JP3494325B2 - Artificial grass with sand - Google Patents
Artificial grass with sandInfo
- Publication number
- JP3494325B2 JP3494325B2 JP22708195A JP22708195A JP3494325B2 JP 3494325 B2 JP3494325 B2 JP 3494325B2 JP 22708195 A JP22708195 A JP 22708195A JP 22708195 A JP22708195 A JP 22708195A JP 3494325 B2 JP3494325 B2 JP 3494325B2
- Authority
- JP
- Japan
- Prior art keywords
- elastic filler
- elastic
- sand
- filler
- filled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は砂入り人工芝生に係
り、さらに詳しく言えば、良好な接地感を長期間維持で
きる砂入り人工芝生に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sand-containing artificial lawn, and more particularly to a sand-containing artificial lawn that can maintain a good ground contact feeling for a long period of time.
【０００２】[0002]
【従来の技術】近年、例えばテニスコートを施工するに
あたっては、導入コスト，維持コストが安価であるとと
もに、比較的天然芝生に近い接地感が得られる砂入り人
工芝生が多用されている。ここで、砂入り人工芝生と
は、面状の基布にパイルが多数植設され、これらのパイ
ル間にデッキブラシや回転ブラシを用いて目砂等の粒状
充填材が充填されているものを指している。2. Description of the Related Art In recent years, for example, when constructing a tennis court, an artificial lawn with sand is widely used because the introduction cost and the maintenance cost are low and the feeling of grounding is relatively close to that of a natural lawn. Here, a sand-containing artificial lawn is one in which a large number of piles are planted on a planar base cloth and granular fillers such as sand grains are filled between these piles using a deck brush or a rotating brush. pointing.
【０００３】ところで、砂入り人工芝生は、競技用スパ
イクによる突き固め、あるいは目砂，パイルの磨耗屑や
通常のごみ，異物等が目砂間の空隙に入り込むことによ
り目砂が固化し、施工当初に得られた良好な接地感が次
第に損なわれるという問題がある。この問題を解決する
ために、目砂に埋没されるループ状のパイルを基布に植
設しておき、これらのパイルの弾力性により良好な接地
感を維持する人工芝生が提案されている（実開平６−１
４０５号公報参照：従来例１）。また、本願出願人も、
パイル間に弾性ゴムチップのみを充填した人工芝生製運
動競技場（特公昭６３−３９７２５号公報参照：従来例
２）およびパイル間に加硫ゴム等の粒状物層を充填し、
その表面層をガラスビーズ等の球形粒状物により構成し
た人工芝生製運動競技場（実公昭６４−６８６２号公報
参照：従来例３）を提案した。By the way, the artificial grass with sand is tampered with by spikes for competition, or the sand is solidified by the sand, the abrasion dust of the pile, ordinary dust, foreign substances, etc. entering into the spaces between the sand. There is a problem that the good ground feeling initially obtained is gradually deteriorated. In order to solve this problem, an artificial lawn has been proposed in which loop piles buried in the sand are planted in the base fabric and the elasticity of these piles maintains a good ground contact feeling ( Actual Kaihei 6-1
See Japanese Patent No. 405: Conventional Example 1). In addition, the applicant of the present application also
An artificial lawn athletic field filled with only elastic rubber chips between the piles (see JP-B-63-39725: Conventional Example 2) and a granular material layer such as vulcanized rubber between the piles,
An artificial lawn athletic stadium (see Japanese Utility Model Publication No. 64-6862: Conventional Example 3) having its surface layer formed of spherical particles such as glass beads was proposed.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、従来例
１では、目砂に埋没するパイルの弾力性が比較的低いた
め、経時変化によりパイルの弾力性が低下し、良好な接
地感を長期間維持できないという問題がある。また、従
来例２では、弾性ゴムチップが弾力性を有しているもの
の、チップ状であるため、長期間の使用により、パイル
からゴムチップが抜け出してしまい、その結果、良好な
接地感が失われる。また、従来例２では、デッキブラシ
や回転ブラシ等による充填作業を行うにあたって、弾力
性を有する弾性ゴムチップの特性上、弾性ゴムチップが
パイル間に充填されにくいとともにパイル間から出やす
い。すなわち、従来例２では、弾性ゴムチップの充填性
が低いため、充填作業に手間が掛かるという問題があ
る。However, in the conventional example 1, since the elasticity of the pile buried in the sand is relatively low, the elasticity of the pile deteriorates with the lapse of time, and a good ground contact feeling is maintained for a long time. There is a problem that you cannot do it. Further, in Conventional Example 2, although the elastic rubber chip has elasticity, since it is in the shape of a chip, the rubber chip comes out of the pile after long-term use, and as a result, a good ground contact feeling is lost. Further, in the conventional example 2, when performing a filling operation with a deck brush, a rotating brush, or the like, the elastic rubber chips are less likely to be filled between the piles and easily come out between the piles due to the characteristics of the elastic rubber chips having elasticity. That is, in Conventional Example 2, since the filling property of the elastic rubber chip is low, there is a problem that the filling work is troublesome.
【０００５】さらに、従来例３では、ガラスビーズを回
転ブラシにより擦り込み充填すると、加硫ゴムとガラス
ビーズとの比重の関係から、加硫ゴムが表面層に出てし
まい、安定性が悪いという問題がある。本発明は、この
ような従来の問題を解決するためになされたもので、そ
の目的は、施工作業を容易に行えるとともに、良好な接
地感を長期間維持できる砂入り人工芝生を提供すること
にある。Further, in Conventional Example 3, when the glass beads were rubbed and filled with a rotating brush, the vulcanized rubber was exposed to the surface layer due to the specific gravity of the vulcanized rubber and the glass beads, resulting in poor stability. There is. The present invention has been made to solve such a conventional problem, and an object thereof is to provide a sand-filled artificial lawn that can easily perform construction work and can maintain a good ground feeling for a long period of time. is there.
【０００６】[0006]
【課題を解決するための手段】前記目的を達成するため
に、本発明は、パイル間に充填された弾性充填材を覆う
ように粒状充填材が積層充填された砂入り人工芝生にお
いて、前記弾性充填材が互いに交差積層し、それらの間
に空隙が生じる略柱形状に形成されていることを特徴と
している。この場合、弾性充填材の材質としては、弾力
性とともに耐候性を有する適宜なゴム，ビニール，プラ
スチック等が採用できる。また、弾性充填材の形状とし
ては、空隙が生じるように交差積層できればよく、例え
ば断面任意形状の略柱形状，略筒形状等が採用でき、あ
るいは捻れ加工を施した略帯形状であってもよい。To SUMMARY OF THE INVENTION To achieve the above object, the present onset Ming, sand containing artificial lawn of particulate filler to cover the filled elastic filler is laminated filled between piles Contact
Further , the elastic fillers are formed into a substantially columnar shape by cross-laminating with each other and forming a void between them . In this case, as the material of the elastic filler, suitable rubber, vinyl, plastic or the like having elasticity and weather resistance can be adopted. Further, the elastic filler may have any shape as long as it can be cross-laminated so as to form voids. For example, a substantially columnar shape having an arbitrary cross section, a substantially cylindrical shape, or the like, or a substantially strip shape having a twisted shape can be used. Good.
【０００７】 本発明によれば、弾性充填材が交差積層
することによりそれらの間に空隙が生じる。したがっ
て、弾性充填材に積層充填された目砂等の粒状充填材が
競技用スパイク等により突き固められたり、あるいは目
砂，パイルの摩耗屑や通常のごみ，異物等により目砂が
固化しても、弾性充填材の弾力性が確保され、良好な接
地感を長期間維持できることになる。また、弾性充填材
が例えば所定長さを有する略柱形状，略筒形状等に形成
されていることにより、人工芝に絡まり易く、充填性，
安定性を高くでき、充填作業を容易に行え、また、充填
後、パイル間からの充填材の抜け出しを防ぎ、良好な接
地感を長期間維持できることになる。 According to the present invention, the cross-lamination of the elastic filler creates voids between them . Therefore, the granular filler such as sand grains laminated and filled with the elastic filler may be tampered with by the spikes for competition, or the sand grains may be solidified by the sand grains, the abrasion dust of the piles, ordinary dust, and foreign substances. Also, the elasticity of the elastic filler is secured, and a good ground contact feeling can be maintained for a long time. Further, a substantially column shape elastic filler having, for example, a predetermined length, by Rukoto is formed in a substantially tubular shape, easily entangled synthetic grass, filling property,
The stability can be increased, the filling operation can be easily performed, and the filling material can be prevented from coming out from between the piles after the filling, and a good ground contact feeling can be maintained for a long time.
【０００８】 また、本発明は、前記弾性充填材の直径
に対する長さの比率が３以上であることを特徴としてい
るため、弾性充填材の充填性，安定性を一層高くできる
とともに、弾性充填材が互いに交差積層した状態を維持
しやすいことになり、これらにより前記目的が達成され
る。[0008] The present onset bright, because it is characterized in that the ratio of length to diameter of the elastic filler is 3 or more, filling property of the elastic filler, with the stability can be further increased, the elastic filling This makes it easier to maintain the material in a state where the materials are cross-laminated with each other, thereby achieving the above object.
【０００９】[0009]
【発明の実施の形態】以下、本発明の実施例を図面に基
づいて説明する。図１には、本発明に係る一実施例が示
されている。図１（Ａ）に示すように、本実施例におけ
る砂入り人工芝生１０は、例えばテニスコート等の運動
競技場を施工するために、基礎地面１１上に打設された
下地材１２の上に敷設される。この砂入り人工芝生１０
は、面状の基布１３にパイル１４が多数植設されてい
る。そして、パイル１４間には、デッキブラシにより弾
性充填材１５が充填されているとともに、この弾性充填
材１５を覆うように回転ブラシにより砂等の粒状充填材
１６が積層充填されている。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 shows an embodiment according to the present invention. As shown in FIG. 1 (A), a sand-containing artificial lawn 10 according to the present embodiment is placed on a base material 12 placed on a foundation ground 11 in order to construct an athletic field such as a tennis court. Is laid. This artificial lawn with sand 10
A large number of piles 14 are planted on a sheet-like base cloth 13. An elastic filler 15 is filled between the piles 14 by a deck brush, and a granular filler 16 such as sand is stacked and filled by a rotating brush so as to cover the elastic filler 15.
【００１０】図１（Ｂ）に示すように、弾性充填材１５
は、弾力性とともに耐候性を有する、例えばＥＰＤＭゴ
ム等により略円柱形状に形成されている。したがって、
弾性充填材１５は、パイル１４間に充填されると、図１
（Ｃ）に示すように、互いに交差積層して、当該間に空
隙１７が生じるようになっている。また、この弾性充填
材１５は、直径Ｄに対する長さＬの比率が３以上となる
ように形成されているため、パイル１４間に充填される
際、パイル１４に絡み付くことにより容易に充填でき、
かつ、パイル１４間から出てくることはない。As shown in FIG. 1B, the elastic filler 15
Is made of, for example, EPDM rubber having elasticity and weather resistance in a substantially cylindrical shape. Therefore,
When the elastic filler 15 is filled between the piles 14, the elastic filler 15 shown in FIG.
As shown in (C), the layers 17 are cross-laminated with each other so that a space 17 is formed therebetween. Further, since the elastic filler 15 is formed such that the ratio of the length L to the diameter D is 3 or more, it can be easily filled by being entangled with the piles 14 when filled between the piles 14,
Moreover, it does not come out from between the piles 14.
【００１１】以上のような本実施例の砂入り人工芝生１
０によれば、弾性充填材１５間に空隙１７が生じるた
め、弾性充填材１５が弾性変形するための余剰空間が確
保される。したがって、粒状充填材１６が競技用スパイ
ク等により突き固められたり、あるいは当該粒状充填材
１６，パイル１４の磨耗屑や通常のごみ，異物等により
固化しても、良好な接地感を長期間維持できる。The artificial grass with sand 1 of the present embodiment as described above
According to 0, since the voids 17 are formed between the elastic fillers 15, an extra space for elastically deforming the elastic fillers 15 is secured. Therefore, even if the granular filling material 16 is tampered with by a spike for competition, or is solidified by the abrasion dust of the granular filling material 16 and the pile 14, ordinary dust, foreign matter, etc., a good ground contact feeling is maintained for a long time. it can.
【００１２】また、弾性充填材１５は、略円柱形状であ
るため容易に形成でき、砂入り人工芝生１０を安価に施
工できる。さらに、弾性充填材１５は、直径Ｄに対する
長さＬの比率が３以上となる略円柱形状であるためパイ
ル１４に容易に絡みつく。したがって、弾性充填材１５
の充填性を高くできる。一方、弾性充填材１５を覆うよ
うに粒状充填材１６を積層充填するにあたっては、弾性
充填材１５がパイル１４に絡みついているため従来に比
較して安定性が高く、回転ブラシを用いても表面に出て
こない。Further, since the elastic filler 15 has a substantially columnar shape, it can be easily formed, and the sand-filled artificial lawn 10 can be constructed at low cost. Furthermore, since the elastic filler 15 has a substantially columnar shape in which the ratio of the length L to the diameter D is 3 or more, it is easily entangled with the pile 14. Therefore, the elastic filler 15
The filling property of can be increased. On the other hand, when the granular filling material 16 is stacked and filled so as to cover the elastic filling material 15, the elastic filling material 15 is entangled with the pile 14 so that the stability is high as compared with the conventional case, and even if a rotating brush is used, the surface is improved. Does not come out.
【００１３】[0013]
【実施例】次に、弾性充填材１５の直径Ｄと長さＬとの
比率を変えて実際に砂入り人工芝生１０を施工し、弾性
充填材１５の充填性，弾性充填材１５の安定性，仕上が
り後Ｇｍａｘおよび踏み固め後Ｇｍａｘを評価したの
で、表１に基づいて比較例とともに説明する。EXAMPLES Next, the artificial lawn 10 containing sand is actually constructed by changing the ratio of the diameter D and the length L of the elastic filler 15, and the filling property of the elastic filler 15 and the stability of the elastic filler 15 are improved. The post-finishing Gmax and the post-compacting Gmax were evaluated, and will be described with reference to Table 1 together with a comparative example.
【００１４】[0014]
【表１】 [Table 1]
【００１５】なお、弾性充填材の充填性は、弾性充填材
１５の充填が完了するまでに要したデッキブラシの通過
回数により評価し、その回数が少ないものほど優れてい
るとした。また、弾性充填材の安定性は、回転ブラシに
より粒状充填材１６を充填する際、粒状充填材１６の表
面に出てきた弾性充填材１５の有無を視認し、○‥無
し，×‥有りとして評価した。The filling property of the elastic filler was evaluated by the number of times the deck brush passed until the filling of the elastic filler 15 was completed. The smaller the number, the better. In addition, the stability of the elastic filler is determined by checking the presence or absence of the elastic filler 15 that has come out on the surface of the granular filler 16 when the granular filler 16 is filled with a rotating brush, and indicates that there is no circle or no circle. evaluated.
【００１６】一方、仕上がり後Ｇｍａｘは、ＪＩＳ−Ａ
６５１９に基づいて測定を行い、測定数値が小さいほど
良好な接地感が得られるものと評価した。さらに、踏み
固め後Ｇｍａｘは、繰り返し圧縮試験機により３ｋｇ／
平方ｃｍの繰り返し荷重を１０００回与えた後に測定を
行い、測定数値が小さいほど良好な接地感が得られるも
のと評価した。そして、この表において、実施例および
比較例に用いた弾性充填材１５の粒径あるいは直径Ｄに
対する長さＬの比率，１個当たりの重量は、弾性充填材
１５の母集団から任意に１００個サンプリングし、測定
した平均値である。On the other hand, Gmax after finishing is JIS-A
The measurement was performed based on 6519, and it was evaluated that the smaller the measured value, the better the feeling of contact with the ground. Furthermore, the Gmax after compaction is 3 kg /
The measurement was performed after applying a repeated load of square cm 1000 times, and it was evaluated that the smaller the measured value, the better the feeling of contact with the ground. In this table, the ratio of the length L to the particle diameter or diameter D of the elastic fillers 15 used in the examples and comparative examples, and the weight per piece are arbitrarily 100 pieces from the population of the elastic fillers 15. It is the average value measured by sampling.
【００１７】本発明に係る実施例１は、弾性充填材１５
を柱状に形成し、直径Ｄに対して長さＬを３．０４に設
定した。この実施例１では、弾性充填材１５の充填性が
２回評価，弾性充填材１５の安定性が○評価，仕上がり
後Ｇｍａｘが７１，踏み固め後Ｇｍａｘが７３となって
いる。また、本発明に係る実施例２は、弾性充填材１５
を柱状に形成し、直径Ｄに対して長さＬを５．６２に設
定した。この実施例２では、弾性充填材１５の充填性が
２回評価，弾性充填材１５の安定性が○評価，仕上がり
後Ｇｍａｘが７２，踏み固め後Ｇｍａｘが７３となって
いる。The first embodiment according to the present invention is the elastic filler 15.
Was formed into a columnar shape, and the length L was set to 3.04 with respect to the diameter D. In Example 1, the filling property of the elastic filler 15 was evaluated twice, the stability of the elastic filler 15 was evaluated as o, the finished Gmax was 71 and the post-compacting Gmax was 73. In addition, the elastic filler 15 according to the second embodiment of the present invention.
Was formed into a columnar shape, and the length L was set to 5.62 with respect to the diameter D. In Example 2, the filling property of the elastic filler 15 was evaluated twice, the stability of the elastic filler 15 was evaluated as o, the finished Gmax was 72 and the post-compacting Gmax was 73.
【００１８】さらに、本発明に係る実施例３は、弾性充
填材１５を柱状に形成し、直径Ｄに対して長さＬを９．
８７に設定した。この実施例３では、弾性充填材１５の
充填性が１回評価，弾性充填材１５の安定性が○評価，
仕上がり後Ｇｍａｘが７１，踏み固め後Ｇｍａｘが７２
となっている。また、本発明に係る実施例４は、弾性充
填材１５を柱状に形成し、直径Ｄに対して長さＬを３．
０９に設定した。この実施例４では、弾性充填材１５の
充填性が１回評価，弾性充填材１５の安定性が○評価，
仕上がり後Ｇｍａｘが７３，踏み固め後Ｇｍａｘが７３
となっている。そして、本発明に係る実施例５は、弾性
充填材１５を柱状に形成し、直径Ｄに対して長さＬを
３．００に設定した。この実施例５では、弾性充填材１
５の充填性が２回評価，弾性充填材１５の安定性が○評
価，仕上がり後Ｇｍａｘが７１，踏み固め後Ｇｍａｘが
７３となっている。Further, in the third embodiment according to the present invention, the elastic filler 15 is formed in a columnar shape, and the length L is 9.
It was set to 87. In Example 3, the filling property of the elastic filler 15 was evaluated once, and the stability of the elastic filler 15 was evaluated as ◯,
Gmax after finishing is 71, Gmax after treading is 72
Has become. Further, in Example 4 according to the present invention, the elastic filler 15 is formed in a columnar shape, and the length L is 3.
It was set to 09. In Example 4, the filling property of the elastic filler 15 was evaluated once, and the stability of the elastic filler 15 was evaluated as ◯,
Gmax after finishing is 73, Gmax after stamping is 73
Has become. Then, in Example 5 according to the present invention, the elastic filler 15 was formed in a columnar shape, and the length L was set to 3.00 with respect to the diameter D. In this Example 5, the elastic filler 1
The filling property of No. 5 was evaluated twice, the stability of the elastic filling material 15 was evaluated as ◯, Gmax after finishing was 71, and Gmax after compacting was 73.
【００１９】一方、比較例１は、パイル１４間に粒状充
填材のみを充填した。この比較例１では、仕上がり後Ｇ
ｍａｘが８０，踏み固め後Ｇｍａｘが９１となってい
る。また、比較例２は、弾性充填材１５を粒状に形成
し、粒径を１．０ｍｍに設定した。この比較例２では、
弾性充填材１５の充填性が５回評価，弾性充填材１５の
安定性が×評価，仕上がり後Ｇｍａｘが７３，踏み固め
後Ｇｍａｘが８１となっている。On the other hand, in Comparative Example 1, only the granular filler was filled between the piles 14. In this comparative example 1, after finishing G
The max is 80 and the Gmax after the compaction is 91. In Comparative Example 2, the elastic filler 15 was formed in a granular shape and the particle diameter was set to 1.0 mm. In this comparative example 2,
The filling property of the elastic filler 15 is evaluated 5 times, the stability of the elastic filler 15 is evaluated x, the finished Gmax is 73 and the post-compacting Gmax is 81.
【００２０】さらに、比較例３は、弾性充填材１５を粒
状に形成し、粒径を４．９ｍｍに設定した。この比較例
３では、弾性充填材１５の充填性が６回評価，弾性充填
材１５の安定性が×評価，仕上がり後Ｇｍａｘが７３，
踏み固め後Ｇｍａｘが７９となっている。そして、比較
例４は、弾性充填材１５を柱状に形成し、直径Ｄに対し
て長さＬを１．９５に設定した。この比較例４では、弾
性充填材１５の充填性が４回評価，弾性充填材１５の安
定性が×評価，仕上がり後Ｇｍａｘが７１，踏み固め後
Ｇｍａｘが７６となっている。Further, in Comparative Example 3, the elastic filler 15 was formed in a granular shape and the particle diameter was set to 4.9 mm. In Comparative Example 3, the filling property of the elastic filler 15 was evaluated 6 times, the stability of the elastic filler 15 was evaluated x, the Gmax after finishing was 73,
After compaction, Gmax is 79. Then, in Comparative Example 4, the elastic filler 15 was formed in a columnar shape, and the length L was set to 1.95 with respect to the diameter D. In Comparative Example 4, the filling property of the elastic filler 15 was evaluated four times, the stability of the elastic filler 15 was evaluated x, the finished Gmax was 71, and the post-compacting Gmax was 76.
【００２１】以上の評価から、実施例１ないし実施例５
が、弾性充填材１５の充填性，弾性充填材１５の安定
性，仕上がり後Ｇｍａｘおよび踏み固め後Ｇｍａｘにつ
いて、つりあいのとれた高い評価を受けていることが判
る。特に、実施例１ないし実施例５と比較例４とを対比
させると、弾性充填材１５は、直径Ｄに対する長さＬの
比率が３以上であれば、充填性および安定性の評価が格
段に高くなることが判る。From the above evaluations, Examples 1 to 5
However, it is understood that the filling property of the elastic filler 15, the stability of the elastic filler 15, the Gmax after finishing, and the Gmax after compacting have been well-balanced and highly evaluated. In particular, when comparing Examples 1 to 5 with Comparative Example 4, the elastic filler 15 is significantly evaluated for its filling property and stability when the ratio of the length L to the diameter D is 3 or more. It turns out to be high.
【００２２】すなわち、実施例１ないし実施例５は、砂
入り人工芝生１０を施工するにあたって、比較例１ない
し比較例４に比較して、弾性充填材１５および粒状充填
材１６の充填作業を容易に行える。また、実施例１ない
し実施例５では、砂入り人工芝生１０の施工直後から接
地感の変化が少なく、例えばテニスコート等に採用した
場合、常に一定した条件を維持できる。That is, in Examples 1 to 5, in constructing the artificial lawn 10 containing sand, compared with Comparative Examples 1 to 4, the filling work of the elastic filler 15 and the granular filler 16 is easier. You can do it. In addition, in Examples 1 to 5, there is little change in the feeling of contact with the ground immediately after construction of the sand-containing artificial grass 10. For example, when the artificial grass 10 is used in a tennis court or the like, a constant condition can be maintained.
【００２３】 なお、本発明は前述した実施例に限定さ
れるものではなく、本発明を達成できる範囲での改良，
変形等は本発明に含まれるものである。例えば、弾性充
填材の形状としては、互いに交差積層し、当該間に空隙
が生じるような形状であればよく、図２（Ａ）に示す弾
性充填材２０のような略角柱形状でもよく、あるいは図
２（Ｂ）に示す弾性充填材２１のような略鹿尾菜（ひじ
き）形状でもよい。また、図２（Ｃ）に示す弾性充填材
２２は、捻れ加工が施された略帯形状とされている。こ
の弾性充填材２２は、互いに交差積層しても面同士が密
着せず、当該間に空隙を形成できるようになっている。It should be noted that the present invention is not limited to the above-described embodiments, and improvements within a range in which the present invention can be achieved,
Modifications and the like are included in the present invention. For example, the elastic filler may have any shape as long as it has a shape in which air gaps are formed between layers of the elastic filler, and may be a substantially prismatic shape such as the elastic filler 20 shown in FIG. The elastic filler 21 shown in FIG. 2 (B) may have a substantially sardine shape. Further, the elastic filler 22 shown in FIG. 2 (C) has a substantially band shape that is twisted. The elastic filler 2 2 do not contact the faces thereof also cross-laminated to one another, so as to form a gap between the.
【００２４】そして、弾性充填材の材質としては、弾力
性とともに耐候性を有する適宜なゴム，ビニール，プラ
スチック等が採用できる。その他、前記実施例で示した
弾性充填材，粒状充填材の材質，形状，寸法，充填量等
は本発明を達成できるものであれば任意であり、限定さ
れない。また、本発明に係るパイルとしては、捲縮タイ
プのパイルを用いることも可能であり、これによれば、
粒状充填材の抜け出しがより確実に防止できる。As the material of the elastic filler, suitable rubber, vinyl, plastic or the like having elasticity and weather resistance can be adopted. In addition, the material, shape, size, filling amount and the like of the elastic filler and the granular filler shown in the above-mentioned embodiment are arbitrary and are not limited as long as the present invention can be achieved. Further, as the pile according to the present invention, it is also possible to use a crimp type pile, and according to this,
It is possible to more reliably prevent the granular filler from coming off.
【００２５】[0025]
【発明の効果】以上説明したように、請求項１に記載し
た発明によれば、充填作業を容易に行えるとともに、良
好な接地感を長期間維持できる。また、弾性充填材を容
易に成形できる。さらに、請求項２に記載した発明によ
れば、弾性充填材の充填性，安定性を一層高くできると
ともに、弾性充填材が互いに交差積層した状態を維持し
やすくできる。As described above , according to the first aspect of the present invention, the filling operation can be easily performed, and a good ground contact feeling can be maintained for a long period of time. Moreover, it can be easily molded elastic filler. Furthermore, according to the invention described in 請 Motomeko 2 can be filled elastic filler, with the stability can be further increased, easily remain elastic filler is cross-laminated with each other.
【図１】本発明の一実施例を示す断面図および斜視図で
ある。FIG. 1 is a sectional view and a perspective view showing an embodiment of the present invention.
【図２】本発明の変形例を示す斜視図である。FIG. 2 is a perspective view showing a modified example of the present invention.
１０ 砂入り人工芝生 １４ パイル １５，２０，２１，２２ 弾性充填材 １６ 粒状充填材 １７ 空隙 Ｄ 直径 Ｌ 長さ 10 Artificial grass with sand 14 piles 15,20,21,22 Elastic filler 16 Granular filler 17 void D diameter L length
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平５−171611（ＪＰ，Ａ) 実開 平７−4504（ＪＰ，Ｕ) 実開 平６−1405（ＪＰ，Ｕ) 実開 昭58−46371（ＪＰ，Ｕ) 特公 昭63−39725（ＪＰ，Ｂ２) 実公 昭64−6862（ＪＰ，Ｙ２) (58)調査した分野(Int.Cl.7，ＤＢ名) E01C 13/08 E01C 13/00 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-5-171611 (JP, A) Actually open 7-4504 (JP, U) Actually open 6-1405 (JP, U) Actually open 58- 46371 (JP, U) JP-B 63-39725 (JP, B2) JP-B 64-6862 (JP, Y2) (58) Fields investigated (Int.Cl. 7 , DB name) E01C 13/08 E01C 13 / 00
Claims (2)
ように粒状充填材が積層充填された砂入り人工芝生にお
いて、 前記弾性充填材が互いに交差積層し、それらの間に空隙
が生じる略柱形状に形成されていることを特徴とする砂
入り人工芝生。1. A sand-filled artificial lawn in which granular fillers are laminated and filled so as to cover elastic fillers filled between piles .
There are, the elastic filler is cross-laminated with each other, containing sand artificial turf, characterized in that it is formed in a substantially prism shape a gap is formed between them.
率が３以上であることを特徴とする請求項１に記載した
砂入り人工芝生。2. A ratio of length to diameter of the elastic filler.
The artificial lawn with sand according to claim 1, wherein the rate is 3 or more .