JP3046633B2 - Transfer foil - Google Patents
Transfer foilInfo
- Publication number
- JP3046633B2 JP3046633B2 JP3062137A JP6213791A JP3046633B2 JP 3046633 B2 JP3046633 B2 JP 3046633B2 JP 3062137 A JP3062137 A JP 3062137A JP 6213791 A JP6213791 A JP 6213791A JP 3046633 B2 JP3046633 B2 JP 3046633B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- weight
- transfer foil
- polyamide
- polypropylene film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明はゴルフボール、特にはア
イオノマー樹脂を外皮にに持つゴルフボール用の転写箔
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf ball, and more particularly to a transfer foil for a golf ball having an ionomer resin as an outer skin.
【0002】[0002]
【従来の技術】従来ゴルフボール用の転写箔としては、
特公昭63−44558号明細書に示されるように、ポ
リプロピレンフィルム上にNC(ニトロセルロース)/
アルキッド系インキを用いて所望の文字を設ける方法が
あった。しかしこの方法ではNC/アルキッド系インキ
のポリプロピレンフィルムからの剥離強度と、NC/ア
ルキッド系インキのゴルフボールに対する接着強度とに
余り差異がなく、転写時に文字の一部に欠けを生じるな
どの欠点を有していた。また、NC/アルキッド系イン
キの自体アイオノマー樹脂に対する密着性もそれほど強
固でないという基本的な問題も有しており、サンドブラ
スト等の表面処理を必要とするという問題点を有してい
た。2. Description of the Related Art Conventional transfer foils for golf balls include:
As shown in JP-B-63-44558, NC (nitrocellulose) /
There has been a method of providing desired characters using an alkyd-based ink. However, in this method, there is not much difference between the peel strength of the NC / alkyd-based ink from the polypropylene film and the adhesive strength of the NC / alkyd-based ink to a golf ball, and disadvantages such as partial chipping during transfer are caused. Had. Further, there is also a basic problem that the adhesion of the NC / alkyd-based ink itself to the ionomer resin is not so strong, and there is a problem that a surface treatment such as sandblasting is required.
【0003】[0003]
【発明が解決しようとする課題】本発明は以上のように
従来技術の欠点を解消しようとするものであって、転写
時に文字等の一部に欠けを生じることなどがなく、また
サンドブラスト処理等の表面処理を必要しないゴルフボ
ール用転写箔を提供するものである。SUMMARY OF THE INVENTION The present invention has been made to solve the drawbacks of the prior art as described above, and does not cause a part of characters or the like to be chipped at the time of transfer. The present invention provides a golf ball transfer foil that does not require a surface treatment.
【0004】[0004]
【問題点を解決するための手段】本発明は、上記問題点
を解決したもので、ポリプロピレンフィルムの表面に、
セルロース誘導体とポリアマイドからなる主剤100重
量部に、塩素化ポリオレフィン樹脂を0.5〜2.0重
量部添加したインキにて文字や絵柄等を印刷したことを
特徴とするゴルフボール用の転写箔である。Means for Solving the Problems The present invention has solved the above problems, and has the following features:
100 weight base agent composed of cellulose derivative and polyamide
The amount unit, a chlorinated polyolefin resin of 0.5 to 2.0-fold
A transfer foil for a golf ball, wherein characters, pictures, and the like are printed with ink added in an amount .
【0005】本発明に於けるポリプロピレンフィルムは
2軸延伸フィルム(OPPフィルム)の方が無延伸フィ
ルム(CPP)に比較して引っ張り強度が高いため取扱
いが容易で作業性が良く、また見当精度も良好である。In the polypropylene film of the present invention, the biaxially stretched film (OPP film) has a higher tensile strength than the non-stretched film (CPP), so that it is easy to handle, has good workability, and has high register accuracy. Good.
【0006】厚みとしては20〜60μが一般的である
が、ゴルフボールの表面(以下ディンプル)への転写性
の点からは20μの厚みのものが良好であった。The thickness is generally 20 to 60 μm, but the thickness of 20 μm is good from the viewpoint of transferability to the surface of a golf ball (hereinafter, dimple).
【0007】またより剥離力を軽くするためにはコロナ
放電処理をしない未処理のフィルムを使用すねることも
可能である。ただし、剥離力が過度に低下し、インキが
脱落しやすくなる弊害もあるため使い分けが必要であ
る。In order to further reduce the peeling force, it is possible to use an untreated film which is not subjected to a corona discharge treatment. However, there is a problem that the peeling force is excessively reduced and the ink easily falls off.
【0008】インキのバインダーとしては、セルロース
誘導体とポリアマイドを主体とした樹脂がポリプロピレ
ンフィルムからの剥離強度の点及びアイオノマー樹脂に
対する密着性の点で優れていた。As a binder for the ink, a resin mainly composed of a cellulose derivative and a polyamide was excellent in terms of peel strength from a polypropylene film and adhesion to an ionomer resin.
【0009】セルロース誘導体はポリプロピレンフィル
ムからの剥離性を向上させる役割のもので、アセチルセ
ルロース、エチルセルロース、ニトロセルロースが良く
用いられるが特にこれらの樹脂に限定されるものではな
い。The cellulose derivative has a role of improving the releasability from the polypropylene film, and acetylcellulose, ethylcellulose and nitrocellulose are often used, but are not particularly limited to these resins.
【0010】ポリアマイドはアイオノマー樹脂に対する
密着性を改善するものであるが、過剰な配合はポリプロ
ピレンフィルムから剥離性を損ねる。[0010] Polyamides improve the adhesion to ionomer resins, but excessive blending impairs the releasability from polypropylene films.
【0011】実験により適性な配合はニトロセルロース
/ポリアマイド=50/50〜70/30の範囲であっ
た。Experiments have shown that a suitable formulation ranged from nitrocellulose / polyamide = 50/50 to 70/30.
【0012】しかるにこれのみでは、アイオノマー樹脂
に対する密着性が十分とはいえない。特にサンドブラス
ト等の表面処理を施していない場合密着性が不十分であ
る。However, this alone does not provide sufficient adhesion to the ionomer resin. In particular, when surface treatment such as sandblasting is not performed, the adhesion is insufficient.
【0013】此の問題は塩素化ポリレフィンを主剤(セ
ルロース誘導体+ポリアマイド)100重量部に対して
0.5〜2.0重量部添加することにより密着性が著し
く改善した。This problem was remarkably improved by adding 0.5 to 2.0 parts by weight of chlorinated polyolefin to 100 parts by weight of the main agent (cellulose derivative + polyamide).
【0014】以上のようにポリプロピレンフィルムの表
面に、セルロース誘導体とポリアマイドからなる主剤1
00重量部に、塩素化ポリオレフィン樹脂を0.5〜
2.0重量部添加したインキにて文字や絵柄等を印刷す
ることにより、転写性に優れるゴルフボール用転写箔を
得ることが可能となった。As described above, the main component 1 comprising a cellulose derivative and a polyamide is formed on the surface of a polypropylene film.
00 parts by weight, 0.5 to chlorinated polyolefin resin
By printing characters or figures such as Te 2.0 parts by weight of the added ink, it has become possible to obtain a transfer foil for a golf ball having excellent transferability.
【0015】[0015]
【作用】従来の方法では、ポリプロピレンフィルムから
の剥離力とアイオノマー樹脂への密着力のバランスを調
整することが困難であり、従って良好な転写性が得られ
なかった。With the conventional method, it is difficult to adjust the balance between the peeling force from the polypropylene film and the adhesive force to the ionomer resin, and therefore, good transferability cannot be obtained.
【0016】本発明では、セルロース誘導体とポリアマ
イドと塩素化ポリオレフィン樹脂の適性な配合比により
良好な転写性を得ることを可能とした。In the present invention, it is possible to obtain a good transfer property by an appropriate mixing ratio of the cellulose derivative, the polyamide and the chlorinated polyolefin resin.
【0017】すなわち基材フィルムにポリプロピレンを
採用することにより、過度な剥離力を得ることができ、
またゴルフボール表面の凹部(ディンプル)への転写性
を良好ならしめた。That is, by using polypropylene for the base film, an excessive peeling force can be obtained,
Further, the transferability to the concave portions (dimples) on the golf ball surface was improved.
【0018】インキのバインダーとしてはセルロース誘
導体がポリプロピレンフィルムから剥離強度低下をポリ
アマイドがアイオノマー樹脂に対する密着性向上させる
役目をなし、かつその配合は、ニトロセルロース/ポリ
アマイド=50/50〜70/30の範囲が適正であ
る。As the binder for the ink, the cellulose derivative serves to reduce the peel strength of the polypropylene film from the polypropylene film, and the polyamide serves to improve the adhesion to the ionomer resin, and its composition is in the range of nitrocellulose / polyamide = 50/50 to 70/30. Is appropriate.
【0019】セルロース誘導体が少ないと(ポリアマイ
ドが多いと)ポリプロピレンフィルムからの剥離強度が
重過ぎ、うまく剥離せず、ポリアマイドが少ないと(セ
ルロース誘導体が多いと)剥離強度は軽くなるがアイオ
ノマー樹脂に対する密着強度が低下し転写がうまくなさ
れないか、転写ができても極めて弱い密着力となる。When the amount of the cellulose derivative is small (when the amount of the polyamide is large), the peel strength from the polypropylene film is too heavy and the film is not peeled off. The strength is reduced and transfer is not performed well, or even if transfer is performed, the adhesion becomes extremely weak.
【0020】さらに塩素化ポリレフィンを主剤(セルロ
ース誘導体+ポリアマイド)100重量部に対して0.
5〜2.0重量部添加することにより、サンドブラスト
等の表面処理を施していないアイオノマー樹脂表面に対
する密着も可能となった。Further, chlorinated polyolefin is used as a base material (cellulose derivative + polyamide) in an amount of 0.1 part by weight based on 100 parts by weight .
By adding 5 to 2.0 parts by weight, adhesion to the surface of the ionomer resin that has not been subjected to surface treatment such as sandblasting has also become possible.
【0021】[0021]
【実施例】厚さ20μのポリプロピレンフィルムの表面
に、下記のような配合の樹脂をバインダーとしたイン
キ、 ニトロセルロース 60重量部 ポリアマイド 40重量部 塩素化ポリプロピレン 1重量部 を作成し、ゴルフボールの品名とマークを印刷し転写箔
とした。EXAMPLE An ink using a resin having the following composition as a binder, nitrocellulose 60 parts by weight , polyamide 40 parts by weight , and chlorinated polypropylene 1 part by weight was prepared on the surface of a polypropylene film having a thickness of 20 μm. And a mark were printed to obtain a transfer foil.
【0022】この転写箔を130°C・1秒の転写条件
で転写したところ剥離強度も軽く、ディンプルの細部ま
で転写されたゴルフボールが得られた。When this transfer foil was transferred under a transfer condition of 130 ° C. for 1 second, a peeling strength was low, and a golf ball transferred to the details of the dimple was obtained.
【0023】[0023]
【効果】本発明は以上の如き構成であって、 ( 1)剥離強度が軽く接着強度が高いため転写性に優れ
る。 ( 2)サンドブラスト等の表面処理を施していないアイオ
ノマー樹脂表面に対する密着も可能。 ( 3)2軸延伸フィルム(0PPフィルム)ポリプロピレ
ンを使用すれば引っ張り強度が高いため取扱いが容易で
作業性が良い。 ( 4)20μのポリプロピレンフィルムの使用でゴルフボー
ル表面の凹部(ディンプル )の転写性に優れる。という
効果を有している。(Effects) The present invention is configured as described above. (1) Since the peel strength is low and the adhesive strength is high, transferability is excellent. (2) Adhesion to ionomer resin surface not subjected to surface treatment such as sandblasting is also possible. (3) If a biaxially stretched film (0PP film) polypropylene is used, it is easy to handle and has good workability because of high tensile strength. (4) Use of a 20μ polypropylene film provides excellent transferability of concave portions (dimples) on the golf ball surface. This has the effect.
Claims (2)
ース誘導体とポリアマイドからなる主剤100重量部
に、塩素化ポリオレフィン樹脂を0.5〜2.0重量部
添加したインキにて文字や絵柄等を印刷したことを特徴
とする転写箔。1. A cellulose film is coated on the surface of a polypropylene film.
DerivativesWhenPolyamide100 parts by weight of a main ingredient consisting of
Chlorinated polyolefin resin, 0.5 to 2.0weightDepartment
Characterized by printing letters and pictures with added ink
Transfer foil.
しない未処理のフィルムを使用することを特徴とする請
求項第1項記載の転写箔。2. The transfer foil according to claim 1, wherein an untreated film not subjected to corona discharge treatment is used as the polypropylene film.