JP5558208B2 - Pneumatic tire - Google Patents
Pneumatic tire Download PDFInfo
- Publication number
- JP5558208B2 JP5558208B2 JP2010125147A JP2010125147A JP5558208B2 JP 5558208 B2 JP5558208 B2 JP 5558208B2 JP 2010125147 A JP2010125147 A JP 2010125147A JP 2010125147 A JP2010125147 A JP 2010125147A JP 5558208 B2 JP5558208 B2 JP 5558208B2
- Authority
- JP
- Japan
- Prior art keywords
- cord
- organic fiber
- layer
- fiber cord
- tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は空気入りタイヤ(以下、単に「タイヤ」とも称する)に関し、詳しくは、タイヤ周方向に対し実質的に平行に配列された有機繊維コードのゴム引き層よりなるベルト補強層の改良に係る乗用車用空気入りタイヤに関する。 The present invention relates to a pneumatic tire (hereinafter, also simply referred to as “tire”), and more particularly, to an improvement in a belt reinforcing layer including a rubberized layer of organic fiber cords arranged substantially parallel to the tire circumferential direction. The present invention relates to a pneumatic tire for passenger cars.
一般に、空気入りタイヤは、左右一対のビードコア間にまたがってトロイド状に延在するカーカスプライと、そのクラウン部のタイヤ径方向外側に、タイヤ周方向に対し傾斜して配置されたベルト層と、そのタイヤ径方向外側に、実質的にタイヤ周方向に配設された有機繊維コードからなるベルト補強層と、を備えた構成を有する。このうちベルト補強層は、従来、タイヤに周方向剛性を付与して、タガ効果をもたらすことを目的として、タイヤ最外層に配置されている。 In general, a pneumatic tire is a carcass ply extending in a toroid shape across a pair of left and right bead cores, a belt layer disposed on the outer side in the tire radial direction of the crown portion and inclined with respect to the tire circumferential direction A belt reinforcement layer made of an organic fiber cord disposed substantially in the tire circumferential direction is provided on the outer side in the tire radial direction. Of these, the belt reinforcing layer is conventionally disposed in the outermost layer of the tire for the purpose of imparting a circumferential rigidity to the tire and providing a tag effect.
一方で、近年、タイヤの転がり抵抗の低減に関する要請は、ますます厳しくなってきている。このような転がり抵抗低減のニーズの高まりに対して、従来は、転がり抵抗の主要因となるゴムのヒステリシスロスを下げることで対応が図られていた(例えば、特許文献1等)。また、タイヤの骨格部材である有機繊維コードの改良により転がり抵抗を低減する手法として、有機繊維コード自体のヒステリシスロスを低減することが効果的であることも知られている。 On the other hand, in recent years, demands for reducing the rolling resistance of tires have become increasingly severe. In response to such an increasing need for reducing rolling resistance, conventionally, countermeasures have been taken by lowering the hysteresis loss of rubber, which is the main cause of rolling resistance (for example, Patent Document 1). It is also known that reducing the hysteresis loss of the organic fiber cord itself is effective as a technique for reducing rolling resistance by improving the organic fiber cord, which is a skeleton member of the tire.
しかしながら、従来のゴム配合や有機繊維コード自体の改良による低ヒステリシスロス化の手法では、近年の転がり抵抗の低減の要請を十分満足できるものではなく、さらなる低転がり抵抗化を達成するための新たな技術の確立が求められていた。 However, the conventional methods of reducing the hysteresis loss by improving the rubber composition and the organic fiber cord itself do not sufficiently satisfy the recent demand for reduction of rolling resistance, and a new technique for achieving further reduction in rolling resistance. The establishment of technology was required.
そこで本発明の目的は、上記問題を解消して、他のタイヤ性能を損なうことなく、さらなる低転がり抵抗化を図った空気入りタイヤを提供することにある。 SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a pneumatic tire that solves the above-described problems and further reduces rolling resistance without impairing other tire performance.
本発明者は、かかる周方向に配設されたベルト補強層に着目して鋭意検討した結果、ベルト補強層を構成する有機繊維コードと、これを被覆するゴムとの界面でのゴムの繰り返し歪が、走行時に生ずるヒステリシスロスに大きく寄与していることを見出した。本発明者はさらに検討した結果、かかるヒステリシスロスの発生を抑制するためには、有機繊維コードの断面形状を真円に近づけることが効果的であることを見出し、また、ベルト補強層を構成するゴム−コード複合体の表面積ファクターとして下記の式(2)の左辺を定義して、その値を下げることで、タイヤの転がり抵抗がより低減されることを見出して、本発明を完成するに至った。 As a result of diligent study focusing on the belt reinforcing layer disposed in the circumferential direction, the present inventor has found that the repeated strain of rubber at the interface between the organic fiber cord constituting the belt reinforcing layer and the rubber covering the organic fiber cord However, it has been found that this greatly contributes to the hysteresis loss that occurs during running. As a result of further investigation, the present inventor has found that it is effective to make the cross-sectional shape of the organic fiber cord close to a perfect circle in order to suppress the occurrence of such hysteresis loss, and constitutes a belt reinforcing layer. By defining the left side of the following formula (2) as the surface area factor of the rubber-cord composite and lowering the value, it was found that the rolling resistance of the tire was further reduced, and the present invention was completed. It was.
すなわち、本発明の空気入りタイヤは、左右一対のビードコア間にまたがってトロイド状に延在する少なくとも1枚のカーカスプライと、該カーカスプライのクラウン部のタイヤ径方向外側に配置され、タイヤ周方向に対し傾斜して配列された補強コードのゴム引き層よりなる少なくとも1層のベルト層と、該ベルト層のタイヤ径方向外側に配置され、タイヤ周方向に対し実質的に平行に配列された有機繊維コードのゴム引き層よりなるベルト補強層とを備える空気入りタイヤにおいて、
前記ベルト補強層を構成する有機繊維コードのコード長手方向に直交する断面における、ディップコードとしての最小径をR1(mm)、最大径をR2(mm)としたとき、R2/R1で定義される該有機繊維コードの真円度が、下記式(1)、
1.0<R2/R1≦1.3 (1)
を満足し、かつ、該有機繊維コードの、JIS規格に準拠して測定されるディップコードとしてのコード径をD(mm)、前記ベルト補強層の、トリートとしての該有機繊維コードの打込み数をE(本/50mm)と定義したとき、下記式(2)、
35.8≦π×D×(R2/R1)×E≦43.6 (2)
で示される関係を満足することを特徴とするものである。
That is, the pneumatic tire according to the present invention is disposed on the outer side in the tire radial direction of the crown portion of the carcass ply and at least one carcass ply extending in a toroid shape across the pair of right and left bead cores, and in the tire circumferential direction. At least one belt layer made of a rubberized layer of reinforcing cords arranged at an inclination relative to the tire, and an organic material arranged on the outer side in the tire radial direction of the belt layer and arranged substantially parallel to the tire circumferential direction In a pneumatic tire provided with a belt reinforcing layer made of a rubberized layer of fiber cord,
In the cross section orthogonal to the cord longitudinal direction of the organic fiber cord constituting the belt reinforcing layer, when the minimum diameter as the dip cord is R1 (mm) and the maximum diameter is R2 (mm), it is defined as R2 / R1. The roundness of the organic fiber cord is expressed by the following formula (1),
1.0 <R2 / R1 ≦ 1.3 (1)
And the cord diameter of the organic fiber cord as a dip cord measured in accordance with JIS standard is D (mm), and the number of driving of the organic fiber cord as a treat of the belt reinforcing layer is When defined as E (book / 50 mm), the following formula (2),
35.8 ≦ π × D × (R2 / R1) × E ≦ 43.6 (2)
It is characterized by satisfying the relationship indicated by.
本発明においては、前記有機繊維コードの総繊度が300dtex以上であることが好ましい。また、前記有機繊維コードが片撚りコードであることが好ましい。さらに、前記有機繊維コードが66−ナイロンからなることが好ましい。 In the present invention, it is preferable that the total fineness of the organic fiber cord is 300 dtex or more. Moreover, it is preferable that the said organic fiber cord is a single twisted cord. Furthermore, the organic fiber cord is preferably made of 66-nylon.
本発明によれば、上記構成としたことにより、他のタイヤ性能を損なうことなく、さらなる低転がり抵抗化を図った空気入りタイヤを実現することが可能となった。 According to the present invention, by adopting the above-described configuration, it is possible to realize a pneumatic tire with further reduced rolling resistance without impairing other tire performance.
以下、本発明の実施の形態について、図面を参照しつつ詳細に説明する。
図1に、本発明の空気入りタイヤの一例の幅方向断面図を示す。図示するタイヤは、ビードコア1が埋設された左右一対のビード部11および一対のサイドウォール部12と、両サイドウォール部12に連なるトレッド部13とを有し、左右一対のビードコア1間にまたがってトロイド状に延在して、これら各部を補強する1枚のカーカスプライ2を備えている。また、カーカスプライ2のクラウン部のタイヤ径方向外側には、タイヤ周方向に対し傾斜して配列された補強コードのゴム引き層よりなる2層のベルト層3a,3bと、タイヤ周方向に対し実質的に平行に配列された有機繊維コードのゴム引き層よりなるベルト補強層4,5と、が配置されている。
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
In FIG. 1, the cross-sectional view of the width direction of an example of the pneumatic tire of this invention is shown. The illustrated tire has a pair of left and right bead portions 11 and a pair of sidewall portions 12 in which the bead cores 1 are embedded, and a tread portion 13 connected to both sidewall portions 12, and spans between the pair of left and right bead cores 1. One carcass ply 2 extending in a toroidal shape and reinforcing these parts is provided. Further, on the outer side in the tire radial direction of the crown portion of the carcass ply 2, two belt layers 3a and 3b made of rubberized layers of reinforcing cords arranged to be inclined with respect to the tire circumferential direction, and the tire circumferential direction Belt reinforcing layers 4 and 5 made of rubberized layers of organic fiber cords arranged substantially in parallel are arranged.
本発明においては、かかるベルト補強層を構成する有機繊維コードのコード長手方向に直交する断面における、ディップコードとしての最小径をR1(mm)、最大径をR2(mm)としたとき、R2/R1で定義される有機繊維コードの真円度が、下記式(1)、
1.0<R2/R1≦1.3 (1)
を満足するものとする。前述したように、この有機繊維コードの真円度が1.0に近く、すなわち、有機繊維コードの断面形状が真円に近いほど、有機繊維コードとその周囲に存在するゴムとが接触する界面の表面積が小さくなり、この界面で走行時に発生するヒステリシスロスが低減して、結果として、低転がり抵抗化を図ることが可能となる。
In the present invention, when the minimum diameter as the dip cord is R1 (mm) and the maximum diameter is R2 (mm) in the cross section perpendicular to the cord longitudinal direction of the organic fiber cord constituting the belt reinforcing layer, R2 / The roundness of the organic fiber cord defined by R1 is expressed by the following formula (1),
1.0 <R2 / R1 ≦ 1.3 (1)
Shall be satisfied. As described above, the interface of the organic fiber cord and the rubber existing around the organic fiber cord comes into contact with each other as the roundness of the organic fiber cord is closer to 1.0, that is, the cross-sectional shape of the organic fiber cord is closer to a perfect circle. As a result, the hysteresis loss generated during traveling at this interface is reduced, and as a result, low rolling resistance can be achieved.
ここで、上記有機繊維コードのディップコードとしての最大径および最小径は、有機繊維コードをその長手方向に対して垂直に切断したときのコード断面において、有機繊維コードをコーティングゴムで被覆した際にコードとゴムの界面とが接する円を描いたとき、最大となる円の直径を最大径とし、最小となる円の直径を最小径として定義される。図2(a),(b)に、有機繊維コードのコード断面の一例の写真を示す。図示する写真中の円が、各有機繊維コードの最大径および最小径を、それぞれ示している。なお、かかる最大径および最小径の測定は、例えば、有機繊維コードを無負荷状態で樹脂に埋め込んだ成型体の断面を観察する等により、行うことができる。ここで、ディップコードとは、接着剤(ディップ液)で処理された後のコードを意味する。また、本発明においてディップコードとしてのコード径としているのは、タイヤ内に埋設される前のコード径を問題とするとの意味である。 Here, the maximum diameter and the minimum diameter of the organic fiber cord as a dip cord are determined when the organic fiber cord is covered with a coating rubber in the cross section of the cord when the organic fiber cord is cut perpendicularly to the longitudinal direction. When a circle in which the interface between the cord and the rubber is in contact is drawn, the maximum circle diameter is defined as the maximum diameter, and the minimum circle diameter is defined as the minimum diameter. 2A and 2B show photographs of examples of the cord cross section of the organic fiber cord. Circles in the photograph shown indicate the maximum diameter and the minimum diameter of each organic fiber cord. The maximum diameter and the minimum diameter can be measured by, for example, observing a cross section of a molded body in which an organic fiber cord is embedded in a resin in an unloaded state. Here, the dip code means a code after being treated with an adhesive (dip solution). In addition, the cord diameter as the dip cord in the present invention means that the cord diameter before being embedded in the tire is a problem.
また、本発明においては、上記有機繊維コードの、JIS規格に準拠して測定されるディップコードとしてのコード径をD(mm)、ベルト補強層の、トリートとしての有機繊維コードの打込み数をE(本/50mm)と定義したとき、下記式(2)、
π×D×(R2/R1)×E<70 (2)
で示される関係を満足することが必要である。上記式(2)に示すように、真円度に見かけのコード断面の周長と打込み数とを掛け合わせることで、転がり抵抗と相関する値を得ることができる。上記式(2)の左辺の値が小さければ小さいほど、転がり抵抗のレベルが良化する。この値が70以上であると、現在の市販タイヤレベルの転がり抵抗しか達成し得ないものとなる。ここで、上記式(2)を満足するD,Eの組み合わせは複数生ずることになるが、その場合、打込み数Eを55(本/50mm)未満、例えば、25〜54(本/50mm)とすることが好ましい。打込み数Eを55(本/50mm)未満とすることで、トリートを裁断する作業が容易となるので、生産性を向上することができる。これに対し、打込み数Eが増加すると、ディップ時にディップ液の膜張り性が悪化して、ディップむらが増えてしまうことに加え、スリッティング作業時に糸切れが生じやすくなる。また、打込み数を25(本/50mm)未満まで下げると、トリートの撚り、織り工程からディップ時の間に、反物の性状が悪化して、作業性が低下する。
In the present invention, the diameter of the organic fiber cord as a dip cord measured in accordance with JIS standards is D (mm), and the number of driven organic fiber cords as a treat of the belt reinforcing layer is E. When defined as (book / 50mm), the following formula (2),
π × D × (R2 / R1) × E <70 (2)
It is necessary to satisfy the relationship indicated by. As shown in the above formula (2), a value correlated with the rolling resistance can be obtained by multiplying the roundness by the peripheral length of the apparent cord cross section and the number of driving. The smaller the value on the left side of the above formula (2), the better the level of rolling resistance. If this value is 70 or more, only the rolling resistance of the current commercial tire level can be achieved. Here, there are a plurality of combinations of D and E that satisfy the above formula (2). In this case, the driving number E is less than 55 (lines / 50 mm), for example, 25 to 54 (lines / 50 mm). It is preferable to do. By making the number of drivings E less than 55 (pieces / 50 mm), the work of cutting the treat becomes easy, and the productivity can be improved. On the other hand, when the driving number E is increased, the film tension of the dip liquid is deteriorated at the time of dipping, and the dip unevenness is increased, and yarn breakage is liable to occur during the slitting operation. Further, when the number of driving is reduced to less than 25 (pieces / 50 mm), the properties of the fabric are deteriorated during the twisting and weaving process of the treat, and the workability is lowered.
なお、本発明において、上記有機繊維コードの真円度は、コードの撚り条件を適宜選定することにより、調整することが可能である。特に、有機繊維コードの真円度を高めるためには、有機繊維コードを片撚りコードとすることが、最も効果的である。 In the present invention, the roundness of the organic fiber cord can be adjusted by appropriately selecting the twisting condition of the cord. In particular, in order to increase the roundness of the organic fiber cord, it is most effective to use the organic fiber cord as a single twisted cord.
本発明においては、ベルト補強層の有機繊維コードとして、上記式(1)および(2)に係る条件を満足するものを用いるものであればよく、これにより本発明の所期の効果を得ることができる。本発明においては、かかる条件を満足する有機繊維コードを用いる以外の点については特に制限はなく、上記有機繊維コードのコード構造や材質、および、ベルト補強層以外のタイヤ構造の詳細等については、所望に応じ、常法に従い適宜選定することができ、特に制限されるものではない。 In the present invention, any organic fiber cord that satisfies the conditions according to the above formulas (1) and (2) may be used as the organic fiber cord of the belt reinforcing layer, thereby obtaining the intended effect of the present invention. Can do. In the present invention, there is no particular limitation with respect to the point other than using an organic fiber cord that satisfies the above conditions. For the cord structure and material of the organic fiber cord, and details of the tire structure other than the belt reinforcing layer, etc. If desired, it can be appropriately selected according to a conventional method, and is not particularly limited.
例えば、上記有機繊維コードの総繊度は、好適には300dtex以上、例えば、460〜3000dtexとする。有機繊維コードの総繊度が300dtex未満であると、原糸の撚り工程において現在用いられているタイヤコードの撚り機では、生産性が著しく低くなってしまう。 For example, the total fineness of the organic fiber cord is preferably 300 dtex or more, for example, 460 to 3000 dtex. When the total fineness of the organic fiber cord is less than 300 dtex, the productivity of the tire cord twisting machine currently used in the raw yarn twisting process is significantly reduced.
また、有機繊維コードの材質としては、一般にベルト補強層の補強コードとして使用されるもののうちから適宜選択して用いることができ、特に制限されるものではないが、好適には、66−ナイロンを用いる。有機繊維コードの材質として66−ナイロンを用いることで、接着性、特に耐熱接着性が良好となり、好適である。 The material of the organic fiber cord can be appropriately selected from those generally used as the reinforcement cord of the belt reinforcement layer, and is not particularly limited. Use. Use of 66-nylon as the material of the organic fiber cord is preferable because the adhesiveness, particularly heat resistant adhesiveness is improved.
カーカスプライ2は、図示する例では1枚であるが、本発明において、カーカスプライ2の枚数はこれに限られるものではなく、2枚以上であってもよい。また、その構造も特に限定されるものではない。ビード部におけるカーカスプライ2の係止構造についても、図示するようにビードコア1の周りに巻き上げて係止した構造に限られず、カーカスプライの端部を2層のビードコアで挟み込んだ構造でもよい(図示せず)。 Although the number of carcass plies 2 is one in the illustrated example, the number of carcass plies 2 is not limited to this in the present invention, and may be two or more. Further, the structure is not particularly limited. The locking structure of the carcass ply 2 in the bead portion is not limited to the structure in which the carcass ply 2 is wound and locked around the bead core 1 as shown in the figure, and may be a structure in which the end portion of the carcass ply is sandwiched between two layers of bead cores (see FIG. Not shown).
また、ベルト層3a,3bは、タイヤ周方向に対し、例えば、±15〜40°で傾斜して延びるコードのゴム引き層、好ましくは、スチールコードのゴム引き層からなる。図示する例では、2層のベルト層3a,3bが、各ベルト層を構成するコード同士がタイヤ赤道面を挟んで互いに交差するように積層されて交錯層を構成しているが、本発明においては、少なくとも1層のベルト層が配置されているものであればよく、図示する例に限られるものではない。 Further, the belt layers 3a and 3b are made of a rubberized layer of a cord, preferably a rubberized layer of a steel cord, extending with an inclination of, for example, ± 15 to 40 ° with respect to the tire circumferential direction. In the illustrated example, the two belt layers 3a and 3b are laminated so that the cords constituting each belt layer intersect with each other across the tire equatorial plane. Is not limited to the illustrated example as long as at least one belt layer is disposed.
さらに、本発明に係るベルト補強層は、図示する例では、ベルト層3の全幅以上にわたり配置されるキャップ層4と、ベルト層3の両端部を覆う領域に配置されるレイヤー層5とからなるが、これには限られず、キャップ層4若しくはレイヤー層5のみ、または、2層以上のキャップ層4および/または2層以上のレイヤー層5の組み合わせであってもよい。かかるベルト補強層は、例えば、複数本の有機繊維コードを引き揃えてゴム被覆してなる一定幅のストリップを、タイヤ周方向に螺旋巻きすることで形成することができる。なお、本発明においては、ベルト補強層が2層以上からなる場合には、各層について、上記有機繊維コードに係る条件を満足することが必要である。 Further, in the illustrated example, the belt reinforcing layer according to the present invention includes a cap layer 4 disposed over the entire width of the belt layer 3 and a layer layer 5 disposed in a region covering both ends of the belt layer 3. However, the cap layer 4 or the layer layer 5 alone or a combination of two or more cap layers 4 and / or two or more layer layers 5 may be used. Such a belt reinforcing layer can be formed, for example, by spirally winding a strip of a certain width formed by aligning a plurality of organic fiber cords and covering them with rubber in the tire circumferential direction. In the present invention, when the belt reinforcing layer is composed of two or more layers, it is necessary for each layer to satisfy the conditions relating to the organic fiber cord.
さらに、図示はしないが、本発明において、タイヤの最内層には通常インナーライナーが配置され、トレッド表面には、適宜トレッドパターンが形成される。さらにまた、本発明の空気入りタイヤにおいて、タイヤ内に充填する気体としては、通常のあるいは酸素分圧を変えた空気、または、窒素等の不活性ガスを用いることができる。 Further, although not shown in the drawings, in the present invention, an inner liner is usually disposed in the innermost layer of the tire, and a tread pattern is appropriately formed on the tread surface. Furthermore, in the pneumatic tire of the present invention, as the gas filled in the tire, normal or changed oxygen partial pressure, or inert gas such as nitrogen can be used.
以下、本発明を、実施例を用いてより詳細に説明する。
タイヤサイズ195/65R14にて、1枚のカーカスプライと、そのクラウン部のタイヤ径方向外側に配置された2層のベルト層と、そのタイヤ径方向外側に配置されたベルト補強層とを備える空気入りタイヤを作製した。カーカスプライは、有機繊維コード(材質:ポリエチレンテレフタレート(PET))と、これを被覆するゴムとからなるものとし、コードの打込み数は60本/50mmとした。また、そのコード角度は、タイヤ周方向に対し90°とした。ベルト層は、スチールコードのゴム引き層からなるものとし、そのコード角度は、タイヤ周方向に対し±25°とした。ベルト補強層は、ベルト層の全幅以上にわたり配置されるキャップ層の1層からなるものとし、下記表中に示す条件を満足する有機繊維コードのゴム引き層を、タイヤ周方向に対し実質的に平行に配列することにより形成した。
Hereinafter, the present invention will be described in more detail with reference to examples.
Air with tire size 195 / 65R14, one carcass ply, two belt layers arranged on the outer side in the tire radial direction of the crown portion, and a belt reinforcing layer arranged on the outer side in the tire radial direction An inset tire was produced. The carcass ply is composed of an organic fiber cord (material: polyethylene terephthalate (PET)) and a rubber covering the cord, and the number of cords to be driven is 60/50 mm. The cord angle was 90 ° with respect to the tire circumferential direction. The belt layer was made of a rubberized layer of steel cord, and the cord angle was ± 25 ° with respect to the tire circumferential direction. The belt reinforcing layer is composed of one layer of a cap layer disposed over the entire width of the belt layer, and a rubberized layer of an organic fiber cord that satisfies the conditions shown in the following table is substantially formed in the tire circumferential direction. It was formed by arranging in parallel.
<転がり抵抗>
比較例および各実施例で得られたタイヤにつき、転がり抵抗を評価した。転がり抵抗は、各供試タイヤをサイズ6J×14のリムに組み、内圧2.0kgf/cm2、荷重440kgfの条件下で、外径1.7mのドラム上に設置してドラムを回転させ、回転速度を120km/時まで上昇させた後、ドラムを惰行させて、回転速度80km/時のときの慣性モーメントを算出し、下記式に基づき評価した。結果は、比較例を100とする指数にて示した。この指数値が小さいほど転がり抵抗が小さく、良好である。
指数値=[(供試タイヤの慣性モーメント)/(従来例のタイヤの慣性モーメント)]×100
その結果を、下記の表中に併せて示す。
<Rolling resistance>
The rolling resistance of the tires obtained in the comparative example and each example was evaluated. Rolling resistance is as follows. Each test tire is assembled on a rim of size 6J × 14, and installed on a drum having an outer diameter of 1.7 m under the conditions of an internal pressure of 2.0 kgf / cm 2 and a load of 440 kgf, and the drum is rotated. After increasing the rotational speed to 120 km / hour, the drum was coasted and the moment of inertia at the rotational speed of 80 km / hour was calculated and evaluated based on the following formula. The results are shown as an index with the comparative example as 100. The smaller the index value, the smaller the rolling resistance and the better.
Index value = [(moment of inertia of test tire) / (moment of inertia of conventional tire)] × 100
The results are also shown in the table below.
<作業性>
各実施例等に係るカーカスプライのトリート製造時における作業性を、下記基準に従い評価した。その結果を、下記の表中に併せて示す。
◎:総作業時間が、比較例1対比で3%以上短い場合。
○:総作業時間が、比較例1対比で1%以上3%未満短い場合。
△:総作業時間が、比較例1対比で0%を超え1%未満短い場合。
×:総作業時間が、比較例1対比で同等である場合。
<Workability>
The workability at the time of treating the carcass ply according to each example was evaluated according to the following criteria. The results are also shown in the table below.
A: When the total work time is 3% or more shorter than that of Comparative Example 1.
○: When the total work time is 1% or more and less than 3% compared to Comparative Example 1.
Δ: When the total work time exceeds 0% and is shorter than 1% compared to Comparative Example 1.
X: When the total work time is equivalent to Comparative Example 1.
*2)式π×D×(R2/R1)×E(D:ディップコードとしてのコード径(mm),E:トリートとしての有機繊維コードの打込み数(本/50mm))に基づき算出された値である。
* 2) Calculated based on the formula π × D × (R2 / R1) × E (D: cord diameter (mm) as a dip cord, E: number of driven organic fiber cords as a treat (pieces / 50 mm)) Value.
上記表中に示すように、本発明に係る上記真円度および表面積ファクターの条件を満足する有機繊維コードをカーカスプライに用いた各実施例においては、かかる条件を満足しない各比較例に比し、良好な転がり抵抗が得られていることがわかる。また、コード直径が同一であれば、打込み数が少なければ少ないほど、有機繊維コードとゴムとが接触する総表面積が少なくなって、発生するロスが低減され、転がり抵抗の良化につながっている。さらに、打込み数Eを55(本/50mm)未満とすることで、作業性をより向上できることについても確かめられた。また、比較例2の結果から、真円度が1.3を超えると、表面積ファクターの値が70未満であっても、コード歪みによる発熱ロスが大きくなり、表面積ファクターの値から予期される転がり抵抗と、実測の転がり抵抗との間に、乖離が生じてしまうことがわかる。 As shown in the above table, in each example in which the organic fiber cord satisfying the conditions of the roundness and the surface area factor according to the present invention was used for the carcass ply, compared with each comparative example not satisfying the conditions. It can be seen that a good rolling resistance is obtained. In addition, if the cord diameter is the same, the smaller the number of driving, the less the total surface area where the organic fiber cord and rubber are in contact with each other, reducing the loss that occurs and leading to better rolling resistance. . Furthermore, it was confirmed that the workability can be further improved by setting the number of driving E to less than 55 (lines / 50 mm). Further, from the result of Comparative Example 2, when the roundness exceeds 1.3, even when the surface area factor value is less than 70, heat loss due to cord distortion increases, and rolling expected from the surface area factor value is expected. It can be seen that there is a divergence between the resistance and the measured rolling resistance.
1 ビードコア
2 カーカスプライ
3a,3b ベルト層
4 キャップ層
5 レイヤー層
11 ビード部
12 サイドウォール部
13 トレッド部
1 Bead core 2 Carcass ply 3a, 3b Belt layer 4 Cap layer 5 Layer layer 11 Bead portion 12 Side wall portion 13 Tread portion
Claims (4)
前記ベルト補強層を構成する有機繊維コードのコード長手方向に直交する断面における、ディップコードとしての最小径をR1(mm)、最大径をR2(mm)としたとき、R2/R1で定義される該有機繊維コードの真円度が、下記式(1)、
1.0<R2/R1≦1.3 (1)
を満足し、かつ、該有機繊維コードの、JIS規格に準拠して測定されるディップコードとしてのコード径をD(mm)、前記ベルト補強層の、トリートとしての該有機繊維コードの打込み数をE(本/50mm)と定義したとき、下記式(2)、
35.8≦π×D×(R2/R1)×E≦43.6 (2)
で示される関係を満足することを特徴とする空気入りタイヤ。 At least one carcass ply extending in a toroidal shape across a pair of left and right bead cores, and a reinforcing cord arranged on the outer side in the tire radial direction of the crown portion of the carcass ply and arranged inclined with respect to the tire circumferential direction Reinforcement of belt comprising at least one belt layer made of a rubberized layer, and a rubberized layer of organic fiber cords arranged outside the belt layer in the tire radial direction and arranged substantially parallel to the tire circumferential direction In a pneumatic tire comprising a layer,
In the cross section orthogonal to the cord longitudinal direction of the organic fiber cord constituting the belt reinforcing layer, when the minimum diameter as the dip cord is R1 (mm) and the maximum diameter is R2 (mm), it is defined as R2 / R1. The roundness of the organic fiber cord is expressed by the following formula (1),
1.0 <R2 / R1 ≦ 1.3 (1)
And the cord diameter of the organic fiber cord as a dip cord measured in accordance with JIS standard is D (mm), and the number of driving of the organic fiber cord as a treat of the belt reinforcing layer is When defined as E (book / 50 mm), the following formula (2),
35.8 ≦ π × D × (R2 / R1) × E ≦ 43.6 (2)
A pneumatic tire characterized by satisfying the relationship indicated by.