JP4236183B2 - Aluminum alloy clad material for automotive heat exchanger - Google Patents
Aluminum alloy clad material for automotive heat exchanger Download PDFInfo
- Publication number
- JP4236183B2 JP4236183B2 JP2004123992A JP2004123992A JP4236183B2 JP 4236183 B2 JP4236183 B2 JP 4236183B2 JP 2004123992 A JP2004123992 A JP 2004123992A JP 2004123992 A JP2004123992 A JP 2004123992A JP 4236183 B2 JP4236183 B2 JP 4236183B2
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- sacrificial anode
- brazing
- heat exchanger
- clad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、自動車熱交換器用アルミニウム合金クラッド材、とくに、不活性ガス雰囲気中でのフッ化物系フラックスやセシウム化物系フラックスを用いたろう付けにより接合されるエバポレータ、コンデンサ、ラジエータやヒータコアなどのアルミニウム合金製自動車熱交換器用のチューブ材、または当該熱交換器と接続される配管材（押出クラッド管）として好適な自動車熱交換器用アルミニウム合金クラッド材に関する。 The present invention relates to an aluminum alloy clad material for automobile heat exchangers, and in particular, aluminum alloys such as evaporators, capacitors, radiators and heater cores joined by brazing using a fluoride flux or a cesium fluoride flux in an inert gas atmosphere. The present invention relates to an aluminum alloy clad material for an automobile heat exchanger suitable as a tube material for an automobile heat exchanger or a piping material (extruded clad pipe) connected to the heat exchanger.
自動車熱交換器、例えばラジエータは、外面にフィンを有し、内面が作動流体（冷媒）の通路となるチューブおよびヘッダーから構成されている。このような自動車のラジエータまたはヒータコアなどのチューブ材、ヘッダープレート材としては、ＪＩＳ Ａ３００３などのＡｌ−Ｍｎ系合金を芯材とし、芯材の片面にＡｌ−Ｓｉ系合金ろう材をクラッドした二層構造のアルミニウム合金クラッド材、芯材の一方の面にろう材をクラッドし、他方の面にＡｌ−Ｚｎ系合金またはＡｌ−Ｚｎ−Ｍｇ系合金の犠牲陽極材をクラッドした三層構造のアルミニウム合金クラッド材が用いられている。 An automobile heat exchanger, for example, a radiator, includes a tube and a header having fins on the outer surface and the inner surface serving as a passage for a working fluid (refrigerant). As a tube material and header plate material such as a radiator or a heater core of such an automobile, a two-layer in which an Al-Mn alloy alloy such as JIS A3003 is used as a core material and an Al-Si alloy brazing material is clad on one side of the core material. Aluminum alloy clad material with a three-layer structure in which a brazing material is clad on one surface of the core material and a sacrificial anode material of Al-Zn alloy or Al-Zn-Mg alloy is clad on the other surface A clad material is used.
クラッド材のＡｌ−Ｓｉ系ろう材は、アルミニウム合金製熱交換器を製作するとき、チューブとフィンとの接合、チューブとヘッダープレートとの接合、またはクラッド板からろう付けによりチューブを製造する場合のろう付け接合のためにクラッドされている。これらのろう付には、最近では一般にフッ化物フラックスやセシウム化物系フラックスを用いる不活性ガス雰囲気ろう付けが適用される。また、犠牲陽極材は、たとえばチューブの内面側に使用され、作動流体と接して犠牲陽極作用を発揮し、芯材の孔食や隙間腐食の発生を防止する。 When manufacturing an aluminum alloy heat exchanger, the clad Al-Si brazing material is used when a tube is manufactured by joining a tube and a fin, joining a tube and a header plate, or brazing a clad plate. It is clad for brazing. In recent years, inert gas atmosphere brazing using a fluoride flux or a cesium fluoride flux is generally applied to these brazings. The sacrificial anode material is used, for example, on the inner surface side of the tube, and exerts a sacrificial anode action in contact with the working fluid to prevent the occurrence of pitting corrosion and crevice corrosion of the core material.
近年、自動車の軽量化の要請に伴い、自動車熱交換器においても省エネルギー、省資源の観点から構成材料の薄肉化が要請され、チューブ材についても薄肉化が進行している。また、各種熱交換器の製造において、従来は図１に示すように、クラッド板を曲成して溶接により偏平チューブ１とし、これをヘッダープレートに組付けて一体ろう付けを行っていたが、最近では、省エネルギーや作業効率化などの観点から、図２に示すように、クラッド板の両端部が犠牲陽極材と当接するように曲げ加工するだけで、溶接することなくＢ型のチューブ形状２とし、ヘッダープレートに組付けた後、一体ろう付けすることが多くなっており、さらに、図３に示すように、チューブ１内にクラッドフィン材３を装入してろう付けすることにより、チューブの剛性を高める手法も行われている。
In recent years, with the demand for lighter automobiles, automobile heat exchangers are also required to be made thinner from the viewpoint of energy saving and resource saving, and the tube materials are also becoming thinner. Also, in the manufacture of various heat exchangers, conventionally, as shown in FIG. 1, the clad plate is bent and welded to form a flat tube 1, which is assembled to the header plate and integrally brazed. Recently, from the viewpoint of energy saving and work efficiency improvement, as shown in FIG. 2, the B-
しかしながら、チューブ材やフィン材が薄肉であるため、クラッドされるろう材量が少なく、図２、図３のように犠牲陽極材がろう付け面となるものにおいては、ろう付け時、ろう材のろうが十分にまわらず、図２のものにおいては、クラッド板の両端部と犠牲陽極材との当接部（点線囲い部−Ａ部）に接合不良が生じることが少なくない。また、図３のように、チューブ１内にクラッドフィン材３を装入して不活性ガス雰囲気中でろう付けする場合、ろう付け中にチューブ内面の空気が不活性ガスに完全に置換されず残存するため、クラッドフィン材３のろう材が接合部に十分に濡れ広がらず、クラッドフィン材３とチューブ材１内面の犠牲陽極材との接触部（点線囲い部−Ｂ部）の接合が不十分となることがある。
However, since the tube material and the fin material are thin, the amount of brazing material to be clad is small, and in the case where the sacrificial anode material is the brazing surface as shown in FIGS. In the case of FIG. 2, the brazing does not sufficiently occur, and it is not uncommon for poor bonding to occur at the abutting portion (dotted line enclosing portion-A portion) between both ends of the clad plate and the sacrificial anode material. Further, as shown in FIG. 3, when the
チューブの内面側（犠牲陽極材面）にさらにろう材をクラッドし、接合部をろう対ろうの組み合わせとすることにより上記の問題を解決することが考えられるが、ろう付け時にろう材から犠牲陽極材へＳｉが拡散し、また犠牲陽極材からろう材へＺｎが拡散することで、充分な犠牲陽極効果が発揮されず、内面側の耐食性が低下するという問題点がある。 It is conceivable that the above problem can be solved by further brazing a brazing material on the inner surface side (sacrificial anode material surface) of the tube and combining the brazing and brazing joints. When Si diffuses into the material and Zn diffuses from the sacrificial anode material into the brazing material, there is a problem that the sufficient sacrificial anode effect is not exhibited and the corrosion resistance on the inner surface side is lowered.
チューブ材として適用される耐エロージョン・コロージョン性に優れたアルミニウム合金クラッド材として、Ａｌ−Ｍｎ系合金芯材の片面に犠牲陽極材としてＳｉ：３．０〜１２．０％を含有し、またはＳｉ：３．０〜１２．０％、Ｚｎ：１〜１０％を含有し、残部Ａｌおよび不純物からなるアルミニウム合金をクラッドしたものが提案されており（特許文献１参照）、このクラッド材を使用し、犠牲陽極材にろう材としての機能をもたせることによって上記の問題を解決することが期待されるが、このものにおいては、ろう付け時における犠牲陽極材の流動が避けられず、犠牲陽極材の耐食性を安定して維持することが困難な場合が多い。
発明者らは、チューブ材における前記従来の問題点を解消するために、犠牲陽極材へのＳｉの添加に着目し、犠牲陽極材面にろう付け性を与えるとともに、犠牲陽極材面の耐食性をも維持し得る犠牲陽極材の組成について試験、検討を行った結果、犠牲陽極材に通常のＡｌ−Ｓｉ系合金ろう材に比べてきわめて少量のＳｉを含有させることにより融点が低下し、ろう付け加熱中に犠牲陽極材中に僅かな液相が生じることによりろう付け性が向上すると同時に、犠牲陽極材はほとんど流動せず、犠牲陽極材の厚さが維持され耐食性の維持も可能であること、犠牲陽極材に多量のＺｎを共存させることによってさらに耐食性を高めることができることを見出した。 In order to solve the above-mentioned conventional problems in the tube material, the inventors paid attention to the addition of Si to the sacrificial anode material, provided brazing properties to the sacrificial anode material surface, and improved the corrosion resistance of the sacrificial anode material surface. As a result of testing and studying the composition of the sacrificial anode material that can be maintained, the sacrificial anode material contains a very small amount of Si as compared with a normal Al-Si alloy brazing material, so that the melting point is lowered. Brazing performance is improved by generating a slight liquid phase in the sacrificial anode material during heating, and at the same time, the sacrificial anode material hardly flows, the thickness of the sacrificial anode material is maintained, and corrosion resistance can be maintained. The present inventors have found that the corrosion resistance can be further improved by allowing a large amount of Zn to coexist in the sacrificial anode material.
本発明は、上記の知見に基づいてさらに検討を加えた結果としてなされたものであり、その目的は、とくに、不活性ガス雰囲気中でのフッ化物系フラックスやセシウム化物系フラックスを用いたろう付けにより接合されるエバポレータ、コンデンサ、ラジエータやヒータコアなどのアルミニウム合金製自動車熱交換器用のチューブ材（クラッド板を曲成して溶接またはろう付けによりチューブ形状とし、犠牲陽極材に他の部材がろう付けされるもの、クラッド板の両端部が犠牲陽極材と当接するように曲げ加工してＢ型のチューブ形状としろう付けするもの）、および熱交換器と接続される配管材（押出クラッド管）として好適な成形性に優れ、犠牲陽極材面のろう付け性、耐食性に優れた自動車熱交換器用アルミニウム合金クラッド材を提供することにある。 The present invention has been made as a result of further investigation based on the above-mentioned knowledge, and the purpose thereof is, in particular, by brazing using a fluoride-based flux or a cesium-based flux in an inert gas atmosphere. Tube materials for aluminum alloy automotive heat exchangers such as evaporators, condensers, radiators and heater cores to be joined (clad plate is bent into a tube shape by welding or brazing, and other members are brazed to the sacrificial anode material Suitable for use as a pipe material (extrusion clad pipe) connected to a heat exchanger and a B-shaped tube shape by bending so that both ends of the clad plate are in contact with the sacrificial anode material) An aluminum alloy clad material for automotive heat exchangers that has excellent formability, brazeability on the sacrificial anode material surface, and corrosion resistance It is to.
上記の目的を達成するための請求項１による自動車熱交換器用アルミニウム合金クラッド材は、芯材の一方の面に犠牲陽極材をクラッドし、他方の面にＡｌ−Ｓｉ系合金ろう材をクラッドしたアルミニウム合金クラッド材で、犠牲陽極材がろう付け面となるものにおいて、芯材がＡｌ−Ｍｎ系合金であり、犠牲陽極材が１．５％を越え３．０％未満のＳｉを含有し、残部Ａｌおよび不純物からなるアルミニウム合金であることを特徴とする。 In order to achieve the above object, an aluminum alloy clad material for an automobile heat exchanger according to claim 1 is obtained by clad a sacrificial anode material on one surface of a core material and clad an Al-Si alloy brazing material on the other surface. In the aluminum alloy clad material, the sacrificial anode material is a brazing surface, the core material is an Al-Mn alloy, the sacrificial anode material contains more than 1.5% and less than 3.0% Si, It is an aluminum alloy composed of the balance Al and impurities.
請求項２による自動車熱交換器用アルミニウム合金クラッド材は、芯材の一方の面に犠牲陽極材をクラッドし、他方の面にＡｌ−Ｓｉ系合金ろう材をクラッドしたアルミニウム合金クラッド材で、犠牲陽極材がろう付け面となるものにおいて、芯材がＡｌ−Ｍｎ系合金であり、犠牲陽極材が１．５％を越え３．０％未満のＳｉを含有するＡｌ−Ｚｎ系合金であることを特徴とする。
An aluminum alloy clad material for an automobile heat exchanger according to
請求項３による自動車熱交換器用アルミニウム合金クラッド材は、請求項１において、前記ろう材がＳｉ：６〜１３％を含有し、残部Ａｌおよび不純物からなるアルミニウム合金であることを特徴とする。また、請求項４による自動車熱交換器用アルミニウム合金クラッド材は、請求項２において、前記ろう材がＳｉ：６〜１３％を含有し、残部Ａｌおよび不純物からなるアルミニウム合金であることを特徴とする。
An aluminum alloy clad material for an automobile heat exchanger according to
請求項５による自動車熱交換器用アルミニウム合金クラッド材は、請求項１または３において、前記ろう材がさらにＦｅ：０．８〜２．０％、Ｚｎ：０．５〜５．０％、Ｓｒ：０．００５〜０．１％のうちの１種または２種以上を含有することを特徴とする。また、請求項６による自動車熱交換器用アルミニウム合金クラッド材は、請求項２または４において、前記ろう材がさらにＦｅ：０．８〜２．０％、Ｚｎ：０．５〜５．０％、Ｓｒ：０．００５〜０．１％のうちの１種または２種以上を含有することを特徴とする。
An aluminum alloy clad material for automobile heat exchanger according to claim 5 is the aluminum alloy clad material according to claim 1 or 3 , wherein the brazing material is further Fe: 0.8-2.0%, Zn: 0.5-5.0%, Sr: It contains one or more of 0.005 to 0.1% . An aluminum alloy clad material for an automobile heat exchanger according to claim 6 is the aluminum alloy clad material according to
請求項７による自動車熱交換器用アルミニウム合金クラッド材は、請求項１、３、５のいずれかにおいて、前記ろう材がさらにＢｉ：０．２％以下、Ｂｅ：０．１％以下のうちの１種または２種を含有することを特徴とする。また、請求項８による自動車熱交換器用アルミニウム合金クラッド材は、請求項２、４、６のいずれかにおいて、前記ろう材がさらにＢｉ：０．２％以下、Ｂｅ：０．１％以下のうちの１種または２種を含有することを特徴とする。
An aluminum alloy clad material for an automobile heat exchanger according to claim 7 is the aluminum alloy clad material according to any one of
請求項９による自動車熱交換器用アルミニウム合金クラッド材は、請求項１、３、５、７のいずれかにおいて、前記ろう材がさらにＩｎ：０．００１〜０．０５％、Ｓｎ：０．００１〜０．０５％のうちの１種または２種を含有することを特徴とする。また、請求項１０による自動車熱交換器用アルミニウム合金クラッド材は、請求項２、４、６、８のいずれかにおいて、前記ろう材がさらにＩｎ：０．００１〜０．０５％、Ｓｎ：０．００１〜０．０５％のうちの１種または２種を含有することを特徴とする。
The aluminum alloy clad material for an automobile heat exchanger according to claim 9 is the aluminum alloy clad material according to any one of
請求項１１による自動車熱交換器用アルミニウム合金クラッド材は、芯材の一方の面に犠牲陽極材をクラッドしたアルミニウム合金クラッド材で、犠牲陽極材がろう付け面となるものにおいて、芯材がＡｌ−Ｍｎ系合金であり、犠牲陽極材が１．５％を越え３．０％未満のＳｉを含有するＡｌ−Ｚｎ系合金であることを特徴とする。 An aluminum alloy clad material for an automobile heat exchanger according to claim 11 is an aluminum alloy clad material in which a sacrificial anode material is clad on one surface of a core material, and the sacrificial anode material serves as a brazing surface. It is a Mn-based alloy, and the sacrificial anode material is an Al—Zn-based alloy containing Si exceeding 1.5% and less than 3.0% .
請求項１２による自動車熱交換器用アルミニウム合金クラッド材は、請求項２、４、６、８、１０、１１のいずれかにおいて、前記犠牲陽極材がＳｉ：１．５％を越え３．０％未満、Ｚｎ：３．０〜１０．０％を含有し、残部Ａｌおよび不純物からなるアルミニウム合金であることを特徴とする。
An aluminum alloy clad material for an automobile heat exchanger according to claim 12 is any one of
請求項１３による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１２のいずれかにおいて、前記犠牲陽極材がさらにＩｎ：０．００１〜０．０５％、Ｓｎ：０．００１〜０．０５％のうちの１種または２種を含有することを特徴とする。 The aluminum alloy clad material for an automobile heat exchanger according to claim 13 is any one of claims 1 to 12 , wherein the sacrificial anode material is further In: 0.001-0.05%, Sn: 0.001-0.05. % Of 1% or 2% .
請求項１４による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１３のいずれかにおいて、前記犠牲陽極材がさらにＭｇ：４．０％以下を含有することを特徴とする。 An aluminum alloy clad material for an automobile heat exchanger according to a fourteenth aspect is characterized in that in any one of the first to thirteenth aspects, the sacrificial anode material further contains Mg: 4.0% or less .
請求項１５による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１４のいずれかにおいて、前記犠牲陽極材がさらにＣｕ：０．０５％以下、Ｔｉ：０．３％以下、Ｃｒ：０．２％以下、Ｚｒ：０．３％以下のうちの１種または２種以上を含有することを特徴とする。 The aluminum alloy clad material for an automobile heat exchanger according to claim 15 is the aluminum alloy clad material according to any one of claims 1 to 14 , wherein the sacrificial anode material is further Cu: 0.05% or less, Ti: 0.3% or less, Cr: 0.00. It is characterized by containing one or more of 2% or less and Zr: 0.3% or less .
請求項１６による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１５のいずれかにおいて、前記犠牲陽極材がさらにＦｅ：０．１５〜２．０％を含有することを特徴とする。 The aluminum alloy clad material for automobile heat exchanger according to claim 16 is characterized in that in any one of claims 1 to 15 , the sacrificial anode material further contains Fe: 0.15 to 2.0% .
請求項１７による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１６のいずれかにおいて、前記犠牲陽極材がさらにＳｒ：０．００５〜０．１％を含有することを特徴とする。 The aluminum alloy clad material for automobile heat exchanger according to claim 17 is characterized in that in any one of claims 1 to 16 , the sacrificial anode material further contains Sr: 0.005 to 0.1% .
請求項１８による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１７のいずれかにおいて、前記芯材がＭｎ：０．３％を越え２．０％以下を含有し、残部Ａｌおよび不純物からなるアルミニウム合金であることを特徴とする。 An aluminum alloy clad material for an automobile heat exchanger according to claim 18 is the aluminum alloy clad material according to any one of claims 1 to 17 , wherein the core material contains Mn: more than 0.3% and not more than 2.0%, and the balance Al and impurities. It is the aluminum alloy which becomes .
請求項１９による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１８のいずれかにおいて、前記芯材がさらにＣｕ：０．１〜１．０％、Ｓｉ：０．１〜１．５％のうちの１種または２種を含有することを特徴とする。 The aluminum alloy clad material for an automobile heat exchanger according to claim 19 is the aluminum alloy clad material according to any one of claims 1 to 18 , wherein the core material is further Cu: 0.1 to 1.0%, Si: 0.1 to 1.5%. It contains 1 type or 2 types of these, It is characterized by the above-mentioned.
請求項２０による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜１９のいずれかにおいて、前記芯材がさらにＭｇ：０．５％以下を含有することを特徴とする。 The aluminum alloy clad material for automobile heat exchanger according to claim 20 is characterized in that in any one of claims 1 to 19 , the core material further contains Mg: 0.5% or less .
請求項２１による自動車熱交換器用アルミニウム合金クラッド材は、請求項１〜２０のいずれかにおいて、前記芯材がさらにＣｒ：０．５％以下、Ｚｒ：０．３％以下のうちの１種または２種以上を含有することを特徴とする。 The aluminum alloy clad material for an automobile heat exchanger according to claim 21 is the aluminum alloy clad material according to any one of claims 1 to 20 , wherein the core material is further one of Cr: 0.5% or less and Zr: 0.3% or less. It contains 2 or more types .
本発明によれば、とくに、不活性ガス雰囲気中でのフッ化物系フラックスやセシウム化物系フラックスを用いたろう付けにより接合されるエバポレータ、コンデンサ、ラジエータやヒータコアなどのアルミニウム合金製自動車熱交換器用のチューブ材（クラッド板を曲成して溶接またはろう付けによりチューブ形状とし、犠牲陽極材に他の部材をろう付けするもの、クラッド板の両端部が犠牲陽極材と当接するように曲げ加工してＢ型のチューブ形状としろう付けするもの）、および熱交換器と接続される配管材（押出クラッド管）として好適な成形性に優れ、犠牲陽極材面のろう付け性、耐食性に優れた自動車熱交換器用アルミニウム合金クラッド材が提供される。 According to the present invention, a tube for an aluminum alloy automobile heat exchanger such as an evaporator, a condenser, a radiator or a heater core, which is joined by brazing using a fluoride flux or a cesium fluoride flux in an inert gas atmosphere. Bending material (bending the clad plate into a tube by welding or brazing, brazing other members to the sacrificial anode material, bending so that both ends of the clad plate are in contact with the sacrificial anode material B Automobile heat exchange with excellent moldability suitable for piping material (extruded clad pipe) connected to a heat exchanger and brazing and corrosion resistance of the sacrificial anode material surface A dexterous aluminum alloy cladding material is provided.
本発明のアルミニウム合金クラッド材の組成およびその限定理由について説明する。
（犠牲陽極材）
Ｓｉ：１．５％を越え３．０％未満
Ｓｉは、犠牲陽極材の融点を低下させ、ろう付け中に極わずか液相を生じさせることにより、ろうとして作用する。Ｓｉの好ましい含有量は１．５％を越え３．０％未満の範囲であり、１．５％以下ではろうとして有効に作用し難く、３．０％以上では、ろう付け加熱時に流動し易くなり、犠牲陽極材としての機能が損なわれる。Ｓｉのさらに好ましい含有範囲は２．０％を越え３．０％未満である。
The composition of the aluminum alloy clad material of the present invention and the reason for limitation will be described.
(Sacrificial anode material)
Si: more than 1.5% and less than 3.0% Si acts as a brazing by lowering the melting point of the sacrificial anode material and creating a negligible liquid phase during brazing. The preferable content of Si is in the range of more than 1.5% and less than 3.0%, and if it is 1.5% or less, it is difficult to act effectively as brazing, and if it is 3.0% or more, it tends to flow during brazing heating. Thus, the function as a sacrificial anode material is impaired. A more preferable content range of Si is more than 2.0% and less than 3.0%.
Ｚｎ：３．０〜１０．０％
Ｚｎは、犠牲陽極材の融点を低下させ、ろう付け中に極わずか液相を生じさせることにより、ろうとして作用する。また、犠牲陽極材の電位を卑にし、芯材に対する犠牲陽極効果を発揮させ、芯材の孔食や隙間腐食の発生を防止する。電位を貴化するＳｉを犠牲陽極材中に含有させるため、Ｚｎも相当量含有させることが必要である。Ｚｎの好ましい含有量は３．０〜１０．０％の範囲であり、Ｚｎの含有量が３．０％未満ではその効果が小策く、１０．０％を越えて含有すると犠牲陽極材の自己耐食性が低下する。Ｚｎのさらに好ましい含有範囲は４．０〜６．０％である。
Zn: 3.0 to 10.0%
Zn acts as a braze by lowering the melting point of the sacrificial anode material and creating a negligible liquid phase during brazing. Further, the potential of the sacrificial anode material is made lower, the sacrificial anode effect on the core material is exhibited, and the occurrence of pitting corrosion and crevice corrosion of the core material is prevented. In order to contain Si that makes the potential noble in the sacrificial anode material, it is necessary to contain a considerable amount of Zn. The preferable content of Zn is in the range of 3.0 to 10.0%. If the Zn content is less than 3.0%, the effect is negligible. If the content exceeds 10.0%, the sacrificial anode material Self-corrosion resistance is reduced. The more preferable content range of Zn is 4.0 to 6.0%.
Ｉｎ：０．００１〜０．０５％
Ｉｎは、微量の添加によって犠牲陽極材の電位を卑にし、芯材に対する犠牲陽極効果を確実に発揮させ、芯材の孔食や隙間腐食の発生を防止する。Ｉｎの好ましい含有量は０．００１〜０．０５％の範囲であり、０．００１％未満ではその効果が十分でなく、０．０５％を越えると、自己耐食性および圧延加工性が低下する。Ｉｎのさらに好ましい含有範囲は０．０１〜０．０３％である。
In: 0.001 to 0.05%
In adds a small amount to make the potential of the sacrificial anode material low, and reliably exert the sacrificial anode effect on the core material, thereby preventing the occurrence of pitting corrosion and crevice corrosion of the core material. The preferable content of In is in the range of 0.001 to 0.05%. If the content is less than 0.001%, the effect is not sufficient, and if it exceeds 0.05%, the self-corrosion resistance and the rolling workability are deteriorated. A more preferable content range of In is 0.01 to 0.03%.
Ｓｎ：０．００１〜０．０５％
Ｓｎは、微量の添加によって犠牲陽極材の電位を卑にし、芯材に対する犠牲陽極効果を確実に発揮させ、芯材の孔食や隙間腐食の発生を防止する。Ｓｎの好ましい含有量は０．００１〜０．０５％の範囲であり、０．００１％未満ではその効果が十分でなく、０．０５％を越えると、自己耐食性および圧延加工性が低下する。Ｓｎのさらに好ましい含有範囲は０．０１〜０．０３％である。
Sn: 0.001 to 0.05%
Sn lowers the potential of the sacrificial anode material by adding a small amount, reliably exerts the sacrificial anode effect on the core material, and prevents the occurrence of pitting corrosion and crevice corrosion of the core material. The preferable content of Sn is in the range of 0.001 to 0.05%. If it is less than 0.001%, the effect is not sufficient, and if it exceeds 0.05%, the self-corrosion resistance and the rolling processability are deteriorated. The more preferable content range of Sn is 0.01 to 0.03%.
Ｍｇ：４．０％以下
Ｍｇは、熱交換器などのろう付け組み立て時、ろう付け加熱中に芯材へ拡散し、芯材中のＳｉやＣｕとともに強度を高めるよう機能する。犠牲陽極材に残存したＭｇはＳｉとともに犠牲陽極材の強度を高め、これらの効果によってクラッド材の強度を改善する。Ｍｇの好ましい含有量は４．０％以下の範囲であり、４．０％を越えると圧延加工性が低下する。Ｍｇのさらに好ましい含有範囲は２．５％以下である。
Mg: 4.0% or less Mg functions to diffuse into the core material during brazing heating during brazing assembly of a heat exchanger or the like and increase the strength together with Si and Cu in the core material. Mg remaining in the sacrificial anode material increases the strength of the sacrificial anode material together with Si, and improves the strength of the clad material by these effects. The preferable content of Mg is in the range of 4.0% or less. If it exceeds 4.0%, the rolling processability is lowered. A more preferable content range of Mg is 2.5% or less.
Ｃｕ：０．０５％以下
Ｃｕは、犠牲陽極材の電位を貴にし、犠牲陽極材へのＺｎの添加による自己耐食性の低下を抑制する。Ｃｕの好ましい含有量は０．０５％以下の範囲であり、０．０５％を越えると、犠牲陽極材と芯材との間の電位差を十分に確保することができず、芯材に対する犠牲陽極効果が低下する。
Cu: 0.05% or less Cu makes the potential of the sacrificial anode material noble and suppresses a decrease in self-corrosion resistance due to the addition of Zn to the sacrificial anode material. The preferable content of Cu is in the range of 0.05% or less, and if it exceeds 0.05%, a sufficient potential difference between the sacrificial anode material and the core material cannot be secured, and the sacrificial anode with respect to the core material. The effect is reduced.
Ｃｒ：０．２％以下、Ｚｒ：０．３％以下
ＣｒおよびＺｒは、犠牲陽極材の結晶粒度を粗大にして、ろう付け加熱中の芯材のＣｕの粒界拡散を抑制する。ＣｒおよびＺｒがそれぞれ０．２％および０．３％を越えると、鋳造時に巨大な晶出物が生成し、健全な板材の製造が困難となる。
Cr: 0.2% or less, Zr: 0.3% or less Cr and Zr increase the crystal grain size of the sacrificial anode material and suppress the Cu grain boundary diffusion of the core material during brazing heating. If Cr and Zr exceed 0.2% and 0.3%, respectively, huge crystallized products are generated during casting, and it becomes difficult to produce a sound plate material.
Ｔｉ：０．３％以下
Ｔｉは、材料の板厚方向に濃度の高い領域と低い領域に分かれ、これらの領域が層状となって交互に分布し、Ｔｉ濃度の低い領域が高い領域に比べ優先的に腐食することにより、腐食形態を層状にする効果を有し、この効果により板厚方向への粒界腐食の進行が妨げられ材料の耐孔食性が向上する。Ｔｉの好ましい含有量は０．３％以下の範囲であり、０．３％を越えると、鋳造が困難となり、また加工性が低下して健全な材料の製造が困難となる。
Ti: 0.3% or less Ti is divided into a high-concentration region and a low-concentration region in the thickness direction of the material. These regions are alternately distributed in layers, and a low-concentration region has priority over a high region. Corrosion has the effect of layering the corrosion form, and this effect prevents the progress of intergranular corrosion in the plate thickness direction and improves the pitting corrosion resistance of the material. The preferable content of Ti is in the range of 0.3% or less, and if it exceeds 0.3%, casting becomes difficult, and workability deteriorates, making it difficult to produce a sound material.
Ｆｅ：０．１５〜２．０％
Ｆｅは、Ａｌ−Ｆｅ−Ｓｉ系化合物を形成し、Ｓｉの固溶度を低下することにより液相率を低下させ、ろうの流動を抑制する。また、Ｆｅは、Ａｌ−Ｆｅ系やＡｌ−Ｆｅ−Ｓｉ系化合物を形成し、それら化合物が腐食の起点となって孔食が分散されることにより耐食性を向上させる。Ｆｅの好ましい含有量は０．１５〜２．０％の範囲であり、０．１５％未満ではその効果が小さく、２．０％を越えると犠牲陽極材の自己耐食性が低下する。Ｆｅのさらに好ましい含有範囲は０．７％を越え１．２％以下である。
Fe: 0.15-2.0%
Fe forms an Al-Fe-Si-based compound, reduces the liquid solubility by reducing the solid solubility of Si, and suppresses the flow of wax. Fe forms an Al-Fe-based or Al-Fe-Si-based compound, and these compounds serve as a starting point for corrosion to improve the corrosion resistance by dispersing pitting corrosion. The preferable content of Fe is in the range of 0.15 to 2.0%. If the content is less than 0.15%, the effect is small, and if it exceeds 2.0%, the self-corrosion resistance of the sacrificial anode material is lowered. A more preferable content range of Fe is more than 0.7% and 1.2% or less.
Ｓｒ：０．００５〜０．１％
Ｓｒは、犠牲陽極材中におけるＳｉ粒子の存在形態をより微細且つ均一にするよう機能し、その結果ろう付け性を向上させる。Ｓｒの好ましい含有量は０．００５〜０．１％の範囲であり、０．００５％未満ではその効果が十分でなく、０．１％を越えて含有してもその効果が飽和する。なお、本発明においては、犠牲陽極材中にＮａ：１〜１００ｐｐｍ、Ｓｂ：０．００１〜０．５％が添加されていてもその効果に影響を与えることはない。
Sr: 0.005 to 0.1%
Sr functions to make the presence form of Si particles in the sacrificial anode material finer and uniform, and as a result, improves brazing properties. The preferable content of Sr is in the range of 0.005 to 0.1%. If the content is less than 0.005%, the effect is not sufficient, and even if the content exceeds 0.1%, the effect is saturated. In the present invention, even if Na: 1 to 100 ppm and Sb: 0.001 to 0.5% are added to the sacrificial anode material, the effect is not affected.
（芯材）
Ｍｎ：０．３〜２．０％
Ｍｎは、芯材の強度を向上させるとともに、芯材の電位を貴にして犠牲陽極材との電位差を大きくして耐食性を高めるよう機能する。Ｍｎの好ましい含有量は０．３〜２．０％の範囲であり、０．３％未満ではその効果が小さく、２．０％を越えると、鋳造時に粗大な化合物が生成し圧延加工性が低下して健全な板材（芯材）が得難くなる。Ｍｎのさらに好ましい含有範囲は０．８〜１．５％である。
(Core material)
Mn: 0.3 to 2.0%
Mn functions to improve the corrosion resistance by improving the strength of the core material and making the potential of the core material noble and increasing the potential difference from the sacrificial anode material. The preferable content of Mn is in the range of 0.3 to 2.0%. If the content is less than 0.3%, the effect is small. If the content exceeds 2.0%, a coarse compound is produced during casting, and the rolling processability is low. It decreases and it becomes difficult to obtain a healthy plate (core material). A more preferable content range of Mn is 0.8 to 1.5%.
Ｃｕ：０．１〜１．０％
Ｃｕは、芯材の強度を向上させるとともに、芯材の電位を貴にし、犠牲陽極材のとの電位差およびろう材との電位差を大きくして耐食性を向上させるよう機能する。また、ろう付け時に犠牲陽極材およびろう材に拡散して、犠牲陽極材およびろう材の厚さ方向になだらかなＣｕの濃度勾配を形成させ、この結果、芯材側の電位は貴となり、犠牲陽極材の表面側およびろう材の表面側の電位は卑となって、犠牲陽極材およびろう材の厚さ方向になだらかな電位勾配が形成されるため、腐食形態が全面腐食型となる。Ｃｕの好ましい含有量は０．１〜１．０％の範囲であり、０．１％未満ではその効果が小さく、１．０％を越えると芯材の耐食性が低下し、また融点が低下してろう付け時に局部的な溶融が生じ易くなる。Ｃｕのさらに好ましい含有範囲は０．４〜０．７％である。
Cu: 0.1 to 1.0%
Cu functions to improve the corrosion resistance by improving the strength of the core material, making the potential of the core material noble, and increasing the potential difference with the sacrificial anode material and the potential difference with the brazing material. In addition, it diffuses into the sacrificial anode material and the brazing material during brazing to form a gentle Cu concentration gradient in the thickness direction of the sacrificial anode material and brazing material. The potentials on the surface side of the anode material and the surface side of the brazing material become base, and a gentle potential gradient is formed in the thickness direction of the sacrificial anode material and the brazing material. The preferable content of Cu is in the range of 0.1 to 1.0%. If the content is less than 0.1%, the effect is small. If the content exceeds 1.0%, the corrosion resistance of the core material is lowered, and the melting point is lowered. Local melting tends to occur during brazing. The more preferable content range of Cu is 0.4 to 0.7%.
Ｓｉ：０．１〜１．５％
Ｓｉは、芯材の強度を向上させる効果を有する。とくに、犠牲陽極材にＭｇが含有する場合、Ｓｉはろう付け中に犠牲陽極材から拡散してくるＭｇと共存してＭｇと結合してＭｇ2 Ｓｉを生成することにより、ろう付け後に時効硬化が生じ、強度がさらに向上する。Ｓｉの好ましい含有量は０．１〜１．５％の範囲であり、０．１％未満ではその効果が小さく、１．５％を越えると、芯材の耐食性が低下するとともに、芯材の融点を下げ、ろう付け時に局部溶融が生じ易くなる。Ｓｉのさらに好ましい含有範囲は０．３〜１．０％である。
Si: 0.1 to 1.5%
Si has the effect of improving the strength of the core material. In particular, when Mg is contained in the sacrificial anode material, Si coexists with Mg diffusing from the sacrificial anode material during brazing, and bonds with Mg to form Mg 2 Si, thereby age-aging after brazing. And the strength is further improved. The preferable content of Si is in the range of 0.1 to 1.5%. If the content is less than 0.1%, the effect is small. If the content exceeds 1.5%, the corrosion resistance of the core material decreases, and The melting point is lowered, and local melting tends to occur during brazing. A more preferable content range of Si is 0.3 to 1.0%.
Ｍｇ：０．５％以下
Ｍｇは、芯材の強度を向上させる。０．５％を越えて含有すると、フッ化物系フラックスを用いて不活性ガス雰囲気中でろう付けを行う場合、ろう付け時にＭｇがフッ化物系フラックスと反応してＭｇのフッ化物が生成し、ろう付け性を低下させるとともに、ろう付け部の外観が悪くなる。Ｍｇのさらに好ましい含有範囲は０．１５％以下である。
Mg: 0.5% or less Mg improves the strength of the core material. When the content exceeds 0.5%, when brazing is performed in an inert gas atmosphere using a fluoride-based flux, Mg reacts with the fluoride-based flux during brazing to produce Mg fluoride. While reducing brazing property, the external appearance of a brazing part worsens. A more preferable content range of Mg is 0.15% or less.
Ｃｒ：０．５％以下、Ｚｒ：０．３％以下
ＣｒおよびＺｒは、芯材の結晶粒度を粗大にし、ろう付け加熱中のろう材中のＳｉの粒界拡散を抑制する。ＣｒおよびＺｒがそれぞれ０．５％および０．３％を越えると、鋳造時に巨大晶出物が生成し、加工性が低下して健全な板材の製造が困難となる。
Cr: 0.5% or less, Zr: 0.3% or less Cr and Zr increase the crystal grain size of the core material and suppress the grain boundary diffusion of Si in the brazing material during brazing heating. When Cr and Zr exceed 0.5% and 0.3%, respectively, giant crystallized substances are generated during casting, and workability is lowered, making it difficult to produce a sound plate material.
（ろう材）
ろう材としては、通常用いられているＡｌ−Ｓｉ系合金、好ましくはＳｉ：６〜１３％を含む合金が使用される。Ｓｉが６％未満では流動性が低下してろう材としての作用が不十分となり、Ｓｉが１３％を越えると、健全な材料の製造が困難となる。
(Brazing material)
As the brazing material, a commonly used Al—Si alloy, preferably an alloy containing Si: 6 to 13% is used. If Si is less than 6%, the fluidity is lowered and the effect as a brazing material is insufficient, and if Si exceeds 13%, it is difficult to produce a sound material.
Ｆｅ：０．８〜２．０％
Ｆｅは、Ａｌ−Ｆｅ系、Ａｌ−Ｆｅ−Ｓｉ系化合物を形成し、これらの化合物が腐食の起点となるため孔食が分散し、外面の耐食性が向上する。Ｆｅの好ましい含有範囲は０．８〜２．０％であり、０．８％未満ではその効果が小さく、２．０％を越えると、外面の耐食性が低下する。
Fe: 0.8 to 2.0%
Fe forms Al—Fe and Al—Fe—Si compounds, and these compounds serve as starting points for corrosion, so that pitting corrosion is dispersed and the corrosion resistance of the outer surface is improved. The preferable content range of Fe is 0.8 to 2.0%. If the content is less than 0.8%, the effect is small.
Ｚｎ：０．５〜５．０％
Ｚｎは、上記の範囲で含有されても本発明の効果を損なうことはない。５．０％を越えて含有すると、自己耐食性が低下する。
Zn: 0.5 to 5.0%
Even if Zn is contained in the above range, the effect of the present invention is not impaired. If the content exceeds 5.0%, the self-corrosion resistance decreases.
Ｓｒ：０．００５〜０．１％
Ｓｒは、ろう材中のＳｉ粒子を微細かつ均一に分散させる効果がある。Ｓｉ粒子が微細かつ均一に分散することにより、ろうの溶融が均一になり、ろう付け性が改善される。Ｓｒの好ましい含有量は０．００５〜０．１％の範囲であり、０．００５％未満ではその効果が小さく、０．１％を越えると、その効果が飽和する。
Sr: 0.005 to 0.1%
Sr has an effect of finely and uniformly dispersing Si particles in the brazing material. When the Si particles are finely and uniformly dispersed, the melting of the brazing becomes uniform and the brazing property is improved. The preferable content of Sr is in the range of 0.005 to 0.1%. If it is less than 0.005%, the effect is small, and if it exceeds 0.1%, the effect is saturated.
Ｂｉ：０．２％以下、Ｂｅ：０．１％以下
ＢｉおよびＢｅは、上記の範囲で含有されても本発明の効果を損なうことはない。ＢｉおよびＢｅが０．２％および０．１％を越えるとろう付け性が低下する。
Bi: 0.2% or less, Be: 0.1% or less Even if Bi and Be are contained in the above ranges, the effect of the present invention is not impaired. When Bi and Be exceed 0.2% and 0.1%, the brazing property decreases.
Ｉｎ：０．００１〜０．０５％、Ｓｎ：０．００１〜０．０５％
ＩｎおよびＳｎは、上記の範囲で含有されても本発明の効果を損なうことはない。ＩｎおよびＳｎが０．０５％を越えると、ろう材の自己耐食性および圧延加工性が低下する。なお、本発明においては、Ｎａ：１〜１００ｐｐｍ、Ｓｂ：０．００１〜０．５％が含有されていても、本発明の効果に影響することはない。
In: 0.001-0.05%, Sn: 0.001-0.05%
Even if In and Sn are contained in the above ranges, the effects of the present invention are not impaired. When In and Sn exceed 0.05%, the self-corrosion resistance and rolling workability of the brazing material are lowered. In the present invention, even if Na: 1 to 100 ppm and Sb: 0.001 to 0.5% are contained, the effect of the present invention is not affected.
本発明のアルミニウム合金クラッド材は、芯材、犠牲陽極材およびＡｌ−Ｓｉ系ろう材を構成するアルミニウム合金を、たとえば、連続鋳造により造塊し、必要に応じて均質化処理後、犠牲陽極材用およびろう材用アルミニウム合金の鋳塊については、それぞれ所定厚さまで熱間圧延し、ついで、芯材用アルミニウム合金鋳塊と、犠牲陽極用アルミニウム合金およびろう材用アルミニウム合金を組み合わせて、常法に従って熱間圧延によりクラッド材とし、その後冷間圧延、中間焼鈍、冷間圧延により所定の厚さとすることによって製造される。 The aluminum alloy clad material of the present invention comprises a core material, a sacrificial anode material, and an aluminum alloy constituting an Al—Si brazing material, for example, ingot by continuous casting, and after homogenization treatment as necessary, a sacrificial anode material The aluminum alloy ingots for solder and brazing material are each hot-rolled to a predetermined thickness, and then the aluminum alloy ingot for core material is combined with the aluminum alloy for sacrificial anode and the aluminum alloy for brazing material. Accordingly, the clad material is manufactured by hot rolling, and then is made to have a predetermined thickness by cold rolling, intermediate annealing, and cold rolling.
なお、本発明は、芯材の一方の面に犠牲陽極材をクラッドしたアルミニウム合金クラッド材で、犠牲陽極材がろう付け面となるものにおいて、芯材がＡｌ−Ｍｎ系合金であり、犠牲陽極材が１．５％を越え３．０％未満のＳｉを含有するＡｌ−Ｚｎ系合金である自動車熱交換器用アルミニウム合金クラッド材を、図４に示すように、犠牲陽極材面にクラッドフィン材をろう付け接合する場合にも有効である。 The present invention is an aluminum alloy clad material in which a sacrificial anode material is clad on one surface of a core material, and the sacrificial anode material serves as a brazing surface. The core material is an Al-Mn alloy, and the sacrificial anode An aluminum alloy clad material for an automobile heat exchanger, which is an Al—Zn-based alloy containing Si exceeding 1.5% and less than 3.0%, is clad fin material on the sacrificial anode material surface as shown in FIG. It is also effective when brazing and joining.
以下、本発明の実施例を比較例と対比して説明する。これらの実施例は、本発明の一実施態様を示すものであり、本発明はこれらに限定されるものではない。 Examples of the present invention will be described below in comparison with comparative examples. These examples show one embodiment of the present invention, and the present invention is not limited to these examples.
実施例１
連続鋳造によって表１に示す組成を有する芯材用合金、表２に示す組成を有する犠牲陽極材用合金、および表３に示す組成を有するろう材用合金を造塊し、得られた鋳塊のうち、芯材用合金および犠牲陽極材用合金の鋳塊については均質化処理を行った。
Example 1
An ingot obtained by ingoting a core material alloy having the composition shown in Table 1, a sacrificial anode material alloy having the composition shown in Table 2, and a brazing alloy having the composition shown in Table 3 by continuous casting. Among these, the ingots of the core material alloy and the sacrificial anode material alloy were subjected to a homogenization treatment.
ついで、犠牲陽極材用合金およびろう材用合金の鋳塊を所定の厚さまで熱間圧延し、これらの熱間圧延板と芯材用合金の鋳塊とを合わせ材として熱間圧延しクラッド材を得た。その後、冷間圧延、中間焼鈍、冷間圧延によって厚さ０．２０ｍｍの板材（クラッド材、調質Ｈ１４）を得た。クラッド材の構成は、犠牲陽極材は０．０２５〜０．０５０ｍｍ、ろう材は０．０２０ｍｍである。 Subsequently, the ingot of the sacrificial anode material alloy and the brazing material alloy is hot-rolled to a predetermined thickness, and the hot-rolled plate and the core alloy ingot are hot-rolled together to form a clad material. Got. Thereafter, a plate material (cladding material, tempered H14) having a thickness of 0.20 mm was obtained by cold rolling, intermediate annealing, and cold rolling. The composition of the clad material is 0.025 to 0.050 mm for the sacrificial anode material and 0.020 mm for the brazing material.
得られたクラッド材を試験材として、以下の方法により（１）クラッド性（圧延性）、（２）ろう付け性、（３）犠牲陽極材の耐食性を評価した。結果を表４〜６に示す。 Using the obtained clad material as a test material, (1) cladability (rollability), (2) brazeability, and (3) corrosion resistance of the sacrificial anode material were evaluated by the following methods. The results are shown in Tables 4-6.
クラッド性（圧延性）：犠牲陽極材、芯材、ろう材の製造、あるいはクラッド材の製造において、圧延加工性がわるく健全な材料の製造ができないものをクラッド性不良（×）とし、健全なクラッド材が得られたものをクラッド性良好（○）とする。 Cladness (rollability): Sacrificial anode material, core material, brazing material production, or clad material production, with poor rolling processability and the failure to produce a sound material. The one obtained from the clad material is defined as good clad property (◯).
ろう付け性：得られたクラッド材（試験材）と、３００３合金板（厚さ１．０ｍｍ）を図５に示すように組み合わせて逆Ｔ字試験片を作製し、フッ化物系フラックスを塗布して、窒素ガス雰囲気中で６００℃（材料温度）のろう付け温度に加熱し接合状態を評価した。接合状態が良好なものは○、接合不良や局部溶融が生じたものは×とした。 Brazing property: The obtained clad material (test material) and 3003 alloy plate (thickness 1.0 mm) are combined as shown in FIG. 5 to produce an inverted T-shaped test piece, and a fluoride-based flux is applied. Then, the joining state was evaluated by heating to a brazing temperature of 600 ° C. (material temperature) in a nitrogen gas atmosphere. The case where the bonding state was good was marked with ◯, and the case where bonding failure or local melting occurred was marked with x.
犠牲陽極材の耐食性：得られたクラッド材（試験材）を、単板のままフッ化物系フラックスを塗布して窒素ガス雰囲気中で６００℃（材料温度）のろう付け温度に加熱した後、犠牲陽極材面について下記の条件で腐食試験を行った。
腐食液：Ｃｌ- ：１９５ｐｐｍ、ＳＯ4 2- ：６０ｐｐｍ、Ｃｕ2+：１ｐｍ、Ｆｅ3+：３０ｐｐｍ
比液量：５ｍＬ／ｃｍ2
シール：ろう材面と端面をシリコン樹脂でシールした。
試験方法：８８℃に加熱した腐食液中に８時間浸漬した後、冷却して２５℃で１６時間保持するサイクルを４か月間繰り返し、最大腐食深さを測定した。
Corrosion resistance of sacrificial anode material: The obtained clad material (test material) was applied as a single plate with fluoride-based flux and heated to a brazing temperature of 600 ° C. (material temperature) in a nitrogen gas atmosphere. A corrosion test was performed on the anode material surface under the following conditions.
Corrosion solution: Cl − : 195 ppm, SO 4 2− : 60 ppm, Cu 2+ : 1 pm, Fe 3+ : 30 ppm
Specific liquid volume: 5 mL / cm 2
Seal: The brazing filler metal surface and the end surface were sealed with silicon resin.
Test method: After immersing in a corrosive liquid heated to 88 ° C. for 8 hours, a cycle of cooling and holding at 25 ° C. for 16 hours was repeated for 4 months, and the maximum corrosion depth was measured.
表４〜６にみられるように、本発明に従う試験 Ｎｏ．１〜１０１はいずれも、クラッド性（圧延性）、ろう付け性に優れ、犠牲陽極材の腐食試験においても最大腐食深さはいずれも０．１ｍｍ未満であり、良好な耐食性をそなえている。 As seen in Tables 4-6, test no. Nos. 1-101 are excellent in cladability (rollability) and brazing properties, and the maximum corrosion depth is less than 0.1 mm in the corrosion test of the sacrificial anode material, and has good corrosion resistance.
比較例１
連続鋳造によって表７に示す組成を有する芯材用合金、表８に示す組成を有する犠牲陽極材用合金、および表９に示す組成を有するろう材用合金を造塊し、芯材用合金および犠牲陽極材用合金の鋳塊を均質化処理した。
Comparative Example 1
An alloy for core material having the composition shown in Table 7 by casting, an alloy for sacrificial anode material having the composition shown in Table 8, and an alloy for brazing material having the composition shown in Table 9 are obtained. The ingot of the sacrificial anode material alloy was homogenized.
ついで、犠牲陽極材用合金の鋳塊およびろう材用合金の鋳塊を所定の厚さまで熱間圧延し、これらの熱間圧延板と芯材用合金の鋳塊とを合わせ材として熱間圧延し、クラッド材を得た。その後、冷間圧延、中間焼鈍、冷間圧延によって厚さ０．２０ｍｍの板材（クラッド材、調質Ｈ１４）を得た。クラッド材の構成は、犠牲陽極材は０．０４０ｍｍ、ろう材は０．０２０ｍｍである。なお、表７〜９において、本発明の条件を外れたものには下線を付した。 Next, the ingot of the alloy for sacrificial anode material and the ingot of the alloy for brazing material are hot-rolled to a predetermined thickness, and these hot-rolled plates and the ingot of the alloy for core material are used as a combined material for hot rolling. Thus, a clad material was obtained. Thereafter, a plate material (cladding material, tempered H14) having a thickness of 0.20 mm was obtained by cold rolling, intermediate annealing, and cold rolling. The structure of the clad material is 0.040 mm for the sacrificial anode material and 0.020 mm for the brazing material. In Tables 7 to 9, those outside the conditions of the present invention are underlined.
得られたクラッド材を試験材として、実施例１と同じ方法で（１）クラッド性（圧延性）、（２）ろう付け性、（３）犠牲陽極材の耐食性を評価した。結果を表１０に示す。 Using the obtained clad material as a test material, (1) cladability (rollability), (2) brazeability, and (3) corrosion resistance of the sacrificial anode material were evaluated in the same manner as in Example 1. The results are shown in Table 10.
表１０に示すように、試験材Ｎｏ．１０２は芯材のＭｎ量が少ないため、犠牲陽極材の耐食性が劣る。試験材Ｎｏ．１０３は芯材のＭｎ量が多いため、芯材の製造において圧延加工性がわるく、健全な芯材の製造が困難となった結果、クラッド性不良となった。試験材Ｎｏ．１０４は芯材のＣｕ量が多いため、ろう付け時に芯材に局部溶融が生じろう付け性が低下した。試験材Ｎｏ．１０５は芯材のＳｉ量が多いため、ろう付け時に芯材に局部溶融が生じろう付け性が低下した。試験材Ｎｏ．１０６は芯材のＭｇ量が多いため、ろう付け性が劣り接合不良が生じた。 As shown in Table 10, the test material No. Since No. 102 has a small amount of Mn in the core material, the corrosion resistance of the sacrificial anode material is inferior. Test material No. Since No. 103 had a large amount of Mn in the core material, rolling workability was poor in the production of the core material, and as a result, it was difficult to produce a sound core material, resulting in poor cladness. Test material No. Since the core material 104 has a large amount of Cu in the core material, local melting occurred in the core material at the time of brazing, and the brazing property was lowered. Test material No. Since No. 105 has a large amount of Si in the core material, local melting occurred in the core material at the time of brazing, and the brazing property was lowered. Test material No. Since the core 106 had a large amount of Mg in the core material, the brazing property was poor and poor bonding occurred.
試験材Ｎｏ．１０７は犠牲陽極材のＳｉ量が少ないため、ろう付け性が劣る。試験材Ｎ．１０８は犠牲陽極材のＳｉ量が多いため、犠牲陽極材が流動して犠牲陽極材としての機能が失われ耐食性が劣る。試験材Ｎｏ．１０９は犠牲陽極材のＺｎ量が多いため、犠牲陽極材の消耗が早くなり耐食性が低下している。試験材Ｎｏ．１１０および１１１は犠牲陽極材のＩｎ量およびＳｎ量が多いため、いずれも犠牲陽極材の製造において圧延加工性がわるく、健全な犠牲陽極材の製造が困難となった結果、クラッド性不良となった。 Test material No. No. 107 is inferior in brazing because the amount of Si in the sacrificial anode material is small. Test material N. No. 108 has a large amount of Si in the sacrificial anode material, so that the sacrificial anode material flows and loses its function as the sacrificial anode material, resulting in poor corrosion resistance. Test material No. No. 109 has a large amount of Zn in the sacrificial anode material, so that the sacrificial anode material is consumed quickly and the corrosion resistance is lowered. Test material No. Since 110 and 111 have a large amount of In and Sn in the sacrificial anode material, both have poor rolling processability in the production of the sacrificial anode material, and as a result, it became difficult to produce a sound sacrificial anode material, resulting in poor cladding properties. It was.
試験材Ｎｏ．１１２は犠牲陽極材のＦｅ量が多いため、自己腐食性が多くなり耐食性が劣る。試験材Ｎｏ．１１３はろう材のＳｉ量が多いため、圧延性が劣り、健全なクラッド材が得られなかった。 Test material No. Since 112 has a large amount of Fe in the sacrificial anode material, self-corrosion increases and corrosion resistance is poor. Test material No. Since No. 113 had a large amount of Si in the brazing material, the rollability was inferior and a sound clad material could not be obtained.
１ チューブ材
２ Ｂ型のチューブ形状
３ クラッドフィン材
1 Tube material 2 B-shaped
Claims (21)