JP6488902B2 - アクリル酸重合用組成物 - Google Patents
アクリル酸重合用組成物 Download PDFInfo
- Publication number
- JP6488902B2 JP6488902B2 JP2015120798A JP2015120798A JP6488902B2 JP 6488902 B2 JP6488902 B2 JP 6488902B2 JP 2015120798 A JP2015120798 A JP 2015120798A JP 2015120798 A JP2015120798 A JP 2015120798A JP 6488902 B2 JP6488902 B2 JP 6488902B2
- Authority
- JP
- Japan
- Prior art keywords
- acrylic acid
- polymerization
- parts
- mass
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1](A)アクリル酸および/またはアクリル酸のアルカリ金属塩;100質量部、
(B)一般式(I)で表される水酸基含有有機過酸化物;0.100〜2質量部、
[式中Rは水素原子またはメチル基]
(C)還元剤;0.005〜2質量部、および、
(D)水;100〜1000質量部
を含むアクリル酸重合用組成物、
[2](A)アクリル酸および/またはアクリル酸のアルカリ金属塩;100質量部、
(B)一般式(I)で表される水酸基含有有機過酸化物;0.050〜2質量部、
[式中Rは水素原子またはメチル基]
(C)還元剤;0.005〜2質量部、および、
(D)水;100〜1000質量部、および、
(E)重合助剤;0.050〜1質量部
を含むアクリル酸重合用組成物、
[3](E)重合助剤が、(E1)過硫酸塩および/または(E2)水溶性アゾ系重合開始剤であるアクリル酸重合用組成物、
である。
イオン交換水170部にアクリル酸100部を混合した。この水溶液をデュワー瓶に入れ、窒素置換を行いながら攪拌し、5℃に温度調節した。次に、10%の3−ヒドロキシ−1,1−ジメチルブチルヒドロペルオキシド水溶液(以下DHB-HPO水溶液という)2.7部、10%のアスコルビン酸水溶液1.4部を加え、混合して重合を開始させた。重合完了後、含水ゲルを取り出し数mmの粒径に細断しながら、48%の水酸化ナトリウム水溶液81部を添加して混合し、細断ゲルを得た。さらに、細断ゲルを乾燥、粉砕し、粉末樹脂粒子を得た。
重合に使用した水酸基含有有機過酸化物を10%の3−ヒドロキシ−1,1−ジメチルプロピルヒドロペルオキシド水溶液(以下DHP-HPO水溶液という)に変更した以外は、実施例1−1と同様にして重合を行い、粉末樹脂粒子を得た。
イオン交換水120部とアクリル酸83部を混合した水溶液に、48%の水酸化ナトリウム水溶液67部を攪拌しながら加え、中和処理を行った。この中和処理後の水溶液をデュワー瓶に入れ、窒素置換を行いながら攪拌し、5℃に温度調節した。次に、10%の3−ヒドロキシ−1,1−ジメチルブチルヒドロペルオキシド2.7部、10%のアスコルビン酸1.4部を加え、混合して重合を開始させた。重合完了後、含水ゲルを取り出し、数mmの粒径に細断した。さらに、得られた細断ゲルを乾燥、粉砕し、粉末樹脂粒子を得た。
重合に使用した重合開始剤および還元剤を下記表1に記載する種類および配合量に変更した以外は、実施例1−2と同様にして重合を行い、粉末樹脂粒子を得た。
イオン交換水120部とアクリル酸83部を混合した水溶液に、48%の水酸化ナトリウム水溶液67部を攪拌しながら加え、中和処理を行った。この中和処理後の水溶液をデュワー瓶に入れ、窒素置換を行いながら攪拌し、5℃に温度調節した。次に、10%のDHB-HPO水溶液0.54部を加え、重合を開始した。本条件ではほんど重合が進まなかった。
重合に使用した重合開始剤および還元剤を下記表1に記載する種類および配合量に変更した以外は、比較例1と同様にして重合を行い、粉末樹脂粒子を得た。
DHB−HPO:3−ヒドロキシ−1,1−ジメチルブチル
ヒドロペルオキシド
DHP−HPO:3−ヒドロキシ−1,1−ジメチルプロピル
ヒドロペルオキシド
ASA :アスコルビン酸
i−ASANa:イソアスコルビン酸ナトリウム
APS :過硫酸アンモニウム
NPS :過硫酸ナトリウム
AAPH :2,2−アゾビス−2−アミジノプロパン
ジヒドロクロリド
TB−HPO :t−ブチルヒドロペルオキシド
100mlビーカーに、粉末樹脂0.4gを量りとり、0.9質量%のNaCl水溶液100gを加え、1時間撹拌する。その後、前記ビーカーの内容物を、100メッシュの金網マス中に濾過し、さらに、濾紙により濾過し、ゲルと濾液を分離した。得られた濾液中に溶解しているモノマー含量を、高速液体クロマトグラフィー(HPLC)により測定した。残存モノマー量を以下基準に分類し、判定した。
評価基準:○…残存モノマー量が0.10%未満
△…残存モノマー量が0.10%以上、0.50%未満
×…残存モノマー量が0.50%以上
Claims (3)
- (E)重合助剤が、(E1)過硫酸塩および/または(E2)水溶性アゾ系重合開始剤である請求項2に記載のアクリル酸重合用組成物。