JP4993517B2 - 刃物の切れ味検査用シート - Google Patents
刃物の切れ味検査用シート Download PDFInfo
- Publication number
- JP4993517B2 JP4993517B2 JP2009041725A JP2009041725A JP4993517B2 JP 4993517 B2 JP4993517 B2 JP 4993517B2 JP 2009041725 A JP2009041725 A JP 2009041725A JP 2009041725 A JP2009041725 A JP 2009041725A JP 4993517 B2 JP4993517 B2 JP 4993517B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- polyvinyl alcohol
- blade
- sharpness
- inspection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)平均重合度が300〜3500であり、ケン化度が90モル%以上であるポリビニルアルコールからなる水性ゲルおよびシリカ粒子を含むシートからなる刃物の切れ味検査用シート、および
(2)平均重合度が300〜3500であり、ケン化度が90モル%以上であるポリビニルアルコールおよびシリカ粒子を含むポリビニルアルコール水溶液をシート状で−10℃以下の温度に冷却し、形成されたシートを解凍することを特徴とする刃物の切れ味検査用シートの製造方法
に関する。
平均重合度が1700であり、ケン化度が約98〜99モル%であるポリビニルアルコール〔(株)クラレ製、商品名:クラレポバールPVA−117〕を濃度が10重量%となるように水に溶解させ、得られたポリビニルアルコール水溶液500gを1L容のビーカーに入れ、80℃で15分間加温した後、常温まで放冷した。
実施例1において、コロイダルシリカを使用しなかったこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1および比較例1で得られた切れ味検査用シートの物性として、貯蔵弾性率、破断強度、接触角および含水率を以下の方法によって調べた。その結果を表1に示す。
動的粘弾性測定装置〔ユービエム社(UBM Co. Ltd)製、商品名:レオゲル(Rheogel) E-4000〕を用いて貯蔵弾性率を測定した。
刃物の切れ味検査用シートを幅5mmのダンベル型に切り抜き、それぞれ3個のサンプルを作製し、引張験機〔(株)島津製作所製、商品名:オートグラフAGS−5kNG〕で1mm/minの速度で引っ張り、破断時における強度(破断強度)を測定し、それぞれ3個の平均値を求めた。
刃物の切れ味検査用シートの表面における水に対する接触角を接触角計〔協和界面科学(株)製、品番:CA−X〕を用いて25℃の大気中にて測定した。
刃物の切れ味検査用シートの質量を測定した後、40℃の乾燥機内に入れて乾燥させ、その質量変化がほとんどなくなるまで乾燥させた後、式:
〔含水率〕
=〔(乾燥前の刃物の切れ味検査用シートの質量)−(乾燥後の刃物の切れ味検査用シートの質量)〕
÷(乾燥前の刃物の切れ味検査用シートの質量)×100
に基づいて、含水率を求めた。
実施例1において、ポリビニルアルコールとして、平均重合度が1000であり、ケン化度が約98〜99モル%であるポリビニルアルコール〔(株)クラレ製、商品名:クラレポバールPVA−110〕を用いたこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、ポリビニルアルコールとして、平均重合度が2000であり、ケン化度が約98〜99モル%であるポリビニルアルコール〔(株)クラレ製、商品名:クラレポバールPVA−120〕を用いたこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、キトサンの量を1gに変更したこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、キトサンの量を80gに変更したこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、コロイダルシリカの量を1mLに変更したこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、コロイダルシリカの量を80mLに変更したこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、ポリビニルアルコール水溶液(液温:20℃)を樹脂容器内に注いだ後、その上面に二軸延伸ポリビニルアルコールフイルムを重ねなかったこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
実施例1において、二軸延伸ポリビニルアルコールフイルム〔日本合成化学工業(株)製、商品名:ボブロン(登録商標)、厚さ:約14μm〕の代わりにポリエステル製ネット(坪量:5g/cm2)を用いたこと以外は、実施例1と同様にして刃物の切れ味検査用シートを作製した。
ポリビニルアルコール粉末(平均重合度:1700、ケン化度:99.0モル%)80gと、ポリビニルアルコール粉末(平均重合度:1800、ケン化度:86〜90モル%)20gとを混合し、ポリビニルアルコール混合物を得た。
比較例2において、ポリビニルアルコール溶液を実施例1で用いたのと同じ樹脂容器内に、深さが1mmとなるように注入した後、この樹脂容器を冷却する温度を室温から−20℃に変更し、この温度で24時間冷凍し、次いで室温に戻して解凍したこと以外は、比較例1と同様にしてゲルを調製した。その結果、比較例1と相違してゲルが得られたが、得られたゲルは、弾力性が小さく、その表面がべとつくことが確認された。
厚さが4mmの市販のシリコーンゴムシートをB5の大きさに裁断することにより、刃物の切れ味検査用シートを作製した。
各実施例および各比較例で得られた刃物の切れ味検査用シートの物性として、外観、切り心地、べとつき感、弾性および切開性を以下の方法にしたがって調べた。その結果を表2に示す。
大学の医学研究科の外科を専攻している学生および教官10名に刃物の切れ味検査用シートの外観を観察してもらい、以下の評価基準に基づいて評価した。なお、Dの評価を下した者がひとりもいないことが合格基準となる。
〔評価基準〕
A:ヒトの皮膚に非常に近似している。
B:ヒトの皮膚に十分に近似している。
C:ヒトの皮膚にやや近似している。
D:ヒトの皮膚に近似していない。
大学の医学研究科の外科を専攻している学生および教官10名に手術用メス〔フェザー安全剃刀(株)製、ステンレス鋼製の外科手術用替刃メスNo.10〕を用いて実際に刃物の切れ味検査用シートに執刀して切り心地を調べてもらい、以下の評価基準に基づいて評価した。なお、Dの評価を下した者がひとりもいないことが合格基準となる。
〔評価基準〕
A:ヒトの皮膚に非常に近似している。
B:ヒトの皮膚に十分に近似している。
C:ヒトの皮膚にやや近似している。
D:ヒトの皮膚に近似していない。
大学の医学研究科の外科を専攻している学生および教官10名に刃物の切れ味検査用シートを指触してそのべとつき感を調べてもらい、以下の評価基準に基づいて評価した。なお、Dの評価を下した者がひとりもいないことが合格基準となる。
〔評価基準〕
A:ヒトの皮膚に非常に近似している。
B:ヒトの皮膚に十分に近似している。
C:ヒトの皮膚にやや近似している。
D:ヒトの皮膚に近似していない。
大学の医学研究科の外科を専攻している学生および教官10名に刃物の切れ味検査用シートを指触してその弾性を調べてもらい、以下の評価基準に基づいて評価した。なお、Dの評価を下した者がひとりもいないことが合格基準となる。
〔評価基準〕
A:ヒトの皮膚に非常に近似している。
B:ヒトの皮膚に十分に近似している。
C:ヒトの皮膚にやや近似している。
D:ヒトの皮膚に近似していない。
大学の医学研究科の外科を専攻している学生および教官10名に手術用メス〔フェザー安全剃刀(株)製、ステンレス鋼製の外科手術用替刃メスNo.10〕を用いて実際に刃物の切れ味検査用シートに執刀して切開部の創傷が生体臓器と同様に広がるかどうかを観察してもらい、以下の評価基準に基づいて評価した。なお、Dの評価を下した者がひとりもいないことが合格基準となる。
〔評価基準〕
A:生体臓器と区別がつかない。
B:生体臓器と非常に近似している。
C:生体臓器に十分に近似している。
D:生体臓器と近似していない。
Claims (13)
- 平均重合度が300〜3500であり、ケン化度が90モル%以上であるポリビニルアルコールからなる水性ゲルおよびシリカ粒子を含むシートからなる刃物の切れ味検査用シート。
- ポリビニルアルコールおよびシリカ粒子を含むポリビニルアルコール水溶液を−10℃以下の温度に冷却した後、形成されたシートを解凍してなる請求項1に記載の刃物の切れ味検査用シート。
- シリカ粒子の量がポリビニルアルコール100重量部あたり0.01〜30重量部である請求項1または2に記載の刃物の切れ味検査用シート。
- さらに、多糖類を含有する請求項1〜3のいずれかに記載の刃物の切れ味検査用シート。
- その一方表面に樹脂シートが積層されてなる請求項1〜4のいずれかに記載の刃物の切れ味検査用シート。
- 樹脂シートがポリビニルアルコールシートである請求項5に記載の刃物の切れ味検査用シート。
- 平均重合度が300〜3500であり、ケン化度が90モル%以上であるポリビニルアルコールおよびシリカ粒子を含むポリビニルアルコール水溶液をシート状で−10℃以下の温度に冷却し、形成されたシートを解凍することを特徴とする刃物の切れ味検査用シートの製造方法。
- 形成されたシートを解凍した後、該シートを35〜80℃に加熱する請求項7に記載の刃物の切れ味検査用シートの製造方法。
- ポリビニルアルコール水溶液におけるポリビニルアルコール濃度が5〜40重量%である請求項7または8に記載の刃物の切れ味検査用シートの製造方法。
- シリカ粒子の量がポリビニルアルコール100重量部あたり0.01〜30重量部である請求項7〜9のいずれかに記載の刃物の切れ味検査用シートの製造方法。
- ポリビニルアルコール水溶液が多糖類を含有する請求項7〜10のいずれかに記載の刃物の切れ味検査用シートの製造方法。
- ポリビニルアルコール水溶液上に樹脂シートを載せるかまたは樹脂シート上にポリビニルアルコール水溶液を載せ、得られたポリビニルアルコール水溶液と樹脂シートとが積層されたシートを−10℃以下の温度に冷却する請求項7〜11のいずれかに記載の刃物の切れ味検査用シートの製造方法。
- 樹脂シートがポリビニルアルコールシートである請求項12に記載の刃物の切れ味検査用シートの製造方法。