JP6593943B2 - 粒子状組成物、液体組成物、粒子状組成物の製造方法、表面改質剤、水分散性の向上方法 - Google Patents
粒子状組成物、液体組成物、粒子状組成物の製造方法、表面改質剤、水分散性の向上方法 Download PDFInfo
- Publication number
- JP6593943B2 JP6593943B2 JP2018562896A JP2018562896A JP6593943B2 JP 6593943 B2 JP6593943 B2 JP 6593943B2 JP 2018562896 A JP2018562896 A JP 2018562896A JP 2018562896 A JP2018562896 A JP 2018562896A JP 6593943 B2 JP6593943 B2 JP 6593943B2
- Authority
- JP
- Japan
- Prior art keywords
- solid particles
- water
- particulate composition
- amphiphile
- dispersed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記両親媒性物質が水中においては閉鎖小胞体の形成能を有する、粒子状組成物。
固体粒子と、水中においては閉鎖小胞体の形成能を有する両親媒性物質を溶解した溶媒との混合物を調製する工程と、
前記混合物中の溶媒を除去する工程と、を有する、方法。
本発明は、固体粒子と、該固体粒子の表面に存在する両親媒性物質と、を含み、両親媒性物質が水中においては閉鎖小胞体の形成能を有する、粒子状組成物である。本発明は、これにより、固体粒子の種類にかかわらず、水又は油性物質への高い分散性を有する。その理由は、以下のとおりと推測される。
本発明に用いられる両親媒性物質は、水中において閉鎖小胞体の形成能を有する両親媒性物質(以下、本明細書において「両親媒性物質」と略称する場合がある。)であり、例えば、水中で二分子膜を形成可能な(つまり、水中でベシクルを形成可能な)ものである。このような水中で二分子膜形成能を有する両親媒性物質としては、下記の一般式1で表されるポリオキシエチレン硬化ひまし油の誘導体もしくは一般式2で表されるようなジアルキルアンモニウム誘導体、トリアルキルアンモニウム誘導体、テトラアルキルアンモニウム誘導体、ジアルケニルアンモニウム誘導体、トリアルケニルアンモニウム誘導体、又はテトラアルケニルアンモニウム誘導体のハロゲン塩の誘導体を採用するとよい。
まず、固体粒子の全表面積(S[nm2])は、以下の式(1)で表される。
油性物質としては、両親媒性物質の溶解度が高い(具体的には、1μmol/L以上)ものでなければ特に限定されず、無極性溶媒及び極性溶媒のいずれを用いることもできる。具体的に、無極性溶媒としては、炭化水素油、例えば直鎖パラフィン、分岐鎖パラフィン、脂環式炭化水素等が挙げられる。また、極性溶媒としては、エステル油、シリコーン油、脂肪酸トリグリセリド等が挙げられる。
本発明は、上述の粒子状組成物の製造方法も包含する。本発明の粒子状組成物は、例えば、以下の方法により製造することができる。つまり、固体粒子と、水中においては閉鎖小胞体の形成能を有する両親媒性物質を溶解した溶媒との混合物を調製する工程と、混合物中の溶媒を除去する工程と、を有する、方法により粒子状組成物を製造することができる。
本発明における調製工程は、固体粒子と、水中においては閉鎖小胞体の形成能を有する両親媒性物質を溶解した溶媒との混合物を調製する工程である。
本発明における除去工程は、調製工程により調製された混合物中の溶媒を除去する工程である。
本発明は、上述の本発明の粒子状組成物と、該粒子状組成物を含む水又は油性物質と、を有する、液体組成物を包含する。
本発明は、水中においては閉鎖小胞体の形成能を有する両親媒性物質からなる、固体粒子の表面改質剤を包含する。
本発明は、固体粒子の表面を、水中においては閉鎖小胞体の形成能を有する両親媒性物質で覆うことによる、水又は油性物質に対する分散性の向上方法を包含する。これにより、固体粒子の水又は油性物質に対する分散性が向上する。
実施例1〜5の粒子状組成物を、後述する表1、2の配合で調製した。具体的には、まず、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の有機溶媒溶液を調製した。このポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質溶液と固体粒子(粒度分布幅の広い未処理の酸化セリウム(以下、「酸化セリウムA」という。)、酸化セリウムAの表面をシリカ処理したもの、酸化セリウムAの表面をステアリン酸処理したもの、酸化セリウムAの表面をシリカ処理したもの、粒度分布幅の狭い未処理の酸化セリウム(以下、「酸化セリウムB」という。)、酸化セリウムBの表面をステアリン酸処理したもの((株)アプローズ社製のAQUACERIAPowderS)、とを有機溶媒のエタノールに添加し、撹拌し、スターラーにより2〜3時間撹拌した。その後、ホットスターラーで撹拌しながら加熱し、溶媒を揮発させた。その後、乾燥機で80℃、2〜3時間乾燥させ、溶媒を完全に除去し、実施例1〜5の粒子状組成物を調製した。
後述する表1、2の量の各固体粒子を準備し、これを参考例1、比較例1〜5の粒子とした。
実施例1〜5の粒子状組成物、比較例1〜5の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、それぞれの粒子状組成物、粒子の乾燥させた状態で全体が10.0gとなるように水を添加し、20wt%の固体粒子分散液を作製し、さらに、水で希釈した後に行った。また、参考例1の粒子をエタノールに分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。それぞれの実施例の粒子状組成物、参考例、比較例の粒子の分散性について、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質により処理をしていない対応する比較例と比較して(例えば、実施例1と比較例1とを比較して)、比較例より水分散時の粒子径が小さく、粉浮きがみられなかった場合、水分散性「〇」(良好)として評価した。水分散性が悪いものは「×」(不良)として評価した。その結果を以下の表1、2に示す。
実施例6〜7の粒子状組成物を、後述する表3の配合で調製した。具体的には、酸化セリウムA(未処理)、酸化セリウムB(未処理)を、粒度分布幅の広い未処理の酸化亜鉛(以下、「酸化亜鉛A」という。))、粒度分布幅の狭い未処理の酸化亜鉛(以下、「酸化亜鉛B」という。)に変更した点以外は、実施例1と同一の手法で、実施例6〜7の粒子状組成物を調製した。また、後述する表3の量の各固体粒子を準備し、これを比較例6〜7の粒子とした。
実施例6〜7の粒子状組成物、比較例6〜7の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、上述の「水に対する分散性評価1」と同一の方法で行った。また、それぞれの実施例の粒子状組成物、比較例の粒子の水分散性について、上述の「水に対する分散性評価1」と同一の基準で評価した。その結果を以下の表3に示す。
実施例8〜11の粒子状組成物を、後述する表4の配合で調製した。具体的には、酸化セリウムA(未処理)を、酸化ケイ素(日本アエロジル社製のアエロジルOX50)に変更し、配合量を表4に示すとおりに変更した点以外は、実施例1と同一の手法で、実施例8の粒子状組成物を調製した。また、酸化セリウムA(未処理)を、酸化ケイ素(日本アエロジル社製のアエロジルOX50)に変更し、配合量を表4に示すとおりに変更し、調製に使用した有機溶媒をエタノールからアセトン、クロロホルム、又はイソプロピルアルコール(IPA)に変更した点以外は、実施例1と同一の手法で、実施例9〜11の粒子状組成物を調製した。また、後述する表4の量の各固体粒子を準備し、これを比較例8の粒子とした。
実施例8〜11の粒子状組成物、比較例8の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、上述の「水に対する分散性評価1」と同一の方法で行った。また、それぞれの実施例の粒子状組成物、比較例の粒子の水分散性について、上述の「水に対する分散性評価1」と同一の基準で評価した。その結果を以下の表4に示す。
実施例12〜18の粒子状組成物を、後述する表5の配合で調製した。具体的には、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質の配合量を表5に示すとおりに変更した点以外は、実施例5と同一の手法で、実施例12〜18の粒子状組成物を調製した。
実施例12〜18の粒子状組成物、比較例5の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、上述の「水に対する分散性評価1」と同一の方法で行った。また、それぞれの実施例の粒子状組成物、比較例の粒子の水分散性について、上述の「水に対する分散性評価1」と同一の基準で評価した。その結果を以下の表5に示す。水分散性判定の項目に関しては、「△」はやや良好を表す。
実施例19〜24の粒子状組成物を、後述する表6、7の配合で調製した。具体的には、酸化セリウムA(未処理)を、酸化鉄(メチコン処理)(SI−2タロックスLLXLO)又は酸化チタン(Al,ステアリン酸処理)(テイカ(株)社製のMT−100Z)に置き換え、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質の配合量を表6、7に示すとおりに変更した点以外は、実施例1と同一の手法で、実施例19〜24の粒子状組成物を調製した。また、後述する表6、7の量の各固体粒子を準備し、これを参考例2、3、比較例9〜10の粒子とした。
実施例19〜24の粒子状組成物、比較例9〜10、参考例2〜3の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、上述の「水に対する分散性評価1」と同一の方法で行った。また、それぞれの実施例の粒子状組成物、参考性、比較例の粒子の水分散性について、上述の「水に対する分散性評価1」と同一の基準で評価した。その結果を以下の表6、7に示す。
実施例25〜30の粒子状組成物を、後述する表8、9の配合で調製した。具体的には、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質をモノステアリン酸テトラグリセリル(TETRAGLYN 1−S)の閉鎖小胞体の形成能を有する両親媒性物質、トリステアリン酸デカグリセリル(DECAGLYN 3−S)の閉鎖小胞体の形成能を有する両親媒性物質、レシチン(SLP ホワイト)の閉鎖小胞体の形成能を有する両親媒性物質、又はショ糖ステアリン酸エステル(S−1670)の閉鎖小胞体の形成能を有する両親媒性物質に変更し、さらに実施例25〜29については調製に使用した有機溶媒をエタノールからイソプロピルアルコール(IPA)又はテトラヒドロフラン(THF)に変更し、各成分の配合量を表8、9に示すとおりに変更した点以外は、実施例1と同一の手法で、実施例25〜30の粒子状組成物を調製した。
実施例25〜30の粒子状組成物、比較例5の粒子を水に分散させ、平均粒子径を動的・電気泳動光散乱光度計(ELSZ,大塚電子株式会社製)により測定した。測定は、上述の「水に対する分散性評価1」と同一の方法で行った。また、それぞれの実施例の粒子状組成物、比較例の粒子の水分散性について、上述の「水に対する分散性評価1」と同一の基準で評価した。その結果を以下の表8、9に示す。
実施例1と同様の手順で、未処理の酸化セリウムB2gの表面をポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質0.1gで処理した実施例31の粒子状組成物を調製した。また、実施例19と同様の手順で、酸化鉄(メチコン処理)2gの表面をポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質0.1gで処理した実施例32の粒子状組成物を調製した。また、未処理の酸化セリウムB2gを比較例11として準備し、酸化鉄(メチコン処理)2gを比較例12として準備した。
実施例31、32の粒子状組成物、比較例11、12の粒子について、乾燥状態の粒子状組成物をペレット状にしてから、紫外・可視分光光度計(UV−vis)(V−570,Jasco株式会社製)によりUV−visスペクトルを測定した。その結果を図1に示す。図1中、(a)が実施例31、比較例11の粒子状組成物についてのUV−visスペクトルを示し、(b)が実施例32、比較例12の粒子状組成物についてのUV−visスペクトルを示す。
実施例1と同様の手順で、酸化ケイ素1gの表面をポリオキシエチレン硬化ひまし油の誘導体(HCO−10)の閉鎖小胞体の形成能を有する両親媒性物質1gで処理した実施例33の粒子状組成物を調製した。また、酸化ケイ素の量をポリエチレン硬化ひまし油の誘導体(HCO−10)の閉鎖小胞体の形成能を有する両親媒性物質の量の半分にした点以外は、実施例33と同様の配合・手順で実施例34の粒子状組成物を調製した。
TEM(透過型電子顕微鏡(JEM−2010,日本電子株式会社製))により、実施例33と実施例34の粒子状組成物を観察した。その結果を図2に示す。図2中、(a)が実施例33の粒子状組成物についてのTEM観察による画像を示し、(b)が実施例34の粒子状組成物についてのTEM観察による画像を示す。
実施例35の粒子状組成物を、後述する表10の配合で調製した。具体的には、まず、ポリオキシエチレン硬化ひまし油の誘導体(HCO−20)の有機溶媒溶液を調製した。このポリオキシエチレン硬化ひまし油の誘導体(HCO−20)の閉鎖小胞体の形成能を有する両親媒性物質溶液と粒度分布幅の広い未処理の炭酸カルシウムとを有機溶媒のイソプロピルアルコールに添加し、撹拌し、スターラーにより2〜3時間撹拌した。その後、ホットスターラーで撹拌しながら加熱し、溶媒を揮発させた。その後、乾燥機で80℃、2〜3時間乾燥させ、溶媒を完全に除去し、実施例35の粒子状組成物を調製した。
後述する表10の量の各固体粒子を準備し、これを比較例13の粒子とした。
ワセリン(融点65〜70℃)20gをビーカーに移し、80℃で加熱攪拌して溶融させた。この溶融ワセリンに、実施例35の粒子状組成物又は比較例13の粒子を20g添加し、10分撹拌した。得られた試料を80℃で加熱しながら光学顕微鏡で観察した。それぞれの試料について、流動性がある場合「〇」(良好)、流動性はあるがわずかに凝集が見られた場合「△」、流動性がない場合「×」(不良)として評価した。その結果を以下の表10に示す。なお、この評価方法においては、粒子状組成物又は粒子の質量比が50質量%と高含有率であるが、このような場合には粒子状組成物又は粒子が分散能を有しないと、凝集して液体の流動性を失わせてしまう。
固形パラフィン(融点68〜70℃)50gをビーカーに移し、120℃で加熱攪拌して溶融させた。この溶融パラフィンに、実施例35の粒子状組成物又は比較例13の粒子を50g添加し、60分撹拌した。得られた試料を90℃で加熱しながら光学顕微鏡で観察した。それぞれの試料について、上述の「ワセリンに対する分散性評価」と同様の基準で評価した。その結果を以下の表10に示す。
流動パラフィン(融点−20〜−25℃)50gをビーカーに移し、実施例35の粒子状組成物又は比較例13の粒子を50g添加し、60分撹拌した。得られた試料を光学顕微鏡で観察した。それぞれの試料について、上述の「ワセリンに対する分散性評価」と同様の基準で評価した。その結果を以下の表10に示す。
実施例36の粒子状組成物を、後述する表11の配合で調製した。具体的には、まず、ポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の有機溶媒溶液を調製した。このポリオキシエチレン硬化ひまし油の誘導体(HCO−40)の閉鎖小胞体の形成能を有する両親媒性物質溶液と酸化セリウムAの表面をステアリン酸処理したものとを有機溶媒のエタノールに添加し、撹拌し、スターラーにより2〜3時間撹拌した。その後、ホットスターラーで撹拌しながら加熱し、溶媒を揮発させた。その後、乾燥機で80℃、2〜3時間乾燥させ、溶媒を完全に除去し、実施例36の粒子状組成物を調製した。
後述する表11の量の各固体粒子を準備し、これを比較例14の粒子とした。
それぞれの実施例の粒子状組成物、比較例の粒子の流動パラフィンに対する分散性について、上述の「ワセリンに対する分散性評価」と同一の基準で評価した。その結果を以下の表11に示す。
ミリスチン酸イソプロピル50gをビーカーに移し、実施例36の粒子状組成物又は比較例14の粒子を50g添加し、60分撹拌した。得られた試料を光学顕微鏡で観察した。それぞれの試料について、上述の「ワセリンに対する分散性評価」と同様の基準で評価した。その結果を以下の表11に示す。
トリ(カプリル酸/カプリン酸)グリセリル50gをビーカーに移し、実施例36の粒子状組成物又は比較例14の粒子を50g添加し、60分撹拌した。得られた試料を光学顕微鏡で観察した。それぞれの試料について、上述の「ワセリンに対する分散性評価」と同様の基準で評価した。その結果を以下の表11に示す。
Claims (10)
- 固体粒子と、該固体粒子の表面に存在する両親媒性物質と、を含む粒子状組成物であって、
前記両親媒性物質が水中においては閉鎖小胞体の形成能を有し、前記両親媒性物質の含有量(mc[g])が以下の式を満たし、
前記粒子状組成物を水に分散させた際、前記両親媒性物質が、6層以上の単分子膜層を形成して前記固体粒子表面を被覆する、粒子状組成物。
- 水又は油性物質に分散させたときの平均粒子径が、被覆処理前の固体粒子をエタノールに分散させたときの平均粒子径に対して1.0倍以上1.5倍以下である、請求項1に記載の粒子状組成物。
- 前記固体粒子が、金属酸化物の粒子である、請求項1又は2に記載の粒子状組成物。
- 請求項1から3のいずれか1項に記載の粒子状組成物と、該粒子状組成物を含む水又は油性物質と、を有する、液体組成物。
- 前記水中において、前記固体粒子表面が前記両親媒性物質によって形成された6層以上の単分子膜層によって被覆された状態で分散している請求項4に記載の液体組成物。
- 化粧料又は塗料用である、請求項4又は5に記載の液体組成物。
- 請求項1から3のいずれか1項に記載の粒子状組成物の製造方法であって、
前記両親媒性物質の含有量(mc[g])が以下の式を満たすように、前記固体粒子と、水中においては閉鎖小胞体の形成能を有する両親媒性物質を溶解した溶媒との混合物を調製する工程と、
前記混合物中の溶媒を除去する工程と、を有する、方法。
- 前記混合物中の溶媒の除去を、溶媒を揮発させることにより行う、請求項7に記載の方法。
- 固体粒子の表面を被覆するための両親媒性物質からなる固体粒子の表面改質剤であって、
前記両親媒性物質は、水中においては閉鎖小胞体の形成能を有し、
前記両親媒性物質の含有量(mc[g])が以下の式を満たし、
前記両親媒性物質が6層以上の単分子膜層を形成して前記固体粒子表面を被覆して、前記固体表面を分散させる、
固体粒子の表面改質剤。
- 水中においては閉鎖小胞体の形成能を有する両親媒性物質を固体粒子に対して、前記両親媒性物質の含有量(mc[g])が以下の式を満たすように添加して、
前記固体粒子の表面を前記両親媒性物質から形成される単分子膜層6層で覆うことによる、水又は油性物質に対する分散性の向上方法。