JP7125335B2 - Uリブ用速硬型軽量充填モルタル組成物及びそのモルタル - Google Patents
Uリブ用速硬型軽量充填モルタル組成物及びそのモルタル Download PDFInfo
- Publication number
- JP7125335B2 JP7125335B2 JP2018219574A JP2018219574A JP7125335B2 JP 7125335 B2 JP7125335 B2 JP 7125335B2 JP 2018219574 A JP2018219574 A JP 2018219574A JP 2018219574 A JP2018219574 A JP 2018219574A JP 7125335 B2 JP7125335 B2 JP 7125335B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- mortar
- parts
- binder
- mortar composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]セメント、カルシウムアルミネート類及び石膏類からなる結合材と、単位容積質量が0.3kg/L以下の軽量骨材とを含み、結合材は、結合材全質量を基準として、カルシウムアルミネート類の質量割合が5~14質量%であり、石膏類の質量割合が5~12質量%であり、軽量骨材の含有量は、結合材100質量部に対し、4~9.5質量部である、Uリブ用速硬型軽量充填モルタル組成物。
[2]減水剤及び/又は増粘剤を更に含む、[1]に記載のモルタル組成物。
[3]アルカリ金属炭酸塩及び/又は凝結遅延剤を更に含む、[1]又は[2]に記載のモルタル組成物。
[4][1]~[3]のいずれかに記載のモルタル組成物と水とを含み、水の含有量が、結合材100質量部に対し、45~55質量部である、Uリブ用速硬型軽量充填モルタル。
セメント:普通ポルトランドセメント
カルシウムアルミネート類:アルミナセメント
石膏類:無水石膏
軽量骨材A:真珠岩系軽量骨材(単位容積質量0.1kg/L)
軽量骨材B:真珠岩系軽量骨材(単位容積質量0.25kg/L)
アルカリ金属炭酸塩:炭酸ナトリウム、炭酸リチウム
増粘剤:メチルセルロース系増粘剤
減水剤:メラミン系減水剤
凝結遅延剤:クエン酸
発泡剤:過炭酸ナトリウム
セメント、カルシウムアルミネート類及び石膏類からなる結合材100質量部に対して、各種材料を表1に示す量として配合設計した。
20℃又は30℃環境下において、10Lの円筒容器に配合設計したモルタル組成物3000gと水を添加し、ハンドミキサーで90秒混練してモルタルを作製した。水は、結合材100質量部に対して51質量部を添加した。
下記の評価方法にて、各種モルタルの評価を行った。20℃で評価した結果を表2に示し、30℃で評価した結果を表3に示す。
・フロー値
JIS R 5201:2015「セメントの物理試験方法」12.フロー試験に準じて、各温度環境下でモルタルのフロー値(0打)を測定した。
・単位容積質量の測定
JIS A 1171:2016「ポリマーセメントモルタルの試験方法」6.4単位容積質量試験に準拠し、単位容積質量を測定した。
・可使時間
20℃又は30℃環境下において、練上がり後のモルタルを5L容器に移し替え、練上がり直後から15分毎に上記フロー試験値を測定した。ただし、測定前はさじでモルタルを5回撹拌したものをサンプルとした。可使時間の指標として、フロー値が160mmを下回るまでの時間を測定した。例えば、75分後のフロー値が160mm以上であり、90分後のフロー値が160mm以下若しくは測定不可の場合、作業時間を75分とした。
・圧縮強度
土木学会基準JSCE-G 505-2010「円柱供試体を用いたモルタル又はセメントペーストの圧縮強度試験方法(案)」に準じて、各材齢におけるモルタル硬化体の圧縮強度を測定した。供試体の寸法は、直径50mm、高さ100mmとした。養生は、材齢が24時間以内のものは材齢直前まで各温度にて型枠のまま湿潤養生とした。材齢28日は、24時間後に型枠を脱枠し、以降材齢28日まで水中養生とした。
Claims (4)
- セメント、カルシウムアルミネート類及び石膏類からなる結合材と、単位容積質量が0.3kg/L以下の軽量骨材とを含み、
前記結合材は、該結合材全質量を基準として、前記カルシウムアルミネート類の質量割合が5~14質量%であり、前記石膏類の質量割合が5~12質量%であり、
前記軽量骨材の含有量は、前記結合材100質量部に対し、4~9.5質量部である、Uリブ用速硬型軽量充填モルタル組成物。 - 減水剤及び/又は増粘剤を更に含む、請求項1に記載のモルタル組成物。
- アルカリ金属炭酸塩及び/又は凝結遅延剤を更に含む、請求項1又は2に記載のモルタル組成物。
- 請求項1~3のいずれか一項に記載のモルタル組成物と水とを含み、
水の含有量が、前記結合材100質量部に対し、45~55質量部である、Uリブ用速硬型軽量充填モルタル。