JP6608836B2 - Wipe sheet - Google Patents

Description

  The present invention relates to a wiping sheet comprising a nonwoven fabric containing two types of cellulose fibers and an impregnation liquid impregnated in the nonwoven fabric.

  As a wet type non-woven fabric impregnated with liquid for human body, for example, stickiness of face and body, body wiping sheet for removing dirt, cleansing sheet for removing makeup dirt, moisturizing face Face masks are widely used. Of these, cleansing sheets and face masks require good slippery and soft feel, so generally these are spunlace nonwoven fabrics mainly made of cellulose fibers such as rayon and cotton. It is done. For example, JP 2007-177373 A (Patent Document 1) discloses a sheet base material for a wet sheet made of a spunlace nonwoven fabric using two or more kinds of cellulose fibers.

  On the other hand, some body wiping sheets are required to have firmness and stiffness from the viewpoint of usability when wiping the whole body. In addition, from the viewpoint of obtaining a feeling of wiping firmly, there is a thing that requires a characteristic that a gritty feel (going sensation) can be obtained when wiping. As a means for improving the above-mentioned harshness and firmness, it is known to use a spunbonded nonwoven fabric in which fibers are bonded with an acrylic adhesive or the like. As a nonwoven fabric for wet wipers that pays attention to such a feeling of tingling, for example, in Japanese Patent Application Laid-Open No. 2013-167028 (Patent Document 2), a heat-fusible binder fiber and a specific pulp fiber are separated by high-pressure columnar water flow. A nonwoven fabric for wet wipers that is three-dimensionally entangled and has a fixing portion due to melting of a heat-bonding binder fiber is disclosed.

  In general, the impregnating liquid for a body wiping sheet contains a lower alcohol (mainly ethanol) at a relatively high concentration from the viewpoint of refreshing feeling and refreshing feeling during use, and quick drying. For this reason, when the adhesive component contained in the nonwoven fabric used as the base material of the wiping sheet for body dissolves in the impregnating solution over time, a bad odor is generated, or the active components (sterilizing component, preservative, etc.) contained in the impregnating solution ) May cause degradation and may have stability problems. Furthermore, with the dissolution of the adhesive component, there may be a case where the wiping feeling of the body wiping sheet and a reduction in the elasticity and stiffness are caused.

  In addition, there is also known a means for improving the harshness and elasticity of a sheet using a nonwoven fabric mainly composed of olefin fiber such as polypropylene. However, non-woven fabrics mainly composed of such olefin fibers have poor retention of the impregnating solution, so they dry quickly when wiping the body, and as a wiping sheet for the body, sufficient wiping properties are obtained. There is a problem that can not be.

  Further, a wet sheet is also known in which a synthetic short fiber and a hydrophilic short fiber are mixed, and the constituent fibers are three-dimensionally entangled with each other to impregnate a non-woven fabric configured to have a specific ratio. (For example, Unexamined-Japanese-Patent No. 2001-336056 (patent document 3)). However, in Patent Document 3, there is no mention of the above-mentioned tingling feeling.

JP 2007-177373 A Japanese Unexamined Patent Publication No. 2013-167028 JP 2001-336056 A

  As described above, all of the conventionally known means for improving the feeling of tingling and firmness are impregnated with a relatively high concentration of lower alcohol and required to have high liquid retention. A wiping sheet suitable for this application has not yet been obtained.

  The present invention has been made in order to solve the above-mentioned problems, and the object thereof is to impregnate a relatively high concentration of a lower alcohol while having a high liquid retention, and It is to provide a wiping sheet having improved elasticity and stiffness.

The wiping sheet of the present invention comprises a nonwoven fabric containing two types of cellulose fibers, an impregnating liquid impregnated in the nonwoven fabric, and containing water and ethanol, and measured by a surface test when wet under pressure by the KFX method. The number of irregularities is in the range of 10 to 30, and the basis weight of the nonwoven fabric is 30 to 100 g / m ² .

  In the wiping sheet of the present invention, it is preferable that the unevenness of the surface on either one or both of the longitudinal and lateral sides of the nonwoven fabric not containing the impregnating liquid is 0.5 to 3.5 mm.

  The wiping sheet of the present invention preferably has a release rate measured by a retentate discharge test by the KFX method in the range of 20 to 50%.

  In the wiping sheet of the present invention, it is preferable that one of the two types of cellulose fibers constituting the nonwoven fabric is rayon and the other is lyocell.

  In the wiping sheet of the present invention, it is preferable that the non-woven fabric further includes a heat-sealing fiber. In this case, the non-woven fabric is 10 to 80% by weight of rayon and 10 to 80% by weight so that the total amount becomes 100% by weight. It is more preferable to contain 5% by weight of lyocell and 5 to 30% by weight of heat-sealing fibers.

In the wiping sheet of the present invention, the apparent density of the nonwoven fabric is preferably 0.05 to 0.15 g / cm ³ .

  The wiping sheet of the present invention is preferably an interpersonal wet wiping sheet, and more preferably a wiping sheet for wiping a human body.

Moreover, this specification is a wiping sheet containing a nonwoven fabric and an impregnating liquid impregnated in the nonwoven fabric as a wiping sheet of a specific embodiment that exhibits the effects of the present invention, and the nonwoven fabric is a total of 10 to 80% by weight of rayon, 10 to 80% by weight of lyocell, and 5 to 30% by weight of heat-sealing fibers, so that the nonwoven fabric is a spunlace nonwoven fabric, and the basis weight of the nonwoven fabric is 100% by weight The amount is 30 to 100 g / m ² , the rayon has a fineness of 2.0 to 5.0 dtex, the lyocell has a fineness of 0.9 to 3.3 dtex, and the heat-fusible fiber has a fineness of 1.2 to 2 .2 dtex, and the impregnation liquid contains water and 30 to 70% by weight of ethanol, and the surface irregularities of the nonwoven fabric in a state where either or both of the longitudinal and horizontal directions of the nonwoven fabric does not contain the impregnation liquid. Is also provided for a wiping sheet having a thickness of 0.5 to 3.5 mm (hereinafter, sometimes referred to as “wiping sheet of embodiment A of the present invention”). Such a wiping sheet of embodiment A of the present invention is also included in the invention described in this specification.

  In the wiping sheet of embodiment A of the present invention, the mass ratio of the impregnating liquid to 100 parts by weight of the nonwoven fabric is preferably 250 to 500 parts by weight.

  The wiping sheet of embodiment A of the present invention is preferably a wet wiping sheet for people, and more preferably a wiping sheet for wiping a human body.

  The wiping sheet of the present invention is a spunlace nonwoven fabric using cellulose fibers, can be applied to an impregnating liquid containing a relatively high concentration of lower alcohol, satisfies the precondition that it has high liquid retention, and It is possible to provide a wiping sheet with improved feeling and firmness.

The wiping sheet of the present invention includes a nonwoven fabric containing two types of cellulose fibers and an impregnation liquid impregnated in the nonwoven fabric, and the number of irregularities of 40 μm or more measured by a surface test when wet under pressure by the KFX method is 10 to 10 μm. It is within the range of 30 pieces, The fabric weight of the said nonwoven fabric is 30-100 g / m < ² >, It is characterized by the above-mentioned. According to the wiping sheet of the present invention having such properties, it is a spunlace nonwoven fabric using cellulose fibers, but it can be applied to an impregnation liquid containing a relatively low concentration of lower alcohol and has high liquid retention. It is possible to provide a wiping sheet that satisfies the conditions and is improved in the feeling of tingling and firmness.

  In the wiping sheet of the present invention, when the number of irregularities of 40 μm or more measured by the surface test when wet under pressure by the KFX method is less than 10, irritation to the skin is reduced. Moreover, when the number of unevenness | corrugations of 40 micrometers or more measured by the surface test at the time of the wetness under pressure by the KFX method mentioned above exceeds 30, there are too many irritation | stimulations with respect to skin and it becomes a pain. In order to obtain an appropriate wiping comfort, the number of irregularities of 40 μm or more measured by a wet surface test under pressure by the KFX method is preferably in the range of 15 to 25. In addition, the nonwoven fabric in which the number of irregularities of 40 μm or more measured by a wet surface test under pressure by the KFX method is in the range of 10 to 30 is a fiber configuration as described in detail in the Examples, In addition, during the production, it is preferably produced by performing the confounding process by jetting high-pressure water flow under the condition that the surface unevenness interval (pattern interval) in one or both of the vertical and horizontal directions is within the range described later. be able to.

Nonwoven fabric constituting the wiping sheet of the present invention is in the range that weight per unit area of 30 to 100 g / ^{m 2,} preferably in the range of 40 and 80 g / ^{m 2.} When the basis weight of the nonwoven fabric is less than 30 g / m ² , the shape stability is lowered, and the wiping sheet tends to be rounded during actual use, and the basis weight of the nonwoven fabric is 100 g / m. If it exceeds ² , the amount of fibers and the amount of impregnating liquid used per wipe sheet will increase, which tends to be disadvantageous in terms of cost. The basis weight of the non-woven fabric constituting the wiping sheet of the present invention is JIS L1906. After leaving the sample in a standard state at a temperature of 20 ° C. and a humidity of 65% for 24 hours, a sample of 1 m in the width direction and 1 m in the length direction is taken. The weight (g) is measured using a balance, and the value is calculated by rounding off the decimal point of the weight (g).

  The wipe sheet of the present invention has a surface irregularity interval (pitch) (pattern interval) of 0.5 to 3.5 mm in one or both of longitudinal and lateral directions in a nonwoven fabric that does not contain an impregnation liquid (dry). It is preferable to be within. Here, in the wiping sheet of the present invention, “longitudinal direction” refers to the advancing direction of the web during production of the nonwoven fabric, and “lateral direction” refers to a direction perpendicular to the longitudinal direction on the same plane. When the unevenness on the surface of the nonwoven fabric not containing the impregnating liquid is less than 0.5 mm, the continuity of the unevenness tends to be too high and irritation to the skin tends to be difficult to obtain. When the thickness exceeds 0.5 mm, the continuous interval between the irregularities is large, and it is difficult to obtain an appropriate continuous stimulus to the skin. From the viewpoint of obtaining a more appropriate irritation to the skin, the interval between the irregularities on the surface of the nonwoven fabric not containing the impregnating liquid is preferably in the range of 1.5 to 2.8 mm.

  In the wiping sheet of the present invention, it is preferable that the release rate measured by the retentate discharge test by the KFX method (when the retentate is water) is in the range of 20 to 50%. When the release rate measured by the retentate discharge test by the KFX method is in the range of 20 to 50%, there is an advantage that an appropriate liquid feeling can be obtained at the time of wiping. When the numerical value measured by the retentate discharging test by the KFX method is less than 20%, a refreshing feeling due to wiping tends to be difficult to obtain, and the numerical value measured by the retentate discharging test by the KFX method is 50. If it exceeds 50%, the liquid tends to drip and become difficult to handle. From the viewpoint of draining the impregnating liquid moderately to give the skin a refreshing feeling and not dripping, the wiping sheet of the present invention has a release rate measured by a retained liquid discharge test by the KFX method in the range of 25 to 45%. More preferably, it is within.

  Preferred examples of the cellulose fiber used in the present invention include natural cellulose fiber, regenerated cellulose fiber, and purified cellulose fiber. Specific examples include natural cellulose fibers such as cotton, hemp, wool, and pulp, regenerated cellulose fibers such as rayon and cupra, and purified cellulose fibers such as lyocell. Especially, from a viewpoint of liquid absorbency and the form stability of a nonwoven fabric, it is preferable that one is a rayon and the other is a lyocell among two types of cellulose fibers which comprise a nonwoven fabric. By using these cellulose fibers in combination, when combining any of these cellulose fibers and cellulose fibers other than these, as well as when combining cellulose fibers other than these, There are advantages such as ease, ease of handling, and ease of blending.

  The fineness of the two types of cellulose fibers used in the present invention is not particularly limited, but the fineness of one of the cellulose fibers (for example, rayon) is preferably within a range of 2.0 to 5.0 dtex. Yes, more preferably within the range of 3.0 to 4.0 dtex. When the fineness of one of the cellulose fibers (for example, rayon) is less than 2.0 dtex, the unevenness that gives a suitable harsh feeling tends to be reduced, and the fineness of one of the cellulose fibers (for example, rayon) is 5 If it exceeds 0.0 dtex, the unevenness of the wiping sheet increases, and the skin irritation is too strong. The fineness of the remaining cellulose fiber (for example, lyocell) of the two types of cellulose fibers is preferably in the range of 0.9 to 3.3 dtex, more preferably in the range of 1.2 to 2.5 dtex. Is within. When the fineness of the other cellulose fiber (for example, lyocell) is less than 0.9 dtex, there is a tendency that the feeling of wrinkle tends to decrease, and when the fineness of the other cellulose fiber (for example, lyocell) exceeds 3.3 dtex. This is because the skin irritation tends to be too strong.

  It is preferable that the nonwoven fabric which comprises the wiping sheet | seat of this invention further contains the heat sealing | fusion fiber other than the two types of cellulose fiber mentioned above. By further including the heat-fusible fiber, there is an advantage that the form stability of the wiping sheet can be improved. Examples of the heat-sealing fibers used in the present invention include single fibers, and composite fibers such as core-sheath fibers (core-shell type) and parallel fibers (side-by-side type). In particular, since the core-sheath conjugate fiber is difficult to form a film on the nonwoven fabric surface, it can improve physical strength while preventing the cellulose fiber on the nonwoven fabric surface from being exposed, and prevent the fibers from falling off during wiping. It is possible and preferable.

  Examples of heat-bonding fibers include a combination of polypropylene (core) and polyethylene (sheath), a combination of polypropylene (core) and ethylene vinyl alcohol (sheath), and a combination of high-melting polyester (core) and low-melting polyester (sheath). Is mentioned.

  The heat-sealing fiber suitably used for the nonwoven fabric constituting the wiping sheet of the present invention is not particularly limited with respect to the fineness, but is preferably in the range of 1.2 to 2.2 dtex, 1.5 to 2 More preferably within the range of 0.0 dtex. This is because when the fineness of the heat-bonding fiber is less than 1.2 dtex, the physical properties of the wiping sheet are not greatly affected, but the card-passing property at the time of web formation tends to be reduced. This is because when the fineness of the attached fiber exceeds 2.2 dtex, the shape stability tends to be lowered due to the decrease in the bonding intersection.

  In the nonwoven fabric constituting the wiping sheet of the present invention, the total content of the heat-fusible fiber with respect to the nonwoven fabric is not particularly limited, but is preferably in the range of 5 to 30% by mass, and in the range of 15 to 25% by mass. More preferably. When the total content of the heat-fusible fiber with respect to the nonwoven fabric is less than 5% by mass, the morphological stability of the wiping sheet tends to decrease. When the total content exceeds 30% by mass, the liquid retaining property decreases. Tend to.

  More preferably, the nonwoven fabric constituting the wiping sheet of the present invention is 10 to 80% by weight of rayon, 10 to 80% by weight of lyocell and 5 to 30% by weight of heat fusion so that the total amount becomes 100% by weight. Includes attached fibers. By including two types of cellulose fibers and heat-sealing fibers in the respective contents within these ranges, it is possible to simultaneously satisfy liquid retention and form stability, which are performances required for the obtained wiping sheet. There is an advantage.

  As long as the nonwoven fabric which comprises the wipe sheet of this invention is a range which does not inhibit the effect of this invention, of course, it may contain fibers other than the two types of cellulose fibers and heat-fusion fiber mentioned above. Examples of such fibers include polyester fibers such as polyethylene terephthalate, polybutylene terephthalate, and copolymers thereof, polyolefin fibers such as polyethylene, polypropylene, and polystyrene, acrylic fibers such as polyacrylonitrile and modacrylic, nylon 6, and nylon. 66, polyamide fiber such as nylon 12, polyvinyl alcohol fiber, polyvinylidene chloride fiber, polyvinyl chloride fiber, synthetic fiber such as urethane fiber, semi-synthetic fiber such as triacetate fiber, diacetate fiber, and the like. The polymers constituting these fibers can be used in the form of homopolymers, modified polymers, blends, copolymers, and the like.

The nonwoven fabric constituting the wiping sheet of the present invention is not particularly limited for its apparent density is preferably in a range of ^{0.05~0.15g / cm 3, 0.07~0.13g / cm} 3 It is more preferable to be within the range. When the apparent density of the nonwoven fabric is less than 0.05 g / cm ³ , the shape stability tends to decrease. When the apparent density of the nonwoven fabric exceeds 0.15 g / cm ³ , liquid retention Tend to decrease. The apparent density of the nonwoven fabric constituting the wiping sheet of the present invention can be calculated from the basis weight (g / m ² ) and thickness (mm) (apparent density of nonwoven fabric (g / cm ³ ) = weight per unit area ( g / m ² ) / thickness (mm) / 1000). The thickness of the non-woven fabric was cut in the MD direction perpendicular to the surface using a razor (“Feather Razor S Single Blade” manufactured by Feather Safety Razor Co., Ltd.), and digital microscope (Keyence Co., Ltd., Digital Micro) It can be measured by observing the cross section of the sample with a scope (DIGITAL MICROSCOPE) VHX-900).

  If the wipe sheet of this invention is a range which does not inhibit the effect of this invention, there will be no restriction | limiting in particular in the layer structure. That is, it may be a non-woven fabric having a single layer structure or a multilayer structure such as two layers or three layers. In the case of a multilayer structure, the fiber composition of each layer may be the same or may be changed.

  As the nonwoven fabric, various nonwoven fabrics such as dry spunlace nonwoven fabric, wet spunlace nonwoven fabric, airlaid nonwoven fabric, air-through nonwoven fabric, meltblown nonwoven fabric, and spunbond nonwoven fabric can be suitably used. Among these nonwoven fabrics, a dry spunlace nonwoven fabric or a wet spunlace nonwoven fabric is preferable from the viewpoints of impregnation performance, retention performance, and texture of a liquid having biocompatibility.

  In the wiping sheet of the present invention, the impregnating liquid contains water and ethanol as essential components. The impregnation liquid preferably further contains a sterilizing component and a cooling component. The impregnating liquid may contain other additive components.

  As water contained in the impregnation liquid, purified water is preferable. The content of water in the impregnating liquid is not particularly limited, but is preferably 30 to 70% by mass, more preferably 35 to 65% by mass, and further preferably 40 to 60% by mass with respect to 100% by mass of the impregnating liquid. It is.

  The content of ethanol in the impregnating liquid is preferably 30 to 70% by mass, more preferably 35 to 65% by mass, and further preferably 40 to 60% by mass with respect to 100% by mass of the impregnating liquid. When the content is 30% by mass or more, quick drying properties and refreshing feeling are improved, and dissolution stability of cooling components and bactericidal components is also improved. On the other hand, when the content exceeds 70% by mass, discomfort due to the strong pungent odor of ethanol occurs, and the impregnating liquid expands due to heat, which may affect the sealing performance of the container.

  The sterilizing component is not particularly limited. Can be mentioned. The content of the sterilizing component in the impregnating liquid is not particularly limited, but is preferably 0.05 to 1.0% by mass, more preferably 0.1 to 0.5% by mass with respect to 100% by mass of the impregnating liquid. It is.

  Although it does not specifically limit as said refreshing component, For example, 1-menthol, 1-menthyl glyceryl ether, eucalyptol, camphor, menthyl lactate, menthyl salicylate, borneol etc. are mentioned. The content of the cooling component in the impregnating liquid is not particularly limited, but is preferably 0.05 to 5.0% by mass, more preferably 0.1 to 3.0% by mass with respect to 100% by mass of the impregnating liquid. It is.

  Although it does not specifically limit as said other additional component, For example, moisturizing components, such as a polyhydric alcohol, polyphenols, and a plant extract; Antiperspirant component; Deodorant component; Surfactant; Anti-inflammatory agent; Powder; Agents; sequestering agents; fragrances; antioxidants; vitamins; animal and plant extracts; pH adjusters; lower alcohols having 3 to 5 carbon atoms.

  The polyhydric alcohol is not particularly limited. For example, ethylene glycol, propylene glycol, isoprene glycol, dipropylene glycol, polyethylene glycol, diethylene glycol, dipropylene glycol, triethylene glycol, 1,3-butylene glycol (1,3 -Butanediol), 1,2-butanediol, 1,2-pentanediol, 1,2-hexanediol, 1,2-octanediol, 1,2-decanediol, glycerin (1,2,3-propanetriol) ), Diglycerin, polyglycerin, sorbitol, maltitol, polyoxyethylene methyl glucoside, polyoxypropylene methyl glucoside and the like. Among these, 1,3-butylene glycol, glycerin, and polyethylene glycol are preferable. The polyhydric alcohol improves the moisturizing effect. Although the number average molecular weight of the said polyethylene glycol is not specifically limited, From a viewpoint of a moisturizing effect and stickiness suppression, 200-30000 are preferable, More preferably, it is 4000-30000.

  The antiperspirant component is not particularly limited, and examples thereof include aluminum chloride, aluminum potassium sulfate, aluminum sulfate, aluminum acetate, chlorohydroxyaluminum, allantochlorohydroxyaluminum, and zinc paraphenolsulfonate. The content of the antiperspirant component in the impregnating liquid is not particularly limited, but is preferably 0.1 to 10% by mass, more preferably 0.2 to 5.0% by mass with respect to 100% by mass of the impregnating liquid. is there.

  The deodorant component is not particularly limited, and examples thereof include metal oxides such as zinc oxide, silica, alkyldiethanolamide, hydroxyapatite, tea extract, and koji extract.

  Although it does not specifically limit as said surfactant, Cationic surfactant, anionic surfactant, nonionic surfactant, amphoteric surfactant, etc. are mentioned. Among these, nonionic surfactants are preferable. The nonionic surfactant is not particularly limited, but sorbitan fatty acid ester, glycerin fatty acid ester, castor oil, hydrogenated castor oil, and alkylene oxide adducts thereof; polyoxyalkylene alkyl ether, polyoxyalkylene fatty acid ester, polyoxy Examples include alkylene alkyl phenyl ether. Among these, alkylene oxide adducts of hydrogenated castor oil and polyoxyalkylene alkyl ethers are preferable. Examples of the alkylene oxide adduct of the hardened castor oil include polyoxyethylene hardened castor oil. Examples of the polyoxyalkylene alkyl ether include polyoxyethylene cetyl ether, polyoxyethylene polyoxypropylene decyl tetradecyl ether, and the like.

  The method for producing the impregnating liquid is not particularly limited, and a known production method can be used. For example, the method of mixing each component, stirring with a paddle mixer, and homogenizing each component is mentioned.

  The wipe sheet of the present invention is a non-woven fabric with conventional additives such as stabilizers (heat stabilizers such as copper compounds, ultraviolet absorbers, light stabilizers, antioxidants, etc.) within a range that does not impair the effects of the present invention. ), Fine particles, colorants, fluorescent brighteners, antistatic agents, flame retardants, deodorants, plasticizers, lubricants, crystallization rate retarders, and the like. These additives can be used alone or in combination of two or more. These additives may be contained in the fiber which comprises a nonwoven fabric, and may be carry | supported on the surface of the nonwoven fabric.

  The wiping sheet of the present invention is suitable for use as a wet wiping sheet for people, and among them, a wiping sheet for wiping a human body is particularly suitable.

Below, the wiping sheet | seat of embodiment A of this invention which is an example of the specific embodiment of this invention is shown. The wiping sheet of embodiment A of the present invention is a wiping sheet comprising a nonwoven fabric and an impregnating liquid impregnated in the nonwoven fabric, and the nonwoven fabric is 10 to 80 wt% so that the total amount is 100 wt%. % Rayon, 10 to 80% by weight of lyocell and 5 to 30% by weight of heat-sealing fibers, the nonwoven fabric is a spunlace nonwoven fabric, and the basis weight of the nonwoven fabric is 30 to 100 g / m ^2. The fineness of the rayon is 2.0 to 5.0 dtex, the fineness of the lyocell is 0.9 to 3.3 dtex, the fineness of the heat fusion fiber is 1.2 to 2.2 dtex, and the impregnation liquid is water, And 30 to 70% by weight of ethanol, and the non-woven fabric in the state of not containing the impregnation liquid has a surface irregularity interval of 0.5 to 3.5 mm in either or both of the longitudinal and lateral directions. It is a wiping sheet. The wiping sheet having the configuration can exhibit the effects of the present invention as described above. Such a wiping sheet of embodiment A of the present invention is included in the invention described herein, independently of the above-described wiping sheet invention of the present invention.

  In the wiping sheet of embodiment A of the present invention, the heat-sealing fiber includes the above-mentioned heat-sealing fiber as the heat-sealing fiber used in the present invention. About the preferable content of a rayon, a lyocell, a heat-fusion fiber, the fineness, etc. in the wiping sheet of embodiment A of the present invention, it is the same as that of the wiping sheet of the present invention described above.

That is, the nonwoven fabric constituting the wiping sheet of embodiment A of the present invention is 10 to 80% by weight of rayon, 10 to 80% by weight of lyocell and 5 to 30% by weight of heat so that the total amount becomes 100% by weight. Includes fused fibers. The content of the rayon is preferably 15 to 60% by weight, more preferably 20 to 40% by weight. The content of the lyocell is preferably 20 to 70% by weight, more preferably 40 to 60% by weight. The content of the heat fusion fiber is preferably 10 to 25% by weight. Moreover, the basis weight of the nonwoven fabric constituting the wiping sheet of the embodiment A of the present invention is 30 to 100 g / ^{m 2,} preferably 40 and 80 g / ^{m 2.}

  Moreover, the nonwoven fabric which comprises the wiping sheet | seat of embodiment A of this invention WHEREIN: The fineness of a rayon is 2.0-5.0 dtex, Preferably it is 3.0-4.0 dtex. The fineness of the lyocell is 0.9 to 3.3 dtex, preferably 1.2 to 2.5 dtex. The fineness of the heat-sealing fiber is 1.2 to 2.2 dtex, and preferably 1.5 to 2.0 dtex.

  In the wiping sheet of embodiment A of the present invention, the impregnating liquid is an impregnating liquid containing water and 30 to 70% by weight of ethanol among the above-described impregnating liquids used in the present invention. is there.

  The content of ethanol in the impregnating liquid is preferably 30 to 70% by mass, more preferably 35 to 65% by mass, and further preferably 40 to 60% by mass with respect to 100% by weight of the impregnating liquid. Moreover, 30-70 mass% is preferable with respect to 100 weight% of impregnating liquids, and, as for content of the water in the said impregnating liquid, More preferably, it is 35-65 mass%, More preferably, it is 40-60 mass%.

  In the wiping sheet of embodiment A of the present invention, the mass ratio of the impregnating liquid to 100 parts by weight of the nonwoven fabric is preferably 250 to 500 parts by weight, more preferably 270 to 450 parts by weight. When the mass ratio is 250 parts by weight or more, wiping performance and usability are improved. On the other hand, if the mass ratio exceeds 500 parts by weight, the skin feels too wet during wiping, and the feeling of use and quick drying may be reduced.

  In the wiping sheet of embodiment A of the present invention, the spacing between the surface irregularities on either or both of the nonwoven fabric in a state where the impregnating liquid is not contained is 0.5 to 3.5 mm, preferably 1.5 to 2.8 mm.

  Hereinafter, the present invention will be described in detail with reference to examples, but the present invention is not limited to the examples. In addition, the physical property of the nonwoven fabric in this invention means what was measured with the following method.

[Weight per unit]
In accordance with JIS L1906, the sample is allowed to stand for 24 hours in a standard state at a temperature of 20 ° C. and a humidity of 65%, then a sample of 1 m in the width direction and 1 m in the length direction is taken, and the weight (g) is measured using a balance. The weight (g) obtained was rounded off to the basis weight.

[Thickness]
Using a razor (“Feather Razor S Single Blade” manufactured by Feather Safety Razor Co., Ltd.), the sample was cut in the MD direction perpendicular to the surface, and a digital microscope [DIGITAL MICROSCOPE manufactured by Keyence Co., Ltd.] was used. ) VHX-900] was used to observe the cross section of the sample and measure the thickness.

[Apparent density]
Calculated from the basis weight (g / m ² ) and the thickness (mm) (apparent density (g / cm ³ ) of nonwoven fabric = weight per unit area (g / m ² ) / thickness (mm) / 1000).

[Surface irregularities (pattern spacing)]
The surface of the sample was observed with a digital microscope (DIGITAL MICROSCOPE VHX-900) manufactured by Keyence Corporation, and the unevenness of the surface in the vertical and horizontal directions (pitch). Was measured.

[Strength at break, elongation at break]
About the obtained nonwoven fabric, it is 45 from the vertical direction according to 6.3.2 of JIS L 1913 "General nonwoven fabric testing method" using a constant-speed extension type tensile tester ("AG-IS" manufactured by Shimadzu Corporation). The tensile strength (N / 5 cm) and elongation (%) at break of a test piece cut by tilting and wetted with a 50% by mass aqueous solution of ethanol were measured. The temperature of the water in which the test piece is immersed was 20 ° C.

[Number of surface irregularities]
About the obtained nonwoven fabric, the sheet | seat which impregnated 300 mass% of ethanol 50 mass% aqueous solution with respect to the dead weight on the raw fabric cut | judged to 25 cm (MD) x 20 cm (CD) is automated surface test machine (KES-FB4-AUTO- A, manufactured by Kato Tech Co., Ltd., and the roughness was measured by sample tension (400 g), load (10 g), surface measurement sample moving speed (1 mm / sec) (surface test when wet under pressure (KFX method)) ). From there, the number of irregularities of 40 μm or more contained in 100 mm (number of irregularities on the surface) was counted.

[Water retention]
It measured according to JIS L1907 7.2 water absorption. A test piece is cut into a 5 cm square and the weight is measured (Ag). The test piece was immersed in water for 30 seconds. After immersion, one side of the test piece was picked up from the liquid and the weight (Bg) after 1 minute was measured. The liquid retention rate (C%) is expressed by the following formula C (%) = [(BA) / A] × 100
It is calculated by.

[Releasability (water)]
The sheet retained by the above method was squeezed with a linear pressure of 0.1 kgf / cm, the sheet weight (Dg) was measured, and the release amount [(BD) g] was obtained. Release rate (E%) is expressed by the following formula: E (%) = [(BD) / (BA)] × 100
Is calculated by

[Form stability (cantilever)]
According to JIS L 1913 6.7.3, the length projected by the cantilever method was measured. However, a sheet cut in a direction of 45 degrees with respect to the progress of the web and impregnated with a 50% by weight aqueous ethanol solution by 300% was used.

[Feeling of rustling]
(1) Preparation of sample The obtained nonwoven fabric was cut into a rectangle of 10 cm in length (longitudinal direction of nonwoven fabric) × 20 cm in width (width direction of nonwoven fabric) and placed in a bag made of (polyethylene terephthalate / aluminum / polypropylene laminated sheet). . Next, the following impregnating solution was put in the bag so as to be impregnated into the non-woven fabric so that the impregnating solution was 300 parts by weight with respect to 100 parts by weight of the non-woven fabric. The bag was sealed and allowed to stand in an atmosphere at 25 ° C. for 3 days to prepare a sample of a wiping sheet (nonwoven fabric impregnated with an impregnating liquid).

<Impregnating liquid>
95% ethanol 50.0% by weight
Isopropyl methylphenol 0.2% by weight
l-Menthol 0.3% by weight
49.5% by weight of purified water
Total 100.0% by weight
(2) Evaluation The evaluation was performed by three professional evaluation panels. With the sample of the wiping sheet obtained above, the back of the hand was wiped 3 times, and the touch at that time was evaluated according to the following criteria.

<Criteria>
5: I felt a strong friction feeling.
4: I clearly felt the friction feeling,
3: Only a slight friction was felt,
2: I only felt a soft friction,
1: The feeling of friction was weak and it was a feeling of sliding.

[Example 1]
As the two types of cellulose fibers, a viscose rayon with a fineness of 3.3 dtex (Hope, manufactured by Ohmi Kenshi) (hereinafter referred to as “cellulose fiber-1”) and a lyocell with a fineness of 1.7 dtex (Tencel ^{(registered trademark)} , lentiling ⁾ Dal) (hereinafter referred to as “cellulose fiber-2”), and this is a heat-bonded fiber having a fineness of 1.7 dtex (core-sheath composite fiber having a core of polypropylene and a sheath of polyethylene, HR-NTW, Ube Excimo Co., Ltd.) was mixed uniformly with a weight ratio of 30:50:20, and a semi-random web was produced by CAD. Next, the card web was placed on a punching drum support having an aperture ratio of 25% and a hole diameter of 0.3 mm and continuously transferred in the longitudinal direction at a speed of 50 m / min. The entanglement process was performed and the entangled fiber web (nonwoven fabric) was manufactured. In this entanglement process, two nozzles in which orifices having a hole diameter of 0.10 mm are provided at intervals of 0.6 mm along the width direction of the web are used (distance 20 cm between adjacent nozzles). The water pressure of the high-pressure water flow injected from the nozzle was 6.5 MPa, and the water pressure of the high-pressure water flow injected from the nozzles in the second row was 7.0 MPa (Table WJ).

  The other surface is placed on a punching drum support having an aperture ratio of 25% and a hole diameter of 0.3 mm, and is continuously transferred in the longitudinal direction at a speed of 50 m / min. The entanglement process was performed and the entangled fiber web (nonwoven fabric) was manufactured. In this entanglement process, one nozzle having orifices with a hole diameter of 0.10 mm provided at intervals of 0.6 mm along the width direction of the web is used, and the water pressure of the high-pressure water flow injected from the nozzles in the first row is changed. The test was performed at 7.0 MPa (back WJ-1). From the same surface as before, the fiber diameter is 0.90 mm, mesh 10 (lines / inch), placed on a flat net support on the whole of the plain weave, and continuously transferred and entangled by jetting high-pressure water flow The unevenness of the net was transferred to the surface of the nonwoven fabric. This entanglement treatment uses three nozzles provided with orifices having a hole diameter of 0.10 mm at intervals of 0.6 mm along the width direction of the web, all under the condition of a high water pressure of 6.0 MPa. (Back WJ-2). Furthermore, it dried at 135 degreeC.

The obtained non-woven fabric was a single layer, having a basis weight of 44.8 g / m ² , a thickness of 0.37 mm, and an apparent density of 0.12 g / cm ³ . Table 1 shows various evaluation results for the obtained nonwoven fabric.

[Example 2]
The same procedure as in Example 1 was performed except that the WJ treatment conditions were changed as follows and the speed was 5.0 m / min.

(WJ treatment)
Table WJ
... 3.0 MPa-4.0 MPa
Back WJ-1
... 5.0 MPa
Back WJ-2
... 3.0 MPa-4.0 MPa-5.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 45.3 g / m ² , a thickness of 0.45 mm, and an apparent density of 0.10 g / cm ³ . Table 1 shows various evaluation results for the obtained nonwoven fabric.

[Example 3]
Cellulose fiber-1, cellulose fiber-2 and heat-sealing fiber are mixed at a weight ratio of 80: 15: 5, and a fiber diameter of 1.20 mm, 12 meshes / inch, and a plain weave are used as a net. The same procedure as in Example 1 was performed except that the WJ treatment was performed under the following conditions and the speed was set to 5.0 m / min.

(WJ treatment)
Table WJ
... 3.0 MPa-5.0 MPa
Back WJ-1
... 7.0 MPa
Back WJ-2
... 3.0 MPa-5.0 MPa-7.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 91.0 g / m ² , a thickness of 0.70 mm, and an apparent density of 0.13 g / cm ³ . Table 1 shows various evaluation results for the obtained nonwoven fabric.

[Example 4]
Cellulose fiber-1, cellulose fiber-2, and heat-sealing fiber are mixed so that the weight ratio is 60:20:20, and as a net (H25) fiber diameter 0.65 mm, mesh 25 / inch, plain weave Was performed in the same manner as in Example 1 except that the WJ treatment was performed under the following conditions, and the speed was 5.0 m / min.

(WJ treatment)
Table WJ
... 2.0 MPa
Back WJ-1
... 3.0 MPa
Back WJ-2
... 2.0 MPa-3.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 32.0 g / m ² , a thickness of 0.31 mm, and an apparent density of 0.10 g / cm ³ . Table 1 shows various evaluation results for the obtained nonwoven fabric.

[Example 5]
Cellulose fiber-1, cellulose fiber-2, and heat-sealing fiber were mixed at a weight ratio of 20:70:10, WJ treatment was performed under the following conditions, and the speed was 5.0 m / min. Except that, the same procedure as in Example 1 was performed.

(WJ treatment)
Table WJ
... 3.0 MPa-4.0 MPa
Back WJ-1
... 5.0 MPa
Back WJ-2
... 3.0 MPa-4.0 MPa-5.0 MPa
The obtained nonwoven fabric was a single layer, having a basis weight of 45.2 g / m ² , a thickness of 0.48 mm, and an apparent density of 0.09 g / cm ³ . Table 1 shows various evaluation results for the obtained nonwoven fabric.

[Comparative Example 1]
Example 1 except that only cellulose fiber-1 was used, a fiber diameter of 1.00 mm, a mesh of 6 pieces / inch, and a plain weave were used, WJ treatment was performed under the following conditions, and the speed was 5.0 m / min. It carried out like.

(WJ processing)
Table WJ
... 3.0 MPa-5.0 MPa
Back WJ-1
... 7.0 MPa
Back WJ-2
... 3.0 MPa-5.0 MPa-7.0 MPa
The obtained non-woven fabric was a single layer and had a basis weight of 24.3 g / m ² , a thickness of 0.24 mm, and an apparent density of 0.10 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

[Comparative Example 2]
Cellulose fiber-2 and heat-sealing fiber are mixed so that the weight ratio is 60:40, the fiber diameter is 0.20 mm, 76 fibers / inch, and plain weave is used, and WJ treatment is performed under the following conditions. The same operation as in Example 1 was performed except that the speed was 5.0 m / min.

(WJ treatment)
Table WJ
... 3.0 MPa-5.0 MPa
Back WJ-1
... 7.0 MPa
Back WJ-2
... 3.0 MPa-5.0 MPa-7.0 MPa
The obtained non-woven fabric was a single layer and had a basis weight of 118.4 g / m ² , a thickness of 0.85 mm, and an apparent density of 0.14 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

[Comparative Example 3]
Using only PET fibers (T471, manufactured by Toray Industries, Inc.) having a fineness of 1.6 dtex, WJ treatment was performed under the following conditions, and the same procedure as in Example 1 was performed except that the speed was 5.0 m / min.

(WJ treatment)
Table WJ
... 3.0 MPa-4.0 MPa
Back WJ-1
... 5.0 MPa
Back WJ-2
... 3.0 MPa-4.0 MPa-5.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 44.3 g / m ² , a thickness of 0.56 mm, and an apparent density of 0.08 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

[Comparative Example 4]
The same procedure as in Example 1 was performed except that the fiber diameter was 0.20 mm, the mesh was 76 pieces / inch, and a plain weave was used, the WJ treatment conditions were changed as follows, and the speed was 5.0 m / min. .

(WJ processing)
Table WJ
... 3.0 MPa-4.0 MPa
Back WJ-1
... 5.0 MPa
Back WJ-2
... 3.0 MPa-4.0 MPa-5.0 MPa
The obtained non-woven fabric was a single layer and had a basis weight of 51.3 g / m ² , a thickness of 0.49 mm, and an apparent density of 0.10 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

[Comparative Example 5]
The same procedure as in Example 1 was performed, except that a fiber diameter of 0.90 mm, 10 fibers / inch, and a plain weave were used as the net, the WJ treatment conditions were changed as follows, and the speed was 5.0 m / min.

(WJ treatment)
Table WJ
... 2.0 MPa
Back WJ-1
... 3.0 MPa
Back WJ-2
... 2.0 MPa-3.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 26.1 g / m ² , a thickness of 0.25 mm, and an apparent density of 0.10 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

[Comparative Example 6]
It was set as Comparative Example 6 using PET spunbond (ELTAS, manufactured by Asahi Kasei Corporation). Various evaluation results are shown in Table 2.

[Comparative Example 7]
Cotton spunlace (Cot Ace, manufactured by Unitika Ltd.) produced by the spunlace method was used as Comparative Example 7. Various evaluation results are shown in Table 2.

[Comparative Example 8]
Benlyse (manufactured by Asahi Kasei Co., Ltd.) was designated as Comparative Example 8. Various evaluation results are shown in Table 2.

[Comparative Example 9]
As the cellulose fiber-1, a viscose rayon having a fineness of 1.7 dtex (Hope, manufactured by Ohmi Kenshi) was used instead of a viscose rayon having a fineness of 3.3 dtex, and the cellulose fiber-1, the cellulose fiber-2 and the heat-sealing fiber were used. Are mixed so that the weight ratio is 60:20:20, the fiber diameter is 0.65 mm, 25 fibers / inch, and a plain weave is used, WJ treatment is performed under the following conditions, and the speed is 5.0 m / The procedure was the same as in Example 1 except that the minute was used.

(WJ processing)
Table WJ
... 2.0 MPa
Back WJ-1
... 3.0 MPa
Back WJ-2
... 2.0 MPa-3.0 MPa
The obtained non-woven fabric was a single layer, having a basis weight of 35.8 g / m ² , a thickness of 0.32 mm, and an apparent density of 0.11 g / cm ³ . Various evaluation results for the obtained nonwoven fabric are shown in Table 2.

Claims (11)

One of which is rayon and the other is lyocell, which contains a nonwoven fabric containing two types of cellulose fibers and a heat-sealable fiber, and an impregnating solution impregnated in the nonwoven fabric and containing water and ethanol. a pressure wet surface unevenness number of more than 40μm as measured by the test is the 10 to 30 range, the basis weight of the nonwoven fabric is 30 to 100 g / ^m are ^two der, the fineness of the rayon from 3.0 to 4 .0dtex Ru der, wiping sheet.   The wiping sheet according to claim 1, wherein the unevenness of the surface on either one or both of the longitudinal and lateral directions of the nonwoven fabric not containing the impregnating liquid is 0.5 to 3.5 mm.   The wiping sheet according to claim 1 or 2, wherein a release rate measured by a retentate discharge test by the KFX method is within a range of 20 to 50%.   The wipe according to claim 1, wherein the nonwoven fabric contains 10 to 80% by weight of rayon, 10 to 80% by weight of lyocell, and 5 to 30% by weight of heat-sealing fibers so that the total amount becomes 100% by weight. Sheet. The wipe sheet of any one of Claims 1-4 whose apparent density of the said nonwoven fabric is 0.05-0.15 g / cm < ³ >.   The wiping sheet according to any one of claims 1 to 5, which is a wet wiping sheet for personal use.   The wiping sheet according to claim 6, which is a wiping sheet for wiping a human body. A wiping sheet comprising a nonwoven fabric and an impregnating liquid impregnated in the nonwoven fabric,
The non-woven fabric includes 10 to 80% by weight of rayon, 10 to 80% by weight of lyocell and 5 to 30% by weight of heat-sealing fibers so that the total amount becomes 100% by weight;
The nonwoven fabric is a spunlace nonwoven fabric;
The basis weight of the nonwoven fabric is 30 to 100 g / m ² ,
The fineness of the rayon is 3.0 to 4.0 dtex , the fineness of the lyocell is 0.9 to 3.3 dtex, and the fineness of the heat-sealing fiber is 1.2 to 2.2 dtex,
The impregnating liquid comprises water and 30 to 70% by weight of ethanol;
The wiping sheet | seat whose space | interval of the unevenness | corrugation by the pattern of the surface in the longitudinal or lateral direction in the nonwoven fabric of the state which does not contain the said impregnation liquid is 0.5-3.5 mm.   The wipe sheet of Claim 8 whose mass ratio of the said impregnating liquid with respect to 100 weight part of said nonwoven fabrics is 250-500 weight part.   The wiping sheet according to claim 8, which is a wet wiping sheet for personal use.   The wiping sheet according to claim 10, which is a wiping sheet for wiping a human body.