JP6346173B2 - 遮光に適したモノフィラメントネット - Google Patents
遮光に適したモノフィラメントネット Download PDFInfo
- Publication number
- JP6346173B2 JP6346173B2 JP2015513784A JP2015513784A JP6346173B2 JP 6346173 B2 JP6346173 B2 JP 6346173B2 JP 2015513784 A JP2015513784 A JP 2015513784A JP 2015513784 A JP2015513784 A JP 2015513784A JP 6346173 B2 JP6346173 B2 JP 6346173B2
- Authority
- JP
- Japan
- Prior art keywords
- net
- sheath
- ratio
- fineness
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1. 繊度100〜1000dtexの鞘芯型熱接着性複合モノフィラメントを経糸および緯糸として密に織編されたネットであって、経糸と緯糸の繊度は同一ではなく、経糸と緯糸の繊度比は、太繊度のフィラメント基準で0.6以下であり、経糸および緯糸の打ち込み本数比は一定の範囲になるよう織編されており、且つ経糸と緯糸の交点が熱接着されているネット。
ビス(2,2’,6,6’−テトラメチル−4−ピペリジル)セバケート、テトラキス(2,2,6,6−テトラメチル−4−ピペリジル)−1,2,3,4−ブタンテトラカルボキシレート、コハク酸ジメチル・1−(2−ヒドロキシエチル)−4−ヒドロキシ−2,2,6,6−テトラメチルピペリジン重縮合物等のヒンダードアミン系の化合物。2,4−ジヒドロキシベンゾフェノン、2−ヒドロキシ−4−メトキシベンゾフェノン、2−ヒドロキシ−4−オクトキシベンゾフェノン、2−ヒドロキシ−4−ドデシロキシベンゾフェノン等のベンゾフェノン系の化合物。2(2’−ヒドロキシ−5−メチルフェニル)ベンゾトリアゾール、2(2’−ヒドロキシ−3’−t−ブチル−5’−メチルフェニル)−5−クロロベンゾトリアゾール等のベンゾトリアゾール系、2,4−ジ−t−ブチル−フェニル−3,5−ジ−t−ブチル−4−ヒドロキシベンゾエート等のベンゾエート系等の各種紫外線吸収剤やラジカル捕捉剤等の耐光剤。
塩素系または臭素系のハロゲン化合物、酸化アンチモンのような無機系難燃剤、1,1,3,3,5,5−ヘキサ(メトキシ)シクロトリホスファゼンのような環状ホスファゼン化合物、または1,1,3,3,5,5−ヘキサ(メトキシ)トリホスファゼンのような鎖状ホスファゼン化合物。
20cm×30cmの大きさのネットを用意した。これを窓ガラスにテープで固定した。窓から2m離れた位置から室内および室外の様子を観察し、隠蔽効果を評価した。評価は下記5段階の目視による官能法で行い、5人の評価結果の平均値で表した。なお評価は春季の晴天時に行なった。また、室内灯を点灯し、外からでも室内がよく見えることを事前に確認した。全てのサンプルは同日に評価した。
1点:ネット越しの様子がよく見える
2点:ネット越しの様子がやや見え、何があるかもうっすら分かる
3点:ネット越しの様子がやや見えるが、注視しないと分からない
4点:ネット越しの様子がやや見えるが、何があるかまでは分からない
5点:ネット越しの様子が全く見えない
(隠蔽効果の評価)
(室外から室内を観察した結果の点数)−(室内から室外を観察した結果の点数)が、
1以上のとき:隠蔽効果あり
1未満のとき:隠蔽効果なし
と判定した。
JIS K 7375に従って実施した。遮光率を全光透過率から下記の式より求めた。
遮光率(%)=100−全光線透過率(%)
遮熱効果の評価は、一般財団法人建材試験センターに依頼し、試験体の日射吸収率を測定した。この結果をもとに、試験体を室外に設置した場合の、厚さ3mmの板ガラスと試験体との組み合わせによる構成体(図3参照)の日射熱取得率および遮蔽係数を算出した。試験体、構成体の作製は、建材試験センターにて行なった。なお、図3に記載の中空層であるが、遮蔽係数算出時に使用する値は、実際の厚みではなく、試験体とフロート板ガラスの間の熱抵抗の値(0.052(m2・K)/W)となる。よって、中空層の厚みは、遮蔽係数の算出に影響を与えない。
日射吸収率は、試験体に入射する日射のうち、試験体に吸収される割合を示すものであり、JIS R 3106に従って測定した。日射域の波長範囲は、300〜2500nmである。試験体から切り出した寸法50mm×50mmの試験片を用いて測定した。なお、測定値は上述したように日射熱取得率および遮蔽係数の測定(算出)の基礎になるものであるため、単純に数値の大小の議論は難しいが、概ね40%以上であることが好ましく、50%以上がより好ましいと考えられる。よって、40%以上あれば利用可能と判断した。
日射熱取得率は、試験片を通過し室内へ流入する日射熱の割合であり、JIS R 3106に準拠して測定し、計算式により算出して求めた。ここで、室内へ流入する日射熱とは、試験片を透過する日射の熱と、試験片に吸収されて室内側に伝達される熱との和である。
厚さ3mmの板ガラスの日射透過率=0.856
厚さ3mmの板ガラスの日射反射率=0.077
板ガラス面の修正放射率=0.842
試験体と板ガラスの間の中空層の熱抵抗=0.052[(m2・K)/W]
室外側表面熱伝達抵抗=0.057[(m2・K)/W]
遮蔽係数は、試験片を通過し室内へ流入する日射熱の割合であり、厚さ3mmのフロート板ガラスの値との比で表わす。数値は0〜1の間の値となり、その値が小さいほど遮蔽性能が高いことを示す。また、厚さ3mmのフロート板ガラスの遮蔽係数は1となる。ここで、室内へ流入する日射熱とは、試験片を透過する日射の熱と、試験片に吸収されて室内側に伝達される熱との和である。
鞘成分が融点138℃のエチレン・プロピレン・ブテン−1コポリマ−、芯成分が融点171℃のポリプロピレンを用い、鞘芯比が鞘:芯=50:50、繊度が320dtexの複合モノフィラメント(繊維A)、繊度が550dtexの複合モノフィラメント(繊維B)、繊度が220dtexの複合モノフィラメント(繊維C)、繊度が250dtexの複合モノフィラメント(繊維D)、繊度が890dtexの複合モノフィラメント(繊維E)を得た。鞘芯比は共通とした。
鞘成分が融点133℃の高密度ポリエチレン、芯成分が融点169℃のポリプロピレンを用い、鞘芯比が鞘:芯=60:40、繊度が320dtexの複合モノフィラメント(繊維H)と、鞘芯比が鞘:芯=40:60、繊度が550dtexの複合モノフィラメント(繊維I)を得た。
鞘成分が融点168℃のポリプロピレン、芯成分が融点254℃のポリエチレンテレフタレートを用い、鞘芯比が鞘:芯=30:70、繊度が320dtexの複合モノフィラメント(繊維J)と、繊度が550dtexの複合モノフィラメント(繊維K)を得た。鞘芯比は共通とした。
得られた繊維A〜Jを用いて、表1に示す構成のネットを織編し、各々繊維交点が熱接着できる温度で熱処理して評価用のネットを得た。
Claims (4)
- 繊度100〜1000dtexの鞘芯型熱接着性複合モノフィラメントを経糸および緯糸として密に織編されたネットであって、経糸と緯糸の繊度は同一ではなく、経糸と緯糸の繊度比は、太繊度のフィラメント基準で0.6以下であり、経糸および緯糸の打ち込み本数比は1インチあたりの経糸および緯糸の打ち込み本数比が、少ない方の打ち込み本数基準で1.6〜2.6の範囲で密に織編されており、且つ経糸と緯糸の交点が熱接着され、遮光率が60%以上であるネット。
- 鞘芯型熱接着性複合モノフィラメントが、融点差15℃以上の低融点熱可塑性樹脂と高融点熱可塑性樹脂からなり、鞘芯比が重量比で鞘:芯=20:80〜60:40の範囲である、請求項1に記載のネット。
- 鞘芯型熱接着性複合モノフィラメントの繊度比が、太繊度のフィラメント基準で0.2〜0.6の範囲である、請求項1または2に記載のネット。
- 請求項1〜3の何れか1項に記載のネットを使用した物品。