数が、前記複数のガラスバンプのうちの1つにおける40N~160Nの負荷に対して0.1~0.4の範囲であり、前記負荷が前記第1の内面と略直交し、
前記複数のガラスバンプが、約80μm~約300μmの高さを有することを特徴とする、請求項4~6のいずれか一項に記載の窓。