JP4699163B2 - Laminated film and package using the same - Google Patents
Laminated film and package using the same Download PDFInfo
- Publication number
- JP4699163B2 JP4699163B2 JP2005294641A JP2005294641A JP4699163B2 JP 4699163 B2 JP4699163 B2 JP 4699163B2 JP 2005294641 A JP2005294641 A JP 2005294641A JP 2005294641 A JP2005294641 A JP 2005294641A JP 4699163 B2 JP4699163 B2 JP 4699163B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- metal foil
- laminated
- laminate resin
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、積層フィルムおよびこれを用いた包装材料に関し、より詳しくは、金属箔のクラックが少なく、外観が良好で高いバリアー性能を有する積層フィルムに関する。 The present invention relates to a laminated film and a packaging material using the laminated film, and more particularly, to a laminated film having few metal foil cracks, good appearance, and high barrier performance.
金属箔が有する光、ガス、水蒸気等のバリアー性を利用した包装材料が知られている。これら包装材料は、一般的に、アルミニウム等の金属箔を介してプラスチックフィルムを積層した構造を有している。例えば、ポリエステル等の基材フィルム上にアルミニウム箔層とポリエチレン等のヒートシーラント層とを積層した積層フィルムが一般的に用いられている。 Packaging materials that utilize barrier properties such as light, gas, and water vapor possessed by metal foils are known. These packaging materials generally have a structure in which a plastic film is laminated via a metal foil such as aluminum. For example, a laminated film in which an aluminum foil layer and a heat sealant layer such as polyethylene are laminated on a base film such as polyester is generally used.
上記積層フィルムは、その各層がウレタン系接着剤等でドライラミネート加工されることにより接着したり、または、基材フィルム、金属箔、ポリエチレンの各層を、ラミネート樹脂を介して押出ラミネート加工を行うことにより接着したりしている。このドライラミネート方式は、主として酢酸エチル系溶剤にてウレタン系接着剤を希釈して接着剤塗布液とし、この塗布液を各層に塗布して乾燥させた後に、各層を貼り合わせて積層するものであるが、加工速度に限界があったり、残ソルが高い、養成時間を要する、といった問題がある。一方、押出ラミネート方式では、上記のような問題がなく、加工速度も高く、養成時間を必要としないといった利点を有する。 The laminated film may be bonded by dry lamination of each layer with a urethane-based adhesive or the like, or each layer of base film, metal foil, and polyethylene may be laminated by extrusion through a laminate resin. It is adhered by. In this dry laminating method, a urethane adhesive is diluted mainly with an ethyl acetate solvent to form an adhesive coating liquid. After the coating liquid is applied to each layer and dried, the layers are bonded and laminated. However, there are problems such as limited processing speed, high residual sol, and long training time. On the other hand, the extrusion laminating method has the above-described problems, has a high processing speed, and does not require a training time.
しかしながら、ラミネート樹脂を用いた押出ラミネート加工された積層フィルムは、図4に示すようなガゼット袋やピロー袋等の包装体9を形成した際に、積層フィルムが重なり合った部分をヒートシール加工すると、その重なり合った部分10の金属箔にクラックが発生するといった問題があった。このクラックの隙間が大きくなると、外観上の問題だけでなく、ガスバリアー性や光バリアー性にも影響するおそれがある。
However, when the laminated film subjected to extrusion lamination processing using a laminating resin is formed into a
本発明者らは、今般、各層を押出ラミネート加工して積層する際、特定のラミネート樹脂を用いることにより、ラミネート加工性が良好で、金属箔積層フィルムを重ね合わせてヒートシール加工した場合であっても、金属箔にクラックが発生せず、外観の良好な包装体が得られる、との知見を得た。 In the present invention, when the layers are laminated by extrusion laminating, the laminating property is good by using a specific laminating resin, and the metal foil laminated film is laminated and heat-sealed. However, the metal foil was not cracked, and the knowledge that a package with a good appearance was obtained was obtained.
したがって、本発明の目的は、ヒートシール加工した場合であっても、金属箔にクラックが発生せず、外観の良好な包装体が得られる、金属箔積層フィルム、およびこれを用いた包装材料を提供することにある。 Therefore, an object of the present invention is to provide a metal foil laminated film, and a packaging material using the same, in which a metal foil does not crack and a good appearance can be obtained even when heat-sealed. It is to provide.
本発明による金属箔積層フィルムは、基材フィルム、金属箔、およびヒートシールフィルムの少なくとも3層からなり、前記基材フィルムと金属箔とが、ラミネート樹脂を介して押出ラミネート加工により接着されてなる積層フィルムであって、前記ラミネート樹脂が、密度0.940〜0.965g/cm3のポリエチレンからなるものである。 The metal foil laminated film according to the present invention comprises at least three layers of a base film, a metal foil, and a heat seal film, and the base film and the metal foil are bonded together by extrusion laminating through a laminating resin. In the laminated film, the laminate resin is made of polyethylene having a density of 0.940 to 0.965 g / cm 3 .
このような密度を有するポリエチレン樹脂をラミネート樹脂として用いることにより、積層フィルムが重なり合った部分をヒートシール加工してガゼット袋等の包装体を製造した場合であっても、その重なり合った部分の金属箔にクラックが発生することはなく、外観の良好な包装体が得られる。 By using a polyethylene resin having such a density as a laminate resin, even when a packaging body such as a gusset bag is manufactured by heat-sealing the overlapping portion of the laminated film, the overlapping portion of the metal foil No cracks are generated and a package having a good appearance can be obtained.
また、本発明の別の態様としての積層フィルムの製造方法は、前記基材フィルムと金属箔とを、前記ラミネート樹脂を介して押出ラミネート加工する際に、前記ラミネート樹脂表面に、接着促進剤塗工液処理および/またはオゾン処理を行うものである。 In another aspect of the present invention, there is provided a method for producing a laminated film comprising: applying an adhesion promoter to the surface of the laminate resin when the base film and the metal foil are extrusion laminated through the laminate resin. The treatment liquid treatment and / or the ozone treatment are performed.
このようにラミネート樹脂表面に、表面処理加工を行うことにより、基材フィルムと、ラミネート樹脂との接着性が高まり、より一層、金属箔のクラックが発生しにくくなる。 Thus, by performing the surface treatment on the surface of the laminate resin, the adhesiveness between the base film and the laminate resin is enhanced, and the cracks of the metal foil are further less likely to occur.
本発明による積層フィルムを、図面を参照しながら説明する。 The laminated film according to the present invention will be described with reference to the drawings.
本発明による積層フィルム1は、図1に示すように、基材フィルム2、金属箔3、およびヒートシールフィルム4の少なくとも3層から構成されており、基材フィルム2と金属箔3とが、ラミネート樹脂5aを介して接着された構造を有している。ラミネート樹脂は、下記に説明するように、溶融押出しコーテイングラミネーター(以下、押出しラミネーターという)により供給され、基材フィルムと金属箔との間に挿入されて、ラミネート加工が行われる。
As shown in FIG. 1, the laminated film 1 according to the present invention is composed of at least three layers of a
基材フィルムと金属箔との接着に使用されるラミネート樹脂は、密度が0.940〜0.965g/cm3の範囲のポリエチレンからなる。密度が0.940g/cm3よりも小さいと、積層フィルムが重なり合った部分をヒートシール加工してガゼット袋等の包装体を製造した場合に、その重なり合った部分の金属箔にクラックが発生する。一方、0.965g/cm3以上であると、ラミネート加工して積層フィルムとした場合に、フィルムの腰が強くなりトリミング加工性が悪化するとともに、カール性も悪化してしまう。なお、本明細書における「密度」とは、JIS-K7112に準拠して測定された値を意味する。 The laminate resin used for bonding the base film and the metal foil is made of polyethylene having a density in the range of 0.940 to 0.965 g / cm 3 . When the density is less than 0.940 g / cm 3 , cracks are generated in the overlapped portion of the metal foil when the overlapped portion of the laminated film is heat sealed to produce a package such as a gusset bag. On the other hand, when it is 0.965 g / cm 3 or more, when laminated to form a laminated film, the stiffness of the film becomes strong, trimming workability is deteriorated, and curling properties are also deteriorated. The “density” in the present specification means a value measured according to JIS-K7112.
また、上記のラミネート樹脂は、MFR(メルトフローレート)が、1〜50g/10分の範囲であることが好ましく、3〜20/10分の範囲であることがより好ましい。このような物性範囲にある樹脂を用いることにより、積層フィルムが重なり合った部分をヒートシール加工してガゼット袋等の包装体を製造した場合であっても、その重なり合った部分の金属箔にクラックが発生することはなく、外観の良好な包装体が得られる。ここで、本願明細書における「MFR」とは、JIS-K7210に準拠して測定されたメルトフローレートの値を意味する。MFRが1g/10分未満であると、樹脂の延展性がなくなり、良好な積層フィルムを形成できず、一方、50g/10分を超えると、押出ラミネーターから押し出される際に、ネックインが大きくなりフィルム成型性が悪化するため、均一な溶融膜が得られなくなる。なお、金属箔積層フィルムを重ね合わせた状態でヒートシールを行うと、金属箔にクラックが発生する理由として、定かではないが、ヒートシールにより積層フィルムに熱が加わると、基材フィルムと金属箔との間のラミネート樹脂部分のみ溶融変形し、この変形により金属箔も追従して変形するためにクラックが発生するものと考えられる。したがって、ラミネート樹脂の溶融粘度は、いずれの剪断速度においても高いことが好ましい。 The laminate resin preferably has an MFR (melt flow rate) in the range of 1 to 50 g / 10 minutes, and more preferably in the range of 3 to 20/10 minutes. By using a resin in such a physical property range, even when a laminated body such as a gusset bag is manufactured by heat-sealing the overlapping portion of the laminated film, cracks are generated in the overlapping metal foil. It does not occur and a package with a good appearance is obtained. Here, “MFR” in the present specification means a melt flow rate value measured in accordance with JIS-K7210. If the MFR is less than 1 g / 10 minutes, the resin spreadability is lost and a good laminated film cannot be formed. On the other hand, if it exceeds 50 g / 10 minutes, the neck-in becomes large when extruded from the extrusion laminator. Since the film moldability deteriorates, a uniform molten film cannot be obtained. In addition, when heat sealing is performed in a state in which the metal foil laminated film is overlaid, the reason for cracks in the metal foil is not clear, but when heat is applied to the laminated film by heat sealing, the base film and the metal foil It is considered that only the laminating resin portion between and melts and deforms, and the metal foil also follows and deforms due to this deformation, so that cracks are generated. Accordingly, the melt viscosity of the laminate resin is preferably high at any shear rate.
本発明の金属箔積層フィルムに用いられるラミネート樹脂は、低密度ポリエチレン(以下、LDPEという)、中密度ポリエチレン(以下、MDPEという)、直鎖状低密度ポリエチレン(以下、LLDPEという)、高密度ポリエチレン(以下、HDPEという)、およびこれらの混合物から選択されるものであることが好ましい。HDPEを単独で用いることもできるが、LDPE、MDPE、およびLLDPEを混合した樹脂を用いることが好ましい。このような混合したポリエチレンを用いることにより、押出ラミネート加工適性を向上させることができる。また、これらの混合物中に、LDPEが5〜60重量%、特に、5〜20重量%含まれてなることが好ましい。上記範囲のLDPEが含まれることにより、押出ラミネート加工適性が向上する。LDPEの含有量が、5重量%未満では、ネックインが大きくフィルム加工適性に劣り、一方、60重量%を超えると、積層フィルムを形成した場合に、ヒートシール加工により、金属箔にクラックが発生する。 The laminate resin used for the metal foil laminated film of the present invention includes low density polyethylene (hereinafter referred to as LDPE), medium density polyethylene (hereinafter referred to as MDPE), linear low density polyethylene (hereinafter referred to as LLDPE), and high density polyethylene. (Hereinafter referred to as HDPE) and mixtures thereof are preferred. Although HDPE can be used alone, it is preferable to use a resin in which LDPE, MDPE, and LLDPE are mixed. By using such a mixed polyethylene, the suitability for extrusion laminating can be improved. Moreover, it is preferable that LDPE is contained in these mixtures 5 to 60weight%, especially 5 to 20weight%. By including LDPE in the above range, extrusion laminating suitability is improved. When the content of LDPE is less than 5% by weight, the neck-in is large and the film processing suitability is poor. On the other hand, when it exceeds 60% by weight, cracks occur in the metal foil due to heat sealing when a laminated film is formed. To do.
上記ラミネート樹脂は、基材フィルムとの接着性を妨げない程度に、添加剤を含有してもよい。添加剤としては、スリップ剤、帯電防止剤、防曇剤、紫外線吸収剤、酸化防止剤等が挙げられる。また、炭酸カルシウム、シリカ、酸化チタン、タルク等の無機充填剤や顔料等を添加してもよい。 The laminate resin may contain an additive to such an extent that the adhesiveness with the base film is not hindered. Examples of the additive include a slip agent, an antistatic agent, an antifogging agent, an ultraviolet absorber, and an antioxidant. In addition, inorganic fillers such as calcium carbonate, silica, titanium oxide, and talc, pigments, and the like may be added.
さらに、基材フィルムと金属箔の間に設けられたラミネート樹脂層は、その厚みが5〜25μmであることが好ましい。この範囲の膜厚とすることにより、接着強度とクラックの発生防止とを両立できる。ラミネート樹脂層の厚みが5μm未満であると、基材フィルムとの接着性が不十分となり、一方、25μmを超えると、ラミネート樹脂層が厚くなりすぎて、ヒートシールの際に金属箔のクラックを生じさせてしまう。 Furthermore, the laminate resin layer provided between the base film and the metal foil preferably has a thickness of 5 to 25 μm. By setting the film thickness within this range, both adhesive strength and prevention of cracks can be achieved. If the thickness of the laminate resin layer is less than 5 μm, the adhesion to the base film becomes insufficient. On the other hand, if the thickness exceeds 25 μm, the laminate resin layer becomes too thick and cracks of the metal foil are caused during heat sealing. It will cause it.
本発明の金属箔積層フィルムに用いられる基材フィルムは、ポリエチレン、ポリプロピレンなどのポリオレフィン系樹脂、ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリビニルアルコール、エチレン・ビニルアルコール共重合体、ポリアクリロニトリル、ポリアミド、アクリル酸エステル又はメタクリ酸エステルを主成分とするアクリル樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル、ポリアセタール、アセチル・ジ又はトリセルロースの繊維素誘導体や、ポリカーボネート等の熱可塑性樹脂からなる延伸または未延伸のフィルムである。特に印刷適性、後加工適性に優れたポリエステルやナイロン6の二軸延伸フィルムが好適に用いられる。基材フィルムの厚みとしては、概ね、5〜35μm程度である。
The base film used for the metal foil laminated film of the present invention is a polyolefin resin such as polyethylene and polypropylene, polystyrene, polyvinyl chloride, polyvinylidene chloride, polyvinyl alcohol, ethylene / vinyl alcohol copolymer, polyacrylonitrile, polyamide, From acrylic resins based on acrylic esters or methacrylic esters, polyesters such as polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyacetal, acetyl di- or tri-cellulose fiber derivatives, and thermoplastic resins such as polycarbonate A stretched or unstretched film. In particular, a polyester or
本発明の金属箔積層フィルムに用いられる金属箔は、光、酸素及び水蒸気を遮断するものであり、アルミニウム、銅、鉄、鉛等の金属を圧延したものである。金属箔は、容易に圧延できるアルミニウム箔が好ましく使用できる。また、金属箔の厚みは、概ね6〜12μm程度である。 The metal foil used for the metal foil laminated film of the present invention blocks light, oxygen and water vapor, and is obtained by rolling a metal such as aluminum, copper, iron and lead. The metal foil is preferably an aluminum foil that can be easily rolled. Moreover, the thickness of metal foil is about 6-12 micrometers in general.
金属箔3に積層してヒートシーラント層を形成するヒートシールフィルム4は、熱可塑性樹脂であれば特に限定されるものではないが、LDPE、MDPE、HDPE、LLDPE等のポリエチレン樹脂、エポリプロピレン樹脂、チレン・酢酸ビニル共重合体、エチレン・アクリル酸共重合体、エチレン・アクリル酸エステル共重合体、アイオノマー、ポリエステルの未延伸フィルム等が好適に用いられる。それらの中でも、特に、ポリエチレン樹脂が好ましい。ヒートシールフィルムの厚みは、概ね、30〜120μm程度である。
The
次に、本発明による金属箔積層フィルムの製造方法について説明する。 Next, the manufacturing method of the metal foil laminated film by this invention is demonstrated.
図2は、押出ラミネーターを用いて、本発明の製造方法を実施する一態様を示したものである。基材フィルム2と金属箔3とが、接厚ドラム7に供給されるとともに、エクストルーダー6から溶融したラミネート樹脂5aが、基材フィルム2と金属箔3との間に供給される。このようにして、形成された基材フィルム/ラミネート樹脂/金属箔の積層フィルムを一旦巻き取って、この積層フィルムのアルミ箔上に、上記と同様にして、押出ラミネーターを用いてラミネート樹脂を介してヒートシールフィルムを貼り合わせたり、または、接着剤を用いてヒートシールフィルムを貼り合わせたりして(ドライラミネーション)積層フィルムを得ることができる。
FIG. 2 shows an embodiment in which the production method of the present invention is carried out using an extrusion laminator. The
本発明にあっては、基材フィルム2と金属箔3とを、ラミネート樹脂5aを介して押出ラミネート加工する際に、ラミネート樹脂表面に、接着促進剤塗工液処理(以下、AC処理という)および/またはオゾン処理が行われるものである。このように、ラミネート樹脂の基材フィルムと接着する側の面にAC処理および/またはオゾン処理を行うことにより、基材フィルムとラミネート樹脂との接着性が向上する。AC処理は、アンカーコート剤をラミネート樹脂フィルムの表面に塗布することにより行うことができる。アンカーコート剤としては、ポリエチレンイミン、2液硬化型ウレタン、アルキルチタネート等を成分とするものを用いることができる。AC処理は、基材フィルムに別途、アンカーコート剤を塗布して行うことも可能であるが、基材フィルム2が、接厚ドラム7に供給される前に、ラミネート工程中で行っても良い。
In the present invention, when the
また、オゾン処理は、積層される前の段階で、ラミネート樹脂5aにオゾン含有ガスを吹き付けることにより行うことができる。具体的には、エアーギャップ内で、ノズルまたはスリット状吹き出し口8から、オゾン含有ガス(空気等)をラミネート樹脂に向けて吹き付けることにより行うことができる。また、基材フィルム2とラミネート樹脂5aとが圧着される部分(接圧ドラム7付近)に、混合ガスを吹き付けてもよい(図示せず)。混合ガスとしては、濃度1〜20g/m3のオゾンを含有させた気体を用いることが好ましい。1g/m3未満であると、処理が不十分となり、基材フィルムとの接着性が向上せず、一方、20g/m3を超えると、臭気の観点から好ましくない。また、オゾン含有ガスの流量は、積層フィルムの加工幅や加工速度にもよるが、概ね流量1〜5Nm3/h程度である。オゾン処理は、基材フィルム表面にも施しておくことが好ましい。かかる処理は、基材フィルムとラミネート樹脂フィルムとが、圧着ローラーにより接着される部分に直接吹き付けて行うこともできる。また、AC処理やオゾン処理は、ヒートシールフィルムと金属箔とを接着する際にも、行うことができる。
Further, the ozone treatment can be performed by spraying an ozone-containing gas on the
本発明にあっては、図3に示すように、タンデム型の押出ラミネーターを用いて、基材フィルム2と金属箔3との接着と、金属箔3とヒートシールフィルム4との接着とを同時に行っても良い。タンデム型の押出ラミネーターを用いることにより、積層フィルムの加工速度が向上する。AC処理および/またはオゾン処理は、上記と同様にして行うことができる。
In the present invention, as shown in FIG. 3, the adhesion between the
ラミネート樹脂を積層フィルムに形成する際の加工温度としては、樹脂温度が250〜330℃、好ましくは、280〜320℃の範囲である。加工温度が250℃未満であると、ラミネート樹脂フィルムの延伸性が悪化し、良好な積層フィルムが得られなくなる。また、基材フィルムとの接着性も悪化する。一方、330℃を超える加工温度では、樹脂の熱分解やゲル化が起こり、臭気の問題とともに、得られる積層フィルムの機械的強度も低下してしまう。 As processing temperature at the time of forming laminated resin in a laminated film, resin temperature is 250-330 degreeC, Preferably, it is the range of 280-320 degreeC. When the processing temperature is less than 250 ° C., the stretchability of the laminated resin film is deteriorated and a good laminated film cannot be obtained. Moreover, adhesiveness with a base film also deteriorates. On the other hand, when the processing temperature exceeds 330 ° C., thermal decomposition and gelation of the resin occur, and the mechanical strength of the resulting laminated film is lowered along with the problem of odor.
上記のようにして得られた積層フィルムを用いて、ガゼット袋やピロー袋等の包装体を形成することができる。本発明にあっては、金属箔積層フィルムを重ね合わせてヒートシールした部分であっても、金属箔のクラック等が発生せず、外観の良好な包装体が得られる。 Using the laminated film obtained as described above, a packaging body such as a gusset bag or a pillow bag can be formed. In this invention, even if it is the part which laminated | stacked the metal foil laminated | multilayer film and heat-sealed, the crack etc. of metal foil do not generate | occur | produce and a package with a favorable external appearance is obtained.
以下に本発明の積層フィルムを、実施例によりさらに詳細に説明するが、本発明がこれら実施例に限定されるものではない。 Hereinafter, the laminated film of the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
実施例1
基材フィルムとして、二軸延伸ポリエチレンテレフタレートフィルム(膜厚12μm、T4102、東洋紡(株)製)を用い、金属箔として、アルミニウム箔(1N30、膜厚7μm)を用いた。また、ヒートシールフィルムとして、LLDPEフィルム(膜厚60μm、UB-1、タマポリ(株)製)を用いた。
Example 1
A biaxially stretched polyethylene terephthalate film (film thickness: 12 μm, T4102, manufactured by Toyobo Co., Ltd.) was used as the base film, and an aluminum foil (1N30, film thickness: 7 μm) was used as the metal foil. Further, an LLDPE film (film thickness: 60 μm, UB-1, manufactured by Tamapoly Co., Ltd.) was used as a heat seal film.
上記の基材フィルム、金属箔、およびヒートシールフィルムを、タンデム型押出ラミネーターを用いて貼り合わせて、積層フィルム1を作製した。基材フィルムと金属箔とを接着するためのラミネート樹脂として、HDPE(密度0.967g/cm3、MFR10g/10分)80重量%とLDPE(密度0.919g/cm3、MFR10g/10分)20重量%をブレンドした混合物(密度0.957g/cm3、MFR10g/10分)を用い、また、金属箔とヒートシールフィルムとを接着するためのラミネート樹脂として、上記と同様の混合物を用いた。これら樹脂を320℃の加工温度にて成形を行い、ラミネート加工を行った。ラミネート加工の際、基材フィルム側の表面にアンカーコート処理を行った。アンカーコート剤として、ウレタン系樹脂(タケラック A3210/A3075の1:1混合物、三井武田ケミカル(株)製)を、酢酸エチルで溶解したもの(ウレタン系樹脂:酢酸エチル=3.2:16)を用い、この塗工液を、基材フィルム表面に、塗布量0.5g/m2となるように塗布することにより、アンカーコート処理を行った。さらに、金属箔側の表面にも上記と同様のアンカーコート処理を行った。 The base film, metal foil, and heat seal film were bonded together using a tandem extrusion laminator to produce a laminated film 1. HDPE (density 0.967 g / cm 3 , MFR 10 g / 10 min) 80 wt% and LDPE (density 0.919 g / cm 3 , MFR 10 g / 10 min) as a laminate resin for bonding the base film and the metal foil A mixture blended with 20% by weight (density 0.957 g / cm 3 , MFR 10 g / 10 min) was used, and the same mixture as described above was used as a laminate resin for bonding the metal foil and the heat seal film. . These resins were molded at a processing temperature of 320 ° C. and laminated. During the laminating process, an anchor coat treatment was performed on the surface of the base film side. As an anchor coating agent, urethane resin (Takelac A3210 / A3075 1: 1 mixture, manufactured by Mitsui Takeda Chemical Co., Ltd.) dissolved in ethyl acetate (urethane resin: ethyl acetate = 3.2: 16) The anchor coating treatment was performed by applying this coating solution on the surface of the base film so that the coating amount was 0.5 g / m 2 . Further, the same anchor coat treatment as described above was performed on the surface of the metal foil.
このようにして、基材フィルム/ラミネート樹脂/金属箔/ラミネート樹脂/ヒートシールフィルムの構成を有する積層フィルム1を得た。得られた積層フィルム1のラミネート樹脂層の厚みは、いずれも15μmであった。 In this way, a laminated film 1 having a configuration of base film / laminate resin / metal foil / laminate resin / heat seal film was obtained. The thickness of the laminate resin layer of the obtained laminated film 1 was 15 μm in all cases.
実施例2
実施例1と同様の基材フィルム、金属箔、およびヒートシールフィルムを用い、同様の構成の積層フィルム2を作製した。基材フィルムと金属箔とを接着するためのラミネート樹脂として、HDPE(密度0.967g/cm3、MFR10g/10分)80重量%とLDPE(密度0.919g/cm3、MFR10g/10分)20重量%をブレンドした混合物(密度0.957g/cm3、MFR10g/10分)を用い、また、金属箔とヒートシールフィルムとを接着するためのラミネート樹脂として、LDPE(密度0.919g/cm3、MFR7g/10分)を用いた。これら樹脂を300℃の加工温度にて成型を行い、ラミネート加工を行った。ラミネート加工の際、基材フィルム側の表面および金属箔側の表面のそれぞれに、実施例1と同様にして、アンカーコート処理を行った。さらに、基材フィルム側の表面にオゾン処理を行った。オゾン処理は、オゾン濃度16g/m3の混合ガスを流量1.5Nm3/hにて、基材フィルム側に吹き付けることにより行った。実施例1と同様のアンカーコート処理を行った。
Example 2
Using the same base film, metal foil, and heat seal film as in Example 1, a
このようにして、基材フィルム/ラミネート樹脂/金属箔/ラミネート樹脂/ヒートシールフィルムの構成を有する積層フィルム2を得た。得られた積層フィルム2のラミネート樹脂層の厚みは、いずれも10μmであった。
Thus, a
比較例1
基材フィルムと金属箔との間に設けるラミネート樹脂、および金属箔とヒートシールフィルムとの間に設けるラミネート樹脂として、LDPE(密度0.919g/cm3、MFR7g/10分)を用いた以外は実施例1と同様にして、基材フィルム/ラミネート樹脂/金属箔/ラミネート樹脂/ヒートシールフィルムの構成を有する積層フィルム3を得た。得られた積層フィルム3のラミネート樹脂層の厚みは、いずれも15μmであった。
Comparative Example 1
Except for using LDPE (density 0.919 g / cm 3 , MFR 7 g / 10 min) as the laminate resin provided between the base film and the metal foil and the laminate resin provided between the metal foil and the heat seal film In the same manner as in Example 1, a
比較例2
基材フィルムと金属箔との間に設けるラミネート樹脂、および金属箔とヒートシールフィルムとの間に設けるラミネート樹脂として、HDPE(密度0.967g/cm3、MFR17g/10分)を用いた以外は実施例1と同様にしてラミネート加工を行った。しかしながら、ラミネート加工中、サイジングが発生して、ラミネート樹脂の厚みが大きく変動したため、積層フィルムを作製することはできなかった。
Comparative Example 2
Except for using HDPE (density 0.967 g / cm 3 , MFR 17 g / 10 min) as the laminate resin provided between the base film and the metal foil and the laminate resin provided between the metal foil and the heat seal film. Lamination was performed in the same manner as in Example 1. However, since sizing occurred during the laminating process and the thickness of the laminating resin fluctuated greatly, a laminated film could not be produced.
比較例3
基材フィルムと金属箔との間に設けるラミネート樹脂、および金属箔とヒートシールフィルムとの間に設けるラミネート樹脂として、HDPE(密度0.955g/cm3、MFR12g/10分)を用いた以外は実施例1と同様にして、基材フィルム/ラミネート樹脂/金属箔/ラミネート樹脂/ヒートシールフィルムの構成を有する積層フィルム4を得た。得られた積層フィルム4のラミネート樹脂層の厚みは、いずれも15μmであった。
Comparative Example 3
Except for using HDPE (density 0.955 g / cm 3 , MFR 12 g / 10 min) as the laminate resin provided between the base film and the metal foil and the laminate resin provided between the metal foil and the heat seal film. In the same manner as in Example 1, a
包装体の作製
得られた積層フィルム1〜4を用いて、ピロー袋1〜4を作製した。ピロー袋の作製は、縦ピロー機(KBF-6100、川島製作所(株)製)を用い、製袋条件は以下の通りであった。
シール形状:波形シール
ヒートシール温度:予備加熱110℃、背貼150℃、頭貼150℃、底貼150℃
Production of packaging body Using the obtained laminated films 1 to 4, pillow bags 1 to 4 were produced. The pillow bag was produced using a vertical pillow machine (KBF-6100, manufactured by Kawashima Seisakusho Co., Ltd.) under the following conditions.
Seal shape: Corrugated seal Heat seal temperature: Pre-heating 110 ° C, Back paste 150 ° C, Head paste 150 ° C, Bottom paste 150 ° C
得られたピロー袋について、ヒートシール部分について、目視および顕微鏡観察により、アルミ箔部分のクラックの有無を調べた。 About the obtained pillow bag, the presence or absence of the crack of an aluminum foil part was investigated by visual observation and microscope observation about the heat seal part.
結果は表1に示される通りであった。
1 積層フィルム
2 基材
3 金属箔
4 ヒートシールフィルム
5a、5b ラミネート樹脂
6 エクストルーダー
7 ローラー
8 吹き出し口
DESCRIPTION OF SYMBOLS 1
Claims (11)
前記ラミネート樹脂が、密度0.940〜0.965g/cm 3 のポリエチレンからなり、低密度ポリエチレンを5〜60重量%含んでなる、積層フィルム。 A laminated film comprising at least three layers of a base film, a metal foil, and a heat seal film, wherein the base film and the metal foil are bonded by extrusion laminating through a laminate resin,
A laminated film in which the laminate resin is made of polyethylene having a density of 0.940 to 0.965 g / cm 3 and contains 5 to 60% by weight of low density polyethylene.
前記基材フィルムと金属箔とを、前記ラミネート樹脂を介して押出ラミネート加工する際に、前記ラミネート樹脂表面に、接着促進剤塗工液処理および/またはオゾン処理を行い、
前記基材フィルムと前記ラミネート樹脂と前記金属箔とを積層し、次いで、
前記金属箔とヒートシールフィルムとを貼り合わせるか、または、前記基材フィルムと前記ラミネート樹脂と前記金属箔との積層と同時に、前記金属箔とヒートシールフィルムとを貼り合わせる、積層フィルムの製造方法。 A method for producing the laminated film according to any one of claims 1 to 4,
When the substrate film and the metal foil are extrusion laminated through the laminate resin, the surface of the laminate resin is subjected to an adhesion promoter coating liquid treatment and / or an ozone treatment,
Laminating the base film, the laminate resin and the metal foil,
The method for producing a laminated film, wherein the metal foil and the heat seal film are bonded together, or the metal foil and the heat seal film are bonded simultaneously with the lamination of the base film, the laminate resin and the metal foil. .