JP6236899B2 - Ground conditioner - Google Patents
Ground conditioner Download PDFInfo
- Publication number
- JP6236899B2 JP6236899B2 JP2013124271A JP2013124271A JP6236899B2 JP 6236899 B2 JP6236899 B2 JP 6236899B2 JP 2013124271 A JP2013124271 A JP 2013124271A JP 2013124271 A JP2013124271 A JP 2013124271A JP 6236899 B2 JP6236899 B2 JP 6236899B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- less
- particles
- particle diameter
- fine aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、一般建築物の屋上やルーフバルコニー等の下地表面に防水シート等の防水層を施工する際、その下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することが可能なアスファルト系下地調整材に関する。 When constructing a waterproof layer such as a waterproof sheet on the base surface of a general building rooftop or roof balcony, etc., the present invention easily adjusts the base surface to be flat and smooth, and constructs the waterproof layer thereon. The present invention relates to an asphalt base material that can be used.
特許文献１にはアルミナセメント、石膏および高炉スラグを含む水硬性成分とアスファルト、減水剤および増粘剤とを含む下地調整材が開示されており、広範囲の温度領域において、下地調整材として十分な流動性と流動保持時間を保持して施工作業性に優れているのみならず、施工翌日の開放が可能な早期開放性を有することが示されている。 Patent Document 1 discloses a ground conditioner containing a hydraulic component including alumina cement, gypsum, and blast furnace slag, and asphalt, a water reducing agent, and a thickener, and is sufficient as a ground conditioner in a wide temperature range. It is shown that not only the workability is excellent by maintaining the fluidity and the fluid retention time, but also has an early opening property that can be opened the day after construction.
特許文献２にはアルミナセメントを含む水硬性成分とハイドロジェンポリシロキサンシリコーンオイルを含む水硬性組成物、とゴムアスファルトエマルションを混合した防水性を有する下地調整材が開示されており、長期貯蔵安定性を有するために、ゴムアスファルトエマルジョンと混合して、硬化時間及び流動性が安定し、十分な仮防水性を有し、水和硬化速度が速く、作業性及び施工性が安定していることが示されている。 Patent Document 2 discloses a water-resistant base preparation that has a hydraulic composition containing alumina cement and a hydraulic composition containing hydrogenpolysiloxane silicone oil, and a rubber asphalt emulsion, and has long-term storage stability. Therefore, it must be mixed with a rubber asphalt emulsion, the curing time and fluidity are stable, it has sufficient temporary waterproofing, the hydration curing speed is fast, and the workability and workability are stable. It is shown.
しかしながら、アスファルト系下地調整材を構成する改質アスファルトエマルジョンと、水硬性成分を含む水硬性組成物と、を均質に混合する際の混ざり易さ（混和性）が温度条件等により変化することにより混和性が低下し、アスファルト系下地調整材にて建築物の下地表面を平坦及び平滑に調整することが困難となる場合もあることから、温度等の施工環境条件の変化に依存しない安定した混和性を有するアスファルト系下地調整材が求められている。また、下地や防水層との一体化をより向上するための温度依存性の小さい寸法安定性（膨張及び収縮の小さい長さ変化率）を有するアスファルト系下地調整材が求められている。 However, the ease of mixing (miscibility) when homogeneously mixing the modified asphalt emulsion constituting the asphalt-based base material and the hydraulic composition containing the hydraulic component varies depending on the temperature condition, etc. Stable admixture that does not depend on changes in construction conditions such as temperature, as miscibility may be reduced, and it may be difficult to adjust the surface of a building to be flat and smooth with an asphalt base conditioner. There is a demand for an asphalt-based base material having a property. There is also a need for an asphalt base conditioner having dimensional stability with low temperature dependency (length change rate with small expansion and contraction) for further improving the integration with the base and waterproof layer.
そこで、本発明は、一般建築物の屋上やルーフバルコニー等の下地表面に防水シート等の防水層を施工する際、その下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することが可能であり、また、下地調整材を構成する改質アスファルトエマルジョンと水硬性組成物との混和性に優れたアスファルト系下地調整材を提供することを目的とする。さらに、下地や防水層との一体化をより向上するための温度依存性の小さい優れた寸法安定性を有するアスファルト系下地調整材を提供することを目的とする。 Therefore, the present invention, when constructing a waterproof layer such as a waterproof sheet on the foundation surface of a general building rooftop or roof balcony, etc., easily adjust the foundation surface to flat and smooth, and install the waterproof layer thereon In addition, an object of the present invention is to provide an asphalt-based base material that is excellent in miscibility between the modified asphalt emulsion constituting the base material and the hydraulic composition. Furthermore, it aims at providing the asphalt type | system | group base preparation material which has the outstanding dimensional stability with small temperature dependence for improving integration with a foundation | substrate and a waterproof layer more.
上記目的を達成するために鋭意検討した結果、本発明者らは、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分と、特定の無機充填材と、細骨材とを含む水硬性組成物、及び改質アスファルトエマルジョンを含む下地調整材を用いることによって、一般建築物の屋上やルーフバルコニー等の下地表面に防水シート等の防水層を施工する際、その下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することが可能であり、また、下地調整材を構成する改質アスファルトエマルジョンと水硬性組成物とを容易に均質に混合できる良好な混和性を有し、さらに下地や防水層との一体化をより向上するための温度依存性の小さい優れた寸法安定性を有する下地調整材が得られることを見出し、本発明を完成するに至った。 As a result of intensive studies to achieve the above object, the present inventors have obtained a hydraulic composition comprising a hydraulic component composed of alumina cement, Portland cement and gypsum, a specific inorganic filler, and fine aggregate, And by using a ground conditioner containing modified asphalt emulsion, when constructing a waterproof layer such as a waterproof sheet on the ground surface of a general building rooftop or roof balcony, the ground surface is easily adjusted to be flat and smooth. It is possible to apply a waterproof layer thereon, and it has good miscibility so that the modified asphalt emulsion constituting the base material and the hydraulic composition can be easily and uniformly mixed. It was found that a substrate adjusting material having excellent dimensional stability with small temperature dependence for further improving the integration with the substrate and the waterproof layer was obtained, and the present invention was completed. It was.
すなわち、本発明は、水硬性組成物及び改質アスファルトエマルジョンを含む下地調整材であって、水硬性組成物は、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分、無機充填材、及び細骨材を含み、無機充填材は炭酸カルシウム微粉末であり、炭酸カルシウム微粉末は、炭酸カルシウム微粉末全体を基準として、粒子径６００μｍ以上の粒子を含まず、粒子径が３００μｍ以上であり且つ６００μｍ未満である粒子の質量割合が５質量％以下であり、粒子径が１５０μｍ以上であり且つ３００μｍ未満である粒子の質量割合が０．５〜１５質量％であり、粒子径が７５μｍ以上であり且つ１５０μｍ未満である粒子の質量割合が５〜４０質量％であり、７５μｍ未満である粒子の質量割合が５０〜９０質量％であり、細骨材は、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下である下地調整材を提供する。 That is, the present invention is a ground preparation material comprising a hydraulic composition and a modified asphalt emulsion, wherein the hydraulic composition comprises a hydraulic component composed of alumina cement, Portland cement and gypsum, an inorganic filler, and fine bone. The inorganic filler is a calcium carbonate fine powder, and the calcium carbonate fine powder does not contain particles having a particle diameter of 600 μm or more, the particle diameter is 300 μm or more, and less than 600 μm, based on the whole calcium carbonate fine powder. The mass ratio of the particles is 5 mass% or less, the particle diameter is 150 μm or more and the mass ratio of the particles less than 300 μm is 0.5 to 15 mass%, the particle diameter is 75 μm or more and 150 μm. The mass ratio of particles that are less than 5 to 40 mass%, the mass ratio of particles that are less than 75 μm is 50 to 90 mass%, The material provides a base preparation material in which the mass ratio of particles having a particle diameter of less than 106 μm is 2% by mass or less based on the whole fine aggregate.
本発明の下地調整材によれば、一般建築物の屋上やルーフバルコニー等の下地表面（例えば、防水層の改修時において防水シート等が敷設されている下地表面）に防水シート等の防水層を施工する際、アスファルト系下地調整材を用いてその下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することが可能であり、また、下地調整材を構成する改質アスファルトエマルジョンと水硬性組成物とを容易に均質に混合できる良好な混和性を有し、さらに、下地や防水層との一体化をより向上するための温度依存性の小さい優れた寸法安定性を有する。このように、本発明の下地調整材において、水硬性組成物と改質アスファルトエマルジョンとの混和性が温度等に依存せず安定して良好である理由や温度依存性が小さく優れた寸法安定性を有する理由は必ずしも明らかではないが、その理由の一つとして、本発明者らは下地調整材に含まれる各成分が相互に作用するとともに、特に特定の炭酸カルシウム微粉末と特定の細骨材との組み合わせによって生じる作用が改質アスファルトエマルジョンとの混和性や下地調整材の寸法安定性の向上に寄与していると考えている。 According to the foundation conditioning material of the present invention, a waterproof layer such as a waterproof sheet is provided on the foundation surface of a general building, such as a roof balcony (for example, a foundation surface on which a waterproof sheet is laid when the waterproof layer is repaired). When constructing, it is possible to easily and evenly adjust the ground surface using an asphalt base conditioning material, and to apply a waterproof layer on it, and to modify the asphalt constituting the ground conditioning material Has good miscibility to easily and homogeneously mix the emulsion and hydraulic composition, and also has excellent dimensional stability with low temperature dependence to further improve integration with the foundation and waterproof layer . As described above, in the base preparation material of the present invention, the miscibility between the hydraulic composition and the modified asphalt emulsion is stable and good without depending on temperature, etc., and the temperature dependence is small and excellent dimensional stability. The reason for having this is not necessarily clear, but as one of the reasons, the present inventors have made it possible for each component contained in the base preparation material to interact with each other, and in particular, a specific calcium carbonate fine powder and a specific fine aggregate. It is considered that the action produced by the combination with the above contributes to the improvement of the miscibility with the modified asphalt emulsion and the dimensional stability of the base material.
本発明の下地調整材は、以下の態様であることが好ましい。本発明の下地調整材は、以下の態様を適宜組み合わせることがより好ましい。 It is preferable that the base material of the present invention has the following mode. It is more preferable that the base preparation material of the present invention is appropriately combined with the following modes.
細骨材は、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下、且つ粒子径が１５０μｍ未満である粒子の質量割合が１０質量％以下であることが好ましい。これにより、良好な混和性や優れた寸法安定性をより向上することができる。 The fine aggregate is based on the whole fine aggregate, and the mass ratio of particles having a particle diameter of less than 106 μm is 2 mass% or less, and the mass ratio of particles having a particle diameter of less than 150 μm is 10 mass% or less. Is preferred. Thereby, favorable miscibility and the outstanding dimensional stability can be improved more.
水硬性成分は、水硬性成分１００質量％中にアルミナセメント２０〜６０質量％、ポルトランドセメント２０〜６０質量％、石膏１０〜５０質量％含むことが好ましい。これにより、一層優れた混和性や寸法安定性を有する下地調整材とすることができる。 It is preferable that a hydraulic component contains 20-60 mass% of alumina cement, 20-60 mass% of Portland cement, and 10-50 mass% of gypsum in 100 mass% of hydraulic components. Thereby, it can be set as the foundation | substrate adjustment material which has the further outstanding miscibility and dimensional stability.
水硬性成分１００質量部に対して、炭酸カルシウム微粉末５０〜２００質量部、細骨材１００〜３５０質量部、改質アスファルトエマルジョン１００〜３００質量部含むことが好ましい。これにより、一層優れた混和性や寸法安定性を有する下地調整材とすることができる。 It is preferable to contain 50 to 200 parts by mass of fine calcium carbonate powder, 100 to 350 parts by mass of fine aggregate, and 100 to 300 parts by mass of the modified asphalt emulsion with respect to 100 parts by mass of the hydraulic component. Thereby, it can be set as the foundation | substrate adjustment material which has the further outstanding miscibility and dimensional stability.
改質アスファルトエマルジョンは、改質アスファルトエマルジョン１００質量％中に固形分２０〜５０質量％含むことが好ましい。これにより、一層優れた混和性や寸法安定性を有する下地調整材とすることができる。 The modified asphalt emulsion preferably contains 20 to 50% by mass of solid content in 100% by mass of the modified asphalt emulsion. Thereby, it can be set as the foundation | substrate adjustment material which has the further outstanding miscibility and dimensional stability.
本発明によれば、一般建築物の屋上やルーフバルコニー等の下地表面（例えば、防水層の改修時において防水シート等が敷設されている下地表面）に防水シート等の防水層を施工する際、アスファルト系下地調整材を用いてその下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することが可能であり、また、下地調整材を構成する改質アスファルトエマルジョンと水硬性組成物とを容易に均質に混合できる良好な混和性を有し、さらに、下地や防水層との一体化をより向上するための温度依存性の小さい優れた寸法安定性を有する下地調整材を提供することができる。 According to the present invention, when constructing a waterproof layer such as a waterproof sheet on a ground surface such as a rooftop of a general building or a roof balcony (for example, a ground surface on which a waterproof sheet or the like is laid when the waterproof layer is repaired) It is possible to easily and evenly adjust the surface of the base using an asphalt base conditioner, and to apply a waterproof layer on it. Also, the modified asphalt emulsion and hydraulic properties that make up the base conditioner A substrate adjusting material having good miscibility that can be easily and homogeneously mixed with the composition, and further having excellent dimensional stability with low temperature dependence to further improve integration with the substrate and waterproof layer. Can be provided.
＜下地調整材＞
本発明の下地調整材の好適な実施形態について以下に説明する。本実施形態の下地調整材は、一般建築物の屋上やルーフバルコニー等の下地表面に施工するアスファルト系下地調整材であり、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分と、特定の無機充填材と、細骨材とを含む水硬性組成物、及び改質アスファルトエマルジョンを含む下地調整材である。
<Ground adjustment material>
A preferred embodiment of the base material of the present invention will be described below. The foundation conditioning material of this embodiment is an asphalt-based foundation conditioning material that is constructed on the foundation surface of a general building rooftop, roof balcony, etc., and includes a hydraulic component composed of alumina cement, Portland cement, and gypsum, and a specific inorganic filler. It is the foundation | substrate conditioner containing the hydraulic composition containing a material and a fine aggregate, and a modified asphalt emulsion.
以下、本実施形態の下地調整材に含まれる各成分について詳細に説明する。 Hereinafter, each component contained in the foundation | substrate adjustment material of this embodiment is demonstrated in detail.
アルミナセメントは、鉱物組成の異なるものが数種知られ市販されているが、それらの主成分はモノカルシウムアルミネート（ＣＡ）であり、市販品はその種類によらず使用することができる。なかでも、４０００〜６０００ｃｍ２／ｇのブレーン比表面積を有するアルミナセメントを用いることが好ましい。アルミナセメントのブレーン比表面積は、ＪＩＳ Ｒ ２５２１：１９９５に準拠して求められる。 Several types of alumina cements having different mineral compositions are known and commercially available, but their main component is monocalcium aluminate (CA), and commercially available products can be used regardless of the type. Especially, it is preferable to use the alumina cement which has a Blaine specific surface area of 4000-6000 cm < 2 > / g. The brane specific surface area of the alumina cement is determined according to JIS R 2521: 1995.
ポルトランドセメントは、水硬性材料として一般的なものであり、いずれの市販品も使用することができる。これらのなかでも、ＪＩＳ Ｒ ５２１０：２００９「ポルトランドセメント」で規定されるポルトランドセメントを用いることが好ましい。 Portland cement is a common hydraulic material, and any commercially available product can be used. Among these, it is preferable to use Portland cement specified by JIS R 5210: 2009 “Portland cement”.
石膏は、例えば、二水石膏、半水石膏及び無水石膏が挙げられ、排煙脱硫やフッ酸製造工程等で副産される石膏、又は天然に産出される石膏のいずれも使用することができる。作業性の観点から、無水石膏の使用が好ましい。 Examples of gypsum include dihydrate gypsum, hemihydrate gypsum, and anhydrous gypsum, and any of gypsum produced as a by-product in flue gas desulfurization and hydrofluoric acid production processes, or gypsum produced in nature can be used. . From the viewpoint of workability, anhydrous gypsum is preferably used.
本発明では、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分を用いることにより、ポルトランドセメント単味と比べ、優れた速硬性を有する下地調整材を得ることができる。 In the present invention, by using a hydraulic component made of alumina cement, Portland cement, and gypsum, it is possible to obtain an undercoat conditioning material that has excellent rapid hardening as compared to Portland cement alone.
水硬性成分は、水硬性成分１００質量％中に、アルミナセメント２０〜６０質量％、ポルトランドセメント２０〜６０質量％、石膏１０〜５０質量％含むことが好ましく、アルミナセメント２５〜５５質量％、ポルトランドセメント２５〜５０質量％、石膏１３〜４０質量％含むことがより好ましく、アルミナセメント３０〜５０質量％、ポルトランドセメント２８〜４３質量％、石膏１６〜３４質量％含むことがさらに好ましく、アルミナセメント４０〜４８質量％、ポルトランドセメント３０〜３８質量％、石膏１８〜２６質量％含むことが特に好ましい。 The hydraulic component preferably contains 20 to 60% by mass of alumina cement, 20 to 60% by mass of Portland cement, and 10 to 50% by mass of gypsum in 100% by mass of the hydraulic component, 25 to 55% by mass of alumina cement, and Portland cement. More preferably 25 to 50% by mass, 13 to 40% by mass of gypsum, more preferably 30 to 50% by mass of alumina cement, 28 to 43% by mass of Portland cement, and 16 to 34% by mass of gypsum. It is particularly preferable to contain -48% by mass, Portland cement 30-38% by mass, and gypsum 18-26% by mass.
アルミナセメント、ポルトランドセメント及び石膏が上記範囲であることにより、ポルトランドセメント単味と比べ、優れた速硬性を有し、硬化中の体積変化が少ない下地調整材を得ることがより確実となる。 When the alumina cement, Portland cement and gypsum are in the above ranges, it is more reliable to obtain a base material that has excellent quick-curing properties and less volume change during curing compared to Portland cement alone.
無機充填材は、炭酸カルシウム微粉末であり、炭酸カルシウム微粉末全体を基準として、粒子径６００μｍ以上の粒子を含まず、粒子径が３００μｍ以上であり且つ６００μｍ未満である粒子の質量割合が５質量％以下であり、粒子径が１５０μｍ以上であり且つ３００μｍ未満である粒子の質量割合が０．５〜１５質量％であり、粒子径が７５μｍ以上であり且つ１５０μｍ未満である粒子の質量割合が５〜４０質量％であり、７５μｍ未満である粒子の質量割合が５０〜９０質量％である。また、より好ましくは、粒子径６００μｍ以上の粒子を含まず、粒子径が３００μｍ以上であり且つ６００μｍ未満である粒子の質量割合が３質量％以下であり、粒子径が１５０μｍ以上であり且つ３００μｍ未満である粒子の質量割合が２〜１２質量％であり、粒子径が７５μｍ以上であり且つ１５０μｍ未満である粒子の質量割合が１０〜３５質量％であり、７５μｍ未満である粒子の質量割合が５５〜８５質量％である。 The inorganic filler is a calcium carbonate fine powder, and based on the whole calcium carbonate fine powder, the mass ratio of the particles having a particle diameter of 300 μm or more and less than 600 μm does not include particles having a particle diameter of 600 μm or more. % Of the particles having a particle diameter of 150 μm or more and less than 300 μm is 0.5 to 15% by mass, and the particle ratio of the particles having a particle diameter of 75 μm or more and less than 150 μm is 5%. It is -40 mass%, and the mass ratio of the particle | grains which are less than 75 micrometers is 50-90 mass%. More preferably, the particles do not contain particles having a particle diameter of 600 μm or more, the particle diameter is 300 μm or more, and the mass ratio of the particles that is less than 600 μm is 3% by mass or less, the particle diameter is 150 μm or more, and less than 300 μm. The mass ratio of the particles is 2 to 12 mass%, the particle diameter is 75 μm or more and the mass ratio of the particles that is less than 150 μm is 10 to 35 mass%, and the mass ratio of the particles that is less than 75 μm is 55 mass%. It is -85 mass%.
炭酸カルシウム微粉末の粒子径が上述の範囲にあることによって、混和性や寸法安定性がより向上する。 When the particle diameter of the calcium carbonate fine powder is in the above range, the miscibility and dimensional stability are further improved.
炭酸カルシウム微粉末の粒子径は、ＪＩＳ Ｚ ８８０１：２００６「試験用ふるい−第１部：金属製網ふるい」に規定される呼び寸法の異なる数個の篩いを用いて測定することができる。また、本明細書において、「粒子径が１５０μｍ以上であり且つ３００μｍ未満である粒子の質量割合」とは、篩目３００μｍの篩いを用いたときに篩目３００μｍの篩いを通過し、且つ、篩目１５０μｍの篩を用いたとき、篩目１５０μｍの篩上に残る粒子の炭酸カルシウム微粉末全体に対する質量割合をいう。 The particle size of the calcium carbonate fine powder can be measured by using several sieves having different nominal sizes as defined in JIS Z 8801: 2006 “Test sieve—Part 1: Metal mesh sieve”. Further, in this specification, “a mass ratio of particles having a particle diameter of 150 μm or more and less than 300 μm” means that when a sieve having a sieve size of 300 μm is used, the sieve passes through a sieve having a sieve size of 300 μm, and When a sieve having a mesh size of 150 μm is used, it means the mass ratio of particles remaining on the sieve having a mesh size of 150 μm to the whole calcium carbonate fine powder.
本実施形態の下地調整材における炭酸カルシウム微粉末の含有量は、水硬性成分１００質量部に対し、好ましくは５０〜２００質量部であり、より好ましくは８０〜１８０質量部であり、さらに好ましくは１００〜１６０質量部であり、特に好ましくは１２０〜１４０質量部である。 The content of the calcium carbonate fine powder in the base preparation material of the present embodiment is preferably 50 to 200 parts by mass, more preferably 80 to 180 parts by mass, and further preferably 100 parts by mass of the hydraulic component. It is 100-160 mass parts, Most preferably, it is 120-140 mass parts.
炭酸カルシウム微粉末を、上述の好ましい範囲で含有することによって、混和性や寸法安定性がより向上する。 By containing the calcium carbonate fine powder in the above-described preferable range, miscibility and dimensional stability are further improved.
細骨材は、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下である。 In the fine aggregate, the mass ratio of particles having a particle diameter of less than 106 μm is 2% by mass or less based on the whole fine aggregate.
また、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下、且つ粒子径が１５０μｍ未満である粒子の質量割合が１０質量％以下であることが好ましく、粒子径が１０６μｍ未満である粒子の質量割合が１質量％以下、且つ粒子径が１５０μｍ未満である粒子の質量割合が５質量％以下であることがより好ましい。 Further, based on the whole fine aggregate, the mass ratio of particles having a particle diameter of less than 106 μm is preferably 2 mass% or less, and the mass ratio of particles having a particle diameter of less than 150 μm is preferably 10 mass% or less. More preferably, the mass ratio of particles having a particle diameter of less than 106 μm is 1% by mass or less, and the mass ratio of particles having a particle diameter of less than 150 μm is 5% by mass or less.
また、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下、且つ粒子径が１５０μｍ未満である粒子の質量割合が１０質量％以下であって、粒子径が６００μｍ以上である粒子の質量割合が４０質量％以下であり、粒子径が４２５μｍ以上であり且つ６００μｍ未満である粒子の質量割合が５０質量％以下であり、粒子径３００μｍ以上であり且つ４２５μｍ未満である粒子の質量割合が５〜６０質量％であり、粒子径２１２μｍ以上であり且つ３００μｍ未満である粒子の質量割合が１〜７０質量％であることが好ましく、粒子径が１０６μｍ未満である粒子の質量割合が１質量％以下、且つ粒子径が１５０μｍ未満である粒子の質量割合が５質量％以下であって、粒子径が６００μｍ以上である粒子の質量割合が５質量％以下であり、粒子径が４２５μｍ以上であり且つ６００μｍ未満である粒子の質量割合が１５質量％以下であり、粒子径３００μｍ以上であり且つ４２５μｍ未満である粒子の質量割合が１０〜５０質量％であり、粒子径２１２μｍ以上であり且つ３００μｍ未満である粒子の質量割合が３０〜６０質量％であることがより好ましい。 Further, based on the whole fine aggregate, the mass ratio of the particles having a particle diameter of less than 106 μm is 2% by mass or less, and the mass ratio of the particles having a particle diameter of less than 150 μm is 10% by mass or less. The mass ratio of particles having a particle diameter of 600 μm or more is 40% by mass or less, the particle diameter is 425 μm or more and the mass ratio of particles having a particle diameter of less than 600 μm is 50% by mass or less, the particle diameter is 300 μm or more and less than 425 μm. Particles having a particle size of 5 to 60% by mass, a particle size of 212 μm or more and less than 300 μm, preferably 1 to 70% by mass, and a particle size of less than 106 μm The mass ratio of particles having a mass ratio of 1 mass% or less and a particle diameter of less than 150 μm is 5 mass% or less and the particle diameter is 600 μm or more. Is 5% by mass or less, the particle size is 425 μm or more and less than 600 μm, the particle mass ratio is 15% by mass or less, and the particle size is 300 μm or more and less than 425 μm. It is more preferable that the mass ratio of particles having a particle diameter of 50% by mass and having a particle diameter of 212 μm or more and less than 300 μm is 30 to 60% by mass.
細骨材の粒子径が、上述の範囲内であることにより、混和性や寸法安定性がより向上する。 When the particle diameter of the fine aggregate is within the above range, the miscibility and dimensional stability are further improved.
細骨材の粒子径は、ＪＩＳ Ｚ ８８０１−１：２００６「試験用ふるい−第１部：金属製網ふるい」に規定される呼び寸法の異なる数個の篩いを用いて測定することができる。また、本明細書において、「粒子径が１０６μｍ未満である粒子の質量割合」とは、篩目１０６μｍの篩を用いたときに篩目１０６μｍの篩を通過した粒子の細骨材全体に対する質量割合をいう。また、「粒子径が２１２μｍ以上であり且つ３００μｍ未満である粒子の質量割合」とは、篩目３００μｍの篩いを用いたときに篩目３００μｍの篩いを通過し、且つ、篩目２１２μｍの篩を用いたとき、篩目２１２μｍの篩上に残る粒子の細骨材全体に対する質量割合をいう。 The particle diameter of the fine aggregate can be measured by using several sieves having different nominal sizes as defined in JIS Z8801-1: 2006 “Test sieve—Part 1: Metal mesh sieve”. Further, in this specification, “the mass ratio of particles having a particle diameter of less than 106 μm” means the mass ratio of particles passing through a sieve having a sieve size of 106 μm to the fine aggregate when using a sieve having a sieve size of 106 μm. Say. Further, “the mass ratio of particles having a particle diameter of 212 μm or more and less than 300 μm” means that when a sieve having a sieve size of 300 μm is used, a sieve having a sieve size of 300 μm is passed through and a sieve having a sieve size of 212 μm is used. When used, it refers to the mass ratio of particles remaining on the sieve having a sieve mesh of 212 μm to the entire fine aggregate.
このような細骨材として、珪砂、川砂、陸砂、海砂、砕砂等の砂類から選択したものを好適に用いることができる。 As such fine aggregates, those selected from sands such as quartz sand, river sand, land sand, sea sand and crushed sand can be suitably used.
本実施形態の下地調整材における細骨材の含有量は、水硬性成分１００質量部に対して、好ましくは１００〜３５０質量部であり、より好ましくは１５０〜３００質量部であり、さらに好ましくは１８０〜２７０質量部であり、特に好ましくは２００〜２５０質量部である。 The content of the fine aggregate in the base preparation material of the present embodiment is preferably 100 to 350 parts by mass, more preferably 150 to 300 parts by mass, and still more preferably with respect to 100 parts by mass of the hydraulic component. It is 180-270 mass parts, Most preferably, it is 200-250 mass parts.
下地調整材中の細骨材の含有量を上記範囲とすることにより、混和性や寸法安定性がより向上する。 By setting the content of the fine aggregate in the base material to be in the above range, the miscibility and dimensional stability are further improved.
改質アスファルトエマルジョンは、下地や上に敷設される防水層との接着性や耐クラック性を向上させるために下地調整材に含まれる。また、改質アスファルトエマルジョンを含む下地調整材は、新設防水層がアスファルト系防水層の場合、プライマーを使用しなくても新設アスファルト系防水層と高い接着力が得られ、トーチ工法の炎に対しても爆裂することなくむしろ溶融に近い状態を経てより高い接着性に寄与する。さらに、改修工事において、下地に古い防水層、特に古いアスファルト系防水層等が残存していたとしても高い接着力が得られ、上に敷設される防水層とも一体化し、良好な防水構造体を得ることができる。 The modified asphalt emulsion is contained in the base preparation material in order to improve adhesion to the base and the waterproof layer laid on the base and crack resistance. In addition, when the new waterproofing layer is an asphalt waterproofing layer, the base preparation material containing the modified asphalt emulsion can achieve high adhesion with the new asphalt waterproofing layer without using a primer. Even though it does not explode, it contributes to higher adhesion through a state close to melting. Furthermore, even if an old waterproof layer, especially an old asphalt waterproof layer, etc. remains on the foundation in the renovation work, a high adhesive force is obtained, and it is integrated with the waterproof layer laid on top, and a good waterproof structure is obtained. Can be obtained.
改質アスファルトエマルジョンは、改質アスファルトを含む固形分を水又は含水溶媒に分散させたものであり、改質アスファルトエマルジョン１００質量％中に固形分２０〜５０質量％含むことが好ましく、固形分３０〜４０質量％含むことがより好ましい。 The modified asphalt emulsion is obtained by dispersing a solid content containing modified asphalt in water or a water-containing solvent, and preferably contains 20 to 50 mass% solid content in 100 mass% modified asphalt emulsion. It is more preferable to contain -40 mass%.
固形分を、上述の範囲で含有することにより、エマルジョンとしてより安定した分散状態を維持できるとともに、水硬性組成物と混和する際に、より良好な混和性が得られる。 By containing the solid content in the above range, a more stable dispersion state can be maintained as an emulsion, and better miscibility can be obtained when blended with the hydraulic composition.
本実施形態の下地調整材における改質アスファルトエマルジョンの含有量は、水硬性成分１００質量部に対して、好ましくは１００〜３００質量部であり、より好ましくは１３０〜２７０質量部であり、さらに好ましくは１６０〜２４０質量部であり、特に好ましくは１８０〜２２０質量部である。 The content of the modified asphalt emulsion in the base preparation material of the present embodiment is preferably 100 to 300 parts by mass, more preferably 130 to 270 parts by mass, further preferably 100 parts by mass of the hydraulic component. Is 160 to 240 parts by mass, particularly preferably 180 to 220 parts by mass.
下地調整材中の改質アスファルトエマルジョンの含有量を上記範囲とすることにより、混和性や寸法安定性がより向上する。 By setting the content of the modified asphalt emulsion in the ground preparation material within the above range, miscibility and dimensional stability are further improved.
改質アスファルトエマルジョンは、公知の製造方法により得られるものを用いることができ、例えば、水又は含水溶媒中で乳化剤の存在下に、アスファルトにゴム、ポリマーなどを混和して改質したアスファルト（改質アスファルト）と、ゴム及び／又はポリマーとが乳化分散しているものなどを用いることができる。また、改質アスファルトエマルジョンは、ゴム及び／又はポリマーと、加熱溶融したアスファルトにゴム及び／又はポリマーなどを混和した改質アスファルトとを乳化機を通して混合する方法などの公知の方法で製造したものを用いることができる。 As the modified asphalt emulsion, one obtained by a known production method can be used. For example, asphalt modified by mixing rubber, polymer, etc. with asphalt in the presence of an emulsifier in water or a water-containing solvent (modified). Quality asphalt) and rubber and / or polymer emulsified and dispersed. The modified asphalt emulsion is prepared by a known method such as a method in which rubber and / or polymer and modified asphalt obtained by mixing rubber and / or polymer with heat-melted asphalt are mixed through an emulsifier. Can be used.
乳化剤としては、公知のものを用いることができ、アニオン性、ノニオン性、カチオン性又は両性の界面活性剤やポリビニルアルコールなどの保護コロイドなどを挙げることができる。 As the emulsifier, known ones can be used, and examples thereof include anionic, nonionic, cationic or amphoteric surfactants and protective colloids such as polyvinyl alcohol.
改質アスファルトエマルジョンにおいて、ゴム成分としては、天然ゴム、エチレンプロピレンジエン共重合ゴム、エチレンブテン共重合ゴム、ポリイソプレン、イソプレン・ブタジエン共重合体、スチレン・ブタジエン共重合体（例えば、ＳＢＳ、ＳＢＲなど）、スチレン・イソプレンブロック共重合ゴム、及びこれらの水素添加物、メタクリレートとブタジエンの共重合体、アクリレートとブタジエンの共重合体、アクリルニトリルとブタジエンの共重合体、ポリブタジエン、ポリクロロプレン、ポリイソブレチン、ブチルゴム、ポリウレタンなど及びこれらのカルボキシル基やグリシジル基などの官能基を導入した変性物などであり、ポリマー成分としては、ポリエチレン、ポリプロピレン、ポリブテン、ポリスチレン、エチレン・アクリレート共重合体、エチレン・メタクリレート共重合体、酢酸ビニール・アクリレート共重合体、酢酸ビニール・メタアクリレート共重合体、エチレン・酢酸ビニル共重合体、酢酸ビニル・脂肪酸ビニルエステル共重合体、酢酸ビニルとマレイン酸、フマール酸、イタコン酸などのジエステルの共重合体、アルキルメタクリレート・アルキルアクリレート共重合体、スチレン・アルキルアクリレート共重合体、エチレン・アルキルアクリレート共重合体、ＡＢＳ樹脂、ポリ塩化ビニル、など及びこれらの重合体にカルボキシル基、マレイン酸などの酸変性などの官能基を導入した変性物などである。 In the modified asphalt emulsion, the rubber component includes natural rubber, ethylene propylene diene copolymer rubber, ethylene butene copolymer rubber, polyisoprene, isoprene / butadiene copolymer, styrene / butadiene copolymer (for example, SBS, SBR, etc.) ), Styrene / isoprene block copolymer rubber, and hydrogenated products thereof, copolymer of methacrylate and butadiene, copolymer of acrylate and butadiene, copolymer of acrylonitrile and butadiene, polybutadiene, polychloroprene, polyisobretin, butyl rubber Polyurethane, etc., and modified products in which functional groups such as carboxyl group and glycidyl group are introduced. Polymer components include polyethylene, polypropylene, polybutene, polystyrene, ethylene Rate copolymer, ethylene / methacrylate copolymer, vinyl acetate / acrylate copolymer, vinyl acetate / methacrylate copolymer, ethylene / vinyl acetate copolymer, vinyl acetate / fatty acid vinyl ester copolymer, vinyl acetate Diester copolymer such as maleic acid, fumaric acid, itaconic acid, alkyl methacrylate / alkyl acrylate copolymer, styrene / alkyl acrylate copolymer, ethylene / alkyl acrylate copolymer, ABS resin, polyvinyl chloride, etc. These polymers are modified products in which a functional group such as acid modification such as carboxyl group and maleic acid is introduced.
アスファルトとしては、天然アスファルトやアスファルタイトなど天然に産するもの、ストレートアスファルト、ブローンアスファルト、カットバックアスファルト等の石油アスファルト、又はこれらのアスファルトの混合物などを好ましく用いることができる。また、アスファルトはプロセスオイル、潤滑油などのオイル、アンスラセンオイル、パイン油、クレオソート油などを少量添加したものを用いることができる。さらに、老化防止剤を添加することもできる。 As the asphalt, naturally occurring asphalt or asphaltite, petroleum asphalt such as straight asphalt, blown asphalt, cutback asphalt, or a mixture of these asphalts can be preferably used. Asphalt may be used with a small amount of process oil, oil such as lubricating oil, anthracene oil, pine oil, creosote oil or the like. Furthermore, an antioxidant can be added.
本実施形態の下地調整材における水硬性組成物は、さらに目的に応じ、本発明の特性を損なわない範囲で流動化剤、増粘剤、消泡剤、凝結調整剤などを適宜選択して添加することができる。 According to the purpose, the hydraulic composition in the base material for adjustment of the present embodiment is appropriately selected from a fluidizing agent, a thickening agent, an antifoaming agent, a coagulation adjusting agent and the like as long as the characteristics of the present invention are not impaired. can do.
水硬性組成物に流動化剤を添加することにより、改質アスファルトエマルジョンと混合して得られるペースト状やスラリー状の下地調整材の材料分離をより抑制することが可能となる。水硬性組成物に増粘剤を添加することにより、改質アスファルトエマルジョンと混合して得られるペースト状やスラリー状の下地調整材の流動性を確保したまま、材料分離をより十分なレベルまで抑えることが可能となる。水硬性組成物に消泡剤を添加することにより、改質アスファルトエマルジョンと混合して得られる下地調整材の気泡によるピンホールをより防止することが可能となる。水硬性組成物に凝結調整剤を添加することにより、改質アスファルトエマルジョンと混合して得られる下地調整材の凝結速度を調整し、比較的長い可使時間と比較的短い硬化開始時間（凝結始発）をより高度に両立することが可能となる。水硬性組成物に消泡剤及び増粘剤を併用添加することにより、改質アスファルトエマルジョンと混合して得られる下地調整材の骨材分離の抑制、気泡発生の抑制、硬化体表面の改善により好ましい効果を与える。 By adding a fluidizing agent to the hydraulic composition, it becomes possible to further suppress the material separation of the paste-like or slurry-like base material prepared by mixing with the modified asphalt emulsion. By adding a thickener to the hydraulic composition, the material separation is suppressed to a more sufficient level while ensuring the fluidity of the paste-like or slurry-like base material prepared by mixing with the modified asphalt emulsion. It becomes possible. By adding an antifoaming agent to the hydraulic composition, it becomes possible to further prevent pinholes due to bubbles in the base preparation obtained by mixing with the modified asphalt emulsion. By adding a coagulation modifier to the hydraulic composition, the coagulation speed of the base preparation obtained by mixing with the modified asphalt emulsion is adjusted, and a relatively long pot life and a relatively short curing start time (condensation initiation time). ) At a higher level. By adding a defoamer and a thickener together with the hydraulic composition, it is possible to suppress the separation of the aggregate of the base preparation obtained by mixing with the modified asphalt emulsion, to suppress the generation of bubbles, and to improve the surface of the cured body. Gives a favorable effect.
流動化剤は、減水効果を合わせ持つ、メラミンスルホン酸のホルムアルデヒド縮合物、カゼイン、カゼインカルシウム、ポリカルボン酸系、ポリエーテル系及びポリエーテルポリカルボン酸系等の市販の流動化剤が、その種類を問わず使用でき、特にポリエーテル系及びポリエーテルポリカルボン酸等の市販の流動化剤を用いることが好ましい。 As for the fluidizing agent, commercially available fluidizing agents such as formaldehyde condensate of melamine sulfonic acid, casein, calcium caseinate, polycarboxylic acid-based, polyether-based and polyether polycarboxylic acid-based, which have a water-reducing effect, are the types. It is preferable to use commercially available fluidizing agents such as polyether and polyether polycarboxylic acid.
流動化剤は、使用する水硬性成分に応じて、特性を損なわない範囲で適宜添加することができ、水硬性成分１００質量部に対して、好ましくは０．０１〜３．０質量部、より好ましくは０．１〜２．０質量部、さらに好ましくは０．２〜１．０質量部、特に好ましくは０．３〜０．７質量部である。流動化剤の添加量が少なすぎると好適な効果を発現せず、また添加量が多すぎても添加量に見合った効果は期待できず、単に不経済であるだけでなく、場合によっては粘稠性も大きくなり所要の流動性を得るための混練水量が増大して強度性状が悪化する場合がある。 The fluidizing agent can be appropriately added within a range that does not impair the characteristics depending on the hydraulic component used, and is preferably 0.01 to 3.0 parts by mass with respect to 100 parts by mass of the hydraulic component. Preferably it is 0.1-2.0 mass parts, More preferably, it is 0.2-1.0 mass part, Most preferably, it is 0.3-0.7 mass part. If the addition amount of the fluidizing agent is too small, a suitable effect will not be exhibited, and if the addition amount is too large, an effect commensurate with the addition amount cannot be expected, which is not only uneconomical, but also in some cases viscous. In some cases, the consistency increases and the amount of kneading water for obtaining the required fluidity increases, resulting in deterioration of strength properties.
増粘剤は、セルロース系、蛋白質系、ラテックス系、及び水溶性ポリマー系などの市販品が挙げられる。中でもセルロース系増粘剤は価格や入手のし易さの観点から好ましい。セルロース系増粘剤には、ヒドロキシエチルセルロース、ヒドロキシエチルメチルセルロース、ヒドロキシプロピルメチルセルロース等があり、その種類を問わず組み合わせて用いることができる。 Examples of the thickener include commercially available products such as cellulose, protein, latex, and water-soluble polymer. Among these, cellulose thickeners are preferable from the viewpoint of price and availability. Cellulosic thickeners include hydroxyethyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, and the like, which can be used in any combination.
増粘剤は、使用する水硬性成分に応じて、特性を損なわない範囲で適宜添加することができ、水硬性成分１００質量部に対して、好ましくは０．０１〜２．０質量部、より好ましくは０．０５〜１．０質量部、さらに好ましくは０．０８〜０．６質量部、特に好ましくは０．１〜０．４質量部である。増粘剤の添加量が少なすぎると好適な効果を発現せず、また添加量が多すぎても添加量に見合った効果は期待できず、単に不経済であるだけでなく、場合によっては粘性も大きくなり作業性が悪化する場合がある。 The thickener can be appropriately added depending on the hydraulic component to be used within a range not to impair the characteristics, and is preferably 0.01 to 2.0 parts by mass with respect to 100 parts by mass of the hydraulic component. Preferably it is 0.05-1.0 mass part, More preferably, it is 0.08-0.6 mass part, Most preferably, it is 0.1-0.4 mass part. If the addition amount of the thickener is too small, a suitable effect will not be exhibited, and if the addition amount is too large, an effect commensurate with the addition amount cannot be expected, which is not only uneconomical, but also viscous in some cases. May also increase workability.
消泡剤は、シリコーン系、アルコール系及び／又はポリエーテル系などの合成物質及び／又は植物由来の天然物質など、公知のものが挙げられる。中でもポリエーテル系消泡剤は価格や入手のし易さの観点から好ましい。消泡剤は、使用する水硬性成分に応じて、特性を損なわない範囲で適宜添加することができ、水硬性成分１００質量部に対して、好ましくは０．０１〜３．０質量部、より好ましくは０．０５〜２．０質量部、さらに好ましくは０．１〜１．０質量部、特に好ましくは０．２〜０．６質量部である。消泡剤の添加量が少なすぎると好適な効果を発現せず、また添加量が多すぎても添加量に見合った効果は期待できない。 Examples of the antifoaming agent include known materials such as synthetic materials such as silicone-based, alcohol-based and / or polyether-based materials and / or natural materials derived from plants. Among these, polyether antifoaming agents are preferable from the viewpoints of price and availability. The antifoaming agent can be appropriately added in a range not impairing the characteristics depending on the hydraulic component used, and is preferably 0.01 to 3.0 parts by mass with respect to 100 parts by mass of the hydraulic component. Preferably it is 0.05-2.0 mass parts, More preferably, it is 0.1-1.0 mass part, Most preferably, it is 0.2-0.6 mass part. If the addition amount of the antifoaming agent is too small, a suitable effect is not exhibited, and if the addition amount is too large, an effect commensurate with the addition amount cannot be expected.
凝結速度調整剤は、水和の促進を行う成分である凝結促進剤、水和の遅延を行う成分である凝結遅延剤などを用いることができる。凝結調整剤としては、凝結促進剤及び凝結遅延剤を併用して用いることが好ましい。凝結調整剤は、用いる水硬性成分や水硬性組成物に応じて、その特性を損なわない範囲で適宜添加することができ、凝結促進剤及び凝結遅延剤の成分、添加量及び混合比率を適宜選択して、可使時間や硬化特性をより調整することができる。 As the setting rate adjusting agent, a setting accelerator that is a component that promotes hydration, a setting retarder that is a component that delays hydration, and the like can be used. As the setting modifier, it is preferable to use a setting accelerator and a setting retarder in combination. Depending on the hydraulic component and hydraulic composition to be used, the setting modifier can be added as appropriate within the range that does not impair the characteristics, and the components, addition amount and mixing ratio of the setting accelerator and setting retarder are appropriately selected. Thus, the pot life and curing characteristics can be further adjusted.
凝結促進剤としては、公知の凝結を促進する成分を用いることができる。例えば、凝結促進効果を有する塩化物、亜硝酸塩、硝酸塩、硫酸塩、炭酸塩、有機酸塩等を好適に用いることができ、これらを単独又は数種組み合わせて使用することができる。 As the setting accelerator, a known component for promoting setting can be used. For example, chlorides, nitrites, nitrates, sulfates, carbonates, organic acid salts and the like having a setting acceleration effect can be suitably used, and these can be used alone or in combination of several kinds.
硫酸塩の一例として、硫酸カルシウム、硫酸ナトリウム、硫酸カリウム、硫酸リチウムを挙げることができる。炭酸塩の一例として、炭酸カルシウム、炭酸ナトリウム、炭酸カリウム、炭酸リチウムを挙げることができる。有機酸塩の一例としては、ギ酸カルシウム、酢酸カルシウム、アクリル酸カルシウムを挙げることができる。 Examples of sulfates include calcium sulfate, sodium sulfate, potassium sulfate, and lithium sulfate. Examples of carbonates include calcium carbonate, sodium carbonate, potassium carbonate, and lithium carbonate. Examples of the organic acid salt include calcium formate, calcium acetate, and calcium acrylate.
凝結遅延剤としては、公知の凝結を遅延する成分を用いることができる。例えば、凝結遅延効果を有するオキシカルボン酸類等の有機酸や、グルコース、マルトース、デキストリン等の糖類、重炭酸ナトリウムやリン酸ナトリウム等を好適に用いることができ、これらを単独又は数種組み合わせて使用することができる。 As the setting retarder, a known component that delays setting can be used. For example, organic acids such as oxycarboxylic acids having a setting retarding effect, sugars such as glucose, maltose and dextrin, sodium bicarbonate and sodium phosphate can be suitably used, and these are used alone or in combination of several kinds. can do.
オキシカルボン酸類は、オキシカルボン酸及びこれらの塩を含む。オキシカルボン酸としては、例えば、クエン酸、グルコン酸、酒石酸、グリコール酸、乳酸、ヒドロアクリル酸、α−オキシ酪酸、グリセリン酸、タルトロン酸、リンゴ酸等の脂肪族オキシ酸、サリチル酸、ｍ−オキシ安息香酸、ｐ−オキシ安息香酸、没食子酸、マンデル酸及びトロパ酸等の芳香族オキシ酸を挙げることができる。 Oxycarboxylic acids include oxycarboxylic acids and their salts. Examples of oxycarboxylic acid include citric acid, gluconic acid, tartaric acid, glycolic acid, lactic acid, hydroacrylic acid, α-oxybutyric acid, glyceric acid, tartronic acid, malic acid and other aliphatic oxyacids, salicylic acid, m-oxy Mention may be made of aromatic oxyacids such as benzoic acid, p-oxybenzoic acid, gallic acid, mandelic acid and tropic acid.
オキシカルボン酸の塩としては、例えば、アルカリ金属塩（具体的にはナトリウム塩及びカリウム塩等）及びアルカリ土類金属塩（具体的にはカルシウム塩、バリウム塩及びマグネシウム塩等）を挙げることができ、ナトリウム塩がより好ましい。オキシカルボン酸塩の一例として、クエン酸ナトリウム、グルコン酸ナトリウム、酒石酸ナトリウムを挙げることができる。 Examples of the salt of oxycarboxylic acid include alkali metal salts (specifically sodium salt and potassium salt) and alkaline earth metal salts (specifically calcium salt, barium salt and magnesium salt). Sodium salts are more preferred. Examples of oxycarboxylates include sodium citrate, sodium gluconate, and sodium tartrate.
本実施形態の下地調整材における水硬性組成物は、一般的な混合機で混合して水硬性組成物を均質に調製することができる。混合機としては、公知の混合機を用いることができ、例えば、ナウターミキサ、リボンミキサ、オムニミキサ等を挙げることができる。 The hydraulic composition in the base material of the present embodiment can be mixed with a general mixer to prepare the hydraulic composition homogeneously. As the mixer, a known mixer can be used, and examples thereof include a Nauter mixer, a ribbon mixer, and an omni mixer.
水硬性組成物は、一般的な混合機で混合して組成物を均質に調製し、粉体状態で一般に使用されているセメントの包装袋、紙袋、ポリエチレン袋、ポリビニール袋の他に、外気接触が無い金属性・有機質系の密閉容器などで貯蔵することができる。 The hydraulic composition is mixed with a general mixer to prepare the composition homogeneously, and in addition to cement packaging bags, paper bags, polyethylene bags and polyvinyl bags, which are generally used in powder form, the outside air It can be stored in a metal / organic airtight container without contact.
本実施形態の下地調整材は、水硬性組成物と改質アスファルトエマルジョンを均質に混合して調製し、一般建築物の屋上やルーフバルコニー等の下地表面に防水シート等の防水層を施工する際、その下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することができる。また、本発明の特性を損なわない範囲で水硬性組成物と改質アスファルトエマルジョンにさらに水を加えて混合することもできる。 The base material of this embodiment is prepared by mixing the hydraulic composition and the modified asphalt emulsion homogeneously, and when applying a waterproof layer such as a waterproof sheet on the base surface of a general building rooftop or roof balcony. The base surface can be easily adjusted to be flat and smooth, and a waterproof layer can be applied thereon. Further, water can be further added to the hydraulic composition and the modified asphalt emulsion within a range not impairing the characteristics of the present invention.
混合して調製した直後の２０℃における下地調整材の粘度は、５００〜３５００ｍＰａ・ｓが好ましく、１０００〜３０００ｍＰａ・ｓがより好ましい。また、３５℃における下地調整材の粘度は、２００〜２５００ｍＰａ・ｓが好ましく、５００〜２０００ｍＰａ・ｓがより好ましい。 The viscosity of the base material at 20 ° C. immediately after mixing and preparation is preferably 500 to 3500 mPa · s, more preferably 1000 to 3000 mPa · s. Moreover, 200-2500 mPa * s is preferable and, as for the viscosity of the base preparation material in 35 degreeC, 500-2000 mPa * s is more preferable.
下地調整材の粘度が上述の範囲にあることにより、水硬性組成物と改質アスファルトエマルジョンとの混和性が良好で、均質な下地調整材を調製することができ、それにより優れた特性を奏することが可能となる。 When the viscosity of the ground preparation material is in the above-mentioned range, the miscibility between the hydraulic composition and the modified asphalt emulsion is good, and a homogeneous ground conditioning material can be prepared, thereby providing excellent characteristics. It becomes possible.
ここで、下地調整材の「粘度」とは、Ｂ型粘度計（ＢＲＯＯＫＦＩＥＬＤ社製デジタル粘度計：ＲＶＤＶ−１＋）を用いてローターＮｏ．６、回転速度１２ｒｐｍ、２０℃及び３５℃で測定した値をいう。 Here, the “viscosity” of the base material is defined by the rotor No. using a B-type viscometer (digital viscometer manufactured by BROOKFIELD: RVDV-1 +). 6. The value measured at a rotational speed of 12 rpm, 20 ° C and 35 ° C.
本実施形態の下地調整材は、施工条件に応じて鏝やゴムベラ、場合によってはローラー刷毛等を用い、１〜１０ｍｍ程度の厚さに下地調整材を平滑に施工することができる。その際、２０℃における下地調整材のフロー値は、２００〜２４０ｍｍが好ましく、２０５〜２３０ｍｍがさらに好ましい。３５℃における下地調整材のフロー値は、２１０〜２５０ｍｍが好ましく、２１５〜２４０ｍｍがさらに好ましい。また、下地調整材のフロー比は２０℃及び３５℃ともに０．９５〜１．０５であることが好ましい。 The foundation adjusting material of the present embodiment can be smoothly applied to a thickness of about 1 to 10 mm using scissors, rubber spatula, or a roller brush depending on the construction conditions. In that case, the flow value of the base material at 20 ° C. is preferably 200 to 240 mm, and more preferably 205 to 230 mm. The flow value of the base material at 35 ° C. is preferably 210 to 250 mm, and more preferably 215 to 240 mm. Moreover, it is preferable that the flow ratios of the base material are 0.95 to 1.05 for both 20 ° C. and 35 ° C.
下地調整材のフロー値が上述の範囲であることにより、良好な施工性を奏することができる。また、下地調整材のフロー比が上述の範囲であることにより、施工可能時間の十分な確保や施工後のフロー値の伸びによるしわ発生等による平滑性の低下を抑制することができる。 When the flow value of the base material is within the above range, good workability can be achieved. Moreover, when the flow ratio of the base material is within the above-described range, it is possible to suppress a decrease in smoothness due to generation of wrinkles due to sufficient securing of construction possible time and elongation of the flow value after construction.
ここで、下地調整材の「フロー値」とは、ＪＡＳＳ １５Ｍ−１０３「社団法人日本建築学会：セルフレベリング材の品質基準」に記載の試験方法に準拠して２０℃及び３５℃で測定した値（単位：ｍｍ）をいう。また、「フロー比」とは、各配合及び各温度において、混合・調製して６０分経過した後のフロー値を、混合・調製した直後のフロー値で除した値をいう。 Here, the “flow value” of the base conditioning material is a value measured at 20 ° C. and 35 ° C. in accordance with the test method described in JASS 15M-103 “Architectural Institute of Japan: Quality standards for self-leveling material”. (Unit: mm). The “flow ratio” refers to a value obtained by dividing the flow value after 60 minutes have passed after mixing and preparation at each composition and each temperature by the flow value immediately after mixing and preparation.
本実施形態の下地調整材は、施工後に下地である床面や上面に敷設される防水層との一体化のための優れた寸法安定性を有する。寸法安定性は下地調整材の長さ変化で表すことができ、２０℃及び３５℃ともに長さ変化率の最大値が−０．１０〜０．２５％であることが好ましく、−０．０５〜０．２０％であることがさらに好ましい。 The base material of this embodiment has excellent dimensional stability for integration with a waterproof layer laid on the floor or upper surface that is the base after construction. The dimensional stability can be expressed by a change in the length of the base material, and the maximum value of the length change rate is preferably −0.10 to 0.25% at both 20 ° C. and 35 ° C., −0.05 More preferably, it is -0.20%.
下地調整材の長さ変化率が上述の範囲であることにより、下地である床面や上面に敷設される防水層との優れた一体化を奏することができる。 When the length change rate of the base adjusting material is in the above range, excellent integration with the waterproof layer laid on the floor surface or the upper surface as the base can be achieved.
ここで、下地調整材の「長さ変化率」とは、図１に示す装置を用いて２０℃及び３５℃で測定し、演算して得られた値（単位：％）をいう。 Here, the “length change rate” of the base material refers to a value (unit:%) obtained by measuring and calculating at 20 ° C. and 35 ° C. using the apparatus shown in FIG.
以上、本発明の好適な実施形態について説明したが、本発明は上記実施形態に何ら限定されるものではない。 The preferred embodiment of the present invention has been described above, but the present invention is not limited to the above embodiment.
以下に実験例を挙げて本発明の内容をより詳細に説明するが、本発明は以下の実験例に限定されるものではない。 The contents of the present invention will be described in more detail with reference to the following experimental examples, but the present invention is not limited to the following experimental examples.
（実験例１）
表１に示す粒度構成を有する細骨材Ａ〜Ｆの各１００質量部に対して、改質アスファルトエマルジョンをそれぞれ４５質量部加えて混合（混練）し、細骨材と改質アスファルトエマルジョンとの混和性を確認した。混練は、温度３５℃の条件下で、攪拌機(ヤマト科学社製、ラボスターラーＬＲ４００Ｄ)を用いて７００ｒｐｍで３分間行った。混練直後に混和性を目視で評価した。
(Experimental example 1)
For each 100 parts by mass of fine aggregates A to F having the particle size constitution shown in Table 1, 45 parts by mass of the modified asphalt emulsion is added and mixed (kneaded), and the fine aggregate and the modified asphalt emulsion are mixed. The miscibility was confirmed. The kneading was performed at 700 rpm for 3 minutes using a stirrer (manufactured by Yamato Scientific Co., Ltd., Lab Stirrer LR400D) under the condition of a temperature of 35 ° C. Immediately after kneading, the miscibility was visually evaluated.
［使用材料］
（１）細骨材
・珪砂（篩を使用して測定した各々の珪砂の粒度構成を表１に示す。）
（２）改質アスファルトエマルジョン
・改質アスファルトエマルジョン（宇部興産社製、主成分としてアスファルト、ブタジエン・スチレン共重合物、水を含む、固形分３５％）
[Materials used]
(1) Fine aggregate and silica sand (Table 1 shows the particle size composition of each silica sand measured using a sieve)
(2) Modified asphalt emulsion / modified asphalt emulsion (manufactured by Ube Industries Co., Ltd., containing asphalt, butadiene / styrene copolymer as main components, water, solid content 35%)
ここで、上述の固形分とは、改質アスファルトエマルジョンを１０５℃で３時間処理して残った不揮発分をいう。 Here, the above-mentioned solid content means a non-volatile content remaining after the modified asphalt emulsion is treated at 105 ° C. for 3 hours.
［物性の評価方法］
（１）細骨材と改質アスファルトエマルジョンとの混和性
混練直後に流動性を有していれば混和性良好（○）とし、流動性を有さない、あるいは偽凝結のようにこわばった状態であれば混和性不良（×）とした。
[Method for evaluating physical properties]
(1) Miscibility between fine aggregate and modified asphalt emulsion If fluidity is present immediately after kneading, good miscibility (○), no fluidity, or stiffening like false condensation If so, the miscibility was poor (x).
実験に用いた細骨材の粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下であるＮｏ．１−１、Ｎｏ．１−２、Ｎｏ．１−３は、改質アスファルトエマルジョンとの混和性が良好であった。また、実験に用いた細骨材の粒子径が１５０μｍ未満である粒子の質量割合が１０質量％以下であるＮｏ．１−１、Ｎｏ．１−２、Ｎｏ．１−３は、改質アスファルトエマルジョンとの混和性が良好であった。 The fine aggregate used in the experiment has a particle diameter of less than 106 μm and the mass ratio of the particles is 2% by mass or less. 1-1, no. 1-2, no. 1-3 had good miscibility with the modified asphalt emulsion. In addition, No. in which the mass ratio of the fine aggregate used in the experiment has a particle size of less than 150 μm is 10% by mass or less. 1-1, no. 1-2, no. 1-3 had good miscibility with the modified asphalt emulsion.
（実験例２）
水硬性成分１００質量部に対し、無機充填材、細骨材、流動化剤、増粘剤、消泡剤及び改質アスファルトエマルジョンを表３に示す質量部で配合して下地調整材を調製した。表３において、水硬性成分であるアルミナセメント、ポルトランドセメント及び石膏は、各質量部の合計が１００質量部になるように配合した。下地調整材の混練は、温度２０℃及び温度３５℃の条件下で、攪拌機(ヤマト科学社製、ラボスターラーＬＲ４００Ｄ)を用いて７００ｒｐｍで３分間行った。混練直後に粘度、フロー値を測定し、図１に示す装置を用いて長さ変化率を２０℃及び３５℃で測定した。
(Experimental example 2)
An inorganic filler, fine aggregate, fluidizing agent, thickener, antifoaming agent and modified asphalt emulsion were blended in 100 parts by mass of the hydraulic component in parts by mass shown in Table 3 to prepare a base preparation. . In Table 3, the hydraulic components alumina cement, Portland cement and gypsum were blended so that the total of each part by mass was 100 parts by mass. The base material was kneaded at 700 rpm for 3 minutes using a stirrer (Yamato Kagaku Co., Ltd., Lab Stirrer LR400D) under the conditions of a temperature of 20 ° C. and a temperature of 35 ° C. Immediately after kneading, the viscosity and flow value were measured, and the rate of change in length was measured at 20 ° C. and 35 ° C. using the apparatus shown in FIG.
［使用材料］
（１）水硬性成分
・アルミナセメント（ケルネオス社製、ブレーン比表面積：３１００ｃｍ２／ｇ）
・早強ポルトランドセメント（宇部三菱セメント社製、ブレーン比表面積：４５８０ｃｍ２／ｇ）
・石膏（天然無水石膏、ブレーン比表面積３７１０ｃｍ２／ｇ）
（２）無機充填材
・高炉スラグ微粉末（千葉リバーメント社製、篩を使用して測定した高炉スラグ微粉末の粒度構成を表２に示す。）
・炭酸カルシウム微粉末（有恒鉱業社製、篩を使用して測定した炭酸カルシウム微粉末の粒度構成を表２に示す。）
[Materials used]
(1) Hydraulic component-Alumina cement (Kelneos, Brain specific surface area: 3100 cm 2 / g)
・ Haya strong Portland cement (manufactured by Ube Mitsubishi Cement, Blaine specific surface area: 4580 cm 2 / g)
Gypsum (natural anhydrous gypsum, Blaine specific surface area 3710 cm 2 / g)
(2) Inorganic filler-Blast furnace slag fine powder (made by Chiba Riverment Co., Ltd., Table 2 shows the particle size composition of the blast furnace slag fine powder measured using a sieve)
Calcium carbonate fine powder (made by Arisa Mining Co., Ltd., Table 2 shows the particle size composition of the calcium carbonate fine powder measured using a sieve)
（３）細骨材
・細骨材Ｂ（珪砂、篩を使用して測定した細骨材Ｂの粒度構成を表１に示す。）
・細骨材Ｅ（珪砂、篩を使用して測定した細骨材Ｅの粒度構成を表１に示す。）
（４）流動化剤
・ポリエーテル系流動化剤（花王社製）
（５）増粘剤
・セルロース系増粘剤（松本油脂社製、主成分：ヒドロキシエチルメチルセルロース、粘度［２０℃、２％水溶液］：２８８００ｍＰａ・ｓ）
（６）消泡剤
・ポリエーテル系消泡剤（日本油脂社製）
（７）改質アスファルトエマルジョン
・改質アスファルトエマルジョン（宇部興産社製、主成分としてアスファルト、ブタジエン・スチレン共重合物、水を含む、固形分３５％）
(3) Fine aggregate-Fine aggregate B (Table 1 shows the particle size composition of fine aggregate B measured using silica sand and sieve)
Fine aggregate E (Table 1 shows the particle size composition of fine aggregate E measured using silica sand and sieve)
(4) Fluidizer-Polyether fluidizer (Kao Corporation)
(5) Thickener ・ Cellulosic thickener (manufactured by Matsumoto Yushi Co., Ltd., main component: hydroxyethyl methylcellulose, viscosity [20 ° C., 2% aqueous solution]: 28800 mPa · s)
(6) Antifoaming agent ・ Polyether antifoaming agent (manufactured by NOF Corporation)
(7) Modified asphalt emulsion / modified asphalt emulsion (manufactured by Ube Industries, Inc., containing asphalt, butadiene / styrene copolymer, water as the main component, solid content 35%)
［物性の評価方法］
調製した各実施例及び各比較例の下地調整材の粘度、フロー値及び長さ変化率を測定した。測定結果は、表４、表５、図２及び図３に示すとおりであった。各測定は、以下に示す方法で行った。
[Method for evaluating physical properties]
The viscosity, flow value, and length change rate of the prepared base preparation materials of each Example and each Comparative Example were measured. The measurement results were as shown in Table 4, Table 5, FIG. 2 and FIG. Each measurement was performed by the method shown below.
（１）粘度の測定方法
２０℃及び３５℃で調製した下地調整材をＢ型粘度計（ＢＲＯＯＫＦＩＥＬＤ社製デジタル粘度計：ＲＶＤＶ−１＋）を用いてローターＮｏ．６、回転速度１２ｒｐｍにて、２０℃及び３５℃で測定した。粘度比は、各温度で一番低い粘度を１．０としたときの配合の違いによる各温度における粘度の比を求めた。
（２）フロー値の測定方法
２０℃及び３５℃で調製した下地調整材をＪＡＳＳ １５Ｍ−１０３「社団法人日本建築学会：セルフレベリング材の品質基準」に記載の試験方法に準拠して２０℃及び３５℃で測定した。また、フロー比は、各配合及び各温度において、混練して６０分経過した後のフロー値を、混練した直後のフロー値で除して求めた。
（３）長さ変化率の測定方法
２０℃及び３５℃で調製した下地調整材を図１に示す装置の型枠内部に型枠の高さｃ（１０ｍｍ）まで打設し、打設直後より長さ変化の測定を開始し、測定間隔は５分毎に行い、材齢１５日まで２０℃及び３５℃にて測定した。長さ変化率は、図１（ａ）に示すＳＵＳ製円盤５５ｂと渦電流式変位センサー５４の端部（ＳＵＳ製円盤５５ｂ側の端部）との間隔の測定間隔毎における変化量（ｍｍ）をＳＵＳ製円盤５５ａとＳＵＳ製円盤５５ｃとの間隔ｂ（４８０ｍｍ）で除して、百分率で表した値とした。長さ変化率にマイナスの符号がつく場合は測定開始より収縮していることを意味し、長さ変化率に符号がつかない場合は測定開始より膨張していることを意味する。
(1) Viscosity Measurement Method The base material prepared at 20 ° C. and 35 ° C. was subjected to rotor No. using a B-type viscometer (BROOKFIELD digital viscometer: RVDV-1 +). 6. Measurement was performed at 20 ° C. and 35 ° C. at a rotation speed of 12 rpm. The viscosity ratio was determined as the ratio of viscosities at each temperature due to the difference in formulation when the lowest viscosity at each temperature was 1.0.
(2) Measurement method of flow value The base material prepared at 20 ° C. and 35 ° C. was prepared at 20 ° C. according to the test method described in JASS 15M-103 “The Architectural Institute of Japan: Quality standards for self-leveling materials”. Measured at 35 ° C. The flow ratio was determined by dividing the flow value after 60 minutes had passed after kneading at each formulation and each temperature by the flow value immediately after kneading.
(3) Measuring method of length change rate The base material prepared at 20 ° C. and 35 ° C. was placed in the mold of the apparatus shown in FIG. 1 to the height c (10 mm) of the mold, and immediately after the casting. The measurement of the length change was started, the measurement interval was performed every 5 minutes, and the measurement was performed at 20 ° C. and 35 ° C. until the age of 15 days. The rate of change in length is the amount of change (mm) at each measurement interval of the distance between the
表４に示すとおり、無機充填材が高炉スラグ微粉末で、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−１は、２０℃及び３５℃ともに粘度が高く、粘度比も２０℃及び３５℃でそれぞれ２．５、２．７と高い値を示した。また、無機充填材が特定の粒度を構成する炭酸カルシウム微粉末であっても、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−２は、Ｎｏ．２−１よりは低い粘度を示したが、２０℃及び３５℃ともに粘度が高く、粘度比も２０℃及び３５℃ともに１．５と高い値を示した。無機充填材が特定の粒度を構成する炭酸カルシウム微粉末で、細骨材がＮｏ．１−２で使用され改質アスファルトエマルジョンとの混和性が良好であった特定の粒度を構成する細骨材ＢであるＮｏ．２−３及びＮｏ．２−４は、水硬性成分の配合割合が異なっていても２０℃及び３５℃ともに良好な粘度を示した。 As shown in Table 4, the inorganic filler is blast furnace slag fine powder, and the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. The viscosity of 2-1 was high at 20 ° C. and 35 ° C., and the viscosity ratio was as high as 2.5 and 2.7 at 20 ° C. and 35 ° C., respectively. Even if the inorganic filler is a calcium carbonate fine powder having a specific particle size, the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. 2-2 is No. Although the viscosity was lower than 2-1, the viscosity was high at both 20 ° C. and 35 ° C., and the viscosity ratio was as high as 1.5 at both 20 ° C. and 35 ° C. The inorganic filler is a calcium carbonate fine powder having a specific particle size. No. 1 is a fine aggregate B used in No. 1-2 and constituting a specific particle size having good miscibility with the modified asphalt emulsion. 2-3 and no. No. 2-4 showed good viscosity at 20 ° C. and 35 ° C. even when the blending ratio of the hydraulic component was different.
表５に示すとおり、無機充填材が高炉スラグ微粉末で、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−１は、２０℃及び３５℃ともに混練直後のフロー値が低く、フロー比も２０℃及び３５℃でそれぞれ０．９４及び０．９０と６０分後のフロー値の伸びが大きくなっていた。また、無機充填材が特定の粒度を構成する炭酸カルシウム微粉末であっても、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−２は、Ｎｏ．２−１よりも混練直後に高いフロー値を示したが、２０℃でのフロー比が０．９２と６０分後のフロー値の伸びが大きくなっていた。無機充填材が特定の粒度を構成する炭酸カルシウム微粉末で、細骨材がＮｏ．１−２で使用され改質アスファルトエマルジョンとの混和性が良好であった特定の粒度を構成する細骨材ＢであるＮｏ．２−３及びＮｏ．２−４は、水硬性成分の配合割合が異なっていても２０℃及び３５℃ともに良好なフロー値及びフロー比を示した。 As shown in Table 5, the inorganic filler is blast furnace slag fine powder, and the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. 2-1 had a low flow value immediately after kneading at 20 ° C. and 35 ° C., and the flow ratios were 0.94, 0.90 and 60 minutes after 60 minutes, respectively. . Even if the inorganic filler is a calcium carbonate fine powder having a specific particle size, the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. 2-2 is No. The flow value was higher immediately after kneading than 2-1, but the flow ratio at 20 ° C. was 0.92, and the elongation of the flow value after 60 minutes was large. The inorganic filler is a calcium carbonate fine powder having a specific particle size. No. 1 is a fine aggregate B used in No. 1-2 and constituting a specific particle size having good miscibility with the modified asphalt emulsion. 2-3 and no. 2-4 showed a good flow value and flow ratio at 20 ° C. and 35 ° C. even when the blending ratio of the hydraulic component was different.
図２に示すとおり、無機充填材が高炉スラグ微粉末で、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−１は、２０℃において長さ変化率の最大値が０．２６％とやや大きな値を示した。また、無機充填材が特定の粒度を構成する炭酸カルシウム微粉末であっても、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−２は、２０℃において長さ変化率の最大値が０．３４％とＮｏ．２−１より大きくなった。無機充填材が特定の粒度を構成する炭酸カルシウム微粉末で、細骨材がＮｏ．１−２で使用され改質アスファルトエマルジョンとの混和性が良好であった特定の粒度を構成する細骨材ＢであるＮｏ．２−３及びＮｏ．２−４は、２０℃において長さ変化率の最大値がそれぞれ０．０９及び０．０４と良好な長さ変化率を示した。中でもＮｏ．２−４が最も良好な値を示した。 As shown in FIG. 2, the inorganic filler is blast furnace slag fine powder, and the fine aggregate is No. 1. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. 2-1, the maximum value of the rate of change in length at 20 ° C. was a slightly large value of 0.26%. Even if the inorganic filler is a calcium carbonate fine powder having a specific particle size, the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. In No. 2-2, the maximum value of the rate of change in length at 20 ° C. was 0.34% and No. It became larger than 2-1. The inorganic filler is a calcium carbonate fine powder having a specific particle size. No. 1 is a fine aggregate B used in No. 1-2 and constituting a specific particle size having good miscibility with the modified asphalt emulsion. 2-3 and no. In 2-4, the maximum length change rate at 20 ° C. was 0.09 and 0.04, respectively. No. 2-4 showed the best value.
図３に示すとおり、無機充填材が高炉スラグ微粉末で、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−１は、３５℃において長さ変化率の最大値が０．６４％とかなり大きな値を示した。また、無機充填材が特定の粒度を構成する炭酸カルシウム微粉末であっても、細骨材がＮｏ．１−５で使用され改質アスファルトエマルジョンとの混和性が不良であった細骨材ＥであるＮｏ．２−２は、３５℃において長さ変化率の測定結果が無いものの、２０℃での長さ変化率の最大値がＮｏ．２−１を上回っていたことから、３５℃においても大きいと推測される。無機充填材が特定の粒度を構成する炭酸カルシウム微粉末で、細骨材がＮｏ．１−２で使用され改質アスファルトエマルジョンとの混和性が良好であった特定の粒度を構成する細骨材ＢであるＮｏ．２−３及びＮｏ．２−４は、３５℃において長さ変化率の最大値がそれぞれ０．１９及び０．０７と２０℃での長さ変化率よりも若干大きくなったが、良好な寸法変化率を示した。中でも、Ｎｏ．２−４が最も良好な値を示した。 As shown in FIG. 3, the inorganic filler is blast furnace slag fine powder, and the fine aggregate is No. 1. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. 2-1, the maximum value of the length change rate at 35 ° C. was 0.64%, which was a considerably large value. Even if the inorganic filler is a calcium carbonate fine powder having a specific particle size, the fine aggregate is No. No. 1 which is fine aggregate E used in No. 1-5 and poorly miscible with the modified asphalt emulsion. In 2-2, although there was no measurement result of the length change rate at 35 ° C., the maximum value of the length change rate at 20 ° C. was No. 2-2. Since it was higher than 2-1, it is presumed to be large even at 35 ° C. The inorganic filler is a calcium carbonate fine powder having a specific particle size. No. 1 is a fine aggregate B used in No. 1-2 and constituting a specific particle size having good miscibility with the modified asphalt emulsion. 2-3 and no. In 2-4, the maximum value of the length change rate at 35 ° C. was slightly larger than the length change rate at 0.19, 0.07, and 20 ° C., respectively, but showed a good dimensional change rate. Among these, No. 2-4 showed the best value.
以上より、Ｎｏ．２−３及びＮｏ．２−４のように、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分と、無機充填材が特定の粒度を構成する炭酸カルシウム微粉末と、特定の粒度を構成する細骨材とを含む水硬性組成物、及び改質アスファルトエマルジョンを含む下地調整材は、水硬性組成物と改質アスファルトエマルジョンとを容易に均質に混合できる良好な混和性を有し、さらに下地や防水層との一体化をより向上するための温度依存性の小さい優れた寸法安定性（膨張及び収縮の小さい長さ変化率）を有することが確認された。すなわち、本願発明の下地調整材は年中いかなる時期に使用されても良好な混和性を示すとともに、一般建築物の屋上やルーフバルコニー等の下地表面に防水シート等の防水層を施工する際、その下地表面を容易に平坦及び平滑に調整し、その上に防水層を施工することができる。 From the above, no. 2-3 and no. As in 2-4, water containing a hydraulic component composed of alumina cement, Portland cement and gypsum, fine calcium carbonate powder with a specific particle size of inorganic filler, and fine aggregate with a specific particle size The base composition containing the hard composition and the modified asphalt emulsion has good miscibility so that the hydraulic composition and the modified asphalt emulsion can be easily and homogeneously mixed, and further integrated with the base and waterproof layer. It was confirmed to have excellent dimensional stability (small rate of change in length of expansion and contraction) having a small temperature dependency for further improving the temperature. That is, the base preparation material of the present invention shows good miscibility regardless of when it is used throughout the year, and when a waterproof layer such as a waterproof sheet is applied to the base surface of a general building rooftop or roof balcony, The base surface can be easily adjusted to be flat and smooth, and a waterproof layer can be applied thereon.
５１…長さ変化測定装置，５２…型枠，５３…緩衝材，５４…渦電流式変位センサー，５５…ＳＵＳ製円盤（５５ａ，５５ｂ，５５ｃ），５６…ＳＵＳ棒（５６ａ，５６ｂ），５７…フッ素樹脂シート。
DESCRIPTION OF
Claims (3)
前記水硬性組成物は、アルミナセメント、ポルトランドセメント及び石膏からなる水硬性成分、無機充填材、及び細骨材を含み、
前記無機充填材は炭酸カルシウム微粉末であり、
前記炭酸カルシウム微粉末は、炭酸カルシウム微粉末全体を基準として、粒子径６００μｍ以上の粒子を含まず、粒子径が３００μｍ以上であり且つ６００μｍ未満である粒子の質量割合が５質量％以下であり、粒子径が１５０μｍ以上であり且つ３００μｍ未満である粒子の質量割合が０．５〜１５質量％であり、粒子径が７５μｍ以上であり且つ１５０μｍ未満である粒子の質量割合が５〜４０質量％であり、７５μｍ未満である粒子の質量割合が５０〜９０質量％である
前記細骨材は、細骨材全体を基準として、粒子径が１０６μｍ未満である粒子の質量割合が２質量％以下であり、
前記水硬性成分は、水硬性成分１００質量％中にアルミナセメント２０〜６０質量％、ポルトランドセメント２０〜６０質量％、石膏１０〜５０質量％含み、
前記水硬性成分１００質量部に対して、炭酸カルシウム微粉末５０〜２００質量部、細骨材１００〜３５０質量部、改質アスファルトエマルジョン１００〜３００質量部含む
下地調整材。 A substrate preparation material comprising a hydraulic composition and a modified asphalt emulsion,
The hydraulic composition includes a hydraulic component made of alumina cement, Portland cement and gypsum, an inorganic filler, and fine aggregate.
The inorganic filler is calcium carbonate fine powder,
The calcium carbonate fine powder is based on the whole calcium carbonate fine powder, does not include particles having a particle diameter of 600 μm or more, and the mass ratio of particles having a particle diameter of 300 μm or more and less than 600 μm is 5% by mass or less, The mass ratio of particles having a particle diameter of 150 μm or more and less than 300 μm is 0.5 to 15 mass%, and the mass ratio of particles having a particle diameter of 75 μm or more and less than 150 μm is 5 to 40 mass%. Yes, the fine aggregate in which the mass ratio of particles less than 75 μm is 50 to 90 mass%, the mass ratio of particles having a particle diameter of less than 106 μm is 2 mass% or less based on the whole fine aggregate The
The hydraulic component contains 20-60 mass% alumina cement, 20-60 mass% Portland cement, 10-50 mass% gypsum in 100 mass% hydraulic component,
A base material adjusting material containing 50 to 200 parts by mass of calcium carbonate fine powder, 100 to 350 parts by mass of fine aggregate, and 100 to 300 parts by mass of a modified asphalt emulsion with respect to 100 parts by mass of the hydraulic component .
請求項１記載の下地調整材。 In the fine aggregate, the mass ratio of particles having a particle diameter of less than 106 μm is 2% by mass or less and the mass ratio of particles having a particle diameter of less than 150 μm is 10% by mass or less, based on the whole fine aggregate. The groundwork adjusting material according to claim 1.
請求項１又は請求項２記載の下地調整材。 The base modifier according to claim 1 or 2, wherein the modified asphalt emulsion contains 20 to 50% by mass of solid content in 100% by mass of the modified asphalt emulsion.