JP5929746B2 - Surface-treated steel sheet - Google Patents
Surface-treated steel sheet Download PDFInfo
- Publication number
- JP5929746B2 JP5929746B2 JP2012283180A JP2012283180A JP5929746B2 JP 5929746 B2 JP5929746 B2 JP 5929746B2 JP 2012283180 A JP2012283180 A JP 2012283180A JP 2012283180 A JP2012283180 A JP 2012283180A JP 5929746 B2 JP5929746 B2 JP 5929746B2
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- polymer
- treated steel
- mass
- chemical conversion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、ＯＡ機器内の摺動部材などに用いられる表面処理鋼板であり、特に、高温の焼付け乾燥を必要とすることなく、優れた防汚性及び耐食性を有する表面処理鋼板に関するものである。 The present invention relates to a surface-treated steel sheet used for sliding members in OA equipment and the like, and particularly to a surface-treated steel sheet having excellent antifouling properties and corrosion resistance without requiring high-temperature baking and drying. .
ＯＡ機器内の摺動部材、食品調理器具、加熱調理器具等に用いられる表面処理鋼板は、それぞれの用途によって、耐汚染性、耐食性、非粘着性、耐熱性等の性能が要求される。そのため、上記性能を満足するべく、従来は鋼板の表面にフッ素樹脂を含有する塗膜を形成した表面処理鋼板が用いられていた。 Surface treated steel sheets used for sliding members, food cooking utensils, cooking utensils, and the like in OA equipment are required to have performances such as contamination resistance, corrosion resistance, non-adhesiveness, and heat resistance depending on their respective uses. Therefore, in order to satisfy the above performance, conventionally, a surface-treated steel sheet in which a coating film containing a fluororesin is formed on the surface of the steel sheet has been used.
例えば特許文献１には、非粘着持続性、加工性を高位に維持しながら、塗膜硬度及び耐摩耗性を改善することを目的として、平均粒径10〜100μmの鱗片状無機質添加材を配合した耐熱樹脂塗料から形成された下塗り塗膜が下地金属板に設けられ、その上に、平均粒径1μm以下の熱溶融性フッ素樹脂及び平均粒径10〜100μmの鱗片状無機質添加材を配合した耐熱樹脂塗料から形成された上塗り塗膜が設けられており、熱溶融性フッ素樹脂から生成した薄膜で塗膜最表層が覆われ、薄膜の下方にある塗膜に鱗片状無機質添加材及び粒状フッ素樹脂が分散していることを特徴とする耐摩耗性に優れた耐熱非粘着塗装金属板が開示されている。 For example, Patent Document 1 contains a scaly inorganic additive having an average particle size of 10 to 100 μm for the purpose of improving the coating film hardness and wear resistance while maintaining non-adhesive sustainability and workability at a high level. An undercoat film formed from the heat-resistant resin coating was provided on the base metal plate, and a heat-meltable fluororesin having an average particle size of 1 μm or less and a flaky inorganic additive having an average particle size of 10 to 100 μm were blended thereon. A top coat film formed from a heat-resistant resin paint is provided, the outermost layer of the paint film is covered with a thin film formed from a heat-meltable fluororesin, and the scaly inorganic additive and granular fluorine are applied to the paint film below the thin film. A heat-resistant and non-adhesive coated metal plate having excellent wear resistance, characterized by resin being dispersed, is disclosed.
また、特許文献２には、耐熱性及び密着性の向上を目的として、金属板の上に耐熱性樹脂を塗装後、最初に予備焼付けを行い、さらに本焼付けを行う二段階焼付けを行うことを特徴とする耐熱性プレコート金属板の製造方法が開示されている。 Patent Document 2 describes that for the purpose of improving heat resistance and adhesion, after performing heat-resistant resin on a metal plate, pre-baking is performed first, followed by two-step baking in which main baking is performed. A method for producing a heat-resistant precoated metal sheet is disclosed.
しかしながら、特許文献１及び特許文献２では、いずれも耐熱性樹脂として粒状のフッ素樹脂を塗膜中に含有しており、所望の耐熱性や耐汚染性を発現するためには、このフッ素樹脂を溶融させる必要があり、製造コストの高騰を招くという問題があった。粒状のフッ素樹脂を溶融させるためには、最低でも300℃以上の高温で焼付け乾燥を行わなければならず、通常の製造ラインで用いられる乾燥手段（最高到達鋼板温度：100〜250℃程度）ではなく、ラインとは別の特殊な乾燥装置を使用する必要があるためである。
そのため、製造コストの改善を図るべく、従来と同等以上の性能を有することに加えて、高温の焼付け乾燥を必要とすることなく通常の製造ラインで得ることができる表面処理鋼板の開発が望まれている。
However, in patent document 1 and patent document 2, both contain the granular fluororesin in a coating film as a heat resistant resin, and in order to express desired heat resistance and stain resistance, this fluororesin is used. There was a problem that it was necessary to melt, and the manufacturing cost was increased. In order to melt the granular fluororesin, it must be baked and dried at a high temperature of 300 ° C or more at the minimum, and with the drying means (maximum reached steel plate temperature: about 100 to 250 ° C) used in a normal production line This is because it is necessary to use a special drying device different from the line.
Therefore, in order to improve the manufacturing cost, in addition to having the same or better performance as before, the development of a surface-treated steel sheet that can be obtained on a normal production line without requiring high-temperature baking and drying is desired. ing.
また、非粘着持続性を付与する塗膜に使用されるフッ素樹脂は、撥水性を有するものが非粘着性に優れるという観点から、有効成分として炭素数が8以上のフルオロアルキル基を有するフッ素系重合体が用いられることが多かった（例えば特許文献３を参照。）。ただし、この炭素数が8以上のパーフルオロアルキル基を有するフッ素系重合体が分解されると、パーフルオロオクタン酸（ＰＦＯＡ）を生成することがある。このＰＦＯＡは、生体への蓄積が懸念されるため、近年では撥水・撥油剤などの分野では炭素数8以上のフルオロアルキル基を有するフッ素系重合体に代わる材料を用いることが望まれている。 In addition, the fluororesin used in the coating film that imparts non-adhesive durability is a fluorine-based resin having a fluoroalkyl group having 8 or more carbon atoms as an active ingredient from the viewpoint that those having water repellency are excellent in non-adhesiveness A polymer was often used (see, for example, Patent Document 3). However, when this fluoropolymer having a perfluoroalkyl group having 8 or more carbon atoms is decomposed, perfluorooctanoic acid (PFOA) may be produced. Since this PFOA is feared to accumulate in the living body, in recent years, in the fields of water and oil repellents, it is desired to use a material that replaces a fluoropolymer having a fluoroalkyl group having 8 or more carbon atoms. .
本発明の目的は、塗料組成物の適正化を図ることで、ＰＦＯＡの生成の懸念がなく、かつ高温の焼付け乾燥を必要とすることなく、優れた防汚性及び耐食性を有する表面処理鋼板を提供することにある。 An object of the present invention is to provide a surface-treated steel sheet that has excellent antifouling properties and corrosion resistance without concern for the formation of PFOA and without requiring high-temperature baking and drying by optimizing the coating composition. It is to provide.
本発明者らは、鋼板の両面に亜鉛系めっき層及び化成処理層が順次形成され、該化成処理層が形成された鋼板の少なくとも片面に、樹脂塗膜が形成された表面処理鋼板について、上記の課題を解決するため検討を重ねた結果、従来の樹脂塗膜中に含まれるフッ素系樹脂は、パーフルオロアルキル基、フルオロアルキレン基等を有しており、炭素原子（C）とフッ素原子（F）との共有結合のエネルギーが大きいため、難燃性、耐候性等に優れるものの、樹脂の融点上昇を招いていることに着目した。
そして、さらに鋭意研究を重ねた結果、前記樹脂塗膜を形成する材料として、炭素数が6以下のパーフルオロアルキル基及び水酸基を有するポリマー（Ａ）と、OH／NCOなる当量比が1.0〜10となるようにポリイソシアネート化合物（Ｂ）とを含む塗料組成物を用いることで、100〜250℃程度での架橋硬化が可能となるため、従来と同等の耐食性を有しつつ、従来に比べて低温で焼付け乾燥できることを見出した。また、得られた樹脂塗膜は、表面自由エネルギーが小さく、高い防汚性を実現できることも見出した。
The inventors of the present invention provide a surface-treated steel sheet in which a zinc-based plating layer and a chemical conversion treatment layer are sequentially formed on both surfaces of a steel plate, and a resin coating film is formed on at least one surface of the steel plate on which the chemical conversion treatment layer is formed. As a result of repeated studies to solve the above problem, the fluorine-based resin contained in the conventional resin coating film has a perfluoroalkyl group, a fluoroalkylene group, etc., and has carbon atoms (C) and fluorine atoms ( Since the energy of the covalent bond with F) is large, it was noted that although it was excellent in flame retardancy and weather resistance, it caused an increase in the melting point of the resin.
As a result of further earnest research, as a material for forming the resin coating film, a polymer (A) having a perfluoroalkyl group having 6 or less carbon atoms and a hydroxyl group and an equivalent ratio of OH / NCO of 1.0 to 10 are used. By using a coating composition containing a polyisocyanate compound (B) so as to become, it becomes possible to cross-link and cure at about 100 to 250 ° C. It was found that it can be baked and dried at low temperatures. It was also found that the obtained resin coating film has low surface free energy and can realize high antifouling properties.
本発明は、このような知見に基づきなされたもので、その要旨は以下の通りである。
（１）鋼板の両面に亜鉛系めっき層及び化成処理層が順次形成され、該化成処理層が形成された鋼板の少なくとも片面に、樹脂塗膜が形成された表面処理鋼板であって、前記樹脂塗膜は、炭素数が６以下のパーフルオロアルキル基及び水酸基を有するポリマー（Ａ）、並びに、ポリイソシアネート化合物（Ｂ）を含み、前記ポリマー（Ａ）のOHと前記ポリイソシアネート化合物（Ｂ）のNCOの当量比（OH／NCO）が1.0〜10である塗料組成物を、前記化成処理層の表面に塗布した後、100〜250℃の最高到達鋼板温度で乾燥してなることを特徴とする表面処理鋼板。
The present invention has been made based on such findings, and the gist thereof is as follows.
(1) A surface-treated steel sheet in which a zinc-based plating layer and a chemical conversion treatment layer are sequentially formed on both surfaces of a steel plate, and a resin coating film is formed on at least one surface of the steel plate on which the chemical conversion treatment layer is formed, The coating film contains a polymer (A) having a perfluoroalkyl group having 6 or less carbon atoms and a hydroxyl group, and a polyisocyanate compound (B), and the OH of the polymer (A) and the polyisocyanate compound (B). A coating composition having an NCO equivalent ratio (OH / NCO) of 1.0 to 10 is applied to the surface of the chemical conversion treatment layer and then dried at a maximum steel sheet temperature of 100 to 250 ° C. Surface treated steel sheet.
（２）前記塗料組成物中の前記ポリマー（Ａ）の固形分含有量が、10〜90質量％であることを特徴とする上記（１）に記載の表面処理鋼板。 (2) The surface-treated steel sheet according to (1) above, wherein the solid content of the polymer (A) in the coating composition is 10 to 90% by mass.
（３）前記塗料組成物は、エポキシ基含有化合物（Ｃ）及び／又はアクリル酸エステル系ポリマー（Ｄ）を、さらに含有することを特徴とする上記（１）又は（２）に記載の表面処理鋼板。 (3) The surface treatment according to (1) or (2) above, wherein the coating composition further contains an epoxy group-containing compound (C) and / or an acrylate polymer (D). steel sheet.
（４）前記塗料組成物中の前記エポキシ基含有化合物（Ｃ）及び／又はアクリル酸エステル系ポリマー（Ｄ）の固形分含有量が、合計で1〜10質量％であることを特徴とする上記（３）に記載の表面処理鋼板。 (4) The solid content of the epoxy group-containing compound (C) and / or the acrylate polymer (D) in the coating composition is 1 to 10% by mass in total. The surface-treated steel sheet according to (3).
（５）前記化成処理層が、防錆剤をさらに含むことを特徴とする上記（１）〜（４）のいずれかに記載の表面処理鋼板。 (5) The surface-treated steel sheet according to any one of (1) to (4), wherein the chemical conversion treatment layer further contains a rust inhibitor.
（６）前記樹脂塗膜の膜厚が、0.1〜5μmであることを特徴とする上記（１）〜（５）のいずれかに記載の表面処理鋼板。 (6) The surface-treated steel sheet according to any one of (1) to (5) above, wherein the resin coating film has a thickness of 0.1 to 5 μm.
本発明によれば、ＰＦＯＡの生成の懸念がなく、かつ高温の焼付け乾燥を必要とすることなく、優れた防汚性及び耐食性を有する表面処理鋼板を提供することが可能となった。 ADVANTAGE OF THE INVENTION According to this invention, it became possible to provide the surface treatment steel plate which has the antifouling property and corrosion resistance, without the concern of the production | generation of PFOA and without requiring high temperature baking drying.
以下、本発明の構成と限定理由を説明する。
本発明による表面処理鋼板は、鋼板の両面に亜鉛系めっき層及び化成処理層が順次形成され、該化成処理層が形成された鋼板の少なくとも片面に、樹脂塗膜が形成された表面処理鋼板である。
Hereinafter, the configuration of the present invention and the reasons for limitation will be described.
The surface-treated steel sheet according to the present invention is a surface-treated steel sheet in which a zinc-based plating layer and a chemical conversion treatment layer are sequentially formed on both surfaces of the steel plate, and a resin coating film is formed on at least one surface of the steel plate on which the chemical conversion treatment layer is formed. is there.
（亜鉛系めっき層）
本発明の亜鉛系めっき層については、特に制限されない。例えば、溶融亜鉛めっき又はこれを合金化した合金化溶融亜鉛めっき、さらには、溶融Zn−5質量%Al合金めっき、溶融Zn−55質量％Al合金めっき、電気亜鉛めっき、電気Zn−12質量%Ni合金めっき等によって形成される層が挙げられる。
(Zinc-based plating layer)
The zinc-based plating layer of the present invention is not particularly limited. For example, hot dip galvanizing or alloying hot dip galvanizing alloyed with this, further hot dip Zn-5 mass% Al alloy plating, hot dip Zn-55 mass% Al alloy plating, electrogalvanizing, electric Zn-12 mass% Examples thereof include a layer formed by Ni alloy plating or the like.
また、前記亜鉛系めっき層の付着量（g／m2）は、片面当たり5〜100g／m2の範囲であることが好ましい。5〜100g／m2の範囲であれば経済的な悪化を招くことなく、優れた耐食性が得られる。10〜70g／m2の範囲であることがより好ましい。 Further, the amount of deposition of the zinc-based plated layer (g / m 2) of preferably in the range of per side 5 to 100 g / m 2. If it is in the range of 5 to 100 g / m 2 , excellent corrosion resistance can be obtained without causing economic deterioration. A range of 10 to 70 g / m 2 is more preferable.
（化成処理層）
本発明の化成処理層は、主として前記亜鉛系めっき層と後述する樹脂塗膜との密着性を向上するために形成される。高い密着性を確保できれば特に限定はされないが、環境保護の観点からクロムを含有しないものとする。
なお、本発明の化成処理層は、クロムを含有しない従来公知の化成処理液をめっき層表面に塗布し、加熱乾燥することにより形成される。
(Chemical conversion treatment layer)
The chemical conversion treatment layer of the present invention is formed mainly for improving the adhesion between the zinc-based plating layer and a resin coating film described later. Although it will not specifically limit if high adhesiveness can be ensured, it shall not contain chromium from a viewpoint of environmental protection.
In addition, the chemical conversion treatment layer of this invention is formed by apply | coating the conventionally well-known chemical conversion treatment liquid which does not contain chromium to the plating layer surface, and heat-drying.
また、前記化成処理層は、密着性に加えて耐食性を向上させるために、防錆剤を含むことが好ましい。
防錆剤の種類については、特に限定はされず、例えば、リン酸亜鉛、亜リン酸亜鉛、リン酸アルミニウム、亜リン酸アルミニウム、リン酸マグネシウム、リン酸マンガン、モリブデン酸塩、リン酸モリブデン酸塩、バナジン酸／リン酸混合顔料、メタバナジン酸アンモニウム、シリカ、カルシウムシリケートと呼ばれるCaを吸着させたタイプのシリカ、炭酸亜鉛、炭酸ジルコニウムアンモニウム、等が挙げられる。
具体的には、密着性と耐食性の点からシリカ微粒子を含有し、耐食性の点からリン酸及び／又はリン酸化合物を含有することが好ましい。前記シリカ微粒子は、湿式シリカ、乾式シリカのいずれを用いても構わないが、密着性向上効果の大きいシリカ微粒子、特に乾式シリカが含有されることが好ましい。前記リン酸及びリン酸化合物については、例えば、オルトリン酸、ピロリン酸、ポリリン酸及びこれらの金属塩や化合物等のうちから選ばれる１種以上を含有すれば良い。
Moreover, it is preferable that the said chemical conversion treatment layer contains a rust preventive agent in order to improve corrosion resistance in addition to adhesiveness.
There are no particular restrictions on the type of rust inhibitor, such as zinc phosphate, zinc phosphite, aluminum phosphate, aluminum phosphite, magnesium phosphate, manganese phosphate, molybdate, and molybdate phosphate. Examples thereof include salts, vanadic acid / phosphoric acid mixed pigments, ammonium metavanadate, silica, silica of a type adsorbed with Ca called calcium silicate, zinc carbonate, and ammonium zirconium carbonate.
Specifically, silica fine particles are preferably contained from the viewpoint of adhesion and corrosion resistance, and phosphoric acid and / or a phosphoric acid compound are preferably contained from the viewpoint of corrosion resistance. As the silica fine particles, either wet silica or dry silica may be used, but it is preferable that silica fine particles having a large effect of improving adhesion, particularly dry silica, be contained. About the said phosphoric acid and a phosphoric acid compound, what is necessary is just to contain 1 or more types chosen from orthophosphoric acid, pyrophosphoric acid, polyphosphoric acid, these metal salts, a compound, etc., for example.
さらに、必要に応じて、アクリル樹脂、エポキシ樹脂、アミン変性エポキシ樹脂、ポリエステル樹脂などの樹脂、シランカップリング剤などの添加剤を添加することもできる。 Furthermore, additives such as resins such as acrylic resins, epoxy resins, amine-modified epoxy resins, and polyester resins, and silane coupling agents can be added as necessary.
なお、前記化成処理層の付着量は、片面当たり10〜500mg／m2の範囲であることが好ましい。化成処理層の付着量が10mg／m2以上であれば、密着性、耐食性が十分に得られ、一方、付着量が500mg／m2以下であれば経済的な悪化を招くことなく上記効果が得られるからである。
前記化成処理層は、ロールコーター、カーテンフローコーター、浸漬引き上げ法などで化成処理液を前記亜鉛系めっき層表面に塗布し、ローラー等で絞った後、水洗することなく最高到達鋼板温度が80〜140℃となるように乾燥することによって形成させることができる。
In addition, it is preferable that the adhesion amount of the said chemical conversion treatment layer is the range of 10-500 mg / m < 2 > per single side | surface. If the adhesion amount of the chemical conversion layer is 10 mg / m 2 or more, sufficient adhesion and corrosion resistance can be obtained. On the other hand, if the adhesion amount is 500 mg / m 2 or less, the above effects can be obtained without causing economic deterioration. It is because it is obtained.
The chemical conversion treatment layer is applied to the surface of the zinc-based plating layer by a roll coater, curtain flow coater, immersion pulling method, etc., and after squeezing with a roller or the like, the maximum reached steel sheet temperature is 80 to 80 without washing with water. It can be formed by drying to 140 ° C.
（樹脂塗膜）
本発明の樹脂塗膜は、炭素数が6以下のパーフルオロアルキル基及び水酸基を有するポリマー（Ａ）、並びに、ポリイソシアネート化合物（Ｂ）を含み、前記ポリマー（Ａ）のOHと前記ポリイソシアネート化合物（Ｂ）のNCOの当量比（OH／NCO）が1.0〜10である塗料組成物を、前記化成処理層の表面に塗布した後、100〜250℃の最高到達鋼板温度で乾燥してなることを特徴とする。
前記ポリマー（Ａ）及びポリイソシアネート化合物（Ｂ）を含み、前記ポリマー（Ａ）のOHと前記ポリイソシアネート化合物（Ｂ）のNCOの当量比（OH／NCO）を1.0〜10の範囲にすることで、ポリマーの架橋硬化温度を低く制御できる結果、通常の製造ラインで用いられる温度（最高到達鋼板温度：100〜250℃）の乾燥によってもパーフルオロアルキル基の作用による高い防汚性及び耐食性を実現できる。また、炭素数が6以下のパーフルオロアルキル基を有するポリマー（Ａ）を使用しているため、上述したＰＦＯＡの生成の懸念もない。
(Resin coating film)
The resin coating film of the present invention comprises a polymer (A) having a perfluoroalkyl group having 6 or less carbon atoms and a hydroxyl group, and a polyisocyanate compound (B). The OH of the polymer (A) and the polyisocyanate compound (B) A coating composition having an NCO equivalent ratio (OH / NCO) of 1.0 to 10 is applied to the surface of the chemical conversion treatment layer and then dried at a maximum steel sheet temperature of 100 to 250 ° C. It is characterized by.
By containing the polymer (A) and the polyisocyanate compound (B), the equivalent ratio (OH / NCO) of OH of the polymer (A) and NCO of the polyisocyanate compound (B) is in the range of 1.0 to 10. As a result of low control of the cross-linking and curing temperature of the polymer, high antifouling and corrosion resistance due to the action of perfluoroalkyl groups is achieved even by drying at temperatures used in normal production lines (maximum steel sheet temperature: 100 to 250 ° C) it can. Moreover, since the polymer (A) having a perfluoroalkyl group having 6 or less carbon atoms is used, there is no concern about the generation of PFOA described above.
・ポリマー（Ａ）
前記ポリマー（Ａ）は炭素数が6以下のパーフルオロアルキル基及び水酸基を有し、炭素数が6以下のパーフルオロアルキル基含有モノマー（ａ１）と、水酸基を含有するモノマー（ａ２）とを共重合させることにより得られる共重合体（コポリマー）である。
・ Polymer (A)
The polymer (A) has a perfluoroalkyl group having 6 or less carbon atoms and a hydroxyl group, and a perfluoroalkyl group-containing monomer (a1) having 6 or less carbon atoms and a monomer (a2) containing a hydroxyl group. It is a copolymer (copolymer) obtained by polymerizing.
炭素数が６以下のパーフルオロアルキル基含有モノマー（ａ１）としては、水素原子がフッ素原子で置換された炭素数1〜6、好ましくは2〜6の炭素原子を有するパーフルオロアルキル基又はフルオロアルキル基を有し、さらに共重合性の不飽和二重結合を併せ持つ化合物であればいずれも使用することができる。
前記パーフルオロアルキル基含有モノマー（ａ１）の具体例としては、パーフルオロヘキシルエチル（メタ）アクリレート、パーフルオロヘキシル（メタ）アクリレート、パーフルオロペンチルプロピル（メタ）アクリレート、パーフルオロペンチルエチル（メタ）アクリレート、パーフルオロブチルエチル（メタ）アクリレート、パーフルオロプロピルエチル（メタ）アクリレート、パーフルオロエチルエチル（メタ）アクリレート、パーフルオロエチルメチル（メタ）アクリレート等が挙げられ、これらの一種または二種以上を組み合わせて使用することができる。これらの化合物のうち、優れた防汚性を付与可能なフッ素系重合体が得られるという観点から、炭素数が５〜６のものが好ましい。
The perfluoroalkyl group-containing monomer (a1) having 6 or less carbon atoms is a perfluoroalkyl group or fluoroalkyl having 1 to 6 carbon atoms, preferably 2 to 6 carbon atoms, in which a hydrogen atom is substituted with a fluorine atom. Any compound having a group and further having a copolymerizable unsaturated double bond can be used.
Specific examples of the perfluoroalkyl group-containing monomer (a1) include perfluorohexylethyl (meth) acrylate, perfluorohexyl (meth) acrylate, perfluoropentylpropyl (meth) acrylate, and perfluoropentylethyl (meth) acrylate. , Perfluorobutylethyl (meth) acrylate, perfluoropropylethyl (meth) acrylate, perfluoroethylethyl (meth) acrylate, perfluoroethylmethyl (meth) acrylate, and the like. Can be used. Among these compounds, those having 5 to 6 carbon atoms are preferable from the viewpoint that a fluorine-based polymer capable of imparting excellent antifouling properties is obtained.
水酸基を含有するモノマー（ａ２）としては、アルコキシ基とポリエチレングリコールとを有する（メタ）アクリレートを使用することが好ましい。メトキシポリエチレングリコールアクリレート及びメトキシポリエチレングリコールメタクリレートから選ばれる一種以上のモノマーがより好ましい。
この水酸基含有モノマー（ａ２）は共重合体中に架橋点を持たせるものとして重要であり、ポリマー（Ａ）を構成するモノマーの合計質量に対して10〜50質量％の割合で含まれていることが好ましい。水酸基含有モノマー（ａ２）が10質量％以上であれば十分な塗膜性能が得られ、50質量％以下であれば架橋密度が高くなりすぎることがなく、樹脂塗膜が脆くなることがないので好ましい。
As the monomer (a2) containing a hydroxyl group, it is preferable to use a (meth) acrylate having an alkoxy group and polyethylene glycol. One or more monomers selected from methoxypolyethylene glycol acrylate and methoxypolyethylene glycol methacrylate are more preferable.
This hydroxyl group-containing monomer (a2) is important as having a crosslinking point in the copolymer, and is contained in a proportion of 10 to 50% by mass relative to the total mass of monomers constituting the polymer (A). It is preferable. If the hydroxyl group-containing monomer (a2) is 10% by mass or more, sufficient coating performance can be obtained, and if it is 50% by mass or less, the crosslinking density does not become too high and the resin coating does not become brittle. preferable.
さらに、上記２種のモノマー（ａ１）と（ａ２）以外にも、公知のモノマーを重合させることができる。例えば、スチレン、ビニルトルエンなどの芳香族系ビニル化合物、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ-ブチル（メタ）アクリレートなどの（メタ）アクリル酸エステル類、マレイン酸、フマル酸もしくはイタコン酸などの不飽和ジカルボン酸類、（メタ）アクリルアミド、ジメチル（メタ）アクリルアミドもしくはN-アルコキシメチル化（メタ）アクリルアミドなどの（メタ）アクリルアミド類、ジメチルアミノエチル（メタ）アクリレートなどのＮ，Ｎ-ジアルキルアミノアルキル（メタ）アクリレート類、β-アシッドホスホキシ（メタ）アクリレートなどの燐酸基含有（メタ）アクリレート類、アクリル酸、マレイン酸、フマル酸もしくはイタコン酸などの不飽和カルボン酸と1価アルコールとのモノエステル類などが例示される。 Furthermore, in addition to the two types of monomers (a1) and (a2), known monomers can be polymerized. For example, aromatic vinyl compounds such as styrene and vinyltoluene, (meth) acrylic acid esters such as methyl (meth) acrylate, ethyl (meth) acrylate and n-butyl (meth) acrylate, maleic acid, fumaric acid or itacone Unsaturated dicarboxylic acids such as acids, (meth) acrylamides, (meth) acrylamides such as dimethyl (meth) acrylamide or N-alkoxymethylated (meth) acrylamide, and N, N-dialkyls such as dimethylaminoethyl (meth) acrylate Phosphoric acid group-containing (meth) acrylates such as aminoalkyl (meth) acrylates, β-acid phosphoxy (meth) acrylates, unsaturated carboxylic acids such as acrylic acid, maleic acid, fumaric acid or itaconic acid, and monohydric alcohols Monoester Etc. are exemplified.
パーフルオロアルキル基含有モノマー（ａ１）と水酸基含有モノマー（ａ２）とを共重合させる際に用いる溶媒としては、モノマーを溶解または縣濁しうるものであればよく、例えば、水、トルエン、キシレン、ｎ−ヘプタン、シクロヘキサン、テトラヒドロフラン、ｎ−ヘキサン、およびイソヘキサン等を単独、または２種以上を混合して使用することができる。 The solvent used when copolymerizing the perfluoroalkyl group-containing monomer (a1) and the hydroxyl group-containing monomer (a2) may be any solvent that can dissolve or suspend the monomer. For example, water, toluene, xylene, n -Heptane, cyclohexane, tetrahydrofuran, n-hexane, isohexane and the like can be used alone or in admixture of two or more.
また、前記ポリマー（Ａ）の重量平均分子量は、10000〜100000の範囲であることが好ましい。重量平均分子量が10000以上であれば耐溶剤性が低下しない。また、重量平均分子量が100000以下であれば塗料組成物としての粘度が高くなりすぎることがないため、塗料組成物の塗布が困難となることがない。 The weight average molecular weight of the polymer (A) is preferably in the range of 10,000 to 100,000. If the weight average molecular weight is 10,000 or more, the solvent resistance is not lowered. Further, when the weight average molecular weight is 100,000 or less, the viscosity of the coating composition does not become too high, so that it is not difficult to apply the coating composition.
・ポリイソシアネート化合物（Ｂ）
本発明の塗料組成物を構成するポリイソシアネート化合物（Ｂ）は上記ポリマー（Ａ）の水酸基との架橋反応を100〜250℃の乾燥でも生じさせることが可能となり上記ポリマー（Ａ）を硬化させ、樹脂塗膜を形成させる。ポリイソシアネート化合物（Ｂ）としては、トリレンジイソシアネート、ジフェニルメタンジイソシアネートもしくはキシリレンジイソシアネートなどの芳香族ジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネートもしくはトリメチルヘキサンジイソシアネートなどの脂肪族ジイソシアネート、イソホロンジイソシアネートなどの脂環族ジイソシアネート、あるいはこれらの各ジイソシアネートとエチレングリコール、プロピレングリコール、ネオペンチルグリコールなどの多価アルコール類などが好適に用いられる。
・ Polyisocyanate compound (B)
The polyisocyanate compound (B) constituting the coating composition of the present invention can cause a crosslinking reaction with the hydroxyl group of the polymer (A) even by drying at 100 to 250 ° C., thereby curing the polymer (A), A resin coating is formed. Examples of the polyisocyanate compound (B) include aromatic diisocyanates such as tolylene diisocyanate, diphenylmethane diisocyanate or xylylene diisocyanate, aliphatic diisocyanates such as tetramethylene diisocyanate, hexamethylene diisocyanate or trimethylhexane diisocyanate, and alicyclic diisocyanates such as isophorone diisocyanate. Alternatively, these diisocyanates and polyhydric alcohols such as ethylene glycol, propylene glycol, and neopentyl glycol are preferably used.
・ポリマー（Ａ）のOHとポリイソシアネート化合物（Ｂ）のNCOの当量比（OH／NCO）が1.0〜10
ポリマー（Ａ）とポリイソシアネート化合物（Ｂ）の配合比については、ポリマー（Ａ）のOHとポリイソシアネート化合物（Ｂ）の当量比（OH／NCO）で、1.0〜10の範囲となるようにする。すなわち、前記当量比（OH／NCO）が10を超えると、十分な塗膜性能が得られず、耐溶剤性が劣る。一方、前記当量比（OH／NCO）が１．０未満の場合には、樹脂塗膜が脆くなり、発泡しやすくなるため、塗装性を阻害し、十分な塗膜性能が得られない。
-The equivalent ratio (OH / NCO) of OH of the polymer (A) and NCO of the polyisocyanate compound (B) is 1.0 to 10
The blending ratio of the polymer (A) and the polyisocyanate compound (B) should be in the range of 1.0 to 10 with the equivalent ratio (OH / NCO) of the OH and the polyisocyanate compound (B) of the polymer (A). . That is, when the equivalent ratio (OH / NCO) exceeds 10, sufficient film performance cannot be obtained and solvent resistance is poor. On the other hand, when the equivalent ratio (OH / NCO) is less than 1.0, the resin coating film becomes brittle and easily foams, so that the paintability is hindered and sufficient coating film performance cannot be obtained.
さらに、前記塗料組成物中の前記ポリマー（Ａ）の含有量が、10〜90質量％であることが好ましい。ポリマー（Ａ）の含有量が10質量％以上であれば、防汚性が低下することがなく、一方、含有量が90質量％以下であれば、形成された樹脂塗膜が硬くなりすぎることがなく、加工時にクラックを生じることがなく、加工後外観や耐食性が低下しない。 Furthermore, it is preferable that content of the said polymer (A) in the said coating composition is 10-90 mass%. If the content of the polymer (A) is 10% by mass or more, the antifouling property does not decrease, while if the content is 90% by mass or less, the formed resin coating film becomes too hard. No cracks are generated during processing, and the appearance and corrosion resistance after processing do not deteriorate.
また、前記塗料組成物は、前記化成処理層との密着性を向上させる点から、エポキシ基含有化合物（Ｃ）を含有することが好ましい。
エポキシ基含有化合物（Ｃ）としては、例えば、エピクロルヒドリン−ビスフェノールＡ型、ノボラック型、グリシジルエーテル型、グリシジルエステル型、グリコールエーテル型、ポリグリコールエーテル型、多価カルボン酸エステル型、アミノグリシジル型、塩素化型、レゾルシン型といった公知の各種のエポキシ基含有ポリマー等が挙げられる。その他にも、フェニルグリシジルエーテル、ｎ−ブチルグリシジルエーテル、アリルグリシジルエーテル、フェノキシエーテル系グリシジルエーテル、α−オレフィンオキサイド、エピクロルヒドリン、スチレンオキサイドなどといったモノエポキシ型のエポキシ基含有化合物も用いることができる。
Moreover, it is preferable that the said coating composition contains an epoxy group containing compound (C) from the point which improves adhesiveness with the said chemical conversion treatment layer.
Examples of the epoxy group-containing compound (C) include epichlorohydrin-bisphenol A type, novolak type, glycidyl ether type, glycidyl ester type, glycol ether type, polyglycol ether type, polycarboxylic acid ester type, aminoglycidyl type, chlorine Various known epoxy group-containing polymers such as a chemical type and a resorcin type are included. In addition, monoepoxy type epoxy group-containing compounds such as phenyl glycidyl ether, n-butyl glycidyl ether, allyl glycidyl ether, phenoxy ether glycidyl ether, α-olefin oxide, epichlorohydrin, styrene oxide, and the like can also be used.
さらに、前記エポキシ基含有化合物（Ｃ）は、塗料組成物の1〜10質量％であることが好ましい。1質量％以上であれば、化成処理層との密着性が向上し、10質量％以下であれば樹脂塗膜の耐溶剤性が劣化しない。 Furthermore, it is preferable that the said epoxy-group containing compound (C) is 1-10 mass% of a coating composition. If it is 1 mass% or more, the adhesiveness with a chemical conversion treatment layer will improve, and if it is 10 mass% or less, the solvent resistance of a resin coating film will not deteriorate.
また、前記塗料組成物は、耐溶剤性及び化成処理層との密着性向上の点から、アクリル酸エステル系ポリマー（Ｄ）を含有することが好ましい。アクリル酸エステル系ポリマー（Ｄ）は、ホモポリマーであってもコポリマーであってもよい。アクリル酸エステル系ポリマー（Ｄ）を構成するモノマーとしては、アクリル酸メチル、アクリル酸エチル、アクリル酸ｎ−ブチル、アクリル酸イソブチル、アクリル酸２−エチルヘキシル、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ｎ-ブチル、メタクリル酸イソブチル、メタクリル酸ｎ−ヘキシル、メタクリル酸ラウリル等が挙げられる。これらのモノマーと共重合しうるその他のモノマーとしては、例えば、スチレン及びその誘導体類などの他のビニルモノマー、あるいはアクリル酸、メタクリル酸、アクリルアミド、メタクリルアミド、アクリル酸グリシジル、メタクリル酸グリシジル、アクリル酸ヒドロキシエチル、メタクリル酸ヒドロキシエチル、プロピルメタクリル酸ヒドロキシプロピルといった官能基を含有するモノマーなどが挙げられる。 Moreover, it is preferable that the said coating composition contains an acrylic ester polymer (D) from the point of solvent resistance and the adhesive improvement with a chemical conversion treatment layer. The acrylic ester polymer (D) may be a homopolymer or a copolymer. As monomers constituting the acrylate polymer (D), methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, n methacrylate -Butyl, isobutyl methacrylate, n-hexyl methacrylate, lauryl methacrylate and the like. Other monomers that can be copolymerized with these monomers include, for example, other vinyl monomers such as styrene and its derivatives, or acrylic acid, methacrylic acid, acrylamide, methacrylamide, glycidyl acrylate, glycidyl methacrylate, acrylic acid Examples thereof include monomers containing a functional group such as hydroxyethyl, hydroxyethyl methacrylate, and propyl hydroxypropyl methacrylate.
さらに、前記アクリル酸エステル系ポリマー（Ｄ）は、塗料組成物の1〜10質量％であることが好ましい。1質量％以上であれば、化成処理層との密着性が向上し、10質量％以下であれば耐溶剤性に優れる。 Furthermore, the acrylate polymer (D) is preferably 1 to 10% by mass of the coating composition. If it is 1 mass% or more, the adhesiveness with a chemical conversion treatment layer will improve, and if it is 10 mass% or less, it will be excellent in solvent resistance.
なお、前記エポキシ基含有化合物（Ｃ）と前記アクリル酸エステル系ポリマー（Ｄ）は、前記塗料組成物中に、いずれか一方が含まれても、両方が含まれても良い。
また、前記エポキシ基含有化合物（Ｃ）及び前記アクリル酸エステル系ポリマー（Ｄ）がいずれも含まれる場合には、合計の含有量が、塗料組成物の1〜10質量％であることが好ましい。
The epoxy group-containing compound (C) and the acrylate ester polymer (D) may be included in the coating composition, or both of them may be included.
Moreover, when both the said epoxy-group containing compound (C) and the said acrylic ester polymer (D) are contained, it is preferable that total content is 1-10 mass% of a coating composition.
前記塗料組成物は、必要に応じて、乾燥剤、湿潤剤、増粘剤、顔料分散剤、レベリング剤、泡消し剤、はじき防止剤、ブロッキング防止剤、紫外線吸収剤等といった、その他の添加物を配合することも可能である。
また、塗料組成物の希釈媒として、トルエン、キシレンなどの有機溶剤を使用することができる。
The coating composition may contain other additives such as a drying agent, a wetting agent, a thickening agent, a pigment dispersant, a leveling agent, a defoaming agent, an anti-fogging agent, an anti-blocking agent, and an ultraviolet absorber. It is also possible to blend.
Moreover, organic solvents, such as toluene and xylene, can be used as a diluent of a coating composition.
・塗布と乾燥
本発明の樹脂塗膜を形成するための塗布は前記塗料組成物を化成処理層の表面に塗布できる方法であればよく、特に限定されない。ロールコーター、カーテンフローコーター、浸漬引き上げ法等によって塗布し、目的とする膜厚となるように塗料組成物の付着量を制御すればよい。
本発明の樹脂塗膜を形成するための乾燥は、最高到達鋼板温度で、100〜250℃の範囲である。これによって、通常の塗装ラインで鋼板上に樹脂塗膜を形成することが可能となる。
前記乾燥温度が100℃未満の場合、温度が低すぎるため乾燥が不十分となり、形成された塗膜の耐溶剤性の劣化を招く。一方、前記乾燥温度が250℃を超えると、従来の製造ラインによって製造できず、経済性の悪化を招く。
-Application | coating and drying Application | coating for forming the resin coating film of this invention should just be a method which can apply | coat the said coating composition on the surface of a chemical conversion treatment layer, and is not specifically limited. Coating may be performed by a roll coater, a curtain flow coater, a dipping method, or the like, and the amount of the coating composition deposited may be controlled so as to achieve a target film thickness.
Drying for forming the resin coating film of the present invention is in the range of 100 to 250 ° C. at the maximum attained steel plate temperature. Thereby, it becomes possible to form a resin coating film on a steel plate with a normal coating line.
When the drying temperature is less than 100 ° C., the temperature is too low, so that the drying is insufficient and the solvent resistance of the formed coating film is deteriorated. On the other hand, if the drying temperature exceeds 250 ° C., it cannot be produced by a conventional production line, resulting in deterioration of economy.
また、前記乾燥の時間（最高到達鋼板温度に到達するまでの時間）は、1〜60秒の範囲であることが好ましい。乾燥時間が1秒以上であれば、時間が短すぎることがないため乾燥が不十分となることがなく、形成された塗膜の耐溶剤性の劣化を招くことがない。一方、乾燥時間が60秒以下であれば、経済的に好ましい。
なお、前記塗料組成物を乾燥するための方法については、最高到達鋼板温度が100〜250℃なるように好ましくは１〜60秒で加熱できる方法であればよく、特に限定されない。
Moreover, it is preferable that the said drying time (time until it reaches the maximum attained steel plate temperature) is in the range of 1 to 60 seconds. If the drying time is 1 second or longer, the time will not be too short, so that the drying will not be insufficient, and the solvent resistance of the formed coating film will not deteriorate. On the other hand, if the drying time is 60 seconds or less, it is economically preferable.
In addition, about the method for drying the said coating composition, what is necessary is just a method which can be heated in 1 to 60 second so that the highest attained steel plate temperature may be 100-250 degreeC, and it does not specifically limit.
また、形成された前記樹脂塗膜の膜厚は、0.1〜5μmの範囲であることが好ましい。膜厚が0.1μm以上であれば、塗膜が鋼板を十分に覆うことができ、防汚性の低下を招くことがない。一方、膜厚が5μm以下であれば、経済的に防汚効果を有することができる。 The film thickness of the formed resin coating film is preferably in the range of 0.1 to 5 μm. When the film thickness is 0.1 μm or more, the coating film can sufficiently cover the steel sheet, and the antifouling property is not lowered. On the other hand, if the film thickness is 5 μm or less, it can have an antifouling effect economically.
上述したところは、この発明の実施形態の一例を示したにすぎず、請求の範囲において種々の変更を加えることができる。 The above description is merely an example of the embodiment of the present invention, and various modifications can be made within the scope of the claims.
本発明の実施例について説明する。
（サンプル１〜１２）
亜鉛系めっき鋼板として、各々板厚0.8mmの溶融亜鉛めっき鋼板（めっき種記号：ＧＩ）を準備した。ＧＩのめっき付着量は片面あたり60g／m2である。
なお、亜鉛系めっき鋼板の一方の面（オモテ面）と他方の面（ウラ面）のめっき付着量、及びめっき組成は同一とした。
準備しためっき鋼板に脱脂処理を行った後、以下の処理工程を行い、表面処理鋼板のサンプルを作製した。
Examples of the present invention will be described.
(Samples 1-12)
As galvanized steel sheets, hot dip galvanized steel sheets (plating type symbol: GI) each having a thickness of 0.8 mm were prepared. The amount of GI plating is 60 g / m 2 per side.
In addition, the plating adhesion amount and the plating composition of one surface (front surface) and the other surface (back surface) of the galvanized steel sheet were the same.
After the degreased treatment was performed on the prepared plated steel sheet, the following treatment process was performed to prepare a sample of the surface-treated steel sheet.
（Ｉ）オモテ面に表２に示す化成処理液を塗布し、加熱10秒後に最高到達鋼板温度が100℃となるように加熱し、オモテ面の化成処理層を形成した。次に、オモテ面と同様の条件でウラ面の化成処理層を形成した。
（ＩＩ）その後、オモテ面に、次に示すようにして作製したポリマー（Ａ）のＡ−１、Ａ−２、ポリイソシアネート化合物（Ｂ）のＢ−１、Ｂ−２、エポキシ基含有化合物（Ｃ）のＣ−１、及びアクリル酸エステル系ポリマー（Ｄ）のＤ−１を含み、残部がミネラルスピリット、トルエン、キシレンからなる混合溶媒であり、表１に示す組成からなる塗料組成物を塗布し、表１に示す時間で最高到達鋼板温度となるような条件で焼付け乾燥を行うことで、表１示す膜厚の樹脂塗膜を形成した。
(I) The chemical conversion treatment liquid shown in Table 2 was applied to the front surface, and heated so that the maximum steel plate temperature reached 100 ° C. after 10 seconds of heating, to form a chemical conversion treatment layer on the front surface. Next, the chemical conversion treatment layer of the back surface was formed under the same conditions as the front surface.
(II) Thereafter, on the front side, A-1 and A-2 of the polymer (A) prepared as shown below, B-1 and B-2 of the polyisocyanate compound (B), an epoxy group-containing compound ( C) of C) and D-1 of acrylic ester polymer (D), the balance being a mixed solvent composed of mineral spirit, toluene and xylene, and a coating composition having the composition shown in Table 1 applied And the resin coating film of the film thickness shown in Table 1 was formed by performing baking drying on the conditions which become the maximum reached steel plate temperature in the time shown in Table 1.
なお、表１中の、ポリマー（Ａ−１）及び（Ａ−２）については、以下の手順で製造した。
・ポリマー（Ａ−１）
攪拌装置、不活性ガス導入口、温度計及び冷却器をとりつけた四つ口フラスコに、キシレン200質量部及び酢酸ブチル500質量部を入れて120℃に昇温した。同温度でパーフルオロシクロヘキシルアクリレート（CH2=CH-COOCH2-C6F11）600質量部、βヒドロキシエチルアクリレート94質量部、メチルメタクリレート200質量部、ｎ−ブチルメタクリレート100質量部、アクリル酸10質量部、酢酸ブチル300質量部、ＡＩＢＮ20質量部、ｔ−ブチルパークタエート10質量部およびジ−ｔ−ブチルパーオキシド10質量部からなる混合物を4時間滴下し、滴下終了後も120℃で約15時間保持した。このようにして、水酸基含有モノマーを10.4質量％含み、分子量50000、OH価20であり、炭素数が６以下のパーフルオロアルキル基及び水酸基を有するポリマーを含む樹脂溶液を得た。
In addition, about the polymer (A-1) and (A-2) in Table 1, it manufactured with the following procedures.
・ Polymer (A-1)
In a four-necked flask equipped with a stirrer, an inert gas inlet, a thermometer, and a condenser, 200 parts by mass of xylene and 500 parts by mass of butyl acetate were added and heated to 120 ° C. At the same temperature, perfluorocyclohexyl acrylate (CH 2 = CH-COOCH 2 -C 6 F 11 ) 600 parts by mass, β-hydroxyethyl acrylate 94 parts by mass, methyl methacrylate 200 parts by mass, n-butyl methacrylate 100 parts by mass, acrylic acid 10 A mixture consisting of 10 parts by mass, 300 parts by mass of butyl acetate, 20 parts by mass of AIBN, 10 parts by mass of t-butyl percarbonate and 10 parts by mass of di-t-butyl peroxide was added dropwise for 4 hours. Hold for 15 hours. In this way, a resin solution containing 10.4% by mass of a hydroxyl group-containing monomer, a molecular weight of 50,000, an OH value of 20, a perfluoroalkyl group having 6 or less carbon atoms and a polymer having a hydroxyl group was obtained.
・ポリマー（Ａ−２）
攪拌装置、不活性ガス導入口、温度計および冷却器をとりつけた四つ口フラスコに、トルエン300質量部及び酢酸イソブチル500質量部を仕込んで120℃に昇温した。モノブチル・モノ（３，３，４，４，５，５，５−ヘプタフルオロ−２−ペンチル）フマレート80質量部、β−ヒドロキシエチルメタクリレート230質量部、スチレン350質量部、メチルメタクリレート180質量部、ジブチルフマレート50質量部、ｎ−ブチルアクリレート100質量部、アクリル酸8質量部、酢酸ブチル200質量部、ＡＩＢＮ10質量部、ｔ−ブチルパーベンゾエート10質量部及びジ-ｔ-ブチルパーオキシド5質量部からなる混合物を同温度で6時間かけて滴下し、120℃で10時間保持した。このようにして、水酸基含有モノマーを23.8質量％含み、分子量10000、OH価50であり、炭素数が６以下のパーフルオロアルキル基及び水酸基を有するポリマーを含む樹脂溶液を得た。
・ Polymer (A-2)
A four-necked flask equipped with a stirrer, an inert gas inlet, a thermometer and a condenser was charged with 300 parts by mass of toluene and 500 parts by mass of isobutyl acetate and heated to 120 ° C. Monobutyl mono (3,3,4,4,5,5,5-heptafluoro-2-pentyl) fumarate 80 parts by mass, β-hydroxyethyl methacrylate 230 parts by mass, styrene 350 parts by mass, methyl methacrylate 180 parts by mass, 50 parts by weight of dibutyl fumarate, 100 parts by weight of n-butyl acrylate, 8 parts by weight of acrylic acid, 200 parts by weight of butyl acetate, 10 parts by weight of AIBN, 10 parts by weight of t-butyl perbenzoate and 5 parts by weight of di-t-butyl peroxide The mixture consisting of was added dropwise at the same temperature over 6 hours and kept at 120 ° C. for 10 hours. In this way, a resin solution containing a polymer having a hydroxyl group-containing monomer of 23.8% by mass, a molecular weight of 10,000, an OH value of 50, a C6 or less perfluoroalkyl group and a hydroxyl group was obtained.
また、表１中の、ポリイソシアネート化合物（Ｂ−１）及び（Ｂ−２）、エポキシ基含有化合物（Ｃ−１）並びにアクリル酸エステル系ポリマー（Ｄ−１）については、以下のものを用いた。
・ポリイソシアネート化合物（Ｂ−１）： ＤＩＣ製 ヘキサメチレンジイソシアネート系 バーノック（登録商標）ＤＮ−９５０
・ポリイソシアネート化合物（Ｂ−２）： ＤＩＣ製 バーノック（登録商標）Ｄ−８００
・エポキシ基含有化合物（Ｃ−１）： バーサティック酸グリシジルエステル
・アクリル酸エステル系ポリマー（Ｄ−１）： アクリル酸ｎ−ブチル・メタクリル酸２−ヒドロキシエチル・アクリル酸・スチレンコポリマー
Moreover, about the polyisocyanate compounds (B-1) and (B-2), the epoxy group-containing compound (C-1), and the acrylic ester polymer (D-1) in Table 1, the following are used. It was.
Polyisocyanate compound (B-1): DIC hexamethylene diisocyanate-based Barnock (registered trademark) DN-950
Polyisocyanate compound (B-2): Burnock (registered trademark) D-800 manufactured by DIC
-Epoxy group-containing compound (C-1): Versatic acid glycidyl ester-Acrylic acid ester polymer (D-1): N-butyl acrylate-2-hydroxyethyl methacrylate-Acrylic acid-Styrene copolymer
＊０ 表１中の種類Ａ〜Ｅは、表２に示したものである。
＊１ 乾式シリカ：日本エアロジル（株）製 アエロジル＃２００
＊２ Zr化合物：第一稀元素化学工業（株）製 炭酸ジルコニウムアンモニウム
＊３ 湿式シリカ：日産化学工業（株）製 スノーテックス０
＊４ Ca交換シリカ：Ｇｒａｃｅ Ｄａｖｉｓｏｎ製シールデックスＣ３０３
* 0 Types A to E in Table 1 are those shown in Table 2.
* 1 Dry silica: Aerosil # 200 manufactured by Nippon Aerosil Co., Ltd.
* 2 Zr compound: Daiichi Rare Element Chemical Industry Co., Ltd. Zirconium Ammonium Carbonate * 3 Wet Silica: Nissan Chemical Industries Co., Ltd. Snowtex 0
* 4 Ca exchanged silica: Shielddex C303 manufactured by Grace Davison
（評価）
以上のようにして得られた表面処理鋼板のサンプルについて、各種評価を行った。評価方法を以下に示す。
(Evaluation)
Various evaluation was performed about the sample of the surface treatment steel plate obtained by making it above. The evaluation method is shown below.
（１）防汚性
各サンプルに対して、Ｑ印フェルトペン（赤色、黒色）でインクを塗布した後、温度20℃、相対湿度65％の恒温恒湿室にて24時間放置した。その後、インクを乾燥ガーゼで拭き取り、インクの残存状態を目視観察して、以下の基準に従って評価した。評価結果を表３に示す。
◎：色残りなし
○：軽微な色残りあり
△：色残りあり
×：色が全く落ちない
(1) Antifouling property Each sample was coated with ink with a Q-mark felt pen (red, black) and then allowed to stand in a constant temperature and humidity chamber at a temperature of 20 ° C. and a relative humidity of 65% for 24 hours. Thereafter, the ink was wiped off with dry gauze, and the remaining state of the ink was visually observed and evaluated according to the following criteria. The evaluation results are shown in Table 3.
◎: No color residue ○: Minor color residue △: Color residue present ×: Color does not fade at all
（２）耐食性
各サンプルから、試験片（大きさ：100mm×50mm）を切り出し、試験片の端部および裏面をテープシールした後、ＪＩＳ Ｚ２３７１−２０００に準拠し、5質量％塩水を35℃で24時間噴霧し続けた。その後、試験片の状態を目視により観察し、以下の基準に従って評価を行った。評価結果を表３に示す。
◎：表面に変化なし
○：表面に若干の発錆がある
×：表面に多数の発錆がある
(2) Corrosion resistance After cutting out a test piece (size: 100 mm x 50 mm) from each sample and tape-sealing the end and back of the test piece, 5 mass% salt water was added at 35 ° C according to JIS Z2371-2000. Spraying continued for 24 hours. Thereafter, the state of the test piece was visually observed and evaluated according to the following criteria. The evaluation results are shown in Table 3.
◎: No change on the surface ○: Some rusting on the surface ×: Many rusting on the surface
（３）耐溶剤性
各サンプルの樹脂塗膜の表面に対し、メチルエチルケトンを浸したガーゼによるラビング試験を、4.9N(0.5kgf)の荷重で１０回行った。その後、樹脂塗膜表面の状態を目視により観察し、以下の基準に従って評価した。評価結果を表３に示す。
◎：表面に変化なし
○：表面に若干の変化がある
×：表面に明瞭な変化がある、または下地の露出がある
(3) Solvent resistance The surface of the resin coating film of each sample was subjected to a rubbing test with gauze dipped in methyl ethyl ketone 10 times with a load of 4.9 N (0.5 kgf). Thereafter, the surface state of the resin coating film was visually observed and evaluated according to the following criteria. The evaluation results are shown in Table 3.
◎: No change on the surface ○: There is a slight change on the surface ×: There is a clear change on the surface, or there is exposure of the base
表３の結果から、本発明の範囲である発明例の各サンプル１〜６及び１０〜１２は、最高到達鋼板温度が250℃以下の焼付け乾燥であっても、比較例のサンプル７〜９に比べて、防汚性、耐食性及び耐溶剤性のいずれについても良好な結果を示すことがわかった。 From the results of Table 3, the samples 1 to 6 and 10 to 12 of the invention examples that are within the scope of the present invention are the same as the samples 7 to 9 of the comparative example, even if the highest achieved steel plate temperature is baked and dried at 250 ° C. or less. In comparison, it was found that good results were obtained with respect to antifouling properties, corrosion resistance, and solvent resistance.
本発明によれば、高温の焼付け乾燥を必要とすることなく、優れた防汚性及び耐食性を有する表面処理鋼板の提供が可能となった。その結果、従来に比べてより低コストで優れた表面処理鋼板を得ることができ、産業上有用である。 According to the present invention, it is possible to provide a surface-treated steel sheet having excellent antifouling properties and corrosion resistance without requiring high-temperature baking and drying. As a result, an excellent surface-treated steel sheet can be obtained at a lower cost than in the prior art, which is industrially useful.
Claims (6)
前記樹脂塗膜は、炭素数が６以下のパーフルオロアルキル基及び水酸基を有するポリマー（Ａ）、並びに、ポリイソシアネート化合物（Ｂ）を含み、前記ポリマー（Ａ）のOHと前記ポリイソシアネート化合物（Ｂ）のNCOの当量比（OH／NCO）が1.0〜10である塗料組成物を、前記化成処理層の表面に塗布した後、100〜250℃の最高到達鋼板温度で乾燥してなることを特徴とする表面処理鋼板。 A zinc-based plating layer and a chemical conversion treatment layer are sequentially formed on both surfaces of the steel plate, and is a surface-treated steel plate in which a resin coating is formed on at least one surface of the steel plate on which the chemical conversion treatment layer is formed,
The resin coating film includes a polymer (A) having a perfluoroalkyl group having 6 or less carbon atoms and a hydroxyl group, and a polyisocyanate compound (B). The OH of the polymer (A) and the polyisocyanate compound (B The coating composition having an NCO equivalent ratio (OH / NCO) of 1.0 to 10 is applied to the surface of the chemical conversion treatment layer and then dried at a maximum steel sheet temperature of 100 to 250 ° C. A surface-treated steel sheet.
The surface-treated steel sheet according to any one of claims 1 to 5, wherein the resin coating film has a thickness of 0.1 to 5 µm.