JP5039817B2 - Porous laminate - Google Patents

Description

The present invention relates to a multi-hole laminates, packaging supplies, hygiene products, livestock supplies, agricultural supplies, building supplies, medical supplies, separation films, light diffusing plates, are intended to be suitably used as a separator reflection sheet or a battery.

  The polymer porous body with many fine communication holes is used for separation membranes used for the production of ultrapure water, generation of chemicals, water treatment, waterproof and moisture permeable films used for clothing and sanitary materials, batteries, etc. It is used in various fields such as battery separators.

Various techniques as described below have been proposed as techniques for creating a large number of fine communication holes in this type of polymer.
For example, Japanese Patent Application Laid-Open No. 5-25305 (Patent Document 1) proposes that a porous film can be obtained by kneading and sheeting ultrahigh molecular weight polyethylene and a solvent, extracting the solvent after stretching.
In this method, as described in paragraph 0045 and the like, the solvent is extracted by washing with an organic solvent for washing, so that a large amount of organic solvent is required, which is not preferable in the environment.

In Japanese Patent No. 3166279 (Patent Document 2), a porous film having communication properties is obtained by inflation-molding a resin composition containing a polyolefin resin and a filler, and uniaxially stretching the obtained film or sheet in the take-off direction. It has been proposed that a sheet be obtained.
Similarly, in Japanese Patent Application Laid-Open No. 2004-95550 (Patent Document 3), a porous film used as a separator for a lithium secondary battery is stretched at least in a uniaxial direction from a sheet formed from a resin composition containing a thermoplastic resin and a filler. It is obtained by doing.
In the porous film or sheet obtained by these methods, there are moderate irregularities due to the presence of the filler on the surface, and the slipperiness of the film is increased, but the presence of the filler in all layers, Since the mass (basis weight) per unit area becomes large, there is room for improvement.

Japanese Patent Application Laid-Open No. 11-060792 (Patent Document 4) discloses that a porous surface made of a polyethylene resin containing a fine particle surface roughening agent such as a filler only on the surface as a method for reducing the weight while maintaining the surface roughness to some extent. (Sections 11, 12, and 0018) have been proposed.
However, in the production of the porous film, the pore formation is performed by removing the plasticizer (Claims 10 to 12 and the like). As in the invention described in Patent Document 1, an organic solvent is used to remove the plasticizer. Since a large amount of is required, there is room for improvement so as to reduce the burden on the environment.

Furthermore, in Japanese Patent Laid-Open No. 10-50286 (Patent Document 5), a high melting point polyolefin film and a low melting point polyolefin film are heat treated to adjust birefringence and elastic recovery rate, respectively, and then subjected to thermocompression bonding. It has been proposed to produce a porous film to be used as a battery separator by obtaining a laminated film of more than one layer, stretching the laminated film in two steps to make it porous, and then heat setting.
In this method, which is generally called a single polymer open-hole stretching method, the conditions under which a preferable porous structure can be obtained under stretching conditions such as stretching temperature, stretch ratio, and multistage stretching are very narrow (column 0025). Column 0028 and the like), which is not preferable in view of process control in production on an industrial scale.

Also known are foaming techniques that use subcritical or supercritical fluids. Specifically, a polymer is impregnated with a subcritical or supercritical fluid to be saturated, and then a supersaturated state is created by a rapid pressure drop or the like, and supersaturated gas is foamed.
This method has the advantage that fine and uniform foaming can be obtained, and if an inert gas subcritical or supercritical fluid such as carbon dioxide or nitrogen is used, the load on the environment is extremely small.
However, in the vicinity of the surface of the polymer, it does not become supersaturated when a sudden pressure drop occurs, and gas is immediately released from the surface by diffusion / evaporation. Exists. For this reason, it was not possible to make a porous laminate having micropores that communicated in the thickness direction.

JP-A-5-25305 Japanese Patent No. 3166279 JP 204-95550 A JP-A-11-060792 Japanese Patent Laid-Open No. 10-50286

The present invention has an object to provide a whole has a uniform communicating pores, and the mass per unit area is small porous laminate.

In order to solve the above problems, the present invention
A resin composition containing an inorganic filler and a thermoplastic resin, a pair of outer layers positioned on the outermost surface,
An intermediate layer made of a polypropylene resin composition that is located between the outer layers on both sides and does not contain an inorganic filler,
A laminate comprising at least three layers,
When the entire laminate is 100 parts by mass, the content of the inorganic filler is 5 to 40 parts by mass,
The polypropylene resin composition of the intermediate layer has polypropylene as a hard segment, ethylene-propylene rubber as a soft segment, the ratio of the hard segment is 5 to 95 mass%, the ratio of the soft segment is 95 to 5 mass%, And the thermoplastic resin of the outer layer on both sides is a high density polyethylene having a density of 0.92 g / cm ³ or more,
Provided is a porous laminate characterized in that the outer layer and the intermediate layer on both sides have a large number of micropores communicating in the thickness direction and have an air permeability of 1 to 10,000 seconds / 100 ml. .
The said porous laminated body is manufactured from the following manufacturing method, for example.
Producing a laminate comprising the three layers;
After the obtained laminate is impregnated with a fluid in a supercritical state or a subcritical state, the micropores are formed in the intermediate layer by releasing the supercritical state or the subcritical state and vaporizing the fluid. And making it porous,
After the intermediate layer is made porous, micropores are formed in the outer layers on both sides to make the micropores communicate with the micropores of the intermediate layer.

The outer layers on both sides are not formed by vaporization when the fluid impregnated in the supercritical state or subcritical state is released from the state , and the porous outer layers are formed by stretching the laminate and the inorganic filler. The micropores are formed by peeling the interface with the resin layer.

The present invention has been made on the basis of results obtained by the inventors through repeated studies and experiments.
That is, the inventors first conducted research and experiments for making a porous structure using a subcritical or supercritical fluid, and made various studies, but avoiding the occurrence of a skin layer on the surface of the problem described above. could not.
Therefore, the present inventors provide a non-porous layer on the surface of the layer to be porous using a subcritical or supercritical fluid, and a so-called lid so that the intermediate layer and the non-porous layer on the outer surface It has been found that a porous laminate having micropores communicating with can be obtained.
That is, when the laminate is impregnated with a subcritical or supercritical fluid and then a sudden drop in pressure or the like is generated, the intermediate layer is covered with the outer non-porous layer. It was possible to create a supersaturated state on the surface of the intermediate layer without vaporizing the gas, and as a result, succeeded in producing micropores in the intermediate layer. Thereafter, when the nonporous layer serving as a lid was made porous by providing micropores by a known technique, a porous laminate having microholes communicating with the micropores of the intermediate layer in the thickness direction could be obtained.

Porous laminate of the present invention comprises an intermediate layer and a laminate consisting of at least three layers of the both sides outer layers that Do a resin composition located on both sides outer surfaces of polypropylene resin composition having a hard segment and a soft segment .

As described above, the polypropylene resin composition constituting the intermediate layer, that have a soft segment consisting of a hard segment and ethylene-propylene rubber of polypropylene. The hard segment serves to maintain the strength of the layer, and the soft segment serves to impregnate the subcritical or supercritical fluid. For each segment play to ensure the roles, the ratio of the hard segment is 5 to 95 wt%, the ratio of the soft segment Ru 95-5% by mass. If the hard segment ratio is less than 5% by mass, the intermediate layer is too soft to maintain the strength, and the subcritical or supercritical fluid cannot remain in the intermediate layer and is degassed. There is a possibility that it cannot be made porous. On the other hand, when the soft segment ratio is less than 5% by mass, the amount of subcritical or supercritical fluid impregnated decreases, making it difficult to obtain sufficient communication.

The polypropylene resin composition constituting the intermediate layer does not contain a filler . This is because the object of the present invention is to provide a porous laminate having a small mass per unit area.

  Delete

  Delete

  Delete

  Delete

The intermediate layer of the present invention, as described above, has a poly propylene in as a hard segment, ethylene as a soft segment - propylene rubber is polypropylene resin composition having a ratio of 5 to 95 wt%.

The ethylene-propylene rubber as a soft segment includes a binary copolymer of ethylene and propylene and a terpolymer containing a small amount of a non-conjugated diene monomer as a third component. It may be used. Examples of the non-conjugated diene monomer include dicyclopentadiene, ethylidene norbornene, and hexadiene.
As the ethylene-propylene rubber, an ethylene-propylene rubber having an ethylene content of 7 to 80% by mass relative to the whole rubber is preferable, and an ethylene-propylene rubber having 10 to 60% by mass is more preferable.
By adjusting the ethylene-propylene rubber content or the ethylene content in the ethylene-propylene rubber, the ethylene content relative to the entire resin composition constituting the intermediate layer is preferably 5 to 95 mass%.

Examples of the types classified by the manufacturing method of the resin of the intermediate layer, ethylene constituting the soft segment of poly propylene emission constituting a hard segment - blending using a kneading machine such as propylene rubber of soft component twin-screw extruder a compound type polymer, there is polymerized polymer of directly polymerizing ethylene emissions and propylene.
Ethylene constituting the soft segment - from the viewpoint of the dispersibility of the soft component of the propylene rubber, it is preferable to use a polymerizable polymer.

As a further method of increasing the content of soft segments, there is a method of blending a soft component of the ethylene propylene rubber to a commercial propylene copolymer. In this case, the content of the soft segment can be easily increased by using a kneader such as a twin screw extruder.
Similarly by blending using a kneading machine such as a twin screw extruder ethylene propylene rubber and polyethylene in to propylene homopolymer, it can be obtained an olefinic thermoplastic resin having a content of preferred soft segment.

Further, if the range that does not impair the properties of the object or the intermediate layer of the present invention, additives to be incorporated in generally the resin composition into a polypropylene resin composition constituting the intermediate layer, for example, antioxidants, You may mix | blend a heat stabilizer, a light stabilizer, a ultraviolet absorber, a neutralizer, an antifogging agent, an antiblocking agent, an antistatic agent, a slip agent, or a coloring agent.

The both-side outer layers positioned on the outermost surfaces on both sides with the intermediate layer interposed therebetween are layers made of a non-porous resin composition without pores before the porous step at the time of manufacture . The outer layers on both sides are made of a thermoplastic resin that is compatible with the polypropylene resin composition constituting the intermediate layer.
If the thermoplastic resin constituting the outer layer on both sides and the thermoplastic resin constituting the intermediate layer do not have compatibility, the subcritical or supercritical fluid is impregnated, and then a sudden pressure drop occurs. However, it is difficult to form a supersaturated state at the interface between the outer layers on both sides and the intermediate layer, and gas is released from the interface by diffusion / evaporation, which may make it impossible to form a hole communicating with the outer layer and the intermediate layer.

As the thermoplastic resin constituting the both outer layers, the density is used 0.92 g / cm ³ or more high-density polyethylene.

Wherein are we 0.92 g / cm ³ or more, the density of the high density polyethylene, in order to impart the required strength and rigidity that does not easily tear the thickness of the layer as thin of about 5 to 40 m. The density of polyethylene is more preferably 0.94 g / cm ³ or more, and the upper limit is not particularly limited, but a density of about 0.97 g / cm ³ is suitable.
The polyethylene has a melt flow rate of 10 g / 10 min or less, preferably 1 g / 10 min or less. If the melt flow rate is greater than 10 g / 10 min, the strength of the porous laminate may be reduced.

  As a method for polymerizing polyethylene, there are one-stage polymerization, two-stage polymerization, or more multistage polymerization, and any method of polyethylene can be used. The polymerization catalyst for polyethylene is not particularly limited, and any of a Ziegler type catalyst, a Philips type catalyst, a Kaminsky type catalyst or the like may be used.

For the outer side layers, the above-described polyethylene may be used alone, but a general thermoplastic resin may be mixed with polyethylene.
Specific examples of the thermoplastic resin that can be mixed with polyethylene include thermoplastic resins such as polyolefin resins other than polyethylene, fluorine resins, polystyrene, vinyl acetate resins, acrylic resins, polyamide resins, acetal resins, and polycarbonates. Preferably, polypropylene, polybutene, propylene ethylene block copolymer, propylene ethylene random copolymer and the like can be mentioned. The thermoplastic resin that can be mixed with polyethylene preferably has a melting point of 140 ° C. or higher.
Thus, when mixing other thermoplastic resin with polyethylene, the compounding quantity of the said other thermoplastic resin is 1-100 mass parts with respect to 100 mass parts of polyethylene, Preferably it is 1-50 mass parts. .

  Additives generally blended in the resin composition may be blended in the composition constituting the outer layers on both sides within a range that does not impair the purpose of the present invention and the characteristics of the outermost layer. As an additive, the same additive as the additive which can be mix | blended with an intermediate | middle layer can be illustrated. It is preferable that the compounding quantity of these additives is about 1-30 mass parts with respect to 100 mass parts of thermoplastic resins which comprise an outermost layer.

Moreover, the inorganic filler is mix | blended with the composition which comprises the said both-sides outer layer.
The outer side layers are preferably made porous by stretching, and in this case, an inorganic filler is blended in the resin, and the interface between the resin and the inorganic filler is peeled off to make it porous.

The pre-quinic filler, calcium carbonate, magnesium carbonate, carbonates such as barium carbonate; calcium sulfate, magnesium sulfate, sulfates such as barium sulfate; calcium oxide; sodium chloride, calcium chloride, chlorides such as magnesium chloride Examples thereof include oxides such as magnesium oxide, zinc oxide, titanium oxide and silica; silicates such as talc, clay and mica. Among these, barium sulfate is preferable.

  In order to improve the dispersibility in the resin, the inorganic filler may be hydrophobized by coating the surface of the inorganic filler with a surface treatment agent. Examples of the surface treatment agent include higher fatty acids such as stearic acid or lauric acid, or metal salts thereof.

  Delete

  The average particle size of the filler is about 0.01 to 25 μm, preferably 0.05 to 7 μm, and more preferably 0.1 to 5 μm. When the average particle size is less than 0.01 μm, the dispersibility is lowered due to aggregation of fillers, causing unevenness of stretching, and it is difficult to obtain a porous structure. On the other hand, if the average particle diameter exceeds 25 μm, it is possible to increase the surface irregularities, but at the same time, the possibility of generating large nonuniformities in the surface pore diameter increases, which is not preferable.

In Although the amount of the filler can not be said sweepingly because varies depending on the type of the filler is preferably 2 5 mass parts or more of the thermoplastic resin 100 parts by constituting the both outer layers, 5 0 mass part or more More preferably. When the blending amount of the filler is less than 25 parts by mass with respect to 100 parts by mass of the resin, the desired good air permeability is hardly expressed, and the appearance and texture are liable to deteriorate. In addition, when the compounding quantity of a filler exceeds 400 mass parts, it will become easy to raise | generate the malfunction on processes, such as resin baking, at the time of laminated body preparation, and the intensity | strength of a porous laminated body will also reduce significantly.
When the whole laminated body which added the intermediate | middle layer which does not contain an inorganic filler to the said both-sides outer layer is 100 mass parts, as mentioned above, content of an inorganic filler shall be 5-40 mass parts.

Furthermore, it is preferable to add a plasticizer to the both outer layers for the purpose of enhancing the dispersibility of the filler in the resin.
Examples of the plasticizer include ester compounds, amide compounds, alcohol compounds, amine salts, amine compounds (excluding amine salts), epoxy compounds, ether compounds, mineral oil, fats and oils, paraffin wax, liquid silicone, fluorine oil, and liquid polyether. , Liquid polybutenes, liquid polybutadienes, long chain fatty acids, carboxylates, carboxylic acid compounds (excluding carboxylates), sulfonates, sulfone compounds (excluding sulfonates), fluorine compounds, etc. Can be mentioned.
Specifically, plastic compounding agents (published by Taiseisha Co., Ltd., November 30, 1987, second edition) P31-P64, P83, P97-P100, P154-P158, P178-P182, P271-P275, P283-294 And the like. More specifically, the plasticizers (TCP, TOP, PS, ESBO, etc.) described in the items of plasticizers P29 to P64 and listed in Tables 4 to 49 and P6 to P54 are listed. It can be used. Further, the surfactant compounds listed in the new introduction to surfactants (published by Sanyo Kasei Kogyo Co., Ltd., August 1992, third edition) can also be suitably used as plasticizers.

Examples of the ester compound include tetraglycerin tristearate, glycerin tristearate, stearyl stearate, glycerin monostearate, sorbitan monostearate, ethylene carbonate, distearyl carbonate or dioctyl naphthalate.
Examples of the amide compound include ethylene bis stearamide and hexamethylene bis stearamide.
Examples of the alcohol compound include stearyl alcohol, oleyl alcohol, and dodecylphenol.
Examples of the amine salt include stearyl dimethyl betaine or lauryl trimethyl ammonium chloride.
Examples of the amine compound include dihydrodiethyl stearylamine and laurylamine.
Examples of the epoxy compound include epoxy soybean oil.
Examples of the ether compound include triethylene glycol.
Examples of the mineral oil include kerosene and naphthenic oil.
Examples of the oil include castor oil, hardened castor oil, and derivatives thereof.
Examples of the fatty acid include stearic acid and caproic acid.
Examples of the carboxylate include calcium stearate and sodium oleate.
Examples of the carboxylic acid compound include stearic acid, oleic acid, and derivatives thereof (excluding salts).
Examples of the sulfonate include sodium dodecylbenzenesulfonate.
The sulfone compound may be a compound having a sulfone bond (excluding a salt), and examples thereof include sulfolane and dipropylsulfonic acid.

Of the plasticizer, hardened castor oil is preferably blended.
Hardened castor oil is an ester of a fatty acid mixture containing 12-hydroxyoctadecanoic acid as a main component and hydrogenated at a double bond portion of ricinoleic acid to form a saturated fatty acid. These esters include monoesters, diesters and triesters, which may be used alone or as a mixture. Especially, what has triester as a main component is preferable.
Examples of fatty acids other than 12-hydroxyoctadecanoic acid contained in the fatty acid mixture include hexadecanoic acid or octadecanoic acid having about 12 to 22 carbon atoms. Such hydrogenated castor oil is industrially produced by hydrogenating castor oil, which is a non-drying oil.

  The blending amount of the plasticizer is preferably about 1 to 30 parts by mass, more preferably 1 to 15 parts by mass, with respect to 100 parts by mass of the thermoplastic resin constituting both outer layers. Is particularly preferred. When the blending amount of the plasticizer is less than 1 part by mass, the appearance and the texture are liable to deteriorate, and when the outermost layer is made porous by stretching, the desired good stretchability is hardly expressed. Moreover, when the compounding quantity of a plasticizer exceeds 30 mass parts, it will become easy to raise | generate the malfunction on processes, such as resin burning, at the time of laminated body preparation.

Product Sotai created in the first step at the time of manufacture, if at least three layers of both outer layers of the two non-hole located on the outermost surface of both sides of the intermediate layer and the intermediate layer described above, particularly the structure Is not limited.
For example, the intermediate layer may be composed of a plurality of layers having different compositions, or one or both of the outermost layers may be composed of a plurality of layers having different compositions. Further, a five-layer structure in which a non-porous layer having the same composition as the outermost layer is sandwiched between intermediate layers may be employed. In that case, two types of intermediate layers having different compositions may be laminated, and a layer that does not contain a filler continuously may be used.

Furthermore, the composition or structure of the outer layers on both sides may be the same or different. For example, when each of the two outer layers is in contact with a different substance, it is necessary to select a thermoplastic resin suitable for each characteristic. For example, when one layer is in contact with water and the other layer is in contact with an organic solvent, the thermoplastic resin constituting the outermost layer in contact with water is water-resistant polystyrene, and the outermost layer in contact with the organic solvent is The thermoplastic resin to be formed can be polypropylene having a high organic solvent resistance.
The same applies to the filler blended in the outer layers on both sides. For example, when both outer layers are in contact with neutral and acidic liquids, the outer layer in contact with the neutral liquid is blended with calcium carbonate and is in contact with the acidic liquid. Can contain barium sulfate.

In product Sotai of the present invention, the ratio tr total to the two outermost layers of the thickness to the thickness t of all layers (= to / t) is 0.05 to 0.95, preferably 0.10 to 0.90 More preferably, it is adjusted to be 0.15 to 0.80.
If tr is smaller than 0.05, the substantial thickness of the outermost layer becomes extremely thin, and as a result, the porous structure on the outermost surface tends to become extremely uneven. Also, if the thickness of the outermost layer is extremely thin, it does not serve as a lid. That is, when impregnating a supercritical or subcritical fluid during manufacturing and then deviating from the supercritical or subcritical state, the gas passes from the surface of the intermediate layer through the thin outermost layer and is released by diffusion and evaporation. Therefore, an area where foaming does not occur in the intermediate layer, that is, a so-called skin layer may occur, which is not preferable.
On the other hand, if tr is larger than 0.95, the intermediate layer becomes extremely thin and substantially does not differ greatly from the porous film containing filler in the entire layer, particularly the mass per unit area (basis weight). ) Will become large.

A known technique may be used as a method for producing a laminate composed of at least three layers of the outer side layers and the intermediate layer. For example, it can be created by the following method.
First, the components constituting each layer may be mixed and granulated once using a powder mixer such as a Henschel mixer or a kneader such as a uniaxial or biaxial kneader or a kneader.
The said laminated body is produced using the resin composition or granulated material which comprises a both-sides outer layer, and the resin composition or granulated material which comprises an intermediate | middle layer.
Examples of the method for producing the laminate include a thermal bonding method, an extrusion lamination method, a dry lamination method, and a coextrusion method. Among these, a co-extrusion method using a T-die molding method or an inflation molding method is particularly preferably used. This is because the method in which the intermediate layer and the outermost layer are separately formed and then fused with a hot roll or the like is difficult to adhere with uniform adhesive strength, and defects such as wrinkles are likely to occur. In particular, when the thickness of a film or the like is thin, since this tendency is remarkable, a coextrusion method is usually used.

In the porous laminate of the present invention , in the production process, the laminate obtained in the first step is impregnated with the fluid in the supercritical state or subcritical state in the second step, and then the supercritical state or subcritical state is added. The intermediate layer is made porous by releasing the liquid from the critical state and evaporating the fluid.

Gases that can be used as subcritical or supercritical fluids are not limited to the following, but include, for example, carbon dioxide, nitrogen, nitrous oxide, ethylene, ethane, tetrafluoroethylene, perfluoroethane, tetrafluoromethane, Trifluoromethane, 1,1-difluoroethylene, trifluoroamide oxide, cis-difluorodiazine, trans-difluorodiazine, nitrogen chloride difluoride, phosphorus deuteride, dinitrogen tetrafluoride, ozone, phosphine, nitrosyl Fluoride, nitrogen trifluoride, deuterium chloride, hydrogen chloride, xenon, sulfur hexafluoride, fluoromethane, perfluoroethane, tetrafluoroethane, pentafluoroethane, tetrafluoromethane, trifluoromethane, 1,1-difluoroethene , Ethin, diborane, water, tetra Le Oro hydrazine, silane, silicon tetrafluoride, four germanium hydride, boron trifluoride, carbonyl fluoride, chlorotrifluoromethane, bromotrifluoromethane and vinyl fluoride, and the like.
Among them, preferable gases include carbon dioxide, nitrogen, nitrous oxide, ethylene, ethane, tetrafluoroethylene, perfluoroethane, tetrafluoromethane, trifluoromethane, and 1,1-difluoroethylene.
Of these, carbon dioxide and nitrogen, which are inert gases, are particularly preferred in that they are non-flammable and non-toxic, are fairly inexpensive, and are non-reactive with most polymers.

The “supercritical state” refers to a state where the temperature (critical temperature) and pressure (critical pressure) at which gas and liquid can coexist are exceeded. “Subcritical state” means a state where the pressure or temperature is in the vicinity of the critical pressure or temperature.
Preferably, assuming that the critical temperature is Tc and the critical pressure is Pc, the temperature is 0.7 Tc or higher and / or the pressure is 0.7 Pc or higher (except when the temperature is Tc or higher and the pressure is Pc or higher. ). In particular, it is more preferable that either the pressure or the temperature exceeds the critical pressure or the critical temperature.

A fluid in a supercritical state or a subcritical state is a special fluid having properties different from those of ordinary gases and liquids, and has a very high impregnation property. Therefore, when the supercritical or subcritical fluid is brought into contact with the laminate obtained in the first step, the laminate is impregnated with the fluid.
A specific method for impregnating the laminate with a fluid in a supercritical state or a subcritical state may be a known method.
For example, the laminate is placed in a pressure-resistant container such as an autoclave, and a gaseous or liquid substance to be impregnated into the laminate is made into a fluid as exemplified above. Next, the temperature or / and pressure in the pressure vessel is increased to create a supercritical state or a subcritical state. That is, the temperature in the pressure vessel is raised to 0.7 Tc or higher, preferably the critical temperature or higher, or the pressure in the pressure vessel is raised to 0.7 Pc or higher, preferably higher than the critical pressure. In particular, it is more preferable to raise the temperature in the pressure vessel to a critical temperature or higher and raise the pressure to a critical pressure or higher.

Specifically, for example, when carbon dioxide is used, the critical temperature of carbon dioxide is 31.1 ° C. and the critical pressure is 7.38 MPa.
When nitrogen is used, since the critical temperature of nitrogen is −147 ° C. and the critical pressure is 3.40 MPa, it is preferable that the pressure is 3 MPa or more while keeping the temperature at room temperature.
When nitrous oxide is used, since the critical temperature of nitrous oxide is 36.4 ° C. and the critical pressure is 7.24 MPa, it is preferable that the pressure is 7 MPa or more with the temperature kept at room temperature.
When ethylene is used, since the critical temperature of ethylene is 9.2 ° C. and the critical pressure is 5.04 MPa, the temperature is preferably 10 ° C. or higher and the pressure is preferably 5 MPa or higher.
When ethane is used, since the critical temperature of ethane is 32 ° C. and the critical pressure is 4.88 MPa, it is preferable that the pressure is 4.5 MPa or more with the temperature kept at room temperature.

  The time for impregnating the fluid in the supercritical state or subcritical state varies depending on the composition of the resin constituting the intermediate layer, the target air permeability, porosity, etc. It is preferable. This is because if the time is less than 1 minute, the intermediate layer cannot be sufficiently impregnated with the fluid. The upper limit value is 10 hours or less, preferably 5 hours or less, more preferably 2 hours or less from the viewpoint of production efficiency.

Next, the intermediate layer is made porous by releasing (deviating) from the supercritical state or subcritical state to vaporize the fluid.
At this time, the temperature or pressure may be rapidly returned to normal temperature or normal pressure, or may be gradually decreased. Alternatively, the temperature may be lowered to a temperature below normal temperature or a pressure below normal pressure and then returned to normal temperature or normal pressure.
In the second step, it is not limited to strictly making only the intermediate layer porous. In the layer in contact with the intermediate layer, the surface is in contact with the intermediate layer and the vicinity thereof is porous. There is no problem at all.

In the porous laminate of the present invention, in the manufacturing method, and porous the non-porous layer of the two located on both outer layers of the laminate having an intermediate layer porosified in the third step.
The method for making the nonporous layer porous is not particularly limited, and for example, a known method such as a stretching method, a phase separation method, an extraction method, a chemical treatment method, a radiation etching method, a foaming method, or a combination of these techniques is used. Among them, the stretching method is preferable among them.

The stretching method is a method of forming pores by a stretching process. In particular,
(A) A method in which an outermost layer is formed using a composition in which a filler is mixed in a resin, and the interface between the resin and the filler is peeled off by stretching to form micropores;
(B) Using a resin having a crystallized structure such as polyethylene, polypropylene, polytetrafluoroethylene, etc. as the resin constituting the outermost layer, and extending the crystal and amorphous interface by stretching to form micropores. In general, the method (a) is preferred.

The stretching treatment for making the outer layers on both sides having the filler (a) porous may be either uniaxial stretching or biaxial stretching, but biaxial stretching is preferred from the viewpoint of isotropic property. Biaxial stretching may be simultaneous biaxial stretching or sequential biaxial stretching in which the film is stretched in the longitudinal direction (longitudinal direction) and then in the transverse direction. As a stretching method, a method using a general apparatus such as a roll stretching machine or a tenter stretching machine may be used. As a draw ratio, it is at least 2 times by area magnification, Preferably it is 4-25 times, More preferably, it is 9-16 times.
The stretching temperature is not particularly limited, but stretching is preferably performed at a temperature lower than the melting point of the thermoplastic resin constituting the outer layers on both sides, preferably 30 ° C. or less from the melting point. If the stretching temperature is too close to the melting point, it will be difficult to express the connectivity at the outermost layer.
Further, if necessary, measures such as heat shrinkage and dimensional stability may be taken by performing heat fixation near the melting point or relaxation after stretching.

Furthermore, if necessary, the porous laminate obtained as described above may be subjected to heat treatment in order to impart thermal dimensional stability.
The heat treatment can be performed by any known method such as contact heating with a heating roll or heating in air in an oven. Moreover, it is also possible to divert the above-mentioned extending | stretching apparatus. The heat treatment temperature can be any temperature below the melting point of the thermoplastic resin constituting the intermediate layer and the outermost layer, but is preferably 100 ° C. or higher and lower than the melting point of the resin, more preferably 110 ° C. or higher and 130 ° C. or lower. It is said.

  The phase separation method is a technique called a conversion method or a microphase separation method, and forms pores based on a phase separation phenomenon of a polymer solution. Specifically, it is roughly classified into (a) a method of forming pores by phase separation of polymer, and (b) a method of forming pores while forming pores during polymerization. As the former method, there are a solvent gelation method using a solvent and a hot melt rapid solidification method, and either method may be used. In the latter method, phase separation is performed by increasing the polymer concentration in the polymerization process from monomer to polymer. In the present invention, however, the outermost layer must be nonporous in the second step of making the intermediate layer porous. The method is not usually used.

In the extraction method, an additive that can be removed in a subsequent step is mixed with the composition constituting the outermost layer, and in the third step, the additive is extracted with a chemical or the like to form pores. Examples of the additive include a polymer additive, an organic additive, and an inorganic additive.
As an example using a polymer additive, the outermost layer is formed using two types of polymers having different solubility in an organic solvent, and the laminate obtained through the first and second steps is used as the two types of polymers. The method of extracting the said one polymer by immersing in the organic solvent in which only one polymer melt | dissolves among these is mentioned. More specifically, a method of forming an outermost layer composed of polyvinyl alcohol and polyvinyl acetate, and extracting polyvinyl acetate with acetone and n-hexane, adding a hydrophilic polymer to the block or graft copolymer. Examples include a method of forming the outermost layer and removing the hydrophilic polymer with water.

As an example using an organic additive, a laminate obtained by going through the first and second steps is formed by blending a soluble material in an organic solvent in which the polymer constituting the both outer layers is insoluble, and forming both outer layers. A method of extracting and removing the substance by immersing in the organic solvent can be mentioned.
Examples of the substance include higher aliphatic alcohols such as stearyl alcohol or seryl alcohol, n-alkanes such as n-decane or n-dodecane, paraffin wax, liquid paraffin, or kerosene. These include isopropanol, ethanol, It can be extracted with an organic solvent such as hexane. Alternatively, examples of the substance include water-soluble substances such as sucrose and sugar. Since these substances can be extracted with water, there is an advantage that the burden on the environment is small.

  The chemical treatment method is a method of forming pores by chemically cleaving a part of the polymer substrate or conversely performing a binding reaction. More specifically, a method of forming pores by chemical treatment such as oxidation-reduction agent treatment, alkali treatment, acid treatment and the like can be mentioned.

  The irradiation etching method is a method of forming minute holes by irradiating with neutron beam or laser. When using this method, the outermost layer is preferably composed of polycarbonate, polyester or the like.

The fusion method is a method of using a polymer fine powder such as polytetrafluoroethylene, polyethylene, or polypropylene and sintering the polymer fine powder after molding.
Examples of the foaming method include a mechanical foaming method, a physical foaming method, and a chemical foaming method, and any of them can be used in the present invention.

  Delete

As described above, the porous laminate of the present invention has an air permeability, which is an index of communication, in the range of 1 to 10,000 seconds / 100 ml. This means that if the air permeability is greater than 10,000 seconds / 100 ml, the numerical value of the air permeability will be obtained in the measurement, but it means that the structure is quite poorly connected. It may be equal to not.
It is preferably 1 to 5,000 seconds / 100 ml, more preferably 50 to 5,000 seconds / 100 ml, and particularly preferably 00 to 5,000 seconds / 100 ml.
The air permeability is measured in accordance with JIS P 8117.

  Moreover, when a polypropylene resin composition is used for an intermediate | middle layer, heat resistance higher than the porous film which consists only of the conventional polyethylene resin can be exhibited. That is, the shape can be maintained even when exposed to high temperatures. As a heat resistance index, the thermal shrinkage rate is preferably 20% or less, more preferably 15% or less, and particularly preferably 10% or less.

In the porous laminate of the present invention, the porosity is also an important factor for limiting the porous structure. Although the measuring method of a porosity is mentioned later, it is preferable to make the porosity of the porous laminated body of this invention into the range of 5 to 80%. If the porosity is less than 5%, it is difficult to substantially obtain communication. Moreover, if the porosity is higher than 80%, handling becomes difficult from the viewpoint of strength, which is not preferable.
The porosity is more preferably 20 to 70%, and particularly preferably 40 to 60%.

Since the range required for the air permeability and the porosity differs depending on the application, the air permeability and the porosity are appropriately adjusted according to the application.
For example, when used for sanitary products such as diapers and sanitary products, the air permeability is preferably 1 to 2,000 seconds / 100 ml.
When used as a battery separator, the air permeability is preferably 1 to 500 seconds / 100 ml.

The air permeability and porosity are, for example, the content of the soft segment in the polypropylene resin composition constituting the intermediate layer, the time for impregnating the fluid in the supercritical state or subcritical state, the fluid in the supercritical state or subcritical state It can be controlled by adjusting the temperature or pressure at the time of impregnation.
If the content of the soft segment in the thermoplastic resin constituting the intermediate layer is increased, the fluid in the supercritical state or the subcritical state is easily impregnated, so that the air permeability and the porosity are increased. Even if the time for impregnating the fluid in the supercritical state or subcritical state is lengthened, or the temperature or pressure at the time of impregnating the fluid in the supercritical state or subcritical state is increased, the air permeability and air The porosity can be increased.

About the porous laminated body of this invention, thickness or a shape is not specifically limited. For example, the porous laminate of the present invention may be any of a film shape having an average thickness of 1 μm or more and less than 250 μm, a sheet shape having a thickness of 250 μm or more and less than several mm, and a molded product having a thickness of several mm or more, It can select suitably according to a use.
Especially, it is preferable that the porous laminated body of this invention exhibits a film form. That is, the average thickness of the porous laminate is 1 to 250 μm, preferably 10 to 200 μm, and more preferably 50 to 150 μm.
Note that the average thickness is a value obtained by measuring five in-plane positions in an unspecified manner with a 1/1000 mm dial gauge and calculating the average.

Porous laminate of the present invention is the surface the uneven surface, it is preferred maximum from the surface height (Rmax) value is 2μm or more. This is because if the maximum height value of the surface is 2 μm or more, there are moderate irregularities on the surface of the porous laminate, and the slipperiness of the porous laminate is enhanced. Preferably, the maximum height (Rmax) value of the surface is 3 μm or more, preferably 5 μm or more, and the upper limit is not particularly limited, but is usually 7 μm or less.
The maximum height of the surface is measured according to the method described in JIS B 0601.

Moreover, the porous laminate of the present invention preferably has a mass per unit area (referred to as a weight) of 10 to 30 g / m ² when converted to a thickness per 25 μm, and preferably 10 to 25 g / m ^2. Is more preferable. By reducing the weight, it is possible to reduce the weight of the device on which the porous laminate of the present invention is mounted.
In order to show the weight, the ratio of the mass of the filler to the total mass of the porous laminate of the present invention, that is, the filler content is 5 to 40 parts by mass, more preferably 5 to 30 parts by mass as described above. It is.

  The porous laminate of the present invention having the above characteristics can be applied to various uses that require air permeability. Battery separators; Sanitary materials such as disposable paper diapers and sanitary items such as pads or bed sheets for absorbing body fluids; Medical materials such as surgical clothing or base materials for warm compresses; Materials for clothing such as jumpers, sportswear or rainwear ; Building materials such as wallpaper, roof waterproofing material, heat insulating material, sound absorbing material; desiccant; moisture-proofing agent; oxygen scavenger; disposable body warmer; can be used very suitably as a material for packaging materials such as freshness preservation packaging or food packaging .

Especially, the porous laminated body of this invention is used suitably as a separator for nonaqueous electrolyte batteries, such as a lithium ion secondary battery utilized as power supplies, such as various electronic devices.
When used as the battery separator, the air permeability is preferably 50 to 500 seconds / 100 ml, more preferably 100 to 300 seconds / 100 ml. When the air permeability is less than 50 seconds / 100 ml, there is a possibility that the electrolyte retention will be reduced, the capacity of the secondary battery will be lowered, and the cycle performance will be reduced. On the other hand, if the air permeability exceeds 500 seconds / 100 ml, the ion conductivity becomes low and sufficient battery characteristics cannot be obtained.
When the porous laminate of the present invention is used as a battery separator, the porosity is preferably 30 to 70%, and more preferably 35 to 65%. If the porosity is less than 30%, the ion permeability is low and it is difficult to obtain sufficient battery performance. Further, if the porosity exceeds 70%, it is not preferable from the viewpoint of battery safety.

As a battery separator, a porous film composed mainly of a polyethylene resin is used because of the necessity of shutdown characteristics. However, by using a polypropylene resin composition for the intermediate layer, the dimensional stability after shutdown is improved and the battery is not suitable. It can be made difficult to fall into a stable state.
The heat resistance can be evaluated by the heat shrinkage rate. The heat shrinkage rate is preferably 0 to 25%, more preferably 0 to 10%. If the thermal shrinkage rate is greater than 25%, there is a concern that the positive electrode and the negative electrode come into contact with each other at the end of the porous laminate, causing a short circuit.

Porous laminate of the present invention can ensure the communication of the thickness direction to eliminate the skin layer on the front surface.
If for porosity of the intermediate layer Ru using subcritical or supercritical fluid, since no or using an organic solvent in large quantities, it is possible to reduce the load on the environment. In particular, if a non-toxic inert gas such as carbon dioxide or nitrogen is used as a subcritical or supercritical fluid, the burden on the environment can be further reduced. Furthermore, the porous laminate of the present invention has a wide range of manufacturing conditions and has the advantage of easy process management.

Further, in the method of making porous by removing the plasticizer and the solvent, the plasticizer and solvent may remain without being removed, but in the present invention, when the intermediate layer is made porous, it is subcritical or supercritical. Since the critical fluid is used, the above-mentioned remaining problem does not occur at least in the intermediate layer, and as a whole, a porous laminate having fewer impurities is obtained .
In particular, it is suitably used as a separator for a non-aqueous electrolyte battery such as a lithium ion secondary battery used as a power source for various electronic devices.

It is a schematic sectional drawing of the porous laminated body of 1st embodiment. It is a schematic sectional drawing of the porous laminated body of 2nd embodiment. It is a schematic sectional drawing of the porous laminated body of 3rd embodiment. It is a partially broken perspective view of the non-aqueous electrolyte battery which accommodates the porous laminated body of this invention as a non-aqueous electrolyte battery separator.

Hereinafter, embodiments of the present invention will be described.
First, FIG. 1 to FIG. 3 show first to third embodiments of a porous laminate of the present invention made of a film-like resin manufactured by a manufacturing method described later. The porous laminates of the first to third embodiments are composed of porous laminates 1 (1-1, 1-2, 1-3) with different numbers of layers, all of which are the same manufacturing method described later. Manufactured.

The porous laminate 1 of the first embodiment shown in FIG. 1 has a three-layer structure, in which an intermediate layer 2 and a pair of both outer layers 3 and 4 positioned on the outer surfaces on both sides are laminated and integrated in the thickness direction. Intermediate layer 2 and both outer layers 3, 4 respectively micropores 2a in, there are many 3a, the 4a, these micropores 2a, 3a, 4a is communicated with the Direction thickness. The outer side layers 3 and 4 are made of the same resin composition, and the intermediate layer 2 is made of a resin different from the outer side layers 3 and 4.
The resin compositions of the outer side layers 3 and 4 may be different.

  The porous laminated body of the second embodiment shown in FIG. 2 has a four-layer structure 1 and two intermediate layers 2 (2A, 2B), and both outer layers 3, 4 on both outer surfaces of the two intermediate layers 2. In the same manner as in the first embodiment, the micro holes 2a to 4a are communicated with each of these layers in the thickness direction.

  The porous laminate 1 of the third embodiment shown in FIG. 3 has a five-layer structure, and includes a central intermediate layer 5 made of the same composition as the outer layers 3 and 4 on both sides between two intermediate layers 2 (2A and 2B). In addition, both exteriors 3 and 4 are provided outside the intermediate layers 2A and 2B, and the micro holes 2a to 5a are communicated with each of the layers in the thickness direction as in the first embodiment.

In the porous laminates 1 of the first to third embodiments, the outer layers 3 and 4 on both sides and the central intermediate layer 5 of the third embodiment are made of a thermoplastic resin containing a filler 7, and the intermediate layer 2 is a filler. It consists of the polypropylene resin composition which has a hard segment and soft segment which do not contain.

Below, the manufacturing method of the porous laminated body 1 of 1st Embodiment of 3 layer structure is demonstrated.
As described above, the method for manufacturing the porous laminate of the second and third embodiments includes the following steps similar to those of the first embodiment.

The method for producing the porous laminate 1 is as follows:
Between both outer layers 3, 4 of the imperforate consisting tree fat composition combined distribution of filler, and a first step of preparing a laminate by placing an intermediate layer 2 made of a polypropylene resin composition,
A second step in which the laminate obtained in the step is impregnated with a fluid in a supercritical state or a subcritical state, and then released from the state to vaporize the fluid to make the intermediate layer porous;
After making the intermediate layer porous, the laminated body is stretched at least in a uniaxial direction to peel the interface between the fillers of the both-side outer layers 3 and 4 and the thermoplastic resin, thereby making the non-porous both-side outer layers 3 and 4 porous. It consists of a 3rd process.

In the present embodiment, a resin composition in which ethylene homopropylene rubber is blended with a polypropylene homopolymer is used as the polypropylene resin composition constituting the intermediate layer 2. The ethylene-propylene rubber content is preferably 5 to 95% by mass, more preferably 15 to 75% by mass, and further preferably 30 to 60% by mass.
As the ethylene-propylene rubber, an ethylene-propylene rubber having an ethylene content of 30 to 55% by mass based on the whole rubber is particularly preferable.
By adjusting the ethylene-propylene rubber content and the ethylene content in the ethylene-propylene rubber, the ethylene content with respect to the entire polypropylene resin composition constituting the intermediate layer is preferably 5 to 70% by mass. It is more preferably ˜50 mass%, and particularly preferably 10 to 30 mass%.

Said as a resin composing both outer layers 3 and 4, density of 0.94 g / cm ³ or more, preferably uses a high-density polyethylene 0.95~0.97g / cm ^3, and a melt The flow rate is preferably 1 g / 10 min or less.

In the present embodiment, an inorganic filler is used as the filler 7 that pays out to the outer layers 3 and 4 on both sides. The inorganic filler may be barium sulfate, calcium carbonate, titanium oxide, or a combination of two or more of these, but barium sulfate is particularly preferred. Furthermore, it is preferable that the average particle diameter of the filler 7 is 0.1-5 micrometers, and it is more preferable that it is 0.1-3 micrometers.
The content of the filler is set to 5 to 40 parts by mass with the entire porous laminate 1 being 100 parts by mass .

Further, for the purpose of improving the dispersibility of the fillers on both side outer layers 3 and 4, a plasticizer selected from the ester compound, amide compound, alcohol compound and the like described above is used as the thermoplastic resin 100 constituting both side outer layers 3 and 4. It is paired to blend 1 to 30 parts by weight parts by weight.
In addition, although the combination of a thermoplastic resin and a filler may be the same on both the outer layers 3 and 4, it does not necessarily need to be the same.

The following method is used as a method of producing a laminate composed of the intermediate layer 2 and the three outer side layers 3 and 4 disposed so as to sandwich the intermediate layer 2 therebetween.
First, for both outer layers 3 and 4, a thermoplastic resin, a filler, and a plasticizer are mixed with a powder mixer such as a Henschel mixer, and heated and kneaded with a uniaxial or biaxial kneader or kneader to form pellets. Yes. In view of the dispersion state of the filler, it is more preferable to use a biaxial kneader.
The moisture content of the pellets is controlled to 1000 ppm or less, preferably 700 ppm or less. This is because if the moisture content of the pellet is larger than 1000 ppm, gel and pinball are extremely generated, which is not preferable.
A film in which the pellets for both outer layers prepared as described above and the polypropylene resin composition for the intermediate layer are co-extruded and laminated into three layers is extruded.
More specifically, lamination is performed under a temperature condition of 150 to 250 ° C, preferably 190 to 220 ° C, using an inflation die or T die for multilayer molding.

The laminate obtained in the first step is placed in a pressure vessel, and carbon dioxide gas or nitrogen gas is sealed in the pressure vessel. The pressure in the pressure vessel is increased, and carbon dioxide gas or nitrogen gas is brought into a supercritical state or a subcritical state.
More specifically, when carbon dioxide gas is used, the pressure is increased to 7 MPa or more, preferably 20 MPa or more. When using nitrogen gas 3MPa more pressure is preferably that has achieved more than 15 MPa.
The temperature in the pressure vessel may be room temperature, but can be heated.

By maintaining the pressure and temperature in the pressure vessel, the laminate is impregnated with carbon dioxide gas or nitrogen gas in a supercritical state or a subcritical state. The impregnation time is 10 minutes to 2 hours, preferably 30 minutes to 2 hours.
Thereafter, the impregnated carbon dioxide gas or nitrogen gas is vaporized by returning the pressure or temperature in the pressure vessel to normal pressure or normal temperature, and micropores 2a are formed in the intermediate layer 2 to be porous. The pressure or temperature in the pressure vessel may be gradually decreased, or may be returned to normal pressure or room temperature at once.
In the second step, the intermediate layer 2 is made porous, but the impregnated gas is released from the outer surface in the outer side layers 3 and 4 so that no pores are formed and no pores are left. Accordingly, the non-porous outer layers 3 and 4 serve as “lids” that do not release the gas to the intermediate layer 2.

Thus, the intermediate layer 2 is made porous in the second step, while the laminated body in which the outer side layers 3 and 4 are left non-porous is stretched in the third step. In the stretching process, peeling occurs at the interface between the filler 7 dispersed in the both-side outer layers 3 and 4 and the resin, and micropores 3 a and 4 a are formed in the both-side outer layers 3 and 4. The micro holes 3a and 4a are communicated with the micro holes 2a opened on both side surfaces of the intermediate layer 2.
The stretching method in the third step is preferably sequential biaxial stretching in which the film is stretched in the longitudinal direction (longitudinal direction) and then in the transverse direction. The draw ratio is 4 to 25 times, preferably 9 to 16 times in terms of area magnification. The stretching temperature is preferably 40 to 80 ° C.

  Furthermore, after the third step, heat treatment may be performed as needed to impart thermal dimensional stability to the porous laminate. The heat treatment can be performed by any known method such as contact heating with a heating roll or heating in the air in an oven. The heat treatment temperature can be any temperature lower than the melting point of the thermoplastic resin constituting the intermediate layer 2 and both outer layers 3 and 4, preferably 100 ° C. or higher and lower than the melting point of the resin, more preferably 110 ° C. or higher. It is 130 degrees C or less.

In the porous laminate 1-2 of the second embodiment, the micro holes 2a communicated in the second step can be formed in the two intermediate layers 2A and 2B, and the micro layers formed in the both outer layers 3 and 4 in the third step thereafter. It communicates with the holes 3a, 4a.
In the porous laminate 1-3 of the third embodiment, the micropores 2a can be formed in the two intermediate layers 2A and 2B in the second step, respectively, and in the subsequent third step, the central intermediate layer 5 and the outer side layers 3 and 4 on both sides are formed. Are formed with holes 5a, 3a, 4a, which communicate with the holes 2a of the intermediate layer 2.

The porous laminate 1 produced as described above has an air permeability as an index of communication of 50 to 5,000 seconds / 100 ml, preferably 100 to 5,000 seconds / 100 ml. The porosity is 30 to 70%, preferably 40 to 60%.
Moreover, since both outer layers 3 and 4 filler of polypropylene resin intermediate layer 2 with consists trees fat composition formulated high density polyethylene, exhibits a high heat resistance than the porous film comprising only conventional polyethylene resin can do. That is, the shape can be maintained even when exposed to high temperatures. As an index of heat resistance, the heat shrinkage rate is 20% or less, preferably 15% or less. The heat shrinkage rate can be measured by the method described in the examples.

The porous laminate 1 has a film shape and has an average thickness of 1 to 250 μm, preferably 10 to 200 μm, more preferably 50 to 150 μm, and is prepared according to the use of the porous laminate. This average thickness is a value obtained by measuring five locations in a plane unspecified with a 1/1000 mm dial gauge and calculating the average.
Furthermore, since the porous laminate 1 is blended with the outer layers 3 and 4 on both sides, it is not a smooth surface but a rough surface with minute irregularities and has improved slipperiness. That is, the maximum height (Rmax) value from the surface is 2 μm or more, preferably 5 μm or more.

Furthermore, the porous laminated body 1 does not contain a filler in the intermediate layer 2, so that the mass per unit area (referred to as the weighing) when converted to a thickness per 25 μm is 10 to 30 g / m ² , preferably 10 The weight of the porous laminate 1 is reduced to 25 g / m ² . In particular, in order to reduce the weight, the filler content relative to the total mass of the porous laminate 1 is 5 to 40 mass%, preferably 5 to 30 mass%.

The porous laminate 1 described above can be used for various applications that require air permeability, and among them, it is preferably used as a battery separator.
When the porous laminate 1 of the present invention is used as a battery separator, the air permeability is 50 to 500 seconds / 100 ml. This is because when the air permeability is less than 50 seconds / 100 ml, the electrolyte solution retainability is lowered and the capacity of the secondary battery is lowered or the cycle performance is lowered. On the other hand, if the air permeability exceeds 500 seconds / 100 ml, the ion conductivity is lowered and sufficient battery characteristics cannot be obtained. Preferably, it is 100 to 300 seconds / 100 ml.
Moreover, the porosity is set to 30 to 70%. This is because if the porosity is less than 30%, the ion permeability is low and it is difficult to obtain sufficient battery performance, whereas if the porosity exceeds 70%, it is not preferable from the viewpoint of battery safety. More preferably, it is 35 to 65%.

As a battery separator, a porous film mainly composed of a polyethylene resin is used because of the necessity of shutdown characteristics, but the porous laminate 1 of the present invention has dimensions after shutdown by using a polypropylene resin composition for the intermediate layer 2. Stability can be improved and it can be made hard to fall into the unstable state as a battery.
The heat resistance can be evaluated by the heat shrinkage rate, and the heat shrinkage rate is 0 to 25%, preferably 0 to 10%. This is because if the heat shrinkage rate is greater than 25%, the positive electrode and the negative electrode may come into contact with each other at the end of the porous laminate, causing a short circuit.

Next, a nonaqueous electrolyte battery containing the porous laminate of the present invention as a battery separator will be described with reference to FIG.
Both electrodes of the positive electrode plate 21 and the negative electrode plate 22 are wound in a spiral shape so as to overlap each other via the separator 10, and the outside is stopped with a winding tape to form a wound body. When winding in this spiral shape, the separator 10 preferably has a thickness of 5 to 40 μm, and more preferably 5 to 30 μm. This is because when the thickness is less than 5 μm, the separator is easily broken, and when it exceeds 40 μm, the battery area is reduced and the battery capacity is reduced when wound in a predetermined battery can as a battery separator.

  A wound body in which the positive electrode plate 21, the separator 10 and the negative electrode plate 22 are integrally wound is housed in a bottomed cylindrical battery case and welded to the positive and negative electrode lead bodies 24 and 25. Next, the electrolyte is injected into the battery can, and after the electrolyte has sufficiently penetrated into the separator 10 or the like, the positive electrode lid 27 is sealed to the periphery of the opening of the battery can via the gasket 26, and precharging and aging are performed. Type non-aqueous electrolyte battery.

As the electrolytic solution, an electrolytic solution in which a lithium salt is used as an electrolytic solution and is dissolved in an organic solvent is used. The organic solvent is not particularly limited. For example, propylene carbonate, ethylene carbonate, butylene carbonate, γ-butyrolactone, γ-valerolactone, esters such as dimethyl carbonate, methyl propionate or butyl acetate, and nitriles such as acetonitrile. 1,2-dimethoxyethane, 1,2-dimethoxymethane, dimethoxypropane, 1,3-dioxolane, ethers such as tetrahydrofuran, 2-methyltetrahydrofuran or 4-methyl-1,3-dioxolane, or sulfolane These may be used alone or in combination of two or more.
Among them, an electrolyte obtained by dissolving lithium hexafluorophosphate (LiPF ₆₎ at a rate of 1.4 mol / L in a solvent obtained by mixing 2 parts by mass of methyl ethyl carbonate relative to ethylene carbonate 1 part by weight is preferred.

As the negative electrode, an alkali metal or a compound containing an alkali metal integrated with a current collecting material such as a stainless steel net is used. Examples of the alkali metal include lithium, sodium, and potassium. Examples of the compound containing an alkali metal include an alloy of an alkali metal and aluminum, lead, indium, potassium, cadmium, tin or magnesium, a compound of an alkali metal and a carbon material, a low potential alkali metal and a metal oxide, and the like. Or a compound with a sulfide or the like.
In the case of using a carbon material for the negative electrode, the carbon material may be any material that can be doped and dedoped with lithium ions. Mesocarbon microbeads, carbon fibers, activated carbon and the like can be used.

  In this embodiment, as a negative electrode, a carbon material having an average particle size of 10 μm is mixed with a solution in which vinylidene fluoride is dissolved in N-methylpyrrolidone to form a slurry, and this negative electrode mixture slurry is passed through a 70-mesh net. After removing the large particles, uniformly apply to both sides of a negative electrode current collector made of a strip-shaped copper foil having a thickness of 18 μm and dry, and then compression-molded with a roll press machine, cut, and strip-shaped negative electrode plate What is used.

  As the positive electrode, lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, manganese dioxide, metal oxide such as vanadium pentoxide or chromium oxide, metal sulfide such as molybdenum disulfide, etc. are used as active materials. , These positive electrode active materials are combined with conductive additives and binders such as polytetrafluoroethylene as appropriate, and finished with a current collector material such as a stainless steel mesh as a core material. It is done.

In the present embodiment, a strip-like positive electrode plate produced as follows is used as the positive electrode. In other words, lithium graphite oxide (LiCoO ₂ ) was added with phosphorous graphite as a conductive additive at a mass ratio of 90: 5 and mixed, and this mixture was mixed with a solution in which polyvinylidene fluoride was dissolved in N-methylpyrrolidone. To make a slurry. The positive electrode mixture slurry is passed through a 70 mesh net to remove large particles, and then uniformly applied to both sides of a positive electrode current collector made of an aluminum foil having a thickness of 20 μm and dried. After compression molding, it is cut into a strip-like positive electrode plate.

  Hereinafter, examples of the porous laminate will be described.

Example 1
As a preparation of the resin composition constituting the outer layers on both sides, 100 parts by mass of high density polyethylene and 100 parts by mass of barium sulfate were blended and compounded. Next, the compound is used as both outermost layers, and a thermoplastic resin composition containing polypropylene and ethylene propylene rubber is used as the intermediate layer polypropylene resin composition, and the layer ratio is outer layer 1 / intermediate layer / outer layer 2 = 25 / While adjusting to 50/25, molding was performed at a temperature of 200 ° C. using a T-die for multilayer molding to obtain a laminate of two types and three layers.
The obtained laminate was charged into a pressure vessel, and carbon dioxide as an inert gas was sealed in the pressure vessel at room temperature. Subsequently, the pressure was increased to 24 MPa to bring carbon dioxide into a subcritical state or a supercritical state. This state was maintained for 1 hour, and the laminate was impregnated with carbon dioxide in the subcritical state or the supercritical state. Thereafter, the pressure vessel valve was fully opened to release the pressure in the vessel.
The resulting laminate is stretched at a stretching temperature of 70 ° C. with a stretcher at a stretching ratio of 2 times in the longitudinal direction (longitudinal direction) and 2 times in the transverse direction, and then heat set at 125 ° C. The porous laminate of Example 1 was obtained.

(Examples 2 to 5)
Except having changed the resin composition which comprises a both-sides outer layer, and extending | stretching conditions as shown in Table 1, it carried out similarly to Example 1, and obtained the porous laminated body of Examples 2-5.

The detail of the component described in the table | surface is shown below.
“7000FP”; high density polyethylene (“HI-ZEX7000FP” manufactured by Prime Polymer Co., Ltd., density: 0.954 g / cm ³ , melt flow rate: 0.04 g / 10 min)
“HY430P”; high density polyethylene (“Novatech HY430P” manufactured by Nippon Polyethylene Co., Ltd., density: 0.955 g / cm ³ , melt flow rate: 0.8 g / 10 min)
“B55”; barium sulfate (“B-55” manufactured by Sakai Chemical Co., Ltd., average particle size 0.66 μm)
“30NC”; barium sulfate (“30NC” manufactured by Sakai Chemical Co., Ltd., average particle size: 0.3 μm)
“B54”; barium sulfate (“B-54” manufactured by Sakai Chemical Co., Ltd., average particle size 1.2 μm)
“HCOP”; hydrogenated castor oil (“HCOP” manufactured by Toyokuni Oil Co., Ltd., density 0.88 g / cm ³ )
“Zelas 5013”; thermoplastic elastomer containing ethylene propylene rubber in polypropylene (“Zelas 5013” manufactured by Mitsubishi Chemical Corporation, density 0.88 g / cm ³ , melt flow rate 0.8 g / 10 min)

(Comparative Example 1)
In Comparative Example 1, a porous film was prepared by the method described in Example 1 of JP-A-5-25305 of Patent Document 1.
That is, 20% by mass of ultra high molecular weight polyethylene (UHMWPE) having a weight average molecular weight of 2.0 × 10 6, 66.7% by mass of high density polyethylene (HDPE) having a weight average molecular weight of 3.9 × 105, and a melt index ( 15 parts by mass of a raw material resin mixed with 13.3% by mass of low density polyethylene (LDPE) of 2.0 g / 10 min at 190 ° C. and 2.16 kg load) and 85 parts by mass of liquid paraffin (64 cst / 40 ° C.) By mixing, a solution of the polyethylene composition was prepared. Next, 100 parts by mass of this polyethylene composition solution was added 0.125 parts by mass of 2,5-di-t-butyl-p-cresol (“BHT”, manufactured by Sumitomo Chemical Co., Ltd.) and tetrakis [methylene -3- (3,5-di-t-butyl-4-hydroxylphenyl) -propionate] methane ("Irganox 1010", Ciba Geigy) 0.25 part by mass was added as an antioxidant. This mixed solution was filled in an autoclave equipped with a stirrer and stirred at 200 ° C. for 90 minutes to obtain a uniform solution.
This solution was extruded from a T die by an extruder having a diameter of 45 mm, and a gel-like sheet was formed while being taken up by a cooling roll.
The obtained sheet was set in a biaxial stretching machine, and simultaneous biaxial stretching was performed 5 × 5 times at a temperature of 115 ° C. and a stretching speed of 0.5 m / min. The obtained stretched membrane was washed with methylene chloride to extract and remove the remaining liquid paraffin, and then heat-set at 100 ° C. for 30 seconds to obtain a polyethylene microporous membrane.

(Comparative Example 2)
In Comparative Example 2, a porous film was prepared by the method described in Example 1 of JP-A-2004-95550 of Patent Document 3.
High density polyethylene (“HI-ZEX7000FP” manufactured by Prime Polymer Co., Ltd., density: 0.956 g / cm ³ , melt flow rate: 0.04 g / 10 min) 100 parts by mass, soft polypropylene (“PER R110E manufactured by Idemitsu Petrochemical Co., Ltd.) 15.6 parts by mass, hardened castor oil (“HY-CASTOR OIL” manufactured by Toyokuni Seiyaku Co., Ltd., molecular weight 938) 9.4 parts by mass, barium sulfate (“B-55” manufactured by Sakai Chemical Co., Ltd.) 187.5 parts by mass Were blended and compounded.
Next, inflation molding was performed at a temperature of 210 ° C. using the obtained compound to obtain a raw sheet.
Next, the obtained raw sheet is stretched by 1.23 times in the longitudinal direction (MD) of the sheet at 70 ° C. and then 2.86 times in the transverse direction (TD) at 11 ° C. to obtain a porous film. It was.

(Comparative Example 3)
In Comparative Example 3, a porous film was produced by the method described in Example 1 of JP-A-11-60792 of Patent Document 4.
8 parts by mass of a polyethylene resin having a viscosity average molecular weight of 500,000, 16 parts by mass of a polyethylene resin having a viscosity average molecular weight of 1 million (the viscosity average molecular weight of the mixed composition is approximately 800,000), paraffin wax (average molecular weight 389) 76 A mixture of 20 parts by mass and 20 parts by mass of calcium carbonate particles (average particle size 18 μm) was extruded using a 40 mmφ twin screw extruder at an extrusion temperature of 170 ° C. and an extrusion rate of 10 kg / h, and a raw film was formed by an inflation method.
The obtained raw film was stretched 2.5 times in the longitudinal direction at 40 ° C. using a roll stretching machine, and then stretched 8 times in the transverse direction at a temperature of 110 ° C. using a tenter stretching machine.
The obtained film was immersed in isopropanol at 60 ° C. to extract and remove paraffin wax.
The obtained film was heat-set at a temperature of 115 ° C. using a roll stretching machine. In heat setting, the roll speed ratio was adjusted so that the stretching ratio in the longitudinal direction was 1.2 times.

The following physical properties were measured for the porous laminates obtained in Examples 1 to 5 and Comparative Examples 1 to 3.
(Measurement 1; thickness)
With a 1/1000 mm dial gauge, five in-plane measurements were made unspecified, and the average was taken as the thickness.
(Measurement 2: Air permeability (Gurley value))
The air permeability (second / 100 ml) was measured according to JIS P 8117.
(Measurement 3: Porosity)
The porosity is a numerical value indicating the proportion of the space portion in the porous laminate. The porosity is calculated by measuring the substantial amount W1 of the porous laminate, calculating the mass W0 when the porosity is 0% from the density and thickness of the resin composition, and the difference from the substantial amount of the porous laminate. Based on the following formula, the porosity is calculated.
Porosity Pv (%) = {(W0−W1) / W0} × 100

(Measurement 4; basis weight)
The basis weight is a numerical value representing the mass per unit area. The measuring method cuts out a 10-cm square porous laminated body, and measures the mass. Since the dependence on the thickness is large, this time was converted to a thickness per 25 μm, this operation was repeated three times, and the average was defined as the basis weight.
(Measurement 5; Rmax (surface irregularity))
Based on the method described in JIS B 0601, the maximum height (Rmax) value of the surface of the porous laminate was measured.

(Measurement 6; heat shrinkage rate (heat resistance))
The porous laminate is cut into 100 mm × 200 mm, wound around a 150 mm square glass plate, and only two sides with a width of 100 mm are fixed. At this time, a mark is put in a direction parallel to the two sides fixed to a half position of the length of 150 mm of the glass plate. Next, after leaving in an oven at 120 ° C. for 2 minutes and taking out from the oven, the width H1 of the marked portion is measured. The shrinkage rate S due to heat obtained by the following formula was used as an index of heat resistance.
Thermal contraction rate S (%) = {(100−H1) / 100} × 100
(Measurement 7; filler content)
The mass Wa of the porous laminate is measured, the entire amount of the resin is carbonized at a high temperature in a crucible, and the mass Wb of the remaining filler is measured.
Filler content (%) = (Wb / Wa) × 100

The results of the above measurements are shown in the following table.

Since the porous film of Comparative Example 1 has no filler on the surface, the surface unevenness is small. This deteriorates the slipperiness of the porous membrane. Moreover, the porous film of Comparative Example 1 is inferior in heat resistance.
In the porous film of the comparative example 2, since the filler exists in all the layers, it turns out that basic weight is large and it becomes heavy. Moreover, the porous film of Comparative Example 2 is also inferior in heat resistance.
Since the porous film of Comparative Example 3 is based on polyethylene resin, the heat resistance is not sufficient.
In contrast to these comparative examples, the porous laminates of Examples 1 to 5 have a certain air permeability such as an air permeability of 480 to 4,900 seconds / 100 ml and a porosity of 42 to 55%, and are sufficiently suitable for practical use. It is. Furthermore, since the filler is localized only on the surface, the weighing is small and the weight can be reduced despite the fact that the surface has unevenness and can exhibit excellent slipperiness. In addition, since a polypropylene composition is used for the intermediate layer, it has high heat resistance and can retain its shape even when exposed to high temperatures.

  The porous laminate of the present invention can be suitably used as a sanitary product such as a diaper, a packaging material, an agricultural / livestock product, a building product, a medical product, a separation film, a light diffusing plate, a reflective sheet, etc. in addition to a battery separator.

DESCRIPTION OF SYMBOLS 1 Porous laminated body 2 Intermediate | middle layer 3, 4 Both-sides outer layer 2a, 3a, 4a Micropore 10 Separator 20 Nonaqueous electrolyte battery 21 Positive electrode plate 22 Negative electrode plate

Claims (6)

A resin composition containing an inorganic filler and a thermoplastic resin, a pair of outer layers positioned on the outermost surface,
An intermediate layer made of a polypropylene resin composition that is located between the outer layers on both sides and does not contain an inorganic filler,
A laminate comprising at least three layers,
When the entire laminate is 100 parts by mass, the content of the inorganic filler is 5 to 40 parts by mass,
The polypropylene resin composition of the intermediate layer has polypropylene as a hard segment, ethylene-propylene rubber as a soft segment, the ratio of the hard segment is 5 to 95 mass%, the ratio of the soft segment is 95 to 5 mass%, And the thermoplastic resin of the outer layer on both sides is a high density polyethylene having a density of 0.92 g / cm ³ or more,
A porous laminate having a large number of micropores communicating in the thickness direction in the outer layer and the intermediate layer on both sides and having an air permeability of 1 to 10,000 seconds / 100 ml. The porous laminate according to claim 1, wherein the inorganic filler is at least one selected from the group consisting of barium sulfate, calcium carbonate, and titanium oxide, and the inorganic filler has an average particle size of 0.01 to 25 µm. body. The plasticizer is contained in the resin composition which comprises the said both-sides outer layer, and the said plasticizer is 1-30 mass parts with respect to 100 mass parts of thermoplastic resins which comprise a both-sides outer layer. Porous laminate. The porous laminate according to any one of claims 1 to 3, wherein the outer surfaces of the outer layers on both sides are rough surfaces having minute irregularities . A battery separator comprising the porous laminate according to any one of claims 1 to 4 . A battery containing the battery separator according to claim 5 .