JP5332250B2 - Self-supporting bag with spout and its manufacturing method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a self-supporting bag with a spout part in which the spout part is easily opened in a cylindrical shape when spouting a content, its shape-keeping property is good, and the content can be smoothly spouted to the last without closing the spout part during the spouting in the field of the self-supporting bag in which a bottom part is formed in a gusset shape, and the spout part is formed in a part of an upper part in a spouting shape. <P>SOLUTION: The self-supporting property is given to the self-supporting bag with the spout part by forming its bottom part in a gusset shape by using a laminate film, and the spout part with its outer periphery being heat-sealed is provided on a part of an upper section in a projecting shape by notching both sides thereof. A cylindrical swollen part which projects outwardly is provided by the heat forming on the laminate film of at least one side of a part in the vicinity of the spout part toward the inner side of the bag over its base part from the spout part, tape-like sheets are arranged at a position on the inner side of the base part of the spout part across an opening part of the swollen part, and heat-bonded to the laminate film on both sides of the opening part. <P>COPYRIGHT: (C)2010,JPO&amp;INPIT

Description

  The present invention relates to a self-supporting bag with a spout portion, and more specifically, the bottom portion of the bag is formed in a gusset form to provide self-supporting properties, and a narrow spout portion is formed on both sides of a portion of the upper portion. In the field of a self-supporting bag with a spout part made of a laminated film provided in a projecting shape, at least a laminated film on one side of the bag has a bulge that is convex outward in the region from the spout part to the inside of the bag The part was formed with good shape retention, and when the contents filled in the bag were poured out, the spout part was opened reliably, and it was opened until the end without closing in the middle. It relates to self-standing bags with spouts.

  Conventionally, as a self-supporting bag with a spout part, a narrow spout part is formed on the upper part of a standing pouch-type self-supporting bag whose bottom part is formed in a gusset form, and its outer periphery is heat-sealed, and the spout part A bag with a notch on the side and a shape that protrudes upward is easy to handle and has some features as a three-dimensional container, so it can be packed compactly for its capacity. In addition, even when the filled liquid content is transferred to another container such as a small-bore bottle, it can be transferred relatively safely. Widely used for sealed packaging of a wide range of contents.

However, such a self-standing bag with a spout portion is excellent in self-supporting property, but when the content is poured out because the width of the spout portion is narrow, the opened spout portion is difficult to spread, and However, there is a problem that the pouring outlet part is easily blocked during pouring, and the pouring operation becomes troublesome.
In order to solve such a problem, for example, a bag with a spout portion is proposed in which the spout portion film is embossed in various shapes to improve the spread of the spout portion, that is, the openability. ing.

  For example, (1) “refillable pouch”, “narrow width formed by heat seal portions on both sides” as a bag that has been embossed to improve the opening and shape retention of the spout portion. A refillable pouch in which a fluid content is hermetically packaged, and is a combination of flat surfaces on at least one wall film near the spout portion, There is a refillable pouch characterized by having a bulging portion whose cross-sectional shape is formed by a combination of straight lines (see Patent Document 1).

In addition, a bag with a spout portion that has improved the opening property of the spout portion and its shape retention by means other than the embossing has also been proposed. For example, as (2) “pouch with spout”, “A pouch in which the peripheral edge is sealed by heat sealing and the contents having fluidity are hermetically packaged, the pouch is provided with a spout portion on the periphery of the pouch, and on the inner surface of the spout portion. There is a pouch with a spout characterized in that a heat-shrinkable film is fixed ”(see Patent Document 2).
Japanese Patent Application Laid-Open No. 11-349012 (pages 2 to 5, FIGS. 1 to 3) Japanese Patent Laid-Open No. 11-91807 (pages 2 to 4, FIGS. 1 to 3)

In the “refillable pouch” described in Patent Document 1, as shown in FIG. 1, FIG. 2, and FIG. 3, at least one wall film in the vicinity of the narrow outlet port 6 has a flat surface. Since the bulging part S which is a combination and the cross-sectional shape in the width direction is formed by a combination of straight lines is provided, the bulging part S is bent at the boundary between the surfaces and the corners are formed in a linear shape. The rib effect improves the shape retention of the bulging portion S and improves the content pouring ability.
只 Even in such a refillable pouch, the bulging part of the spout part is formed by thermoforming, so when bundling empty pouches and storing for a long time, the bulging parts overlap and squeeze and work over time. In this case, since the return of thermoforming occurs, the bulging portion slightly expands in the width direction, and the height tends to decrease, and the effect of improving the pouring suitability tends to decrease, and there is room for improvement.

In the “pouch with spout” described in Patent Document 2, as shown in FIGS. 1 and 2, a heat-shrinkable film is stretched between the heat seal portions on both sides of the inner surface of the spout portion. Since it is fixed so that it passes, for example, by heating the spout part when filling the contents, only the heat-shrinkable film shrinks, so the film on the spout part on both sides rises outward and automatically A spout part is opened in a cylindrical shape, and the suitability for pouring the contents is imparted.
However, since the heat-shrinkable film itself is between the films on both sides of the spout, it is difficult to heat uniformly, heat shrinking becomes somewhat unstable, and the spout is reliably opened in the desired cylindrical shape. It was still inadequate in terms of making it happen.

  The present invention has been made in order to solve the above-described problems, and the problem is that the bottom of the bag is formed in a gusset form, and a narrow outlet is formed on both sides of the upper portion. In the field of self-standing bags with spouts that are cut out and protruded, the spouts are easy to pour out when filling liquid contents as well as being excellent in self-supporting To provide a self-supporting bag with a spout part that opens in a cylindrical shape, has good shape retention, and can be poured out safely and easily without clogging the spout part during pouring. It is.

The above problems can be solved by the following present invention.
That is, in the invention described in claim 1, the bottom portion of the bag is formed in a gusset form so as to be self-supporting, and a narrow spout portion is formed in a part of the upper portion, and both side portions thereof are notched and protruded. In a self-supporting bag with a spout part made of a laminated film provided in a shape, toward at least one side of the laminated film in the vicinity including the spout part, from the spout part to the inside of the bag beyond its base And a bulge portion having a convex shape on the outside is provided by thermoforming, and the tape-like sheet is disposed so that the bulge portion traverses the opening of the bulge portion at a position on the inner side of the base of the spout port portion. In addition, the tape-like sheet is made of a self-standing bag with a spout portion, characterized in that the tape-like sheet is a plastic material having a thickness of 150 μm to 400 μm .

Further, the invention described in claim 2, the tensile strength of the tape-like sheet, consisting spout with self-standing bag according to claim 1, characterized in that the 15~150N / 15mm width.
Invention described in claim 3, according to the opening position of the tip end of the spout, to claim 1 or 2, characterized in that at least half-cut line and the notch is provided as a easy-open means A self-supporting bag with a spout.
The invention described in claim 4 has a shape in which the bottom portion of the bag is formed in a gusset form so as to be self-supporting, and a spout portion having a narrow width is formed in a part of the upper portion, and both side portions thereof are notched and protruded. A self-supporting bag made of laminated film with a spout part, which is at least on one side of the laminated film including the spout part, from the spout part to the inside of the bag beyond its base A self-supporting bag with a spout portion in which a bulge portion that is convex outward is formed and a tape-like sheet is fixed at a position on the inner side of the base portion of the spout portion so as to cross the opening of the bulge portion In this manufacturing method, at least one side of the laminated film is heated, and then the laminated film is press-molded with a male mold and a female mold to form a bulge, and then the bulge is formed at a position inside the base of the spout. Tape-like sheet across the opening of After placement, it consists method for manufacturing a spout with self-standing bag, characterized by heat-bonding to the laminated film, the tape-shaped sheet with the exception of the opening.

In the present invention, the laminated film used for the production of the self-supporting bag is not particularly limited, and any known multi-layer film conventionally used for self-supporting bags such as a standing pouch can be used.
Further, in the present invention, the tape-like sheet used for fixing the bulging portion provided from the spout portion beyond the base portion toward the inner side of the bag is a sealant layer on the inner surface of the laminated film of the self-supporting bag. There is no particular limitation as long as it can be thermally bonded, but in order to efficiently perform thermal bonding of a tape-like sheet mechanically efficiently, it should have moderate rigidity and tensile strength and at the same time be free of curl and curl. is necessary.
Accordingly, when the tape-like sheet is formed of a plastic material, the width is preferably in the range of 5 mm to 15 mm, and the thickness is in the range of 150 μm to 400 μm .
Moreover, it is preferable that the tensile strength of a tape-shaped sheet is 15-150 N / 15mm width. When the tensile strength is less than 15 N / 15 mm width, the effect of fixing (holding) the bulging portion is insufficient, which is not preferable. When the tensile strength exceeds 150 N / 15 mm width, the tensile strength is already sufficient. This is not desirable because it is not necessary and rather disadvantageous in terms of economy.
The tensile strength is measured in accordance with the tensile test method for JIS K7127 plastic film and sheet. The test apparatus is a Tensilon universal tester [Model: SAT-, manufactured by A & D Corporation. 1150] and a test speed F: measured at 50 ± 5.0 mm per minute.

  Regarding the material of the tape-like sheet, at least the surface that is thermally bonded to the sealant layer on the inner surface of the self-supporting bag may be selected from those that can be thermally bonded from among polyolefin-based resins according to the material of the sealant layer. In most cases, polyethylene or polypropylene such as linear low-density polyethylene and high-pressure method low-density polyethylene is used for the sealant layer, so whether the entire tape-like sheet is made of a single layer of polyethylene or polypropylene. , And can be formed of a laminate in which the polyethylene or polypropylene is laminated on one surface. In the case of a laminate, it is preferable to use a resin having a melting point higher than that of the polyethylene or polypropylene for the layer opposite to the polyethylene or polypropylene layer, and use it by appropriately selecting from polyethylene terephthalate, nylon, polypropylene, etc. can do.

In addition, it is preferable to provide an easy-opening means for facilitating opening by tearing in addition to an opening instruction line by printing at the opening position on the tip side of the spout part.
As easy-opening means, a notch and a method of laminating a uniaxially stretched film in a laminated film of a bag by laser beam irradiation or the like (in this case, the stretched direction of the uniaxially stretched film is the spout portion. In the present invention, it is preferable to use a combination of a plurality of layers such as a notch and a half-cut line, or a lamination of a notch and a uniaxially stretched film.

As the notch, a single-shaped or V-shaped notch is usually used, but the shape is not particularly limited, and any shape having an acute angle portion in the cutting direction can be used.
The half-cut line is not limited to a linear half-cut line, and can be provided as an intermittent half-cut line such as a perforation. Such a half-cut line may be one, but assuming a case where the tear line is removed, a plurality of half-cut lines such as one to three on each side of the center half-cut line are arranged in parallel, Alternatively, it can be provided in an arbitrary shape such as a shape converging on the central half-cut line, or a combination of a plurality of parallel half-cut lines and an oblique half-cut line obliquely intersecting this.
Such a half-cut line is preferably provided on the laminated film on both the front and rear sides of the opening position of the spout part by laser light irradiation, and the depth of the half-cut line is a depth at which at least the surface base material layer is cut If it is.

According to the first aspect of the present invention, the self-supporting bag with the spout portion is formed such that the bottom portion of the bag is formed in a gusset form and is provided with self-supporting properties. In a self-standing bag with a spout part made of a laminated film provided with a shape in which the part is cut out and projecting, at least one side of the laminated film in the vicinity including the spout part extends beyond the base from the spout part A bulge that protrudes outward is provided by thermoforming toward the inner side of the bag, and the bulge crosses the opening of the bulge at a position on the inner side of the base of the spout. configuration tape-like sheet is arranged Rutotomoni, the tape-like sheet is heat-bonded to the laminated film, except the opening, by the tape-like sheet is a plastic material having a thickness 150Myuemu～400myuemu, fixed to When Therefore, the following effects can be obtained.
(1) Since the bottom portion of the bag is formed in a gusset form and is provided with independence, the bottom can be the same as that of a standing pouch, and excellent independence can be imparted to the independence bag.
(2) Since a narrow spout is provided in a part of the upper part of the bag so that both sides thereof are cut out and protruded, the liquid content filled in the self-supporting bag is reduced in diameter. Even when transferring to a container such as a bottle, it can be safely transferred without spilling the contents because the spout portion can be inserted into the mouth of the bottle and poured out.
(3) Since the self-supporting bag with the spout is made of a laminated film, by selecting the laminated film configuration, it is possible to provide excellent performance such as sealing performance, gas barrier properties, moisture resistance, and storage of contents. Can increase the sex.
(4) At least one side of the laminated film in the vicinity including the spout portion is provided with a bulging portion that protrudes outward from the spout portion to the inner side of the bag through the base by thermoforming. together is, the bulge portion, infusion outlet portion of the base portion of the inner side of the tape-like sheet across the opening of the bulge portion is disposed at a position Rutotomoni, the tape-shaped sheet with the exception of the opening Since the tape-like sheet is a plastic material having a thickness of 150 μm to 400 μm, which is thermally bonded to the laminated film, it is configured to be fixed, so that the bulging part returns over time, more specifically, over time. Among the changes in which the height of the bulge portion decreases and the width of the bulge portion increases, at least the change in which the width of the bulge portion widens is stopped by the tape-like sheet. The part is held in a shape closer to the shape at the time of molding.
In addition, since the bulging portion is provided by thermoforming, it is less likely to cause distortion in the surrounding laminated film, and in particular, wrinkles that are likely to occur in the heat seal portion on the outer periphery of the spout portion may be eliminated. And the appearance can be improved.
Further, since the bulging portion is provided on at least one side of the laminated film of the bag, a cylindrical bulging portion is formed from the spout portion to the inner side of the bag beyond the base portion. By cutting off the tip of the outlet portion at the opening position, the spout portion opens in a cylindrical shape with good shape retention.
Therefore, it is possible to smoothly pour out to the end without blocking the pour-out part during the pouring of the contents.

Moreover, the tape-like sheet, than has been the plastic material of thickness 150μm~400μm formed in (polyethylene or single layer of polypropylene, or one of polyethylene or polypropylene surface is to laminate laminated) construction, Te when thermal bonding to fix the expanded portion to the sealant layer of the inner surface of the laminated film of the self-standing bag the-loop-shaped sheet machine, it is possible to have sufficient rigidity and tensile strength that is required.
According to the invention described in claim 2 , in the structure of the self-standing bag with spout portion of the invention described in claim 1 , the tape-like sheet has a tensile strength of 15 to 150 N / 15 mm width. Therefore, in addition to the effect of the invention described in claim 1 , the effect of fixing the tubular bulge portion can be obtained more reliably.

According to the invention described in claim 3 , in the structure of the self-standing bag with the spout portion according to any one of the first and second aspects, the easy-opening means is provided at the opening position on the tip side of the spout portion. Since at least a half cut line and a notch are provided, in addition to the effects of the invention described in claim 1 or 2 , when taking out the contents filled in the self-supporting bag, the spout The tip of the part can be easily torn and opened at the opening position by hand, so that the spout part automatically opens into a cylindrical shape with good shape retention by the bulging part.

Embodiments of a laminated film used for manufacturing a self-supporting bag with a spout portion and a self-supporting bag with a spout portion of the present invention will be described below with reference to the drawings.
First, as described above, the laminated film used for the production of the self-supporting bag with the spout portion of the present invention is not particularly limited, and any known laminated film used for a self-supporting bag such as a standing pouch is used. be able to.
Moreover, although the laminated film of the same structure may be used for the laminated film used for the wall surface of a self-supporting bag, and the laminated film used for a bottom face, the laminated film of a different structure can also be used as needed.

As the laminated film, in a simple configuration, a laminated film having a configuration in which a sealant layer is laminated on a base film layer is used. However, the type and amount of contents filled in a bag, or water vapor and other gas barrier properties. Depending on the performance required, such as light shielding properties and various mechanical strengths, water vapor and other gas barrier layers, light shielding layers, strength improving layers, etc. were laminated between the base film layer and the sealant layer. A laminated film of construction can be used.
The above-mentioned base film layer, water vapor and other gas barrier layers, light shielding layer, strength improving layer, sealant layer and the like may each be formed as a single layer, or may be formed by laminating a plurality of layers. .

As the base film layer, a biaxially stretched film of polyester such as polyethylene terephthalate or polyethylene naphthalate, a biaxially stretched film of polyamide such as nylon 6, nylon 66, MXD6 (polymetaxylylene adipamide), or biaxially stretched A plastic film such as a polypropylene film can be suitably used, and synthetic paper, paper, and the like can also be used.
These may be used singly or may be used by combining a plurality.

  Examples of the gas barrier layer include films of saponified ethylene / vinyl acetate copolymer (EVOH), polyvinylidene chloride (PVDC), MXD6, polyacrylonitrile (PAN), metal foil such as aluminum foil, or silica. Biaxially stretched with a vapor-deposited layer of inorganic oxide such as alumina, zinc oxide, magnesium oxide or ITO, or a metal such as aluminum, or a coating layer such as PVDC, polyvinyl alcohol (PVA) or polyacrylic acid (PAA) A nylon film (ON film), a biaxially stretched polyethylene terephthalate film (PET film), a biaxially stretched polypropylene film (OPP film), or the like can be used.

The inorganic oxide or metal vapor-deposited layer can be formed by being deposited on the base film so as to have a thickness of about 200 to 1200 mm by means of vapor deposition, sputtering, ion plating or the like.
The inorganic oxide vapor-deposited layer may be formed of a single layer, but by forming it with a plurality of layers, a more excellent gas barrier property can be obtained.
In addition, the deposited layer of the inorganic oxide improves the adhesion or prevents damage such as cracks and effectively exhibits excellent gas barrier properties. Reactive acrylic resin, polyurethane resin, acrylic resin containing silane coupling agent, water-soluble polymer containing metal alkoxide, ethylene / vinyl acetate A gas barrier layer can be formed as a composite layer by providing a resin layer such as a polymer saponified product.

Of the gas barrier layers, an aluminum foil or a film provided with an aluminum vapor deposition layer is opaque and can also serve as a light shielding layer.
As the strength improving layer, any one of the base films may be additionally laminated as appropriate, and a biaxially stretched high-density polyethylene film or the like may also be laminated as a moisture-proof layer.
A known dry lamination method or extrusion lamination method (sandwich lamination method) can be used for laminating the base film layer, the gas barrier layer, the light shielding layer, and the strength improving layer.

The sealant layer includes linear low density polyethylene (L / LDPE), high pressure low density polyethylene (LDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), ethylene / α-olefin copolymer, ethylene In addition to vinyl acetate copolymers, ethylene / acrylic acid copolymers, ethylene / acrylic acid ester copolymers, ionomers, and the like, polypropylene and copolymers thereof can be used.
The sealant layer is laminated by forming the above resin into a film and laminating it by a dry lamination method or an extrusion lamination method, or by applying the above resin onto a laminated surface such as a base film layer or a gas barrier layer. Then, a method of laminating can be adopted. However, in the case where the content easily penetrates into the sealant layer or contains it, it is preferable to laminate by the dry lamination method.

The linear low density polyethylene (L / LDPE) is excellent in heat seal stability and content resistance, for example, stress cracking resistance against surfactants, etc., for packaging contents that require these performances. Suitable for
In addition, ethylene / α-olefin copolymers polymerized using a single site catalyst have a narrow molecular weight distribution and a stable copolymerization ratio, so they have excellent low-temperature heat sealability and hot sealability. As in the self-supporting bag of the present invention, a self-supporting bag formed by providing a gusset portion at the bottom, or a sealant layer of a bag having a step difference due to a difference in film overlap on a heat seal portion such as a normal gusset bag It is suitable in that it can prevent the occurrence of pinholes due to disconnection.

Next, the self-supporting bag with a spout part of the present invention manufactured using the laminated film as described above will be described with reference to the drawings. However, the present invention is not limited to these drawings unless it exceeds the gist.
FIG. 1 is a front view showing a configuration of an embodiment of a self-supporting bag with a spout portion of the present invention.
2 is an enlarged cross-sectional view taken along line XX in FIG.
FIG. 3 shows a self-supporting bag with a spout part of the present invention, which is provided with a bulging part that protrudes outward from the laminated film on the wall surface from the spout part to the inner side of the bag beyond its base part. It is sectional drawing of the principal part explaining an example of the method of fixing.

  A self-supporting bag 100 with a spout portion shown in FIG. 1 is a bag formed in a standing pouch form, and the body of the bag has longitudinal edges on both sides of the laminated films 1a and 1b on the front and rear walls. It is formed by heat-sealing at the side seal portions 6a and 6b, and the bottom portion of the bag is folded back inwardly between the laminated films 1a and 1b on the front and rear wall surfaces, and the laminated film folding portion 2 on the bottom surface is folded inside. In this case, semi-circular bottom laminated film cutout portions 3a and 3b are provided in the vicinity of the lower ends of both sides of the bottom laminated film which is formed in the form having a gusset portion 4 inserted to the bottom. The gusset portion 4 is formed by heat-sealing with a bottom seal portion 5 of a ship-bottom-shaped seal pattern in which the inside is concave in an arc shape from both sides to the center portion.

And in one corner part (left corner part in a figure) of the upper part of the self-supporting bag 100, the narrow outlet spout 10 which faces the outer side diagonally formed by heat-sealing the outer periphery with the spout sealing part 7 is shown. However, the cut-out portions 9a and 9b are provided on both sides to protrude so that the opening position on the tip side of the spout portion 10 is an easy-opening means. A notch 12 is provided in the cut line 11 and the upper end (the right end in the figure). Further, just above the portion where the notch 12 is provided on the distal end side of the spout portion 10, a pick portion 16 is provided by expanding the width of the spout portion seal portion 7, and the spout portion is formed by the notch 12 and the half cut line 11. The operability when opening 10 is improved.
In addition, the laminated films 1a and 1b on the front and rear wall surfaces are cylinders that protrude outwardly from the spout 10 to the inner side of the bag beyond the base (line B indicating the base of the spout). Shaped bulges 13a and 13b (see also FIG. 2 as appropriate) are provided by thermoforming, and the tubular bulges 13a and 13b are respectively located at the positions inside the base (B) of the spout 10. The tape-like sheets 14a and 14b are arranged so as to cross the openings 17 (see also FIG. 3) of the cylindrical bulges 13a and 13b, and the heat bonding parts are attached to the laminated films 1a and 1b on both sides of the openings 17. It is configured to be fixed by thermal bonding at (15a, 15b), (15c, 15d).
In addition, although the part except the part which provided the spout part 10 among the upper parts of the self-supporting bag 100 is heat-sealed by the upper seal part 8, since this part is used for the filling port of the contents, filling of the contents It is sealed by heat sealing later.

  FIG. 2 is an enlarged cross-sectional view taken along line XX of the self-supporting bag 100 with the spout portion shown in FIG. 1. In particular, the base film (note) Cylindrical bulging portions 13a and 13b provided toward the inner side of the bag beyond the line B) indicating the base portion of the outlet portion are respectively positioned at the inner side positions of the base portion (B) of the spout portion 10 at The tape-like sheets 14a and 14b are arranged so as to cross the opening of the bulge-like bulge, and the heat bonding portions (15a and 15b) or the heat bonding portions are attached to the inner surfaces of the laminated films 1a and 1b on both sides of the opening. It is a figure explaining the structure fixed by heat-bonding by (15c, 15d).

In FIG. 2, the laminated films 1a and 1b shown above and below are each provided with a tubular bulging portion 13a or a bulging portion 13b bulging outward, and the bulging portion 13a provided on the upper laminated film 1a. Is a laminated film on both sides of the opening portion of the tape-like sheet 14a disposed across the opening of the bulging portion 13a at a position (see FIG. 1) inside the base portion (B) of the spout portion 10. It is fixed to the inner surface of 1a by heat bonding with heat bonding portions (15a, 15b). Further, the bulging portion 13b provided in the lower laminated film 1b is similarly disposed at the position inside the base (B) of the spout portion 10 so as to cross the opening of the bulging portion 13b. The tape-like sheet 14b is fixed to the inner surface of the laminated film 1b at both sides of the opening by heat bonding with heat bonding portions (15c, 15d).
The self-standing bag 100 with the spout portion shown in FIG. 1 is produced by superimposing the bulging portion 13a and the bulging portion 13b thus fixed so that the openings face each other. Can form a cylindrical bulge having a double cross-sectional area in a region extending from the spout 10 to the inner side of the bag beyond the base (line B indicating the base of the spout). .
In the position shown in FIG. 2 (the position of the cross section along line XX in FIG. 1), the tape-like sheets 14a and 14b are interposed between the bulging portion 13a and the bulging portion 13b. Since the tape-like sheets 14a and 14b do not exist in the region from the tip portion of the tenth portion to the base portion (B), the opening portions of the bulging portions 13a and 13b are in contact with each other at this portion.
Further, the bulging portions 13a and 13b shown in FIG. 2 are thermoformed so that the cross-sectional shape thereof is a trapezoid, but may be a semi-cylindrical shape that is convex outward, and two large and small trapezoids. A multi-stage trapezoidal shape formed by stacking the layers may be used.

FIG. 3 shows a self-supporting bag with a spout part of the present invention, which is provided with a bulging part that protrudes outward from the laminated film on the wall surface from the spout part to the inner side of the bag beyond its base part. It is sectional drawing of the principal part explaining an example of the method to fix, for example, can provide a cylindrical bulge part and can fix it in the procedure shown to (A)-(D).
That is, (A) shows that one of the laminated films 1a, 1b on the front and rear wall surfaces of the self-supporting bag has a predetermined position on one laminated film 1a, and the cross section shown in FIGS. It is sectional drawing of the principal part which shows the condition immediately before forming the cylindrical bulging part 13a which becomes convex, for example by hot press molding, and it can be moved up and down, respectively, and a cross section is a trapezoidal cylinder. Is a laminate in which a male die 19 having a convex portion and a female die 18 having a reverse trapezoidal cross section and a cylindrical concave portion are aligned and heated to about 80 to 100 ° C. in advance. It is a figure which shows the state by which the film 1a was supplied with the predetermined pitch so that the sealant layer side might face the male type | mold 19. FIG.
The male mold 19 and the female mold 18 are preferably adjusted to about 35 to 55 ° C. so that the laminated film 1a can be cooled simultaneously with the molding at the time of press molding.
Next, (b) is a cross-sectional view showing a state in which the male mold 19 is lowered and the female mold 18 is raised and the laminated film 1a is press-molded. At this time, the clearance between the male mold 19 and the female mold 18 may be substantially the same as the thickness of the laminated film 1a.
Further, the vertical movement of the male mold 19 and the female mold 18 can be, for example, the female mold 18 can be fixed, and only the male mold 19 can be moved up and down for press molding. In this case, auxiliary means such as a spring or air blowing may be used to remove the molded part from the female mold 18.
(C) is a cross-sectional view showing a state in which the male mold 19 and the female mold 18 are removed after the cylindrical bulge is formed on the laminated film 1a by the method shown in (B), and the laminated film 1a. Is provided with a cylindrical bulging portion 13a having a trapezoidal cross section that protrudes outward from the spout portion toward the inner side of the bag through the base portion, and the inner side of the bulging portion 13a (see FIG. The upper side) is open as shown in the opening 17.
(D) is a position on the inner side of the base of the spout part of the laminated film 1a (see FIG. 1) in order to fix the cylindrical bulging part 13a formed in the shape shown in (c) in that state. ), A tape-like sheet 14a is disposed so as to cross the opening 17 of the cylindrical bulge 13a, and is thermally bonded to the laminated film 1a on both sides of the opening 17 as shown in the thermal bonding portions 15a and 15b. A cylindrical bulging portion 13a is fixed.

  Of the laminated films 1a and 1b on the front and back walls of the self-supporting bag, the other laminated film 1b is also provided with a cylindrical bulging portion 13b (see FIG. 2) similar to the bulging portion 13a. Since it can be formed and fixed by the same method as described in (i) to (d) above, description of the method is omitted.

  Hereinafter, the present invention will be described more specifically with reference to examples.

The self-standing bag with spout portion of the configuration shown in FIG. 1 is made into a bag with the following dimensions by using a laminated film having the following configuration on the wall surface and bottom surface of the bag, and the self-standing bag with spout portion of Example 1 A bag.
(1) Structure of laminated film (1a, 1b) (outside) biaxially stretched nylon film (thickness 15 μm), printing layer / adhesive / silicon oxide vapor deposition layer, biaxially stretched polyethylene terephthalate film (thickness 12 μm) / adhesive / Linear low density polyethylene film (thickness 80μm)
The above films are bonded together by a dry lamination method, and the adhesive between the films uses a two-component curable polyurethane adhesive for dry lamination (coating amount when dried: 3 g / m ² ). It is.

(2) Dimensions of each part of the self-supporting bag The external dimensions of the self-supporting bag are a width of 135 mm and a height (length) of 230 mm, and the height of the bottom gusset 4, that is, a laminated film from the bottom to the bottom of the bag The height to the folded part (upper end of the gusset part) 2 was 38 mm.
The ship bottom-shaped seal pattern for heat-sealing the gusset portion 4 is a seal pattern in which the inside is concave in an arc shape from both sides to the center as shown in the figure.
The widths of the side seal portions 6a and 6b on both sides of the bag were 5 mm each.
The spout part 10 was provided in such a shape that the maximum part width of the shape shown in the spout part seal part 7 was 48 mm and the maximum part length was 52 mm.
As for details, the full width of the position where the half-cut line 11 is provided is 22 mm, the length from the half-cut line 11 to the line B indicating the base of the spout part is 23 mm, and the taper angle of the spout part 10 is approximately 10 °. It was provided to become.

Cross sections provided on the laminated films 1a and 1b on the front and rear wall surfaces of the self-supporting bag 100 from the spout portion 10 toward the inner side of the bag through the base portion have a trapezoidal shape and the cylindrical bulging portions 13a and 13b have a width. The length is constant at 10 mm, and the length is 27 mm on the outer side (outlet side), 33 mm on the inner side (inside the bag), and 60 mm in total length with reference to the line B indicating the base of the outlet. It was provided by press molding.
Further, as the tape-like sheets 14a and 14b for fixing the bulging portions 13a and 13b, a linear low-density polyethylene monolayer tape-like sheet having a width of 10 mm, a length of 36 mm, and a thickness of 0.3 mm is used. Then, at a position 2 mm inward from the line B indicating the base portion of the spout portion, a thermal bonding portion (15a, 15b) is formed in the vicinity of both side portions of the bulging portions 13a, 13b in a direction perpendicular to the cylindrical bulging portions 13a, 13b. ) And (15c, 15d), and the bulging portions 13a, 13b were fixed by heat bonding.

  In the structure of the self-supporting bag with the spout part of Example 1, only the material structure of the tape-like sheets 14a and 14b thermally bonded to fix the bulging parts 13a and 13b is made of high-density polyethylene, medium-density polyethylene, and low Except for changing to a three-layer tape-shaped sheet co-extruded with density polyethylene at a thickness ratio of 2: 1: 1 and a total thickness of 250 μm, all were formed in the same manner as in Example 1. Thus, a self-supporting bag with a spout portion of Example 2 was produced.

About the self-supporting bag with the spout part of Examples 1 and 2 produced as described above, in particular, the opening property of the spout part when taking out the filled liquid content, and the openability of the opened spout part In order to evaluate the shape-retaining property and the content pouring property, each was filled with 400 ml of shampoo as a content, sealed with a degassing seal, stored for one month, and then manually placed on the spout. When the tip part was torn along the half-cut line from the notch and opened, all of them could be opened well. In addition, the opened spout part has a trapezoidal cross section on both sides of the laminated film and is provided with a cylindrical bulging part. It was.
Next, when the contents of the spout were inserted by inserting the spout into the mouth of the small-bore bottle, each of the self-standing bags with spouts of Examples 1 and 2 had a cylindrical expansion of the spout. The shape retention was good, and the spout was not blocked during the pouring, and the contents could be transferred smoothly to the end.

  The self-supporting bag with a spout part of the present invention includes various household liquid detergents used in bathrooms, washrooms, kitchens, shampoos, conditioners, body soaps, liquid seasonings, cooking oils, various beverages, etc. It is particularly suitable as a packaging bag for refilling that is used by sealing the liquid contents and transferring them to other containers such as bottles when using the contents. There are no particular restrictions on the application.

It is a front view which shows the structure of one Example of the self-supporting bag with a spout part of this invention. It is an expanded sectional view of the XX line of FIG. In the self-supporting bag with a spout portion of the present invention, a method is provided in which a bulge portion that is convex outward is provided on the laminated film on the wall surface from the spout portion to the inner side of the bag beyond the base portion, and the method is fixed. It is sectional drawing of the principal part explaining an example.

Explanation of symbols

1a, 1b Wall laminated film 2 Bottom laminated film folded part 3a, 3b Bottom laminated film cutout 4 Gusset part 5 Bottom seal part 6a, 6b Side seal part 7 Outlet part seal part 8 Upper seal part 9a, 9b Notch portion 10 Outlet portion 11 Half cut wire 12 Notch 13a, 13b Swelling portion 14a, 14b Tape-like sheet 15a, 15b, 15c, 15d Thermal bonding portion 16 Knob portion 17 Opening portion 18 Female die 19 Male die B Outlet Line indicating the base of the part 100 Self-standing bag with spout

Claims (4)

The bottom of the bag is formed in a gusset form to provide self-supporting properties, and the spout made of laminated film is provided with a narrow width spout in a part of the top, with both sides notched and protruding In the self-supporting bag with a portion, the bulging portion that protrudes outward from the spout portion to the inner side of the bag is heated on at least one side of the laminated film including the spout portion. provided by the molding, it is disposed tape-like sheet across the opening of the bulge portion on the inner side of the position of the base of the infusion outlet Rutotomoni, the tape-like sheet in the laminated film, except the opening A self-standing bag with a spout portion, wherein the self-standing bag is made of a plastic material having a thickness of 150 μm to 400 μm that is thermally bonded. The self-standing bag with a spout portion according to claim 1, wherein the tape-like sheet has a tensile strength of 15 to 150 N / 15 mm width. The self-standing bag with a spout part according to claim 1 or 2 , wherein at least a half-cut line and a notch are provided as an easy-opening means at the opening position on the tip side of the spout part. The bottom of the bag is formed in a gusset form to provide self-supporting properties, and the spout made of laminated film is provided with a narrow width spout in a part of the top, with both sides notched and protruding A self-supporting bag with a portion, and a bulging portion that protrudes outwardly from the spout portion to the inner side of the bag over the base portion of the laminated film in the vicinity including the spout portion In the method for manufacturing a self-supporting bag with a spout portion, in which a tape-like sheet is fixed so as to cross the opening of the bulge portion at a position on the inner side of the base portion of the spout portion. After the film is heated, the laminated film is press-molded with a male mold and a female mold to form a bulge, and then in a tape shape so as to cross the opening of the bulge at the position inside the base of the spout After placing the sheet, remove the opening. Note manufacturing method of the outlet section with self-standing bag, characterized by heat-bonding to the laminated film, the tape-like sheet Te.

Images