JP5707610B2 - Decorative flooring and floor structure - Google Patents
Decorative flooring and floor structure Download PDFInfo
- Publication number
- JP5707610B2 JP5707610B2 JP2010119323A JP2010119323A JP5707610B2 JP 5707610 B2 JP5707610 B2 JP 5707610B2 JP 2010119323 A JP2010119323 A JP 2010119323A JP 2010119323 A JP2010119323 A JP 2010119323A JP 5707610 B2 JP5707610 B2 JP 5707610B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- decorative flooring
- decorative
- flooring
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、適度なクッション性と強度を有する化粧床材等に関する。 The present invention relates to a decorative flooring material having appropriate cushioning properties and strength.
従来、住宅などのフローリングの上に、クッション性に優れたフロアマットが敷き詰められる場合がある。
このような用途に使用されるフロアマットとして、表皮材と、所定密度のウレタンフォーム層と、所定密度のチップウレタンフォーム層と、所定密度の圧縮ウレタンフォーム層が順次積層され、ＪＩＳ Ｋ ６４００：２００４に基づく反発弾性率が３０〜４５であるフロアマットが知られている（特許文献１）。
Conventionally, floor mats excellent in cushioning properties may be spread on flooring of a house or the like.
As a floor mat used for such an application, a skin material, a urethane foam layer having a predetermined density, a chip urethane foam layer having a predetermined density, and a compressed urethane foam layer having a predetermined density are sequentially laminated. JIS K 6400: 2004 A floor mat having a rebound resilience of 30 to 45 is known (Patent Document 1).
ところで、近年、住宅などにおいて、二重床構造が採用されつつある。
二重床の構造は、基礎下地（モルタル面など）の上に所定間隔を開けて立設された複数の支柱と、各支柱の上に取り付けられた構造下地材（パーティクルボードなど）と、その構造下地材の上に接着剤などを介して接着された捨て貼り材（合板など）と、その捨て貼り材の上に敷設された化粧床材と、からなる。二重床は、基礎下地と捨て貼り材の間に床下空間を有する。そのため、二重床は、遮音性に優れ、さらに、その床下空間に電気通信用配線や給排水用管などの設備を設けることが可能である。
By the way, in recent years, a double floor structure is being adopted in houses and the like.
The double-floor structure consists of a plurality of pillars erected on a foundation foundation (such as a mortar surface) at predetermined intervals, a structural foundation material (such as a particle board) attached on each pillar, and It consists of a discarded paste (such as plywood) bonded on a structural base material via an adhesive or the like, and a decorative floor material laid on the discarded paste. The double floor has an underfloor space between the foundation substrate and the discarded paste material. Therefore, the double floor is excellent in sound insulation, and further, facilities such as telecommunications wiring and water supply / drainage pipes can be provided in the space under the floor.
しかしながら、上記二重床においては、構造下地材に捨て貼り材を接着しているので、メンテナンス（例えば、床下空間内の設備の点検、補修及び変更など）を容易に行えない。
この点、捨て貼り材を使用せず、構造下地材の上に化粧床材を直接敷設すれば、メンテナンスなどを容易に行い得る。
However, in the above-described double floor, since the pasting material is adhered to the structural base material, maintenance (for example, inspection, repair and change of equipment in the space under the floor) cannot be easily performed.
In this regard, maintenance and the like can be easily performed by directly laying the decorative floor material on the structural base material without using the discarded paste material.
しかしながら、捨て貼り材を設けずにクッション性に優れた化粧床材を敷設すると、構造下地材の不陸が化粧床材の表面に現れやすい。従って、このような構造下地材の上に敷設した場合でも、その不陸の影響を受け難い化粧床材が求められる。 However, if a decorative floor material having excellent cushioning properties is laid without disposing a paste material, unevenness of the structural base material tends to appear on the surface of the decorative floor material. Therefore, even when laid on such a structural base material, a decorative floor material that is not easily affected by unevenness is required.
本発明の目的は、適度なクッション性を有し、さらに、施工面の不陸の影響を受け難い剛直性を有する化粧床材及び床構造を提供することである。 An object of the present invention is to provide a decorative flooring material and a floor structure that have moderate cushioning properties and that have rigidity that is not easily affected by unevenness of the construction surface.
本発明の化粧床材は、芯材と、前記芯材の表面側に設けられたクッション材と、前記クッション材の表面側に設けられた表装材と、前記芯材の裏面側に設けられた下地層と、を有し、前記芯材が、曲げ破断強度１Ｎ／ｍｍ２以上であり、前記クッション材が、反発弾性率１０％〜５０％であり、前記下地層が、第１層と前記第１層の裏面に貼り合わされた第２層とを有する。 The decorative flooring of the present invention is provided with a core material, a cushion material provided on the surface side of the core material, a cover material provided on the surface side of the cushion material, and a back surface side of the core material. includes a base layer, wherein the core material is a flexural breaking strength 1N / mm 2 or more, the cushion material, Ri repulsion elasticity of 10% to 50% der, the underlying layer is a first layer And a second layer bonded to the back surface of the first layer .
本発明の好ましい化粧床材は、前記芯材の曲げ破断強度が２０Ｎ／ｍｍ２以上である。
本発明の好ましい化粧床材は、前記第１層が、合成樹脂製発泡体及び不織布の何れか一方から形成され、前記第２層が、合成樹脂製発泡体及び不織布の何れか一方から形成されている。
本発明の好ましい化粧床材は、前記下地層の第２層が、防滑性又は吸着性を有する。
In a preferred decorative flooring of the present invention, the core material has a bending breaking strength of 20 N / mm 2 or more.
In a preferred decorative flooring material of the present invention, the first layer is formed from one of a synthetic resin foam and a nonwoven fabric, and the second layer is formed from either a synthetic resin foam or a nonwoven fabric. It is .
In a preferred decorative flooring material of the present invention, the second layer of the foundation layer has anti-slip property or adsorptivity.
本発明の別の局面によれば、床構造を提供する。
この床構造は、同じ厚みの上記化粧床材の複数が、施工面に並んで敷設されている。好ましくは、前記施工面は二重床構造である。
According to another aspect of the present invention, a floor structure is provided.
In this floor structure, a plurality of the above-mentioned decorative flooring materials having the same thickness are laid side by side on the construction surface. Preferably, the construction surface has a double floor structure.
本発明の化粧床材は、適度なクッション性を有するので、使用時に適度に変形する。従って、本発明の化粧床材を用いれば、その上に座る又は歩行する使用者に対して、良好な使用感を与えることができる。
さらに、本発明の化粧床材は、施工面の不陸の影響を受け難いので、前記不陸に起因する凹凸が表面に現れにくい。従って、本発明の化粧床材を用いれば、敷設後も表面平滑性に優れ、綺麗な床を構成できる。
Since the decorative flooring of the present invention has an appropriate cushioning property, it is appropriately deformed during use. Therefore, if the decorative flooring of the present invention is used, a good feeling of use can be given to a user who sits on or walks on the floor.
Furthermore, since the decorative flooring of the present invention is not easily affected by unevenness of the construction surface, the unevenness due to the unevenness is unlikely to appear on the surface. Therefore, if the decorative flooring of the present invention is used, a beautiful floor having excellent surface smoothness even after laying can be constructed.
［本発明の化粧床材の層構成］
図１において、本発明の化粧床材１は、芯材２と、芯材２の表面側に設けられたクッション材３と、クッション材３の表面側に設けられた表装材４と、を有する。さらに、芯材２の裏面側には、必要に応じて、下地層５が設けられている。
化粧床材１は、通常、平面視四角形状に形成される。もっとも、化粧床材１の平面視形状は、四角形状に限定されるわけではない。
[Layer structure of the decorative flooring of the present invention]
In FIG. 1, a
The
クッション材３は、芯材２の表面に載置されている。必要に応じて、クッション材３の裏面の全体又は一部分が、芯材２の表面に接着剤を用いて接着されていてもよい。
表装材４は、クッション材３の表面に載置されている。必要に応じて、表装材４の裏面の全体又は一部分が、クッション材３の表面に接着剤を用いて接着されていてもよい。
表装材４の周囲は、クッション材３及び芯材２に巻き込まれ、表装材４の四方の下端部４ａが、芯材２の裏面の四方辺部２ａに取り付けられている。従って、表装材４は、クッション材３の表面だけでなく、クッション材３の周側面及び芯材２の周側面までも被覆している。表装材４の各下端部４ａを芯材２の裏面の四方辺部２ａに取り付ける方法としては、接着剤を用いた接着、又は、鋲などの固定具を用いた止着などが挙げられる。
The
The surface covering material 4 is placed on the surface of the
The outer periphery of the cover material 4 is wound around the
下地層５は、例えば、芯材２の裏面に貼り付けられた第１層５１と、前記第１層５１の下面に貼り合わされた第２層５２と、を有する。第２層５２の裏面は、施工面（床面）に接地する面であるので、第２層５２は、防滑性又は吸着性を有することが好ましい。
The
［芯材］
上記芯材は、主として化粧床材に剛直性を付与し、化粧床材の形状を維持するための層である。
本発明の化粧床材の芯材は、その曲げ破断強度が１Ｎ／ｍｍ２以上とされており、好ましくは２０Ｎ／ｍｍ２以上であり、より好ましくは１００Ｎ／ｍｍ２以上である。このような曲げ破断強度を有する芯材を用いれば、施工面に存する不陸の影響を受け難い、剛直性を有する化粧床材を構成できる。
芯材の曲げ破断強度の上限は特に限定されない。その曲げ破断強度の一般的な上限は、２００Ｎ／ｍｍ２程度である。
ここで、上記曲げ破断強度は、ＪＩＳ Ｋ ７２２１−２：２００６に準拠して測定された値をいう。
[Core]
The core material is a layer for mainly imparting rigidity to the decorative floor material and maintaining the shape of the decorative floor material.
The core material of the decorative flooring of the present invention has a bending breaking strength of 1 N / mm 2 or more, preferably 20 N / mm 2 or more, more preferably 100 N / mm 2 or more. By using a core material having such a bending rupture strength, it is possible to constitute a decorative floor material that is hard to be affected by unevenness existing on the construction surface and has rigidity.
The upper limit of the bending rupture strength of the core material is not particularly limited. The general upper limit of the bending rupture strength is about 200 N / mm 2 .
Here, the said bending fracture strength says the value measured based on JISK7221-2: 2006.
芯材の形成材料は、芯材の曲げ破断強度が上記の値を有するものを形成できることを条件として特に限定されない。芯材の形成材料としては、例えば、ＭＤＦ、インシュレーションボード、合板、合成樹脂製硬質発泡体、セラミックボードなどが挙げられる。
比較的軽量で、破断強度が高く、更に柔軟性を有することから、芯材としてＭＤＦを用いることが好ましい。
前記合成樹脂製硬質発泡体の主成分としては、特に限定されず、ポリプロピレン、ポリスチレン、ポリウレタン、ポリ塩化ビニルなどが挙げられる。発泡体の発泡倍率は、５〜３０倍が好ましく、８〜１５倍がより好ましい。発泡倍率が大きすぎると剛直性が低下してしまう。一方、発泡倍率が小さすぎると、軽量性及び切断容易性などの発泡体としての特性を殆ど有さなくなる。
The material for forming the core material is not particularly limited as long as the core material can be formed with the bending fracture strength of the core material described above. Examples of the material for forming the core material include MDF, insulation board, plywood, synthetic resin hard foam, and ceramic board.
It is preferable to use MDF as a core material because it is relatively lightweight, has high breaking strength, and has flexibility.
The main component of the synthetic resin hard foam is not particularly limited, and examples thereof include polypropylene, polystyrene, polyurethane, and polyvinyl chloride. The expansion ratio of the foam is preferably 5 to 30 times, and more preferably 8 to 15 times. If the expansion ratio is too large, the rigidity is lowered. On the other hand, if the foaming ratio is too small, the foamed material such as lightness and ease of cutting has little characteristics.
芯材は、２種以上の複合構造でもよい。例えば、芯材は、上記ＭＤＦと合成樹脂製硬質発泡体が貼り合わされた複合体、上記ＭＤＦなどに合成樹脂製フィルムや織布などが貼り合わされた複合体などでもよい。 The core material may have a composite structure of two or more. For example, the core material may be a composite in which the MDF and a synthetic resin hard foam are bonded together, a composite in which a synthetic resin film or a woven fabric is bonded to the MDF, or the like.
なお、芯材の厚みは、芯材の曲げ破断強度が上記の値を有することを条件として特に限定されないが、例えば、１〜２０ｍｍであり、好ましくは２〜１０ｍｍである。 In addition, although the thickness of a core material is not specifically limited on condition that the bending fracture strength of a core material has said value, For example, it is 1-20 mm, Preferably it is 2-10 mm.
［クッション材］
クッション材は、主として化粧床材に適度なクッション性を付与し、化粧床材に対する使用感を向上させる層である。つまり、表装材上に載った使用者の荷重によってクッション材が少し凹むので、化粧床材に対する使用感（化粧床材に対する座り心地や歩行感など）が向上する。
本発明のクッション材は、その反発弾性率が１０％〜５０％とされており、好ましくは２０〜５０％である。このような反発弾性率を有するクッション材は、適度なクッション性を有し、化粧床材の使用感を向上させ得る。ただし、前記反発弾性率は、ＪＩＳ Ｋ ６４００−３に準拠して測定された値をいう。
[Cushion material]
The cushion material is a layer that mainly imparts an appropriate cushioning property to the decorative floor material and improves the feeling of use with respect to the decorative floor material. That is, since the cushion material is slightly recessed due to the load of the user who is placed on the cover material, the feeling of use for the decorative flooring (sitting comfort or walking feeling for the decorative flooring) is improved.
The cushioning material of the present invention has a rebound resilience of 10% to 50%, preferably 20 to 50%. The cushion material having such a rebound resilience has an appropriate cushioning property and can improve the feeling of use of the decorative floor material. However, the said impact resilience rate says the value measured based on JISK6400-3.
クッション材の形成材料は、適度な弾性を有していれば特に限定されず、例えば、合成樹脂製発泡体、各種の不織布などが挙げられる。クッション材を形成する発泡体の主成分としては、ポリウレタン、ポリ塩化ビニル、酢酸ビニル、ポリエチレン、アクリル系樹脂などが挙げられ、その発泡倍率としては、２〜５０倍が好ましい。適度なクッション性を有し、凹み回復性も良好であることから、クッション材としてポリウレタン製の発泡体を用いることが好ましい。クッション材を形成する不織布としては、各種の合成樹脂繊維、ガラス繊維、天然繊維などが挙げられる。 The material for forming the cushion material is not particularly limited as long as it has an appropriate elasticity, and examples thereof include synthetic resin foams and various nonwoven fabrics. Examples of the main component of the foam forming the cushion material include polyurethane, polyvinyl chloride, vinyl acetate, polyethylene, acrylic resin, and the like, and the expansion ratio is preferably 2 to 50 times. It is preferable to use a polyurethane foam as the cushioning material because it has an appropriate cushioning property and good dent recovery. Examples of the nonwoven fabric forming the cushion material include various synthetic resin fibers, glass fibers, and natural fibers.
クッション材の厚みは、特に限定されないが、好ましくは２ｍｍ〜１５ｍｍであり、より好ましくは４ｍｍ〜１０ｍｍである。クッション材の厚みが余りに厚いと、化粧床材に荷重が加わったときに沈み込みが大きくなり過ぎて使用感が悪くなり、一方、余りに薄いと殆ど沈み込まず使用感の向上が期待できない。 Although the thickness of a cushion material is not specifically limited, Preferably it is 2 mm-15 mm, More preferably, it is 4 mm-10 mm. If the thickness of the cushion material is too thick, when the load is applied to the decorative flooring material, the sinking becomes too large and the feeling of use becomes worse.
［表装材］
表装材は、主として化粧床材の表面に化粧を付与し、使用者が直に接触する層である。
表装材の形成材料は、特に限定されず、例えば、畳表、織物、編物、不織布、タフト生地、合成樹脂シートから選ばれる少なくとも１種が挙げられる。
畳表としては、例えば、イ草畳表、イ草を模倣した人工イ草畳表（合成樹脂、無機材料などから形成されたイ草似の繊維からなる畳表）などが挙げられる。織物としては、天然繊維又は合成繊維を織り込んだ模様生地又は無模様生地が挙げられ、必要に応じて、薄いシート（薄い紙など）が貼り合わされていてもよい。編物としては、天然繊維又は合成繊維を編み込んだ模様生地又は無模様生地が挙げられ、必要に応じて、薄いシート（薄い紙など）が貼り合わされていてもよい。不織布としては、天然繊維又は合成繊維からなる不織布生地が挙げられ、必要に応じて、不織布に模様を印刷したり、或いは、不織布に薄いシート（薄い紙など）を貼り合わしてもよい。
[Surface material]
The surface covering material is a layer that mainly applies makeup to the surface of the decorative flooring and is directly contacted by the user.
The material for forming the covering material is not particularly limited, and examples thereof include at least one selected from a tatami mat, a woven fabric, a knitted fabric, a nonwoven fabric, a tufted fabric, and a synthetic resin sheet.
Examples of the tatami mat include a moss tatami mat, an artificial moss tatami mat imitating rush (a tatami mat composed of moss-like fibers formed from a synthetic resin, an inorganic material, and the like). Examples of the woven fabric include a patterned fabric or a non-patterned fabric in which natural fibers or synthetic fibers are woven, and a thin sheet (such as thin paper) may be bonded as necessary. Examples of the knitted fabric include a patterned fabric or a non-patterned fabric knitted with natural fibers or synthetic fibers, and a thin sheet (such as a thin paper) may be bonded as necessary. Examples of the non-woven fabric include non-woven fabric made of natural fibers or synthetic fibers. If necessary, a pattern may be printed on the non-woven fabric, or a thin sheet (such as thin paper) may be bonded to the non-woven fabric.
表装材の引裂き強度は、特に限定されないが、５Ｎ／１．５ｃｍ以上が好ましく、１０Ｎ／１．５ｃｍ以上がより好ましい。このような強度の表装材は、良好な耐久性を有する。前記引裂き強度は、ＪＩＳ Ｐ ８１１６に準じて測定された値をいう。
表装材の厚みは、特に限定されないが、０．１〜５ｍｍが好ましく、０．１〜２ｍｍがより好ましい。表装材の厚みが余りに厚いと、表装材をクッション材及び芯材に巻き込み難く、一方、余りに薄いと表装材の耐久性が低くなる。
The tear strength of the cover material is not particularly limited, but is preferably 5 N / 1.5 cm or more, and more preferably 10 N / 1.5 cm or more. A covering material having such strength has good durability. The tear strength refers to a value measured according to JIS P 8116.
Although the thickness of a surface covering material is not specifically limited, 0.1-5 mm is preferable and 0.1-2 mm is more preferable. If the thickness of the surface covering material is too thick, it is difficult to wrap the surface covering material around the cushion material and the core material. On the other hand, if the surface covering material is too thin, the durability of the surface covering material is lowered.
［下地層］
下地層は、主として化粧床材に下地追従性を付与し、さらに、施工後の化粧床材の位置ずれを防止するための層である。
下地層の形成材料は、特に限定されず、例えば、アクリル系樹脂などの合成樹脂製発泡体、不織布などが挙げられる。下地層が上記第１層と第２層を有する場合には、例えば、第１層として合成樹脂製発泡シートを用い、第２層として不織布を用いることができ、或いは、第１層として不織布を用い、第２層として合成樹脂製発泡シートを用いることができる。
[Underlayer]
The foundation layer is a layer mainly for imparting foundation followability to the decorative floor material and further preventing positional displacement of the decorative floor material after construction.
The material for forming the underlayer is not particularly limited, and examples thereof include synthetic resin foams such as acrylic resins, and nonwoven fabrics. When the ground layer has the first layer and the second layer, for example, a synthetic resin foam sheet can be used as the first layer, and a nonwoven fabric can be used as the second layer, or a nonwoven fabric can be used as the first layer. A synthetic resin foam sheet can be used as the second layer.
また、第２層として、防滑性を有する素材（例えば、ポリ塩化ビニルやポリ酢酸ビニルなどの樹脂、又は、発泡樹脂など）を不織布に含浸又は不織布の裏面に付着させたものを用いてもよい。このような防滑性を有する第２層は、施工後の化粧床材の位置ずれを効果的に防止できる。
さらに、第２層として、吸着性を有する層を用いてもよい。吸着性を有する第２層としては、例えば、複数の微細な穴が開口された柔軟な発泡体（合成樹脂製発泡体など）などが挙げられる。このような発泡体は、床材を施工面に施工したときに、微細な穴から空気が逃げる。従って、この発泡体から形成された第２層は、その吸盤機能により施工面に対して吸着力を発揮し、施工後の化粧床材の位置ずれを効果的に防止できる。
下地層の厚みは、特に限定されないが、下地追従性を考慮すると、０．５ｍｍ〜５ｍｍが好ましい。
Further, as the second layer, a non-slip material (for example, a resin such as polyvinyl chloride or polyvinyl acetate, or a foamed resin) impregnated into a nonwoven fabric or adhered to the back surface of the nonwoven fabric may be used. . Such a second layer having anti-slip properties can effectively prevent displacement of the decorative flooring material after construction.
Furthermore, an adsorbing layer may be used as the second layer. Examples of the second layer having adsorptivity include a flexible foam (such as a synthetic resin foam) in which a plurality of fine holes are opened. In such a foam, air escapes from a fine hole when the flooring is applied to the construction surface. Therefore, the 2nd layer formed from this foam exhibits the adsorption power with respect to a construction surface by the suction cup function, and can prevent the position shift of the decorative flooring material after construction.
The thickness of the foundation layer is not particularly limited, but is preferably 0.5 mm to 5 mm in consideration of foundation followability.
上記構成からなる化粧床材の反発弾性率（ＪＩＳ Ｋ ６４００−３に準拠）は、例えば、１０〜５０％であり、好ましくは２０〜４０％であり、より好ましくは２０〜３０％である。かかる化粧床材は、適度なクッション性を有する。
さらに、上記構成からなる化粧床材の曲げ破断強度（ＪＩＳ Ｋ ７２２１−２：２００６に準拠）は、例えば、１Ｎ／ｍｍ２以上であり、好ましくは２０Ｎ／ｍｍ２以上であり、より好ましくは１００Ｎ／ｍｍ２以上である。かかる化粧床材は、施工面に存する不陸の影響を受け難い（剛直性を有する）。
従って、上記化粧床材を施工面上に敷設することによって、使用者に対して良好な使用感を与え、さらに、表面平滑性に優れた綺麗な床を構成できる。
The rebound resilience (based on JIS K 6400-3) of the decorative flooring having the above configuration is, for example, 10 to 50%, preferably 20 to 40%, and more preferably 20 to 30%. Such a decorative flooring has an appropriate cushioning property.
Furthermore, the bending breaking strength (conforming to JIS K 7221-2: 2006) of the decorative flooring material having the above-described configuration is, for example, 1 N / mm 2 or more, preferably 20 N / mm 2 or more, more preferably 100 N. / Mm 2 or more. Such a decorative flooring material is not easily affected by unevenness existing on the construction surface (has rigidity).
Therefore, by laying the decorative floor material on the construction surface, it is possible to give a good feeling to the user and to form a beautiful floor having excellent surface smoothness.
［化粧床材の使用例］
本発明の化粧床材１は、住宅の床面などのような、所望の場所に施工される。
図２及び図３は、乾式二重床上に本発明の化粧床材を施工する一例を示している。
この二重床９は、次のような構造からなる。モルタル面のような基礎下地９１上の束９２の上に支柱９３が立設されている。この支柱９３は、所定間隔を開けて複数配置されている。この支柱９３の上端部には、支柱９３の上端面（支持面）の受け面積を広くするため、固定部材９４が設けられている。各固定部材９４の上には、パーティクルボードのような構造下地材９５が載せられている。構造下地材９５の大きさは特に限定されないが、例えば、５００ｍｍ角、厚み２５ｍｍである。
この構造下地材９５は、固定部材９４に対して着脱可能とするために、ビス止めにて固定部材９４に固定されている。この構造下地材９５と基礎下地９１の間は、床下空間９６を有する。この床下空間９６に、電気通信用配線や給排水用管などの設備（図示せず）を設けることが可能である。
[Usage example of decorative flooring]
The
2 and 3 show an example in which the decorative flooring of the present invention is constructed on a dry double floor.
The
The
この構造下地材９５の上に、本発明の化粧床材１を敷設する。
具体的な施工方法としては、まず最初に化粧床材１を載せる施工面（構造下地材９５）に、墨（位置決め用の目印線）を引き、その墨に沿って化粧床材１を軽く置く。化粧床材１を位置合わせした後、この上から押さえて敷設し、これを順次繰り返していく。図３に示すように、隣接する構造下地材９５の接合部９５ａを覆うように、化粧床材１を位置合わせして敷設することが好ましい。また、化粧床材１の敷設順序は、二重床９の中央部から敷設し、壁面９７の方に順次化粧床材１を敷設することが好ましい。壁面９７に接する化粧床材１については、必要に応じて、壁面９７の形状に合わせて切断した後、敷設される。
化粧床材１は、構造下地材９５上に並べて載せていくだけでよい。もっとも、着脱可能な固定具を用いて構造下地材９５に化粧床材１を固定してもよい。
The
As a specific construction method, first, black (a marking line for positioning) is drawn on the construction surface (structure base material 95) on which the
The
また、化粧床材１の施工に際して、構造下地材９５に下地処理（例えば、構造下地材９５にフィルムを貼付、或いは、構造下地材９５に下地処理剤の塗布など）を行ってもよい。このような下地処理の実施は、化粧床材１の施工後、その表面を特に平滑にできるので好ましい。
In addition, when the
構造下地材９５に着脱可能な化粧床材１は、その上から容易に取り外すことができる。前記構造下地材９５は、ビスを外せば簡単に取り外すことができる。また、従って、床下空間９６にアクセスでき、床下空間９６に設けられた設備のメンテナンスを容易に行うことができる。
また、化粧床材１が下地層５を有する場合、施工後の化粧床材１の位置ズレを防止できる。特に、アクリル系樹脂の発泡樹脂を有する下地層５が設けられた化粧床材１は、位置ズレ防止効果に優れ、且つ、メンテナンスの際に施工面（構造下地材９５上など）から容易に引き剥がすことができる。
本発明の化粧床材１は、施工面の不陸の影響を受け難いので、捨て貼り材が接着されていない構造下地材９５の上にそれを敷設した場合であっても、表面平滑性に優れた綺麗な床を構成できる。
The
Moreover, when the
Since the
以下、本発明の実施例及び比較例を示して本発明を更に詳述する。ただし、本発明は、下記実施例に限定されるものではない。 Hereinafter, the present invention will be described in further detail with reference to Examples and Comparative Examples of the present invention. However, the present invention is not limited to the following examples.
［実施例及び比較例で使用した表装材］
紙布：ムライ（株）製、商品名「ＷＥＮ６４２０」。
織物：小嶋織物（株）製、商品名「ＷＥＮ６０３９」。
[Surface materials used in Examples and Comparative Examples]
Paper cloth: Product name “WEN6420” manufactured by Murai Co., Ltd.
Textile: Kojima Textile Co., Ltd., trade name “WEN6039”.
［実施例及び比較例で使用したクッション材］
ウレタンチップ発泡体（Ａ）：ブリジストン化成品（株）製。厚み５ｍｍ。発泡倍率５倍。比重０．１５。
ウレタンチップ発泡体（Ｂ）：ブリジストン化成品（株）製。厚み５ｍｍ。発泡倍率５倍。比重０．２０。
[Cushion materials used in Examples and Comparative Examples]
Urethane chip foam (A): manufactured by Bridgestone Chemicals. Thickness 5mm.
Urethane chip foam (B): manufactured by Bridgestone Chemicals. Thickness 5mm.
アンダーレイシート：東リ（株）製、商品名「アンダーレイシート」。塩化ビニル製。厚み４．５ｍｍ。
テンダーシート：東リ（株）製、商品名「デンダーシート」。塩化ビニル製。厚み９ｍｍ。
ポリエチレン発泡体：積水化学工業（株）製、商品名「ソフトロン」。厚み５ｍｍ。発泡倍率３０倍。
不織布：サンケミカル（株）製。ニードルパンチによるポリエチレンテレフタレート繊維不織布。目付量９００ｇ／ｍ２。
ポリエチレンエラストマー発泡体：（株）第一化学製、商品名「タフフォーム１５」。厚み５ｍｍ。発泡倍率１５倍。
Underlay sheet: Trade name “Underlay Sheet” manufactured by Toli Corporation. Made of vinyl chloride. Thickness 4.5mm.
Tender sheet: Tori Co., Ltd., trade name “Dender Sheet”. Made of vinyl chloride. Thickness 9mm.
Polyethylene foam: Sekisui Chemical Co., Ltd., trade name "Softlon". Thickness 5mm. The expansion ratio is 30 times.
Non-woven fabric: manufactured by Sun Chemical Co., Ltd. Polyethylene terephthalate fiber nonwoven fabric by needle punch. The basis weight is 900 g / m 2 .
Polyethylene elastomer foam: product name “Tough Form 15” manufactured by Daiichi Chemical Co., Ltd. Thickness 5mm. The expansion ratio is 15 times.
上記各クッション材の反発弾性率を、ＪＩＳ Ｋ ６４００−３に準拠して測定した。その結果を、表１に示す。 The rebound resilience of each of the cushion materials was measured according to JIS K 6400-3. The results are shown in Table 1.
［実施例及び比較例で使用した芯材］
ＭＤＦ：（株）ノダ製。厚み５．５ｍｍ。
オレフィン系硬質発泡体：積水化学工業（株）製、商品名「ゼットロン」。厚み５ｍｍ。発泡倍率３０倍。
ＮＧＰボード：日本グラスファイバー工業（株）製、商品名「ＮＧＰボード」。厚み５ｍｍ。
合板：厚み１２ｍｍの市販品。
セラミックタイル：（株）ＩＮＡＸ製、商品名「ストロータッチ」。厚み７ｍｍ。
ウレタンチップ発泡体（Ａ）：クッション材で使用したウレタンチップ発泡体（Ａ）と同じ製品。
ウレタンチップ発泡体（Ｂ）：クッション材で使用したウレタンチップ発泡体（Ｂ）と同じ製品。
アンダーレイシート：クッション材で使用したアンダーレイシートと同じ製品。
テンダーシート：クッション材で使用したテンダーシートと同じ製品。
[Core materials used in Examples and Comparative Examples]
MDF: manufactured by Noda Co., Ltd. Thickness 5.5mm.
Olefin-based rigid foam: Product name “Zetron” manufactured by Sekisui Chemical Co., Ltd. Thickness 5mm. The expansion ratio is 30 times.
NGP board: Nippon Glass Fiber Industry Co., Ltd., trade name “NGP board”. Thickness 5mm.
Plywood: A commercial product with a thickness of 12 mm.
Ceramic tile: Product name "Straw Touch", manufactured by INAX Corporation. Thickness 7mm.
Urethane chip foam (A): The same product as the urethane chip foam (A) used in the cushioning material.
Urethane chip foam (B): The same product as the urethane chip foam (B) used in the cushioning material.
Underlay sheet: The same product as the underlay sheet used for the cushioning material.
Tender sheet: The same product as the tender sheet used for cushioning.
上記各芯材の曲げ破断強度を、ＪＩＳ Ｋ ７２２１−２：２００６に準拠して測定した。その結果を表２に示す。 The bending fracture strength of each of the core materials was measured in accordance with JIS K 7221-2: 2006. The results are shown in Table 2.
［実施例１〜８及び比較例１〜７］
表３及び表４に示す表装材、クッション材、芯材及び下地層を、上から順に積層接着して化粧床材を作製した。ただし、表３及び表４には、下地層を記載していないが、各実施例及び各比較例の何れも、同一の下地層を使用した。その下地層は、太さ１００デニール、長さ４０〜６０ｍｍのポリエステル繊維からなる不織布（目付量１００ｇ／ｍ２）の裏面に、アクリル系発泡樹脂を付着させたものである。
なお、各材間の接着にあたっては、変性エチレン酢酸ビニル系接着剤を使用した。
[Examples 1-8 and Comparative Examples 1-7]
The facing material shown in Table 3 and Table 4, the cushion material, the core material, and the base layer were laminated and bonded in order from the top to prepare a decorative floor material. However, although Table 3 and Table 4 do not describe the underlayer, the same underlayer was used in each of the examples and the comparative examples. The undercoat layer is obtained by attaching an acrylic foamed resin to the back surface of a nonwoven fabric (weight per unit area: 100 g / m 2 ) made of polyester fibers having a thickness of 100 denier and a length of 40 to 60 mm.
Note that a modified ethylene vinyl acetate adhesive was used for bonding between the materials.
［反発弾性率及び曲げ破断強度の測定］
実施例１〜８及び比較例１〜７の化粧床材について、それぞれ反発弾性率及び破断強度を測定した。その結果を、表３及び表４に示す。
なお、上記各床材の反発弾性率は、ＪＩＳ Ｋ ６４００−３に準拠し、表装材側の反発弾性率を測定した。
各床材の曲げ破断強度は、ＪＩＳ Ｋ ７２２１−２：２００６に準拠して測定した。
[Measurement of impact resilience and bending strength]
For the decorative flooring materials of Examples 1 to 8 and Comparative Examples 1 to 7, the resilience modulus and the breaking strength were measured, respectively. The results are shown in Tables 3 and 4.
In addition, the rebound resilience of each flooring was measured in accordance with JIS K 6400-3.
The bending rupture strength of each flooring was measured according to JIS K 7221-2: 2006.
［歩行試験］
実施例１〜８及び比較例１〜７の化粧床材をそれぞれ４枚準備し、この４枚の床材をコンクリート面上に直列に敷設した。各実施例及び比較例の化粧床材の上を、素足で歩き、そのときの歩行感をそれぞれ評価した。その結果を表３及び表４に示す。
ただし、表中の記号は下記評価を意味する。
◎：適度な沈み込みと適度な反発があり、歩行したときの感触が非常に良かった。
○：適度な沈み込みと適度な反発があり、歩行したときの感触が良かった。
△：反発を感じ、歩き難かった。
×：沈み込み量が大きく、歩き難かった。
[Walking test]
Four decorative flooring materials of Examples 1-8 and Comparative Examples 1-7 were prepared, and the four flooring materials were laid in series on the concrete surface. It walked with the bare feet on the decorative flooring of each Example and the comparative example, and the walk feeling at that time was evaluated, respectively. The results are shown in Tables 3 and 4.
However, the symbols in the table mean the following evaluation.
A: There was moderate sinking and moderate repulsion, and the feeling when walking was very good.
○: There was moderate sinking and moderate repulsion, and the feeling when walking was good.
Δ: Feeling rebound and difficult to walk.
X: The sinking amount was large and it was difficult to walk.
［不陸発現性試験］
実施例１〜８及び比較例１〜７の化粧床材を、図４に示すように、２ｍｍの段差がある施工面の該段差を覆うようにそれぞれ敷き詰めた。各実施例及び比較例の化粧床材の表面を観察し、不陸が現れているかどうかをそれぞれ評価した。その結果を表３及び表４に示す。
ただし、表中の記号は下記評価を意味する。
○：隣接する床材の突き合わせ端部が綺麗に収まっていた。
×：段差に追従し過ぎて、床材の表面に段差が生じていた。
[Roughness development test]
As shown in FIG. 4, each of the decorative flooring materials of Examples 1 to 8 and Comparative Examples 1 to 7 was laid so as to cover the level difference of the construction surface having a level difference of 2 mm. The surface of the decorative flooring material of each Example and Comparative Example was observed to evaluate whether unevenness appeared. The results are shown in Tables 3 and 4.
However, the symbols in the table mean the following evaluation.
○: The butt end portion of the adjacent floor material was neatly accommodated.
X: The level | step difference had arisen on the surface of the flooring material too much following the level | step difference.
特に、実施例１及び２の化粧床材は、適度な沈み込みと適度な反発があり、歩行したときの感触が非常に良く、軽量でありながら床材として十分な剛直性を有していた。 In particular, the decorative flooring materials of Examples 1 and 2 had moderate sinking and moderate repulsion, had a very good feel when walking, and had sufficient rigidity as a flooring material while being lightweight. .
本発明の化粧床材は、一般住宅、マンション、オフィスビルなどの室内の床面に敷いて使用される。 The decorative flooring of the present invention is used by being laid on a floor surface in a room such as a general house, a condominium, and an office building.
１…化粧床材、２…芯材、３…クッション材、４…表装材、５…下地層
DESCRIPTION OF
Claims (6)
前記芯材が、曲げ破断強度１Ｎ／ｍｍ２以上であり、
前記クッション材が、反発弾性率１０〜５０％であり、
前記下地層が、第１層と前記第１層の裏面に貼り合わされた第２層とを有する、化粧床材。 A core material, a cushion material provided on the front surface side of the core material, a surface material provided on the front surface side of the cushion material, and a base layer provided on the back surface side of the core material ,
The core material has a bending breaking strength of 1 N / mm 2 or more,
The cushion material, Ri 10-50% der rebound resilience,
The decorative flooring material, wherein the foundation layer includes a first layer and a second layer bonded to the back surface of the first layer .