JP5192739B2 - 補強されたコンクリート床版の脱塩工法 - Google Patents
補強されたコンクリート床版の脱塩工法 Download PDFInfo
- Publication number
- JP5192739B2 JP5192739B2 JP2007182133A JP2007182133A JP5192739B2 JP 5192739 B2 JP5192739 B2 JP 5192739B2 JP 2007182133 A JP2007182133 A JP 2007182133A JP 2007182133 A JP2007182133 A JP 2007182133A JP 5192739 B2 JP5192739 B2 JP 5192739B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- mortar
- floor slab
- concrete floor
- reinforcing bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかしながら、近年、塩害などによる早期劣化が社会問題として取り上げられ、構造物としての耐用年数の確保や維持管理のあり方が議論されている。
この方法では、コンクリートの表面を電解質溶液とセルロースファイバーからなる付着性塗布材料で一時的に被覆し、この被覆塗布材料に外部電極を埋設して陽極とし、コンクリートの内部鉄筋を陰極として、電極の間に直流電流を印加することにより、コンクリートの内部から陽極に向かって塩化物イオンを泳動させ、コンクリートから塩化物イオンを除去するものである。
しかしながら、電気抵抗部材の幅や電気抵抗値等、脱塩を充分に行うのに適切な条件について、示唆するものではなかった。
上面が補強されたコンクリート道路床版において、表層のアスファルトを剥がし、さらに、該上面の補強部の鋼繊維補強コンクリート等をピックやウォータージェットにより除去すると、コンクリート床版上面が現れる。コンクリート床版内部の上端鉄筋の位置を施工図面や鉄筋探査機により調べ、図2〜5に示されるように鉄筋直上を電気抵抗の大きいモルタルで被覆する。補強コンクリートを除去する際、部分的に上端鉄筋が露出してしまい、かぶりがなくなる場合があるため、その部分にも電気抵抗の大きいモルタルで被覆し、短絡を防ぐようにする。被覆するときの厚みは特に制限されないが、脱塩を充分に行うには50mm以下が好ましい。
寒冷地に立地する道路から、塩害により劣化した床版を一部撤去した(図1参照)。この道路は冬期の路面凍結を防止するために凍結防止剤を路面に散布しており、脱塩前における既設コンクリート中の上面鉄筋近傍の塩化物イオン含有量が1.5kg/m3と高く、鉄筋が腐食しやすい状態にあった。磨耗したアスファルトを剥ぎ取り、鋼繊維補強コンクリートで補強された部分を除去した。
電極間の電圧:クランプメータにより測定した。
塩化物イオン含有量:JIS A 1154:2003「硬化コンクリート中に含まれる塩化物イオンの試験方法」に基づき、全塩化物イオン量を測定した。
実験例1の実験No.1-5において、被覆するモルタルの電気抵抗値を水セメント比や混和材、ポリマーの添加により変えたこと以外は、実験例1と同様に行った。なお、実験No.2-5として、実験No.2-4の電流密度を半分にして行った。結果を表2に併記する。
2:上端鉄筋
3:下端鉄筋
4:鋼繊維補強コンクリート
5:アスファルト
6:被覆モルタル
7:外部電極(陽極)
8:電解質溶液保持材
9:直流定電流電源
10:リード線
11:塩化物イオン含有量測定位置(鉄筋近傍)
12:塩化物イオン含有量測定位置(鉄筋間)
Claims (3)
- 上面が補強されたコンクリート床版において、該上面の補強部を除去した後、コンクリート床版内部の上端鉄筋の直上をモルタルで被覆し、その上に外部電極を設置して陽極とし、コンクリート床版内部の鉄筋を陰極として、陽極と陰極の間に直流電流を流すことを特徴とする床版の脱塩工法。
- モルタルで被覆する幅が、上端鉄筋のあきの50%以上であることを特徴とする請求項1記載の床版の脱塩工法。
- モルタルの電気抵抗値が、コンクリート床版の電気抵抗値以上であることを特徴とする請求項1または2記載の床版の脱塩工法。