JP6391882B1 - Sealant for liquid crystal display element, vertical conduction material, and liquid crystal display element - Google Patents

Abstract

An object of the present invention is to provide a sealant for a liquid crystal display element that can maintain excellent adhesion even when substrate deformation is repeated and can obtain a cured product having excellent impact resistance. To do. Another object of the present invention is to provide a vertical conduction material and a liquid crystal display element using the sealing agent for a liquid crystal display element. The present invention is a sealing agent for liquid crystal display elements containing a curable resin and a polymerization initiator and / or a thermosetting agent, the storage elastic modulus of the cured product at 25 ° C. is 2.0 GPa or less, and It is a sealing agent for liquid crystal display elements whose loss elastic modulus in 25 degreeC of hardened | cured material is 0.1 GPa or more and 1.0 GPa or less.

Description

The present invention relates to a sealant for a liquid crystal display element that can maintain excellent adhesiveness even when substrate deformation is repeated and can obtain a cured product having excellent impact resistance. Moreover, this invention relates to the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal display elements.

In recent years, as a method for manufacturing a liquid crystal display element, a curable resin, a photopolymerization initiator, and a heat as disclosed in Patent Document 1 and Patent Document 2 from the viewpoint of shortening tact time and optimizing the amount of liquid crystal used. A liquid crystal dropping method called a dropping method using a photothermal combined curing type sealing agent containing a curing agent is used.

In the dropping method, first, a rectangular seal pattern is formed on one of two transparent substrates with electrodes by dispensing. Next, a liquid crystal micro-droplet is dropped on the entire surface of the transparent substrate frame in a state where the sealant is uncured, and the other transparent substrate is immediately overlaid, and the seal portion is irradiated with light such as ultraviolet rays for temporary curing. . Thereafter, heating is performed to perform main curing, and a liquid crystal display element is manufactured. A liquid crystal display element can be manufactured with extremely high efficiency by bonding the substrates under a reduced pressure, and this dropping method is currently the mainstream method for manufacturing liquid crystal display elements.

Conventionally, a glass substrate has been mainly used as a substrate for a liquid crystal display element, but in recent years, a flexible substrate using polyethylene terephthalate, polycarbonate, polyimide, etc. as a substrate used for a curved display formed by bending a panel. Is attracting attention. However, the conventional sealing agent has a problem that when the substrate is repeatedly deformed, the sealing agent cannot follow the deformation and display failure occurs in the liquid crystal display element.

JP 2001-133794 A JP-A-5-295087

An object of the present invention is to provide a sealant for a liquid crystal display element that can maintain excellent adhesion even when substrate deformation is repeated and can obtain a cured product having excellent impact resistance. To do. Another object of the present invention is to provide a vertical conduction material and a liquid crystal display element using the sealing agent for a liquid crystal display element.

The present invention is a sealing agent for liquid crystal display elements containing a curable resin and a polymerization initiator and / or a thermosetting agent, the storage elastic modulus of the cured product at 25 ° C. is 2.0 GPa or less, and It is a sealing agent for liquid crystal display elements whose loss elastic modulus in 25 degreeC of hardened | cured material is 0.1 GPa or more and 1.0 GPa or less.
The present invention is described in detail below.

The present inventor has studied to lower the storage elastic modulus in order to improve the bending resistance of the cured product of the sealant for liquid crystal display elements. However, if the storage elastic modulus is simply lowered, peeling or deformation may occur when the substrate deformation is repeated, or the impact resistance may be inferior. Then, this inventor examined making the loss elastic modulus in 25 degreeC of hardened | cured material into a specific range in addition to the storage elastic modulus in 25 degreeC of hardened | cured material. As a result, it has been found that a sealing agent for a liquid crystal display element can be obtained, which can maintain excellent adhesion even when substrate deformation is repeated and can obtain a cured product having excellent impact resistance. The invention has been completed.

By setting the storage elastic modulus at 25 ° C. and the loss elastic modulus at 25 ° C. in the cured product of the sealant for liquid crystal display elements of the present invention to a specific range, the cured product is excellent even when the substrate deformation is repeated. The reason why the adhesiveness can be maintained and the impact resistance is excellent is as follows. That is, in order to maintain an excellent adhesive force even when the substrate is repeatedly deformed, it is necessary to facilitate the deformation of the cured product and to prevent the plastic deformation from occurring. And a low loss elastic modulus is preferable. Moreover, in order to be excellent in impact resistance, the shape of the test piece must be restored in addition to being easy to deform, so the storage elastic modulus is low and a certain loss or more is required. It preferably has an elastic modulus. From these things, it is thought that such an effect is exhibited by making the storage elastic modulus at 25 ° C. and the loss elastic modulus at 25 ° C. into specific ranges, respectively.

As for the sealing compound for liquid crystal display elements of this invention, the upper limit of the storage elastic modulus in 25 degreeC of hardened | cured material is 2.0 GPa. The storage elastic modulus at 25 ° C. of the cured product is within this range, and the loss elastic modulus at 25 ° C. of the cured product is 0.1 GPa or more and 1.0 GPa or less, whereby the sealing agent for liquid crystal display elements of the present invention is used. Can maintain excellent adhesion even when the substrate is repeatedly deformed, and a cured product having excellent impact resistance can be obtained. The preferable upper limit of the storage elastic modulus at 25 ° C. of the cured product is 1.9 GPa, the more preferable upper limit is 1.8 GPa, and the further preferable upper limit is 1.5 GPa.
Further, from the viewpoint of adhesiveness when the adherends are bonded together, a preferable lower limit of the storage elastic modulus at 25 ° C. of the cured product is 1 MPa, a more preferable lower limit is 0.01 GPa, and a further preferable lower limit is 1.1 GPa. .
The cured product for measuring the storage elastic modulus and the loss elastic modulus described later was irradiated with 100 mW / cm ² ultraviolet rays (wavelength 365 nm) for 30 seconds using a metal halide lamp as a sealant, and then at 120 ° C. What was hardened by heating for 1 hour is used. Moreover, this hardened | cured material means the sealing agent hardened | cured material used for bonding and sealing of a board | substrate etc. in a liquid crystal display element.
In addition, the storage elastic modulus and the loss elastic modulus described later are measured using a dynamic viscoelasticity measuring device (for example, “DVA-200” manufactured by IT Measurement Control Co., Ltd.), a tensile mode, a test piece width of 5 mm, and a thickness of 0. .35 mm, grip width 25 mm, temperature rising rate 10 ° C./min, frequency 10 Hz.

In the sealing agent for liquid crystal display elements of the present invention, the lower limit of the loss elastic modulus at 25 ° C. of the cured product is 0.1 GPa, and the upper limit is 1.0 GPa. The loss elastic modulus at 25 ° C. of the cured product is within this range, and the storage elastic modulus of the cured product at 25 ° C. is 2.0 GPa or less, whereby the sealing agent for a liquid crystal display element of the present invention is deformed on the substrate. Even when is repeated, excellent adhesion can be maintained, and the impact resistance is also excellent. The preferable lower limit of the loss elastic modulus at 25 ° C. of the cured product is 0.2 GPa, the preferable upper limit is 0.8 GPa, the more preferable upper limit is 0.7 GPa, and the further preferable upper limit is 0.3 GPa.

The sealing agent for liquid crystal display elements of this invention contains curable resin, a polymerization initiator, and / or a thermosetting agent.
In the sealing agent for liquid crystal display elements of the present invention, the cured product has a storage elastic modulus at 25 ° C. of 2.0 GPa or less, and the cured product has a loss elastic modulus at 25 ° C. of 0.1 GPa or more and 1.0 GPa or less. Examples of the curable resin include a method of using a compound having a polymerizable functional group and a rubber structure as the curable resin, a method of blending rubber particles in a sealing agent, and the like. Among these, a method using a compound having the polymerizable functional group and a rubber structure is preferable.
In this specification, the compound having a rubber structure is a vulcanized rubber obtained by adding sulfur to raw rubber, a synthetic rubber obtained by addition polymerization and having a double bond in the molecular main chain, or a peroxide on polymethylsiloxane. Means a compound having rubber elasticity, such as silicone rubber crosslinked with The compound having the rubber structure has a low storage elastic modulus and can be easily deformed, but has a high internal stress, and thus has a feature that the shape is easily restored. The compound having the rubber structure in a curable resin It is possible to individually adjust the storage elastic modulus and the loss elastic modulus by blending an appropriate amount.

Examples of the polymerizable functional group possessed by the compound having a polymerizable functional group and a rubber structure include a (meth) acryloyl group and an epoxy group. Of these, a (meth) acryloyl group is preferable. Moreover, it is preferable that the compound which has the said polymeric functional group and rubber structure has 2 or more of the said polymeric functional groups in 1 molecule.
In the present specification, the “(meth) acryloyl” means acryloyl or methacryloyl.

The rubber structure of the compound having a polymerizable functional group and a rubber structure is preferably a structure having an unsaturated bond in the main chain or a structure having a polysiloxane skeleton in the main chain.
Examples of the structure having an unsaturated bond in the main chain include a structure having a skeleton formed by polymerization of a conjugated diene in the main chain.
Examples of the skeleton obtained by polymerization of the conjugated diene include a polybutadiene skeleton, a polyisoprene skeleton, a styrene-butadiene skeleton, a polyisobutylene skeleton, and a polychloroprene skeleton. Among these, the rubber structure is more preferably a structure having a polybutadiene skeleton, a polyisoprene skeleton, or a polysiloxane skeleton.

The preferable lower limit of the molecular weight of the compound having a polymerizable functional group and a rubber structure is 500, and the preferable upper limit is 50,000. When the molecular weight of the compound having the polymerizable functional group and the rubber structure is within this range, the obtained sealing agent for liquid crystal display elements is excellent in the bending resistance of the cured product. The minimum with more preferable molecular weight of the compound which has the said polymeric functional group and rubber structure is 1000, and a more preferable upper limit is 30000.
In the present specification, the “molecular weight” is a molecular weight obtained from the structural formula for a compound whose molecular structure is specified, but for a compound having a wide distribution of polymerization degree and a compound whose modification site is unspecified, Sometimes expressed using weight average molecular weight. The “weight average molecular weight” is a value determined by polystyrene conversion after measurement using tetrahydrofuran as a solvent by gel permeation chromatography (GPC). As a column used when measuring the weight average molecular weight by polystyrene conversion by GPC, Shodex LF-804 (made by Showa Denko KK) etc. are mentioned, for example.

Specific examples of the compound having a polymerizable functional group and a rubber structure include a terminal amino group-containing butadiene-acrylonitrile (ATBN) -modified epoxy (meth) acrylate and a terminal carboxyl group-containing butadiene-acrylonitrile (CTBN) -modified epoxy. (Meth) acrylate, (meth) acryl modified isoprene rubber, (meth) acryl modified butadiene rubber, (meth) acryl modified silicone rubber, terminal amino group-containing butadiene-acrylonitrile (ATBN) modified epoxy resin, isoprene modified epoxy resin, butadiene modified Examples include epoxy resins, terminal carboxyl group-containing polybutadiene-acrylonitrile (CTBN) -modified epoxy resins, butadiene-modified urethane acrylates, and the like. The compound having a polymerizable functional group and a rubber structure may be used alone or in combination of two or more.

The minimum with preferable content of the compound which has the said polymerizable functional group and rubber structure in 100 weight part of said curable resin whole is 20 weight part, and a preferable upper limit is 75 weight part. When the content of the compound having a polymerizable functional group and a rubber structure is within this range, the storage elastic modulus and the loss elastic modulus at 25 ° C. of the cured product of the obtained sealing agent for liquid crystal display elements are the ranges described above, respectively. It becomes easy to do. A more preferable lower limit of the content of the compound having a polymerizable functional group and a rubber structure is 30 parts by weight, a more preferable upper limit is 70 parts by weight, and a still more preferable lower limit is 51 parts by weight.

The curable resin is used for the purpose of adjusting the storage elastic modulus and loss elastic modulus at 25 ° C. of the cured product, and further improving the adhesion and low liquid crystal contamination when the adherend is bonded. It is preferable to contain a curable resin other than the compound having the polymerizable functional group and the rubber structure. As said other curable resin, other epoxy compounds other than the compound which has the said polymeric functional group and rubber structure, and another (meth) acryl compound are used suitably.
In the present specification, the “(meth) acryl” means acryl or methacryl, and the “(meth) acryl compound” means a compound having a (meth) acryloyl group.

Examples of the other epoxy compounds include bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol E type epoxy resin, bisphenol S type epoxy resin, 2,2′-diallyl bisphenol A type epoxy resin, and hydrogenated bisphenol type. Epoxy resin, propylene oxide-added bisphenol A type epoxy resin, resorcinol type epoxy resin, biphenyl type epoxy resin, sulfide type epoxy resin, diphenyl ether type epoxy resin, dicyclopentadiene type epoxy resin, naphthalene type epoxy resin, phenol novolac type epoxy resin, Orthocresol novolac epoxy resin, dicyclopentadiene novolac epoxy resin, biphenyl novolac epoxy resin, naphthalene phenol Novolak type epoxy resins, glycidyl amine type epoxy resin, alkyl polyol type epoxy resins, glycidyl ester compounds.

As what is marketed among the said bisphenol A type epoxy resins, jER828EL, jER1004 (all are the Mitsubishi Chemical company make), Epiklon 850CRP (made by DIC company), etc. are mentioned, for example.
As what is marketed among the said bisphenol F-type epoxy resins, jER806, jER4004 (all are the Mitsubishi Chemical company make) etc. are mentioned, for example.
As what is marketed among the said bisphenol E-type epoxy resins, R710 (made by Printec Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said bisphenol S-type epoxy resins, Epicron EXA1514 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said 2,2'- diallyl bisphenol A type epoxy resins, RE-810NM (made by Nippon Kayaku Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said hydrogenated bisphenol type | mold epoxy resins, Epicron EXA7015 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said propylene oxide addition bisphenol A type epoxy resins, EP-4000S (made by ADEKA) etc. are mentioned, for example.
As what is marketed among the said resorcinol type epoxy resins, EX-201 (made by Nagase ChemteX Corporation) etc. are mentioned, for example.
As what is marketed among the said biphenyl type epoxy resins, jER YX-4000H (made by Mitsubishi Chemical Corporation) etc. are mentioned, for example.
As what is marketed among the said sulfide type epoxy resins, YSLV-50TE (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said diphenyl ether type epoxy resins, YSLV-80DE (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said dicyclopentadiene type epoxy resins, EP-4088S (made by ADEKA) etc. are mentioned, for example.
As what is marketed among the said naphthalene type | mold epoxy resins, Epicron HP4032, Epicron EXA-4700 (all are the products made from DIC) etc. are mentioned, for example.
As what is marketed among the said phenol novolak-type epoxy resins, Epicron N-770 (made by DIC Corporation) etc. are mentioned, for example.
As what is marketed among the said ortho cresol novolak-type epoxy resins, Epicron N-670-EXP-S (made by DIC) etc. are mentioned, for example.
As what is marketed among the said dicyclopentadiene novolak-type epoxy resins, epiclone HP7200 (made by DIC) etc. are mentioned, for example.
As what is marketed among the said biphenyl novolak-type epoxy resins, NC-3000P (made by Nippon Kayaku Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said naphthalene phenol novolak-type epoxy resins, ESN-165S (made by Nippon Steel & Sumikin Chemical Co., Ltd.) etc. are mentioned, for example.
As what is marketed among the said glycidyl amine type epoxy resins, jER630 (made by Mitsubishi Chemical Corporation), Epicron 430 (made by DIC Corporation), TETRAD-X (made by Mitsubishi Gas Chemical Co., Inc.) etc. are mentioned, for example.
Examples of commercially available alkyl polyol type epoxy resins include ZX-1542 (manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.), Epiklon 726 (manufactured by DIC Corporation), Epolite 80MFA (manufactured by Kyoeisha Chemical Co., Ltd.), Denacol EX-611. (Manufactured by Nagase ChemteX Corporation).
As what is marketed among the said glycidyl ester compounds, Denacol EX-147 (made by Nagase ChemteX Corporation) etc. is mentioned, for example.
Other commercially available epoxy compounds include, for example, YDC-1312, YSLV-80XY, YSLV-90CR (all manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.), XAC4151 (manufactured by Asahi Kasei Co., Ltd.), jER1031, jER1032 (any And Mitsubishi Chemical Corporation), EXA-7120 (DIC Corporation), TEPIC (Nissan Chemical Corporation), and the like.

Moreover, the said curable resin may contain the compound which has an epoxy group and a (meth) acryloyl group in 1 molecule as said other epoxy compound. Examples of such a compound include a partial (meth) acryl-modified epoxy resin obtained by reacting a part of an epoxy group having two or more epoxy groups with (meth) acrylic acid.

Examples of commercially available partial (meth) acrylic-modified epoxy resins include UVACURE1561 and KRM8287 (both manufactured by Daicel Ornex).

Examples of the other (meth) acrylic compounds include epoxy (meth) acrylates, (meth) acrylic acid ester compounds, urethane (meth) acrylates, and the like. Of these, epoxy (meth) acrylate is preferable. The other (meth) acrylic compounds are preferably those having two or more (meth) acryloyl groups in the molecule because of their high reactivity.
In the present specification, the “(meth) acrylate” means acrylate or methacrylate, and the “epoxy (meth) acrylate” means that all epoxy groups in the epoxy compound react with (meth) acrylic acid. Represents the compound.

Examples of the epoxy (meth) acrylate include those obtained by reacting an epoxy compound and (meth) acrylic acid in the presence of a basic catalyst according to a conventional method.

As an epoxy compound used as a raw material for synthesize | combining the said epoxy (meth) acrylate, the thing similar to the other epoxy compound mentioned above is mentioned.

Examples of commercially available epoxy (meth) acrylates include, for example, an epoxy (meth) acrylate manufactured by Daicel Ornex, an epoxy (meth) acrylate manufactured by Shin-Nakamura Chemical Co., Ltd., and an epoxy ( Examples include (meth) acrylate and epoxy (meth) acrylate manufactured by Nagase ChemteX Corporation.
Examples of the epoxy (meth) acrylates manufactured by Daicel Ornex Co., Ltd. include EBECRYL860, EBECRYL3200, EBECRYL3201, EBECRYL3412, EBECRYL3600, EBECRYL3700, EBECRYL3701, EBECRY3370, EBECRYL3702,
Examples of the epoxy (meth) acrylate manufactured by Shin-Nakamura Chemical Co., Ltd. include EA-1010, EA-1020, EA-5323, EA-5520, EA-CHD, EMA-1020, and the like.
Examples of the epoxy (meth) acrylate manufactured by Kyoeisha Chemical Co., Ltd. include epoxy ester M-600A, epoxy ester 40EM, epoxy ester 70PA, epoxy ester 200PA, epoxy ester 80MFA, epoxy ester 3002M, epoxy ester 3002A, epoxy ester 1600A, Epoxy ester 3000M, epoxy ester 3000A, epoxy ester 200EA, epoxy ester 400EA, and the like can be given.
Examples of the epoxy (meth) acrylate manufactured by Nagase ChemteX include Denacol acrylate DA-141, Denacol acrylate DA-314, Denacol acrylate DA-911, and the like.

Among the above (meth) acrylic acid ester compounds, as monofunctional ones, for example, methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth) acrylate , T-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, n-octyl (meth) acrylate, isooctyl (meth) acrylate, isononyl (meth) acrylate, isodecyl (meth) acrylate, lauryl (meth) acrylate, iso Myristyl (meth) acrylate, stearyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, 4-hydroxy Til (meth) acrylate, cyclohexyl (meth) acrylate, isobornyl (meth) acrylate, bicyclopentenyl (meth) acrylate, benzyl (meth) acrylate, 2-methoxyethyl (meth) acrylate, 2-ethoxyethyl (meth) acrylate, 2 -Butoxyethyl (meth) acrylate, 2-phenoxyethyl (meth) acrylate, methoxyethylene glycol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, phenoxydiethylene glycol (meth) acrylate, phenoxypolyethylene glycol (meth) acrylate, tetrahydrofur Furyl (meth) acrylate, ethyl carbitol (meth) acrylate, 2,2,2-trifluoroethyl (meth) acrylate 2,2,3,3-tetrafluoropropyl (meth) acrylate, 1H, 1H, 5H-octafluoropentyl (meth) acrylate, imide (meth) acrylate, dimethylaminoethyl (meth) acrylate, diethylaminoethyl (meth) ) Acrylate, 2- (meth) acryloyloxyethyl succinic acid, 2- (meth) acryloyloxyethyl hexahydrophthalic acid, 2- (meth) acryloyloxyethyl 2-hydroxypropyl phthalate, 2- (meth) acrylic Examples include leuoxyethyl phosphate and glycidyl (meth) acrylate.

Moreover, as a bifunctional thing among the said (meth) acrylic acid ester compounds, for example, 1,3-butanediol di (meth) acrylate, 1,4-butanediol di (meth) acrylate, 1,6-hexane Diol di (meth) acrylate, 1,9-nonanediol di (meth) acrylate, 1,10-decanediol di (meth) acrylate, ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, tetraethylene glycol di (Meth) acrylate, polyethylene glycol di (meth) acrylate, 2-n-butyl-2-ethyl-1,3-propanediol di (meth) acrylate, dipropylene glycol di (meth) acrylate, tripropylene glycol di (meth) ) Acrylate, poly Lopylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, ethylene oxide-added bisphenol A di (meth) acrylate, propylene oxide-added bisphenol A di (meth) acrylate, ethylene oxide-added bisphenol F di (meth) acrylate, dimethylol Dicyclopentadienyl di (meth) acrylate, ethylene oxide modified isocyanuric acid di (meth) acrylate, 2-hydroxy-3- (meth) acryloyloxypropyl (meth) acrylate, carbonate diol di (meth) acrylate, polyether diol Di (meth) acrylate, polyester diol di (meth) acrylate, polycaprolactone diol di (meth) acrylate, polybutadiene diol (Meth) acrylate.

Further, among the above (meth) acrylic acid ester compounds, those having three or more functions include, for example, trimethylolpropane tri (meth) acrylate, ethylene oxide-added trimethylolpropane tri (meth) acrylate, propylene oxide-added trimethylolpropane tri ( (Meth) acrylate, caprolactone-modified trimethylolpropane tri (meth) acrylate, ethylene oxide-added isocyanuric acid tri (meth) acrylate, glycerin tri (meth) acrylate, propylene oxide-added glycerin tri (meth) acrylate, pentaerythritol tri (meth) acrylate, Tris (meth) acryloyloxyethyl phosphate, ditrimethylolpropane tetra (meth) acrylate, pentaerythritol tetra Meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate.

The urethane (meth) acrylate is obtained, for example, by reacting 2 equivalents of a (meth) acrylic acid derivative having a hydroxyl group with 1 equivalent of an isocyanate compound having two isocyanate groups in the presence of a catalytic amount of a tin-based compound. be able to.

Examples of the isocyanate compound include isophorone diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, diphenylmethane-4,4′-diisocyanate (MDI), and hydrogenation. MDI, polymeric MDI, 1,5-naphthalene diisocyanate, norbornane diisocyanate, tolidine diisocyanate, xylylene diisocyanate (XDI), hydrogenated XDI, lysine diisocyanate, triphenylmethane triisocyanate, tris (isocyanatophenyl) thiophosphate, tetramethylxylylene diene An isocyanate, 1,6,11-undecane triisocyanate etc. are mentioned.

As the isocyanate compound, a chain-extended isocyanate compound obtained by a reaction between a polyol and an excess of an isocyanate compound can also be used.
Examples of the polyol include ethylene glycol, propylene glycol, glycerin, sorbitol, trimethylolpropane, carbonate diol, polyether diol, polyester diol, and polycaprolactone diol.

Examples of the (meth) acrylic acid derivative having a hydroxyl group include hydroxyalkyl mono (meth) acrylate, mono (meth) acrylate of divalent alcohol, mono (meth) acrylate or di (meth) acrylate of trivalent alcohol. And epoxy (meth) acrylate.
Examples of the hydroxyalkyl mono (meth) acrylate include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, and 4-hydroxybutyl (meth) acrylate. Can be mentioned.
Examples of the divalent alcohol include ethylene glycol, propylene glycol, 1,3-propanediol, 1,3-butanediol, 1,4-butanediol, polyethylene glycol, and the like.
Examples of the trivalent alcohol include trimethylolethane, trimethylolpropane, and glycerin.
Examples of the epoxy (meth) acrylate include bisphenol A type epoxy acrylate.

Examples of commercially available urethane (meth) acrylates include, for example, urethane (meth) acrylate manufactured by Toagosei Co., Ltd., urethane (meth) acrylate manufactured by Daicel Ornex, and urethane (meth) manufactured by Negami Kogyo Co., Ltd. Examples thereof include acrylate, urethane (meth) acrylate manufactured by Shin-Nakamura Chemical Co., Ltd., urethane (meth) acrylate manufactured by Kyoeisha Chemical Co., Ltd., and the like.
Examples of the urethane (meth) acrylate manufactured by Toagosei Co., Ltd. include M-1100, M-1200, M-1210, and M-1600.
The urethane (meth) acrylate manufactured by the Daicel Orunekusu Inc., for example, EBECRYL210, EBECRYL220, EBECRYL230, EBECRYL270, EBECRYL1290, EBECRYL2220, EBECRYL4827, EBECRYL4842, EBECRYL4858, EBECRYL5129, EBECRYL6700, EBECRYL8402, EBECRYL8803, EBECRYL8804, EBECRYL8807, EBECRYL9260 etc. Can be mentioned.
Examples of the urethane (meth) acrylate manufactured by Negami Kogyo Co., Ltd. include Art Resin UN-330, Art Resin SH-500B, Art Resin UN-1200TPK, Art Resin UN-1255, Art Resin UN-3320HB, Art Resin UN- 7100, Art Resin UN-9000A, Art Resin UN-9000H, and the like.
Examples of the urethane (meth) acrylate manufactured by Shin-Nakamura Chemical Co., Ltd. include U-2HA, U-2PHA, U-3HA, U-4HA, U-6H, U-6HA, U-6LPA, U-10H, U-15HA, U-108, U-108A, U-122A, U-122P, U-324A, U-340A, U-340P, U-1084A, U-2061BA, UA-340P, UA-4000, UA- 4100, UA-4200, UA-4400, UA-5201P, UA-7100, UA-7200, UA-W2A, and the like.
Examples of the urethane (meth) acrylate manufactured by Kyoeisha Chemical Co., Ltd. include AH-600, AI-600, AT-600, UA-101I, UA-101T, UA-306H, UA-306I, and UA-306T. It is done.

The said curable resin may be used independently and 2 or more types may be used in combination.

In the sealing agent for liquid crystal display elements of the present invention, the content ratio of (meth) acryloyl groups in the total of (meth) acryloyl groups and epoxy groups in the curable resin may be 50 mol% or more and 95 mol% or less. preferable.

Examples of the rubber particles include silicone rubber particles, butadiene rubber particles, isoprene rubber particles, nitrile rubber particles, styrene rubber particles, and acrylic rubber particles. Among these, at least one selected from the group consisting of silicone rubber particles, butadiene rubber particles, and isoprene rubber particles is preferable.

The preferable lower limit of the average particle diameter of the rubber particles is 0.1 μm, and the preferable upper limit is 5 μm. When the average particle diameter of the rubber particles is within this range, it becomes easy to set the storage elastic modulus and loss elastic modulus at 25 ° C. of the obtained cured product of the sealing agent for liquid crystal display elements to the ranges described above. The more preferable lower limit of the average particle diameter of the rubber particles is 0.5 μm, and the more preferable upper limit is 3 μm.
In the present specification, the average particle diameter of the rubber particles means a value obtained by measuring with a laser diffraction particle size distribution measuring device for the particles before blending with the sealant. As the laser diffraction particle size distribution measuring device, Mastersizer 2000 (manufactured by Malvern) or the like can be used. Further, the average particle diameter of the rubber particles means an average value of the particle diameters of 10 particles observed at a magnification of 10,000 times using a scanning electron microscope for the particles contained in the sealant. As the scanning electron microscope, a field emission scanning electron microscope S-4800 (manufactured by Hitachi High-Technologies Corporation) or the like can be used.

The preferable lower limit of the content of the rubber particles in 100 parts by weight of the sealant for liquid crystal display elements of the present invention is 10 parts by weight, and the preferable upper limit is 70 parts by weight. When the content of the rubber particles is within this range, the storage elastic modulus and loss elastic modulus at 25 ° C. of the cured product of the obtained sealant for liquid crystal display elements can be easily set within the ranges described above. A more preferable lower limit of the content of the rubber particles is 20 parts by weight, and a more preferable upper limit is 50 parts by weight.

The sealing agent for liquid crystal display elements of this invention contains a polymerization initiator and / or a thermosetting agent.
Examples of the polymerization initiator include radical polymerization initiators and cationic polymerization initiators.

Examples of the radical polymerization initiator include a thermal radical polymerization initiator that generates radicals by heating, a photo radical polymerization initiator that generates radicals by light irradiation, and the like.

Examples of the photo radical polymerization initiator include benzophenone compounds, acetophenone compounds, acylphosphine oxide compounds, titanocene compounds, oxime ester compounds, benzoin ether compounds, thioxanthones, and the like.

As what is marketed among the said radical photopolymerization initiators, the radical photopolymerization initiator by BASF, the radical photopolymerization initiator by Tokyo Chemical Industry, etc. are mentioned, for example.
Examples of the photo radical polymerization initiators manufactured by BASF include IRGACURE 184, IRGACURE 369, IRGACURE 379, IRGACURE 651, IRGACURE 819, IRGACURE 907, IRGACURE 2959, IRGACURE OXE01, and Lucillin TPO.
Examples of the photo radical polymerization initiator manufactured by Tokyo Chemical Industry Co., Ltd. include benzoin methyl ether, benzoin ethyl ether, and benzoin isopropyl ether.
These radical photopolymerization initiators may be used alone or in combination of two or more.

As said thermal radical polymerization initiator, what consists of an azo compound, an organic peroxide, etc. is mentioned, for example. Among these, a polymer azo initiator composed of a polymer azo compound is preferable.
In the present specification, the polymer azo compound means a compound having an azo group and generating a radical capable of curing a (meth) acryloyloxy group by heat and having a number average molecular weight of 300 or more.

The preferable lower limit of the number average molecular weight of the polymer azo compound is 1000, and the preferable upper limit is 300,000. When the number average molecular weight of the polymer azo compound is within this range, it can be easily mixed into the curable resin while preventing adverse effects on the liquid crystal. The more preferable lower limit of the number average molecular weight of the polymer azo compound is 5000, the more preferable upper limit is 100,000, the still more preferable lower limit is 10,000, and the still more preferable upper limit is 90,000.
In addition, in this specification, the said number average molecular weight is a value calculated | required by polystyrene conversion, measuring using tetrahydrofuran as a solvent by gel permeation chromatography (GPC). Examples of the column for measuring the number average molecular weight in terms of polystyrene by GPC include Shodex LF-804 (manufactured by Showa Denko KK).

Examples of the polymer azo compound include those having a structure in which a plurality of units such as polyalkylene oxide and polydimethylsiloxane are bonded via an azo group.
As the polymer azo compound having a structure in which a plurality of units such as polyalkylene oxide are bonded via the azo group, those having a polyethylene oxide structure are preferable.
Specific examples of the polymer azo compound include polycondensates of 4,4′-azobis (4-cyanopentanoic acid) and polyalkylene glycol, and 4,4′-azobis (4-cyanopentanoic acid). And a polycondensate of polydimethylsiloxane having a terminal amino group.
Examples of commercially available polymer azo compounds include VPE-0201, VPE-0401, VPE-0601, VPS-0501, and VPS-1001 (all manufactured by Wako Pure Chemical Industries, Ltd.). .
Moreover, as what is marketed as an azo compound which is not a polymer | macromolecule, V-65, V-501 (all are Wako Pure Chemical Industries Ltd. make) etc. are mentioned, for example.

Examples of the organic peroxide include ketone peroxide, peroxyketal, hydroperoxide, dialkyl peroxide, peroxyester, diacyl peroxide, and peroxydicarbonate.

As the cationic polymerization initiator, a photocationic polymerization initiator can be suitably used. The cationic photopolymerization initiator is not particularly limited as long as it generates a protonic acid or a Lewis acid by light irradiation, and may be of an ionic photoacid generation type or a nonionic photoacid generation type. It may be.
Examples of the photocationic polymerization initiator include onium salts such as aromatic diazonium salts, aromatic halonium salts, and aromatic sulfonium salts, organometallic complexes such as iron-allene complexes, titanocene complexes, and arylsilanol-aluminum complexes. Is mentioned.

Examples of commercially available photocationic polymerization initiators include Adekaoptomer SP-150 and Adekaoptomer SP-170 (both manufactured by ADEKA).

The said polymerization initiator may be used independently and 2 or more types may be used in combination.

The content of the polymerization initiator is preferably 0.1 parts by weight and preferably 30 parts by weight with respect to 100 parts by weight of the curable resin. When the content of the polymerization initiator is 0.1 parts by weight or more, the obtained sealing agent for liquid crystal display elements is more excellent in curability. When the content of the polymerization initiator is 30 parts by weight or less, the obtained sealing agent for liquid crystal display elements is more excellent in storage stability. A more preferable lower limit of the content of the polymerization initiator is 1 part by weight, a more preferable upper limit is 10 parts by weight, and a still more preferable upper limit is 5 parts by weight.

Examples of the thermosetting agent include organic acid hydrazides, imidazole derivatives, amine compounds, polyhydric phenol compounds, acid anhydrides, and the like. Among these, solid organic acid hydrazide is preferably used.

Examples of the solid organic acid hydrazide include 1,3-bis (hydrazinocarboethyl) -5-isopropylhydantoin, sebacic acid dihydrazide, isophthalic acid dihydrazide, adipic acid dihydrazide, malonic acid dihydrazide, and the like.
Examples of commercially available solid organic acid hydrazides include organic acid hydrazides manufactured by Otsuka Chemical Co., Ltd., organic acid hydrazides manufactured by Nippon Finechem Co., Ltd., organic acid hydrazides manufactured by Ajinomoto Fine Techno Co., and the like.
Examples of the organic acid hydrazide manufactured by Otsuka Chemical Co., Ltd. include SDH and ADH.
Examples of the organic acid hydrazide manufactured by Nippon Finechem Co., Ltd. include MDH.
Examples of the organic acid hydrazide manufactured by Ajinomoto Fine Techno Co. include Amicure VDH, Amicure VDH-J, Amicure UDH, and the like.

The said thermosetting agent may be used independently and 2 or more types may be used in combination.

The content of the thermosetting agent is preferably 1 part by weight with respect to 100 parts by weight of the curable resin, and 50 parts by weight with respect to the preferable upper limit. When the content of the thermosetting agent is 1 part by weight or more, the obtained sealing agent for liquid crystal display elements is more excellent in thermosetting. When the content of the thermosetting agent is 50 parts by weight or less, the obtained sealing agent for liquid crystal display elements is more excellent in applicability. The upper limit with more preferable content of the said thermosetting agent is 30 weight part.

The sealing agent for liquid crystal display elements of the present invention may contain a filler for the purpose of improving the viscosity, further improving the adhesion due to the stress dispersion effect, improving the linear expansion coefficient, improving the moisture resistance of the cured product, and the like. preferable.

As the filler, an inorganic filler or an organic filler can be used.
Examples of the inorganic filler include silica, talc, glass beads, asbestos, gypsum, diatomaceous earth, smectite, bentonite, montmorillonite, sericite, activated clay, alumina, zinc oxide, iron oxide, magnesium oxide, tin oxide, and titanium oxide. , Calcium carbonate, magnesium carbonate, magnesium hydroxide, aluminum hydroxide, aluminum nitride, silicon nitride, barium sulfate, calcium silicate and the like.
Examples of the organic filler include polyester fine particles, polyurethane fine particles, vinyl polymer fine particles, and acrylic polymer fine particles.

The preferable lower limit of the content of the filler in 100 parts by weight of the sealant for liquid crystal display elements of the present invention is 10 parts by weight, and the preferable upper limit is 70 parts by weight. When content of the said filler is this range, effects, such as an adhesive improvement, can be exhibited more, suppressing deterioration, such as applicability | paintability. The minimum with more preferable content of the said filler is 20 weight part, and a more preferable upper limit is 60 weight part.

The sealing agent for liquid crystal display elements of the present invention preferably contains a silane coupling agent for the purpose of further improving the adhesiveness. The silane coupling agent mainly has a role as an adhesion assistant for favorably bonding the sealing agent and the substrate.
As the silane coupling agent, for example, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane and the like are preferably used.

The minimum with preferable content of the said silane coupling agent in 100 weight part of sealing agents for liquid crystal display elements of this invention is 0.1 weight part, and a preferable upper limit is 20 weight part. When the content of the silane coupling agent is within this range, the effect of improving the adhesiveness can be further exhibited while suppressing the occurrence of liquid crystal contamination. The minimum with more preferable content of the said silane coupling agent is 0.5 weight part, and a more preferable upper limit is 10 weight part.

The sealing agent for liquid crystal display elements of the present invention may contain a light shielding agent. By containing the said light shielding agent, the sealing compound for liquid crystal display elements of this invention can be used suitably as a light shielding sealing agent.

Examples of the light-shielding agent include iron oxide, titanium black, aniline black, cyanine black, fullerene, carbon black, and resin-coated carbon black. Of these, titanium black is preferable.

Titanium black is a substance having higher transmittance for light in the vicinity of the ultraviolet region, particularly for light with a wavelength of 370 nm to 450 nm, compared to the average transmittance for light with a wavelength of 300 nm to 800 nm. That is, the above-described titanium black sufficiently shields light having a wavelength in the visible light region, thereby providing a light shielding property to the sealing agent for liquid crystal display elements of the present invention, while transmitting light having a wavelength in the vicinity of the ultraviolet region. A shading agent. The light shielding agent contained in the liquid crystal display element sealant of the present invention is preferably a highly insulating material, and titanium black is also preferred as the highly insulating light shielding agent.

The above-mentioned titanium black exhibits a sufficient effect even if it is not surface-treated, but the surface is treated with an organic component such as a coupling agent, silicon oxide, titanium oxide, germanium oxide, aluminum oxide, oxidized Surface-treated titanium black such as those coated with an inorganic component such as zirconium or magnesium oxide can also be used. Especially, what is processed with the organic component is preferable at the point which can improve insulation more.
In addition, the liquid crystal display element produced using the sealing agent for liquid crystal display elements of the present invention containing the above-described titanium black as a light-shielding agent has a sufficient light-shielding property, and thus has high contrast without light leakage. A liquid crystal display element having excellent image display quality can be realized.

Examples of commercially available titanium black include titanium black manufactured by Mitsubishi Materials Corporation and titanium black manufactured by Ako Kasei Co., Ltd.
Examples of the titanium black manufactured by Mitsubishi Materials Corporation include 12S, 13M, 13M-C, 13R-N, and 14M-C.
Examples of the titanium black manufactured by Ako Kasei Co., Ltd. include Tilac D.

The preferable lower limit of the specific surface area of the titanium black is 13 m ² / g, the preferable upper limit is 30 m ² / g, the more preferable lower limit is 15 m ² / g, and the more preferable upper limit is 25 m ² / g.
Further, the preferred lower limit of the volume resistance of the titanium black is 0.5 Ω · cm, the preferred upper limit is 3 Ω · cm, the more preferred lower limit is 1 Ω · cm, and the more preferred upper limit is 2.5 Ω · cm.

The primary particle diameter of the light-shielding agent is not particularly limited as long as it is not more than the distance between the substrates of the liquid crystal display element, but the preferred lower limit is 1 nm and the preferred upper limit is 5 μm. When the primary particle diameter of the light-shielding agent is within this range, the viscosity and thixotropy of the obtained sealing agent for liquid crystal display elements are not greatly increased, and the coating property is excellent. The more preferable lower limit of the primary particle diameter of the light shielding agent is 5 nm, the more preferable upper limit is 200 nm, the still more preferable lower limit is 10 nm, and the still more preferable upper limit is 100 nm.
The primary particle size of the light-shielding agent can be measured using a particle size distribution meter (for example, “NICOMP 380ZLS” manufactured by PARTICLE SIZING SYSTEMS).

The preferable lower limit of the content of the light-shielding agent in 100 parts by weight of the sealant for liquid crystal display elements of the present invention is 5 parts by weight, and the preferable upper limit is 80 parts by weight. When the content of the light-shielding agent is within this range, the effect of improving the light-shielding property is exhibited without lowering the adhesiveness, strength after curing, and drawing property of the obtained sealing agent for liquid crystal display elements. it can. The more preferable lower limit of the content of the light shielding agent is 10 parts by weight, the more preferable upper limit is 70 parts by weight, the still more preferable lower limit is 30 parts by weight, and the still more preferable upper limit is 60 parts by weight.

The sealing agent for liquid crystal display elements of the present invention is further added with a stress relaxation agent, reactive diluent, thixotropic agent, spacer, curing accelerator, antifoaming agent, leveling agent, polymerization inhibitor, etc., if necessary. An agent may be contained.

As a method for producing the sealing agent for liquid crystal display elements of the present invention, for example, using a mixer such as a homodisper, a homomixer, a universal mixer, a planetary mixer, a kneader, a three roll, a curable resin, and a polymerization Examples thereof include a method of mixing an initiator and / or a thermosetting agent and an additive such as a silane coupling agent added as necessary.

A vertical conducting material can be produced by blending conductive fine particles with the liquid crystal display element sealant of the present invention. Such a vertical conduction material containing the sealing agent for liquid crystal display elements of the present invention and conductive fine particles is also one aspect of the present invention.

As the conductive fine particles, a metal ball, a resin fine particle formed with a conductive metal layer on the surface, or the like can be used. Among them, the one in which the conductive metal layer is formed on the surface of the resin fine particles is preferable because the conductive connection is possible without damaging the transparent substrate due to the excellent elasticity of the resin fine particles.

The liquid crystal display element using the sealing agent for liquid crystal display elements of this invention or the vertical conduction material of this invention is also one of this invention.

The sealing agent for liquid crystal display elements of this invention can be used suitably for manufacture of the liquid crystal display element by a liquid crystal dropping method.
Examples of the method for producing the liquid crystal display element of the present invention by the liquid crystal dropping method include the following methods.
First, a step of forming a rectangular seal pattern on the substrate by screen printing, dispenser application, or the like with the sealing agent for liquid crystal display elements of the present invention is performed. Next, the liquid crystal display element sealant or the like of the present invention is applied in an uncured state by applying liquid crystal microdroplets onto the entire surface of the transparent substrate and immediately stacking another substrate. Thereafter, a step of irradiating the seal pattern portion of the sealant for the liquid crystal display element of the present invention with light such as ultraviolet rays to temporarily cure the sealant, and a step of heating and temporarily curing the temporarily cured sealant A liquid crystal display element can be obtained by performing the method.

As the substrate, a flexible substrate is suitable.
Examples of the flexible substrate include plastic substrates using polyethylene terephthalate, polyester, poly (meth) acrylate, polycarbonate, polyether sulfone, polyimide, and the like. Moreover, the sealing compound for liquid crystal display elements of this invention may be used when adhere | attaching a normal glass substrate.
The substrate is usually formed with a transparent electrode made of indium oxide or the like, an alignment film made of polyimide or the like, an inorganic ion shielding film, or the like.

According to the present invention, it is possible to provide a sealing agent for a liquid crystal display element capable of maintaining excellent adhesiveness even when substrate deformation is repeated and obtaining a cured product having excellent impact resistance. it can. Moreover, according to this invention, the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal display elements can be provided.

Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.

(Synthesis Example 1)
In a reaction flask, 15 parts by weight of a terminal amino group-containing butadiene-acrylonitrile copolymer (manufactured by Ube Industries, "ATBN 1300X16") and 60 parts by weight of bisphenol A type epoxy acrylate (manufactured by Daicel Ornex, "EBECRYL3700") I put it in. Next, the mixture in the reaction flask was reacted by stirring at 120 ° C. for 3 hours to obtain a terminal amino group-containing butadiene-acrylonitrile (ATBN) -modified epoxy acrylate as a compound having a polymerizable functional group and a rubber structure.

(Synthesis Example 2)
In a reaction flask, 3550 parts by weight of a terminal carboxyl group-containing butadiene-acrylonitrile copolymer (UBE Industries, “CTBN1300X8”), 400 parts by weight of 4-hydroxybutyl acrylate glycidyl ether (Nippon Kasei), and a polymerization inhibitor 10 parts by weight of p-methoxyphenol and 10 parts by weight of triethylamine were added as a reaction catalyst. Next, the mixture in the reaction flask is reacted by refluxing and stirring at 110 ° C. for 5 hours while feeding air into the reaction flask, whereby a terminal carboxyl group-containing butadiene-acrylonitrile (as a compound having a polymerizable functional group and a rubber structure) CTBN) modified epoxy acrylate was obtained.

(Synthesis Example 3)
A reaction flask was charged with 72 parts by weight of acrylic acid, 312 parts by weight of bisphenol F diglycidyl ether, 0.3 parts by weight of p-methoxyphenol as a polymerization inhibitor, and 0.3 parts by weight of triethylamine as a reaction catalyst. Subsequently, the partially acrylic modified bisphenol F type epoxy resin was obtained by making it react for 5 hours, heating at 90 degreeC with a mantle heater, and making the mixture in a reaction flask react.

(Examples 1 to 10 and Comparative Examples 1 to 4)
After mixing each material of the compounding ratio described in Tables 1 and 2 using a planetary stirrer (manufactured by Shinky Co., Ltd., “Awatori Nertaro”), by further mixing using three rolls, The sealing agents for liquid crystal display elements of Examples 1 to 10 and Comparative Examples 1 to 4 were prepared.
About each obtained sealing compound for liquid crystal display elements, after irradiating 100 mW / cm < ² > of ultraviolet rays (wavelength 365nm) for 30 seconds using a metal halide lamp, it heated at 120 degreeC for 1 hour, and hardened | cured material was obtained. About the obtained hardened | cured material, using a dynamic viscoelasticity measuring apparatus (IT measurement control company make, "DVA-200"), test piece width 5mm, thickness 0.35mm, grip width 25mm, temperature increase rate 10 degreeC / Storage elastic modulus and loss elastic modulus were measured under the condition of a partial frequency of 10 Hz. Tables 1 and 2 show the storage elastic modulus and loss elastic modulus at 25 ° C. of each cured product.

<Evaluation>
The following evaluation was performed about each sealing compound for liquid crystal display elements obtained by the Example and the comparative example. The results are shown in Tables 1 and 2.

(One-side bending test)
Each sealant for liquid crystal display elements obtained in the examples and comparative examples was irradiated with 100 mW / cm ² ultraviolet rays (wavelength 365 nm) for 30 seconds using a metal halide lamp, and then heated at 120 ° C. for 1 hour to a thickness of 300 μm. A film was prepared as a test piece. Each of the obtained test pieces was wound around a SUS rod having a diameter of 30 mm, and the state of each test piece when it was fixed with an adhesive tape (“Cloth Tape 601S” manufactured by Sekisui Chemical Co., Ltd.) was visually observed.
As a result, when the peeling between the test piece and the adhesive tape was not confirmed, “◯”, when the peeling was confirmed on the test piece, but the adhesive tape was partially fixed, “△”, the test piece In addition, the case where peeling was confirmed on the adhesive tape was evaluated as “×”. In this test, since it is better that the test piece is easily deformed, a lower storage elastic modulus is advantageous.

(Left / right bending test)
About five test pieces produced in the same manner as the above “(one-side bending test)”, the test pieces were bent 90 degrees along an arc of a roll having a diameter about 10 times the long side of the test piece, and then returned to a flat shape. Next, after bending 90 degrees in the opposite direction and returning to a flat state for 10 minutes at a rate of 20 times per minute, the state of each test piece was visually observed.
As a result, “◯” indicates that no deformation was observed on all five test pieces, “Δ” indicates that deformation was observed on one or more and three or less test pieces, and “△” indicates that four or more test pieces were present. The case where deformation was confirmed was evaluated as “×”. In this test, since it is necessary to prevent plastic deformation from occurring in the test piece, a lower loss elastic modulus is advantageous.

(Impact resistance test)
About five test pieces produced in the same manner as the above “(one-side bending test)”, each test piece was placed on the floor, and after dropping a 100 g weight from a height of 50 cm to each test piece, each test piece The state of was observed visually.
As a result, “◯” indicates that no cracks or cracks were observed on all five test pieces, “△” indicates that cracks or cracks were observed on one or more and three or less test pieces, and “four” or more. The case where a crack or a crack was confirmed in the test piece was evaluated as “x”. In this test, since the deformation of the test piece is easy and the shape needs to be restored after the deformation, it is advantageous that the storage elastic modulus is low and the loss elastic modulus is high.

According to the present invention, it is possible to provide a sealing agent for a liquid crystal display element capable of maintaining excellent adhesiveness even when substrate deformation is repeated and obtaining a cured product having excellent impact resistance. it can. Moreover, according to this invention, the vertical conduction material and liquid crystal display element which use this sealing compound for liquid crystal display elements can be provided.

Claims (9)

A sealing agent for a liquid crystal display element comprising a curable resin and a polymerization initiator and / or a thermosetting agent,
The storage elastic modulus at 25 ° C. of the cured product is 2.0 GPa or less, and the loss elastic modulus at 25 ° C. of the cured product is 0.1 GPa or more and 1.0 GPa or less,
The said curable resin contains the compound which has a polymerizable functional group and a rubber structure, The sealing compound for liquid crystal display elements characterized by the above-mentioned. 2. The sealant for a liquid crystal display element according to claim 1, wherein the rubber structure is a structure having an unsaturated bond in the main chain or a structure having a polysiloxane skeleton in the main chain. The sealing agent for liquid crystal display elements according to claim 1 or 2, wherein the content of the compound having a polymerizable functional group and a rubber structure in 100 parts by weight of the entire curable resin is 20 parts by weight or more and 75 parts by weight or less. The liquid crystal display element sealing agent according to claim 3, wherein the content of the compound having a polymerizable functional group and a rubber structure in 100 parts by weight of the entire curable resin is 51 parts by weight or more and 70 parts by weight or less. The said curable resin is a sealing compound for liquid crystal display elements of Claim 1, 2, 3 or 4 containing an epoxy (meth) acrylate. A sealing agent for a liquid crystal display element comprising a curable resin and a polymerization initiator and / or a thermosetting agent,
The storage elastic modulus at 25 ° C. of the cured product is 2.0 GPa or less, and the loss elastic modulus at 25 ° C. of the cured product is 0.1 GPa or more and 1.0 GPa or less,
A sealing agent for a liquid crystal display element, comprising rubber particles. The sealant for a liquid crystal display element according to claim 6, wherein the rubber particles are at least one selected from the group consisting of silicone rubber particles, butadiene rubber particles, and isoprene rubber particles. A vertical conduction material containing a sealing agent for liquid crystal display elements and conductive fine particles,
The liquid crystal display element sealant contains a curable resin and a polymerization initiator and / or a thermosetting agent, and a cured product of the liquid crystal display element sealant has a storage elastic modulus at 25 ° C. of 2.0 GPa or less. There, and vertically conducting material loss elastic modulus at 25 ° C. of the cured product characterized by the following der Turkey 1.0GPa least 0.1 GPa. A liquid crystal display element using the sealing agent for a liquid crystal display element according to claim 1, 2, 3, 4, 5, 6 or 7, or the vertical conduction material according to claim 8.