JP5378454B2

JP5378454B2 - Toilet Paper

Info

Publication number: JP5378454B2
Application number: JP2011121432A
Authority: JP
Inventors: 徹也上原; 芳紀清水; 浩大野
Original assignee: Daio Paper Corp
Current assignee: Daio Paper Corp
Priority date: 2011-05-31
Filing date: 2011-05-31
Publication date: 2013-12-25
Anticipated expiration: 2024-12-28
Also published as: JP2011236546A

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method of producing an embossed sheet that enables embossing clearly and provides an embossed sheet with good design. <P>SOLUTION: A sheet is embossed with an embossing member having a group of geometrical pattern protrusions 10 and a group of decorative pattern protrusions 20 composed of protrusions 21 which is smaller in number than the group of geometrical pattern protrusions 10. The group of decorative pattern protrusions 20 are 0.01-1.0 mm higher than the group of geometrical pattern protrusions 10. <P>COPYRIGHT: (C)2012,JPO&INPIT

Description

本発明は、トイレットペーパーに関するものである。 The present invention relates to toilet paper.

現在、例えば、トイレットペーパー等の衛生薄葉紙などは、エンボス（凹凸模様）の付いたものとすることが、一般的になっている。この種のトイレットペーパーのエンボスには、例えば、嵩だか性や柔軟性、吸収性等の機能性の向上を図ることを、主な目的とする幾何学的柄のエンボスや、見栄え、つまり意匠性の向上を図ることを、主な目的とする装飾的柄のエンボスなどがある。そして、近年では、これら複数の目的を並存させるためとして、例えば、幾何学的柄のエンボスと装飾的柄のエンボスとの組み合わせなどの、２種類以上のエンボスの付いたトイレットペーパーが、提供されるようになっている（例えば、特許文献１参照。）。 At present, for example, sanitary thin paper such as toilet paper is generally provided with an emboss (uneven pattern). The embossing of this kind of toilet paper is, for example, to improve the functionality such as bulkiness, flexibility, absorbability, etc. There is a decorative pattern embossing, etc. whose main purpose is to improve. In recent years, toilet paper with two or more types of embossing, such as a combination of embossing with a geometric pattern and embossing with a decorative pattern, is provided in order to coexist these multiple purposes. (For example, refer to Patent Document 1).

しかしながら、この種のトイレットペーパーは、１枚のシート又は複数枚のシートが積層されてなる積層シートに、２種類以上のエンボスが付いたものであるがゆえに、次のような問題を有することがわかった。
すなわち、この種のトイレットペーパーは、複数のエンボスが同時に使用者の目に入ることになるために、使用者に粗野な感覚を与えてしまい、意匠性に劣るのである。特に、意匠性の向上を図ろうと、装飾的柄のエンボスを付けた場合は、逆に粗野な感覚を与えてしまうこともあり、本末転倒ともいえる。 However, this type of toilet paper has the following problems because two or more kinds of embosses are attached to a laminated sheet obtained by laminating one sheet or a plurality of sheets. all right.
That is, this type of toilet paper gives a rough feeling to the user because a plurality of embossments are simultaneously in the eyes of the user, and is poor in design. In particular, when embellishment of decorative patterns is applied to improve the design, it may give a rough feeling, and it can be said that this is a fall.

また、製造という観点からみても、次のような問題がある。例えば、幾何学的柄の凸部郡と、これよりも少数の凸部からなる装飾的柄の凸部郡と、を有するエンボスロールなどによって、１枚のシート又は積層シートに、エンボスを付与しようとすると、多数の凸部からなる幾何学的柄の凸部郡によって、シートが引っ張られてしまい、一般に、より強い印象を与えたいとされる装飾的柄のエンボスが、不鮮明なものとなってしまうのである。装飾的柄のエンボスが、不鮮明になるということは、当然、意匠性の低下を意味する。
特表２００２−５０１９９２号公報 Further, from the viewpoint of manufacturing, there are the following problems. For example, embossing is applied to one sheet or laminated sheet by an embossing roll having a convex pattern group of geometric patterns and a convex pattern group of decorative patterns made up of a smaller number of convex parts. Then, the sheet is pulled by the convex pattern group of the geometric pattern consisting of a large number of convex parts, and the emboss of the decorative pattern that is generally desired to give a stronger impression becomes unclear. It ends up. The fact that the embossing of the decorative pattern becomes unclear naturally means a decrease in design.
Japanese translation of PCT publication No. 2002-501992

本発明が解決しようとする主たる課題の１つは、意匠性に優れたトイレットペーパーを、提供することにある。また、本発明は、エンボスを鮮明に付与することができ、得られるトイレットペーパーが意匠性に優れたものとなるエンボスシートの製造方法をも提供する。 One of the main problems to be solved by the present invention is to provide a toilet paper excellent in design. The present invention also provides a method for producing an embossed sheet that can give emboss clearly and the resulting toilet paper is excellent in design.

この課題を解決した本発明は、次のとおりである。
〔請求項１記載の発明〕
シート１枚当たりの坪量が１２．０〜１７．０ｇ／ｍ²トイレットペーパーであって、
幾何学的柄のエンボスを付与する凸部群と装飾的柄のエンボスを付与する凸部群とを有し、
前記幾何学的柄のエンボスを付与する凸部群が、凹凸が縦横に等間隔に並びかつ頂部相互間の距離が縦横ともに２．５〜１０ｍｍであるとともに、頂部とこの頂部と隣接する頂部との相互間に連なる稜線部を有し、
前記装飾的柄のエンボスを付与する凸部群が、頂部の平面視での面積が平面視の全面積の０．５〜２０％であり、
前記装飾的柄の凸部群と前記幾何学的柄の凸部群とが離間している、
エンボスロールによって付与された、
前記幾何学的柄のエンボスを付与する凸部群と装飾的柄のエンボスを付与する凸部群とに対応する、幾何学的柄のエンボスと装飾的柄のエンボスとの２種のエンボスとを有し、
その装飾的柄のエンボスの深さが前記幾何学的柄のエンボスの深さのよりも深く、その差が０ｍｍ超０．４ｍｍ以下である、
ことを特徴とするトイレットペーパー。 The present invention that has solved this problem is as follows.
[Invention of Claim 1]
The basis weight per sheet is 12.0 to 17.0 g / m ² toilet paper ,
A convex group for imparting geometric pattern embossing and a convex group for imparting decorative pattern embossing;
The convexity group to which the embossing of the geometric pattern is imparted is such that the irregularities are arranged at equal intervals in the vertical and horizontal directions, and the distance between the tops is 2.5 to 10 mm in both vertical and horizontal directions, and the top and the top adjacent to the top. Ridges that are continuous between each other,
The convex part group which gives the emboss of the decorative pattern has an area in a plan view of a top part of 0.5 to 20% of a total area in a plan view,
The convex part group of the decorative pattern and the convex part group of the geometric pattern are spaced apart,
Granted by embossing roll ,
Two types of embossing of the geometric pattern embossing and the decorative pattern embossing corresponding to the convex group of embossing of the geometric pattern and the convex group of embossing of the decorative pattern. Have
The embossed depth of the decorative pattern is deeper than the embossed depth of the geometric pattern , and the difference is more than 0 mm and not more than 0.4 mm.
Toilet paper characterized by that.

〔請求項２記載の発明〕
前記装飾的柄の凸部群と前記幾何学的柄の凸部群との離間距離のうち最も短い距離に、前記装飾的柄の凸部群の高さとこれよりも低い前記幾何学的柄の凸部群との高さとの差を足した値が１〜１０ｍｍである、請求項１記載のトイレットペーパー。 [Invention of Claim 2]
The shortest distance of the distance between the convex part group of the decorative pattern and the convex part group of the geometric pattern is the height of the convex part group of the decorative pattern and the geometric pattern lower than the distance. The toilet paper of Claim 1 whose value which added the difference with the height with a convex part group is 1-10 mm.

〔請求項３記載の発明〕
幾何学的柄のエンボスを付与する凸部郡の頂部の周端部のエッジが０．０１〜０．５ｍｍの曲率半径で削られたものである請求項１又は２記載のトイレットペーパー。 [Invention of Claim 3]
The toilet paper according to claim 1 or 2, wherein the edge of the peripheral edge portion at the top of the convex group that gives the emboss of the geometric pattern is shaved with a curvature radius of 0.01 to 0.5 mm.

〔請求項４記載の発明〕
幾何学的柄のエンボスを付与する凸部群の頂部の平面視での面積が平面視での全面積の５〜２５％である請求項１〜３のいずれか１項に記載のトイレットペーパー。 [Invention of Claim 4]
The toilet paper according to any one of claims 1 to 3, wherein an area of the top of the convex group to which the embossing of the geometric pattern is imparted is 5 to 25% of the total area in the plan view.

（主な作用効果）
（１）エンボスの深さが、種類ごとに異なると、エンボスの視認性が、種類ごとに異なり、強弱（メリハリ）あるものとなる。したがって、メリハリがあるという点で、意匠性に優れる。 (Main effects)
(1) When the depth of the emboss is different for each type, the visibility of the emboss is different for each type, and the strength is sharp. Therefore, it is excellent in design property in that there is sharpness.

（２）２種類以上のエンボスに、少なくとも幾何学的柄のエンボスと装飾的柄のエンボスとが含まれると、柄の変化に富むという点で、意匠性に優れる。 (2) When two or more types of embossing include at least a geometric pattern embossing and a decorative pattern embossing, the design is excellent in that the pattern varies greatly.

（３）装飾的柄のエンボスの深さが、幾何学的柄のエンボスの深さよりも、０ｍｍを超えて深いと、一般に、より強い印象を与えたいとされる装飾的柄のエンボスが、幾何学的柄のエンボスよりも、強調される。したがって、装飾的柄が強調されているという点でも、意匠性に優れる。 (3) When the embossed depth of the decorative pattern is deeper than 0 mm than the embossed depth of the geometric pattern, the embossed decorative pattern, which is generally desired to give a stronger impression, It is emphasized rather than the embossing of the scientific pattern. Therefore, it is excellent in design property also in that the decorative pattern is emphasized.

（４）両エンボスの深さの差が、０．４ｍｍ以下に抑えられていると、幾何学的柄の存在意義が失われないという点で、意匠性に優れる。 (4) If the difference in depth between the two embossments is suppressed to 0.4 mm or less, the design significance is excellent in that the presence of the geometric pattern is not lost.

（５）幾何学的柄の凸部郡と、これよりも少数の凸部からなる装飾的柄の凸部郡と、を有し、しかもこの装飾的柄の凸部郡の高さが、前記幾何学的柄の凸部郡の高さよりも、０．０１〜１．０ｍｍ高いエンボス部材によって、シートにエンボスを付与すると、上述（１）〜（４）と同様の作用効果を奏するトイレットペーパーが得られる。 (5) a convex group of geometric patterns and a decorative group of decorative patterns composed of a smaller number of convex parts, and the height of the convex group of decorative patterns is When embossing is given to a sheet by an embossing member that is 0.01 to 1.0 mm higher than the height of the convexity group of the geometric pattern, toilet paper that exhibits the same effects as the above (1) to (4) is obtained. can get.

（６）一般に、一枚のシート又は積層シートに、幾何学的柄の凸部郡と、これよりも少数の凸部からなる装飾的柄の凸部郡と、を有するエンボス部材によって、エンボスを付与しようとすると、多数の凸部からなる幾何学的柄の凸部郡によって、シートが引っ張られてしまい、より強い印象を与えたい装飾的柄のエンボスが、不鮮明なものとなる。しかしながら、装飾的柄の凸部郡の高さが、幾何学的柄の凸部郡の高さよりも、少なくとも０．０１ｍｍ以上高いエンボス部材によって、シートにエンボスを付与すると、引っ張る力のバランスがとれ、装飾的柄のエンボスが、不鮮明になるとの問題が生じない。 (6) In general, embossing is performed on one sheet or laminated sheet by an embossing member having a convex group of geometric patterns and a convex group of decorative patterns composed of a smaller number of convex parts. If it tries to give, the sheet will be pulled by the convex part group of the geometric pattern which consists of many convex parts, and the emboss of the decorative pattern which wants to give a stronger impression will become unclear. However, when embossing is applied to the sheet by an embossing member whose height of the convex pattern of the decorative pattern is at least 0.01 mm higher than the height of the convex pattern of the geometric pattern, the tensile force is balanced. The embossing of the decorative pattern does not cause a problem that it becomes unclear.

（７）装飾的柄の凸部郡が、幾何学的柄の凸部郡から離間していると、上述（５）及び（６）と同様の作用効果を得ることについて、装飾的柄の凸部郡の高さとこれよりも低い幾何学的柄の凸部郡の高さとの差の許容範囲が広がる。具体的には、両凸部郡の離間距離のうち最も短い距離に、両凸部郡の高さの差を足した値が、１〜１０ｍｍとなっていればよい。 (7) protrusions county decorative pattern may, when spaced apart from the convex portion County geometric pattern, for obtaining the same effects as described above (5) and (6), convex decorative pattern The tolerance of the difference between the height of the county and the height of the convex pattern with a lower geometric pattern is widened. Specifically, the value obtained by adding the difference in height between the two convex portions to the shortest distance among the separation distances between the two convex portions may be 1 to 10 mm.

（８）凸部郡が、規則的に並ぶ頂部と、この頂部と隣接する頂部との相互間に連なる稜線部と、を有し、頂部の周端部のエッジが削られていると、エンボス付与に際して、シートを引っ張る力が、エッジによって遮断されることがなく、シートの、頂部と当接する部分にも伝わる。したがって、エンボス付与に際して、シートを引っ張る力が、シート全体に均一に分散され、装飾的柄のエンボスが不鮮明になるのを防止するという観点において、効果的である。 (8) When the convex section group has a top part regularly arranged and a ridge line part connected to the top part adjacent to the top part, and the edge of the peripheral end part of the top part is shaved, embossing At the time of application, the force pulling the sheet is not interrupted by the edge, but is transmitted to the portion of the sheet that contacts the top. Therefore, when embossing is applied, the pulling force of the sheet is uniformly distributed throughout the sheet, which is effective from the viewpoint of preventing the embossing of the decorative pattern from becoming unclear.

（９）凸部郡が、規則的に並ぶ頂部と、この頂部と隣接する頂部との相互間に連なる稜線部と、を有し、頂部の周端部のエッジが削られていると、得られるエンボスシートは、裏面の凸部（表面の凹部）が、頂部によって形成されるため、エッジを有しないものとなる。したがって、裏面がざらざらしないという点で、肌触り感が向上し、また、見た目が滑らかになるという点で、意匠性が向上した、トイレットペーパーが得られる。 (9) When the convexity group has a top part regularly arranged and a ridge line part connected to the top part adjacent to the top part, and the edge of the peripheral end part of the top part is shaved, In the embossed sheet, the convex portion on the back surface (the concave portion on the front surface) is formed by the top portion, and therefore has no edge. Therefore, a toilet paper with improved design is obtained in that the feeling of touch is improved because the back surface is not rough, and the appearance is smooth.

（１０）上述（８）及び（９）の作用効果は、頂部の周端部のエッジが、０．０１〜０．５ｍｍの曲率半径で削られていると、特に優れたものとなる。 (10) The effects of the above (8) and (9) are particularly excellent when the edge of the peripheral edge of the top is cut with a radius of curvature of 0.01 to 0.5 mm.

（１１）一般に、シートは、エンボス付与に際して、幾何学的柄の凸部郡の頂部と当接する部分よりも、その他の部分の方が、より強く引っ張られる。そこで、頂部の平面視での面積を、平面視での全面積の５％以上とし、より強く引っ張られる部分の面積を限界付けるのが好ましい。このことは、装飾的柄のエンボスが不鮮明になるのを防止するという観点において、特に効果的である。 (11) In general, when embossing is performed, the sheet is pulled more strongly in the other part than in the part that abuts the top of the convex portion group of the geometric pattern. Therefore, it is preferable that the area of the top in plan view is 5% or more of the total area in plan view to limit the area of the portion that is more strongly pulled. This is particularly effective in terms of preventing the embossing of the decorative pattern from becoming blurred.

（１２）装飾的柄の凸部郡の頂部の平面視での面積が、平面視での全面積の０．５％未満となっていると、幾何学的柄と遜色がなくなり、装飾としての機能が劣る。他方、装飾的柄の凸部郡の頂部の平面視での面積が、平面視での全面積の２０％を超えると、装飾性が際立ち、意匠性において、くどい印象を与えてしまう。 (12) If the area of the top of the convex group of the decorative pattern in plan view is less than 0.5% of the total area in plan view, the geometric pattern and fading disappear, The function is inferior. On the other hand, if the area in the plan view of the top of the convex group of the decorative pattern exceeds 20% of the total area in the plan view, the decorativeness will stand out and the design will be terrible.

（１３）頂部相互間を、４ｍｍ以上離すと、シートを引っ張る力が均一に分散されることになる。このことは、装飾的柄のエンボスが不鮮明になるのを防止するという観点において、特に効果的である。 (13) When the top portions are separated from each other by 4 mm or more, the force for pulling the sheet is uniformly dispersed. This is particularly effective in terms of preventing the embossing of the decorative pattern from becoming blurred.

本発明によれば、エンボスを鮮明に付与された意匠性に優れたトイレットペーパーとなる。 According to this invention, it becomes the toilet paper excellent in the designability to which the emboss was provided clearly.

次に、本発明の実施の形態を説明する。
〔定義等〕
（１）本明細書のトイレットペーパーとは、２種類以上のエンボスが付いたトイレットペーパーである。本トイレットペーパーには、１枚のシートにエンボスが付いたもののほか、２枚、３枚、４枚又はそれ以上の複数枚のシートが重なってなる積層シートにエンボスが付いたものも含む。 Next, an embodiment of the present invention will be described.
[Definition etc.]
(1) The toilet paper of this specification is a toilet paper with two or more types of embossing. The toilet paper includes not only one sheet with an emboss, but also a sheet laminated with two, three, four or more sheets with an emboss.

（２）本明細書の幾何学的柄のエンボスとは、凹凸が、縦、横、斜め等に規則的に並んでできた模様を意味する。例えば、特開平７−２６８８００号公報の図１や、特開２００３−７３９９９号公報の図２０、米国特許第５１７３３５１号公報の図４、等に示されるエンボスが、その例である。 (2) The geometric pattern embossing in the present specification means a pattern in which irregularities are regularly arranged vertically, horizontally, diagonally, and the like. For example, the embossing shown in FIG. 1 of JP-A-7-268800, FIG. 20 of JP-A-2003-73999, FIG. 4 of US Pat. No. 5,173,351, and the like are examples.

（３）一方、本明細書の装飾的柄のエンボスとは、凹凸によって描き出された、例えば、花、木、草等の植物や、人、動物、魚、貝、昆虫等の生き物、山、川、海、雲、森、林等の自然、月、太陽、星等の惑星・衛星、車、飛行機、電車等の人工物、などのデザイン性のある模様を意味する。例えば、特開平６−２０６２６９号公報の図１１や、特開平７−２５８９９９号公報の図５、特開昭５９−１１６５００号公報の図３、等に示されるエンボスが、その例である。 (3) On the other hand, the embossment of the decorative pattern in the present specification refers to, for example, plants such as flowers, trees and grass, creatures such as humans, animals, fish, shellfish and insects, mountains, It means designs with nature such as rivers, seas, clouds, forests, forests, etc., planets / satellite such as moon, sun, stars, etc., artificial objects such as cars, airplanes, trains, etc. For example, the embossing shown in FIG. 11 of JP-A-6-206269, FIG. 5 of JP-A-7-258999, FIG. 3 of JP-A-59-116500, and the like are examples.

（４）本明細書の幾何学的柄の凸部郡及び装飾的柄の凸部郡とは、平板やロール等からなるエンボス部材の表面に設けられた、凸部の集まりを意味する。これらは、幾何学的柄のエンボス又は装飾的柄のエンボスを、シートに付与するためのものである。 (4) The convex pattern group of the geometric pattern and the convex pattern group of the decorative pattern in this specification means a group of convex parts provided on the surface of an embossed member made of a flat plate, a roll, or the like. These are for imparting geometric pattern embossing or decorative pattern embossing to the sheet.

（５）本明細書のエンボスの深さとは、エンボス部分の凹凸差を意味する。この凹凸差は、基本的に、エンボスを付与するための、エンボス部材の表面に設けられた凸部の高さに沿う。ただし、シートの素材、エンボス付与方法などによって、誤差が生じることがあり、完全に一致するものではない。 (5) The emboss depth in the present specification means a difference in unevenness of the embossed portion. This uneven | corrugated difference follows the height of the convex part provided in the surface of the embossing member for providing embossing fundamentally. However, errors may occur depending on the material of the sheet, the embossing method, etc., and they do not completely match.

以下、本発明の幾何学的柄のエンボスと装飾的柄のエンボスとが付いたトイレットペーパーの実施形態を説明する。 Hereinafter, embodiments of the toilet paper with the geometric pattern embossing and the decorative pattern embossing according to the present invention will be described.

〔シートの原料・抄紙等〕
本発明において、シートの原料は、パルプ繊維を使用することができる。
具体的なパルプ繊維（原料パルプ）としては、木材パルプ、非木材パルプ、合成パルプ、古紙パルプなどから、より具体的には、砕木パルプ（ＧＰ）、ストーングランドパルプ（ＳＧＰ）、リファイナーグランドパルプ（ＲＧＰ）、加圧式砕木パルプ（ＰＧＷ）、サーモメカニカルパルプ（ＴＭＰ）、ケミサーモメカニカルパルプ（ＣＴＭＰ）、ブリーチケミサーモメカニカルパルプ（ＢＣＴＭＰ）等の機械パルプ（ＭＰ）、化学的機械パルプ（ＣＧＰ）、半化学的パルプ（ＳＣＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒クラフトパルプ（ＮＢＫＰ）等のクラフトパルプ（ＫＰ）、ソーダパルプ（ＡＰ）、サルファイトパルプ（ＳＰ）、溶解パルプ（ＤＰ）等の化学的パルプ（ＣＰ）、ナイロン、レーヨン、ポリエステル、ポリビニルアルコール（ＰＶＡ）等を原料とする合成パルプ、脱墨パルプ（ＤＩＰ）、ウエストパルプ（ＷＰ）等の古紙パルプ、かすパルプ（ＴＰ）、木綿、アマ、麻、黄麻、マニラ麻、ラミー等を原料とするぼろパルプ、わらパルプ、エスパルトパルプ、バガスパルプ、竹パルプ、ケナフパルプ等の茎稈パルプ、靭皮パルプ等の補助パルプなどから、一種又は数種を適宜選択して使用することができる。 [Sheet materials, papermaking, etc.]
In the present invention, pulp fibers can be used as the raw material of the sheet.
Specific pulp fibers (raw pulp) include wood pulp, non-wood pulp, synthetic pulp, waste paper pulp, and more specifically, groundwood pulp (GP), stone grand pulp (SGP), refiner ground pulp ( RGP), pressurized groundwood pulp (PGW), thermomechanical pulp (TMP), chemithermomechanical pulp (CTMP), bleached chemithermomechanical pulp (BCTMP) and other mechanical pulp (MP), chemical mechanical pulp (CGP), Kraft pulp (KP) such as semi-chemical pulp (SCP), hardwood bleached kraft pulp (LBKP), softwood bleached kraft pulp (NBKP), soda pulp (AP), sulfite pulp (SP), dissolved pulp (DP), etc. Chemical pulp (CP), nylon, rayon, polyester, poly Synthetic pulp made from nil alcohol (PVA), deinked pulp (DIP), waste paper pulp such as waist pulp (WP), waste pulp (TP), cotton, flax, hemp, jute, manila hemp, ramie, etc. One or several kinds of rag pulp, straw pulp, esparto pulp, bagasse pulp, bamboo pulp, kenaf pulp, and other auxiliary pulps such as bast pulp can be appropriately selected and used.

パルプ繊維等からなる原料は、例えば、公知の抄紙工程、具体的には、ワイヤパート、プレスパート、ドライヤパート、サイズプレス、カレンダパート等を経るなどして、エンボス付与の対象となるシートとする。この抄紙に際しては、例えば、分散剤、苛性ソーダ、アンモニア水等のｐＨ調整剤、消泡剤、防腐剤、蛍光染料、離型剤、耐水化剤、流動変性剤、歩留まり向上剤などの適宜の薬品を添加することができる。 The raw material consisting of pulp fibers, for example, is a known paper-making process, specifically, a wire part, a press part, a dryer part, a size press, a calender part, etc. to form a sheet to be embossed. . In this papermaking, for example, suitable chemicals such as a dispersant, caustic soda, aqueous ammonia and other pH adjusters, antifoaming agents, preservatives, fluorescent dyes, mold release agents, water resistance agents, flow modifiers, yield improvers, etc. Can be added.

〔エンボスの付与〕
原料を抄紙して得たシートは、平板、ロール等からなるエンボス部材を押圧することによって、本実施の形態では、一対のロール間を通すことによって、エンボスを付け（エンボス付与）、エンボスシートとする。 [Grant emboss]
In the present embodiment, the sheet obtained by paper-making the raw material is pressed with an embossing member made of a flat plate, a roll, etc. In this embodiment, embossing is imparted by passing between a pair of rolls (embossing), To do.

このエンボスの付与は、シートが、例えば、パルプ繊維、再生繊維及びレーヨンの群から選ばれた１種又は２種以上の原料からなる場合は、一対のロールの一方又は双方を、加熱して行うのが好ましい。ロールを加熱して、エンボスを付与すると、エンボスが鮮明・明瞭に付与されるようになる。 The embossing is performed by heating one or both of a pair of rolls when the sheet is made of, for example, one or more raw materials selected from the group of pulp fiber, regenerated fiber and rayon. Is preferred. When the roll is heated to give emboss, the emboss is given clearly and clearly.

一対のロールは、双方とも金属ロールとすることもできるが、一方を、少なくとも表面がゴム等からなる弾性ロールとし、他方を、表面に複数の凸部が設けられた金属ロール（エンボスロール）とするのが、好ましい。弾性ロール及び金属ロールの組み合わせ（スチールラバー方式）によると、ロールのクリアランス調整の問題や、ロールに紙粉等が詰まるとの問題などが生じない。本実施の形態では、スチールラバー方式とする。 Both of the pair of rolls can be metal rolls, but one is an elastic roll having at least a surface made of rubber or the like, and the other is a metal roll (embossing roll) provided with a plurality of convex portions on the surface. It is preferable to do this. According to the combination of the elastic roll and the metal roll (steel rubber method), there is no problem of adjusting the clearance of the roll or the problem that the roll is clogged with paper dust or the like. In this embodiment, a steel rubber system is used.

一対のロールの一方のみを加熱する場合、加熱ロールは、弾性ロールであってもよいが、金属ロールである方が、好ましい。これは、金属ロールの方が、熱伝導率がよく効果的に加熱による効果が発揮されるということのほか、金属ロールが加熱されていると、エンボスの形状に対応したかたちで、シートに熱が与えられることになり、付与されるエンボスが、より鮮明・明瞭になるということ、からである。 When only one of the pair of rolls is heated, the heating roll may be an elastic roll, but is preferably a metal roll. This is because the metal roll has better thermal conductivity and the effect of heating is exhibited effectively, and when the metal roll is heated, the sheet is heated in a form corresponding to the shape of the emboss. This is because the embossing given becomes clearer and clearer.

加熱ロールの表面温度は、一対のロールが、双方とも金属ロールであるか、弾性ロール及び金属ロールの組み合わせであるか、双方が加熱されているか、一方のみが加熱されているか、弾性ロール及び金属ロールのいずれが加熱されているか、などに関わらず、４０〜１４０℃であるのが好ましく、６０〜１２０℃であるのがより好ましく、８０〜１００℃であるのが特に好ましい。表面温度が低すぎると、エンボスが鮮明になるとの効果が、十分に発揮されない。他方、表面温度が高すぎると、エネルギーロスとなるほか、シートが焼き付くおそれや、製造されるトイレットペーパーが固くなるおそれがある。 The surface temperature of the heating roll is such that the pair of rolls are both a metal roll, a combination of an elastic roll and a metal roll, whether both are heated, only one of them is heated, an elastic roll and a metal. Regardless of which of the rolls is heated, it is preferably 40 to 140 ° C, more preferably 60 to 120 ° C, and particularly preferably 80 to 100 ° C. When the surface temperature is too low, the effect that the emboss becomes clear is not sufficiently exhibited. On the other hand, if the surface temperature is too high, energy loss may occur, the sheet may be burned, and the manufactured toilet paper may be hardened.

以上の加熱方式による場合、エンボスの付与は、一対のロール間のエンボス圧（ニップ圧）が、５〜３０ｋｇ／ｃｍとなるように行うのが好ましく、１０〜２５ｋｇ／ｃｍとなるように行うのがより好ましく、１５〜２０ｋｇ／ｃｍとなるように行うのが特に好ましい。エンボス圧が低すぎると、エンボスが鮮明になるとの効果が、十分に発揮されない。他方、エンボス圧が高すぎると、シートがちぎれてしまうおそれがある。 In the case of the above heating method, embossing is preferably performed such that the embossing pressure (nip pressure) between the pair of rolls is 5 to 30 kg / cm, and is preferably 10 to 25 kg / cm. Is more preferable, and it is particularly preferably performed so as to be 15 to 20 kg / cm. When the embossing pressure is too low, the effect that the embossing becomes clear is not sufficiently exhibited. On the other hand, if the embossing pressure is too high, the sheet may be torn off.

一対のロールを、弾性ロール及び金属ロールの組み合せとする場合、弾性ロールは、その表面のショア硬度（Ｓｈｏｒｅｈａｒｄｎｅｓｓ）が、５０〜９０であるのが好ましく、６０〜７０であるのがより好ましい。ショア硬度が低すぎると、つまり弾性ロール表面がやわらかすぎると、シートが破断するおそれがある。他方、ショア硬度が高すぎると、つまり弾性ロール表面が硬すぎると、シートにエンボスが付かなくなるおそれがある。 When the pair of rolls is a combination of an elastic roll and a metal roll, the elastic roll preferably has a Shore hardness of 50 to 90, more preferably 60 to 70. If the Shore hardness is too low, that is, if the elastic roll surface is too soft, the sheet may break. On the other hand, if the Shore hardness is too high, that is, if the elastic roll surface is too hard, the sheet may not be embossed.

ところで、以上の加熱スチールラバー方式によると、シートの坪量を、例えば、１２．０〜１７．０ｇ／ｍ²とすることができる。このように坪量が小さいと、一般にエンボスを鮮明・明瞭に付与することができないとされるが、以上の方式による場合は、可能である。 By the way, according to the above heated steel rubber system, the basic weight of a sheet | seat can be 12.0-17.0g / m < ² >, for example. When the basis weight is small as described above, it is generally considered that embossing cannot be given clearly and clearly, but it is possible in the case of the above method.

エンボス付与に際するシートの搬送速度（加工速度）は、特に限定されない。ただし、操業効率の観点からは、１００〜１０００ｍ／分とするのが好ましく、６００〜１０００ｍ／分とするのがより好ましい。 The sheet conveyance speed (processing speed) for embossing is not particularly limited. However, from the viewpoint of operation efficiency, it is preferably 100 to 1000 m / min, and more preferably 600 to 1000 m / min.

また、以上の加熱方式によるか否かに関わらず、本トイレットペーパーをロール製品とするにあたっては、ドロー率〔（ワインダ速度−アンワインダ速度）／アンワインダ速度ラ１００〕を、−３．０〜１０％とするのが好ましく、−２．０〜５％とするのがより好ましく、０〜５％とするのが特に好ましい。ドロー率が低すぎると、シートが弛んでしわが入るおそれがあり、また、ロール製品が、巻きの弱いものとなって、例えば、運搬中に芯が飛び出すおそれがある。他方、ドロー率が高すぎると、シート切れ（断裂）が生じるおそれがあり、また、ロール製品とするための巻き取り時に、装飾的柄のエンボスにしわが入るおそれや、装飾的柄のエンボスが不鮮明になるおそれがある。 Further, regardless of whether or not the above heating method is used, when the toilet paper is used as a roll product, the draw rate [(winder speed−unwinder speed) / unwinder speed ra 100] is set to −3.0 to 10%. Preferably, the content is -2.0 to 5%, more preferably 0 to 5%. If the draw rate is too low, the sheet may be loosened and wrinkles may occur, and the roll product may become weakly wound, for example, the core may pop out during transportation. On the other hand, if the draw ratio is too high, the sheet may be cut (ruptured), and the decorative pattern embossing may be wrinkled or the embossing of the decorative pattern may be unclear when winding the roll product. There is a risk of becoming.

なお、ワインダ速度とは、シートをロール状に巻き取る際におけるシートの搬送速度（流通速度）を意味する。他方、アンワインダ速度とは、原反（ジャンボロール）からシートを繰り出す際におけるシートの搬送速度（流通速度）を意味する。 The winder speed means a sheet conveyance speed (circulation speed) when the sheet is wound into a roll. On the other hand, the unwinder speed means the sheet conveyance speed (distribution speed) when the sheet is unwound from the original fabric (jumbo roll).

本実施の形態の金属ロール、つまりエンボスロールは、図１に示すように、その表面（周面）に、多数の凸部１１，１２…からなる幾何学的柄の凸部郡１０と、これよりも少数の凸部２１，２１からなる、花及び葉がデザインされた装飾的柄の凸部郡２０と、が設けられている。本エンボスロールによると、シートに、幾何学的柄のエンボスと装飾的柄のエンボスとが付与されることになるため、柄の変化に富むという点で、意匠性に優れたエンボスシートが得られる。 As shown in FIG. 1, the metal roll of the present embodiment, that is, the embossing roll, has a convex group 10 of geometric patterns composed of a large number of convex parts 11, 12,. There are provided a convex group 20 having a decorative pattern in which flowers and leaves are designed. According to this embossing roll, the embossing of the geometric pattern and the embossing of the decorative pattern are imparted to the sheet, so that an embossed sheet excellent in design can be obtained in that the pattern changes. .

また、本実施の形態では、図２に示すように、装飾的柄の凸部郡２０の高さが、幾何学的柄の凸部郡１０の高さよりも、０．０１〜１．０ｍｍ、好ましくは０．３５〜０．６ｍｍ高くなっている（高低差Ｘ）。一般に、一枚のシート又は積層シートからなるシートに、幾何学的柄の凸部郡１０と、これよりも少数の凸部２１，２１…からなる装飾的柄の凸部郡２０と、を有するエンボスロールによって、エンボスを付与しようとすると、多数の凸部１１，１２…からなる幾何学的柄の凸部郡１０によって、シートが引っ張られてしまい、より強い印象を与えたい装飾的柄のエンボスが、不鮮明なものとなる。しかしながら、装飾的柄の凸部郡２０の高さが、幾何学的柄の凸部郡１０の高さよりも、０．０１ｍｍ以上高いと、シートを引っ張る力のバランスがとれ、装飾的柄のエンボスが、不鮮明になるとの問題が生じない。また、本エンボスロールによると、シートに付与される装飾的柄のエンボスの深さが、幾何学的柄のエンボスの深さよりも、少なくとも０ｍｍを超えて深くなるため、より強い印象を与えたい装飾的柄のエンボスが、幾何学的柄のエンボスよりも、強調される。したがって、装飾的柄が強調されているという点で、意匠性に優れたエンボスシートが得られる。また、両エンボスの深さの差が、少なくとも０．４ｍｍ以下に抑えられると、幾何学的柄の存在意義が失われず、この点でも、意匠性に優れたエンボスシートが得られる。 Moreover, in this Embodiment, as shown in FIG. 2, the height of the convex pattern 20 of a decorative pattern is 0.01-1.0 mm higher than the height of the convex pattern 10 of a geometric pattern, Preferably it is 0.35-0.6 mm high (level difference X). In general, a sheet made of a single sheet or a laminated sheet has a convex group 10 having a geometric pattern and a convex group 20 having a decorative pattern having a smaller number of convex parts 21, 21,. When embossing is to be applied by the embossing roll, the sheet is pulled by the geometrical pattern convexity group 10 consisting of a large number of convexities 11, 12,... However, it becomes unclear. However, if the height of the convex pattern 20 of the decorative pattern is 0.01 mm or more higher than the height of the convex pattern 10 of the geometric pattern, the force of pulling the sheet is balanced, and the decorative pattern There is no problem with embossing becoming blurred. Also, according to the embossing roll, the embossing depth of the decorative pattern imparted to the sheet is deeper than the depth of the geometric pattern embossing by at least 0 mm. The embossing of the target pattern is emphasized over the embossing of the geometric pattern. Therefore, an embossed sheet excellent in design is obtained in that the decorative pattern is emphasized. The difference in the depth of both embossed and suppressed at least 0.4mm below the geometric pattern existence is not lost, in this regard, the embossed sheet with excellent design properties can be obtained.

ただし、以上の幾何学的柄の凸部郡１０と、装飾的柄の凸部郡２０と、の高低差Ｘは、絶対的なものではない。装飾的柄の凸部郡２０が、幾何学的柄の凸部郡１０から離間している場合、つまり図２に示すように、装飾的柄の凸部郡２０の周端部に位置する凸部２１と、幾何学的柄の凸部郡１０の周端部に位置する凸部１１又は１２と、が離間している場合は、この離間距離のうち最も短い距離Ｙに、高低差Ｘを足した値が、１〜１０ｍｍとなる範囲で、好ましくは１．４〜３．０ｍｍとなる範囲で、高低差Ｘの範囲を狭め、あるいは広げることができる。両凸部郡１０，２０を離間させることによって、装飾的柄のエンボスの強調効果が、ある程度得られるためである。 However, the height difference X between the convex group 10 of the geometric pattern and the convex group 20 of the decorative pattern is not absolute. When the decorative pattern convex group 20 is separated from the geometric pattern convex group 10, that is, as shown in FIG. When the portion 21 and the convex portion 11 or 12 located at the peripheral end portion of the convex portion group 10 of the geometric pattern are separated from each other, the height difference X is set to the shortest distance Y among the separation distances. The range of the height difference X can be narrowed or widened in the range where the added value is 1 to 10 mm, preferably in the range of 1.4 to 3.0 mm. This is because the embossing effect of the decorative pattern embossing can be obtained to some extent by separating the both convexity groups 10 and 20.

一方、図１のほか、図３及び図４にも示すように、幾何学的柄の凸部郡１０は、規則的に並ぶ、本形態では縦横に等間隔に並ぶ、実質的に平坦な頂面を有するほぼ正方形の頂部１１，１１…と、この頂部１１，１１…と隣接する頂部１１，１１…との相互間に連なる稜線部１２，１２…と、から主になる（頂部１１，１１…を頂点とし、稜線部１２，１２…によって囲まれる部分が、底部１３，１３…となっている。）。もちろん、頂面の形状は、正方形に限定されず、例えば、菱形、円形、楕円形、多角形などとすることができ、更には、例えば、星形とすることもできる。ただし、頂面に細長い形状の部分があると、その部分が破損しやすいため、星形は、実用的でない。 On the other hand, as shown in FIG. 3 and FIG. 4 in addition to FIG. 1, the convex groups 10 of the geometric pattern are regularly arranged, and in this embodiment, the substantially flat tops are arranged at equal intervals vertically and horizontally. Are substantially square-shaped top portions 11, 11..., And ridge line portions 12, 12... Connected between the top portions 11, 11. ..., And the portion surrounded by the ridge line portions 12, 12... Is the bottom portion 13, 13. Of course, the shape of the top surface is not limited to a square, and may be, for example, a rhombus, a circle, an ellipse, or a polygon, and may be a star, for example. However, if there is an elongated part on the top surface, the part is easily damaged, and the star shape is not practical.

本幾何学的柄の凸部郡１０によると、シートに、いわゆる富士山型のエンボスが付くことになるため、嵩だか性、吸収性が向上する。富士山型のエンボスとしては、この他にも、例えば、特開平１−１１１０９６号公報に示されるものを、例示することができる。 According to the convexity group 10 of this geometric pattern, since a so-called Mt. Fuji-type emboss is attached to the sheet, the bulkiness and absorbability are improved. Other examples of the Mt. Fuji type embossing include those disclosed in Japanese Patent Application Laid-Open No. 1-11096.

ただし、本形態では、かかる公報記載のものと異なり、図２に示すように、頂部１１，１１…の周端部のエッジＥを削って、丸みをおびたものとしている。これにより、エンボス付与に際して、シートを引っ張る力が、エッジＥによって遮断されず、シートの、頂部１１，１１…と当接する部分にも伝わる。したがって、エンボス付与に際して、シートを引っ張る力が、シート全体に均一に分散され、装飾的柄のエンボスが不鮮明になるのを防止するという観点において、大変効果的である。また、これにより得られるエンボスシートは、裏面の凸部（表面の凹部に対応）が、頂部１１，１１…によって形成されるため、エッジを有しないものとなる。したがって、裏面がざらざらしないという点で、肌触り感が向上し、また、見た目が滑らかになるという点で、意匠性が向上した、エンボスシートが得られる。 However, in this embodiment, unlike the one described in this publication, as shown in FIG. 2, the edges E of the top portions 11, 11,... Thereby, when embossing is applied, the force for pulling the sheet is not blocked by the edge E, but is transmitted to the portion of the sheet that contacts the top portions 11, 11. Therefore, when embossing is applied, the pulling force of the sheet is uniformly distributed throughout the sheet, which is very effective from the viewpoint of preventing the embossing of the decorative pattern from becoming unclear. Moreover, since the embossed sheet obtained by this has the convex part on the back surface (corresponding to the concave part on the front surface) formed by the top parts 11, 11..., It does not have an edge. Therefore, it is possible to obtain an embossed sheet in which the feeling of touch is improved because the back surface is not rough and the design is improved in that the appearance is smooth.

以上のエッジＥは、０．０１〜０．５ｍｍの曲率半径で削られているのが好ましく、０．０３〜０．１ｍｍの曲率半径で削られているのがより好ましい。曲率半径が０．０１ｍｍ未満であると、頂部１１，１１…の周端部が鋭過ぎ、シートが破れ、あるいはシートの強度が落ちるおそれがある。他方、曲率半径が０．５ｍｍ超であると、頂部１１，１１…の周端部がなだらか過ぎ、エンボスが鮮明に付与されなくなるおそれがある。 The edge E is preferably cut with a radius of curvature of 0.01 to 0.5 mm, and more preferably with a radius of curvature of 0.03 to 0.1 mm. If the radius of curvature is less than 0.01 mm, the peripheral ends of the top portions 11, 11... Are too sharp and the sheet may be torn or the strength of the sheet may be reduced. On the other hand, if the radius of curvature exceeds 0.5 mm, the peripheral ends of the top portions 11, 11... Are too gentle, and embossing may not be clearly imparted.

ところで、幾何学的柄の凸部郡１０の凸部１１，１１…が、エッジＥを有しないものとする場合、幾何学的柄の凸部郡１０は、頂部１１，１１…の平面視での面積（合計面積）が、平面視での全面積（幾何学的柄の凸部郡１０が存在する領域の全面積）の５〜２５％となっているのが好ましく、６〜１５％となっているのがより好ましい。一般に、シートは、エンボス付与に際して、頂部１１，１１…と当接する部分よりも、その他の部分の方が、より強く引っ張られる。そこで、頂部１１，１１…の平面視での面積を、平面視での全面積の５％以上とし、より強く引っ張られる部分の面積を限界付けることによって、装飾的柄のエンボスが不鮮明になるのを防止するものである。 By the way, when the convex part 11,11 ... of the convex group 10 of a geometric pattern shall not have the edge E, the convex part group 10 of a geometric pattern is planar view of the top part 11,11 ... Is preferably 5 to 25% of the total area in plan view (the total area of the region in which the convexity group 10 of the geometric pattern exists), and is 6 to 15%. More preferably. In general, when embossing is applied, the sheet is pulled more strongly in the other portions than in the portions that contact the top portions 11, 11,. Therefore, the embossment of the decorative pattern becomes unclear by setting the area of the top portions 11, 11... In a plan view to 5% or more of the total area in the plan view and limiting the area of the portion pulled more strongly. Is to prevent.

なお、頂部１１，１１…の平面視での面積の範囲は、例えば、図２で説明すると、符号Ｍで示す位置まで、つまり凸部１１の周面が、断面視で高さ方向へ大きく変化する位置まで、である。一方、平面視での全面積の範囲は、幾何学的柄の凸部郡１０の周端部に位置する凸部１１又は１２の境界位置Ｎまで、である。 The range of the area of the top portions 11, 11... In plan view is, for example, described with reference to FIG. 2, up to the position indicated by symbol M, that is, the peripheral surface of the convex portion 11 greatly changes in the height direction in cross-sectional view. Until the position to do. On the other hand, the range of the total area in plan view is up to the boundary position N of the convex portion 11 or 12 located at the peripheral end portion of the convex group 10 of the geometric pattern.

一方、装飾的柄の凸部郡２０の頂部２１の平面視での面積（合計面積）は、平面視での全面積（装飾的柄の凸部郡２０が存在する領域の全面積）の０．５〜２０％となっているのが好ましく、１〜１０％となっているのがより好ましい。０．５％未満となっていると、幾何学的柄と遜色がなくなり、装飾としての機能が劣る。他方、２０％を越えると、装飾性が際立ち、意匠性において、くどい印象を与えてしまう。 On the other hand, the area (total area) in the plan view of the top portion 21 of the convex pattern 20 of the decorative pattern is 0 of the total area (total area of the region in which the convex pattern 20 of the decorative pattern exists) in the planar view. 5 to 20% is preferable, and 1 to 10% is more preferable. If it is less than 0.5%, the geometric pattern and the discoloration disappear, and the function as a decoration is inferior. On the other hand, if it exceeds 20%, the decorativeness stands out and gives a terrible impression in design.

さらに、本形態では、図３に示すように、頂部１１，１１…相互間の距離（ピッチ）Ｌを、縦横ともに、２．５〜１０ｍｍ、好ましくは４〜６ｍｍとしている。頂部１１，１１…相互間を、２．５ｍｍ以上離すと、シートを引っ張る力が均一に分散されることになるので、装飾的柄のエンボスが不鮮明になるのを防止するという観点において、いっそう効果的である。また、この場合、幾何学的柄の凸部郡１０の凸部１１，１１…は、例えば、１０ｍｍ²あたりに、約５〜２０個、設けることができる。 Furthermore, in this embodiment, as shown in FIG. 3, the distance (pitch) L between the top portions 11, 11... Is 2.5 to 10 mm, preferably 4 to 6 mm, both vertically and horizontally. When the top portions 11, 11... Are separated from each other by 2.5 mm or more, the pulling force of the sheet is uniformly dispersed, so that the effect of preventing the embossing of the decorative pattern from becoming blurred is further effective Is. In this case, for example, about 5 to 20 convex portions 11, 11... Of the geometric pattern convex portion group 10 can be provided per 10 mm ² .

〔その他〕
（１）幾何学的柄の凸部郡１０の各凸部１１の面積は、０．０１〜２．０ｍｍ²とするのが好ましく、０．８〜１．５ｍｍ²とするのがより好ましい。０．０１ｍｍ²未満とすると、エンボスのベースである柔らかさとしての機能が出なくなってしまう。他方、２．０ｍｍ²を越えると、製品裏面にざらつきが生じてしまう。 [Others]
(1) area of each convex portion 11 of the projecting portion gun 10 of the geometric pattern may preferably be 0.01 to 2.0 mm ^2, and more preferably, 0.8 to 1.5 mm ^2. If it is less than 0.01 mm ² , the function as the softness that is the base of the emboss will not be produced. On the other hand, if it exceeds 2.0 mm ² , the back surface of the product becomes rough.

（２）装飾的柄の凸部郡２０の各凸部２１の幅は、０．１〜１．５ｍｍとするのが好ましい。０．１ｍｍ未満とすると、エンボスをかける時に、シートの破断が生じやすくなるとともに、装飾としての柄が見えにくくなってしまう。他方、１．５ｍｍを越えると、エンボスが十分にシートに押し込まれず、鮮明に入らない。 (2) The width of each convex portion 21 of the convex pattern 20 of the decorative pattern is preferably 0.1 to 1.5 mm. If the thickness is less than 0.1 mm, the sheet tends to break when embossed, and the pattern as a decoration becomes difficult to see. On the other hand, if it exceeds 1.5 mm, the embossing is not sufficiently pushed into the sheet and does not enter clearly.

本発明は、例えば、トイレットペーパーやティシュペーパー等の衛生薄様紙、キッチンペーパー、トイレ空間の拭き掃除用のトイレクリーナー、台所周りの拭き掃除用のキッチンクリーナーなどのエンボスシート及びその製造方法として、適用可能である。 The present invention can be applied, for example, as an embossed sheet such as sanitary thin paper such as toilet paper or tissue paper, kitchen paper, toilet cleaner for wiping the toilet space, kitchen cleaner for wiping around the kitchen, and the manufacturing method thereof. It is.

幾何学的柄の凸部郡及び装飾的柄の凸部郡を示す図である。It is a figure which shows the convex group of a geometric pattern, and the convex group of a decorative pattern. 凸部の構成を説明するための断面模式図である。It is a cross-sectional schematic diagram for demonstrating the structure of a convex part. 幾何学的柄の凸部郡の一部拡大図である。It is a partial enlarged view of the convex part county of a geometric pattern. 図３のＩ−Ｉ線断面図である。It is the II sectional view taken on the line of FIG.

１０…幾何学的柄の凸部郡、１１…幾何学的柄の凸部郡の頂部、１２…稜線部、２０…装飾的柄の凸部郡、２１…装飾的柄の凸部郡の凸部。 DESCRIPTION OF SYMBOLS 10 ... Geometric pattern convexity group, 11 ... Geometrical pattern convexity group top part, 12 ... Ridge line part, 20 ... Decorative pattern convexity group, 21 ... Decorative pattern convexity group convexity Department.

Claims

The basis weight per sheet is 12.0 to 17.0 g / m ² toilet paper ,
A convex group for imparting geometric pattern embossing and a convex group for imparting decorative pattern embossing;
The convexity group to which the embossing of the geometric pattern is imparted is such that the irregularities are arranged at equal intervals in the vertical and horizontal directions, and the distance between the tops is 2.5 to 10 mm in both vertical and horizontal directions, and the top and the top adjacent to the top. Ridges that are continuous between each other,
The convex part group which gives the emboss of the decorative pattern has an area in a plan view of a top part of 0.5 to 20% of a total area in a plan view,
The convex part group of the decorative pattern and the convex part group of the geometric pattern are spaced apart,
Granted by embossing roll ,
Two types of embossing of the geometric pattern embossing and the decorative pattern embossing corresponding to the convex group of embossing of the geometric pattern and the convex group of embossing of the decorative pattern. Have
The embossed depth of the decorative pattern is deeper than the embossed depth of the geometric pattern , and the difference is more than 0 mm and not more than 0.4 mm.
Toilet paper characterized by that.

The shortest distance of the distance between the convex part group of the decorative pattern and the convex part group of the geometric pattern is the height of the convex part group of the decorative pattern and the geometric pattern lower than the distance. The toilet paper of Claim 1 whose value which added the difference with the height with a convex part group is 1-10 mm .

The toilet paper according to claim 1 or 2, wherein the edge of the peripheral edge portion at the top of the convex group that gives the emboss of the geometric pattern is shaved with a curvature radius of 0.01 to 0.5 mm.

The toilet paper according to any one of claims 1 to 3, wherein an area of the top of the convex group to which the embossing of the geometric pattern is imparted is 5 to 25% of the total area in the plan view.