JP6408983B2 - Liquid crystal dropping method sealing agent, vertical conduction material, and liquid crystal display element - Google Patents
Liquid crystal dropping method sealing agent, vertical conduction material, and liquid crystal display element Download PDFInfo
- Publication number
- JP6408983B2 JP6408983B2 JP2015518702A JP2015518702A JP6408983B2 JP 6408983 B2 JP6408983 B2 JP 6408983B2 JP 2015518702 A JP2015518702 A JP 2015518702A JP 2015518702 A JP2015518702 A JP 2015518702A JP 6408983 B2 JP6408983 B2 JP 6408983B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- meth
- acrylate
- group
- crystal dropping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、光硬化性に優れ、かつ、液晶汚染を抑制することができる液晶滴下工法用シール剤に関する。また、本発明は、該液晶滴下工法用シール剤を用いてなる上下導通材料及び液晶表示素子に関する。 The present invention relates to a sealing agent for a liquid crystal dropping method, which is excellent in photocurability and can suppress liquid crystal contamination. Moreover, this invention relates to the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal dropping methods.
近年、液晶表示セル等の液晶表示素子の製造方法としては、タクトタイム短縮、使用液晶量の最適化といった観点から、特許文献1、特許文献2に開示されているような、硬化性樹脂と光重合開始剤と熱硬化剤とを含有する光熱併用硬化型のシール剤を用いた滴下工法と呼ばれる液晶滴下方式が用いられている。
滴下工法では、まず、2枚の電極付き透明基板の一方に、ディスペンスにより長方形状のシールパターンを形成する。次いで、シール剤が未硬化の状態で液晶の微小滴を透明基板の枠内全面に滴下し、すぐに他方の透明基板を重ね合わせ、シール部に紫外線等の光を照射して仮硬化を行う。その後、液晶アニール時に加熱して本硬化を行い、液晶表示素子を作製する。基板の貼り合わせを減圧下で行うようにすれば、極めて高い効率で液晶表示素子を製造することができ、現在この滴下工法が液晶表示素子の製造方法の主流となっている。In recent years, as a method of manufacturing a liquid crystal display element such as a liquid crystal display cell, a curable resin and a light as disclosed in Patent Document 1 and Patent Document 2 from the viewpoint of shortening tact time and optimizing the amount of liquid crystal used. A liquid crystal dropping method called a dropping method using a photothermal combined curing type sealing agent containing a polymerization initiator and a thermosetting agent is used.
In the dropping method, first, a rectangular seal pattern is formed on one of two transparent substrates with electrodes by dispensing. Next, a liquid crystal micro-droplet is dropped on the entire surface of the transparent substrate frame in a state where the sealant is uncured, and the other transparent substrate is immediately overlaid, and the seal portion is irradiated with light such as ultraviolet rays for temporary curing. . Thereafter, heating is performed at the time of liquid crystal annealing to perform main curing, and a liquid crystal display element is manufactured. If the substrates are bonded together under reduced pressure, a liquid crystal display element can be manufactured with extremely high efficiency, and this dripping method is currently the mainstream method for manufacturing liquid crystal display elements.
ところで、携帯電話、携帯ゲーム機等、各種液晶パネル付きモバイル機器が普及している現代において、装置の小型化は最も求められている課題である。装置の小型化の手法としては、液晶表示部の狭額縁化が挙げられ、例えば、シール部の位置をブラックマトリックス下に配置することが行われている(以下、狭額縁設計ともいう)。 By the way, in the present age when mobile devices with various liquid crystal panels such as mobile phones and portable game machines are widespread, downsizing of devices is the most demanded issue. As a method for reducing the size of the apparatus, there is a narrow frame of the liquid crystal display unit. For example, the position of the seal portion is arranged under the black matrix (hereinafter also referred to as a narrow frame design).
しかしながら、狭額縁設計ではシール剤がブラックマトリックスの直下に配置されるため、滴下工法を行うと、シール剤を光硬化させる際に照射した光が遮られ、シール剤の内部まで光が到達せず硬化が不充分となるという問題があった。このようにシール剤の硬化が不充分となると、未硬化のシール剤成分が液晶中に溶出し、溶出したシール剤成分による硬化反応が液晶中において進行することで液晶汚染が発生するという問題があった。 However, in the narrow frame design, the sealant is placed directly under the black matrix, so when the dripping method is used, the light irradiated when photocuring the sealant is blocked, and the light does not reach the inside of the sealant. There was a problem that the curing was insufficient. If the sealant is insufficiently cured in this manner, the uncured sealant component is eluted in the liquid crystal, and the curing reaction by the eluted sealant component proceeds in the liquid crystal, resulting in liquid crystal contamination. there were.
液晶汚染を抑制する方法として、特許文献3には、シール剤に高感度の光重合開始剤を配合することが開示されている。しかしながら、高感度の光重合開始剤を配合しただけでは、充分に液晶汚染を抑制することができなかった。 As a method for suppressing liquid crystal contamination, Patent Document 3 discloses that a highly sensitive photopolymerization initiator is blended with a sealant. However, liquid crystal contamination could not be sufficiently suppressed only by blending a highly sensitive photopolymerization initiator.
本発明は、光硬化性に優れ、かつ、液晶汚染を抑制することができる液晶滴下工法用シール剤を提供することを目的とする。また、本発明は、該液晶滴下工法用シール剤を用いてなる上下導通材料及び液晶表示素子を提供することを目的とする。 An object of this invention is to provide the sealing compound for liquid crystal dropping methods which is excellent in photocurability and can suppress liquid-crystal contamination. Moreover, an object of this invention is to provide the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal dropping methods.
本発明は、硬化性樹脂と光ラジカル重合開始剤とを含有する液晶滴下工法用シール剤であって、上記硬化性樹脂中における誘電率が10以上の硬化性樹脂の含有割合が100重量%であり、上記光ラジカル重合開始剤は、極性基を有するオキシムエステル化合物である液晶滴下工法用シール剤である。
以下に本発明を詳述する。
The present invention is a liquid crystal dropping method sealing agent containing a curable resin and a radical photopolymerization initiator, wherein the content of the curable resin having a dielectric constant of 10 or more in the curable resin is 100% by weight . Yes, the photo radical polymerization initiator is a liquid crystal dropping method sealing agent which is an oxime ester compound having a polar group.
The present invention is described in detail below.
本発明者は、誘電率が10以上である硬化性樹脂と、極性基を有するオキシムエステル化合物とを組み合わせて用いることにより、光硬化性に優れ、かつ、液晶汚染を抑制することができる液晶滴下工法用シール剤を得ることができることを見出し、本発明を完成させるに至った。 The present inventor uses a combination of a curable resin having a dielectric constant of 10 or more and an oxime ester compound having a polar group to provide a liquid crystal drop excellent in photocurability and capable of suppressing liquid crystal contamination. The inventors have found that a sealing agent for a construction method can be obtained, and have completed the present invention.
本発明の液晶滴下工法用シール剤は、硬化性樹脂を含有する。
上記硬化性樹脂は、誘電率が10以上である。上記硬化性樹脂は、誘電率が10以上であることにより、液晶へ溶出しにくいものとなり、更に、後述する極性基を有するオキシムエステル化合物との相溶性が高くなって、得られる液晶滴下工法用シール剤が光硬化性に優れるものとなり、かつ、均一な硬化物を得ることができる。上記硬化性樹脂の誘電率の好ましい下限は11、より好ましい下限は12である。また、上記硬化性樹脂の誘電率は、高ければ高いほどがよいが、実質的な上限は20である。
なお、本発明の液晶滴下工法用シール剤が、上記硬化性樹脂として2種以上の化合物を含有する場合、上記硬化性樹脂の誘電率は、上記硬化性樹脂を構成するそれぞれの化合物の誘電率と硬化性樹脂中における重量分率とから算出できる。
上記「誘電率」は、インピーダンスアナライザー(例えば、ソーラトロン社製、「1260型」等)を用いて25℃、1MHzの条件で複素比誘電率を測定することにより測定でき、実数部で定義される。The sealing agent for liquid crystal dropping method of the present invention contains a curable resin.
The curable resin has a dielectric constant of 10 or more. When the above curable resin has a dielectric constant of 10 or more, it becomes difficult to elute into the liquid crystal, and the compatibility with the oxime ester compound having a polar group described later is further increased. The sealing agent is excellent in photocurability, and a uniform cured product can be obtained. The preferable lower limit of the dielectric constant of the curable resin is 11, and the more preferable lower limit is 12. The higher the dielectric constant of the curable resin is, the better, but the practical upper limit is 20.
In addition, when the sealing compound for liquid crystal dropping method of this invention contains 2 or more types of compounds as said curable resin, the dielectric constant of the said curable resin is the dielectric constant of each compound which comprises the said curable resin. And the weight fraction in the curable resin.
The above-mentioned “dielectric constant” can be measured by measuring the complex dielectric constant under the conditions of 25 ° C. and 1 MHz using an impedance analyzer (for example, “1260 type” manufactured by Solartron), and is defined by the real part. .
誘電率が10以上の硬化性樹脂としては、後述するエポキシ(メタ)アクリレートや部分(メタ)アクリル変性エポキシ樹脂が好適に用いられる。上記エポキシ(メタ)アクリレートや上記部分(メタ)アクリル変性エポキシ樹脂の原料となるエポキシ樹脂としては、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェノールS型エポキシ樹脂、レゾルシノール型エポキシ樹脂、ビフェニル型エポキシ樹脂、ジフェニルエーテル型エポキシ樹脂等が挙げられる。 As the curable resin having a dielectric constant of 10 or more, an epoxy (meth) acrylate or a partial (meth) acryl-modified epoxy resin described later is preferably used. Examples of the epoxy resin used as a raw material for the epoxy (meth) acrylate and the partial (meth) acryl-modified epoxy resin include bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, resorcinol type epoxy resin, Biphenyl type epoxy resin, diphenyl ether type epoxy resin and the like can be mentioned.
本発明の液晶滴下工法用シール剤が、上記硬化性樹脂として2種以上の化合物を含有する場合、2種以上を配合した硬化性樹脂の平均の誘電率が10以上であることが好ましく、液晶への溶出をより抑制する観点から、上記硬化性樹脂を構成する全ての化合物の誘電率が10以上であることがより好ましい。
また、上記硬化性樹脂として2種以上の化合物を含有する場合、硬化性樹脂中における上記誘電率が10以上の硬化性樹脂の含有割合は、50重量%以上であることが好ましく、80重量%以上であることがより好ましく、100重量%であることが最も好ましい。When the sealing agent for liquid crystal dropping method of the present invention contains two or more compounds as the curable resin, the average dielectric constant of the curable resin containing two or more compounds is preferably 10 or more. From the viewpoint of further suppressing elution into the resin, it is more preferable that the dielectric constant of all the compounds constituting the curable resin is 10 or more.
When the curable resin contains two or more compounds, the content of the curable resin having a dielectric constant of 10 or more in the curable resin is preferably 50% by weight or more, and 80% by weight. More preferably, it is 100% by weight.
上記硬化性樹脂は、(メタ)アクリロイル基を有する化合物を含有することが好ましく、反応性の高さから1分子中に(メタ)アクリロイル基を2〜3個有する化合物を含有することがより好ましい。 The curable resin preferably contains a compound having a (meth) acryloyl group, and more preferably contains a compound having 2 to 3 (meth) acryloyl groups in one molecule because of high reactivity. .
上記(メタ)アクリロイル基を有する化合物としては、例えば、(メタ)アクリル酸とエポキシ樹脂とを反応させることにより得られるエポキシ(メタ)アクリレートや部分(メタ)アクリル変性エポキシ樹脂、(メタ)アクリル酸に水酸基を有する化合物を反応させることにより得られるエステル化合物、イソシアネートに水酸基を有する(メタ)アクリル酸誘導体を反応させることにより得られるウレタン(メタ)アクリレート等が挙げられる。なかでも、高い誘電率を得やすいことから、エポキシ(メタ)アクリレート及び/又は部分(メタ)アクリル変性エポキシ樹脂を含有することがより好ましく、エポキシ(メタ)アクリレートを含有することが更に好ましい。
なお、本明細書において、上記「(メタ)アクリロイル基」とは、アクリロイル基又はメタクリロイル基を意味し、上記「(メタ)アクリル」とは、アクリル又はメタクリルを意味し、上記「(メタ)アクリレート」とは、アクリレート又はメタクリレートを意味する。また、上記「エポキシ(メタ)アクリレート」とは、エポキシ樹脂中の全てのエポキシ基を(メタ)アクリル酸と反応させた化合物のことを表し、上記「部分(メタ)アクリレート」とは、1分子中にエポキシ基と(メタ)アクリロイル基とをそれぞれ1つ以上有する樹脂を表す。Examples of the compound having the (meth) acryloyl group include an epoxy (meth) acrylate obtained by reacting (meth) acrylic acid and an epoxy resin, a partial (meth) acryl-modified epoxy resin, and (meth) acrylic acid. And an ester compound obtained by reacting a compound having a hydroxyl group with urethane, and a urethane (meth) acrylate obtained by reacting a (meth) acrylic acid derivative having a hydroxyl group with isocyanate. Especially, since it is easy to obtain a high dielectric constant, it is more preferable to contain an epoxy (meth) acrylate and / or a partial (meth) acryl modified epoxy resin, and it is still more preferable to contain an epoxy (meth) acrylate.
In the present specification, the “(meth) acryloyl group” means an acryloyl group or a methacryloyl group, the “(meth) acryl” means acryl or methacryl, and the “(meth) acrylate” "Means acrylate or methacrylate. The “epoxy (meth) acrylate” means a compound obtained by reacting all epoxy groups in the epoxy resin with (meth) acrylic acid, and the “partial (meth) acrylate” is one molecule. A resin having one or more epoxy groups and one or more (meth) acryloyl groups therein.
上記エポキシ(メタ)アクリレートとしては、例えば、エポキシ樹脂と(メタ)アクリル酸とを、常法に従って塩基性触媒の存在下で反応することにより得られるもの等が挙げられる。 Examples of the epoxy (meth) acrylate include those obtained by reacting an epoxy resin and (meth) acrylic acid in the presence of a basic catalyst according to a conventional method.
上記エポキシ(メタ)アクリレートを合成するための原料となるエポキシ樹脂としては、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェノールS型エポキシ樹脂、2,2’−ジアリルビスフェノールA型エポキシ樹脂、水添ビスフェノール型エポキシ樹脂、プロピレンオキシド付加ビスフェノールA型エポキシ樹脂、レゾルシノール型エポキシ樹脂、ビフェニル型エポキシ樹脂、スルフィド型エポキシ樹脂、ジフェニルエーテル型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、ナフタレン型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、オルトクレゾールノボラック型エポキシ樹脂、ジシクロペンタジエンノボラック型エポキシ樹脂、ビフェニルノボラック型エポキシ樹脂、ナフタレンフェノールノボラック型エポキシ樹脂、グリシジルアミン型エポキシ樹脂、アルキルポリオール型エポキシ樹脂、ゴム変性型エポキシ樹脂、グリシジルエステル化合物等が挙げられる。 Examples of the epoxy resin that is a raw material for synthesizing the epoxy (meth) acrylate include bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, and 2,2′-diallyl bisphenol A type epoxy resin. , Hydrogenated bisphenol type epoxy resin, propylene oxide added bisphenol A type epoxy resin, resorcinol type epoxy resin, biphenyl type epoxy resin, sulfide type epoxy resin, diphenyl ether type epoxy resin, dicyclopentadiene type epoxy resin, naphthalene type epoxy resin, phenol Novolac epoxy resin, ortho-cresol novolac epoxy resin, dicyclopentadiene novolac epoxy resin, biphenyl novolac epoxy resin, naphtha Emissions phenol novolak type epoxy resin, glycidyl amine type epoxy resin, alkyl polyol type epoxy resin, rubber-modified epoxy resins, glycidyl ester compounds.
上記ビスフェノールA型エポキシ樹脂のうち市販されているものとしては、例えば、jER808、jER828EL、jER1004(いずれも三菱化学社製)、エピクロン850CRP(DIC社製)等が挙げられる。
上記ビスフェノールF型エポキシ樹脂のうち市販されているものとしては、例えば、jER806、jER4004(いずれも三菱化学社製)等が挙げられる。
上記ビスフェノールS型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンEXA1514(DIC社製)等が挙げられる。
上記2,2’−ジアリルビスフェノールA型エポキシ樹脂のうち市販されているものとしては、例えば、RE−810NM(日本化薬社製)等が挙げられる。
上記水添ビスフェノール型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンEXA7015(DIC社製)等が挙げられる。
上記プロピレンオキシド付加ビスフェノールA型エポキシ樹脂のうち市販されているものとしては、例えば、EP−4000S(ADEKA社製)等が挙げられる。
上記レゾルシノール型エポキシ樹脂のうち市販されているものとしては、例えば、EX−201(ナガセケムテックス社製)等が挙げられる。
上記ビフェニル型エポキシ樹脂のうち市販されているものとしては、例えば、jERYX−4000H(三菱化学社製)等が挙げられる。
上記スルフィド型エポキシ樹脂のうち市販されているものとしては、例えば、YSLV−50TE(新日鐵住金化学社製)等が挙げられる。
上記ジフェニルエーテル型エポキシ樹脂のうち市販されているものとしては、例えば、YSLV−80DE(新日鐵住金化学社製)等が挙げられる。
上記ジシクロペンタジエン型エポキシ樹脂のうち市販されているものとしては、例えば、EP−4088S(ADEKA社製)等が挙げられる。
上記ナフタレン型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンHP4032、エピクロンEXA−4700(いずれもDIC社製)等が挙げられる。
上記フェノールノボラック型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンN−770(DIC社製)等が挙げられる。
上記オルトクレゾールノボラック型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンN−670−EXP−S(DIC社製)等が挙げられる。
上記ジシクロペンタジエンノボラック型エポキシ樹脂のうち市販されているものとしては、例えば、エピクロンHP7200(DIC社製)等が挙げられる。
上記ビフェニルノボラック型エポキシ樹脂のうち市販されているものとしては、例えば、NC−3000P(日本化薬社製)等が挙げられる。
上記ナフタレンフェノールノボラック型エポキシ樹脂のうち市販されているものとしては、例えば、ESN−165S(新日鐵住金化学社製)等が挙げられる。
上記グリシジルアミン型エポキシ樹脂のうち市販されているものとしては、例えば、jER630(三菱化学社製)、エピクロン430(DIC社製)、TETRAD−X(三菱ガス化学社製)等が挙げられる。
上記アルキルポリオール型エポキシ樹脂のうち市販されているものとしては、例えば、ZX−1542(新日鐵住金化学社製)、エピクロン726(DIC社製)、エポライト80MFA(共栄社化学社製)、デナコールEX−611(ナガセケムテックス社製)等が挙げられる。
上記ゴム変性型エポキシ樹脂のうち市販されているものとしては、例えば、YR−450、YR−207(いずれも新日鐵住金化学社製)、エポリードPB(ダイセル社製)等が挙げられる。
上記グリシジルエステル化合物のうち市販されているものとしては、例えば、デナコールEX−147(ナガセケムテックス社製)等が挙げられる。
上記エポキシ樹脂のうちその他に市販されているものとしては、例えば、YDC−1312、YSLV−80XY、YSLV−90CR(いずれも新日鐵住金化学社製)、XAC4151(旭化成社製)、jER1031、jER1032(いずれも三菱化学社製)、EXA−7120(DIC社製)、TEPIC(日産化学社製)等が挙げられる。As what is marketed among the said bisphenol A type epoxy resins, jER808, jER828EL, jER1004 (all are the Mitsubishi Chemical company make), Epiklon 850CRP (made by DIC company), etc. are mentioned, for example.
As what is marketed among the said bisphenol F-type epoxy resins, jER806, jER4004 (all are the Mitsubishi Chemical company make) etc. are mentioned, for example.
As what is marketed among the said bisphenol S-type epoxy resins, Epicron EXA1514 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said 2,2'- diallyl bisphenol A type epoxy resins, RE-810NM (made by Nippon Kayaku Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said hydrogenated bisphenol type | mold epoxy resins, Epicron EXA7015 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said propylene oxide addition bisphenol A type epoxy resins, EP-4000S (made by ADEKA) etc. are mentioned, for example.
As what is marketed among the said resorcinol type epoxy resins, EX-201 (made by Nagase ChemteX Corporation) etc. are mentioned, for example.
As what is marketed among the said biphenyl type epoxy resins, jERYX-4000H (made by Mitsubishi Chemical Corporation) etc. are mentioned, for example.
As what is marketed among the said sulfide type epoxy resins, YSLV-50TE (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said diphenyl ether type epoxy resins, YSLV-80DE (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said dicyclopentadiene type epoxy resins, EP-4088S (made by ADEKA) etc. are mentioned, for example.
As what is marketed among the said naphthalene type | mold epoxy resins, Epicron HP4032, Epicron EXA-4700 (all are the products made from DIC) etc. are mentioned, for example.
As what is marketed among the said phenol novolak-type epoxy resins, Epicron N-770 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said ortho cresol novolak-type epoxy resins, Epicron N-670-EXP-S (made by DIC) etc. are mentioned, for example.
As what is marketed among the said dicyclopentadiene novolak-type epoxy resins, epiclone HP7200 (made by DIC) etc. are mentioned, for example.
As what is marketed among the said biphenyl novolak-type epoxy resins, NC-3000P (made by Nippon Kayaku Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said naphthalene phenol novolak-type epoxy resins, ESN-165S (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said glycidyl amine type epoxy resins, jER630 (made by Mitsubishi Chemical Corporation), Epicron 430 (made by DIC Corporation), TETRAD-X (made by Mitsubishi Gas Chemical Co., Inc.) etc. are mentioned, for example.
Among the above-mentioned alkyl polyol type epoxy resins, those commercially available include, for example, ZX-1542 (manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.), Epicron 726 (manufactured by DIC Corporation), Epolite 80MFA (manufactured by Kyoeisha Chemical Co., Ltd.), Denacol EX -611 (manufactured by Nagase ChemteX Corporation).
Examples of commercially available rubber-modified epoxy resins include YR-450, YR-207 (all manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.), Epolide PB (manufactured by Daicel Corporation), and the like.
As what is marketed among the said glycidyl ester compounds, Denacol EX-147 (made by Nagase ChemteX Corporation) etc. is mentioned, for example.
Other commercially available epoxy resins include, for example, YDC-1312, YSLV-80XY, YSLV-90CR (all manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.), XAC4151 (manufactured by Asahi Kasei Co., Ltd.), jER1031, and jER1032. (All manufactured by Mitsubishi Chemical Corporation), EXA-7120 (manufactured by DIC Corporation), TEPIC (manufactured by Nissan Chemical Industries, Ltd.) and the like.
上記エポキシ(メタ)アクリレートのうち市販されているものとしては、例えば、EBECRYL860、EBECRYL3200、EBECRYL3201、EBECRYL3412、EBECRYL3600、EBECRYL3700、EBECRYL3701、EBECRYL3702、EBECRYL3703、EBECRYL3800、EBECRYL6040、EBECRYLRDX63182(いずれもダイセル・オルネクス社製)、EA−1010、EA−1020、EA−5323、EA−5520、EA−CHD、EMA−1020(いずれも新中村化学工業社製)、エポキシエステルM−600A、エポキシエステル40EM、エポキシエステル70PA、エポキシエステル200PA、エポキシエステル80MFA、エポキシエステル3002M、エポキシエステル3002A、エポキシエステル1600A、エポキシエステル3000M、エポキシエステル3000A、エポキシエステル200EA、エポキシエステル400EA(いずれも共栄社化学社製)、デナコールアクリレートDA−141、デナコールアクリレートDA−314、デナコールアクリレートDA−911(いずれもナガセケムテックス社製)等が挙げられる。 Examples of commercially available epoxy (meth) acrylates include, for example, EBECRYL860, EBECRYL3200, EBECRYL3201, EBECRYL3412, EBECRYL3600, EBECRYL3700, EBECRYL3701, EBECRYL3702, EBECRYL3703, EBECRY3603 EA-1010, EA-1020, EA-5323, EA-5520, EA-CHD, EMA-1020 (all manufactured by Shin-Nakamura Chemical Co., Ltd.), epoxy ester M-600A, epoxy ester 40EM, epoxy ester 70PA, epoxy Ester 200PA, epoxy ester 80MFA Epoxy ester 3002M, Epoxy ester 3002A, Epoxy ester 1600A, Epoxy ester 3000M, Epoxy ester 3000A, Epoxy ester 200EA, Epoxy ester 400EA (all manufactured by Kyoeisha Chemical Co., Ltd.), Denacol acrylate DA-141, Denacol acrylate DA-314, Denacol acrylate DA-911 (all manufactured by Nagase ChemteX Corporation) and the like.
上記部分(メタ)アクリル変性エポキシ樹脂は、例えば、2つ以上のエポキシ基を有するエポキシ樹脂の一部分のエポキシ基を、(メタ)アクリル酸と反応させることによって得ることができる。
上記部分(メタ)アクリル変性エポキシ樹脂の原料となるエポキシ樹脂としては、上記エポキシ(メタ)アクリレートを合成するための原料として挙げたもの等が挙げられる。The partial (meth) acryl-modified epoxy resin can be obtained, for example, by reacting an epoxy group of a part of an epoxy resin having two or more epoxy groups with (meth) acrylic acid.
As an epoxy resin used as the raw material of the said partial (meth) acryl modified epoxy resin, what was mentioned as a raw material for synthesize | combining the said epoxy (meth) acrylate, etc. are mentioned.
上記部分(メタ)アクリル変性エポキシ樹脂のうち、市販されているものとしては、例えば、UVACURE1561(ダイセル・オルネクス社製)が挙げられる。 Examples of commercially available partial (meth) acrylic-modified epoxy resins include UVACURE 1561 (manufactured by Daicel Ornex).
上記(メタ)アクリル酸に水酸基を有する化合物を反応させることにより得られるエステル化合物のうち単官能のものとしては、例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−プロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、t−ブチル(メタ)アクリレート、n−オクチル(メタ)アクリレート、イソオクチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、イソノニル(メタ)アクリレート、イソデシル(メタ)アクリレート、ラウリル(メタ)アクリレート、イソミリスチル(メタ)アクリレート、ステアリル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、イソボルニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、ベンジル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、2−ヒドロキシブチル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−メトキシエチル(メタ)アクリレート、2−エトキシエチル(メタ)アクリレート、2−ブトキシエチル(メタ)アクリレート、メトキシエチレングリコール(メタ)アクリレート、メトキシポリエチレングリコール(メタ)アクリレート、エチルカルビトール(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、2−フェノキシエチル(メタ)アクリレート、フェノキシジエチレングリコール(メタ)アクリレート、フェノキシポリエチレングリコール(メタ)アクリレート、2,2,2−トリフルオロエチル(メタ)アクリレート、2,2,3,3−テトラフルオロプロピル(メタ)アクリレート、1H,1H,5H−オクタフルオロペンチル(メタ)アクリレート、ジメチルアミノエチル(メタ)アクリレート、ジエチルアミノエチル(メタ)アクリレート、イミド(メタ)アクリレート、2−(メタ)アクリロイロキシエチルコハク酸、2−(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、2−(メタ)アクリロイロキシエチル2−ヒドロキシプロピルフタレート、グリシジル(メタ)アクリレート、2−(メタ)アクリロイロキシエチルホスフェート等が挙げられる。 Among the ester compounds obtained by reacting the above (meth) acrylic acid with a compound having a hydroxyl group, examples of monofunctional compounds include methyl (meth) acrylate, ethyl (meth) acrylate, and n-propyl (meth) acrylate. , N-butyl (meth) acrylate, isobutyl (meth) acrylate, t-butyl (meth) acrylate, n-octyl (meth) acrylate, isooctyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isononyl (meth) acrylate , Isodecyl (meth) acrylate, lauryl (meth) acrylate, isomyristyl (meth) acrylate, stearyl (meth) acrylate, cyclohexyl (meth) acrylate, isobornyl (meth) acrylate, dicyclopenteni (Meth) acrylate, benzyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-methoxy Ethyl (meth) acrylate, 2-ethoxyethyl (meth) acrylate, 2-butoxyethyl (meth) acrylate, methoxyethylene glycol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, ethyl carbitol (meth) acrylate, tetrahydrofur Furyl (meth) acrylate, 2-phenoxyethyl (meth) acrylate, phenoxydiethylene glycol (meth) acrylate, phenoxypolyethylene glycol (meth) acrylate 2,2,2-trifluoroethyl (meth) acrylate, 2,2,3,3-tetrafluoropropyl (meth) acrylate, 1H, 1H, 5H-octafluoropentyl (meth) acrylate, dimethylaminoethyl ( (Meth) acrylate, diethylaminoethyl (meth) acrylate, imide (meth) acrylate, 2- (meth) acryloyloxyethyl succinic acid, 2- (meth) acryloyloxyethyl hexahydrophthalic acid, 2- (meth) acryloyl Examples include roxyethyl 2-hydroxypropyl phthalate, glycidyl (meth) acrylate, 2- (meth) acryloyloxyethyl phosphate, and the like.
また、上記エステル化合物のうち2官能のものとしては、例えば、1,3−ブタンジオールジ(メタ)アクリレート、1,4−ブタンジオールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、1,9−ノナンジオールジ(メタ)アクリレート、1,10−デカンジオールジ(メタ)アクリレート、2−n−ブチル−2−エチル−1,3−プロパンジオールジ(メタ)アクリレート、エチレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、テトラエチレングリコールジ(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、ジプロピレングリコールジ(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、ポリプロピレングリコール(メタ)アクリレート、エチレンオキシド付加ビスフェノールAジ(メタ)アクリレート、プロピレンオキシド付加ビスフェノールAジ(メタ)アクリレート、エチレンオキシド付加ビスフェノールFジ(メタ)アクリレート、ジメチロールジシクロペンタジエニルジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、エチレンオキシド変性イソシアヌル酸ジ(メタ)アクリレート、2−ヒドロキシ−3−(メタ)アクリロイロキシプロピル(メタ)アクリレート、カーボネートジオールジ(メタ)アクリレート、ポリエーテルジオールジ(メタ)アクリレート、ポリエステルジオールジ(メタ)アクリレート、ポリカプロラクトンジオールジ(メタ)アクリレート、ポリブタジエンジオールジ(メタ)アクリレート等が挙げられる。 Examples of the bifunctional one of the ester compounds include 1,3-butanediol di (meth) acrylate, 1,4-butanediol di (meth) acrylate, and 1,6-hexanediol di (meth). Acrylate, 1,9-nonanediol di (meth) acrylate, 1,10-decandiol di (meth) acrylate, 2-n-butyl-2-ethyl-1,3-propanediol di (meth) acrylate, ethylene glycol Di (meth) acrylate, diethylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, polyethylene glycol di (meth) acrylate, dipropylene glycol di (meth) acrylate, tripropylene glycol di (meth) acrylate, polypropylene glycol (Meth) acrylate, ethylene oxide-added bisphenol A di (meth) acrylate, propylene oxide-added bisphenol A di (meth) acrylate, ethylene oxide-added bisphenol F di (meth) acrylate, dimethylol dicyclopentadienyl di (meth) acrylate, neo Pentyl glycol di (meth) acrylate, ethylene oxide modified isocyanuric acid di (meth) acrylate, 2-hydroxy-3- (meth) acryloyloxypropyl (meth) acrylate, carbonate diol di (meth) acrylate, polyether diol di (meth) ) Acrylate, polyester diol di (meth) acrylate, polycaprolactone diol di (meth) acrylate, polybutadiene diol di (meth) acrylate Etc. The.
また、上記エステル化合物のうち3官能以上のものとしては、例えば、トリメチロールプロパントリ(メタ)アクリレート、エチレンオキシド付加トリメチロールプロパントリ(メタ)アクリレート、プロピレンオキシド付加トリメチロールプロパントリ(メタ)アクリレート、カプロラクトン変性トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、エチレンオキシド付加イソシアヌル酸トリ(メタ)アクリレート、グリセリントリ(メタ)アクリレート、プロピレンオキシド付加グリセリントリ(メタ)アクリレート、トリス(メタ)アクリロイルオキシエチルフォスフェート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート等が挙げられる。 Examples of the ester compound having three or more functions include trimethylolpropane tri (meth) acrylate, ethylene oxide-added trimethylolpropane tri (meth) acrylate, propylene oxide-added trimethylolpropane tri (meth) acrylate, and caprolactone. Modified trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, ethylene oxide-added isocyanuric acid tri (meth) acrylate, glycerin tri (meth) acrylate, propylene oxide-added glycerol tri (meth) acrylate, tris (meth) acryloyl Oxyethyl phosphate, ditrimethylolpropane tetra (meth) acrylate, pentaerythritol tetra (meth) acrylate , Dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate.
上記イソシアネートに水酸基を有する(メタ)アクリル酸誘導体を反応させることにより得られるウレタン(メタ)アクリレートとしては、例えば、2つのイソシアネート基を有する化合物1当量に対して水酸基を有する(メタ)アクリル酸誘導体2当量を、触媒量のスズ系化合物存在下で反応させることによって得ることができる。 Examples of the urethane (meth) acrylate obtained by reacting the above isocyanate with a (meth) acrylic acid derivative having a hydroxyl group include, for example, a (meth) acrylic acid derivative having a hydroxyl group with respect to 1 equivalent of a compound having two isocyanate groups. Two equivalents can be obtained by reacting in the presence of a catalytic amount of a tin-based compound.
上記イソシアネートとしては、例えば、イソホロンジイソシアネート、2,4−トリレンジイソシアネート、2,6−トリレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、ジフェニルメタン−4,4’−ジイソシアネート(MDI)、水添MDI、ポリメリックMDI、1,5−ナフタレンジイソシアネート、ノルボルナンジイソシアネート、トリジンジイソシアネート、キシリレンジイソシアネート(XDI)、水添XDI、リジンジイソシアネート、トリフェニルメタントリイソシアネート、トリス(イソシアネートフェニル)チオフォスフェート、テトラメチルキシレンジイソシアネート、1,6,11−ウンデカントリイソシアネート等が挙げられる。 Examples of the isocyanate include isophorone diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, diphenylmethane-4,4′-diisocyanate (MDI), and hydrogenated MDI. , Polymeric MDI, 1,5-naphthalene diisocyanate, norbornane diisocyanate, tolidine diisocyanate, xylylene diisocyanate (XDI), hydrogenated XDI, lysine diisocyanate, triphenylmethane triisocyanate, tris (isocyanatophenyl) thiophosphate, tetramethylxylene diisocyanate, Examples include 1,6,11-undecane triisocyanate.
また、上記イソシアネートとしては、例えば、エチレングリコール、プロピレングリコール、グリセリン、ソルビトール、トリメチロールプロパン、カーボネートジオール、ポリエーテルジオール、ポリエステルジオール、ポリカプロラクトンジオール等のポリオールと過剰のイソシアネートとの反応により得られる鎖延長されたイソシアネート化合物も使用することができる。 Moreover, as said isocyanate, the chain | strand obtained by reaction of polyols, such as ethylene glycol, propylene glycol, glycerol, sorbitol, trimethylol propane, carbonate diol, polyether diol, polyester diol, polycaprolactone diol, and excess isocyanate, for example. Extended isocyanate compounds can also be used.
上記水酸基を有する(メタ)アクリル酸誘導体としては、例えば、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、2−ヒドロキシブチル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート等のヒドロキシアルキル(メタ)アクリレートや、エチレングリコール、プロピレングリコール、1,3−プロパンジオール、1,3−ブタンジオール、1,4−ブタンジオール、ポリエチレングリコール等の二価のアルコールのモノ(メタ)アクリレートや、トリメチロールエタン、トリメチロールプロパン、グリセリン等の三価のアルコールのモノ(メタ)アクリレート又はジ(メタ)アクリレートや、ビスフェノールA型エポキシアクリレート等のエポキシ(メタ)アクリレート等が挙げられる。 Examples of the (meth) acrylic acid derivative having a hydroxyl group include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, and 4-hydroxybutyl (meth) acrylate. Such as hydroxyalkyl (meth) acrylates such as ethylene glycol, propylene glycol, 1,3-propanediol, 1,3-butanediol, 1,4-butanediol, polyethylene glycol and the like mono (meth) Acrylate, mono (meth) acrylate or di (meth) acrylate of trivalent alcohol such as trimethylolethane, trimethylolpropane, glycerin, and epoxy (meth) acrylate such as bisphenol A type epoxy acrylate, etc. And the like.
上記ウレタン(メタ)アクリレートのうち市販されているものとしては、例えば、M−1100、M−1200、M−1210、M−1600(いずれも東亞合成社製)、EBECRYL230、EBECRYL270、EBECRYL4858、EBECRYL8402、EBECRYL8804、EBECRYL8803、EBECRYL8807、EBECRYL9260、EBECRYL1290、EBECRYL5129、EBECRYL4842、EBECRYL210、EBECRYL4827、EBECRYL6700、EBECRYL220、EBECRYL2220(いずれもダイセル・オルネクス社製)、アートレジンUN−9000H、アートレジンUN−9000A、アートレジンUN−7100、アートレジンUN−1255、アートレジンUN−330、アートレジンUN−3320HB、アートレジンUN−1200TPK、アートレジンSH−500B(いずれも根上工業社製)、U−122P、U−108A、U−340P、U−4HA、U−6HA、U−324A、U−15HA、UA−5201P、UA−W2A、U−1084A、U−6LPA、U−2HA、U−2PHA、UA−4100、UA−7100、UA−4200、UA−4400、UA−340P、U−3HA、UA−7200、U−2061BA、U−10H、U−122A、U−340A、U−108、U−6H、UA−4000(いずれも新中村化学工業社製)、AH−600、AT−600、UA−306H、AI−600、UA−101T、UA−101I、UA−306T、UA−306I(いずれも共栄社化学社製)等が挙げられる。 Examples of commercially available urethane (meth) acrylates include M-1100, M-1200, M-1210, M-1600 (all manufactured by Toagosei Co., Ltd.), EBECRYL230, EBECRYL270, EBECRYL4858, EBECRYL8402, EBECRYL8804, EBECRYL8803, EBECRYL8807, EBECRYL9260, EBECRYL1290, EBECRYL5129, EBECRYL4842, EBECRYL210, EBECRYL4827, EBECRYL6700, EBECRYL6700, EBECRYL6700 , Art resin N-1255, Art Resin UN-330, Art Resin UN-3320HB, Art Resin UN-1200TPK, Art Resin SH-500B (all manufactured by Negami Industrial Co., Ltd.), U-122P, U-108A, U-340P, U- 4HA, U-6HA, U-324A, U-15HA, UA-5201P, UA-W2A, U-1084A, U-6LPA, U-2HA, U-2PHA, UA-4100, UA-7100, UA-4200, UA-4400, UA-340P, U-3HA, UA-7200, U-2061BA, U-10H, U-122A, U-340A, U-108, U-6H, UA-4000 (all Shin-Nakamura Chemical Industries Manufactured by AH), AH-600, AT-600, UA-306H, AI-600, UA-101T, UA-101I, A-306T, UA-306I (all manufactured by Kyoeisha Chemical Co., Ltd.).
上記硬化性樹脂は、液晶汚染を抑える点で、−OH基、−NH−基、−NH2基等の水素結合性のユニットを有するものが好ましい。The curable resin preferably has a hydrogen bonding unit such as —OH group, —NH— group, and —NH 2 group in terms of suppressing liquid crystal contamination.
本発明の液晶滴下工法用シール剤は、光ラジカル重合開始剤を含有する。
上記光ラジカル重合開始剤は、極性基を有するオキシムエステル化合物である。本発明の液晶滴下工法用シール剤は、上記光ラジカル重合開始剤として、極性基を有するオキシムエステル化合物を上記誘電率が10以上である硬化性樹脂と組み合わせて用いることにより、光硬化性に優れ、液晶汚染を抑制することができるものとなる。The sealing agent for liquid crystal dropping method of the present invention contains a photo radical polymerization initiator.
The photo radical polymerization initiator is an oxime ester compound having a polar group. The sealing agent for liquid crystal dropping method of the present invention is excellent in photocurability by using an oxime ester compound having a polar group in combination with a curable resin having a dielectric constant of 10 or more as the photoradical polymerization initiator. , Liquid crystal contamination can be suppressed.
上記極性基を有するオキシムエステル化合物の極性基は、−OH基、−COOH基、−SH基、−CONH2基、及び、−NH2基からなる群より選択される少なくとも一種であることが好ましい。なかでも、液晶との相溶性が低くなることから、−OH基がより好ましい。The polar group of the oxime ester compound having the polar group is preferably at least one selected from the group consisting of —OH group, —COOH group, —SH group, —CONH 2 group, and —NH 2 group. . Especially, since compatibility with a liquid crystal becomes low, -OH group is more preferable.
上記極性基を有するオキシムエステル化合物としては、具体的には、下記式(1)で表される化合物が好ましい。 Specifically, the oxime ester compound having a polar group is preferably a compound represented by the following formula (1).
式(1)中、Xは、炭素数1〜6のアルキレン基を表す。
式(1)中、Xで表される炭素数1〜6のアルキレン基としては、例えば、メチレン基、エチレン基、n−プロピレン基、イソプロピレン基、n−ブチレン基、1−エチルエチレン基、n−ペンチレン基、n−へキシレン基等が挙げられる。なかでも、エチレン基が好ましい。In formula (1), X represents an alkylene group having 1 to 6 carbon atoms.
In the formula (1), examples of the alkylene group having 1 to 6 carbon atoms represented by X include a methylene group, an ethylene group, an n-propylene group, an isopropylene group, an n-butylene group, a 1-ethylethylene group, Examples thereof include an n-pentylene group and an n-hexylene group. Of these, an ethylene group is preferable.
上記極性基を有するオキシムエステル化合物の含有量は、硬化性樹脂100重量部に対して、好ましい下限が0.1重量部、好ましい上限が10重量部である。上記極性基を有するオキシムエステル化合物の含有量が0.1重量部未満であると、得られる液晶滴下工法用シール剤の光硬化反応が充分に進行しないことがある。上記極性基を有するオキシムエステル化合物の含有量が10重量部を超えると、得られる液晶滴下工法用シール剤が耐候性や保存安定性に劣るものとなったり、液晶汚染が生じたりすることがある。上記極性基を有するオキシムエステル化合物の含有量のより好ましい下限は0.5重量部、より好ましい上限は5重量部である。 The content of the oxime ester compound having a polar group is preferably 0.1 parts by weight and preferably 10 parts by weight with respect to 100 parts by weight of the curable resin. When the content of the oxime ester compound having a polar group is less than 0.1 parts by weight, the photocuring reaction of the obtained liquid crystal dropping method sealing agent may not sufficiently proceed. If the content of the oxime ester compound having a polar group exceeds 10 parts by weight, the resulting liquid crystal dropping method sealing agent may be inferior in weather resistance and storage stability, or liquid crystal contamination may occur. . The minimum with more preferable content of the oxime ester compound which has the said polar group is 0.5 weight part, and a more preferable upper limit is 5 weight part.
本発明の液晶滴下工法用シール剤は、上記光ラジカル重合開始剤として、上記極性基を有するオキシムエステル化合物に加えて、その他の光ラジカル重合開始剤を含有してもよいが、光硬化性と液晶汚染を抑制する効果とを両立する観点から、その他の光ラジカル重合開始剤は含有しないことが好ましい。 The sealing agent for liquid crystal dropping method of the present invention may contain other photoradical polymerization initiator as the photoradical polymerization initiator in addition to the oxime ester compound having the polar group. From the viewpoint of achieving both the effect of suppressing liquid crystal contamination, it is preferable that no other radical photopolymerization initiator is contained.
本発明の液晶滴下工法用シール剤は、増感剤を含有することが好ましい。
本発明の液晶滴下工法用シール剤は、上記増感剤を含有することにより、高感度でより光硬化性に優れる液晶滴下工法用シール剤を得ることができる。The sealing agent for liquid crystal dropping method of the present invention preferably contains a sensitizer.
By containing the above sensitizer, the liquid crystal dropping method sealing agent of the present invention can provide a liquid crystal dropping method sealing agent with high sensitivity and more excellent photocurability.
上記増感剤は、紫外・可視領域に充分な光吸収帯を有すること好ましいことから、ベンゾフェノン骨格、アントラセン骨格、アントラキノン骨格、クマリン骨格、チオキサントン骨格、及び、フタロシアニン骨格からなる群より選択される少なくとも一種の骨格を有する化合物を含有することが好ましく、アントラセン骨格、アントラキノン骨格、及び、チオキサントン骨格からなる群より選択される少なくとも一種の骨格を有する化合物を含有することがより好ましい。 Since the sensitizer preferably has a sufficient light absorption band in the ultraviolet / visible region, at least selected from the group consisting of a benzophenone skeleton, an anthracene skeleton, an anthraquinone skeleton, a coumarin skeleton, a thioxanthone skeleton, and a phthalocyanine skeleton. It is preferable to contain a compound having one kind of skeleton, and it is more preferred to contain a compound having at least one kind of skeleton selected from the group consisting of an anthracene skeleton, an anthraquinone skeleton, and a thioxanthone skeleton.
上記ベンゾフェノン骨格を有する化合物としては、例えば、ベンゾフェノン、2,4−ジクロロベンゾフェノン、4,4’−ビス(ジメチルアミノ)ベンゾフェノン、4,4’−ビス(ジエチルアミノ)ベンゾフェノン等が挙げられる。
上記アントラセン骨格を有する化合物としては、例えば、9,10−ジブトキシアントラセン、9,10−ジプロキシアントラキノン、9,10−エトキシアントラキノン等が挙げられる。
上記アントラキノン骨格を有する化合物としては、例えば、2−エチルアントラキノン、1−メチルアントラキノン、1,4−ジヒドロキシアントラキノン、2−(2−ヒドロキシエトキシ)−アントラキノン等が挙げられる。
上記クマリン骨格を有する化合物としては、例えば、7−ジエチルアミノ−4−メチルクマリン等が挙げられる。
上記チオキサントン骨格を有する化合物としては、例えば、2,4−ジエチルチオキサントン、2−クロロチオキサントン、4−イソプロピルチオキサントン、1−クロロ−4−プロピルチオキサントン等が挙げられる。
上記フタロシアニン骨格を有する化合物としては、例えば、フタロシアニン等が挙げられる。
これらの増感剤のなかでも、得られる液晶滴下工法用シール剤が遮光部の硬化性に特に優れるものとなることから、4,4’−ビス(ジメチルアミノ)ベンゾフェノン及び4,4’−ビス(ジエチルアミノ)ベンゾフェノンの少なくともいずれかが好ましい。Examples of the compound having a benzophenone skeleton include benzophenone, 2,4-dichlorobenzophenone, 4,4′-bis (dimethylamino) benzophenone, 4,4′-bis (diethylamino) benzophenone, and the like.
Examples of the compound having an anthracene skeleton include 9,10-dibutoxyanthracene, 9,10-diproxyanthraquinone, and 9,10-ethoxyanthraquinone.
Examples of the compound having an anthraquinone skeleton include 2-ethylanthraquinone, 1-methylanthraquinone, 1,4-dihydroxyanthraquinone, 2- (2-hydroxyethoxy) -anthraquinone, and the like.
Examples of the compound having a coumarin skeleton include 7-diethylamino-4-methylcoumarin.
Examples of the compound having a thioxanthone skeleton include 2,4-diethylthioxanthone, 2-chlorothioxanthone, 4-isopropylthioxanthone, 1-chloro-4-propylthioxanthone, and the like.
Examples of the compound having a phthalocyanine skeleton include phthalocyanine.
Among these sensitizers, the resulting liquid crystal dropping method sealant is particularly excellent in light-curing part curability, so that 4,4′-bis (dimethylamino) benzophenone and 4,4′-bis. At least one of (diethylamino) benzophenone is preferred.
上記増感剤の含有量は、上記光重合開始剤100重量部に対して、好ましい下限が2重量部、好ましい上限が50重量部である。上記増感剤の含有量が2重量部未満であると、得られる液晶滴下工法用シール剤の光硬化性をより向上させる効果が充分に発揮されないことがある。上記増感剤の含有量が50重量部を超えると、液晶汚染が発生することがある。上記増感剤の含有量のより好ましい下限は5重量部、より好ましい上限は40重量部である。 The content of the sensitizer is such that a preferred lower limit is 2 parts by weight and a preferred upper limit is 50 parts by weight with respect to 100 parts by weight of the photopolymerization initiator. If the content of the sensitizer is less than 2 parts by weight, the effect of further improving the photocurability of the obtained liquid crystal dropping method sealing agent may not be sufficiently exhibited. When the content of the sensitizer exceeds 50 parts by weight, liquid crystal contamination may occur. The minimum with more preferable content of the said sensitizer is 5 weight part, and a more preferable upper limit is 40 weight part.
本発明の液晶滴下工法用シール剤は、熱ラジカル重合開始剤を含有してもよい。
上記熱ラジカル重合開始剤としては、例えば、アゾ化合物、有機過酸化物等からなるものが挙げられる。なかでも、高分子アゾ化合物からなる開始剤(以下、「高分子アゾ開始剤」ともいう)が好ましい。
なお、本明細書において高分子アゾ化合物とは、アゾ基を有し、熱によってラジカルを生成する、数平均分子量が300以上の化合物を意味する。The sealing agent for liquid crystal dropping method of the present invention may contain a thermal radical polymerization initiator.
As said thermal radical polymerization initiator, what consists of an azo compound, an organic peroxide, etc. is mentioned, for example. Among these, an initiator made of a polymer azo compound (hereinafter also referred to as “polymer azo initiator”) is preferable.
In the present specification, the polymer azo compound means a compound having an azo group and generating a radical by heat and having a number average molecular weight of 300 or more.
上記高分子アゾ開始剤の数平均分子量の好ましい下限は1000、好ましい上限は30万である。上記高分子アゾ開始剤の数平均分子量が1000未満であると、高分子アゾ開始剤が液晶に悪影響を与えることがある。上記高分子アゾ開始剤の数平均分子量が30万を超えると、硬化性樹脂への混合が困難になることがある。上記高分子アゾ開始剤の数平均分子量のより好ましい下限は5000、より好ましい上限は10万であり、更に好ましい下限は1万、更に好ましい上限は9万である。
なお、本明細書において、上記数平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)で測定を行い、ポリスチレン換算により求められる値である。GPCによってポリスチレン換算による数平均分子量を測定する際のカラムとしては、例えば、Shodex LF−804(昭和電工社製)等が挙げられる。The preferable lower limit of the number average molecular weight of the polymeric azo initiator is 1000, and the preferable upper limit is 300,000. When the number average molecular weight of the polymer azo initiator is less than 1000, the polymer azo initiator may adversely affect the liquid crystal. When the number average molecular weight of the polymeric azo initiator exceeds 300,000, mixing with the curable resin may be difficult. The more preferable lower limit of the number average molecular weight of the polymeric azo initiator is 5000, the more preferable upper limit is 100,000, the still more preferable lower limit is 10,000, and the still more preferable upper limit is 90,000.
In addition, in this specification, the said number average molecular weight is a value calculated | required by polystyrene conversion by measuring with gel permeation chromatography (GPC). Examples of the column for measuring the number average molecular weight in terms of polystyrene by GPC include Shodex LF-804 (manufactured by Showa Denko KK).
上記高分子アゾ開始剤としては、例えば、アゾ基を介してポリアルキレンオキサイドやポリジメチルシロキサン等のユニットが複数結合した構造を有するものが挙げられる。
上記アゾ基を介してポリアルキレンオキサイド等のユニットが複数結合した構造を有する高分子アゾ開始剤としては、ポリエチレンオキサイド構造を有するものが好ましい。このような高分子アゾ開始剤としては、例えば、4,4’−アゾビス(4−シアノペンタン酸)とポリアルキレングリコールの重縮合物や、4,4’−アゾビス(4−シアノペンタン酸)と末端アミノ基を有するポリジメチルシロキサンの重縮合物等が挙げられ、具体的には例えば、VPE−0201、VPE−0401、VPE−0601、VPS−0501、VPS−1001(いずれも和光純薬工業社製)等が挙げられる。
また、高分子ではないアゾ化合物の例としてはV−65、V−501(いずれも和光純薬工業社製)等が挙げられる。Examples of the polymer azo initiator include those having a structure in which a plurality of units such as polyalkylene oxide and polydimethylsiloxane are bonded via an azo group.
As the polymer azo initiator having a structure in which a plurality of units such as polyalkylene oxide are bonded via the azo group, those having a polyethylene oxide structure are preferable. Examples of such a polymeric azo initiator include polycondensates of 4,4′-azobis (4-cyanopentanoic acid) and polyalkylene glycol, and 4,4′-azobis (4-cyanopentanoic acid). Examples include polycondensates of polydimethylsiloxane having a terminal amino group, and specific examples include VPE-0201, VPE-0401, VPE-0601, VPS-0501, and VPS-1001 (all of which are Wako Pure Chemical Industries, Ltd.). Manufactured) and the like.
Examples of azo compounds that are not polymers include V-65 and V-501 (both manufactured by Wako Pure Chemical Industries, Ltd.).
上記有機過酸化物としては、例えば、ケトンパーオキサイド、パーオキシケタール、ハイドロパーオキサイド、ジアルキルパーオキサイド、パーオキシエステル、ジアシルパーオキサイド、パーオキシジカーボネート等が挙げられる。 Examples of the organic peroxide include ketone peroxide, peroxyketal, hydroperoxide, dialkyl peroxide, peroxyester, diacyl peroxide, and peroxydicarbonate.
上記熱ラジカル重合開始剤の含有量は、硬化性樹脂100重量部に対して、好ましい下限が0.05重量部、好ましい上限が10重量部である。上記熱ラジカル重合開始剤の含有量が0.05重量部未満であると、得られる液晶滴下工法用シール剤の熱硬化反応が充分に進行しないことがある。上記熱ラジカル重合開始剤の含有量が10重量部を超えると、得られる液晶滴下工法用シール剤が液晶汚染を引き起こすことがある。上記熱ラジカル重合開始剤の含有量のより好ましい下限は0.1重量部、より好ましい上限は5重量部である。 The content of the thermal radical polymerization initiator is preferably 0.05 parts by weight and preferably 10 parts by weight with respect to 100 parts by weight of the curable resin. When the content of the thermal radical polymerization initiator is less than 0.05 parts by weight, the thermosetting reaction of the obtained liquid crystal dropping method sealing agent may not sufficiently proceed. When content of the said thermal radical polymerization initiator exceeds 10 weight part, the sealing compound for liquid crystal dropping methods obtained may cause liquid crystal contamination. The minimum with more preferable content of the said thermal radical polymerization initiator is 0.1 weight part, and a more preferable upper limit is 5 weight part.
本発明の液晶滴下工法用シール剤は、熱硬化剤を含有してもよい。
上記熱硬化剤としては、例えば、有機酸ヒドラジド、イミダゾール誘導体、アミン化合物、多価フェノール系化合物、酸無水物等が挙げられる。なかでも、有機酸ヒドラジドが好適に用いられる。The sealing agent for liquid crystal dropping method of the present invention may contain a thermosetting agent.
Examples of the thermosetting agent include organic acid hydrazides, imidazole derivatives, amine compounds, polyhydric phenol compounds, acid anhydrides, and the like. Of these, organic acid hydrazide is preferably used.
上記有機酸ヒドラジドとしては、例えば、セバシン酸ジヒドラジド、イソフタル酸ジヒドラジド、アジピン酸ジヒドラジド、マロン酸ジヒドラジド等が挙げられる。
上記有機酸ヒドラジドのうち市販されているものとしては、例えば、SDH、ADH(いずれも大塚化学社製)、アミキュアVDH、アミキュアVDH−J、アミキュアUDH、アミキュアUDH−J(いずれも味の素ファインテクノ社製)等が挙げられる。Examples of the organic acid hydrazide include sebacic acid dihydrazide, isophthalic acid dihydrazide, adipic acid dihydrazide, malonic acid dihydrazide, and the like.
Examples of commercially available organic acid hydrazides include SDH, ADH (all manufactured by Otsuka Chemical Co., Ltd.), Amicure VDH, Amicure VDH-J, Amicure UDH, Amicure UDH-J (all of which are Ajinomoto Fine Techno Co., Ltd.). Manufactured) and the like.
上記熱硬化剤の含有量は、上記硬化性樹脂100重量部に対して、好ましい下限が1重量部、好ましい上限が50重量部である。上記熱硬化剤の含有量が1重量部未満であると、得られる液晶滴下工法用シール剤を充分に熱硬化させることができないことがある。上記熱硬化剤の含有量が50重量部を超えると、得られる液晶滴下工法用シール剤の粘度が高くなり、塗布性が悪くなることがある。上記熱硬化剤の含有量のより好ましい上限は30重量部である。 The content of the thermosetting agent is preferably 1 part by weight with respect to 100 parts by weight of the curable resin, and 50 parts by weight with respect to the preferable upper limit. When the content of the thermosetting agent is less than 1 part by weight, the resulting sealing agent for liquid crystal dropping method may not be sufficiently cured. When content of the said thermosetting agent exceeds 50 weight part, the viscosity of the sealing compound for liquid crystal dropping methods obtained will become high, and applicability | paintability may worsen. The upper limit with more preferable content of the said thermosetting agent is 30 weight part.
本発明の液晶滴下工法用シール剤は、粘度の向上、応力分散効果による接着性の改善、線膨張率の改善、硬化物の耐湿性の更なる向上等を目的として充填剤を含有することが好ましい。 The sealing agent for liquid crystal dropping method of the present invention may contain a filler for the purpose of improving the viscosity, improving the adhesiveness due to the stress dispersion effect, improving the coefficient of linear expansion, and further improving the moisture resistance of the cured product. preferable.
上記充填剤としては、例えば、タルク、石綿、シリカ、珪藻土、スメクタイト、ベントナイト、炭酸カルシウム、炭酸マグネシウム、アルミナ、モンモリロナイト、酸化亜鉛、酸化鉄、酸化マグネシウム、酸化錫、酸化チタン、水酸化マグネシウム、水酸化アルミニウム、ガラスビーズ、窒化珪素、硫酸バリウム、石膏、珪酸カルシウム、セリサイト、活性白土、窒化アルミニウム等の無機充填剤や、ポリエステル微粒子、ポリウレタン微粒子、ビニル重合体微粒子、アクリル重合体微粒子等の有機充填剤が挙げられる。これらの充填剤は、単独で用いられてもよいし、2種以上が組み合わせて用いられてもよい。 Examples of the filler include talc, asbestos, silica, diatomaceous earth, smectite, bentonite, calcium carbonate, magnesium carbonate, alumina, montmorillonite, zinc oxide, iron oxide, magnesium oxide, tin oxide, titanium oxide, magnesium hydroxide, water Inorganic fillers such as aluminum oxide, glass beads, silicon nitride, barium sulfate, gypsum, calcium silicate, sericite, activated clay, aluminum nitride, and organic materials such as polyester fine particles, polyurethane fine particles, vinyl polymer fine particles, and acrylic polymer fine particles A filler is mentioned. These fillers may be used alone or in combination of two or more.
本発明の液晶滴下工法用シール剤全体100重量部中における上記充填剤の含有量の好ましい下限は10重量部、好ましい上限は70重量部である。上記充填剤の含有量が10重量部未満であると、接着性の改善等の効果が充分に発揮されないことがある。上記充填剤の含有量が70重量部を超えると、得られる液晶滴下工法用シール剤が、粘度が高すぎて塗布性に劣るものとなることがある。上記充填剤の含有量のより好ましい下限は20重量部、より好ましい上限は60重量部である。 The minimum with preferable content of the said filler in 100 weight part of whole sealing compound for liquid crystal dropping methods of this invention is 10 weight part, and a preferable upper limit is 70 weight part. When the content of the filler is less than 10 parts by weight, effects such as improvement of adhesiveness may not be sufficiently exhibited. When content of the said filler exceeds 70 weight part, the sealing compound for liquid crystal dropping methods obtained may have a viscosity too high, and may become inferior to applicability | paintability. The minimum with more preferable content of the said filler is 20 weight part, and a more preferable upper limit is 60 weight part.
本発明の液晶滴下工法用シール剤は、シランカップリング剤を含有することが好ましい。上記シランカップリング剤は、主にシール剤と基板等とを良好に接着するための接着助剤としての役割を有する。 The sealing agent for liquid crystal dropping method of the present invention preferably contains a silane coupling agent. The silane coupling agent mainly has a role as an adhesion assistant for favorably bonding the sealing agent and the substrate.
上記シランカップリング剤としては、基板等との接着性を向上させる効果に優れ、硬化性樹脂と化学結合することにより液晶中への硬化性樹脂の流出を抑制することができることから、例えば、3−アミノプロピルトリメトキシシラン、3−メルカプトプロピルトリメトキシシラン、3−グリシドキシプロピルトリメトキシシラン、3−イソシアネートプロピルトリメトキシシラン等が好適に用いられる。これらのシランカップリング剤は、単独で用いられてもよいし、2種以上が組み合わせて用いられてもよい。 As said silane coupling agent, since it is excellent in the effect which improves adhesiveness with a board | substrate etc. and it can suppress the outflow of curable resin in a liquid crystal by chemically bonding with curable resin, it is 3 for example. -Aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-isocyanatopropyltrimethoxysilane and the like are preferably used. These silane coupling agents may be used alone or in combination of two or more.
本発明の液晶滴下工法用シール剤100重量部中における上記シランカップリング剤の含有量の好ましい下限は0.1重量部、好ましい上限は10重量部である。上記シランカップリング剤の含有量が0.1重量部未満であると、接着性を向上させる等の効果が充分に発揮されないことがある。上記シランカップリング剤の含有量が10重量部を超えると、得られる液晶滴下工法用シール剤が液晶汚染を引き起こすことがある。上記シランカップリング剤の含有量のより好ましい下限は0.3重量部、より好ましい上限は5重量部である。 The minimum with preferable content of the said silane coupling agent in 100 weight part of sealing agents for liquid crystal dropping methods of this invention is 0.1 weight part, and a preferable upper limit is 10 weight part. When the content of the silane coupling agent is less than 0.1 parts by weight, effects such as improvement of adhesiveness may not be sufficiently exhibited. When content of the said silane coupling agent exceeds 10 weight part, the sealing compound for liquid crystal dropping methods obtained may cause liquid-crystal contamination. The minimum with more preferable content of the said silane coupling agent is 0.3 weight part, and a more preferable upper limit is 5 weight part.
本発明の液晶滴下工法用シール剤は、遮光剤を含有してもよい。上記遮光剤を含有することにより、本発明の液晶滴下工法用シール剤は、遮光シール剤として好適に用いることができる。 The sealing agent for liquid crystal dropping method of the present invention may contain a light shielding agent. By containing the said light shielding agent, the sealing compound for liquid crystal dropping methods of this invention can be used suitably as a light shielding sealing agent.
上記遮光剤としては、例えば、酸化鉄、チタンブラック、アニリンブラック、シアニンブラック、フラーレン、カーボンブラック、樹脂被覆型カーボンブラック等が挙げられる。なかでも、絶縁性が高いことから、チタンブラックが好ましい。 Examples of the light-shielding agent include iron oxide, titanium black, aniline black, cyanine black, fullerene, carbon black, and resin-coated carbon black. Of these, titanium black is preferred because of its high insulating properties.
上記チタンブラックは、表面処理されていないものでも充分な効果を発揮するが、表面がカップリング剤等の有機成分で処理されているものや、酸化ケイ素、酸化チタン、酸化ゲルマニウム、酸化アルミニウム、酸化ジルコニウム、酸化マグネシウム等の無機成分で被覆されているもの等、表面処理されたチタンブラックを用いることもできる。なかでも、有機成分で処理されているものは、より絶縁性を向上できる点で好ましい。
また、遮光剤として上記チタンブラックを含有する本発明の液晶滴下工法用シール剤を用いて製造した液晶表示素子は、充分な遮光性を有するため、光の漏れ出しがなく高いコントラストを有し、優れた画像表示品質を有する液晶表示素子を実現することができる。The above-mentioned titanium black exhibits a sufficient effect even if it is not surface-treated, but the surface is treated with an organic component such as a coupling agent, silicon oxide, titanium oxide, germanium oxide, aluminum oxide, oxidized Surface-treated titanium black such as those coated with an inorganic component such as zirconium or magnesium oxide can also be used. Especially, what is processed with the organic component is preferable at the point which can improve insulation more.
In addition, the liquid crystal display device manufactured using the sealing agent for liquid crystal dropping method of the present invention containing the above-described titanium black as a light-shielding agent has a sufficient light-shielding property, and thus has a high contrast without light leakage. A liquid crystal display element having excellent image display quality can be realized.
上記チタンブラックのうち市販されているものとしては、例えば、12S、13M、13M−C、13R−N、14M−C(いずれも三菱マテリアル社製)、ティラックD(赤穂化成社製)等が挙げられる。 Examples of commercially available titanium black include 12S, 13M, 13M-C, 13R-N, 14M-C (all manufactured by Mitsubishi Materials Corporation), Tilak D (manufactured by Ako Kasei Co., Ltd.), and the like. Can be mentioned.
上記チタンブラックの比表面積の好ましい下限は13m2/g、好ましい上限は30m2/gであり、より好ましい下限は15m2/g、より好ましい上限は25m2/gである。
また、上記チタンブラックの体積抵抗の好ましい下限は0.5Ω・cm、好ましい上限は3Ω・cmであり、より好ましい下限は1Ω・cm、より好ましい上限は2.5Ω・cmである。The preferable lower limit of the specific surface area of the titanium black is 13 m 2 / g, the preferable upper limit is 30 m 2 / g, the more preferable lower limit is 15 m 2 / g, and the more preferable upper limit is 25 m 2 / g.
Further, the preferred lower limit of the volume resistance of the titanium black is 0.5 Ω · cm, the preferred upper limit is 3 Ω · cm, the more preferred lower limit is 1 Ω · cm, and the more preferred upper limit is 2.5 Ω · cm.
上記遮光剤の一次粒子径は、液晶表示素子の基板間の距離以下であれば特に限定されないが、好ましい下限は1nm、好ましい上限は5μmである。上記遮光剤の一次粒子径が1nm未満であると、得られる液晶滴下工法用シール剤の粘度やチクソトロピーが大きく増大してしまい、作業性が悪くなることがある。上記遮光剤の一次粒子径が5μmを超えると、得られる液晶滴下工法用シール剤の基板への塗布性が悪くなることがある。上記遮光剤の一次粒子径のより好ましい下限は5nm、より好ましい上限は200nm、更に好ましい下限は10nm、更に好ましい上限は100nmである。
なお、上記遮光剤の一次粒子径は、NICOMP 380ZLS(PARTICLE SIZING SYSTEMS社製)を用いて、上記遮光剤を溶媒(水、有機溶媒等)に分散させて測定することができる。The primary particle diameter of the light-shielding agent is not particularly limited as long as it is not more than the distance between the substrates of the liquid crystal display element, but the preferred lower limit is 1 nm and the preferred upper limit is 5 μm. When the primary particle diameter of the light-shielding agent is less than 1 nm, the viscosity and thixotropy of the obtained liquid crystal dropping method sealing agent are greatly increased, and workability may be deteriorated. When the primary particle diameter of the light-shielding agent exceeds 5 μm, the coating property of the obtained liquid crystal dropping method sealing agent on the substrate may be deteriorated. The more preferable lower limit of the primary particle diameter of the light shielding agent is 5 nm, the more preferable upper limit is 200 nm, the still more preferable lower limit is 10 nm, and the still more preferable upper limit is 100 nm.
The primary particle size of the light shielding agent can be measured by using NICOMP 380ZLS (manufactured by PARTICS SIZING SYSTEMS) and dispersing the light shielding agent in a solvent (water, organic solvent, etc.).
本発明の液晶滴下工法用シール剤100重量部中における上記遮光剤の含有量の好ましい下限は5重量部、好ましい上限は80重量部である。上記遮光剤の含有量が5重量部未満であると、充分な遮光性が得られないことがある。上記遮光剤の含有量が80重量部を超えると、得られる液晶滴下工法用シール剤の基板に対する密着性や硬化後の強度が低下したり、描画性が低下したりすることがある。上記遮光剤の含有量のより好ましい下限は10重量部、より好ましい上限は70重量部であり、更に好ましい下限は30重量部、更に好ましい上限は60重量部である。 The preferable lower limit of the content of the light shielding agent in 100 parts by weight of the sealing agent for liquid crystal dropping method of the present invention is 5 parts by weight, and the preferable upper limit is 80 parts by weight. If the content of the light shielding agent is less than 5 parts by weight, sufficient light shielding properties may not be obtained. When the content of the light-shielding agent exceeds 80 parts by weight, the adhesion of the obtained sealing agent for liquid crystal dropping method to the substrate and the strength after curing may be lowered, or the drawing property may be lowered. The more preferable lower limit of the content of the light shielding agent is 10 parts by weight, the more preferable upper limit is 70 parts by weight, the still more preferable lower limit is 30 parts by weight, and the still more preferable upper limit is 60 parts by weight.
本発明の液晶滴下工法用シール剤を製造する方法としては、例えば、ホモディスパー、ホモミキサー、万能ミキサー、プラネタリーミキサー、ニーダー、3本ロール等の混合機を用いて、硬化性樹脂と、光ラジカル重合開始剤と、必要に応じて添加するシランカップリング剤等の添加剤とを混合する方法等が挙げられる。 As a method for producing the sealing agent for liquid crystal dropping method of the present invention, for example, using a mixer such as a homodisper, a homomixer, a universal mixer, a planetary mixer, a kneader, or a three roll, a curable resin, a light Examples thereof include a method of mixing a radical polymerization initiator and an additive such as a silane coupling agent added as necessary.
本発明の液晶滴下工法用シール剤に、導電性微粒子を配合することにより、上下導通材料を製造することができる。このような本発明の液晶滴下工法用シール剤と導電性微粒子とを含有する上下導通材料もまた、本発明の1つである。 A vertical conduction material can be produced by blending conductive fine particles with the sealant for the liquid crystal dropping method of the present invention. Such a vertical conduction material containing the sealing agent for liquid crystal dropping method of the present invention and conductive fine particles is also one aspect of the present invention.
上記導電性微粒子としては、金属ボール、樹脂微粒子の表面に導電金属層を形成したもの等を用いることができる。なかでも、樹脂微粒子の表面に導電金属層を形成したものは、樹脂微粒子の優れた弾性により、透明基板等を損傷することなく導電接続が可能であることから好適である。 As the conductive fine particles, a metal ball, a resin fine particle formed with a conductive metal layer on the surface, or the like can be used. Among them, the one in which the conductive metal layer is formed on the surface of the resin fine particles is preferable because the conductive connection is possible without damaging the transparent substrate due to the excellent elasticity of the resin fine particles.
本発明の液晶滴下工法用シール剤又は本発明の上下導通材料を用いてなる液晶表示素子もまた、本発明の1つである。 The liquid crystal display element using the sealing agent for liquid crystal dropping method of the present invention or the vertical conduction material of the present invention is also one aspect of the present invention.
本発明の液晶表示素子を製造する方法としては、例えば、ITO薄膜等の電極付きのガラス基板やポリエチレンテレフタレート基板等の2枚の透明基板の一方に、本発明の液晶滴下工法用シール剤等をスクリーン印刷、ディスペンサー塗布等により長方形状のシールパターンを形成する工程、本発明の液晶滴下工法用シール剤等が未硬化の状態で液晶の微小滴を透明基板の枠内全面に滴下塗布し、すぐに別の基板を重ね合わせる工程、及び、本発明の液晶滴下工法用シール剤等のシールパターン部分に紫外線等の光を照射してシール剤を仮硬化させる工程、及び、仮硬化させたシール剤を加熱して本硬化させる工程を有する方法等が挙げられる。 As a method for producing the liquid crystal display element of the present invention, for example, the sealing agent for the liquid crystal dropping method of the present invention is applied to one of two transparent substrates such as a glass substrate with electrodes such as an ITO thin film or a polyethylene terephthalate substrate. The process of forming a rectangular seal pattern by screen printing, dispenser application, etc., the liquid crystal drop method sealing agent of the present invention is uncured, and liquid crystal microdrops are dropped on the entire surface of the transparent substrate and applied immediately. A step of superimposing another substrate on the substrate, a step of irradiating the seal pattern portion of the sealant for the liquid crystal dropping method of the present invention with light such as ultraviolet rays, and the step of pre-curing the sealant, and a pre-cured sealant The method etc. which have the process of heating this and making it harden | cure are mentioned.
本発明によれば、光硬化性に優れ、かつ、液晶汚染を抑制することができる液晶滴下工法用シール剤を提供することができる。また、本発明によれば、該液晶滴下工法用シール剤を用いてなる上下導通材料及び液晶表示素子を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the sealing compound for liquid crystal dropping methods which can be excellent in photocurability and can suppress liquid crystal contamination can be provided. Moreover, according to this invention, the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal dropping methods can be provided.
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されない。 Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.
(実施例1)
硬化性樹脂として、ビスフェノールA型エポキシアクリレート(ダイセル・オルネクス社製、「EBECRYL3700」、誘電率14)40重量部、及び、部分アクリル変性ビスフェノールA型エポキシ樹脂(ダイセル・オルネクス社製、「UVACURE1561」、誘電率13)20重量部と、光ラジカル重合開始剤として、下記式(2)で表される化合物(ADEKA社製、「NCI−930」)1重量部と、熱硬化剤として、アジピン酸ジヒドラジド(大塚化学社製、「ADH」)3重量部と、充填剤として、シリカ(アドマテックス社製、「アドマファインSO−C2」)15重量部、及び、タルク(日本タルク社製、「ナノエースD600」)5重量部と、シランカップリング剤として、3−グリシドキシプロピルトリメトキシシラン(信越化学工業社製、「KBM−403」)1重量部とを配合し、遊星式撹拌機(シンキー社製、「あわとり練太郎」)にて撹拌した後、セラミック3本ロールにて均一に混合して液晶滴下工法用シール剤を得た。Example 1
As curable resin, 40 parts by weight of bisphenol A type epoxy acrylate (manufactured by Daicel Ornex Co., Ltd., “EBECRYL3700”, dielectric constant 14), and partially acrylic modified bisphenol A type epoxy resin (manufactured by Daicel Ornex Co., Ltd., “UVACURE 1561”) Dielectric constant 13) 20 parts by weight, 1 part by weight of a compound represented by the following formula (2) (made by ADEKA, “NCI-930”) as a radical photopolymerization initiator, and adipic acid dihydrazide as a thermosetting agent 3 parts by weight (manufactured by Otsuka Chemical Co., Ltd., “ADH”), 15 parts by weight of silica (manufactured by Admatechs, “Admafine SO-C2”) as a filler, and talc (manufactured by Nippon Talc, “Nanoace D600” ") 5 parts by weight, and 3-glycidoxypropyltrimethoxy as a silane coupling agent After blending 1 part by weight of silane (manufactured by Shin-Etsu Chemical Co., Ltd., “KBM-403”) and stirring with a planetary stirrer (manufactured by Shinky Co., Ltd. “Netaro Awatori”), with three ceramic rolls It mixed uniformly and the sealing compound for liquid crystal dropping methods was obtained.
(参考例2、実施例3〜11、比較例1〜5)
表1、2に記載された配合比に従い、各材料を、実施例1と同様にして、遊星式撹拌機(シンキー社製、「あわとり練太郎」)を用いて混合した後、更に3本ロールを用いて混合することにより参考例2、実施例3〜11、比較例1〜5の液晶滴下工法用シール剤を調製した。
なお、表1、2中に記載した、「式(3)で表される化合物」は、下記式(3)で表される化合物であり、「式(4)で表される化合物」は、下記式(4)で表される化合物である。
( Reference Example 2, Examples 3 to 11, Comparative Examples 1 to 5)
According to the blending ratios described in Tables 1 and 2, each material was mixed using a planetary stirrer (manufactured by Shinky Co., Ltd., “Awatori Netaro”) in the same manner as in Example 1, and then 3 more The sealing agent for liquid crystal dropping methods of Reference Example 2, Examples 3 to 11, and Comparative Examples 1 to 5 was prepared by mixing using a roll.
The “compound represented by the formula (3)” described in Tables 1 and 2 is a compound represented by the following formula (3), and the “compound represented by the formula (4)” It is a compound represented by following formula (4).
なお、表1、2中の部分アクリル変性フェノールノボラック型エポキシ樹脂は、以下の方法により調製した。
即ち、フェノールノボラック型エポキシ樹脂(DIC社製、「N−770」)190gをトルエン500mLに溶解させ、この溶液にトリフェニルホスフィン0.1gを加え、均一な溶液とした。得られた溶液にアクリル酸35gを還流撹拌下にて2時間かけて滴下した後、更に還流撹拌を6時間行った。トルエンを除去することによって、フェノールノボラック型エポキシ樹脂の50モル%のエポキシ基がアクリル基に変性した部分アクリル変性フェノールノボラック型エポキシ樹脂(誘電率9)を得た。In addition, the partial acrylic modified phenol novolac type epoxy resins in Tables 1 and 2 were prepared by the following method.
That is, 190 g of phenol novolac type epoxy resin (manufactured by DIC, “N-770”) was dissolved in 500 mL of toluene, and 0.1 g of triphenylphosphine was added to the solution to obtain a uniform solution. After 35 g of acrylic acid was added dropwise to the obtained solution under reflux stirring over 2 hours, the mixture was further stirred under reflux for 6 hours. By removing toluene, a partially acrylic-modified phenol novolac epoxy resin (dielectric constant 9) in which 50 mol% of the epoxy group of the phenol novolac epoxy resin was modified to an acrylic group was obtained.
<評価>
実施例、参考例、及び、比較例で得られた各液晶滴下工法用シール剤について以下の評価を行った。結果を表1、2に示した。
<Evaluation>
The following evaluation was performed about each sealing agent for liquid crystal dropping methods obtained by the Example , the reference example, and the comparative example. The results are shown in Tables 1 and 2.
(光硬化性)
実施例、参考例、及び、比較例で得られた各液晶滴下工法用シール剤をガラス基板上に約5μm塗布し、その基板に同サイズのガラス基板を重ね合わせ、次に、メタルハライドランプを用いて100mW/cm2の光を10秒照射した。なお、照射装置とガラス基板との間に380nm以下の波長をカットする基板を挿入した。赤外分光装置(BIORAD社製、「FTS3000」)を用い、アクリロイル基由来ピークの光照射前後での変化量を測定することで光硬化性の評価を行った。光照射後のアクリロイル基由来のピークの減少率が93%以上であった場合を「◎」、85%以上93%未満であった場合を「○」、75%以上85%未満であった場合を「△」、75%未満であった場合を「×」として光硬化性を評価した。
(Photo-curing)
Examples, reference examples, and the respective liquid crystal dropping process sealant obtained in Comparative Example for about 5μm coated on a glass substrate, superposing the glass substrates of the same size on the substrate, then, using a metal halide lamp 100 mW / cm 2 of light was irradiated for 10 seconds. A substrate that cuts a wavelength of 380 nm or less was inserted between the irradiation device and the glass substrate. Photocurability was evaluated by measuring the amount of change in the acryloyl group-derived peak before and after light irradiation using an infrared spectroscope (BIORAD, “FTS3000”). When the rate of decrease in the peak derived from the acryloyl group after light irradiation is 93% or more, “「 ”, when it is 85% or more and less than 93%,“ ◯ ”, when it is 75% or more and less than 85% Was evaluated as “Δ”, and the case where it was less than 75% was evaluated as “×”.
(液晶汚染性)
実施例、参考例、及び、比較例で得られた各液晶滴下工法用シール剤100重量部にスペーサ微粒子(積水化学工業社製、「ミクロパールSI−H050」)1重量部を分散させ、2枚のラビング済み配向膜及び透明電極付き基板の一方にシール剤の線幅が1mmになるようにディスペンサーで塗布した。続いて液晶(チッソ社製、「JC−5004LA」)の微小滴を透明電極付き基板のシール剤の枠内全面に滴下塗布し、すぐにもう一方の透明電極付き基板を貼り合わせ、シール剤部分にメタルハライドランプを用いて100mW/cm2の紫外線を30秒照射してシール剤を硬化させ、更に、120℃で1時間加熱して液晶表示素子を得た。
得られた液晶表示素子について、作製直後、シール剤付近の液晶配向乱れを光学顕微鏡観察によって確認した。液晶配向乱れは表示部の色むらより判断しており、色むらの程度に応じて、色むらが全くなかった場合を「◎」、色むらが微かにあった場合を「○」、色むらが少しあった場合を「△」、色むらがかなりあった場合を「×」として液晶汚染性を評価した。
なお、評価が「◎」、「○」の液晶表示素子は実用に全く問題のないレベルであり、「△」は液晶表示素子の表示設計によって問題になる可能性があるレベルであり、「×」は実用に耐えないレベルである。
(Liquid crystal contamination)
Examples, reference examples, and the spacer particles (Sekisui Chemical Co., Ltd., "Micro Pearl SI-H050") to 100 parts by weight of the liquid crystal dropping process sealant obtained in Comparative Example was dispersed with 1 part by weight, 2 It applied with the dispenser so that the line | wire width of a sealing agent might be set to 1 mm to one of the board | substrate with a rubbing alignment film and a transparent electrode. Subsequently, liquid droplets (manufactured by Chisso Corporation, "JC-5004LA") are dropped onto the entire surface of the sealing agent frame of the substrate with the transparent electrode, and the other substrate with the transparent electrode is immediately pasted together. A metal halide lamp was used to irradiate 100 mW / cm 2 of ultraviolet rays for 30 seconds to cure the sealant, and further heated at 120 ° C. for 1 hour to obtain a liquid crystal display element.
About the obtained liquid crystal display element, immediately after preparation, liquid crystal alignment disorder near the sealant was confirmed by observation with an optical microscope. The liquid crystal alignment disorder is judged from the color unevenness of the display part. Depending on the degree of the color unevenness, “◎” indicates that there is no color unevenness, “○” indicates that the color unevenness is slight, and “color unevenness”. The liquid crystal contamination property was evaluated as “△” when there was a slight amount of color, and “X” when there was considerable color unevenness.
In addition, the liquid crystal display elements with the evaluations “◎” and “O” are at a level where there is no problem in practical use, and “Δ” is a level at which the display design of the liquid crystal display element may cause a problem. "Is a level that can not be put into practical use.
本発明によれば、光硬化性に優れ、かつ、液晶汚染を抑制することができる液晶滴下工法用シール剤を提供することができる。また、本発明によれば、該液晶滴下工法用シール剤を用いてなる上下導通材料及び液晶表示素子を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the sealing compound for liquid crystal dropping methods which can be excellent in photocurability and can suppress liquid crystal contamination can be provided. Moreover, according to this invention, the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal dropping methods can be provided.
Claims (10)
前記硬化性樹脂中における誘電率が10以上の硬化性樹脂の含有割合が100重量%であり、
前記光ラジカル重合開始剤は、極性基を有するオキシムエステル化合物である
ことを特徴とする液晶滴下工法用シール剤。 A liquid crystal dropping method sealing agent containing a curable resin and a radical photopolymerization initiator,
The content of the dielectric constant is 10 or more curable resin in the curable resin is 100% by weight,
The said radical photopolymerization initiator is an oxime ester compound which has a polar group, The sealing compound for liquid crystal dropping methods characterized by the above-mentioned.