JP5843907B2 - Colored photosensitive resin composition, black matrix, color filter, and liquid crystal display - Google Patents

Description

  The present invention relates to a colored photosensitive resin composition, a black matrix, a color filter, and a liquid crystal display.

  A display body such as a liquid crystal display has a structure in which a liquid crystal layer is sandwiched between two substrates on which a pair of electrodes facing each other is formed. A color filter made up of pixel regions of each color such as red (R), green (G), and blue (B) is formed inside one substrate. In this color filter, normally, a black matrix is formed so as to partition red, green, and blue pixel regions.

  Generally, a color filter is manufactured by a lithography method. That is, first, a black colored photosensitive resin composition is applied and dried on a substrate, and then exposed and developed to form a black matrix. Next, for each colored photosensitive resin composition of each color of red, green, and blue, coating, drying, exposure, and development are repeated to form a pixel region of each color at a predetermined position to manufacture a color filter.

  In recent years, in the manufacture of a liquid crystal display, an attempt has been made to improve the contrast of an image displayed on the liquid crystal display by improving the light shielding property by the black matrix. In order to improve the light shielding property by the black matrix, it is necessary to increase the amount of the black pigment added to the black resist.

  Here, Patent Document 1 discloses, as an example of a colored photosensitive resin composition, a black resist composition containing a binder resin made of an acrylic resin and carbon black that is a black pigment.

Japanese Patent Application Laid-Open No. 10-010311

  However, in the invention described in Patent Document 1, when the content of the black pigment is increased in order to improve the light-shielding property of the black matrix, in the vacuum drying (VCD, vacuum drying) step after the coating film, There was a problem that aggregates were generated by the aggregation.

  The present invention has been made in view of the above problems, and is capable of preventing the formation of aggregates at the time of drying under reduced pressure after application of a colored photosensitive resin composition and forming a black matrix having a high light-shielding property. It aims at providing a conductive resin composition.

  The inventors include (A) a photopolymerizable compound, (B) a photopolymerization initiator, (C) a black pigment, and (S) a solvent, and (C) the black pigment is 40% by mass per solid content. When more colored photosensitive resin composition contains at least one (R) hardly volatile solvent whose solubility parameter and boiling point satisfy the predetermined conditions as the (S) solvent, an aggregate after drying under reduced pressure As a result, the present invention has been completed.

  Specifically, the present invention provides the following.

The first aspect of the present invention contains (A) a photopolymerizable compound, (B) a photopolymerization initiator, (C) a black pigment, and (S) a solvent, and the (C) black pigment contains a solid content. More than 40% by mass of the colored photosensitive resin composition, the (S) solvent has a solubility parameter of 8.7 (cal / cm ³ ) ^1/2 or more and a boiling point of 200 ° C. under atmospheric pressure. It contains at least one (R) hardly volatile solvent that is 250 ° C. or lower, and the content of the (R) hardly volatile solvent is 3% by mass or more and 10% by mass with respect to the total amount of the (S) solvent. % Of the colored photosensitive resin composition.

  The second aspect of the present invention is a black matrix having a pattern formed using the colored photosensitive resin composition of the present invention.

  The third aspect of the present invention is a color filter having the black matrix of the present invention and a liquid crystal display having the color filter.

  According to the present invention, since the (S) solvent contains the (R) hardly volatile solvent, it is possible to prevent agglomerates from being generated in the coating film formed from the colored photosensitive resin composition even during drying under reduced pressure. be able to.

  Hereinafter, embodiments of the present invention will be described in detail. In addition, this invention is not limited to the following embodiment at all.

<Colored photosensitive resin composition>
The colored photosensitive resin composition of the present invention contains (A) a photopolymerizable compound, (B) a photopolymerization initiator, (C) a black pigment, and (S) a solvent.

[(A) Photopolymerizable compound]
The photopolymerizable compound contains a resin or monomer having an ethylenically unsaturated group. Moreover, as a photopolymerizable compound, it is more preferable to combine the resin and monomer which have an ethylenically unsaturated group. By combining a resin having an ethylenically unsaturated group and a monomer having an ethylenically unsaturated group, the curability can be improved and the pattern shape can be facilitated. In the present specification, among compounds having an ethylenically unsaturated group, those having a mass average molecular weight of 1000 or more are referred to as “resin having an ethylenically unsaturated group”, and those having a mass average molecular weight of less than 1000 are referred to as “ It will be referred to as a “monomer having an ethylenically unsaturated group”.

(Resin having an ethylenically unsaturated group)
As the resin having an ethylenically unsaturated group, (meth) acrylic acid, fumaric acid, maleic acid, monomethyl fumarate, monoethyl fumarate, 2-hydroxyethyl (meth) acrylate, ethylene glycol monomethyl ether (meth) acrylate, ethylene Glycol monoethyl ether (meth) acrylate, glycerol (meth) acrylate, (meth) acrylamide, acrylonitrile, methacrylonitrile, methyl (meth) acrylate, ethyl (meth) acrylate, isobutyl (meth) acrylate, 2-ethylhexyl (meth) Acrylate, benzyl (meth) acrylate, ethylene glycol di (meth) acrylate, diethylene glycol diacrylate, triethylene glycol di (meth) acrylate, tetrae Lenglycol di (meth) acrylate, butylene glycol dimethacrylate, propylene glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, tetramethylolpropane tetra (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra Oligomers in which (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, 1,6-hexanediol di (meth) acrylate, cardoepoxy diacrylate, etc. are polymerized; polyhydric alcohol Polyester (meth) acrylate obtained by reacting (meth) acrylic acid with a polyester prepolymer obtained by condensation of a monobasic acid with a polybasic acid. Polyurethane (meth) acrylate obtained by reacting a rate, a polyol and a compound having two isocyanate groups and then reacting with (meth) acrylic acid; and bisphenol A type epoxy resin and bisphenol F type epoxy resin Bisphenol S type epoxy resin, phenol or cresol novolak type epoxy resin, resol type epoxy resin, triphenolmethane type epoxy resin, polycarboxylic acid polyglycidyl ester, polyol polyglycidyl ester, aliphatic or cycloaliphatic epoxy resin, amine epoxy Examples thereof include an epoxy (meth) acrylate resin obtained by reacting a resin and an epoxy resin such as a dihydroxybenzene type epoxy resin with (meth) acrylic acid. Further, a resin obtained by reacting an epoxy (meth) acrylate resin with a polybasic acid anhydride can be used.

  Moreover, as resin which has an ethylenically unsaturated group, the reaction material of an epoxy compound (a1) and an ethylenically unsaturated group containing carboxylic acid compound (a2) is made to react with a polybasic acid anhydride (a3) further. The resin obtained by this can be used preferably.

(Epoxy compound (a1))
As the epoxy compound (a1), glycidyl ether type, glycidyl ester type, glycidyl amine type, alicyclic type, bisphenol A type, bisphenol F type, bisphenol S type, biphenyl type, naphthalene type, fluorene type, phenol novolak type, and An ortho-cresol type epoxy resin etc. are mentioned.

(Ethylenically unsaturated group-containing carboxylic acid compound (a2))
The ethylenically unsaturated group-containing carboxylic acid compound (a2) is preferably a monocarboxylic acid compound containing a reactive ethylenic double bond such as an acryl group or a methacryl group in the molecule. Examples of such ethylenically unsaturated group-containing carboxylic acid compounds include acrylic acid, methacrylic acid, β-styrylacrylic acid, β-furfurylacrylic acid, α-cyanocinnamic acid, and cinnamic acid. This ethylenically unsaturated group-containing carboxylic acid compound (a2) may be used alone or in combination of two or more.

  As a method of reacting the epoxy compound (a1) with the ethylenically unsaturated group-containing carboxylic acid compound (a2), a known method can be used. For example, an epoxy compound (a1) and an ethylenically unsaturated group-containing carboxylic acid compound (a2) are converted into a tertiary amine such as triethylamine and benzylethylamine, dodecyltrimethylammonium chloride, tetramethylammonium chloride, tetraethylammonium chloride, and benzyl. Examples thereof include a method of reacting in an organic solvent at a reaction temperature of 50 ° C. or more and 150 ° C. or less for several hours to several tens of hours using a quaternary ammonium salt such as triethylammonium chloride, pyridine, triphenylphosphine, or the like as a catalyst.

  The use amount ratio in the reaction between the epoxy compound (a1) and the ethylenically unsaturated group-containing carboxylic acid compound (a2) is the same as the epoxy equivalent of the epoxy compound (a1) and the carboxyl of the ethylenically unsaturated group-containing carboxylic acid compound (a2). The ratio to the acid equivalent is usually 1: 0.5 to 1: 2, preferably 1: 0.8 to 1: 1.25, more preferably 1: 1. By setting it as the above range, the crosslinking efficiency tends to be improved.

(Polybasic acid anhydride (a3))
Examples of the polybasic acid anhydride (a3) include maleic anhydride, succinic anhydride, itaconic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, methylhexahydrophthalic anhydride, methyltetrahydrophthalic anhydride. Acid, trimellitic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic dianhydride, 3-methylhexahydrophthalic anhydride, 4-methylhexahydrophthalic anhydride, 3-ethylhexahydrophthalic anhydride, 4- Examples include ethylhexahydrophthalic anhydride, tetrahydrophthalic anhydride, 3-methyltetrahydrophthalic anhydride, 4-methyltetrahydrophthalic anhydride, 3-ethyltetrahydrophthalic anhydride, and 4-ethyltetrahydrophthalic anhydride. These polybasic acid anhydrides may be used alone or in combination of two or more.

  As a method of reacting the epoxy compound (a1) with the ethylenically unsaturated group-containing carboxylic acid compound (a2) and further reacting the polybasic acid anhydride (a3), a known method can be used. The ratio of the amounts used is the number of moles of OH groups in the reaction product of the epoxy compound (a1) and the ethylenically unsaturated group-containing carboxylic acid compound (a2) and the acid anhydride of the polybasic acid anhydride (a3). The equivalent ratio of groups is usually 1: 1 to 1: 0.1, preferably 1: 0.8 to 1: 0.2. By making it into said range, there exists a tendency for the solubility to a developing solution to become moderate.

  The acid value of the resin obtained by further reacting the reaction product of the epoxy compound (a1) with the ethylenically unsaturated group-containing carboxylic acid compound (a2) with the polybasic acid anhydride (a3) is the resin solid content. It is preferably 10 mgKOH / g or more and 150 mgKOH / g or less, and more preferably 70 mgKOH / g or more and 110 mgKOH / g or less. By setting the acid value of the resin to 10 mgKOH / g or more, sufficient solubility in the developer can be obtained, and by setting it to 150 mgKOH / g or less, sufficient curability can be obtained and the surface property should be improved. Can do.

  Further, the mass average molecular weight (Mw) of the resin is preferably 1000 or more and 40000 or less, and more preferably 2000 or more and 30000 or less. By making the mass average molecular weight 1000 or more, heat resistance and film strength can be improved, and by making it 40000 or less, sufficient solubility in a developer can be obtained.

  Moreover, as resin which has an ethylenically unsaturated group, resin which has a cardo structure in a molecule | numerator can be used preferably. Since the resin having a cardo structure has high heat resistance and chemical resistance, the heat resistance and chemical resistance of the colored photosensitive resin composition can be improved by using it as a photopolymerizable compound. For example, a resin represented by the following formula (1) can be preferably used.

In formula (1), n is an integer of 1 to 20, and X is a group represented by the following formula (2).

  In the formula (1), Y is maleic anhydride, succinic anhydride, itaconic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, methylendomethylenetetrahydrophthalic anhydride, chlorendic anhydride, methyl It is a residue obtained by removing a carboxylic anhydride group (—CO—O—CO—) from a dicarboxylic anhydride such as tetrahydrophthalic anhydride and glutaric anhydride.

  In the formula (1), Z is 2 from tetracarboxylic dianhydrides such as pyromellitic anhydride, benzophenone tetracarboxylic dianhydride, biphenyl tetracarboxylic dianhydride, and biphenyl ether tetracarboxylic dianhydride. This residue is obtained by removing one carboxylic anhydride group.

(Monomer having an ethylenically unsaturated group)
Monomers having an ethylenically unsaturated group include monofunctional monomers and polyfunctional monomers.

  Monofunctional monomers include (meth) acrylamide, methylol (meth) acrylamide, methoxymethyl (meth) acrylamide, ethoxymethyl (meth) acrylamide, propoxymethyl (meth) acrylamide, butoxymethoxymethyl (meth) acrylamide, N-methylol ( (Meth) acrylamide, N-hydroxymethyl (meth) acrylamide, (meth) acrylic acid, fumaric acid, maleic acid, maleic anhydride, itaconic acid, itaconic anhydride, citraconic acid, citraconic anhydride, crotonic acid, 2-acrylamide- 2-methylpropane sulfonic acid, tert-butylacrylamide sulfonic acid, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate Cyclohexyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, 2-phenoxy-2-hydroxypropyl (meth) acrylate, 2- (Meth) acryloyloxy-2-hydroxypropyl phthalate, glycerin mono (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, dimethylamino (meth) acrylate, glycidyl (meth) acrylate, 2,2,2-trifluoroethyl ( And (meth) acrylate, 2,2,3,3-tetrafluoropropyl (meth) acrylate, and phthalic acid derivative half (meth) acrylate. These monofunctional monomers may be used alone or in combination of two or more.

  On the other hand, as the polyfunctional monomer, ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate, butylene glycol Di (meth) acrylate, neopentyl glycol di (meth) acrylate, 1,6-hexane glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, glycerin di (meth) acrylate, pentaerythritol triacrylate, pentaerythritol Tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, pentaerythritol di (meta Acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, 2,2-bis (4- (meth) acryloxydi Ethoxyphenyl) propane, 2,2-bis (4- (meth) acryloxypolyethoxyphenyl) propane, 2-hydroxy-3- (meth) acryloyloxypropyl (meth) acrylate, ethylene glycol diglycidyl ether di (meth) Acrylate, diethylene glycol diglycidyl ether di (meth) acrylate, diglycidyl phthalate ester di (meth) acrylate, glycerin triacrylate, glycerin polyglycidyl ether poly (Meth) acrylate, urethane (meth) acrylate (that is, tolylene diisocyanate), reaction product of trimethylhexamethylene diisocyanate and hexamethylene diisocyanate and 2-bidoxyethyl (meth) acrylate, methylenebis (meth) acrylamide, (meth) acrylamide methylene Examples include ethers, condensates of polyhydric alcohols and N-methylol (meth) acrylamide, and triacryl formal. These polyfunctional monomers may be used alone or in combination of two or more.

  The content of the monomer having an ethylenically unsaturated group is preferably 5% by mass or more and 50% by mass or less, more preferably 10% by mass or more and 40% by mass with respect to the solid content of the colored photosensitive resin composition. The range is as follows. By setting it as the above range, it tends to be easy to balance sensitivity, developability, and resolution. In addition, solid content means the sum total of components other than a solvent.

  The content of the photopolymerizable compound is preferably 5% by mass or more and 50% by mass or less, and more preferably 10% by mass or more and 40% by mass or less with respect to the solid content of the colored photosensitive resin composition. By setting it as the above range, it tends to be easy to balance sensitivity, developability, and resolution.

[(B) Photopolymerization initiator]
As photopolymerization initiators, 1-hydroxycyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenylpropan-1-one, 1- [4- (2-hydroxyethoxy) phenyl] -2-hydroxy-2 -Methyl-1-propan-1-one, 1- (4-isopropylphenyl) -2-hydroxy-2-methylpropan-1-one, 1- (4-dodecylphenyl) -2-hydroxy-2-methylpropane -1-one, 2,2-dimethoxy-1,2-diphenylethane-1-one, bis (4-dimethylaminophenyl) ketone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpho Linopropan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, ethanone-1- [ -Ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] -1- (O-acetyloxime), 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 4-benzoyl-4'-methyl Dimethyl sulfide, 4-dimethylaminobenzoic acid, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, butyl 4-dimethylaminobenzoate, 4-dimethylamino-2-ethylhexylbenzoic acid, 4-dimethylamino- 2-isoamylbenzoic acid, benzyl-β-methoxyethyl acetal, benzyldimethyl ketal, 1-phenyl-1,2-propanedione-2- (O-ethoxycarbonyl) oxime, methyl O-benzoylbenzoate, 2,4- Diethylthioxanthone, 2-chlorothioxanthone, 2 4-dimethylthioxanthone, 1-chloro-4-propoxythioxanthone, thioxanthene, 2-chlorothioxanthene, 2,4-diethylthioxanthene, 2-methylthioxanthene, 2-isopropylthioxanthene, 2-ethylanthraquinone, octamethylanthraquinone 1,2-benzanthraquinone, 2,3-diphenylanthraquinone, azobisisobutyronitrile, benzoyl peroxide, cumene peroxide, 2-mercaptobenzoimidazole, 2-mercaptobenzoxazole, 2-mercaptobenzothiazole, 2, -(O-chlorophenyl) -4,5-di (m-methoxyphenyl) -imidazolyl dimer, benzophenone, 2-chlorobenzophenone, p, p'-bisdimethylaminobenzophenone, 4,4 ' Bisdiethylaminobenzophenone, 4,4'-dichlorobenzophenone, 3,3-dimethyl-4-methoxybenzophenone, benzyl, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin-n-butyl ether, benzoin isobutyl ether, benzoin Butyl ether, acetophenone, 2,2-diethoxyacetophenone, p-dimethylacetophenone, p-dimethylaminopropiophenone, dichloroacetophenone, trichloroacetophenone, p-tert-butylacetophenone, p-dimethylaminoacetophenone, p-tert-butyltrichloro Acetophenone, p-tert-butyldichloroacetophenone, α, α-dichloro-4-phenoxyace Tophenone, thioxanthone, 2-methylthioxanthone, 2-isopropylthioxanthone, dibenzosuberone, pentyl-4-dimethylaminobenzoate, 9-phenylacridine, 1,7-bis- (9-acridinyl) heptane, 1,5-bis- (9-acridinyl) pentane, 1,3-bis- (9-acridinyl) propane, p-methoxytriazine, 2,4,6-tris (trichloromethyl) -s-triazine, 2-methyl-4,6-bis (Trichloromethyl) -s-triazine, 2- [2- (5-methylfuran-2-yl) ethenyl] -4,6-bis (trichloromethyl) -s-triazine, 2- [2- (furan-2) -Yl) ethenyl] -4,6-bis (trichloromethyl) -s-triazine, 2- [2- (4-diethylamino) -2-methylphenyl) ethenyl] -4,6-bis (trichloromethyl) -s-triazine, 2- [2- (3,4-dimethoxyphenyl) ethenyl] -4,6-bis (trichloromethyl) -s -Triazine, 2- (4-methoxyphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4-ethoxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2 -(4-n-butoxyphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2,4-bis-trichloromethyl-6- (3-bromo-4-methoxy) phenyl-s-triazine, 2,4-bis-trichloromethyl-6- (2-bromo-4-methoxy) phenyl-s-triazine, 2,4-bis-trichloromethyl-6- (3-bromo-4- Butoxy) styryl phenyl -s- triazine, and 2,4-bis - trichloromethyl-6- (2-bromo-4-methoxy) styrylphenyl -s- triazine. Among these, it is particularly preferable in terms of sensitivity to use an oxime-based photopolymerization initiator. These photopolymerization initiators may be used alone or in combination of two or more.

  The content of the photopolymerization initiator is preferably 0.5% by mass or more and 30% by mass or less, and more preferably 1% by mass or more and 20% by mass or less with respect to the solid content of the colored photosensitive resin composition. preferable. By setting it as said range, sufficient heat resistance and chemical-resistance can be acquired, a coating-film formation ability can be improved, and photocuring failure can be suppressed.

[(C) Black pigment]
Although it does not specifically limit as a black pigment, The conventionally well-known pigment used for a black resist can be used. Specifically, carbon black (CB), titanium black, chromium oxide, iron oxide, aniline black, perylene pigment, and C.I. I. Solvent black 123 or the like can be used. Carbon black coated with an epoxy resin or the like; inorganic black pigments such as composite oxides such as titanium, manganese, iron, copper, and cobalt can also be appropriately employed.

  In the colored photosensitive resin composition, the black pigment can also be dispersed using a black pigment dispersion, and “carbon dispersion CF black (carbon concentration 20% content) ”,“ Carbon dispersion CF black (containing high resistance carbon 24%) ”manufactured by Mikuni Dye Co., Ltd., and the like can be used.

  The content of the black pigment is more than 40% by mass with respect to the solid content of the colored photosensitive resin composition, but is preferably 45% by mass or more, and more preferably 50% by mass or more. . By making it more than 40 mass%, the colored photosensitive resin composition excellent in light-shielding property can be obtained. On the other hand, it is preferable that content of the said black pigment is 70 mass% or less with respect to solid content of a coloring photosensitive resin composition. Thereby, a sensitivity, the heat resistance of the coating film after hardening, and chemical resistance are kept favorable.

  In the colored photosensitive resin composition, when the black pigment is contained within the above content range, a colored photosensitive resin composition having high light shielding properties (optical density, OD value) can be obtained. Specifically, the optical density when the black matrix having a thickness of 1 μm is formed using the colored photosensitive resin composition of the present invention by increasing the black pigment content to more than 40% by mass is 4.0 or more. Value. The optical density is more preferably 4.3 or more, and even more preferably 4.5 or more.

  In addition, for the purpose of increasing the resistance value and adjusting the color tone, other colorants such as organic pigments and dyes listed below can be added to the black pigment as long as the light shielding performance is not lowered.

As an organic pigment, specifically, a color index number (CI No.),
Yellow pigment: C.I. I. 20, 24, 83, 86, 93, 109, 110, 117, 125, 129, 137, 138, 139, 147, 148, 150, 153, 154, 166, 168, 180, 185, 195
Orange pigment: C.I. I. 36, 43, 51, 55, 59, 61
Red pigment: C.I. I. 9, 97, 122, 123, 149, 168, 177, 180, 192, 215, 216, 217, 220, 223, 224, 226, 227, 228, 240, 254
Purple pigment: C.I. I. 19, 23, 29, 30, 37, 40, 50
Blue pigment: C.I. I. 15, 15: 3, 15: 6, 22, 60, 64
Green pigment: C.I. I. 7, 36
Brown pigment: C.I. I. 23, 25, 26
Can be suitably used because of its high transparency and excellent heat resistance, weather resistance, and chemical resistance.

  In addition, in order to suppress the reddish color tone of carbon black and make the overall black more preferable, “Violet Dispersion (containing 10% violet pigment)” manufactured by Mikuni Dye and “Blue Pigment Dispersion CF” manufactured by Mikuni Dye Blue (containing 20% of blue pigment) "and the like can also be mixed.

Specific examples of the dye include C.I. I. No. so,
Yellow dye: C.I. I. Direct Yellow 1, C.I. I. Direct Yellow 11, C.I. I. Direct Yellow 12, C.I. I. Direct Yellow 28, C.I. I. Acid Yellow 1, C.I. I. Acid Yellow 3, C.I. I. Acid Yellow 11, C.I. I. Acid Yellow 17, C.I. I. Acid Yellow 23, C.I. I. Acid Yellow 38, C.I. I. Acid Yellow 40, C.I. I. Acid Yellow 42, C.I. I. Acid Yellow 76, C.I. I. Acid Yellow 98, C.I. I. Basic Yellow 1, C.I. I. Disperse Yellow 3, C.I. I. Disperse Yellow 4, C.I. I. Disperse Yellow 7, C.I. I. Disperse Yellow 31, C.I. I. Disperse Yellow 61, C.I. I. Solvent Yellow 2, C.I. I. Solvent Yellow 14, C.I. I. Solvent Yellow 15, C.I. I. Solvent Yellow 16, C.I. I. Solvent Yellow 21, C.I. I. Solvent Yellow 33, C.I. I. Solvent Yellow 56
Orange dye: C.I. I. Acid Orange 1, C.I. I. Acid Orange 7, C.I. I. Acid Orange 8, C.I. I. Acid Orange 10, C.I. I. Acid Orange 20, C.I. I. Acid Orange 24, C.I. I. Acid Orange 28, C.I. I. Acid Orange 33, C.I. I. Acid Orange 56, C.I. I. Acid Orange 74, C.I. I. Direct Orange 1, C.I. I. Disperse Orange 5, C.I. I. Solvent Orange 1, C.I. I. Solvent Orange 2, C.I. I. Solvent Orange 5, C.I. I. Solvent Orange 6, C.I. I. Solvent Orange 45
Red dye: C.I. I. Direct Red 20, C.I. I. Direct Red 37, C.I. I. Direct Red 39, C.I. I. Direct Red 44, C.I. I. Acid Red 6, C.I. I. Acid Red 8, C.I. I. Acid Red 9, C.I. I. Acid Red 13, C.I. I. Acid Red 14, C.I. I. Acid Red 18, C.I. I. Acid Red 26, C.I. I. Acid Red 27, C.I. I. Acid Red 51, C.I. I. Acid Red 52, C.I. I. Acid Red 87, C.I. I. Acid Red 88, C.I. I. Acid Red 89, C.I. I. Acid Red 92, C.I. I. Acid Red 94, C.I. I. Acid Red 97, C.I. I. Acid Red 111, C.I. I. Acid Red 114, C.I. I. Acid Red 115, C.I. I. Acid Red 134, C.I. I. Acid Red 145, C.I. I. Acid Red 154, C.I. I. Acid Red 180, C.I. I. Acid Red 183, C.I. I. Acid Red 184, C.I. I. Acid Red 186, C.I. I. Acid Red 198, C.I. I. Basic Red 12, C.I. I. Basic Red 13, C.I. I. Disper thread 5, C.I. I. Disper thread 7, C.I. I. Disperse thread 13, C.I. I. Disperse thread 17, C.I. I. Disperse thread 58, C.I. I. Solvent Red 1, C.I. I. Solvent Red 3, C.I. I. Solvent Red 8, C.I. I. Solvent Red 23, C.I. I. Solvent Red 24, C.I. I. Solvent Red 25, C.I. I. Solvent Red 27, C.I. I. Solvent Red 30, C.I. I. Solvent Red 49, C.I. I. Solvent Red 100
Purple dye: C.I. I. Direct violet 22, C.I. I. Acid Violet 49, C.I. I. Basic Violet 2, C.I. I. Basic Violet 7, C.I. I. Basic Violet 10, C.I. I. Disper Violet 24
Blue dye: C.I. I. Direct Blue 25, C.I. I. Direct Blue 86, C.I. I. Direct Blue 90, C.I. I. Direct Blue 108, C.I. I. Acid Blue 1, C.I. I. Acid Blue 7, C.I. I. Acid Blue 9, C.I. I. Acid Blue 15, C.I. I. Acid Blue 103, C.I. I. Acid Blue 104, C.I. I. Acid Blue 158, C.I. I. Acid Blue 161, C.I. I. Basic Blue 1, C.I. I. Basic Blue 3, C.I. I. Basic Blue 9, C.I. I. Basic Blue 25
Green dye: C.I. I. Acid Green 3, C.I. I. Acid Green 9, C.I. I. Acid Green 16, C.I. I. Basic Green 1, C.I. I. Basic green 4
Brown dye: C.I. I. Direct Brown 6, C.I. I. Direct Brown 58, C.I. I. Direct Brown 95, C.I. I. Direct Brown 101, C.I. I. Direct Brown 173, C.I. I. Acid Brown 14
Etc. are preferably used.

  In the case of chromatic colors such as red, green, blue, cyan, magenta, and yellow, mention may be made of, for example, the pigments or dyes described in JP-A-60-237403 and JP-A-4-310901. Can do.

[(S) solvent]
The (S) solvent in the present invention contains at least one (R) hardly volatile solvent.

((R) hardly volatile solvent)
(R) The hardly volatile solvent has a solubility parameter of 8.7 (cal / cm ³ ) ^1/2 or more, preferably 9 (cal / cm ³ ) ^1/2 or more, and has a boiling point of 200 ° C. under atmospheric pressure. The temperature is 250 ° C. or higher. When the solubility parameter of the hardly volatile solvent having a boiling point of 200 ° C. or more and 250 ° C. or less is 8.7 (cal / cm ³ ) ^1/2 or more, the hardly volatile solvent and the black pigment in the colored photosensitive resin composition Compatibility with solid components other than the above can be improved, and after drying under reduced pressure, generation of aggregates in the coating film formed from the colored photosensitive resin composition can be prevented. This is because in the coating film formed from the colored photosensitive resin composition, the non-volatile solvent remains until the end of the vacuum drying, and the dispersibility of the black pigment is maintained, so the black pigment in the coating film This is thought to be due to the suppression of aggregation. Further, the hardly volatile solvent preferably has a solubility parameter of 11 (cal / cm ³ ) ^1/2 or less. When the solubility parameter is 11 (cal / cm ³ ) ^1/2 or less, it is possible to prevent a decrease in compatibility between the hardly volatile solvent and the solid component other than the black pigment in the colored photosensitive resin composition, The generation of aggregates can be further suppressed.

  Furthermore, when the boiling point is 200 ° C. or higher, it is possible to prevent surface roughness and uneven drying of the coating film after drying under reduced pressure. Moreover, when a boiling point is 250 degrees C or less, a hardly volatile solvent is easily removed in the post-baking after the pattern formation of a coloring photosensitive resin composition. That is, it is possible to prevent the solvent from remaining in the black matrix formed from the colored photosensitive resin composition of the present invention. Further, even when a substrate having a large area is used, drying unevenness of the coating film can be prevented.

  Moreover, it is preferable that the saturation vapor pressure in 20 degreeC of a hardly volatile solvent is 2 mmHg or less.

  In addition, the hardly volatile solvent preferably has a weight change rate at 100 ° C. of 10 TG% or less. By setting the weight change rate of the hardly volatile solvent to 10 TG% or less, it is possible to further prevent the occurrence of aggregates after drying under reduced pressure in the coating film formed from the colored photosensitive resin composition of the present invention. In addition, surface roughness and drying unevenness in the dried coating film can be prevented. The weight change rate is more preferably 1 TG% or more and 9 TG% or less, and further preferably 4 TG% or more and 8 TG% or less in that the effect is further improved.

  Here, “weight change rate at 100 ° C.” refers to a change in the weight of the solvent per unit time. In the present specification, the measurement is performed by adding a solvent to a thermobalance kept at 100 ° C. and determining the amount of change in the weight of the solvent in the atmosphere.

  The content of the hardly volatile solvent is preferably 0.1% by mass or more based on the total amount of the solvent. When the content of the hardly volatile solvent is 0.1% by mass or more, generation of aggregates in the coating film formed from the colored photosensitive resin composition can be further suppressed, and surface roughness and drying unevenness can be suppressed. Can also be prevented. Moreover, it is preferable that content of a hardly volatile solvent is 10 mass% or less with respect to the whole quantity of a solvent. When the content of the hardly volatile solvent is 10% by mass or less, the coating property and the film forming ability of the colored photosensitive resin composition can be kept good, and the removal of the hardly volatile solvent at the time of post-baking can be performed. It is easy to prevent the solvent from remaining in the black matrix to be formed. In order to further enhance the above effects, the content is more preferably 1% by mass or more and 8% by mass or less, and further preferably 3% by mass or more and 7% by mass or less.

  Specific examples of the hardly volatile solvent include 1,3-butylene glycol diacetate (1,3-BGA), dipropylene glycol methyl ether acetate (DPMA), diethylene glycol monoethyl ether acetate (EDGAC), or diethylene glycol mono Mention may be made of butyl ether acetate (BDGAC). Among these, 1,3-butylene glycol diacetate and diethylene glycol monobutyl ether acetate are preferable.

  The solvent may contain a solvent other than the hardly volatile solvent (other solvents). The other solvent is not particularly limited, and a solvent usually used for the colored photosensitive resin composition can be used. Specific examples of other solvents include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-propyl ether, ethylene glycol mono-n-butyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol mono- n-propyl ether, diethylene glycol mono-n-butyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol mono-n-propyl ether, propylene glycol mono-n -Butyl ether, dipropylene glycol monomethyl ether (Poly) alkylene glycol monoalkyl such as dipropylene glycol monoethyl ether, dipropylene glycol mono-n-propyl ether, dipropylene glycol mono-n-butyl ether, tripropylene glycol monomethyl ether, and tripropylene glycol monoethyl ether Ethers; (poly) alkylene glycol monoalkyl ether acetates such as ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monomethyl ether acetate, propylene glycol monomethyl ether acetate, and propylene glycol monoethyl ether acetate; diethylene glycol dimethyl ether; Diethylene glycol Other ethers such as ruethyl ether, diethylene glycol diethyl ether, and tetrahydrofuran; ketones such as methyl ethyl ketone, cyclohexanone, 2-heptanone, and 3-heptanone; methyl 2-hydroxypropionate and ethyl 2-hydroxypropionate Lactic acid alkyl esters; ethyl 2-hydroxy-2-methylpropionate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, ethyl 3-ethoxypropionate, ethyl ethoxyacetate, hydroxyacetic acid Ethyl, 2-hydroxy-3-methylbutanoic acid methyl, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, 3-methyl-3-methoxybutylpropionate, ethyl acetate N-propyl acetate, i-propyl acetate, n-butyl acetate, i-butyl acetate, n-pentyl formate, i-pentyl acetate, n-butyl propionate, ethyl butyrate, n-propyl butyrate, i-propyl butyrate , Other esters such as n-butyl butyrate, methyl pyruvate, ethyl pyruvate, n-propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, and ethyl 2-oxobutanoate; aromatic carbonization such as toluene and xylene Hydrogen; and amides such as N-methylpyrrolidone, N, N-dimethylformamide, and N, N-dimethylacetamide. Among these, 3-methoxybutyl acetate is preferable because it exhibits excellent solubility in a photopolymerizable compound and a photopolymerization initiator and improves dispersibility of an insoluble component such as a black pigment. Also preferred are propylene glycol monomethyl ether acetate and cyclohexanone. Other solvents may be used alone or in combination of two or more. It is particularly preferable to use a combination of 3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, and cyclohexanone.

  The solvent in the colored photosensitive resin composition of the present invention is preferably in an amount such that the solid content concentration is 1% by mass or more and 50% by mass or less, and is an amount that provides 5% by mass or more and 30% by mass or less. It is more preferable. When the amount of the solvent is within the above range, the film forming ability and the coating property in the colored photosensitive resin composition can be kept good.

[Other ingredients]
The colored photosensitive resin composition of the present invention may contain an additive as necessary. Additives include thermal polymerization inhibitors, antifoaming agents, surfactants, sensitizers, curing accelerators, photocrosslinking agents, photosensitizers, dispersants, dispersion aids, fillers, adhesion promoters, oxidation Examples thereof include an inhibitor, an ultraviolet absorber, and an aggregation inhibitor. As the dispersant, a polymer dispersant such as a urethane resin dispersant is preferably used.

[Method for preparing colored photosensitive resin composition]
The colored photosensitive resin composition of the present invention can be obtained by mixing all the above components with a stirrer. In addition, you may filter using a filter so that the obtained mixture may become uniform.

<Black matrix and color filter>
The black matrix in the color filter is formed using the colored photosensitive resin composition of the present invention. That is, the colored photosensitive resin composition of the present invention is applied to a substrate made of glass, polyethylene terephthalate, acrylic resin, polycarbonate, and the like. Apparatus), a slit coater, and a curtain flow coater.

  Next, the applied colored photosensitive resin composition is dried to form a coating film. The drying method is not particularly limited, and for example, vacuum drying is performed at room temperature using a vacuum drying apparatus, and then, at a temperature of 80 ° C. to 120 ° C., preferably 90 ° C. to 100 ° C. for 60 seconds on a hot plate. The method of drying for 120 seconds or less can be mentioned.

Next, this coating film is partially exposed by irradiating active energy rays such as ultraviolet rays and excimer laser light through a negative mask. Energy dose to be irradiated also differ depending on the composition of the colored photosensitive resin composition is preferably, for example, 30 mJ / cm ² or more 2000 mJ / cm ² or less.

  Next, the exposed coating film is developed into a desired shape by developing with a developer. The development method is not particularly limited, and for example, an immersion method, a spray method, or the like can be used. Examples of the developer include organic ones such as monoethanolamine, diethanolamine, and triethanolamine, and aqueous solutions such as sodium hydroxide, potassium hydroxide, sodium carbonate, ammonia, and quaternary ammonium salts.

  Next, the pattern after development is post-baked at about 220 ° C. to 250 ° C., preferably about 230 ° C. to 240 ° C. At this time, it is preferable to expose the entire surface of the formed pattern. As described above, a black matrix having a predetermined pattern shape can be formed.

  The above operation is performed on the colored photosensitive resin composition in which red, green, and blue pigments are dispersed to form pixel patterns of each color. Thereby, a color filter is formed.

  Conventionally known colored photosensitive resin compositions in which red, green, and blue pigments are dispersed can be used.

  In the production of the color filter of the present invention, the ink of each color of red, green, and blue is ejected from the inkjet nozzles in each region partitioned by the black matrix, and the stored ink is cured by heat or light, Color filters can also be manufactured.

  The colored photosensitive resin composition of the present invention can prevent the formation of aggregates and form a black matrix with high light-shielding properties even when drying under reduced pressure using a vacuum drying apparatus after coating on a substrate. can do.

<Liquid crystal display>
The liquid crystal display of the present invention includes the color filter having the black matrix of the present invention. In manufacturing the liquid crystal display of the present invention, the color filter is formed on a substrate, and then electrodes, spacers, and the like are sequentially formed. Then, an electrode or the like is formed on another substrate, the two are bonded together, and a predetermined amount of liquid crystal is injected and sealed.

<Example 1>
[Synthesis of photopolymerizable compound]
First, in a 500 ml four-necked flask, 235 g of bisphenolfluorene type epoxy resin (epoxy equivalent 235), 110 mg of tetramethylammonium chloride, 100 mg of 2,6-di-tert-butyl-4-methylphenol, and 72. 0 g was charged and dissolved by heating at 90 ° C. to 100 ° C. while blowing air at a rate of 25 ml / min. Next, the temperature was gradually raised while the solution was clouded, and the solution was heated to 120 ° C. to be completely dissolved. Here, the solution gradually became transparent and viscous, but stirring was continued as it was. During this time, the acid value was measured, and heating and stirring were continued until the acid value was less than 1.0 mgKOH / g. It took 12 hours for the acid value to reach the target. And it cooled to room temperature and obtained the bisphenol fluorene type epoxy acrylate.

  Next, after adding 600 g of 3-methoxybutyl acetate to 307.0 g of the bisphenolfluorene type epoxy acrylate thus obtained and dissolving, 80.5 g of benzophenone tetracarboxylic dianhydride and 1 g of tetraethylammonium bromide Were mixed, gradually heated, and reacted at 110 ° C. to 115 ° C. for 4 hours. After confirming the disappearance of the acid anhydride, 38.0 g of 1,2,3,6-tetrahydrophthalic anhydride was mixed and reacted at 90 ° C. for 6 hours to obtain a photopolymerizable compound 1. The disappearance of the acid anhydride was confirmed by IR spectrum.

  Photopolymerizable compound 1 (Mw: 3400, solid content: 55%, solvent: 3-methoxybutyl acetate); 23.6 parts by mass, dipentaerythritol hexaacrylate; 4.8 parts by mass, photopolymerization initiator (“IRGACURE” OXE 02 ", manufactured by Ciba Specialty Chemicals Co., Ltd .; 1.4 parts by mass, and a carbon dispersion (" CF Black EX-1455 "manufactured by Mikuni Dye Co., Ltd., high resistance carbon: 24%, dispersant: 5%, solvent: 3-methoxybutyl acetate); 100 parts by mass was adjusted with a solvent so that the solid content concentration was 18% by mass. The solvent was 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate: 1,3-butylene glycol diacetate = 55: 30: 12: 3 (mass ratio). These mixtures were mixed for 2 hours with a stirrer and then filtered with a 5 μm membrane filter to obtain a colored photosensitive resin composition.

  In addition, Table 1 shows the boiling point under atmospheric pressure, the weight change rate at 100 ° C., and the value of the solubility parameter of each solvent used for the preparation of the colored photosensitive resin composition. Table 2 shows the carbon black (CB) content in the solid content.

[Formation of coating film]
After coating the colored photosensitive resin composition on a glass substrate of 680 mm × 880 mm, it is dried under reduced pressure at 66 Pa for 30 seconds, and then pre-baked at 110 ° C. for 120 seconds to obtain a coating film having a film thickness of about 1.0 μm. It was.

<Example 2>
A colored photosensitive resin composition was prepared in the same manner as in Example 1 except that diethylene glycol monoethyl ether acetate was used in place of 1,3-butylene glycol diacetate as the hardly volatile solvent. The functional resin composition was applied on a glass substrate in the same manner as in Example 1.

<Example 3>
1,3-butylene glycol diacetate was used as the hardly volatile solvent, and the solvent was 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate: 1,3-butylene glycol diacetate = 55: 26: 12: 7 ( A colored photosensitive resin composition was prepared by the same method as in Example 1 except that the weight ratio was set, and the colored photosensitive resin composition was applied on a glass substrate by the same method as in Example 1.

<Example 4>
Photopolymerizable compound 1 (Mw: 3400, solid content: 55%, solvent: 3-methoxybutyl acetate); 24.5 parts by mass, dipentaerythritol hexaacrylate; 4.5 parts by mass, photopolymerization initiator (“IRGACURE” OXE 02 ", manufactured by Ciba Specialty Chemicals Co., Ltd .; 1.4 parts by mass and, as a carbon dispersion," carbon dispersion CF black "(carbon concentration: 20%, dispersant: 5%, solvent: 3-methoxybutyl acetate A colored photosensitive resin composition was prepared by the same method as in Example 1 except that 100 parts by mass was used, and the colored photosensitive resin composition was prepared in the same manner as in Example 1. Was applied onto a glass substrate.

<Example 5>
As the hardly volatile solvent, dipropylene glycol methyl ether acetate is used instead of 1,3-butylene glycol diacetate, and the solvent is 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate: dipropylene glycol methyl ether acetate = 65 : A colored photosensitive resin composition was prepared by the same method as in Example 1 except that the ratio was 15: 15: 5 (mass ratio), and the colored photosensitive resin composition was prepared by the same method as in Example 1. It apply | coated on the glass substrate.

<Example 6>
As the hardly volatile solvent, diethylene glycol monobutyl ether acetate is used instead of 1,3-butylene glycol diacetate, and the solvent is 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate: diethylene glycol monobutyl ether acetate = 65: 15: 15 : A colored photosensitive resin composition was prepared by the same method as in Example 1 except that it was 5 (mass ratio), and the colored photosensitive resin composition was prepared on the glass substrate by the same method as in Example 1. Applied.

<Comparative Example 1>
Photopolymerizable compound 1 (Mw: 3400, solid content: 55%, solvent: 3-methoxybutyl acetate); 30 parts by mass, dipentaerythritol hexaacrylate; 6.5 parts by mass, photopolymerization initiator (“IRGACURE OXE 02 "Ciba Specialty Chemicals Co., Ltd."; 2 parts by mass, and as a carbon dispersion, "carbon dispersion CF black" (carbon concentration: 20%, dispersant: 5%, solvent: 3-methoxybutyl acetate, Mikuni Dye Co., Ltd.) 100 parts by mass, 1-butylene glycol diacetate was not added, and the mixing ratio was 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate = 60: 20: 20. A colored photosensitive resin composition was prepared in the same manner as in Example 1, It was coated on a glass substrate in the same manner as in Example 1 the color photosensitive resin composition.

<Comparative Example 2>
Photopolymerizable compound 1 (Mw: 3400, solid content: 55%, solvent: 3-methoxybutyl acetate); 24.5 parts by mass, dipentaerythritol hexaacrylate; 4.5 parts by mass, photopolymerization initiator (“IRGACURE” OXE 02 ", manufactured by Ciba Specialty Chemicals); a colored photosensitive resin composition was prepared in the same manner as in Comparative Example 1 except that the amount was 1.4 parts by mass, and the colored photosensitive resin composition was used as a comparative example. 1 was applied on a glass substrate by the same method.

<Comparative Example 3>
As the solvent, 1,3-butylene glycol diacetate was not added, and the mixing ratio was the same as in Example 1 except that 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate = 55: 30: 15 A colored photosensitive resin composition was prepared by the method, and the colored photosensitive resin composition was applied on a glass substrate by the same method as in Example 1.

<Comparative Example 4>
A colored photosensitive resin composition was prepared by the same method as in Comparative Example 3 except that the mixing ratio of the solvent was 3-methoxybutyl acetate: cyclohexanone: propylene glycol monomethyl ether acetate = 50: 30: 20, and the coloring was performed. The photosensitive resin composition was apply | coated on the glass substrate by the method similar to the comparative example 3.

<Comparative Example 5>
A colored photosensitive resin composition was prepared in the same manner as in Example 1 except that dipropylene glycol dimethyl ether was used instead of 1,3-butylene glycol diacetate, and the colored photosensitive resin composition was carried out. It coated on the glass substrate by the method similar to Example 1.

  Here, the weight change rate is obtained by adding a solvent to a thermobalance (“TG / DTA6200 (trade name)”, manufactured by SII Nanotechnology Co., Ltd.) kept at 100 ° C. and determining the amount of change in the weight of the solvent in the atmosphere. Was measured.

[Evaluation of aggregates]
The colored photosensitive resin compositions prepared in Examples 1-6 and Comparative Examples 1-5 were applied to an 8-inch wafer, and the coating was formed under the same conditions as in Examples 1-6 and Comparative Examples 1-5. About a film | membrane (film thickness; about 1 micrometer), using "KLA-213X" (made by KLA-Tencor Co., Ltd.), the surface defect is inspected and the generation of aggregates is measured Was evaluated. The results are shown in Table 2. The number of defects is preferably less than 20 in terms of product quality.

[Evaluation of uneven drying]
Regarding the surfaces of the coating films formed in Examples 1 to 6 and Comparative Examples 1 to 5, when observing by irradiating with sodium lamp light, x is a problem in appearance, and ○ is not a problem in appearance. As a result, drying unevenness was evaluated. The results are shown in Table 2.

[Evaluation of surface roughness]
About the coating film formed in the said Examples 1-6 and Comparative Examples 1-5, surface roughness (Ra) was evaluated using atomic force microscope ("AFM (device name)", SII nanotechnology company make). The results are shown in Table 2. In the evaluation, Ra is less than 60 cm, Å is 60 cm or more and less than 100 cm, and x is 100 cm or more, and the value is described in parentheses.

[Evaluation of optical density (OD value)]
When forming the coating film in Examples 1 to 6 and Comparative Examples 1 to 5, the film thickness of the black matrix was set to 1 μm, and the OD value was measured with an OD measuring device “D-200II” (manufactured by Gretag Macbeth). .

As can be seen from Table 2, the solvent was added with a hardly volatile solvent having a solubility parameter of 8.7 (cal / cm ³ ) ^1/2 or more and a boiling point of 200 ° C. or more and 250 ° C. or less under atmospheric pressure. In Examples 1 to 6, although the carbon black content in the total solid content is more than 40% by mass (OD value is 4.0 or more), the occurrence of agglomerates is small with less occurrence of defects in the coating film. It is understood that is suppressed. On the other hand, in Comparative Example 1, although the number of defects is small, an OD value of 4.0 or higher cannot be achieved, and it can be seen that sufficient light shielding properties are not obtained. Moreover, in Comparative Examples 2-5, it turned out that many defects have generate | occur | produced. In addition, in Examples 1-6, it turned out that surface roughness and drying nonuniformity are not seen compared with Comparative Examples 1-5.

Claims (7)

(A) A photopolymerizable compound, (B) a photopolymerization initiator, (C) a black pigment, and (S) a solvent, wherein the (C) black pigment is more than 40% by mass per solid content. A resin composition comprising:
The (S) solvent has a solubility parameter of 8.7 (cal / cm ³ ) ^½ or more and at least one kind of (R) hardly volatile having a boiling point of 200 ° C. or more and 250 ° C. or less under atmospheric pressure. It contains a solvent (excluding dipropylene glycol methyl ether acetate (DPMA)), and the content of the (R) hardly volatile solvent is 3% by mass or more and 10% by mass with respect to the total amount of the (S) solvent. The colored photosensitive resin composition which is the following. (A) A photopolymerizable compound, (B) a photopolymerization initiator, (C) a black pigment, and (S) a solvent, wherein the (C) black pigment is more than 40% by mass per solid content. A resin composition comprising:
The (S) solvent has a solubility parameter of 8.7 (cal / cm ³ ) ^½ or more and at least one kind of (R) hardly volatile having a boiling point of 200 ° C. or more and 250 ° C. or less under atmospheric pressure. The solvent contains a solvent, and the (R) hardly volatile solvent is diethylene glycol monoethyl ether acetate (EDGAC), and the content of the (R) hardly volatile solvent is 3 mass with respect to the total amount of the (S) solvent. % To 10% by mass or less of a colored photosensitive resin composition.   The colored photosensitive resin composition according to claim 2, wherein the (B) photopolymerization initiator is an oxime-based photopolymerization initiator. The colored photosensitive resin composition of Claim 2 except the thing containing the compound represented by following General formula (1).

(In the formula, R ¹ represents a linear or branched alkylene group having ² to 6 carbon atoms, R ² represents a linear or branched alkylene group having 1 to 6 carbon atoms, and n represents an integer of 1 to 4). ) The manufacturing method of a black matrix which has the process of forming a pattern using the colored photosensitive resin composition in any one of Claim 1 to 4. The manufacturing method of the color filter which has the process of forming a pattern using the colored photosensitive resin composition in any one of Claim 1 to 4. The manufacturing method of the liquid crystal display which has the process of forming a pattern using the colored photosensitive resin composition in any one of Claim 1 to 4.