JP4343183B2 - ナノスケールθ相アルミナ微粒子の製造方法 - Google Patents
ナノスケールθ相アルミナ微粒子の製造方法 Download PDFInfo
- Publication number
- JP4343183B2 JP4343183B2 JP2006079622A JP2006079622A JP4343183B2 JP 4343183 B2 JP4343183 B2 JP 4343183B2 JP 2006079622 A JP2006079622 A JP 2006079622A JP 2006079622 A JP2006079622 A JP 2006079622A JP 4343183 B2 JP4343183 B2 JP 4343183B2
- Authority
- JP
- Japan
- Prior art keywords
- phase
- fine particles
- alumina
- phase alumina
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、ナノスケールθ相アルミナ微粒子の製造方法であって、θ相アルミナ初期粉末と混合されたベーマイトの比率を制御した後に、少なくとも一つの相変態を行い、粒径が均一で相純度が高いナノスケールθ相アルミナ微粒子を生成する前記方法を提供する。以下の記載において、本発明のナノスケールθ相アルミナ微粒子の製造方法をより詳細かつ完全明確に説明する。
先ず、未処理の工業用θ相アルミナ粉末の粒径及び相同定を、それぞれ透過型電子顕微鏡(Transmission Electron Microscopy:TEM)及びX線回折(X-ray diffraction:XRD)システムで評価した。本発明の実施例において、XRDシステムは、走査速度が毎分4°であり、走査角度(2θ°)は20°から80°の間である。
先ず、約95重量%の工業用θ相アルミナ粉末と約5重量%のベーマイトとの混合物を出発材料に用い、毎分50℃よりも高い加熱速度で1000℃まで加熱した後、1000℃に3分間維持してから、直ちに室温まで急冷した。続いて、得られたアルミナ微粒子を、毎分50℃よりも高い加熱速度で800℃まで加熱した後、800℃に2分間維持してナノスケールθ相アルミナ微粒子を得た。そして、比較例と同じTEM及びXRDシステムを用い、得られたナノスケールθ相アルミナ微粒子の粒径及び相同定を分析した。
先ず、約44重量%の工業用θ相アルミナ粉末と約56重量%のベーマイトとの混合物を出発材料に用い、毎分50℃よりも高い加熱速度で1200℃まで加熱した後、1200℃に4分間維持してから、直ちに室温まで急冷した。続いて、得られたアルミナ微粒子を、毎分50℃よりも高い加熱速度で700℃まで加熱した後、700℃に3分間維持してナノスケールθ相アルミナ微粒子を得た。
先ず、約44重量%の工業用θ相アルミナ粉末と約56重量%のベーマイトとの混合物を出発材料に用い、毎分10℃の加熱速度で1150℃まで加熱した後、1150℃に10分間維持してから直ちに700℃まで急冷し、700℃に4分間維持してナノスケールθ相アルミナ微粒子を得た。
先ず、約40重量%の工業用θ相アルミナ粉末と約60重量%のベーマイトとの混合物を出発材料に用い、毎分20℃の加熱速度で1150℃まで加熱し、1150℃に10分間維持した後に直ちに800℃まで急冷し、800℃に4分間維持してナノスケールθ相アルミナ微粒子を得た。
Claims (3)
- θ相アルミナ粉末とベーマイトとを含むアルミナ混合粉末であって、該アルミナ混合粉末における前記θ相アルミナ粉末の含有量が30から95重量%の間であり、該アルミナ混合粉末における前記ベーマイトのアルミナ当量が5から70重量%の間であるものを提供する工程と、
前記アルミナ混合粉末を空気雰囲内において、毎分50℃よりも高い加熱速度で、600℃から1200℃の間の第1の温度まで加熱した後、前記第1の温度に1分間から10分間の第1の期間維持し、前記アルミナ混合粉末に第1の相変態を発生させてα’相アルミナ微粒子を生成する工程と、
前記α’相アルミナ微粒子を空気雰囲内において毎分50℃よりも高い冷却速度で室温まで急冷し、α’相アルミナ微粒子を毎分50℃よりも高い加熱速度で、500℃から900℃の間の第2の温度まで加熱し、第2の温度に1分間から10分間の第2の期間維持して、前記α’相アルミナ微粒子に少なくとも一つの第2の相変態を発生させ、粒径が30nmから150nmの間のθ相アルミナ微粒子を生成する工程とを含む、θ相アルミナ微粒子の製造方法。 - θ相アルミナ微粒子の直径が、30nmから50nmの間であることを特徴とする、請求項1に記載のθ相アルミナ微粒子の製造方法。
- θ相アルミナ微粒子の直径が、50nmから150nmの間であることを特徴とする、請求項1に記載のθ相アルミナ微粒子の製造方法。