JPH04296588A - Transfer foil - Google Patents
Transfer foilInfo
- Publication number
- JPH04296588A JPH04296588A JP3062137A JP6213791A JPH04296588A JP H04296588 A JPH04296588 A JP H04296588A JP 3062137 A JP3062137 A JP 3062137A JP 6213791 A JP6213791 A JP 6213791A JP H04296588 A JPH04296588 A JP H04296588A
- Authority
- JP
- Japan
- Prior art keywords
- transfer foil
- golf ball
- resin
- polyamide
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】0001
【産業上の利用分野】本発明はゴルフボール、特にはア
イオノマー樹脂を外皮にに持つゴルフボール用の転写箔
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf ball, and more particularly to a transfer foil for a golf ball having an outer skin coated with an ionomer resin.
【0002】0002
【従来の技術】従来ゴルフボール用の転写箔としては、
特公昭63−44558号明細書に示されるように、ポ
リプロピレンフィルム上にNC(ニトロセルロース)/
アルキッド系インキを用いて所望の文字を設ける方法が
あった。しかしこの方法ではNC/アルキッド系インキ
のポリプロピレンフィルムからの剥離強度と、NC/ア
ルキッド系インキのゴルフボールに対する接着強度とに
余り差異がなく、転写時に文字の一部に欠けを生じるな
どの欠点を有していた。また、NC/アルキッド系イン
キの自体アイオノマー樹脂に対する密着性もそれほど強
固でないという基本的な問題も有しており、サンドブラ
スト等の表面処理を必要とするという問題点を有してい
た。[Prior Art] Conventional transfer foils for golf balls include:
As shown in Japanese Patent Publication No. 63-44558, NC (nitrocellulose)/
There was a method of creating desired characters using alkyd ink. However, with this method, there is not much difference in the peel strength of the NC/alkyd-based ink from the polypropylene film and the adhesion strength of the NC/alkyd-based ink to the golf ball, and there are drawbacks such as part of the characters being chipped during transfer. had. Furthermore, there is a fundamental problem in that the adhesion of the NC/alkyd ink itself to the ionomer resin is not very strong, and there is a problem in that surface treatment such as sandblasting is required.
【0003】0003
【発明が解決しようとする課題】本発明は以上のように
従来技術の欠点を解消しようとするものであって、転写
時に文字等の一部に欠けを生じることなどがなく、また
サンドブラスト処理等の表面処理を必要しないゴルフボ
ール用転写箔を提供するものである。[Problems to be Solved by the Invention] The present invention is intended to solve the drawbacks of the prior art as described above. The present invention provides a transfer foil for golf balls that does not require surface treatment.
【0004】0004
【問題点を解決する手段】本発明は、上記問題点を解消
したもので、ポリプロピレンフィルムの表面に、セルロ
ース誘導体・ポリアマイドを主体とした樹脂に、塩素化
ポリオレフィン樹脂を 0 . 5〜 2. 0部添
加したインキにて文字や絵柄等を印刷したことを特徴と
するゴルフボール用の転写箔である。[Means for Solving the Problems] The present invention solves the above-mentioned problems by coating the surface of a polypropylene film with a resin mainly composed of cellulose derivatives and polyamides, and a chlorinated polyolefin resin. 5~2. This is a transfer foil for golf balls, characterized in that characters, patterns, etc. are printed using 0 parts of added ink.
【0005】本発明に於けるポリプロピレンフィルムは
2軸延伸フィルム(OPPフィルム)の方が無延伸フィ
ルム(CPP)に比較して引っ張り強度が高いため取扱
いが容易で作業性が良く、また見当精度も良好である。[0005] The polypropylene film used in the present invention is a biaxially stretched film (OPP film) which has higher tensile strength than an unstretched film (CPP), so it is easy to handle and has good workability, and also has good registration accuracy. In good condition.
【0006】厚みとしては20〜60μが一般的である
が、ゴルフボールの表面(以下ディンプル)への転写性
の点からは20μの厚みのものが良好であった。The thickness is generally 20 to 60 μm, but a thickness of 20 μm is good in terms of transferability to the surface of a golf ball (hereinafter referred to as dimples).
【0007】またより剥離力を軽くするためにはコロナ
放電処理をしない未処理のフィルムを使用すねることも
可能である。ただし、剥離力が過度に低下し、インキが
脱落しやすくなる弊害もあるため使い分けが必要である
。In order to further reduce the peeling force, it is also possible to use an untreated film that has not been subjected to corona discharge treatment. However, it has the disadvantage that the peeling force decreases excessively and the ink easily falls off, so it is necessary to use them appropriately.
【0008】インキのバインダーとしては、セルロース
誘導体・ポリアマイドを主体とした樹脂がポリプロピレ
ンフィルムからの剥離強度の点及びアイオノマー樹脂に
対する密着性の点で優れていた。As the binder for the ink, resins mainly composed of cellulose derivatives and polyamides have been found to be excellent in terms of peel strength from polypropylene films and adhesion to ionomer resins.
【0009】セルロース誘導体はポリプロピレンフィル
ムからの剥離性を向上させる役割のもので、アセチルセ
ルロース、エチルセルロース、ニトロセルロースが良く
用いられるが特にこれらの樹脂に限定されるものではな
い。[0009] The cellulose derivative has the role of improving the peelability from the polypropylene film, and acetyl cellulose, ethyl cellulose, and nitrocellulose are often used, but the resin is not limited to these resins.
【0010】ポリアマイドはアイオノマー樹脂に対する
密着性を改善するものであるが、過剰な配合はポリプロ
ピレンフィルムから剥離性を損ねる。Although polyamide improves adhesion to ionomer resins, excessive blending impairs releasability from polypropylene films.
【0011】実験により適性な配合はニトロセルロース
/ポリアマイド=50/50〜70/30の範囲であっ
た。Experiments have shown that a suitable blend is in the range of nitrocellulose/polyamide from 50/50 to 70/30.
【0012】しかるにこれのみでは、アイオノマー樹脂
に対する密着性が十分とはいえない。特にサンドブラス
ト等の表面処理を施していない場合密着性が不十分であ
る。However, this alone does not provide sufficient adhesion to the ionomer resin. In particular, adhesion is insufficient when surface treatment such as sandblasting is not performed.
【0013】此の問題は塩素化ポリオレフィンを主剤(
セルロース誘導体+ポリアマイド)に対して0.5〜2
.0重量部添加することにより密着性が著しく改善した
。[0013] This problem occurs when chlorinated polyolefin is used as the main agent (
0.5 to 2 for cellulose derivative + polyamide)
.. Adhesion was significantly improved by adding 0 parts by weight.
【0014】以上のようにポリアマイド不の表面にセル
ロース誘導体・ポリアマイドを主体とした樹脂に、塩素
化ポリオレフィン樹脂を0.5〜2.0重量部添加した
インキに文字や絵柄等を印刷することにより、転写性に
優れるゴルフボール用転写箔を得ることが可能となった
。As described above, by printing letters, patterns, etc. on the surface of non-polyamide using ink made by adding 0.5 to 2.0 parts by weight of chlorinated polyolefin resin to resin mainly composed of cellulose derivatives and polyamide. It became possible to obtain a transfer foil for golf balls with excellent transferability.
【0015】[0015]
【作用】従来の方法では、ポリプロピレンフィルムから
の剥離力とアイオノマー樹脂への密着力のバランスを調
整することが困難であり、従って良好な転写性が得られ
なかった。[Function] In the conventional method, it was difficult to adjust the balance between the peeling force from the polypropylene film and the adhesion force to the ionomer resin, and therefore good transferability could not be obtained.
【0016】本発明では、セルロース誘導体とポリアマ
イドと塩素化ポリオレフィン樹脂の適性な配合比により
良好な転写性を得ることを可能とした。[0016] In the present invention, it is possible to obtain good transferability by appropriately blending the cellulose derivative, polyamide, and chlorinated polyolefin resin.
【0017】すなわち基材フィルムにポリプロピレンを
採用することにより、過度な剥離力を得ることができ、
またゴルフボール表面の凹部(ディンプル)への転写性
を良好ならしめた。[0017] That is, by using polypropylene for the base film, excessive peeling force can be obtained,
Furthermore, the transferability to the dimples on the surface of the golf ball was improved.
【0018】インキのバインダーとしてはセルロース誘
導体がポリプロピレンフィルムから剥離強度低下をポリ
アマイドがアイオノマー樹脂に対する密着性向上させる
役目をなし、かつその配合は、ニトロセルロース/ポリ
アマイド=50/50〜70/30の範囲が適正である
。As a binder for the ink, the cellulose derivative serves to reduce the peel strength from the polypropylene film, and the polyamide serves to improve the adhesion to the ionomer resin, and the blend is in the range of nitrocellulose/polyamide = 50/50 to 70/30. is appropriate.
【0019】セルロース誘導体が少ないと(ポリアマイ
ドが多いと)ポリプロピレンフィルムからの剥離強度が
重過ぎ、うまく剥離せず、ポリアマイドが少ないと(セ
ルロース誘導体が多いと)剥離強度は軽くなるがアイオ
ノマー樹脂に対する密着強度が低下し転写がうまくなさ
れないか、転写ができても極めて弱い密着力となる。If the amount of cellulose derivative is small (if the amount of polyamide is large), the peel strength from the polypropylene film will be too high and it will not be peeled off properly, and if the amount of polyamide is small (if the amount of cellulose derivative is large), the peel strength will be light but the adhesion to the ionomer resin will be poor. The strength decreases and the transfer is not successful, or even if the transfer is successful, the adhesion is extremely weak.
【0020】さらに塩素化ポリオレフィンを主剤(セル
ロース誘導+ポリアマイド)に対して0.5〜2.0重
量部添加することにより、サンドブラスト等の表面処理
を施していないアイオノママー樹脂表面に対する密着も
可能となった。Furthermore, by adding 0.5 to 2.0 parts by weight of chlorinated polyolefin to the base material (cellulose derivative + polyamide), it is possible to adhere to the ionomer resin surface that has not been subjected to surface treatment such as sandblasting. Ta.
【0021】[0021]
【実施例】厚さ20μのポリアマイドフィルムの表面に
、下記のような配合の樹脂をバインダーとしたインキ、
ニトロセルロース
60部ポリアマイド
40部塩素化
ポリプロピレン
1部を作成し、ゴルフボールの品名とマークを
印刷し転写箔とした。[Example] Ink and nitrocellulose with the following composition of resin as a binder were applied to the surface of a 20μ thick polyamide film.
60 parts polyamide
40 parts chlorinated polypropylene
One copy was made, and the product name and mark of the golf ball were printed on it, and it was used as a transfer foil.
【0022】この転写箔を130°C・1秒の転写条件
で転写したところ剥離強度も軽く、ディンプルの細部ま
で転写されたゴルフボールが得られた。[0022] When this transfer foil was transferred under transfer conditions of 130°C and 1 second, a golf ball with light peel strength and in which even the details of the dimples were transferred was obtained.
【0023】[0023]
【効果】本発明は以上の如き構成であって、( 1)剥
離強度が軽く接着強度が高いため転写性に優れる。
( 2)サンドブラスト等の表面処理を施していないア
イオノマー樹脂表面に対する密着も可能。
( 3)2軸延伸フィルム(0PPフィルム)ポリプロ
ピレンを使用すれば引っ張り強度が高いため取扱いが容
易で作業性が良い。
( 4)20μのポリプロピレンフィルムの使用でゴル
フボール表面の凹部(ディンプル )の転写性に優れる
。という効果を有している。[Effects] The present invention has the above structure, and (1) has excellent transferability due to its light peel strength and high adhesive strength. (2) It is also possible to adhere to ionomer resin surfaces that have not been subjected to surface treatments such as sandblasting. (3) Biaxially stretched film (0PP film) If polypropylene is used, it has high tensile strength, so it is easy to handle and has good workability. (4) The use of a 20μ polypropylene film provides excellent transferability of dimples on the surface of a golf ball. It has this effect.
Claims (2)
ース誘導体・ポリアマイドを主体とした樹脂に、塩素化
ポリオレフィン樹脂を 0 . 5〜 2. 0部添
加したインキにて文字や絵柄等を印刷したことを特徴と
する転写箔。Claim 1: On the surface of a polypropylene film, 0.0% of a chlorinated polyolefin resin is applied to a resin mainly composed of cellulose derivatives and polyamides. 5~2. A transfer foil characterized in that characters, patterns, etc. are printed using ink containing 0 parts.
い未処理のフィルムを使用することを特徴とする請求項
第1項記載の転写箔。2. The transfer foil according to claim 1, wherein the polypropylene film is an untreated film that does not undergo corona discharge.