JPH04213375A - Gravure ink for heat lamination - Google Patents
Gravure ink for heat laminationInfo
- Publication number
- JPH04213375A JPH04213375A JP2401340A JP40134090A JPH04213375A JP H04213375 A JPH04213375 A JP H04213375A JP 2401340 A JP2401340 A JP 2401340A JP 40134090 A JP40134090 A JP 40134090A JP H04213375 A JPH04213375 A JP H04213375A
- Authority
- JP
- Japan
- Prior art keywords
- lamination
- gravure ink
- weight percent
- binder
- gunze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】0001
【産業上の利用分野】本発明は熱ラミネーション用グラ
ビアインキに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a gravure ink for thermal lamination.
【0002】0002
【従来の技術】従来、印刷フィルムのラミネーションの
工業的方法として、次の方法がある。(イ)ドライラミ
ネーションインキが印刷してある面に、接着剤を塗布し
、乾燥後、他のシーラントフィルムをロール間で熱圧着
する方法。2. Description of the Related Art Conventionally, there are the following industrial methods for laminating printed films. (a) A method in which adhesive is applied to the surface printed with dry lamination ink, and after drying, another sealant film is bonded under heat between rolls.
【0003】(ロ)エクストル−ジョンラミネーション
インキが印刷してある面に、アンカ−剤を塗布し、その
上にLDPEを代表とする熱熔触接着性材料をエクスト
ル−ダ−から熔触薄膜状態にてスリットより押し出して
張り合わせる方法。しかし、これらの方法は接着剤やア
ンカ−剤を使用しなければならず、したがって製造費、
残留溶剤量及びエージング時間の点で問題があった。(b) An anchor agent is applied to the surface printed with extrusion lamination ink, and a hot melt adhesive material, typically LDPE, is melted into a thin film from an extruder on top of the anchor agent. A method of extruding through the slit and pasting it together. However, these methods require the use of adhesives or anchoring agents, thus increasing manufacturing costs and
There were problems with the amount of residual solvent and aging time.
【0004】0004
【発明が解決しょうとする課題】本発明者らは、特定の
印刷インキを使用することで、ドライラミネート用等の
接着剤を不要とし、接着剤の塗布に起因する残留溶剤を
無くし、さらに接着剤のエージング時間をも不要とする
ことを目的として研究を進めた結果、本発明に到達した
。[Problems to be Solved by the Invention] The present inventors have discovered that by using a specific printing ink, adhesives such as those for dry lamination are unnecessary, residual solvents caused by adhesive application are eliminated, and adhesive As a result of research aimed at eliminating the need for aging time for agents, the present invention was achieved.
【0005】[0005]
【課題を解決するための手段】本発明は、エチレン酢酸
ビニル共重合体、塩素化ポリプロピレン及び塩化ビニル
イソブチルビニルエーテル共重合体をバインダーとして
含有することを特徴とする熱ラミネーション用グラビア
インキに関するものである。本発明に係わる熱ラミネー
ション用グラビアインキは、バインダ−としてはエチレ
ン酢酸ビニル共重合体、塩素化ポリプロピレン及び塩化
ビニルイソブチルビニルエーテル共重合体を含有し、必
要に応じて環化ゴムをさらに含有する。[Means for Solving the Problems] The present invention relates to a gravure ink for thermal lamination, characterized in that it contains an ethylene vinyl acetate copolymer, a chlorinated polypropylene, and a vinyl chloride isobutyl vinyl ether copolymer as a binder. . The gravure ink for thermal lamination according to the present invention contains an ethylene vinyl acetate copolymer, a chlorinated polypropylene, and a vinyl chloride isobutyl vinyl ether copolymer as a binder, and further contains a cyclized rubber as required.
【0006】エチレン酢酸ビニル共重合体は、酢酸ビニ
ル含有量が35重量%〜45重量%、分子量が8000
〜15000のものが好ましい。塩素化ポリプロピレン
は、分子量が10000〜30000、塩素化度が15
%〜40%のものが好ましい。塩化ビニルイソブチルビ
ニルエーテル共重合体は、例えば、BASF社製のラロ
フレックスMP25、ラロフレックスMP35、ラロフ
レックスMP45、ラロフレックスMP60が使用可能
であるが、ラロフレックスMP45が最も好ましい。エ
チレン酢酸ビニル共重合体と塩素化ポリプロピレンとの
使用割合は、重量比で20:80〜60:40とするこ
とが好ましい。また、塩化ビニルイソブチルビニルエー
テル共重合体の使用割合は、重量比で、エチレン酢酸ビ
ニル共重合体と塩素化ポリプロピレンの合計を100と
すると20〜40とすることが好ましい。The ethylene vinyl acetate copolymer has a vinyl acetate content of 35% to 45% by weight and a molecular weight of 8000.
~15,000 is preferred. Chlorinated polypropylene has a molecular weight of 10,000 to 30,000 and a degree of chlorination of 15.
% to 40% is preferred. As the vinyl chloride isobutyl vinyl ether copolymer, for example, Laroflex MP25, Laroflex MP35, Laroflex MP45, and Laroflex MP60 manufactured by BASF can be used, but Laroflex MP45 is most preferable. The ratio of the ethylene vinyl acetate copolymer to the chlorinated polypropylene used is preferably 20:80 to 60:40 by weight. The proportion of the vinyl chloride isobutyl vinyl ether copolymer used is preferably 20 to 40 in terms of weight ratio, where the total of the ethylene vinyl acetate copolymer and the chlorinated polypropylene is 100.
【0007】本発明に係わる熱ラミネーション用グラビ
アインキは、通常のグラビアインキと同様に有機溶剤、
顔料及び必要に応じて添加剤を含有する。有機溶剤の種
類としては、トルエン、キシレン、n−ヘキサン、シク
ロヘキサン、酢酸メチル、酢酸エチル、酢酸イソプロピ
ル、酢酸−n−プロピル、酢酸−n−ブチル、酢酸第二
ブチル、メタノール、エタノール、n−プロピルアルコ
ール、イソプロピルアルコール、n−ブチルアルコール
、イソブチルアルコール、第2ブチルアルコール、アセ
トン、メチルエチルケトン、メチルイソブチルケトン、
プロピレングリコールモノエチルエーテル、プロピレン
グリコールモノエチルエーテル、プロピレングリコール
モノエチルエーテルアセテート、エチレングリコールモ
ノメチルエーテル、エチレングリコールモノメチルエー
テルアセテート、エチレングリコールモノエチルエーテ
ル、エチレングリコールモノエチルエーテルアセテート
、石油系炭化水素溶剤が使用可能である。[0007] The gravure ink for thermal lamination according to the present invention, like ordinary gravure inks, uses an organic solvent,
Contains pigments and additives if necessary. Types of organic solvents include toluene, xylene, n-hexane, cyclohexane, methyl acetate, ethyl acetate, isopropyl acetate, n-propyl acetate, n-butyl acetate, sec-butyl acetate, methanol, ethanol, n-propyl Alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, sec-butyl alcohol, acetone, methyl ethyl ketone, methyl isobutyl ketone,
Propylene glycol monoethyl ether, propylene glycol monoethyl ether, propylene glycol monoethyl ether acetate, ethylene glycol monomethyl ether, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate, petroleum hydrocarbon solvents are used It is possible.
【0008】顔料としては通常のグラビアインキ用顔料
が使用可能であり、例えばモノアゾ系、ジスアゾ系、フ
タロシアニン系、ジオキサジン系等の有機顔料や二酸化
チタン、酸化第二鉄等の無機顔料及びカ−ボンブラック
が使用可能である。添加剤としては、ポリエチレンワッ
クス、アマイドワックス等の滑剤や静電防止剤を使用す
ることができる。As the pigment, ordinary pigments for gravure ink can be used, such as organic pigments such as monoazo, disazo, phthalocyanine, and dioxazine, inorganic pigments such as titanium dioxide and ferric oxide, and carbon. Black is available. As additives, lubricants such as polyethylene wax and amide wax and antistatic agents can be used.
【0009】処理二軸延伸ポリプロピレンフィルム(以
下、処理OPPフィルムと略す)に本発明に係わる熱ラ
ミネーション用グラビアインキを使用して印刷し、次い
で処理シーラントフィルムをグンゼ(株)製GTLラミ
ネート機等を使用して熱圧着することによりラミネート
することができる。この用途に使用することができる熱
ラミネーション可能な処理OPPフィルムとしてはグン
ゼ(株)にて開発されたシルファンLAGタイプがある
。シーラントフィルムとしては、一般の処理無延伸ポリ
プロピレンフィルム(以下、処理CPPフィルムと略す
)が使用可能である。[0009] A treated biaxially oriented polypropylene film (hereinafter abbreviated as treated OPP film) is printed using the gravure ink for thermal lamination according to the present invention, and then the treated sealant film is printed using a GTL laminating machine manufactured by Gunze Co., Ltd., etc. It can be laminated by thermocompression bonding. A thermally laminable treated OPP film that can be used for this purpose is the SILFAN LAG type developed by Gunze Co., Ltd. As the sealant film, a general treated unstretched polypropylene film (hereinafter abbreviated as treated CPP film) can be used.
【0010】熱ラミネーションに使用可能なラミネート
機としては、グンゼ(株)に於いて作成されたGTLラ
ミネート機を挙げることができる本発明に係わる熱ラミ
ネーション用グラビアインキを印刷した処理OPPフィ
ルムと処理CPPフィルムとの熱ラミネーションの条件
としては、温度90℃〜150℃、圧力20kg/cm
2〜60kg/cm2、ラミネート速度50m/分〜1
80m/分である。特に好ましい条件としては、温度1
15℃〜125℃、圧力35kg/cm2〜45kg/
cm2、ラミネート速度120m/分〜130m/分で
ある。[0010] As a laminating machine that can be used for thermal lamination, a GTL laminating machine manufactured by Gunze Co., Ltd. can be mentioned. Treated OPP film and treated CPP printed with gravure ink for thermal lamination according to the present invention can be mentioned. The conditions for thermal lamination with the film are a temperature of 90°C to 150°C and a pressure of 20kg/cm.
2~60kg/cm2, lamination speed 50m/min~1
The speed is 80m/min. Particularly preferable conditions include temperature 1
15℃~125℃, pressure 35kg/cm2~45kg/
cm2, and the laminating speed is 120 m/min to 130 m/min.
【0011】この方法によるラミネート物は、50g/
15mm〜200g /15mm(T形剥離、速度20
0mm/分)のラミネート強度を示す。また、残留溶剤
量は、従来のドライラミネーションのようにラミネート
加工により残留溶剤量が増加する傾向はなく、むしろ低
下する傾向にあり、1.5mg/m2〜3.0mg/m
2以下となる。[0011] The laminate produced by this method has a weight of 50g/
15mm~200g/15mm (T-peel, speed 20
0 mm/min). Furthermore, unlike conventional dry lamination, the amount of residual solvent does not tend to increase due to lamination processing, but rather tends to decrease, ranging from 1.5 mg/m2 to 3.0 mg/m2.
2 or less.
【0012】0012
【実施例】以下、実施例とともに本発明を説明する。
実施例1
サンドミルにより次のような配合の熱ラミネーション用
グラビアインキを調整した。
酸化チタン 30.0 重量パ−
セントバインダ− 9.0
重量パ−セント有機溶剤 60
.0 重量パ−セントポリエチレンワックス 0.
8 重量パ−セント静電防止剤
0.2 重量パ−セント ここでバインダ−組
成は次の通りである。
エチレン酢酸ビニル共重合体
35.5 重量パ−セント塩素化ポリプ
ロピレン
39.5 重量パーセント塩化ビニルイソブチ
ルビニルエーテル共重合体 25.0 重量パ−セ
ントまた、有機溶剤組成は次の通りである。
トルエン 50.0
重量パ−セント酢酸エチル
15.0 重量パ−セントメチルエチルケトン
30.0 重量パ−セントイソプロピルア
ルコ−ル 5.0 重量パ−セント得られた熱
ラミネーション用グラビアインキを使用してグンゼシル
ファンLAG#40(グンゼ社製処理OPPフィルム)
に印刷し、次いでグンゼ社製GTLラミネート機を使用
してラミネート速度120m/分、ラミネート温度13
2℃でシーラントフィルムとしてトーセロCHC#20
(東セロ社製処理CPPフィルム)を熱圧着することに
より、グンゼシルファンLAG#40にトーセロCHC
#20をラミネートした。[Examples] The present invention will be explained below with reference to Examples. Example 1 A gravure ink for thermal lamination having the following formulation was prepared using a sand mill. Titanium oxide 30.0 Weight percent
Saint Binder 9.0
Weight percent organic solvent 60
.. 0 weight percent polyethylene wax 0.
8 Weight percent antistatic agent
0.2 weight percent Here, the binder composition is as follows. Ethylene vinyl acetate copolymer
35.5 Weight percent chlorinated polypropylene
39.5 weight percent Vinyl chloride isobutyl vinyl ether copolymer 25.0 weight percent The organic solvent composition is as follows. Toluene 50.0
Weight percent ethyl acetate
15.0 Weight percent methyl ethyl ketone
30.0% by weight Isopropyl alcohol 5.0% by weight Using the obtained gravure ink for thermal lamination, Gunze Silphan LAG #40 (treated OPP film manufactured by Gunze Co., Ltd.)
and then using a Gunze GTL laminating machine at a laminating speed of 120 m/min and a laminating temperature of 13
Torcello CHC#20 as a sealant film at 2℃
By thermo-compression bonding (treated CPP film made by Tocello Co., Ltd.), Tocello CHC is attached to Gunze Silfan LAG #40.
#20 was laminated.
【0013】得られたラミネートフィルムのラミネート
強度及び残留溶剤量を測定すると、次の通りであった。
実施例2
サンドミルにより次のような配合の熱ラミネーション用
グラビアインキを調整した。二酸化チタン
30.0 重量パ−セント
バインダ− 9.0 重量パ
−セント有機溶剤 60.0
重量パ−セントポリエチレンワックス 0.8
重量パ−セント静電防止剤 0
.2 重量パ−セントここでバインダ−組成は次の通
りである。
エチレン酢酸ビニル共重合体
20.0 重量パ−セント塩素化ポリプ
ロピレン
55.0 重量パーセント塩化ビニルイソブチ
ルビニルエーテル共重合体 25.0 重量パ−セ
ントまた有機溶剤組成は次の通りである。トルエン
50.0 重量パ−セント
酢酸エチル 15.0 重量
パ−セントメチルエチルケトン 30.0 重
量パ−セントイソプロピルアルコ−ル 5.0 重
量パ−セント得られた熱ラミネーション用グラビアイン
キを使用してグンゼシルファンLAG#40(グンゼ社
製処理OPPフィルム)に印刷し、次いでグンゼ社製G
TLラミネート機を使用してラミネート速度120m/
分、ラミネート温度132℃でシーラントフィルムとし
てトーセロCHC#20(東セロ社製処理CPPフィル
ム)を熱圧着することにより、グンゼシルファンLAG
#40にトーセロCHC#20をラミネートした。The lamination strength and residual solvent amount of the obtained laminated film were measured and found to be as follows. Example 2 A gravure ink for thermal lamination having the following formulation was prepared using a sand mill. titanium dioxide
30.0 Weight percent binder 9.0 Weight percent Organic solvent 60.0
Weight percent polyethylene wax 0.8
Weight percent antistatic agent 0
.. 2 weight percent, where the binder composition is as follows: Ethylene vinyl acetate copolymer
20.0 weight percent chlorinated polypropylene
55.0 Weight percent Vinyl chloride isobutyl vinyl ether copolymer 25.0 Weight percent The organic solvent composition is as follows. toluene
50.0% by weight Ethyl acetate 15.0% by weight Methyl ethyl ketone 30.0% by weight Isopropyl alcohol 5.0% by weight Gunze Silphan using the obtained gravure ink for thermal lamination Print on LAG #40 (treated OPP film manufactured by Gunze), then print on LAG #40 (treated OPP film manufactured by Gunze)
Using TL laminating machine, laminating speed 120m/
Gunze Silphan LAG
Torcello CHC #20 was laminated onto #40.
【0014】得られたラミネートフィルムのラミネート
強度及び残留溶剤量を測定すると、次の通りであった。
実施例3サンドミルにより次のような配合の熱ラミネー
ション用グラビアインキを調整した。二酸化チタン
30.0 重量パ−セント
バインダ− 9.0 重量パ
−セント有機溶剤 60.0
重量パ−セントポリエチレンワックス 0.8
重量パ−セント静電防止剤 0
.2 重量パ−セントここでバインダ−組成は次の通
りである。
エチレン酢酸ビニル共重合体
15.0 重量パ−セント塩素化ポリプ
ロピレン
65.0 重量パーセント塩化ビニルイソブチ
ルビニルエーテル共重合体 20.0 重量パ−セ
ントまた有機溶剤組成は次の通りである。トルエン
50.0重量パ−セント
酢酸エチル 15.0
重量パ−セントメチルエチルケトン 30.
0 重量パ−セントイソプロピルアルコ−ル
5.0 重量パ−セント得られた熱ラミネーション用
グラビアインキを使用してグンゼシルファンLAG#4
0(グンゼ社製処理OPPフィルム)に印刷し、次いで
グンゼ社製GTLラミネート機を使用してラミネート速
度120m/分、ラミネート温度132℃でシーラント
フィルムとしてトーセロCHC#20(東セロ社製処理
CPPフィルム)を熱圧着することにより、グンゼシル
ファンLAG#40)にトーセロCHC#20をラミネ
ートした。The lamination strength and residual solvent amount of the obtained laminated film were measured and found to be as follows. Example 3 A gravure ink for thermal lamination having the following formulation was prepared using a sand mill. titanium dioxide
30.0 Weight percent binder 9.0 Weight percent Organic solvent 60.0
Weight percent polyethylene wax 0.8
Weight percent antistatic agent 0
.. 2 weight percent, where the binder composition is as follows: Ethylene vinyl acetate copolymer
15.0 Weight percent chlorinated polypropylene
65.0 Weight percent Vinyl chloride isobutyl vinyl ether copolymer 20.0 Weight percent The organic solvent composition is as follows. toluene
50.0 weight percent ethyl acetate 15.0
Weight percent methyl ethyl ketone 30.
0 weight percent isopropyl alcohol
5.0 weight percent Gunze Silfan LAG #4 using the obtained thermal lamination gravure ink
0 (treated OPP film manufactured by Gunze Corporation), and then printed on Tocello CHC #20 (treated CPP film manufactured by Tocello Corporation) as a sealant film using a GTL laminating machine manufactured by Gunze Corporation at a laminating speed of 120 m/min and a lamination temperature of 132°C. Tocello CHC #20 was laminated onto Gunze Silfan LAG #40) by thermocompression bonding.
【0015】得られたラミネートフィルムのラミネート
強度及び残留溶剤量を測定すると、次の通りであった。
実施例4
実施例1で得られた熱ラミネーション用グラビアインキ
を使用してグンゼシルファンLAG#40(グンゼ社製
処理OPPフィルム)に印刷し、次いでグンゼ社製GT
Lラミネート機を使用してラミネート速度120m/分
、ラミネート温度132℃でシーラントフィルムとして
パイレン#20(東洋紡社製処理CPPフィルム)を熱
圧着することにより、グンゼシルファンLAG#40に
パイレン#20をラミネートした。The lamination strength and residual solvent amount of the obtained laminated film were measured and found to be as follows. Example 4 The gravure ink for thermal lamination obtained in Example 1 was used to print on Gunze Silphan LAG #40 (treated OPP film manufactured by Gunze Co., Ltd.), and then printed on Gunze Silfane LAG #40 (treated OPP film manufactured by Gunze Co., Ltd.).
Pyrene #20 was bonded to Gunze Silfan LAG #40 by thermocompression bonding Pyrene #20 (treated CPP film manufactured by Toyobo Co., Ltd.) as a sealant film at a laminating speed of 120 m/min and a laminating temperature of 132°C using an L laminating machine. Laminated.
【0016】得られたラミネートフィルムのラミネート
強度及び残留溶剤量を測定すると、次の通りであった。
実施例5
実施例1で得られた熱ラミネーション用グラビアインキ
を使用してグンゼシルファンLAG#40(グンゼ社製
処理OPPフィルム)に印刷し、次いでグンゼ社製GT
Lラミネート機を使用してラミネート速度120m/分
、ラミネート温度132℃で次表にしめす各種のシーラ
ントフィルムを熱圧着することにより、グンゼシルファ
ンLAG#40に各種のシーラントフィルムをラミネー
トした。The lamination strength and residual solvent amount of the obtained laminated film were measured and found to be as follows. Example 5 The gravure ink for thermal lamination obtained in Example 1 was used to print on Gunze Silphan LAG #40 (treated OPP film manufactured by Gunze Co., Ltd.), and then printed on Gunze Co., Ltd. GT
Gunze Silfan LAG #40 was laminated with various sealant films by thermocompression bonding the various sealant films shown in the following table using an L laminating machine at a lamination speed of 120 m/min and a lamination temperature of 132°C.
【0017】得られたラミネートフィルムのラミネート
強度を翌日及び6日後測定すると、次の通りであった。The lamination strength of the obtained laminated film was measured on the next day and 6 days later and was as follows.
【0018】[0018]
【表1】[Table 1]
【0019】[0019]
【発明の効果】本発明の印刷インキを使用すれば、印刷
フィルムをラミネートする際に、ドライラミネート用等
の接着剤を不要とし、接着剤の塗布に起因する残留溶剤
を無くし、さらに接着剤のエージング時間をも不要とす
ることができる。[Effects of the invention] By using the printing ink of the present invention, when laminating printing films, adhesives such as those for dry lamination are not required, residual solvents caused by adhesive application are eliminated, and adhesive It is also possible to eliminate the need for aging time.
Claims (1)
ポリプロピレン及び塩化ビニルイソブチルビニルエーテ
ル共重合体をバインダーとして含有することを特徴とす
る熱ラミネーション用グラビアインキ。1. A gravure ink for thermal lamination, characterized in that it contains an ethylene vinyl acetate copolymer, a chlorinated polypropylene, and a vinyl chloride isobutyl vinyl ether copolymer as a binder.