JP5617020B2 - 金属材料と硬質材料の接合方法 - Google Patents
金属材料と硬質材料の接合方法 Download PDFInfo
- Publication number
- JP5617020B2 JP5617020B2 JP2013191997A JP2013191997A JP5617020B2 JP 5617020 B2 JP5617020 B2 JP 5617020B2 JP 2013191997 A JP2013191997 A JP 2013191997A JP 2013191997 A JP2013191997 A JP 2013191997A JP 5617020 B2 JP5617020 B2 JP 5617020B2
- Authority
- JP
- Japan
- Prior art keywords
- hard material
- temperature
- metal material
- stress
- transformation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
dεtr=K×(1−ξ)dξ×σ …(3)
但し、dεtr:変態塑性歪増分、K:材料ごとに決まる係数、ξはマルテンサイトの体積分率、dξ:マルテンサイトの体積分率の増分、σ:負荷応力の夫々を示す。
0≦[M10]M−[M50]S …(1)
0≧[M90]M−[M10]S …(2)
Ms=521−353×[C]−22×[Si]−24×[Mn]−8×[Cu]−17×[Ni]−18×[Cr]−26×[Mo] …(3)
但し、[C],[Si],[Mn],[Cu],[Ni],[Cr]および[Mo]は、夫々C,Si,Mn,Cu,Ni,CrおよびMoの含有量(質量%)を示し、その元素を含有しない場合には、その項がないものとして計算する。
σ1=(σx+σy)/2+{[(σx−σy)2+4τxy 2]/2}1/2 …(4)
但し、σx:x方向の残留応力、σy:y方向の残留応力、4τxy:xy面の剪断応力
σ1={(σx+σy)/2}+{|σx−σy|/2} …(5)
Claims (3)
- マルテンサイト変態を生じる特性を有する金属材料と、マルテンサイト変態を生じる硬質材料とを接合するにあたり、
(a)前記金属材料は、該金属材料の相変態温度域を前記硬質材料の相変態温度に応じて設定されるように選ぶか、または(b)前記硬質材料は、該硬質材料の相変態温度域を前記金属材料の相変態温度に応じて設定されるように選ぶ金属材料と硬質材料の接合方法において、
温度−伸び曲線に基づいて求められる相当体積分率を用い、前記金属材料におけるマルテンサイト組織の相当体積分率が10%となる温度[M10] M と、前記硬質材料におけるマルテンサイト組織の相当体積分率が50%となる温度[M50] S が、下記(1)式の関係を満足することを特徴とする金属材料と硬質材料の接合方法。
0≦[M10] M −[M50] S …(1) - 前記金属材料は、マルエージング鋼、析出硬化系ステンレス鋼、またはニッケル鋼のいずれかである請求項1に記載の接合方法。
- 前記硬質材料は、セラミックス、サーメット、または超硬合金のいずれかである請求項1または2に記載の接合方法。