JP4601267B2 - Photosensitive black composition, black matrix substrate and color filter using the same - Google Patents

Photosensitive black composition, black matrix substrate and color filter using the same Download PDF

Info

Publication number
JP4601267B2
JP4601267B2 JP2003176274A JP2003176274A JP4601267B2 JP 4601267 B2 JP4601267 B2 JP 4601267B2 JP 2003176274 A JP2003176274 A JP 2003176274A JP 2003176274 A JP2003176274 A JP 2003176274A JP 4601267 B2 JP4601267 B2 JP 4601267B2
Authority
JP
Japan
Prior art keywords
black
photosensitive
black matrix
composition
carbon black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2003176274A
Other languages
Japanese (ja)
Other versions
JP2005010604A (en
Inventor
佐々木  寛
和則 山田
港  浩一
健 糸井
瑞仁 谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toyo Ink SC Holdings Co Ltd
Toppan Inc
Original Assignee
Toyo Ink SC Holdings Co Ltd
Toppan Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Ink SC Holdings Co Ltd, Toppan Inc filed Critical Toyo Ink SC Holdings Co Ltd
Priority to JP2003176274A priority Critical patent/JP4601267B2/en
Priority to KR1020040044347A priority patent/KR101072425B1/en
Priority to TW093117595A priority patent/TWI287694B/en
Priority to CNB2004100600327A priority patent/CN1329749C/en
Publication of JP2005010604A publication Critical patent/JP2005010604A/en
Application granted granted Critical
Publication of JP4601267B2 publication Critical patent/JP4601267B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は、液晶の表示装置または固体撮像素子等と組み合わせて用いるカラーフィルタのブラックマトリックスの製造に用いられる感光性黒色組成物、それを用いたブラックマトリックス基板およびカラーフィルタに関する。
【0002】
【従来の技術】
カラーフィルタの赤、緑、青のフィルタセグメントの隙間部分には、コントラスト向上を目的として、遮光性を有するブラックマトリックスと呼ばれる格子状の黒色パターンを形成するのが一般的である。
従来、ブラックマトリックスは、クロム、ニッケル等の金属の薄膜で形成されていたが、表示品位およびコストの点から、カーボンブラック等の黒色顔料または数種類の顔料を混合して黒色にした顔料を分散した感光性黒色組成物を用いて形成する検討がなされている。感光性黒色組成物を用いて形成されるブラックマトリックスは、表面の光の反射率が低く、製造工程の短縮化が可能で、大型のカラーフィルタの生産が可能なことから、クロム等の金属材料を用いて形成されるブラックマトリックスより優れた点が多い。
【0003】
しかし、感光性黒色組成物を用いてフォトリソグラフィ法でブラックマトリックスを形成しようとする場合、高遮光性を得るために多量のカーボンブラック等の黒色顔料を組成物中に配合する必要があるが、顔料含有量が高くなる程、顔料を均一に分散させることが困難になり、感光性黒色組成物の経時粘度増加といった分散安定性の低下を生じる問題があった。また、遮光性が高くなるにつれ感度が著しく低下し、活性エネルギー線の照射を行っても硬化塗膜が得られにくくなり、充分な硬化塗膜を得るには、より多くの露光量が必要となり生産性の低下、ブラックマトリックス形状の劣化を招く点で問題があった。
【0004】
このような問題を解決するため、ブラックマトリックス形成用組成物に、下記一般式(B)で示される色素誘導体が配合されていた(例えば、特許文献1参照。)。
一般式(B)
【化3】

Figure 0004601267
[Qは有機色素残基、X1は水素原子またはカルボキシル基、スルホン酸基、X2は以下に示す置換基、i, jはそれぞれ独立に1〜4の整数を示す。
【化4】
Figure 0004601267
1、R2はそれぞれ独立に水素原子または置換基を有していてもよいアルキル基、アリール基もしくは複素環残基、Yは水素原子、ハロゲン原子、−NO2、−NH2もしくは−SO3H、kは1〜4までの整数、nは1〜4までの整数、Aは下記一般式で示される2価の結合基
【化5】
Figure 0004601267
1は、直接結合、−CONH−R3−、−SO2NH−R3−、もしくは−CH2NHCOCH3−R3−、Z2は−NH−もしくは−O−、Z3は水酸基、アルコキシ基もしくは下記一般式で示される置換基を示す。
【化6】
Figure 0004601267
またはiが1の場合−NH−Z1−Qであってもよい。]
【0005】
【特許文献1】
特開平3-153780号公報
【0006】
【発明が解決しようとする課題】
しかし、一般式(B)で示される色素誘導体を含む感光性黒色組成物は、耐熱性、耐薬品性等において優れた特性を示すが、分散安定性、感度、ブラックマトリックス形状、基板に対する密着性、遮光性に関しては要求性能を満たすことはできなかった。
そこで、本発明は、耐熱性、耐薬品性等において優れた特性を示し、さらに分散安定性、感度、ブラックマトリックス形状、基板に対する密着性、遮光性にも優れる感光性黒色組成物、それを用いたブラックマトリックス基板およびカラーフィルタの提供を目的とする。
【0007】
【課題を解決するための手段】
本発明における感光性黒色組成物は、比表面積が50〜200m2/gであるカーボンブラック、フタロシアニン系色素誘導体、アントラキノン系色素誘導体およびベンズイミダゾロン系色素誘導体からなる群から選ばれる下記一般式(A)で示される色素誘導体、及びエチレン性不飽和化合物を含有することを特徴とする感光性黒色組成物である。
一般式(A)
【化7】
Figure 0004601267
(式中、Qはフタロシアニン系、アントラキノン系またはベンズイミダゾロン系有機色素残基、Xは直接結合、−CONH−Y2−、−SO2NH−Y2−、または−CH2NHCOCH2NH−Y2−(但し、Y2は置換基を有してもよいアルキレン基またはアリール基を表す。)、
1は−NH−または−O−、Zは水酸基、アルコキシ基、下記一般式で示される置換基、またはnが1の場合には−NH−X−Q、
【化8】
Figure 0004601267
(式中、Y3は−NH−または−O−)、
1およびR2は、それぞれ独立に置換もしくは無置換のアルキル基、またはR1とR2とで形成される少なくとも窒素原子を含むヘテロ環、mは1から6の整数、nは1から4の整数を表す。)
【0008】
本発明における感光性黒色組成物において、カーボンブラックのフタル酸ジブチルの吸油量は120cc/100g以下であることが好ましく、カーボンブラックの平均1次粒子径は20〜50nmであることが好ましい。
また、本発明におけるブラックマトリックス基板は、上記感光性黒色組成物から形成されているブラックマトリックスを具備するものであり、ブラックマトリックスの乾燥膜厚1μmあたりの光学濃度は3.0以上であることが好ましい。
さらに、本発明におけるカラーフィルタは、上記ブラックマトリックス基板上に、黒色以外の少なくとも2色のフィルタセグメントが形成されているカラーフィルタである。
【0009】
【発明の実施の形態】
まず、感光性黒色組成物について説明する。
感光性黒色組成物は、比表面積が50〜200m2/gであるカーボンブラック、フタロシアニン系色素誘導体、アントラキノン系色素誘導体およびベンズイミダゾロン系色素誘導体からなる群から選ばれる上記一般式(A)で示される色素誘導体、及びエチレン性不飽和化合物を含有する組成物である。
感光性黒色組成物に含有されるカーボンブラックは、遮光性を有する黒色顔料であり、市販のカーボンブラックとしては、例えば、三菱化学(株)製#260、#25、#30、#32、#33、#40、#44、#45、#45L、#47、#50、#52、MA7、MA8、MA11、MA100、MA100R、MA100S、MA230、DEGUSSA社製 Printex L, Printex P, Printex 30, Printex 35, Printex 40, Printex 45, Printex 55, Printex 60, Printex 300, Printex 350, Special Black 4, Special Black 350, Special Black 550等が挙げられる。カーボンブラックは、1種を単独で使用しても、2種以上を混合して使用してもよい。
【0010】
カーボンブラックとしては、ブラックマトリックスの形状の観点から、比表面積が50〜200m2/gであるものを用いる。比表面積が50 m2/g未満のカーボンブラックを用いる場合には、ブラックマトリックス形状の劣化を引き起こし、200 m2/gより大きいカーボンブラックを用いる場合には、カーボンブラックに一般式(A)で示される色素誘導体が過度に吸着してしまい、諸物性を発現させるためには多量の一般式(A)で示される色素誘導体を配合する必要が生じるためである。
【0011】
また、カーボンブラックとしては、感度の点から、フタル酸ジブチル(以下、「DBP」という。)の吸油量が120cc/100g以下のものが好ましく、少なければ少ないものほどより好ましい。
更に、カーボンブラックの平均1次粒子径は、20〜50nmであることが好ましい。平均1次粒子径が20nm未満のカーボンブラックは、高濃度に分散させることが困難であり、経時安定性の良好な感光性黒色組成物が得られ難く、50nmより大きいカーボンブラックを用いると、ブラックマトリックス形状の劣化を招くことがあるためである。
感光性黒色組成物中のカーボンブラックの含有量は、組成物の固形分を基準として20〜70重量%であることが好ましく、30〜60重量%であることがより好ましい。カーボンブラックの含有量が20重量%未満の場合は充分な遮光性が得られず、70重量%より多い場合は分散安定性が得られ難く、感度の低下を招き、ブラックマトリックスの形成が困難になる可能性がある。
【0012】
感光性黒色組成物に含有される色素誘導体は、フタロシアニン系色素誘導体、アントラキノン系色素誘導体およびベンズイミダゾロン系色素誘導体からなる群から選ばれる一般式(A)で示されるものであり、カーボンブラックをエチレン性不飽和化合物中に分散させる働きをする。一般式(A)で示される色素誘導体としては、例えば、下記一般式(1)〜(10)で示される色素誘導体が挙げられる。
【化9】
Figure 0004601267
【0013】
【化10】
Figure 0004601267
【0014】
【化11】
Figure 0004601267
【0015】
一般式(A)で示される色素誘導体を構成する有機色素としては、フタロシアニン系、アントラキノン系、ベンズイミダゾロン系の有機顔料または染料が挙げられる。
【0016】
一般式(A)で示される色素誘導体は、1種を単独で使用しても、2種以上を混合して使用してもよい。
一般式(A)で示される色素誘導体の含有量は、カーボンブラック100重量部に対して0.1〜30重量部であることが好ましく、0.5〜20重量部であることがより好ましい。色素誘導体の含有量が0.1重量部より少ない場合は、カーボンブラックを分散する効果が充分に発揮されず、30重量部より多い場合は、カーボンブラックの分散が不安定になるため好ましくない。
【0017】
感光性黒色組成物に含有されるエチレン性不飽和化合物は、エチレン性不飽和二重結合を1個または2個以上有する化合物であり、モノマー、オリゴマー、感光性樹脂を用いることができる。モノマーとしては、例えば、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート等が挙げられる。また、オリゴマーとしては、エポキシ(メタ)アクリレート、ウレタン(メタ)アクリレート、エステル(メタ)アクリレート等が挙げられ、感光性樹脂としては、ポリエステル、ポリウレタン、エポキシ樹脂、アクリル樹脂等に公知の方法でエチレン性不飽和二重結合を導入したものが挙げられる。
エチレン性不飽和化合物は、1種を単独で使用しても、2種以上を混合して使用してもよい。
【0018】
感光性黒色組成物には、該組成物を紫外線照射により硬化してブラックマトリックスを形成する場合には、光重合開始剤を含有させる。光重合開始剤としては、例えば、4−フェノキシジクロロアセトフェノン、4−t−ブチル−ジクロロアセトフェノン、ジエトキシアセトフェノン、1−(4−イソプロピルフェニル)−2−ヒドロキシ−2−メチルプロパン−1オン、1−ヒドロキシシクロヘキシルフェニルケトン、2−ベンジル−2−ジメチルアミノ−1−(4−モルフォリノフェニル)−ブタン−1−オン等のアセトフェノン系光重合開始剤、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンジルジメチルケタール等のベンゾイン系光重合開始剤、ベンゾフェノン、ベンゾイル安息香酸、ベンゾイル安息香酸メチル、4−フェニルベンゾフェノン、ヒドロキシベンゾフェノン、アクリル化ベンゾフェノン、4−ベンゾイル−4’−メチルジフェニルサルファイド等のベンゾフェノン系光重合開始剤、チオキサンソン、2−クロルチオキサンソン、2−メチルチオキサンソン、イソプロピルチオキサンソン、2,4−ジイソプロピルチオキサンソン等のチオキサンソン系光重合開始剤、2,4,6−トリクロロ−s−トリアジン、2−フェニル−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−メトキシフェニル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−トリル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−ピペロニル−−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−−ビス(トリクロロメチル)−6−スチリルs−トリアジン、2−(ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(4−メトキシ−ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−トリクロロメチル−(ピペロニル)−6−トリアジン、2,4−トリクロロメチル(4’−メトキシスチリル)−6−トリアジン等のトリアジン系光重合開始剤、カルバゾール系光重合開始剤、イミダゾール系光重合開始剤等が挙げられる。上記光重合開始剤は、1種を単独で、あるいは2種以上を混合して用いられる。
【0019】
また、感光性黒色組成物には、増感剤を含有させてもよい。増感剤としては、例えば、α−アシロキシエステル、アシルフォスフィンオキサイド、メチルフェニルグリオキシレート、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、エチルアンスラキノン、4,4’−ジエチルイソフタロフェノン、3,3’,4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、4,4’−ジエチルアミノベンゾフェノン等が挙げられる。上記増感剤は、1種を単独で、あるいは2種以上を混合して用いられる。
【0020】
さらに、感光性黒色組成物には、該組成物をアルカリ現像型とするため、アルカリ可溶性樹脂を含有させることができる。また、感光性黒色組成物には、耐熱性や密着性の付与等の目的に応じて、アルカリ可溶性樹脂と共に、アルカリ可溶性を有しない樹脂を含有させることもできる。
アルカリ可溶性樹脂としては、例えば、(メタ)アクリル酸共重合体やスチレン−無水マレイン酸共重合体、カルボキシル基を有するポリエステル樹脂等が挙げられる。
【0021】
アルカリ可溶性樹脂は、塗膜の耐熱性や耐溶剤性、耐薬品性の付与など種々の目的に応じて2種以上の樹脂を組み合わせて用いることもできる。
アルカリ可溶性樹脂の含有量は、感光性黒色組成物の固形分を基準として3〜70重量%であることが好ましく、5〜60重量%であることがより好ましい。アルカリ可溶性樹脂の含有量が3重量%未満ではアルカリ現像性が低くなり、70重量%を越えると感光性黒色組成物の硬化性や、ブラックマトリックスの形成に用いる場合には遮光性が低くなる。
【0022】
感光性黒色組成物には、カーボンブラックを充分に分散させ、所望の膜厚のブラックマトリックスを形成するために溶剤を含有させることができる。溶剤としては、例えばシクロヘキサノン、エチルセロソルブアセテート、ブチルセロソルブアセテート、1−メトキシ−2−プロピルアセテート、ジエチレングリコールジメチルエーテル、エチルベンゼン、エチレングリコールジエチルエーテル、キシレン、エチルセロソルブ、メチル−nアミルケトン、プロピレングリコールモノメチルエーテル、トルエン、メチルエチルケトン、酢酸エチル、メタノール、エタノール、イソプロピルアルコール、ブタノール、イソブチルケトン、石油系溶剤等が挙げられ、これらを単独もしくは混合して用いる。
【0023】
感光性黒色組成物には、塗工性向上、感度の向上、密着性の向上などを目的として、連鎖移動剤、界面活性剤、シランカップリング剤、他の添加剤などを添加しても良い。
感光性黒色組成物は、カーボンブラック、一般式(A)で示される色素誘導体、エチレン性不飽和化合物、および必要に応じて光重合開始剤、アルカリ可溶性樹脂、溶剤、その他の添加剤を混合し、三本ロールミル、二本ロールミル、サンドミル、ニーダー、アトライター等の各種分散装置を用いて分散することにより製造することができる。
感光性黒色組成物は、遠心分離、焼結フィルタ、メンブレンフィルタ等の手段にて、5μm以上の粗大粒子、好ましくは1μm以上の粗大粒子、さらに好ましくは0.5μm以上の粗大粒子および混入した塵の除去を行うことが好ましい。
【0024】
次に、ブラックマトリックス基板について説明する。
ブラックマトリックス基板は、ガラス板等の透明基板上に、スピンコート、スリットコート、ロールコート等の塗布方法により感光性黒色組成物を塗布したのち、フォトマスクを介して組成物塗布面側から活性エネルギー線を照射し、溶剤またはアルカリ現像液に漬浸するかスプレーなどにより現像液を噴霧して未照射部、すなわち未硬化部を除去して現像を行い、所望の形状のブラックマトリックスを形成することにより作成される。
【0025】
感光性黒色組成物の塗布膜厚は、0.2〜5μm(乾燥時)の範囲であることが好ましく、塗工性と遮光性のバランス取りが容易な0.5〜2μmの範囲であることがより好ましい。
また、ブラックマトリックスの乾燥膜厚1μmあたりの光学濃度は、高遮光性の観点から、3.0以上であることが好ましい。光学濃度は、高いほど好ましいが、活性エネルギー線が紫外線、可視光である場合に硬化塗膜が得られにくくなることから、概ね4.5以下が望ましい。
【0026】
アルカリ現像液としては、炭酸ナトリウム、水酸化ナトリウム等の水溶液が使用され、ジメチルベンジルアミン、トリエタノールアミン等の有機アルカリを用いることもできる。また、現像液には、消泡剤や界面活性剤を添加することもできる。
なお、活性エネルギー線による露光感度を上げるために、感光性黒色組成物を塗布乾燥後、水溶性あるいはアルカリ可溶性樹脂、例えばポリビニルアルコールや水溶性アクリル樹脂等を塗布乾燥し酸素による重合阻害を防止する膜を形成した後、組成物塗布面側から活性エネルギー線を照射することもできる。
【0027】
活性エネルギー線としては、電子線、紫外線、400〜500nmの可視光を使用することができる。組成物塗布面側から照射する電子線の線源には、熱電子放射銃、電界放射銃等を使用することができる。また、紫外線および400〜500nmの可視光の線源(光源)には、例えば、高圧水銀灯、超高圧水銀灯、メタルハライド灯、ガリウム灯、キセノン灯、カーボンアーク灯等を使用することができる。具体的には、点光源であること、輝度が安定であることから、超高圧水銀ランプ、キセノン水銀ランプが用いられることが多い。組成物塗布面側から照射する活性エネルギー線量は、5〜1000mJの範囲で適時設定できるが、工程上管理しやすい20〜300mJの範囲であることが好ましい。
【0028】
最後に、カラーフィルタについて説明する。
カラーフィルタは、上記ブラックマトリックス基板上に、黒以外の少なくとも2色のフィルタセグメントが形成されているものである。フィルタセグメントの色は、青色、緑色、赤色、シアン、エロー、マゼンタ、橙色、紫色などから2〜6色程度選択される。同色系の色で、濃度の違うフィルタセグメントが形成されていてもよい。
ブラックマトリックス基板上へのフィルタセグメントの形成法としては、グラビアオフセット印刷法、水無しオフセット印刷法、シルクスクリーン印刷法、溶剤現像型あるいはアルカリ現像型着色レジストを用いるフォトリソグラフィー法、コロイド粒子の電気泳動により着色材を透明導電膜の上に電着形成する電着法、転写ベースシートの表面に予め形成したフィルタセグメント層をブラックマトリックス基板上に転写させる転写法等が挙げられる。
【0029】
印刷法は、印刷と乾燥を繰り返すだけでパターン化ができるため、カラーフィルタの製造法としては、低コストで量産性に優れている。さらに、印刷技術の発展により高い寸法精度および平滑度を有する微細パターンの印刷を行うことができる。印刷法によりカラーフィルタを製造する場合には、印刷機上でのインキの流動性の制御が重要であり、分散剤や体質顔料によるインキ粘度の調整を行うこともできる。
溶剤現像型あるいはアルカリ現像型着色レジストを用いるフォトリソグラフィー法は、ブラックマトリックス基板上に、スピンコート、スリットコート、ロールコート等の塗布方法により着色レジストを塗布し、次いでフォトマスクを介して紫外線露光を行い、未露光部を溶剤またはアルカリ現像液で洗い流して所望のパターンを形成したのち、同様の操作を他の色について繰り返してカラーフィルタを製造する方法である。この製造法は、上記印刷法より精度の高いカラーフィルタが製造できる。
【0030】
着色レジストは、本発明における感光性黒色組成物に含有されるカーボンブラックの代わりに、所望の色の着色剤を含有するレジストであるが、一般式(A)で示される色素誘導体は必ずしも含有しなくてもよい。着色剤としては、各種の耐性に優れた着色剤が使用されるが、耐光性、耐熱性や耐溶媒性の観点から顔料を使用することが好ましく、光吸収能の大きさから有機顔料を使用することが特に好ましい。代表的な顔料の具体例をカラーインデックス(CI)ナンバーで示す。
【0031】
イエローの着色剤としては、ピグメントイエロー12,13,14,20,24,83,86,93,94,109,110,117,125,137,138,139,147,148,153,154,166,173等が挙げられる。
橙色の着色剤としては、ピグメントオレンジ13,31,36,38,40,42,43,51,55,59,61,64,65等が挙げられる。
赤色およびマゼンタの着色剤としては、ピグメントレッド9,97,122,123,144,149,166,168,177,190,192,215,216,224,254,255等が挙げられる。
【0032】
紫色の着色剤としては、ピグメントバイオレット19,23,29,32,33,36,37,38等が挙げられる。
青色およびシアンの着色剤としては、ピグメントブルー15(15,15:1,15:2,15:3,15:4、15:6等)、21、22,60,64等が挙げられる。
緑色の着色剤としては、ピグメントグリーン7,10,36,47等が挙げられる。
これらの着色剤は、所望の色を得るために2種以上を組み合わせて用いてもよい。
【0033】
【実施例】
以下、本発明を実施例に基づいて具体的に説明する。なお、実施例中、「部」および「%」は、「重量部」および「重量%」をそれぞれ表す。
[アクリル樹脂溶液の調製]
反応容器にシクロヘキサノン800部を入れ、容器に窒素ガスを注入しながら100℃に加熱して、同温度でメタクリル酸60.0部、メタクリル酸ブチル65.0部、メタクリル酸メチル65.0部、スチレン60.0部、及びアゾビスイソブチロニトリル10.0部の混合物を1時間かけて滴下し、更に100℃で3時間反応させた後、アゾビスイソブチロニトリル2.0部をシクロヘキサノン50部で溶解させたものを添加し、更に100℃で1時間反応を続けて樹脂溶液を合成した。室温まで冷却した後、樹脂溶液約2gをサンプリングして180℃で20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20%となるようにシクロヘキサノンを添加してアクリル樹脂溶液を調製した。尚、アクリル樹脂の重量平均分子量は40000であった。
【0034】
[カーボンブラック分散体の調製]
下記の実施例および比較例に記載したカーボンブラックおよび色素誘導体を、上記アクリル樹脂溶液24部、シクロヘキサノン40部と均一に混合し、直径1mmのガラスビーズを用いてサンドミルにて5時間分散することによりカーボンブラック分散体を調製した。実施例および比較例に使用したカーボンブラックの物性値を表1に示す。
【0035】
【表1】
Figure 0004601267
【0036】
【化12】
Figure 0004601267
【0037】
(実施例1)
・カーボンブラック(三菱化学社製「#40」) 10.0部
・色素誘導体▲1▼ 0.5部
(実施例2)
・カーボンブラック(三菱化学社製「#260」) 8.0部
・色素誘導体▲2▼ 0.3部
(実施例3)
・カーボンブラック(三菱化学社製「MA77」) 12.0部
・色素誘導体▲3▼ 1.0部
【0038】
(比較例1)
・カーボンブラック(CABOT社製「ブラックパールズ800」) 8.0部
・色素誘導体▲1▼ 0.2部
(比較例2)
・カーボンブラック(CABOT社製「MONARCH120」) 10.0部
・色素誘導体▲2▼ 0.8部
【0039】
[カーボンブラック分散体の経時安定性評価]
カーボンブラック分散体の分散直後の粘度と40℃で7日間保存後の粘度を比較し、経時安定性を評価した。結果を表2に示す。
[感光性黒色組成物の調製]
カーボンブラック分散体60部、トリメチロールプロパントリアクリレート(新中村化学社製「NKエステルATMPT」)4.3部、光重合開始剤(チバガイギー社製「イルガキュア907」)1.4部、増感剤(保土ヶ谷化学社製「EAB-F」)0.2部、及びシクロヘキサノン21.6部の混合物を均一に攪拌混合した後、1μmのフィルターで濾過して感光性黒色組成物を調製した。得られた感光性黒色組成物について、感度、ブラックマトリックス形状、ガラス密着性、光学濃度を下記の方法で評価した。結果を表2に示す。
【0040】
[感度]
感光性黒色組成物をスピンコート法により10cm×10cmのガラス基板に塗工した後、70℃で15分の乾燥により乾燥膜厚1μmの塗膜を作成した。その後、超高圧水銀ランプを用い、フォトマスクを介して紫外線を100mJ/cm2露光した。次いで、炭酸ナトリウム水溶液を用いて未露光部をスプレー現像した後、イオン交換水で洗浄し未露光部を取り除き、露光部分の現像後の膜厚を測定した。
[ブラックマトリックス形状]
ブラックマトリックス基板を上記方法にて作成した。露光部分に形成されたブラックマトリックス形状の直線性の良否を光学顕微鏡により観察して評価を行った。
【0041】
[ガラス密着性]
感光性黒色組成物を上記方法によりガラス基板に塗工し、超高圧水銀ランプを用い、フォトマスクを介して紫外線を300mJ/cm2露光した。次いで、炭酸ナトリウム水溶液を用いて未露光部をスプレー現像した後、イオン交換水で洗浄し未露光部を取り除き、230℃で1時間加熱した。次いでJIS K5400に準じた碁盤目付着性試験方法により塗膜のガラス密着性を評価し、碁盤目100個中の剥離個数を数えた。
[光学濃度]
感光性黒色組成物を上記方法によりガラス基板に塗工した後、230℃で1時間加熱した。このようにして得られた感光性黒色組成物塗工基板の光学濃度(OD)を、マクベス濃度計(GRETAG D200-II)により測定し、膜厚1.0μmにおける光学濃度(OD)を求めた。
【0042】
【表2】
Figure 0004601267
【0043】
Figure 0004601267
【0044】
表2に示すように、比表面積が50〜200m2/gであるカーボンブラックを用いない場合には、カーボンブラック分散体の経時安定性、感度が得られず、ブラックマトリックスの形状不良を招き、ガラス密着性が得られなかった。これに対して、比表面積が50〜200m2/gであるカーボンブラックを用いた場合には、カーボンブラック分散体の経時安定性が良好で、感度に優れ、ブラックマトリックス形状、ガラス密着性が良好であった。
【0045】
【発明の効果】
本発明により、高濃度に、安定してカーボンブラックを分散することができるようになった。また、本発明の感光性黒色組成物は、経時安定性に優れ、高感度化が達成されており、本発明の感光性黒色組成物を用いることにより、ブラックマトリックス形状、ガラス密着性、光学濃度ともに良好であり、ブラックマトリックスを構成する際に要求される性能を備えているブラックマトリックス基板が得られるようになった。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a photosensitive black composition used for producing a black matrix of a color filter used in combination with a liquid crystal display device or a solid-state imaging device, a black matrix substrate and a color filter using the same.
[0002]
[Prior art]
In order to improve contrast, a lattice-like black pattern called a black matrix having a light shielding property is generally formed in a gap portion between the red, green, and blue filter segments of the color filter.
Conventionally, a black matrix was formed of a thin film of metal such as chromium or nickel, but from the viewpoint of display quality and cost, a black pigment such as carbon black or a pigment made black by mixing several kinds of pigments was dispersed. Studies have been made to form a photosensitive black composition. The black matrix formed using the photosensitive black composition has low surface light reflectance, can shorten the manufacturing process, and can produce large color filters. There are many advantages over the black matrix formed using.
[0003]
However, when a black matrix is to be formed by photolithography using a photosensitive black composition, a large amount of black pigment such as carbon black needs to be blended in the composition in order to obtain high light shielding properties. The higher the pigment content, the more difficult it is to disperse the pigment uniformly, and there is a problem in that the dispersion stability decreases, such as an increase in viscosity over time of the photosensitive black composition. In addition, as the light-shielding property increases, the sensitivity decreases remarkably, and it becomes difficult to obtain a cured coating film even after irradiation with active energy rays, and a larger amount of exposure is required to obtain a sufficient cured coating film. There was a problem in that the productivity decreased and the black matrix shape deteriorated.
[0004]
In order to solve such a problem, a pigment derivative represented by the following general formula (B) was blended in the black matrix forming composition (for example, see Patent Document 1).
General formula (B)
[Chemical Formula 3]
Figure 0004601267
[Q is an organic dye residue, X 1 Is a hydrogen atom or carboxyl group, sulfonic acid group, X 2 Is a substituent shown below, and i and j each independently represents an integer of 1 to 4.
[Formula 4]
Figure 0004601267
R 1 , R 2 Are each independently a hydrogen atom or an optionally substituted alkyl group, aryl group or heterocyclic residue, Y is a hydrogen atom, a halogen atom, -NO 2 , -NH 2 Or -SO Three H and k are integers from 1 to 4, n is an integer from 1 to 4, A is a divalent linking group represented by the following general formula
[Chemical formula 5]
Figure 0004601267
Z 1 Is a direct bond, -CONH-R Three -, -SO 2 NH-R Three -Or -CH 2 NHCOCH Three -R Three -, Z 2 Is —NH— or —O—, Z Three Represents a hydroxyl group, an alkoxy group or a substituent represented by the following general formula.
[Chemical 6]
Figure 0004601267
Or when i is 1 -NH-Z 1 -Q may be sufficient. ]
[0005]
[Patent Document 1]
Japanese Unexamined Patent Publication No. 3-153780
[0006]
[Problems to be solved by the invention]
However, the photosensitive black composition containing the dye derivative represented by the general formula (B) exhibits excellent properties in heat resistance, chemical resistance, etc., but dispersion stability, sensitivity, black matrix shape, adhesion to the substrate. Regarding the light shielding property, the required performance could not be satisfied.
Accordingly, the present invention provides a photosensitive black composition that exhibits excellent characteristics in heat resistance, chemical resistance, etc., and also has excellent dispersion stability, sensitivity, black matrix shape, adhesion to a substrate, and light shielding properties, and uses the same. An object of the present invention is to provide a black matrix substrate and a color filter.
[0007]
[Means for Solving the Problems]
The photosensitive black composition in the present invention has a specific surface area of 50 to 200 m. 2 Carbon black which is / g, Selected from the group consisting of phthalocyanine dye derivatives, anthraquinone dye derivatives, and benzimidazolone dye derivatives A photosensitive black composition comprising a dye derivative represented by the following general formula (A) and an ethylenically unsaturated compound.
Formula (A)
[Chemical 7]
Figure 0004601267
(Where Q is Phthalocyanine, anthraquinone or benzimidazolone Organic dye residue, X is a direct bond, -CONH-Y 2 -, -SO 2 NH-Y 2 -, Or -CH 2 NHCOCH 2 NH-Y 2 -(However, Y 2 Represents an alkylene group or an aryl group which may have a substituent. ),
Y 1 Is —NH— or —O—, Z is a hydroxyl group, an alkoxy group, a substituent represented by the following general formula, or when n is 1, —NH—XQ,
[Chemical 8]
Figure 0004601267
(Where Y Three Is —NH— or —O—),
R 1 And R 2 Each independently represents a substituted or unsubstituted alkyl group, or R 1 And R 2 And at least a nitrogen atom containing a nitrogen atom, m represents an integer of 1 to 6, and n represents an integer of 1 to 4. )
[0008]
In the photosensitive black composition of the present invention, the oil absorption of dibutyl phthalate of carbon black is preferably 120 cc / 100 g or less, and the average primary particle size of carbon black is preferably 20 to 50 nm.
The black matrix substrate in the present invention comprises a black matrix formed from the photosensitive black composition, and the optical density per 1 μm of the dry thickness of the black matrix is preferably 3.0 or more.
Furthermore, the color filter in the present invention is a color filter in which filter segments of at least two colors other than black are formed on the black matrix substrate.
[0009]
DETAILED DESCRIPTION OF THE INVENTION
First, the photosensitive black composition will be described.
The photosensitive black composition has a specific surface area of 50 to 200 m. 2 Carbon black which is / g, Selected from the group consisting of phthalocyanine dye derivatives, anthraquinone dye derivatives, and benzimidazolone dye derivatives It is a composition containing the pigment derivative represented by the general formula (A) and an ethylenically unsaturated compound.
Carbon black contained in the photosensitive black composition is a black pigment having a light-shielding property. Examples of commercially available carbon black include # 260, # 25, # 30, # 32, # 32 manufactured by Mitsubishi Chemical Corporation. 33, # 40, # 44, # 45, # 45L, # 47, # 50, # 52, MA7, MA8, MA11, MA100, MA100R, MA100S, MA230, manufactured by DEGUSSA Printex L, Printex P, Printex 30, Printex 35, Printex 40, Printex 45, Printex 55, Printex 60, Printex 300, Printex 350, Special Black 4, Special Black 350, Special Black 550, and the like. Carbon black may be used individually by 1 type, or 2 or more types may be mixed and used for it.
[0010]
Carbon black has a specific surface area of 50 to 200m from the viewpoint of the shape of the black matrix. 2 Use / g. Specific surface area 50 m 2 If carbon black less than / g is used, it will cause deterioration of the black matrix shape and 200 m 2 When carbon black larger than / g is used, the dye derivative represented by the general formula (A) is excessively adsorbed on the carbon black, and a large amount of the general formula (A) is required to develop various physical properties. This is because it is necessary to add a pigment derivative.
[0011]
Carbon black preferably has an oil absorption of 120 cc / 100 g or less of dibutyl phthalate (hereinafter referred to as “DBP”) from the viewpoint of sensitivity.
Further, the average primary particle size of carbon black is preferably 20 to 50 nm. Carbon black having an average primary particle size of less than 20 nm is difficult to disperse at a high concentration, and it is difficult to obtain a photosensitive black composition having good stability over time. This is because the matrix shape may be deteriorated.
The content of carbon black in the photosensitive black composition is preferably 20 to 70% by weight, more preferably 30 to 60% by weight, based on the solid content of the composition. When the carbon black content is less than 20% by weight, sufficient light-shielding properties cannot be obtained, and when it is more than 70% by weight, it is difficult to obtain dispersion stability, resulting in a decrease in sensitivity and making it difficult to form a black matrix. There is a possibility.
[0012]
The pigment derivative contained in the photosensitive black composition is Selected from the group consisting of phthalocyanine dye derivatives, anthraquinone dye derivatives, and benzimidazolone dye derivatives It is represented by the general formula (A) and functions to disperse carbon black in the ethylenically unsaturated compound. Examples of the dye derivative represented by the general formula (A) include dye derivatives represented by the following general formulas (1) to (10).
[Chemical 9]
Figure 0004601267
[0013]
[Chemical Formula 10]
Figure 0004601267
[0014]
Embedded image
Figure 0004601267
[0015]
Examples of the organic dye constituting the dye derivative represented by the general formula (A) include phthalocyanine-based, anthraquinone-based, and benzimidazolone-based organic pigments or dyes.
[0016]
The pigment derivative represented by the general formula (A) may be used alone or in combination of two or more.
The content of the pigment derivative represented by the general formula (A) is preferably 0.1 to 30 parts by weight, and more preferably 0.5 to 20 parts by weight with respect to 100 parts by weight of carbon black. When the content of the pigment derivative is less than 0.1 parts by weight, the effect of dispersing the carbon black is not sufficiently exhibited, and when it is more than 30 parts by weight, the dispersion of the carbon black becomes unstable, which is not preferable.
[0017]
The ethylenically unsaturated compound contained in the photosensitive black composition is a compound having one or more ethylenically unsaturated double bonds, and monomers, oligomers, and photosensitive resins can be used. Examples of the monomer include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, cyclohexyl (meth) acrylate, polyethylene glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, and pentaerythritol tris. (Meth) acrylate, dipentaerythritol hexa (meth) acrylate, etc. are mentioned. In addition, examples of the oligomer include epoxy (meth) acrylate, urethane (meth) acrylate, ester (meth) acrylate and the like, and examples of the photosensitive resin include polyester, polyurethane, epoxy resin, acrylic resin, and the like by a known method. And those having an unsaturated double bond introduced therein.
An ethylenically unsaturated compound may be used individually by 1 type, or may mix and use 2 or more types.
[0018]
The photosensitive black composition contains a photopolymerization initiator when the composition is cured by ultraviolet irradiation to form a black matrix. Examples of the photopolymerization initiator include 4-phenoxydichloroacetophenone, 4-t-butyl-dichloroacetophenone, diethoxyacetophenone, 1- (4-isopropylphenyl) -2-hydroxy-2-methylpropan-1-one, 1 Acetophenone photopolymerization initiators such as -hydroxycyclohexyl phenyl ketone, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin Benzoin photopolymerization initiators such as isopropyl ether and benzyldimethyl ketal, benzophenone, benzoylbenzoic acid, methyl benzoylbenzoate, 4-phenylbenzophenone, hydroxybenzophenone, acrylated benzophenone, Benzophenone photopolymerization initiators such as benzoyl-4′-methyldiphenyl sulfide, thioxanthones such as thioxanthone, 2-chlorothioxanthone, 2-methylthioxanthone, isopropylthioxanthone, 2,4-diisopropylthioxanthone Photopolymerization initiator, 2,4,6-trichloro-s-triazine, 2-phenyl-4,6-bis (trichloromethyl) -s-triazine, 2- (p-methoxyphenyl) -4,6-bis ( Trichloromethyl) -s-triazine, 2- (p-tolyl) -4,6-bis (trichloromethyl) -s-triazine, 2-piperonyl-4,6-bis (trichloromethyl) -s-triazine, 2, , 4-Bis (trichloromethyl) -6-styryl s-triazine, 2- (naphth-1-yl) -4,6 Bis (trichloromethyl) -s-triazine, 2- (4-methoxy-naphth-1-yl) -4,6-bis (trichloromethyl) -s-triazine, 2,4-trichloromethyl- (piperonyl) -6 -Triazine photoinitiators such as triazine and 2,4-trichloromethyl (4'-methoxystyryl) -6-triazine, carbazole photoinitiators, imidazole photoinitiators and the like. The said photoinitiator is used individually by 1 type or in mixture of 2 or more types.
[0019]
Moreover, you may make a photosensitive black composition contain a sensitizer. Examples of the sensitizer include α-acyloxy ester, acylphosphine oxide, methylphenylglyoxylate, benzyl, 9,10-phenanthrenequinone, camphorquinone, ethylanthraquinone, 4,4′-diethyliso Examples include phthalophenone, 3,3 ′, 4,4′-tetra (t-butylperoxycarbonyl) benzophenone, 4,4′-diethylaminobenzophenone, and the like. The above sensitizers are used alone or in combination of two or more.
[0020]
Further, the photosensitive black composition can contain an alkali-soluble resin in order to make the composition into an alkali development type. In addition, the photosensitive black composition may contain an alkali-soluble resin and a resin that does not have alkali solubility depending on the purpose such as imparting heat resistance or adhesion.
Examples of the alkali-soluble resin include (meth) acrylic acid copolymers, styrene-maleic anhydride copolymers, and polyester resins having a carboxyl group.
[0021]
The alkali-soluble resin can be used in combination of two or more resins according to various purposes such as imparting heat resistance, solvent resistance, and chemical resistance of the coating film.
The content of the alkali-soluble resin is preferably 3 to 70% by weight, more preferably 5 to 60% by weight, based on the solid content of the photosensitive black composition. When the content of the alkali-soluble resin is less than 3% by weight, the alkali developability is low, and when it exceeds 70% by weight, the curability of the photosensitive black composition and the light shielding property when used for forming a black matrix are low.
[0022]
The photosensitive black composition may contain a solvent in order to sufficiently disperse carbon black and form a black matrix having a desired film thickness. Examples of the solvent include cyclohexanone, ethyl cellosolve acetate, butyl cellosolve acetate, 1-methoxy-2-propyl acetate, diethylene glycol dimethyl ether, ethylbenzene, ethylene glycol diethyl ether, xylene, ethyl cellosolve, methyl-n amyl ketone, propylene glycol monomethyl ether, toluene, Examples thereof include methyl ethyl ketone, ethyl acetate, methanol, ethanol, isopropyl alcohol, butanol, isobutyl ketone, petroleum solvent, etc., and these are used alone or in combination.
[0023]
A chain transfer agent, a surfactant, a silane coupling agent, and other additives may be added to the photosensitive black composition for the purpose of improving coatability, improving sensitivity, and improving adhesion. .
The photosensitive black composition is a mixture of carbon black, a dye derivative represented by the general formula (A), an ethylenically unsaturated compound, and, if necessary, a photopolymerization initiator, an alkali-soluble resin, a solvent, and other additives. In addition, it can be produced by dispersing using various dispersing devices such as a three-roll mill, a two-roll mill, a sand mill, a kneader, and an attritor.
The photosensitive black composition is prepared by means of centrifugal separation, sintering filter, membrane filter, or the like, with coarse particles of 5 μm or more, preferably coarse particles of 1 μm or more, more preferably coarse particles of 0.5 μm or more and mixed dust. Is preferably removed.
[0024]
Next, the black matrix substrate will be described.
The black matrix substrate is coated with a photosensitive black composition on a transparent substrate such as a glass plate by a coating method such as spin coating, slit coating, or roll coating, and then activated energy from the composition coating surface side through a photomask. Irradiate the wire, soak in a solvent or alkaline developer, or spray the developer with a spray to remove unirradiated parts, that is, uncured parts, and develop to form a black matrix of the desired shape Created by.
[0025]
The coating thickness of the photosensitive black composition is preferably in the range of 0.2 to 5 μm (when dried), and more preferably in the range of 0.5 to 2 μm, which makes it easy to balance coating properties and light shielding properties.
Further, the optical density per 1 μm of the dry thickness of the black matrix is preferably 3.0 or more from the viewpoint of high light shielding properties. The higher the optical density, the better. However, when the active energy ray is ultraviolet light or visible light, it is difficult to obtain a cured coating film.
[0026]
As the alkali developer, an aqueous solution such as sodium carbonate or sodium hydroxide is used, and an organic alkali such as dimethylbenzylamine or triethanolamine can also be used. Moreover, an antifoamer and surfactant can also be added to a developing solution.
In order to increase the exposure sensitivity by active energy rays, after coating and drying the photosensitive black composition, a water-soluble or alkali-soluble resin such as polyvinyl alcohol or water-soluble acrylic resin is applied and dried to prevent polymerization inhibition by oxygen. After the film is formed, active energy rays can be irradiated from the composition application surface side.
[0027]
As the active energy ray, an electron beam, ultraviolet rays, or visible light of 400 to 500 nm can be used. A thermionic emission gun, a field emission gun, or the like can be used as the electron beam source irradiated from the composition application surface side. For example, a high-pressure mercury lamp, an ultrahigh-pressure mercury lamp, a metal halide lamp, a gallium lamp, a xenon lamp, a carbon arc lamp, or the like can be used as a source (light source) of ultraviolet light and visible light of 400 to 500 nm. Specifically, since it is a point light source and the luminance is stable, an ultrahigh pressure mercury lamp or a xenon mercury lamp is often used. The active energy dose irradiated from the composition coated surface side can be set in a timely manner within a range of 5 to 1000 mJ, but is preferably within a range of 20 to 300 mJ that can be easily managed in the process.
[0028]
Finally, the color filter will be described.
In the color filter, filter segments of at least two colors other than black are formed on the black matrix substrate. The color of the filter segment is selected from about 2 to 6 colors from blue, green, red, cyan, yellow, magenta, orange, purple and the like. Filter segments having the same color system and different densities may be formed.
Filter segment formation on black matrix substrate includes gravure offset printing method, waterless offset printing method, silk screen printing method, photolithographic method using solvent developing type or alkali developing type colored resist, colloidal particle electrophoresis Examples thereof include an electrodeposition method in which a coloring material is electrodeposited on a transparent conductive film, a transfer method in which a filter segment layer previously formed on the surface of a transfer base sheet is transferred onto a black matrix substrate, and the like.
[0029]
Since the printing method can be patterned simply by repeating printing and drying, the color filter manufacturing method is low in cost and excellent in mass productivity. Furthermore, it is possible to print a fine pattern having high dimensional accuracy and smoothness by the development of printing technology. In the case of producing a color filter by a printing method, it is important to control the fluidity of the ink on the printing press, and the ink viscosity can be adjusted with a dispersant or extender pigment.
A photolithography method using a solvent development type or alkali development type colored resist is a method in which a colored resist is applied on a black matrix substrate by a coating method such as spin coating, slit coating, roll coating, and then exposed to ultraviolet rays through a photomask. This is a method for producing a color filter by repeating the same operation for other colors after forming a desired pattern by washing away an unexposed portion with a solvent or an alkali developer. This manufacturing method can manufacture a color filter with higher accuracy than the above printing method.
[0030]
The colored resist is a resist containing a colorant having a desired color instead of the carbon black contained in the photosensitive black composition in the present invention, but does not necessarily contain the dye derivative represented by the general formula (A). It does not have to be. As the colorant, various colorants having excellent resistance are used. However, it is preferable to use a pigment from the viewpoint of light resistance, heat resistance and solvent resistance, and an organic pigment is used because of its light absorption ability. It is particularly preferable to do this. Specific examples of typical pigments are indicated by color index (CI) numbers.
[0031]
Examples of yellow colorants include Pigment Yellow 12, 13, 14, 20, 24, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 153, 154, and 166. , 173 and the like.
Examples of the orange colorant include Pigment Orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, and the like.
Examples of red and magenta colorants include Pigment Red 9, 97, 122, 123, 144, 149, 166, 168, 177, 190, 192, 215, 216, 224, 254, and 255.
[0032]
Examples of purple colorants include Pigment Violet 19, 23, 29, 32, 33, 36, 37, 38, and the like.
Examples of blue and cyan colorants include Pigment Blue 15 (15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6, etc.), 21, 22, 60, 64, and the like.
Examples of the green colorant include Pigment Green 7, 10, 36, 47, and the like.
These colorants may be used in combination of two or more in order to obtain a desired color.
[0033]
【Example】
Hereinafter, the present invention will be specifically described based on examples. In the examples, “parts” and “%” represent “parts by weight” and “% by weight”, respectively.
[Preparation of acrylic resin solution]
Put 800 parts of cyclohexanone in a reaction vessel, heat to 100 ° C while injecting nitrogen gas into the vessel, and at the same temperature, 60.0 parts of methacrylic acid, 65.0 parts of butyl methacrylate, 65.0 parts of methyl methacrylate, 60.0 parts of styrene, and azo A mixture of 10.0 parts of bisisobutyronitrile was added dropwise over 1 hour, and further reacted at 100 ° C. for 3 hours. Then, 2.0 parts of azobisisobutyronitrile dissolved in 50 parts of cyclohexanone was added. The reaction was continued at 100 ° C. for 1 hour to synthesize a resin solution. After cooling to room temperature, sample approximately 2 g of the resin solution, heat and dry at 180 ° C. for 20 minutes to measure the nonvolatile content, and add cyclohexanone to the previously synthesized resin solution so that the nonvolatile content is 20%. An acrylic resin solution was prepared. The weight average molecular weight of the acrylic resin was 40000.
[0034]
[Preparation of carbon black dispersion]
Carbon black and pigment derivatives described in the following examples and comparative examples were mixed uniformly with 24 parts of the acrylic resin solution and 40 parts of cyclohexanone, and dispersed in a sand mill for 5 hours using glass beads having a diameter of 1 mm. A carbon black dispersion was prepared. Table 1 shows the physical property values of the carbon black used in Examples and Comparative Examples.
[0035]
[Table 1]
Figure 0004601267
[0036]
Embedded image
Figure 0004601267
[0037]
(Example 1)
・ Carbon black (Mitsubishi Chemical "# 40") 10.0 parts
・ Dye derivative (1) 0.5 part
(Example 2)
・ Carbon black (Mitsubishi Chemical "# 260") 8.0 parts
・ Dye derivative (2) 0.3 parts
(Example 3)
Carbon black (Mitsubishi Chemical "MA77") 12.0 parts
・ Dye derivative (3) 1.0 part
[0038]
(Comparative Example 1)
・ Carbon black (CABOT "Black Pearls 800") 8.0 parts
・ Dye derivative (1) 0.2 parts
(Comparative Example 2)
・ Carbon black (CABOT "MONARCH120") 10.0 parts
・ Dye derivative (2) 0.8 parts
[0039]
[Stability evaluation of carbon black dispersion over time]
The viscosity immediately after dispersion of the carbon black dispersion was compared with the viscosity after storage at 40 ° C. for 7 days to evaluate the stability over time. The results are shown in Table 2.
[Preparation of photosensitive black composition]
60 parts of carbon black dispersion, 4.3 parts of trimethylolpropane triacrylate (“NK ester ATMPT” manufactured by Shin-Nakamura Chemical Co., Ltd.), 1.4 parts of photopolymerization initiator (“Irgacure 907” manufactured by Ciba Geigy Co.), sensitizer (Hodogaya Chemical Co., Ltd.) A mixture of 0.2 parts of “EAB-F” and 21.6 parts of cyclohexanone was uniformly stirred and mixed, and then filtered through a 1 μm filter to prepare a photosensitive black composition. About the obtained photosensitive black composition, the sensitivity, the black matrix shape, the glass adhesion, and the optical density were evaluated by the following methods. The results are shown in Table 2.
[0040]
[sensitivity]
The photosensitive black composition was applied to a 10 cm × 10 cm glass substrate by spin coating, and then dried at 70 ° C. for 15 minutes to form a coating film having a dry film thickness of 1 μm. Then, using an ultra-high pressure mercury lamp, UV light is emitted through a photomask at 100 mJ / cm 2 Exposed. Subsequently, the unexposed area was spray-developed using an aqueous sodium carbonate solution, then washed with ion-exchanged water to remove the unexposed area, and the film thickness after development of the exposed area was measured.
[Black matrix shape]
A black matrix substrate was prepared by the above method. Evaluation was made by observing the linearity of the black matrix shape formed in the exposed portion with an optical microscope.
[0041]
[Glass adhesion]
The photosensitive black composition is applied to a glass substrate by the above method, and an ultraviolet ray is applied at 300 mJ / cm through a photomask using an ultrahigh pressure mercury lamp. 2 Exposed. Next, the unexposed area was spray-developed using an aqueous sodium carbonate solution, washed with ion-exchanged water to remove the unexposed area, and heated at 230 ° C. for 1 hour. Next, the glass adhesion of the coating film was evaluated by a cross-cut adhesion test method according to JIS K5400, and the number of peels in 100 cross-cuts was counted.
[Optical density]
The photosensitive black composition was applied to a glass substrate by the above method and then heated at 230 ° C. for 1 hour. The optical density (OD) of the photosensitive black composition coated substrate thus obtained was measured with a Macbeth densitometer (GRETAG D200-II), and the optical density (OD) at a film thickness of 1.0 μm was determined.
[0042]
[Table 2]
Figure 0004601267
[0043]
Figure 0004601267
[0044]
As shown in Table 2, the specific surface area is 50-200m 2 When carbon black of / g was not used, the stability over time and sensitivity of the carbon black dispersion could not be obtained, the black matrix was poorly shaped, and the glass adhesion could not be obtained. In contrast, the specific surface area is 50-200m 2 When carbon black of / g was used, the carbon black dispersion had good stability over time, excellent sensitivity, black matrix shape, and good glass adhesion.
[0045]
【The invention's effect】
According to the present invention, carbon black can be stably dispersed at a high concentration. Further, the photosensitive black composition of the present invention has excellent stability over time and high sensitivity has been achieved, and by using the photosensitive black composition of the present invention, the black matrix shape, glass adhesion, optical density Both of them are good, and a black matrix substrate having the performance required for forming a black matrix can be obtained.

Claims (6)

比表面積が50〜200m2/gであるカーボンブラック、フタロシアニン系色素誘導体、アントラキノン系色素誘導体およびベンズイミダゾロン系色素誘導体からなる群から選ばれる下記一般式(A)で示される色素誘導体、及びエチレン性不飽和化合物を含有することを特徴とする感光性黒色組成物。
一般式(A)
Figure 0004601267
(式中、Qはフタロシアニン系、アントラキノン系またはベンズイミダゾロン系有機色素残基、Xは直接結合、−CONH−Y2−、−SO2NH−Y2−、または−CH2NHCOCH2NH−Y2−(但し、Y2は置換基を有してもよいアルキレン基またはアリール基を表す。)、Y1は−NH−または−O−、Zは水酸基、アルコキシ基、下記一般式で示される置換基、またはnが1の場合には−NH−X−Q、
Figure 0004601267
(式中、Y3は−NH−または−O−)、
1およびR2は、それぞれ独立に置換もしくは無置換のアルキル基、またはR1とR2とで形成される少なくとも窒素原子を含むヘテロ環、mは1から6の整数、nは1から4の整数を表す。)
Carbon black having a specific surface area of 50 to 200 m 2 / g, a phthalocyanine dye derivative, an anthraquinone dye derivative and a dye derivative represented by the following general formula (A) selected from the group consisting of a benzimidazolone dye derivative, and ethylene A photosensitive black composition comprising a photosensitive unsaturated compound.
Formula (A)
Figure 0004601267
( Wherein Q is a phthalocyanine-based, anthraquinone-based or benzimidazolone-based organic dye residue, X is a direct bond, —CONH—Y 2 —, —SO 2 NH—Y 2 —, or —CH 2 NHCOCH 2 NH— Y 2 — (wherein Y 2 represents an alkylene group or an aryl group which may have a substituent), Y 1 represents —NH— or —O—, Z represents a hydroxyl group, an alkoxy group, represented by the following general formula Or a substituent when n is 1, -NH-XQ,
Figure 0004601267
Wherein Y 3 is —NH— or —O—.
R 1 and R 2 are each independently a substituted or unsubstituted alkyl group, or a heterocycle containing at least a nitrogen atom formed by R 1 and R 2 , m is an integer of 1 to 6, and n is 1 to 4 Represents an integer. )
カーボンブラックのフタル酸ジブチルの吸油量が120cc/100g以下であることを特徴とする請求項1記載の感光性黒色組成物。  The photosensitive black composition according to claim 1, wherein the oil absorption of dibutyl phthalate of carbon black is 120 cc / 100 g or less. カーボンブラックの平均1次粒子径が20〜50nmであることを特徴とする請求項1または2記載の感光性黒色組成物。  The photosensitive black composition according to claim 1 or 2, wherein the carbon black has an average primary particle size of 20 to 50 nm. 請求項1ないし3いずれか1項に記載の感光性黒色組成物から形成されているブラックマトリックスを具備することを特徴とするブラックマトリックス基板。  A black matrix substrate comprising a black matrix formed from the photosensitive black composition according to any one of claims 1 to 3. ブラックマトリックスの乾燥膜厚1μmあたりの光学濃度が3.6以上4.5以下であることを特徴とする請求項4記載のブラックマトリックス基板。 5. The black matrix substrate according to claim 4, wherein the optical density per 1 [mu] m of the dry thickness of the black matrix is 3.6 or more and 4.5 or less . 請求項4または5記載のブラックマトリックス基板上に、黒色以外の少なくとも2色のフィルタセグメントが形成されていることを特徴とするカラーフィルタ。  6. A color filter, wherein filter segments of at least two colors other than black are formed on the black matrix substrate according to claim 4 or 5.
JP2003176274A 2003-06-20 2003-06-20 Photosensitive black composition, black matrix substrate and color filter using the same Expired - Fee Related JP4601267B2 (en)