JP4784550B2 - 透明導電塗料及び透明導電膜 - Google Patents
透明導電塗料及び透明導電膜 Download PDFInfo
- Publication number
- JP4784550B2 JP4784550B2 JP2007123236A JP2007123236A JP4784550B2 JP 4784550 B2 JP4784550 B2 JP 4784550B2 JP 2007123236 A JP2007123236 A JP 2007123236A JP 2007123236 A JP2007123236 A JP 2007123236A JP 4784550 B2 JP4784550 B2 JP 4784550B2
- Authority
- JP
- Japan
- Prior art keywords
- transparent conductive
- binder resin
- film
- conductive film
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
導電性酸化物粒状粉として、平均粒径0.03μmのITO粒状粉(住友金属鉱山(株)製、SUFP−HX)を用いた。バインダー樹脂として架橋性のフェノキシ樹脂(東都化成(株)製、FX−293;Tg:163℃、水酸基価163KOHmg/g)を用い、その硬化剤にはHDI系ブロックイソシアネート(旭化成(株)製のMF−K60X、固形分(硬化剤成分)約60%、最低硬化温度90℃、NCO:6.5wt%)を用いた。また、溶剤としては、イソホロンを使用した。
透明導電膜のヘイズ値(%)=(透明導電膜付き基材のヘイズ値)−(基板のヘイズ値)
バインダー樹脂として、アクリルポリオール樹脂(三菱レイヨン(株)製、GS−5756、Tg:102℃、水酸基29KOHmg/g)を用いた以外は、上記実施例1と同様にして、透明導電塗料を得た。この透明導電塗料の組成は、ITO:30%、アクリルポリオール樹脂8%、ブロックイソシアネート2%、イソホロン60%であった。また、ITO粒状粉:バインダー樹脂の重量比は75:25であり、NCO(イソシアネート基)/OH(水酸基)のモル比は0.6であった。
上記実施例1において、架橋性樹脂と硬化剤の比率を維持したままバインダー樹脂量を減らし、ITO粒状粉:バインダー樹脂の重量比を70:30にした以外は上記実施例1と同様にして透明導電塗料を得た。
上記実施例1において、架橋性樹脂と硬化剤の比率を維持したままバインダー樹脂量を増やし、ITO粒状粉:バインダー樹脂の重量比を96:4にした以外は上記実施例1と同様にして透明導電塗料を得た。
上記実施例1において、ITO粒状物とバインダー樹脂との重量比率を維持したまま、架橋性樹脂と硬化剤の比率をNCO(イソシアネート基)/OH(水酸基)のモル比で0.04まで減らした以外は上記実施例1と同様にして透明導電塗料を得た。
上記実施例1において、ITO粒状物とバインダー樹脂の重量比率を維持したまま、架橋性樹脂と硬化剤の比率をNCO(イソシアネート基)/OH(水酸基)のモル比で6まで増やした以外は上記実施例1と同様にして透明導電塗料を得た。
Claims (6)
- 酸化インジウム、酸化錫、酸化亜鉛から選ばれた少なくとも1種を主成分とする平均粒径1〜100nmの導電性酸化物粒状粉が、バインダー樹脂を含む溶剤中に分散した透明導電塗料であって、前記バインダー樹脂が架橋性フェノキシ系樹脂であり且つ前記溶剤中に硬化剤が含有されていて、該バインダー樹脂の架橋前のガラス転移点(Tg)が120℃以上であることを特徴とする透明導電塗料。
- 前記バインダー樹脂のガラス転移点(Tg)が140℃以上であることを特徴とする、請求項1に記載の透明導電塗料。
- 前記導電性酸化物粒状粉:前記バインダー樹脂の重量比が75:25〜95:5の範囲であることを特徴とする、請求項1又は2に記載の透明導電塗料。
- 前記硬化剤がイソシアネート化合物であって、前記架橋性フェノキシ系樹脂の水酸基に対する該イソシアネート化合物のイソシアネート基のモル比が0.05〜5であることを特徴とする、請求項1〜3のいずれかに記載の透明導電塗料。
- 前記硬化剤のイソシアネート化合物がブロックイソシアネートであることを特徴とする、請求項4に記載の透明導電塗料。
- 請求項1〜5のいずれかに記載の透明導電塗料を用いて形成された透明導電膜であって、バインダー樹脂中に分散した導電性酸化物粒状粉を含み、膜の比抵抗が1.0Ω・cm以下であることを特徴とする透明導電膜。