JP3017196U - Agricultural film - Google Patents
Agricultural filmInfo
- Publication number
- JP3017196U JP3017196U JP1994010467U JP1046794U JP3017196U JP 3017196 U JP3017196 U JP 3017196U JP 1994010467 U JP1994010467 U JP 1994010467U JP 1046794 U JP1046794 U JP 1046794U JP 3017196 U JP3017196 U JP 3017196U
- Authority
- JP
- Japan
- Prior art keywords
- film
- fine
- fine irregularities
- convex portion
- irregularities
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
(57)【要約】
【目的】 光線の透過率を悪化させることなく、フィル
ムの密着を低減でき、しかも汚れ防止効果も有する農業
用フィルムを提供する。
【構成】 塩化ビニル系樹脂を主成分とし、片面に微細
凹凸を設けた微細凹凸部１２と微細凹凸を設けない非微
細凹凸部１１を有するフィルム１０の微細凹凸を設けて
いない側の面に、水系、溶剤系または紫外線硬化系の塗
料からなる塗膜１３を設けた農業用フィルムであって、
少なくともフィルム端部のいずれか１つに沿った１ｍ幅
の範囲内においては、微細凹凸部１２および／または非
微細凹凸部１１が不連続で、かつ微細凹凸部１２の形成
比率が１０〜９０％になるように微細凹凸を形成した農
業用フィルム。
(57) [Summary] [Object] To provide an agricultural film which can reduce the adhesion of a film without deteriorating the transmittance of light rays and also have an antifouling effect. [Structure] A film 10 having a vinyl chloride resin as a main component and having a fine concavo-convex portion 12 having fine concavo-convex portions on one surface and a non-fine concavo-convex portion 11 having no fine concavo-convex portion is provided on a surface on which the fine concavo-convex portion is not provided, An agricultural film provided with a coating film 13 made of a water-based, solvent-based or UV-curable coating material,
Within the range of at least 1 m width along any one of the film end portions, the fine concavo-convex portion 12 and / or the non-fine concavo-convex portion 11 are discontinuous, and the formation rate of the fine concavo-convex portion 12 is 10 to 90%. Agricultural film with fine irregularities.
Description
【０００１】[0001]
本考案は、農業用フィルムに関し、さらに詳しくは光線の透過率を悪化させる ことなく、フィルムの密着性を抑制し、しかも塵埃の付着防止効果も有する農業 用フィルムに関する。 The present invention relates to an agricultural film, and more particularly to an agricultural film that suppresses the adhesiveness of the film without deteriorating the transmittance of light rays and also has an effect of preventing adhesion of dust.
【０００２】[0002]
従来、例えばビニルハウスは、所定形状に屈曲された鉄製あるいはステンレス 製のパイプを連結して骨組を造り、所定箇所に天窓や出入り口を設けて、その表 面を透明な塩化ビニル系樹脂フィルムにより被っている。 Conventionally, for example, a vinyl house is made by connecting iron or stainless steel pipes bent into a predetermined shape to form a frame, providing a skylight or an entrance at a predetermined position, and covering the surface with a transparent vinyl chloride resin film. ing.
【０００３】 上記のようなビニルハウスでは、夏期の暑い日には、日差しが強くてハウス内 の温度が高くなり過ぎるので、出入り口を開けるのはもちろん、ビニルハウスの 側面をロール状に巻き上げたり、天窓を押し上げたりして換気を良くすることに より室内温度の調整が行われている。In such a vinyl house, on a hot summer day, the sunshine is strong and the temperature inside the house becomes too high, so of course, not only opening the doorway, but also winding up the sides of the vinyl house in a roll shape. The room temperature is adjusted by pushing up the skylight and improving ventilation.
【０００４】[0004]
ところで、従来のビニルハウスを被っているフィルムには、表面がベタつき易 い一般の塩化ビニル系樹脂フィルムが使用されているので、例えば側面をロール 状に巻き上げた際に接触している部分が互いに密着してしまい、巻き上げや巻き 戻し時に大変な手間がかかっていた。 By the way, since conventional vinyl chloride resin films that have a sticky surface are used for the film that covers conventional vinyl houses, for example, the parts that are in contact when the side surfaces are rolled up are They were in close contact with each other, and it took a lot of time and effort when hoisting and rewinding.
【０００５】 そこで、フィルムの全表面に梨地加工したり、無機質微粉末を添加してフィル ムの全表面を荒らしたりして、フィルムどうしが密着するのを防止することも提 案されているが、このようなフィルムでは、ハウス内で栽培される作物に必要な 日光の透過率が不充分で、日光をハウス内に取り入れて温室栽培を行うビニルハ ウス本来の機能を充分に果たせないという、別の問題が発生していた。Therefore, it has been proposed to prevent the films from adhering to each other by performing satin finish on the entire surface of the film or adding inorganic fine powder to roughen the entire surface of the film. , Such a film does not have sufficient sunlight transmittance for the crops cultivated in the greenhouse, and cannot perform the original function of the vinyl house that is used for greenhouse cultivation by incorporating sunlight into the greenhouse. Was having problems.
【０００６】 本考案は、このような従来技術を背景になされたもので、光線の透過率を悪化 させることなく、フィルムの密着を低減でき、しかも汚れ防止効果も有する農業 用フィルムを提供することを目的とする。The present invention has been made against the background of such a conventional technique, and provides an agricultural film which can reduce the adhesion of the film without deteriorating the transmittance of light and have an antifouling effect. With the goal.
【０００７】[0007]
本考案は、塩化ビニル系樹脂を主成分とし、片面に微細凹凸を設けた微細凹凸 部と微細凹凸を設けない非微細凹凸部を有するフィルムの微細凹凸を設けていな い側の面に、水系、溶剤系または紫外線硬化系の塗料からなる塗膜を設けた農業 用フィルムであって、少なくともフィルム端部のいずれか１つに沿った１ｍ幅の 範囲内においては、微細凹凸部および／または非微細凹凸部が不連続で、かつ微 細凹凸部の形成比率が１０〜９０％になるように微細凹凸を形成したことを特徴 とする農業用フィルムを提供するものである。 The present invention is based on a vinyl chloride resin as a main component and has a water-based surface on the non-fine side of a film having fine unevenness with fine unevenness on one side and non-fine unevenness without fine unevenness. An agricultural film provided with a coating film composed of a solvent-based or UV-curable coating material, and within a range of 1 m width along at least one of the film edges, fine irregularities and / or non-convex parts. It is intended to provide an agricultural film characterized in that the fine irregularities are discontinuous, and the fine irregularities are formed so that the formation rate of the fine irregularities is 10 to 90%.
【０００８】 また、上記の微細凹凸部は、５００〜６００ｎｍの波長の平行光線平均透過率 が４０％以下、全光線平均透過率が７５％以上とし、微細凹凸を設けない非微細 凹凸部は、５００〜６００ｎｍの波長の平行光線平均透過率が６０％以上、全光 線平均透過率が８０％以上とすることが好ましい。The fine irregularities have a parallel light ray average transmittance of 40% or less and a total light ray average transmittance of 75% or more at a wavelength of 500 to 600 nm, and a non-fine irregularity portion having no fine unevenness is It is preferable that the parallel light beam average transmittance at a wavelength of 500 to 600 nm is 60% or more, and the total light beam average transmittance is 80% or more.
【０００９】[0009]
本考案の農業用フィルムにおいては、フィルムの少なくとも一端部から１ｍ幅 の範囲内で、微細凹凸を設けた微細凹凸部を形成比率が１０〜９０％となるよう に形成しているので、フィルムを巻き上げたり重ねたりした場合でも、少なくと も一端部から１ｍ幅の範囲内ではフィルムどうしが密着するのを防止でき、また 微細凹凸を設けない非微細凹凸部を微細凹凸部を有する領域内では９０〜１０％ とすることにより、農業用フィルムに要求される透光性をも確保することができ る。 しかも、本考案の農業用フィルムは、上記の微細凹凸を設けていない側の面に 水系、溶剤系または紫外線硬化系の塗料からなる塗膜を設けたことにより、塵埃 などの付着が防止される。 In the agricultural film of the present invention, the fine concavo-convex portion provided with the fine concavo-convex portion is formed within a range of 1 m width from at least one end portion of the film so that the forming ratio is 10 to 90%. Even when rolled up or piled up, it is possible to prevent the films from sticking to each other within a width of at least 1 m from one end, and to prevent non-fine irregularities without fine irregularities from being 90% By setting it to 10%, it is possible to secure the translucency required for the agricultural film. Moreover, the agricultural film of the present invention is provided with a coating film made of a water-based, solvent-based, or UV-curing paint on the surface on which the fine irregularities are not provided, thereby preventing the adhesion of dust and the like. .
【００１０】[0010]
以下、本考案の一実施例を図面に基づいて詳細に説明する。本実施例ではビニ ルハウス用の農業用フィルムを例とする。 An embodiment of the present invention will be described below in detail with reference to the drawings. In this example, an agricultural film for a vinyl house is used as an example.
【００１１】 図１は本考案の一実施例の農業用フィルムの一部平面図、図２は実施例の農業 用フィルムの一部拡大断面図であり、図中１０はビニルハウスの外装材である、 塩化ビニル系樹脂を主成分とする農業用フィルムである。農業用フィルム１０の フィルム片面には、斜めに真っ直ぐ延びる非微細凹凸部１１と梨地加工の微細凹 凸部１２とが一定間隔で交互に配置されており、非微細凹凸部１１側の面には、 水系、溶剤系または紫外線硬化系の塗料からなるベタつき防止および汚れ防止用 の塗膜１３が設けられている。FIG. 1 is a partial plan view of an agricultural film according to an embodiment of the present invention, and FIG. 2 is a partially enlarged cross-sectional view of the agricultural film of the embodiment. In FIG. An agricultural film whose main component is vinyl chloride resin. On one surface of the film 10 for agricultural use, non-fine concavo-convex portions 11 extending obliquely straight and fine concavo-convex convex portions 12 having a satin finish are alternately arranged at regular intervals. A coating film 13 made of water-based, solvent-based or UV-curable coating material for preventing stickiness and stains is provided.
【００１２】 農業用フィルム１０の主成分である塩化ビニル系樹脂としては、ポリ塩化ビニ ルのほか、塩化ビニルと他の樹脂のモノマー、例えばエチレン、プロピレン、塩 化ビニリデン、アクリロニトリル、マレイン酸、イタコン酸、メタクリル酸、酢 酸ビニル、マレイン酸エステル、メタクリル酸メチルなどのメタクリル酸アルキ ルエステル、アクリル酸メチルなどのアクリル酸アルキルエステル、高級ビニル エーテルなどとの共重合樹脂、もしくはこれらのブレンド物などが使用できる。As the vinyl chloride-based resin which is the main component of the agricultural film 10, in addition to polyvinyl chloride, vinyl chloride and other resin monomers such as ethylene, propylene, vinylidene chloride, acrylonitrile, maleic acid, and itacone. Acid, methacrylic acid, vinyl acetate, maleic acid ester, methacrylic acid alkyl ester such as methyl methacrylate, acrylic acid alkyl ester such as methyl acrylate, copolymer resin with higher vinyl ether, or blends of these Can be used.
【００１３】 この塩化ビニル系樹脂１００重量部当たり、０．５〜６重量部の防滴剤を添加 することができる。０．５重量部未満では防滴性が悪く、一方６重量部を超える とフィルム表面へのふき出しが多くなり好ましくない。0.5 to 6 parts by weight of the dripproofing agent may be added to 100 parts by weight of the vinyl chloride resin. If the amount is less than 0.5 part by weight, the drip-proof property is poor, while if it exceeds 6 parts by weight, the amount of bleeding on the film surface increases, which is not preferable.
【００１４】 この防滴剤としては、ソルビタン脂肪酸エステル、ソルビトール脂肪酸エステ ル、グリセリン脂肪酸エステル、ジグリセリン脂肪酸エステル、ソルビタン脂肪 酸・二塩基酸エステル、ソルビトール脂肪酸・二塩基酸エステル、ジグリセリン 脂肪酸・二塩基酸エステル、グリセリン脂肪酸・二塩基酸エステルなどの多価ア ルコールと脂肪酸とのエステル、多価アルコールと脂肪酸および二塩基酸とのエ ステル、あるいはこれらにエチレンオキサイド、プロピレンオキサイド、ブチレ ンオキサイドなどのアルキレンオキサイドが付加された化合物などが挙げられ、 具体的にはソルビタンパルミテート、ソルビタンステアレート、ソルビタンステ アレート・エチレンオキサイド２モル付加物、ソルビタンステアレート・プロピ レンオキサイド３モル付加物、ソルビトールステアレート、ソルビトールステア レート・エチレンオキサイド３モル付加物、ジグリセリンパルミテート、ジグリ セリンステアレート、グリセリンステアレート、グリセリンパルミテート・エチ レンオキサイド２モル付加物、ソルビタンステアレートアジペート・エチレンオ キサイド３モル付加物、ソルビトールステアレートアジペート・エチレンオキサ イド２モル付加物、ジグリセリンパルミテートセバケート・プロピレンオキサイ ド３モル付加物、ソルビトールパルミテートアジペート・エチレンオキサイド３ モル付加物などが挙げられる。これらの防滴剤は、単独または２種以上を組み合 わせて使用することができる。Examples of the antidrip agent include sorbitan fatty acid ester, sorbitol fatty acid ester, glycerin fatty acid ester, diglycerin fatty acid ester, sorbitan fatty acid / dibasic acid ester, sorbitol fatty acid / dibasic acid ester, diglycerin fatty acid / dicarboxylic acid ester. Basic acid ester, ester of polyhydric alcohol and fatty acid such as glycerin fatty acid / dibasic acid ester, ester of polyhydric alcohol and fatty acid and dibasic acid, or ethylene oxide, propylene oxide, butylene oxide, etc. Examples thereof include compounds to which alkylene oxide is added. Specific examples include sorbitan palmitate, sorbitan stearate, sorbitan stearate / ethylene oxide 2 mol adduct, sorbitan stearate / propylate. 3 mol adduct of nitro oxide, sorbitol stearate, 3 mol adduct of sorbitol stearate / ethylene oxide, diglycerin palmitate, diglycerin stearate, glycerin stearate, glycerin palmitate / 2 mol adduct of ethylene oxide, sorbitan stearate Rate adipate / ethylene oxide 3 mol adduct, sorbitol stearate adipate / ethylene oxide 2 mol adduct, diglycerin palmitate sebacate / propylene oxide 3 mol adduct, sorbitol palmitate adipate / ethylene oxide 3 mol adduct And so on. These drip-proof agents can be used alone or in combination of two or more kinds.
【００１５】 本考案の農業用フィルムには、この防滴剤とともに、塩化ビニル系樹脂１００ 重量部当たり０．０１〜１．０重量部、好ましくは０．０５〜０．５重量部の含 フッ素系化合物を添加することができる。In the agricultural film of the present invention, 0.01 to 1.0 part by weight, preferably 0.05 to 0.5 part by weight, of fluorine-containing resin is added per 100 parts by weight of the vinyl chloride resin together with this drip-proofing agent. A system compound can be added.
【００１６】 含フッ素系化合物としては、１分子中に含フッ素基と水酸基またはアルキレン オキサイド基の少なくとも１種を有する含フッ素系化合物であり、含フッ素基と しては、パーフルオロアルキル基（Ｃn Ｆ2n+1基）、パーフルオロアルコキシ基 （Ｃn Ｆ2n+1Ｏ基）、ポリフルオロアルキル基（Ｈm Ｃn Ｆ2n+1-m基）、パーフ ルオロアルケニル基（Ｃn Ｆ2n-1基）、ポリフルオロアルケニル基（Ｈm Ｃn Ｆ 2n-1-m 基）、パーフルオロアルキレン基（Ｃn Ｆ2n基）などがあり、式中ｍ＝１ 〜３、ｎ＝３〜２０の整数である。アルキレンオキサイド基としては、（C2H4O) n 、（C3H4O)n などがあり、式中ｎ＝１〜３０である。The fluorinated compound is a fluorinated compound having at least one of a fluorinated group and a hydroxyl group or an alkylene oxide group in one molecule, and the fluorinated group includes a perfluoroalkyl group (CnF2n + 1Group), perfluoroalkoxy group (CnF2n + 1O group), polyfluoroalkyl group (HmCnF2n + 1-mGroup), perfluoroalkenyl group (CnF2n-1Group), polyfluoroalkenyl group (HmCnF 2n-1-m Group), perfluoroalkylene group (CnF2nGroup) and the like, and m = 1 to 3 and n = 3 to 20 in the formula. As the alkylene oxide group, (C2HFourO) n , (C3HFourO)nAnd n = 1 to 30 in the formula.
【００１７】 含フッ素系化合物の具体例としては、 C8F17C2H4O(C2H4O)8CH3 、 C8F17CH2CH2OHCH2O(C2H4O)10CH3 、 C14F21CH2CH(OCH3)CH2O(C2H4O)10CH3 、 C14F21CH2CH(OH)CH2O(C2H6O)10H 、 C8F17CH2CH(OCOH3)CH2O(C3H6O)8CH3、 C8F17SO2N(C2H5)(C2H4O)12、 C6F13CON(C2H5)(C2H4O)8H 、 C8F17SO2N[CH2CH(OH)CH2CH]2、 HCF2C5F10CH2O(C2H4O)10H 、 C3F7OC3F6CH2CH2SCH(COOH)CH2COO(C2H4O)10H、 C3F7OC3F10CH2CH2SCH(CH2COOH)CH2COO(C2H4O)15H、 H(CH−CH2 ) 2 −(CH-CH2)2H COOC2 H4C8F17 COO(C2 H4O)8H、 H[C(CH3)CH2]2 −〔C(CH3)CH2 〕2 −[C(CH3)CH2]H COOC2H4C10F21 COO(C3H6O)2H COO(C2H4O)8H などが挙げられるが、これらに限定されるものではない。Specific examples of the fluorine-containing compound include C 8 F 17 C 2 H 4 O (C 2 H 4 O) 8 CH 3 and C 8 F 17 CH 2 CH 2 OHCH 2 O (C 2 H 4 O ) 10 CH 3 , C 14 F 21 CH 2 CH (OCH 3 ) CH 2 O (C 2 H 4 O) 10 CH 3 , C 14 F 21 CH 2 CH (OH) CH 2 O (C 2 H 6 O) 10 H, C 8 F 17 CH 2 CH (OCOH 3 ) CH 2 O (C 3 H 6 O) 8 CH 3 , C 8 F 17 SO 2 N (C 2 H 5 ) (C 2 H 4 O) 12 , C 6 F 13 CON (C 2 H 5 ) (C 2 H 4 O) 8 H, C 8 F 17 SO 2 N [CH 2 CH (OH) CH 2 CH] 2 , HCF 2 C 5 F 10 CH 2 O (C 2 H 4 O) 10 H, C 3 F 7 OC 3 F 6 CH 2 CH 2 SCH (COOH) CH 2 COO (C 2 H 4 O) 10 H, C 3 F 7 OC 3 F 10 CH 2 CH 2 SCH (CH 2 COOH) CH 2 COO (C 2 H 4 O) 15 H, H (CH-CH 2 ) 2- (CH-CH 2 ) 2 H COOC 2 H 4 C 8 F 17 COO (C 2 H 4 O) 8 H, H [C (CH 3 ) CH 2 ] 2- [C (CH 3 ) CH 2 ] 2- [C (CH 3 ) CH 2 ] H COOC 2 H 4 C 10 F 21 COO (C 3 H 6 O) 2 H COO (C 2 H 4 O) 8 H and the like are included, but are not limited thereto.
【００１８】 また、本考案の農業用フィルムには、必要に応じて可塑剤、安定剤、滑剤また は粘着防止剤、紫外線吸収剤、抗酸化剤、光安定剤、無機質充填剤などを添加す ることができる。 塩化ビニル系樹脂に添加される可塑剤としては、一般可塑剤、リン酸エステル 系可塑剤、エポキシ系可塑剤が使用できる。In addition, a plasticizer, stabilizer, lubricant or anti-adhesive agent, ultraviolet absorber, antioxidant, light stabilizer, inorganic filler, etc. may be added to the agricultural film of the present invention as needed. You can As the plasticizer added to the vinyl chloride resin, a general plasticizer, a phosphoric acid ester plasticizer, or an epoxy plasticizer can be used.
【００１９】 一般可塑剤としては、ジ−ｎ−オクチルフタレート、ジ−２−エチルヘキシル フタレート、ジイソノニルフタレート、ジブチルフタレート、ブチルベンジルフ タレート、ジラウリルフタレート、ジデシルフタレート、ジウナデシルフタレー ト、ジトリデシルフタレートなどのフタル酸エステル系可塑剤、ジオクチルアジ ペート、ジトリノニルアジペート、ジイソデシルアジペートなどのアジピン酸エ ステル系可塑剤のほか、ポリエステル系可塑剤、セバチン酸系可塑剤、トリメリ ット酸系可塑剤なども使用できる。Examples of the general plasticizer include di-n-octyl phthalate, di-2-ethylhexyl phthalate, diisononyl phthalate, dibutyl phthalate, butylbenzyl phthalate, dilauryl phthalate, didecyl phthalate, diunadecyl phthalate, ditridecyl phthalate. Phthalates such as phthalate plasticizers, dioctyl adipate, ditrinonyl adipate, diisodecyl adipate and other adipate ester plasticizers, as well as polyester plasticizers, sebacic acid plasticizers, trimellitic acid plasticizers Can also be used.
【００２０】 リン酸エステル系可塑剤としては、トリクレジルホスフェート、トリキシリル ホスフェート、トリス（イソプロピルフェニル）ホスフェート、トリブチルホス フェート、トリエチルホスフェート、トリフェニルホスフェート、トリエチルフ ェニルホスフェートなどが使用できる。As the phosphate ester-based plasticizer, tricresyl phosphate, trixylyl phosphate, tris (isopropylphenyl) phosphate, tributylphosphate, triethylphosphate, triphenylphosphate, triethylphenylphosphate and the like can be used.
【００２１】 エポキシ系可塑剤としては、植物油のエポキシ化物、エポキシ樹脂が使用でき る。 植物油のエポキシ化物としては、エポキシ化大豆油、エポキシ化アマニ油など が使用できる。As the epoxy plasticizer, epoxidized vegetable oil and epoxy resin can be used. Epoxidized soybean oil, epoxidized linseed oil and the like can be used as the epoxidized vegetable oil.
【００２２】 エポキシ樹脂としては、エポキシ化ポリブタジエン、エポキシステアリン酸メ チル、エポキシステアリン酸ブチル、エポキシステアリン酸エチルヘキシル、ト リス（エポキシプロピル）イソシアヌレート、３−（２−キセノキシ）−１，２ −エポキシプロパン、ビスフェノールＡ、ジグリシジルエーテル、ビニルジシク ロヘキセンジエポキシサイド、２，２−ビス（４−ヒドロキシフェニル）プロパ ンとエピクロルヒドリンの重縮合物が挙げられる。 前記可塑剤は、１種または２種以上混合して用いられるが、好ましい添加量は 、塩化ビニル系樹脂１００重量部当たり、フタル酸エステル系可塑剤３０〜７０ 重量部、リン酸エステル系可塑剤１〜７重量部、エポキシ系可塑剤０．５〜７重 量部である。Epoxy resins include epoxidized polybutadiene, epoxy methyl stearate, butyl epoxy stearate, ethylhexyl epoxy stearate, tris (epoxypropyl) isocyanurate, 3- (2-xenoxy) -1,2-epoxy. Examples thereof include propane, bisphenol A, diglycidyl ether, vinyl dicyclohexene diepoxyside, and a polycondensation product of 2,2-bis (4-hydroxyphenyl) propane and epichlorohydrin. The above-mentioned plasticizers may be used alone or in combination of two or more, and the preferable addition amount is 30 to 70 parts by weight of phthalate ester-based plasticizer and 100 parts by weight of vinyl chloride-based resin, and phosphate ester-based plasticizer. 1 to 7 parts by weight and 0.5 to 7 parts by weight of epoxy plasticizer.
【００２３】 安定剤としては、金属セッケン、有機ホスファイト系安定剤などの通常使用さ れる安定剤が使用できる。 金属セッケンとしては、ステアリン酸亜鉛、ステアリン酸バリウム、ステアリ ン酸カルシウム、リシノール酸バリウム、ラウリン酸カルシウム、オレイン酸カ ルシウム、オクトイン酸亜鉛などが挙げられる。As the stabilizer, commonly used stabilizers such as metal soap and organic phosphite stabilizer can be used. Examples of the metal soap include zinc stearate, barium stearate, calcium stearate, barium ricinoleate, calcium laurate, calcium oleate, zinc octoinate and the like.
【００２４】 有機ホスファイト系安定剤としては、ジフェニルデシルホスファイト、トリフ ェニルホスファイト、トリス（ノニルフェニル）ホスファイト、トリデシルホス ファイト、トリス（２−エチルヘキシル）ホスファイト、トリステアリルホスフ ァイト、オクチルジフェニルホスファイトなどが挙げられる。 これらの安定剤は、１種または２種以上を用いることができる。Examples of the organic phosphite stabilizer include diphenyldecylphosphite, triphenylphosphite, tris (nonylphenyl) phosphite, tridecylphosphite, tris (2-ethylhexyl) phosphite, tristearylphosphite, octyldiphenylphosphite. Examples include fights. These stabilizers may be used either individually or in combination of two or more.
【００２５】 滑剤または粘着防止剤としては、ステアリン酸、イソステアリン酸、パルミチ ン酸などの脂肪酸系滑剤、ステアリン酸アミド、メチレンビスステアロアミド、 エチレンビスステアロアミドなどの脂肪酸アミド系滑剤、ブチルパルミテート、 ブチルステアレートなどのエステル系滑剤、バリウムイソデシルホスフェート、 カルシウムオクタデシルホスフェートなどの有機リン酸金属塩系滑剤、ポリエチ レンワックス、流動パラフィンなどが挙げられ、これらの１種または２種以上を 用いることができる。As the lubricant or anti-sticking agent, fatty acid type lubricants such as stearic acid, isostearic acid and palmitic acid, fatty acid amide type lubricants such as stearic acid amide, methylene bis stearoamide and ethylene bis stearoamide, butyl palmi Examples include ester lubricants such as tate and butyl stearate, organophosphate metal salt lubricants such as barium isodecyl phosphate and calcium octadecyl phosphate, polyethylene wax, liquid paraffin, etc., and one or more of them may be used. be able to.
【００２６】 紫外線吸収剤としては、一般に使用されているベンゾフェノン系、ベンゾトリ アゾール系、サリチル酸エステル系、シアノアクリレート系などの紫外線吸収剤 が挙げられ、これらの１種または２種以上を用いることができる。Examples of the ultraviolet absorber include generally used benzophenone-based, benzotriazole-based, salicylate-based, and cyanoacrylate-based ultraviolet absorbers, and one or more of them can be used. .
【００２７】 抗酸化剤としては、フェノール系、チオジプロピオン酸エステル系、脂肪族サ ルファイド系などの抗酸化剤を１種または２種以上を用いることができる。 光安定剤としては、ヒンダードアミンなどの一般に使用されている光安定剤を １種または２種以上を用いることができる。As the antioxidant, one kind or two or more kinds of antioxidants such as phenol type, thiodipropionate type, and aliphatic sulfide type can be used. As the light stabilizer, one or more commonly used light stabilizers such as hindered amines can be used.
【００２８】 無機質微粉末は、フィルム表面のベタツキ防止や保温性を向上させる目的で使 用することができる。このような無機質微粉末としては、炭酸マグネシウム、マ グネシウムケイ酸塩、酸化ケイ素、酸化アルミニウム、水酸化アルミニウム、水 酸化マグネシウム、ハイドロタルサイト類の少なくとも１種以上を用いることが でき、微粉末の粒径は２０μｍ以下が好ましい。The inorganic fine powder can be used for the purpose of preventing stickiness of the film surface and improving heat retention. As such an inorganic fine powder, at least one kind of magnesium carbonate, magnesium silicate, silicon oxide, aluminum oxide, aluminum hydroxide, magnesium hydroxide and hydrotalcites can be used. The particle size is preferably 20 μm or less.
【００２９】 農業用フィルム１０のフィルムに形成された微細凹凸部１２は、フィルム片面 にエンボス加工などにより微細凹凸が形成されている。 また、上記の微細凹凸部１２は、５００〜６００ｎｍの波長の平行光線平均透 過率が４０％以下、全光線平均透過率が７５％以上とするのが好ましく、本実施 例における上記平行光線平均透過率は約７％、全光線平均透過率は約８０％にな っている。微細凹凸部１２の光線平均透過率を上記のようにすることで、フィル ム全体としての光線透過が良好となり、ハウス内の環境を作物の成育により適し たものとすることができる。The fine unevenness portion 12 formed on the film of the agricultural film 10 has fine unevenness formed on one surface of the film by embossing or the like. Further, it is preferable that the fine concavo-convex portion 12 has a parallel light beam average transmittance of 40% or less and a total light beam average transmittance of 75% or more at a wavelength of 500 to 600 nm. The transmittance is about 7% and the average transmittance for all rays is about 80%. By setting the average light transmittance of the fine concavo-convex portion 12 as described above, the light transmittance of the entire film becomes good, and the environment in the house can be made more suitable for the growth of crops.
【００３０】 上記の微細凹凸部１２の形成比率は、フィルムの少なくとも一端部から１ｍ幅 の範囲内で１０〜９０％、好ましくは２０〜７０％とする。本実施例では、フィ ルム全表面に略均一に微細凹凸部１２が形成されており、形成比率は２５％程度 となっている。微細凹凸部１２の形成比率が高すぎると、農業用フィルムに要求 される光線透過が確保できず、作物の成育に悪影響を及ぼす恐れがあり、逆に微 細凹凸部１２の形成比率が低すぎると、フィルムどうしが密着し、巻き上げ作業 などが困難になる。The formation ratio of the fine concavo-convex portion 12 is 10 to 90%, preferably 20 to 70% within the range of 1 m width from at least one end of the film. In this embodiment, the fine concavo-convex portion 12 is formed substantially uniformly on the entire surface of the film, and the forming ratio is about 25%. If the formation ratio of the fine concavo-convex portion 12 is too high, the light transmission required for the agricultural film cannot be secured, which may adversely affect the growth of the crop. On the contrary, the formation ratio of the fine concavo-convex portion 12 is too low. Then, the films stick to each other, making it difficult to wind them.
【００３１】 また、微細凹凸部１２は、該微細凹凸部１２または微細凹凸を設けない非微細 凹凸部１１の少なくとも一方が不連続となるように設けることが肝要である。例 えば、一端部から８０ｃｍ幅の範囲内全域に微細凹凸を設け、その他の部分を非 微細凹凸部１１としても、微細凹凸部１２の形成比率は、フィルムの少なくとも 一端部から１ｍ幅の範囲内で１０〜９０％の範囲内となるが、このようにしては 、ハウス内で日光の透過率が他に比較して低い部分が生じてしまうため、その部 分に栽培された作物の成育に悪影響を及ぼす。 従って、微細凹凸部１２は、本実施例のように、フィルムの少なくとも一端部 から１ｍ幅の範囲内の任意の箇所に選定した１ｍ四方の正方形内では、どの箇所 においても形成比率が１０〜９０％の範囲内に入り、微細凹凸部１２および非微 細凹凸部１１が略均一に分散しているように設けるのが望ましい。Further, it is important that the fine concavo-convex portion 12 is provided such that at least one of the fine concavo-convex portion 12 and the non-fine concavo-convex portion 11 on which the fine concavo-convex is not provided is discontinuous. For example, even if fine concavities and convexities are provided in the entire area within a width of 80 cm from one end and the other portions are non-fine concavo-convex portions 11, the formation ratio of the fine concavo-convex portions 12 is within a range of 1 m width from at least one end of the film. However, in this way, there will be some parts of the house where the sunlight transmittance is lower than other parts, so the growth of the crops cultivated in those parts will occur. Adversely affect. Therefore, the fine unevenness portion 12 has a formation ratio of 10 to 90 at any position within a 1 m square, which is selected at an arbitrary position within a width of 1 m from at least one end of the film as in the present embodiment. It is desirable that the fine unevenness portion 12 and the non-fine unevenness portion 11 are provided so as to be dispersed substantially uniformly within the range of%.
【００３２】 微細な凹凸が設けられていない非微細凹凸部１１は、フィルムの全表面中の１ ０％以上とするのが好ましく、さらに好ましくは３０％以上である。本実施例で は、フィルムの全表面の約７５％となっている。非微細凹凸部１１の形成比率が 小さいと、充分な光線透過が得られず、栽培された作物の成育に悪影響を及ぼす 。 また、非微細凹凸部１１は、５００〜６００ｎｍの波長の平行光線平均透過率 が６０％以上、全光線平均透過率が８０％以上とするのが好ましく、本実施例に おける上記平行光線平均透過率は約８５％、全光線平均透過率は約９０％となっ ている。このようにすることで、フィルム全体としての光線透過が良好となり、 ハウス内の環境を作物の成育により適したものとするとともに、ハウス内外の様 子がフィルムを通して判別することができ、農作業の効率化につながる。The non-fine concavo-convex portion 11 having no fine concavities and convexities is preferably 10% or more, and more preferably 30% or more of the entire surface of the film. In this example, it is about 75% of the total surface of the film. When the formation ratio of the non-fine concavo-convex portion 11 is small, sufficient light transmission cannot be obtained, which adversely affects the growth of the cultivated crop. Further, it is preferable that the non-fine concavo-convex portion 11 has an average transmittance of parallel rays at a wavelength of 500 to 600 nm of 60% or more and an average transmittance of all rays of 80% or more. The transmittance is about 85% and the average transmittance of all rays is about 90%. By doing so, the light transmission of the film as a whole will be good, making the environment in the house more suitable for the growth of crops, and the elements inside and outside the house can be discriminated through the film, thus improving the efficiency of agricultural work. Lead to
【００３３】 本実施例では、微細凹凸部１２と非微細凹凸部１１を、斜めのストライプ状に 交互に配置してなるが、これに限定されず、フィルムの少なくとも一端部から１ ｍ幅の範囲内で、微細凹凸を設けた微細凹凸部１２の形成比率が１０〜９０％で 、かつ微細凹凸部１２または非微細凹凸部１１の少なくとも一方が不連続であれ ば、いかなる配置をとってもよく、たとえば微細凹凸部１２または非微細凹凸部 １１を縦あるいは横のストライプ状、格子状、水玉状に配置してもよい。In this embodiment, the fine concavo-convex portions 12 and the non-fine concavo-convex portions 11 are alternately arranged in a diagonal stripe shape. However, the present invention is not limited to this, and a range of 1 m width from at least one end portion of the film. In the above, any arrangement may be adopted as long as the formation ratio of the fine concavo-convex portion 12 having the fine concavo-convex is 10 to 90% and at least one of the fine concavo-convex portion 12 and the non-fine concavo-convex portion 11 is discontinuous, for example, The fine concavo-convex portion 12 or the non-fine concavo-convex portion 11 may be arranged vertically or horizontally in a striped pattern, a lattice pattern, or a polka dot pattern.
【００３４】 また、本実施例においては、フィルム全表面を微細凹凸部１２の形成領域とし たが、本考案の農業用フィルムは、必ずしもフィルム全面を微細凹凸部１２の形 成領域とする必要はなく、フィルムの少なくとも一端部から１ｍ幅の範囲内を上 記の微細凹凸部１２の形成領域とすれば、本考案の目的とする光線透過率を悪化 させることなく、巻き上げ作業なども容易である農業用フィルムを得ることがで きる。 なお、微細凹凸部１２の形成領域以外の部分については、いかなる状態であっ てよく、例えば全域にわたって微細凹凸を設けてもよいし、全く微細凹凸を設け なくてもよいが、充分な光線を透過させるためには、全域にわたって微細凹凸を 設けないか、本実施例のように微細凹凸部１２と非微細凹凸部１１が混然となる ように微細凹凸を設けるのが望ましい。Further, in the present embodiment, the entire surface of the film is used as the formation area of the fine unevenness portion 12, but the agricultural film of the present invention does not necessarily need to have the entire surface of the film as the formation area of the fine unevenness portion 12. If the area within 1 m width from at least one end of the film is used as the formation area of the above-mentioned fine concavo-convex portion 12, the light-transmitting rate, which is the object of the present invention, is not deteriorated, and the winding operation is easy. Agricultural film can be obtained. It should be noted that the portion other than the formation region of the fine concavo-convex portion 12 may be in any state, for example, the fine concavo-convex may be provided over the entire region, or the fine concavo-convex may not be provided at all, but sufficient light rays are transmitted. In order to do so, it is desirable not to provide fine unevenness over the entire region, or to provide fine unevenness so that the fine unevenness portion 12 and the non-fine unevenness portion 11 are mixed as in this embodiment.
【００３５】 また、本考案の農業用フィルムは、微細凹凸が設けられていない面に、水系、 溶剤系または紫外線硬化系の塗料からなる塗膜１３が設けられている。この塗膜 １３により、塵埃などの付着が抑止され、またフィルムに防滴剤を配合した場合 には、防滴持続性も良好になるという効果が得られる。Further, the agricultural film of the present invention is provided with a coating film 13 made of a water-based, solvent-based or ultraviolet-curable coating material on the surface on which the fine irregularities are not provided. The coating film 13 has the effect of suppressing the adhesion of dust and the like, and when the film is mixed with a drip-proof agent, the drip-proof durability is also improved.
【００３６】 水系、溶剤系または紫外線硬化系の塗料として、具体的には下記のようなもの が挙げられる。 水系としては、アクリル樹脂系、ポリエステル樹脂系、ポリウレタン樹脂系、 エポキシ樹脂系などが使用できる。 また、溶剤系としては、アクリル樹脂系、セルロース樹脂系、塩化ビニル樹脂 系、フッ素樹脂系、ポリアミド樹脂系、ポリウレタン樹脂系、エポキシ樹脂系、 シリコーン樹脂系などが挙げられる。 さらに、紫外線硬化系としては、ポリエステルアクリレート系、エポキシアク リレート系、ポリウレタンアクリレート系などが挙げられる。Specific examples of the water-based, solvent-based or ultraviolet-curable coating materials include the following. As the water system, acrylic resin system, polyester resin system, polyurethane resin system, epoxy resin system and the like can be used. Examples of the solvent system include acrylic resin system, cellulose resin system, vinyl chloride resin system, fluororesin system, polyamide resin system, polyurethane resin system, epoxy resin system and silicone resin system. Further, examples of the ultraviolet curing system include polyester acrylate system, epoxy acrylate system and polyurethane acrylate system.
【００３７】 本実施例の農業用フィルムの使用にあっては、図外のビニルハウスの骨組を外 方から被うように微細凹凸部１２が形成された面を内側にし、かつ微細凹凸部１ ２の形成領域が巻き上げる部分となるようにして取りつける。このようにして取 り付け、例えば夏期の日差しが強い日に、ビニルハウス内の換気を良くするため に、ハウスの側面を被う農業用フィルム１０を外側に巻き上げれば、密着しにく い微細凹凸部１２が、密着し易い非微細凹凸部１１の表面に点接着状態で巻き上 げられる。このような点接着は、面接着に比べて剥がし易いので、フィルム１０ を巻き戻してビニルハウスの開口された側面を閉じる際に、フィルムどうしが密 着することなく、スムーズに巻き戻しの作業が行える。 また、塵埃などの付着し易い外側には、水系、溶剤系または紫外線硬化系の塗 料からなる塗膜が設けてあるので、塵埃が付着し難く、塵埃付着による光線透過 率の低下を抑制することができる。 なお、本考案の農業用フィルムをビニルハウスの天窓に使用する場合にも、同 様である。In the use of the agricultural film of the present embodiment, the surface on which the fine concavo-convex portion 12 is formed so that the frame of the vinyl house (not shown) is covered from the outside, and the fine concavo-convex portion 1 is formed. Attach so that the formation area of 2 becomes the part to be rolled up. In this way, if the agricultural film 10 covering the sides of the greenhouse is rolled up to improve ventilation in the greenhouse, for example, on a day with strong sunlight in the summer, it will be difficult to adhere. The fine concavo-convex portion 12 is wound on the surface of the non-fine concavo-convex portion 11 which is easily adhered in a point-bonded state. Since such point adhesion is easier to peel off than surface adhesion, when the film 10 is rewound to close the open side surface of the vinyl house, the films do not stick to each other and the rewinding operation is smooth. You can do it. In addition, a coating film made of water-based, solvent-based, or UV-curable coating is provided on the outside where dust is likely to adhere, so it is difficult for dust to adhere, and the decrease in light transmittance due to dust adhesion is suppressed. be able to. The same applies when the agricultural film of the present invention is used for a skylight of a vinyl house.
【００３８】 以上、本考案の実施例を具体的に説明したが、本考案はこの実施例に限定され るものではなく、要旨を逸脱しない範囲での設計変更などがあっても本考案に含 まれる。 例えば、本考案の農業用フィルムは、ビニルハウスの外装材としてのみでなく 、例えばカーテン、トンネルなどにも適用できる。Although the embodiment of the present invention has been specifically described above, the present invention is not limited to this embodiment, and even if there are design changes and the like without departing from the scope of the invention, the present invention is not limited thereto. Get caught For example, the agricultural film of the present invention can be applied not only as an exterior material for vinyl houses, but also for curtains, tunnels, and the like.
【００３９】[0039]
本考案の農業用フィルムは、農業用フィルムに要求される透光性を確保しつつ 、フィルムどうしの密着を防止することができる。従って、ビニルハウス内など で栽培する作物の成育に適した環境を作り、かつ巻き上げ作業なども容易に行え るという効果を奏するものである。しかも、一方の面に、水系、溶剤系または紫 外線硬化系の塗料からなる塗膜が設けてあるので、塵埃が付着し難く、長期にわ たって使用しても塵埃付着による光線透過率の低下が生じない。 INDUSTRIAL APPLICABILITY The agricultural film of the present invention can prevent the films from sticking to each other while ensuring the translucency required for the agricultural film. Therefore, it is possible to create an environment suitable for growing crops cultivated in a vinyl house and to easily perform winding work. Moreover, since a coating film made of water-based, solvent-based, or UV-curing paint is provided on one surface, it is difficult for dust to adhere, and the light transmittance decreases due to dust adhesion even after long-term use. Does not occur.
【提出日】平成６年９月１３日[Submission date] September 13, 1994
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Correction target item name] Full text
【補正方法】変更[Correction method] Change
【０００１】[0001]
本考案は、農業用フィルムに関し、さらに詳しくは光線の透過率を悪化させる ことなく、フィルムの密着性を抑制し、しかも塵埃の付着防止効果も有する農業 用フィルムに関する。 The present invention relates to an agricultural film, and more particularly to an agricultural film that suppresses the adhesiveness of the film without deteriorating the transmittance of light rays and also has an effect of preventing adhesion of dust.
【０００２】[0002]
従来、例えばビニルハウスは、所定形状に屈曲された鉄製あるいはステンレス 製のパイプを連結して骨組を造り、所定箇所に天窓や出入り口を設けて、その表 面を透明な塩化ビニル系樹脂フィルムにより被っている。 Conventionally, for example, a vinyl house is made by connecting iron or stainless steel pipes bent into a predetermined shape to form a frame, providing a skylight or an entrance at a predetermined position, and covering the surface with a transparent vinyl chloride resin film. ing.
【０００３】 上記のようなビニルハウスでは、夏期の暑い日には、日差しが強くてハウス内 の温度が高くなり過ぎるので、出入り口を開けるのはもちろん、ビニルハウスの 側面をロール状に巻き上げたり、天窓を押し上げたりして換気を良くすることに より室内温度の調整が行われている。In such a vinyl house, on a hot summer day, the sunshine is strong and the temperature inside the house becomes too high, so of course, not only opening the doorway, but also winding up the sides of the vinyl house in a roll shape. The room temperature is adjusted by pushing up the skylight and improving ventilation.
【０００４】[0004]
ところで、従来のビニルハウスを被っているフィルムには、表面がベタつき易 い一般の塩化ビニル系樹脂フィルムが使用されているので、例えば側面をロール 状に巻き上げた際に接触している部分が互いに密着してしまい、巻き上げや巻き 戻し時に大変な手間がかかっていた。 By the way, since conventional vinyl chloride resin films that have a sticky surface are used for the film that covers conventional vinyl houses, for example, the parts that are in contact when the side surfaces are rolled up are They were in close contact with each other, and it took a lot of time and effort when hoisting and rewinding.
【０００５】 そこで、フィルムの全表面に梨地加工したり、無機質微粉末を添加してフィル ムの全表面を荒らしたりして、フィルムどうしが密着するのを防止することも提 案されているが、このようなフィルムでは、ハウス内で栽培される作物に必要な 日光の透過率が不充分で、日光をハウス内に取り入れて温室栽培を行うビニルハ ウス本来の機能を充分に果たせないという、別の問題が発生していた。Therefore, it has been proposed to prevent the films from adhering to each other by performing satin finish on the entire surface of the film or adding inorganic fine powder to roughen the entire surface of the film. , Such a film does not have sufficient sunlight transmittance for the crops cultivated in the greenhouse, and cannot perform the original function of the vinyl house that is used for greenhouse cultivation by incorporating sunlight into the greenhouse. Was having problems.
【０００６】 本考案は、このような従来技術を背景になされたもので、光線の透過率を悪化 させることなく、フィルムの密着を低減でき、しかも汚れ防止効果も有する農業 用フィルムを提供することを目的とする。The present invention has been made against the background of such a conventional technique, and provides an agricultural film which can reduce the adhesion of the film without deteriorating the transmittance of light and have an antifouling effect. With the goal.
【０００７】[0007]
【課題を解決するための手段】 本考案は、塩化ビニル系樹脂を主成分とし、片面に微細凹凸を設けた微細凹凸 部と微細凹凸を設けない非微細凹凸部を有するフィルムの微細凹凸を設けていな い側の面に、水系、溶剤系または紫外線硬化系の塗料からなる塗膜を設けた農業 用フィルムであって、少なくともフィルム端部のいずれか１つに沿った１ｍ幅の 範囲内においては、微細凹凸部および／または非微細凹凸部が不連続で、かつ微 細凹凸部の形成比率が１０〜９０％になるように微細凹凸を形成したことを特徴 とする農業用フィルムを提供するものである。Means for Solving the Problems The present invention provides a fine unevenness of a film containing a vinyl chloride resin as a main component and having a fine unevenness portion having fine unevenness on one surface and a non-fine unevenness portion having no fine unevenness. An agricultural film having a coating film made of a water-based, solvent-based, or UV-curable coating on the side that is not covered, within a width of 1 m along at least one of the film edges. Provides an agricultural film characterized in that the fine irregularities and / or the non-fine irregularities are discontinuous, and the fine irregularities are formed so that the formation ratio of the fine irregularities is 10 to 90%. It is a thing.
【０００８】 また、上記の微細凹凸部は、５００〜６００ｎｍの波長の平行光線平均透過率 が４０％以下、全光線平均透過率が７５％以上とし、微細凹凸を設けない非微細 凹凸部は、５００〜６００ｎｍの波長の平行光線平均透過率が６０％以上、全光 線平均透過率が８０％以上とすることが好ましい。The fine irregularities have a parallel light ray average transmittance of 40% or less and a total light ray average transmittance of 75% or more at a wavelength of 500 to 600 nm, and a non-fine irregularity portion having no fine unevenness is It is preferable that the parallel light beam average transmittance at a wavelength of 500 to 600 nm is 60% or more, and the total light beam average transmittance is 80% or more.
【０００９】[0009]
本考案の農業用フィルムにおいては、フィルムの少なくとも一端部から１ｍ幅 の範囲内で、微細凹凸を設けた微細凹凸部を形成比率が１０〜９０％となるよう に形成しているので、フィルムを巻き上げたり重ねたりした場合でも、少なくと も一端部から１ｍ幅の範囲内ではフィルムどうしが密着するのを防止でき、また 微細凹凸を設けない非微細凹凸部を微細凹凸部を有する領域内では９０〜１０％ とすることにより、農業用フィルムに要求される透光性をも確保することができ る。 しかも、本考案の農業用フィルムは、上記の微細凹凸を設けていない側の面に 水系、溶剤系または紫外線硬化系の塗料からなる塗膜を設けたことにより、塵埃 などの付着が防止される。 In the agricultural film of the present invention, the fine concavo-convex portion provided with the fine concavo-convex portion is formed within a range of 1 m width from at least one end portion of the film so that the forming ratio is 10 to 90%. Even when rolled up or piled up, it is possible to prevent the films from sticking to each other within a width of at least 1 m from one end, and to prevent non-fine irregularities without fine irregularities from being 90% By setting it to 10%, it is possible to secure the translucency required for the agricultural film. Moreover, the agricultural film of the present invention is provided with a coating film made of a water-based, solvent-based, or UV-curing paint on the surface on which the fine irregularities are not provided, thereby preventing the adhesion of dust and the like. .
【００１０】[0010]
以下、本考案の一実施例を図面に基づいて詳細に説明する。本実施例ではビニ ルハウス用の農業用フィルムを例とする。 An embodiment of the present invention will be described below in detail with reference to the drawings. In this example, an agricultural film for a vinyl house is used as an example.
【００１１】 図１は本考案の一実施例の農業用フィルムの一部平面図、図２は実施例の農業 用フィルムの一部拡大断面図であり、図中１０はビニルハウスの外装材である、 塩化ビニル系樹脂を主成分とする農業用フィルムである。農業用フィルム１０の フィルム片面には、斜めに真っ直ぐ延びる非微細凹凸部１１と梨地加工の微細凹 凸部１２とが一定間隔で交互に配置されており、非微細凹凸部１１側の面には、 水系、溶剤系または紫外線硬化系の塗料からなるベタつき防止および汚れ防止用 の塗膜１３が設けられている。FIG. 1 is a partial plan view of an agricultural film according to an embodiment of the present invention, and FIG. 2 is a partially enlarged cross-sectional view of the agricultural film of the embodiment. In FIG. An agricultural film whose main component is vinyl chloride resin. On one surface of the film 10 for agricultural use, non-fine concavo-convex portions 11 extending obliquely straight and fine concavo-convex convex portions 12 having a satin finish are alternately arranged at regular intervals. A coating film 13 made of water-based, solvent-based or UV-curable coating material for preventing stickiness and stains is provided.
【００１２】 農業用フィルム１０の主成分である塩化ビニル系樹脂としては、ポリ塩化ビニ ルのほか、塩化ビニルと他の樹脂のモノマー、例えばエチレン、プロピレン、塩 化ビニリデン、アクリロニトリル、マレイン酸、イタコン酸、メタクリル酸、酢 酸ビニル、マレイン酸エステル、メタクリル酸メチルなどのメタクリル酸アルキ ルエステル、アクリル酸メチルなどのアクリル酸アルキルエステル、高級ビニル エーテルなどとの共重合樹脂、もしくはこれらのブレンド物などが使用できる。As the vinyl chloride-based resin which is the main component of the agricultural film 10, in addition to polyvinyl chloride, vinyl chloride and other resin monomers such as ethylene, propylene, vinylidene chloride, acrylonitrile, maleic acid, and itacone. Acid, methacrylic acid, vinyl acetate, maleic acid ester, methacrylic acid alkyl ester such as methyl methacrylate, acrylic acid alkyl ester such as methyl acrylate, copolymer resin with higher vinyl ether, or blends of these Can be used.
【００１３】 この塩化ビニル系樹脂１００重量部当たり、０．５〜６重量部の防滴剤を添加 することができる。０．５重量部未満では防滴性が悪く、一方６重量部を超える とフィルム表面へのふき出しが多くなり好ましくない。0.5 to 6 parts by weight of the dripproofing agent may be added to 100 parts by weight of the vinyl chloride resin. If the amount is less than 0.5 part by weight, the drip-proof property is poor, while if it exceeds 6 parts by weight, the amount of bleeding on the film surface increases, which is not preferable.
【００１４】 この防滴剤としては、ソルビタン脂肪酸エステル、ソルビトール脂肪酸エステ ル、グリセリン脂肪酸エステル、ジグリセリン脂肪酸エステル、ソルビタン脂肪 酸・二塩基酸エステル、ソルビトール脂肪酸・二塩基酸エステル、ジグリセリン 脂肪酸・二塩基酸エステル、グリセリン脂肪酸・二塩基酸エステルなどの多価ア ルコールと脂肪酸とのエステル、多価アルコールと脂肪酸および二塩基酸とのエ ステル、あるいはこれらにエチレンオキサイド、プロピレンオキサイド、ブチレ ンオキサイドなどのアルキレンオキサイドが付加された化合物などが挙げられ、 具体的にはソルビタンパルミテート、ソルビタンステアレート、ソルビタンステ アレート・エチレンオキサイド２モル付加物、ソルビタンステアレート・プロピ レンオキサイド３モル付加物、ソルビトールステアレート、ソルビトールステア レート・エチレンオキサイド３モル付加物、ジグリセリンパルミテート、ジグリ セリンステアレート、グリセリンステアレート、グリセリンパルミテート・エチ レンオキサイド２モル付加物、ソルビタンステアレートアジペート・エチレンオ キサイド３モル付加物、ソルビトールステアレートアジペート・エチレンオキサ イド２モル付加物、ジグリセリンパルミテートセバケート・プロピレンオキサイ ド３モル付加物、ソルビトールパルミテートアジペート・エチレンオキサイド３ モル付加物などが挙げられる。これらの防滴剤は、単独または２種以上を組み合 わせて使用することができる。Examples of the antidrip agent include sorbitan fatty acid ester, sorbitol fatty acid ester, glycerin fatty acid ester, diglycerin fatty acid ester, sorbitan fatty acid / dibasic acid ester, sorbitol fatty acid / dibasic acid ester, diglycerin fatty acid / dicarboxylic acid ester. Basic acid ester, ester of polyhydric alcohol and fatty acid such as glycerin fatty acid / dibasic acid ester, ester of polyhydric alcohol and fatty acid and dibasic acid, or ethylene oxide, propylene oxide, butylene oxide, etc. Examples thereof include compounds to which alkylene oxide is added. Specific examples include sorbitan palmitate, sorbitan stearate, sorbitan stearate / ethylene oxide 2 mol adduct, sorbitan stearate / propylate. 3 mol adduct of nitro oxide, sorbitol stearate, 3 mol adduct of sorbitol stearate / ethylene oxide, diglycerin palmitate, diglycerin stearate, glycerin stearate, glycerin palmitate / 2 mol adduct of ethylene oxide, sorbitan stearate Rate adipate / ethylene oxide 3 mol adduct, sorbitol stearate adipate / ethylene oxide 2 mol adduct, diglycerin palmitate sebacate / propylene oxide 3 mol adduct, sorbitol palmitate adipate / ethylene oxide 3 mol adduct And so on. These drip-proof agents can be used alone or in combination of two or more kinds.
【００１５】 本考案の農業用フィルムには、この防滴剤とともに、塩化ビニル系樹脂１００ 重量部当たり０．０１〜１．０重量部、好ましくは０．０５〜０．５重量部の含 フッ素系化合物を添加することができる。In the agricultural film of the present invention, 0.01 to 1.0 part by weight, preferably 0.05 to 0.5 part by weight, of fluorine-containing resin is added per 100 parts by weight of the vinyl chloride resin together with this drip-proofing agent. A system compound can be added.
【００１６】 含フッ素系化合物としては、１分子中に含フッ素基と水酸基またはアルキレン オキサイド基の少なくとも１種を有する含フッ素系化合物であり、含フッ素基と しては、パーフルオロアルキル基（Ｃn Ｆ2n+1基）、パーフルオロアルコキシ基 （Ｃn Ｆ2n+1Ｏ基）、ポリフルオロアルキル基（Ｈm Ｃn Ｆ2n+1-m基）、パーフ ルオロアルケニル基（Ｃn Ｆ2n-1基）、ポリフルオロアルケニル基（Ｈm Ｃn Ｆ 2n-1-m 基）、パーフルオロアルキレン基（Ｃn Ｆ2n基）などがあり、式中ｍ＝１ 〜３、ｎ＝３〜２０の整数である。アルキレンオキサイド基としては、（C2H4O) n 、（C3H4O)n などがあり、式中ｎ＝１〜３０である。The fluorinated compound is a fluorinated compound having at least one of a fluorinated group and a hydroxyl group or an alkylene oxide group in one molecule, and the fluorinated group includes a perfluoroalkyl group (CnF2n + 1Group), perfluoroalkoxy group (CnF2n + 1O group), polyfluoroalkyl group (HmCnF2n + 1-mGroup), perfluoroalkenyl group (CnF2n-1Group), polyfluoroalkenyl group (HmCnF 2n-1-m Group), perfluoroalkylene group (CnF2nGroup) and the like, and m = 1 to 3 and n = 3 to 20 in the formula. As the alkylene oxide group, (C2HFourO) n , (C3HFourO)nAnd n = 1 to 30 in the formula.
【００１７】 含フッ素系化合物の具体例としては、 C8F17C2H4O(C2H4O)8CH3 、 C8F17CH2CH2OHCH2O(C2H4O)10CH3 、 C14F21CH2CH(OCH3)CH2O(C2H4O)10CH3 、 C14F21CH2CH(OH)CH2O(C2H6O)10H 、 C8F17CH2CH(OCOH3)CH2O(C3H6O)8CH3、 C8F17SO2N(C2H5)(C2H4O)12、 C6F13CON(C2H5)(C2H4O)8H 、 C8F17SO2N[CH2CH(OH)CH2CH]2、 HCF2C5F10CH2O(C2H4O)10H 、 C3F7OC3F6CH2CH2SCH(COOH)CH2COO(C2H4O)10H、 C3F7OC3F10CH2CH2SCH(CH2COOH)CH2COO(C2H4O)15H、 H(CH−CH2 ) 2 −(CH-CH2)2H COOC2 H4C8F17 COO(C2 H4O)8H、 H[C(CH3)CH2]2 −〔C(CH3)CH2 〕2 −[C(CH3)CH2]H COOC2H4C10F21 COO(C3H6O)2H COO(C2H4O)8H などが挙げられるが、これらに限定されるものではない。Specific examples of the fluorine-containing compound include C 8 F 17 C 2 H 4 O (C 2 H 4 O) 8 CH 3 and C 8 F 17 CH 2 CH 2 OHCH 2 O (C 2 H 4 O ) 10 CH 3 , C 14 F 21 CH 2 CH (OCH 3 ) CH 2 O (C 2 H 4 O) 10 CH 3 , C 14 F 21 CH 2 CH (OH) CH 2 O (C 2 H 6 O) 10 H, C 8 F 17 CH 2 CH (OCOH 3 ) CH 2 O (C 3 H 6 O) 8 CH 3 , C 8 F 17 SO 2 N (C 2 H 5 ) (C 2 H 4 O) 12 , C 6 F 13 CON (C 2 H 5 ) (C 2 H 4 O) 8 H, C 8 F 17 SO 2 N [CH 2 CH (OH) CH 2 CH] 2 , HCF 2 C 5 F 10 CH 2 O (C 2 H 4 O) 10 H, C 3 F 7 OC 3 F 6 CH 2 CH 2 SCH (COOH) CH 2 COO (C 2 H 4 O) 10 H, C 3 F 7 OC 3 F 10 CH 2 CH 2 SCH (CH 2 COOH) CH 2 COO (C 2 H 4 O) 15 H, H (CH-CH 2 ) 2- (CH-CH 2 ) 2 H COOC 2 H 4 C 8 F 17 COO (C 2 H 4 O) 8 H, H [C (CH 3 ) CH 2 ] 2- [C (CH 3 ) CH 2 ] 2- [C (CH 3 ) CH 2 ] H COOC 2 H 4 C 10 F 21 COO (C 3 H 6 O) 2 H COO (C 2 H 4 O) 8 H and the like are included, but are not limited thereto.
【００１８】 また、本考案の農業用フィルムには、必要に応じて可塑剤、安定剤、滑剤また は粘着防止剤、紫外線吸収剤、抗酸化剤、光安定剤、無機質充填剤などを添加す ることができる。 塩化ビニル系樹脂に添加される可塑剤としては、一般可塑剤、リン酸エステル 系可塑剤、エポキシ系可塑剤が使用できる。In addition, a plasticizer, stabilizer, lubricant or anti-adhesive agent, ultraviolet absorber, antioxidant, light stabilizer, inorganic filler, etc. may be added to the agricultural film of the present invention as needed. You can As the plasticizer added to the vinyl chloride resin, a general plasticizer, a phosphoric acid ester plasticizer, or an epoxy plasticizer can be used.
【００１９】 一般可塑剤としては、ジ−ｎ−オクチルフタレート、ジ−２−エチルヘキシル フタレート、ジイソノニルフタレート、ジブチルフタレート、ブチルベンジルフ タレート、ジラウリルフタレート、ジデシルフタレート、ジウナデシルフタレー ト、ジトリデシルフタレートなどのフタル酸エステル系可塑剤、ジオクチルアジ ペート、ジトリノニルアジペート、ジイソデシルアジペートなどのアジピン酸エ ステル系可塑剤のほか、ポリエステル系可塑剤、セバチン酸系可塑剤、トリメリ ット酸系可塑剤なども使用できる。Examples of the general plasticizer include di-n-octyl phthalate, di-2-ethylhexyl phthalate, diisononyl phthalate, dibutyl phthalate, butylbenzyl phthalate, dilauryl phthalate, didecyl phthalate, diunadecyl phthalate, ditridecyl phthalate. Phthalates such as phthalate plasticizers, dioctyl adipate, ditrinonyl adipate, diisodecyl adipate and other adipate ester plasticizers, as well as polyester plasticizers, sebacic acid plasticizers, trimellitic acid plasticizers Can also be used.
【００２０】 リン酸エステル系可塑剤としては、トリクレジルホスフェート、トリキシリル ホスフェート、トリス（イソプロピルフェニル）ホスフェート、トリブチルホス フェート、トリエチルホスフェート、トリフェニルホスフェート、トリエチルフ ェニルホスフェートなどが使用できる。As the phosphate ester-based plasticizer, tricresyl phosphate, trixylyl phosphate, tris (isopropylphenyl) phosphate, tributylphosphate, triethylphosphate, triphenylphosphate, triethylphenylphosphate and the like can be used.
【００２１】 エポキシ系可塑剤としては、植物油のエポキシ化物、エポキシ樹脂が使用でき る。 植物油のエポキシ化物としては、エポキシ化大豆油、エポキシ化アマニ油など が使用できる。As the epoxy plasticizer, epoxidized vegetable oil and epoxy resin can be used. Epoxidized soybean oil, epoxidized linseed oil and the like can be used as the epoxidized vegetable oil.
【００２２】 エポキシ樹脂としては、エポキシ化ポリブタジエン、エポキシステアリン酸メ チル、エポキシステアリン酸ブチル、エポキシステアリン酸エチルヘキシル、ト リス（エポキシプロピル）イソシアヌレート、３−（２−キセノキシ）−１，２ −エポキシプロパン、ビスフェノールＡ、ジグリシジルエーテル、ビニルジシク ロヘキセンジエポキシサイド、２，２−ビス（４−ヒドロキシフェニル）プロパ ンとエピクロルヒドリンの重縮合物が挙げられる。 前記可塑剤は、１種または２種以上混合して用いられるが、好ましい添加量は 、塩化ビニル系樹脂１００重量部当たり、フタル酸エステル系可塑剤３０〜７０ 重量部、リン酸エステル系可塑剤１〜７重量部、エポキシ系可塑剤０．５〜７重 量部である。Epoxy resins include epoxidized polybutadiene, epoxy methyl stearate, butyl epoxy stearate, ethylhexyl epoxy stearate, tris (epoxypropyl) isocyanurate, 3- (2-xenoxy) -1,2-epoxy. Examples thereof include propane, bisphenol A, diglycidyl ether, vinyl dicyclohexene diepoxyside, and a polycondensation product of 2,2-bis (4-hydroxyphenyl) propane and epichlorohydrin. The above-mentioned plasticizers may be used alone or in combination of two or more, and the preferable addition amount is 30 to 70 parts by weight of phthalate ester-based plasticizer and 100 parts by weight of vinyl chloride-based resin, and phosphate ester-based plasticizer. 1 to 7 parts by weight and 0.5 to 7 parts by weight of epoxy plasticizer.
【００２３】 安定剤としては、金属セッケン、有機ホスファイト系安定剤などの通常使用さ れる安定剤が使用できる。 金属セッケンとしては、ステアリン酸亜鉛、ステアリン酸バリウム、ステアリ ン酸カルシウム、リシノール酸バリウム、ラウリン酸カルシウム、オレイン酸カ ルシウム、オクトイン酸亜鉛などが挙げられる。As the stabilizer, commonly used stabilizers such as metal soap and organic phosphite stabilizer can be used. Examples of the metal soap include zinc stearate, barium stearate, calcium stearate, barium ricinoleate, calcium laurate, calcium oleate, zinc octoinate and the like.
【００２４】 有機ホスファイト系安定剤としては、ジフェニルデシルホスファイト、トリフ ェニルホスファイト、トリス（ノニルフェニル）ホスファイト、トリデシルホス ファイト、トリス（２−エチルヘキシル）ホスファイト、トリステアリルホスフ ァイト、オクチルジフェニルホスファイトなどが挙げられる。 これらの安定剤は、１種または２種以上を用いることができる。Examples of the organic phosphite stabilizer include diphenyldecylphosphite, triphenylphosphite, tris (nonylphenyl) phosphite, tridecylphosphite, tris (2-ethylhexyl) phosphite, tristearylphosphite, octyldiphenylphosphite. Examples include fights. These stabilizers may be used either individually or in combination of two or more.
【００２５】 滑剤または粘着防止剤としては、ステアリン酸、イソステアリン酸、パルミチ ン酸などの脂肪酸系滑剤、ステアリン酸アミド、メチレンビスステアロアミド、 エチレンビスステアロアミドなどの脂肪酸アミド系滑剤、ブチルパルミテート、 ブチルステアレートなどのエステル系滑剤、バリウムイソデシルホスフェート、 カルシウムオクタデシルホスフェートなどの有機リン酸金属塩系滑剤、ポリエチ レンワックス、流動パラフィンなどが挙げられ、これらの１種または２種以上を 用いることができる。As the lubricant or anti-sticking agent, fatty acid type lubricants such as stearic acid, isostearic acid and palmitic acid, fatty acid amide type lubricants such as stearic acid amide, methylene bis stearoamide and ethylene bis stearoamide, butyl palmi Examples include ester lubricants such as tate and butyl stearate, organophosphate metal salt lubricants such as barium isodecyl phosphate and calcium octadecyl phosphate, polyethylene wax, liquid paraffin, etc., and one or more of them may be used. be able to.
【００２６】 紫外線吸収剤としては、一般に使用されているベンゾフェノン系、ベンゾトリ アゾール系、サリチル酸エステル系、シアノアクリレート系などの紫外線吸収剤 が挙げられ、これらの１種または２種以上を用いることができる。Examples of the ultraviolet absorber include benzophenone-based, benzotriazole-based, salicylate-based, and cyanoacrylate-based ultraviolet absorbers that are commonly used, and one or more of these can be used. .
【００２７】 抗酸化剤としては、フェノール系、チオジプロピオン酸エステル系、脂肪族サ ルファイド系などの抗酸化剤を１種または２種以上を用いることができる。 光安定剤としては、ヒンダードアミンなどの一般に使用されている光安定剤を １種または２種以上を用いることができる。As the antioxidant, one kind or two or more kinds of antioxidants such as phenol type, thiodipropionate type, and aliphatic sulfide type can be used. As the light stabilizer, one or more commonly used light stabilizers such as hindered amines can be used.
【００２８】 無機質微粉末は、フィルム表面のベタツキ防止や保温性を向上させる目的で使 用することができる。このような無機質微粉末としては、炭酸マグネシウム、マ グネシウムケイ酸塩、酸化ケイ素、酸化アルミニウム、水酸化アルミニウム、水 酸化マグネシウム、ハイドロタルサイト類の少なくとも１種以上を用いることが でき、微粉末の粒径は２０μｍ以下が好ましい。The inorganic fine powder can be used for the purpose of preventing stickiness of the film surface and improving heat retention. As such an inorganic fine powder, at least one kind of magnesium carbonate, magnesium silicate, silicon oxide, aluminum oxide, aluminum hydroxide, magnesium hydroxide and hydrotalcites can be used. The particle size is preferably 20 μm or less.
【００２９】 農業用フィルム１０のフィルムに形成された微細凹凸部１２は、フィルム片面 にエンボス加工などにより微細凹凸が形成されている。 また、上記の微細凹凸部１２は、５００〜６００ｎｍの波長の平行光線平均透 過率が４０％以下、全光線平均透過率が７５％以上とするのが好ましく、本実施 例における上記平行光線平均透過率は約７％、全光線平均透過率は約８０％にな っている。微細凹凸部１２の光線平均透過率を上記のようにすることで、フィル ム全体としての光線透過が良好となり、ハウス内の環境を作物の成育により適し たものとすることができる。The fine unevenness portion 12 formed on the film of the agricultural film 10 has fine unevenness formed on one surface of the film by embossing or the like. Further, it is preferable that the fine concavo-convex portion 12 has a parallel light beam average transmittance of 40% or less and a total light beam average transmittance of 75% or more at a wavelength of 500 to 600 nm. The transmittance is about 7% and the average transmittance for all rays is about 80%. By setting the average light transmittance of the fine concavo-convex portion 12 as described above, the light transmittance of the entire film becomes good, and the environment in the house can be made more suitable for the growth of crops.
【００３０】 上記の微細凹凸部１２の形成比率は、フィルムの少なくとも一端部から１ｍ幅 の範囲内で１０〜９０％、好ましくは２０〜７０％とする。本実施例では、フィ ルム全表面に略均一に微細凹凸部１２が形成されており、形成比率は２５％程度 となっている。微細凹凸部１２の形成比率が高すぎると、農業用フィルムに要求 される光線透過が確保できず、作物の成育に悪影響を及ぼす恐れがあり、逆に微 細凹凸部１２の形成比率が低すぎると、フィルムどうしが密着し、巻き上げ作業 などが困難になる。The formation ratio of the fine concavo-convex portion 12 is 10 to 90%, preferably 20 to 70% within the range of 1 m width from at least one end of the film. In this embodiment, the fine concavo-convex portion 12 is formed substantially uniformly on the entire surface of the film, and the forming ratio is about 25%. If the formation ratio of the fine concavo-convex portion 12 is too high, the light transmission required for the agricultural film cannot be secured, which may adversely affect the growth of the crop. On the contrary, the formation ratio of the fine concavo-convex portion 12 is too low. Then, the films stick to each other, making it difficult to wind them.
【００３１】 また、微細凹凸部１２は、該微細凹凸部１２または微細凹凸を設けない非微細 凹凸部１１の少なくとも一方が不連続となるように設けることが肝要である。例 えば、一端部から８０ｃｍ幅の範囲内全域に微細凹凸を設け、その他の部分を非 微細凹凸部１１としても、微細凹凸部１２の形成比率は、フィルムの少なくとも 一端部から１ｍ幅の範囲内で１０〜９０％の範囲内となるが、このようにしては 、ハウス内で日光の透過率が他に比較して低い部分が生じてしまうため、その部 分に栽培された作物の成育に悪影響を及ぼす。 従って、微細凹凸部１２は、本実施例のように、フィルムの少なくとも一端部 から１ｍ幅の範囲内の任意の箇所に選定した１ｍ四方の正方形内では、どの箇所 においても形成比率が１０〜９０％の範囲内に入り、微細凹凸部１２および非微 細凹凸部１１が略均一に分散しているように設けるのが望ましい。Further, it is important that the fine concavo-convex portion 12 is provided such that at least one of the fine concavo-convex portion 12 and the non-fine concavo-convex portion 11 on which the fine concavo-convex is not provided is discontinuous. For example, even if fine concavities and convexities are provided in the entire area within a width of 80 cm from one end and the other portions are non-fine concavo-convex portions 11, the formation ratio of the fine concavo-convex portions 12 is within a range of 1 m width from at least one end of the film. However, in this way, there will be some areas in the house where the sunlight transmittance is lower than other areas, so that the growth of the crops cultivated in those areas will occur. Adversely affect. Therefore, the fine unevenness portion 12 has a formation ratio of 10 to 90 at any position within a 1 m square, which is selected at an arbitrary position within a width of 1 m from at least one end of the film as in the present embodiment. It is desirable that the fine unevenness portion 12 and the non-fine unevenness portion 11 are provided so as to be dispersed substantially uniformly within the range of%.
【００３２】 微細な凹凸が設けられていない非微細凹凸部１１は、フィルムの全表面中の１ ０％以上とするのが好ましく、さらに好ましくは３０％以上である。本実施例で は、フィルムの全表面の約７５％となっている。非微細凹凸部１１の形成比率が 小さいと、充分な光線透過が得られず、栽培された作物の成育に悪影響を及ぼす 。 また、非微細凹凸部１１は、５００〜６００ｎｍの波長の平行光線平均透過率 が６０％以上、全光線平均透過率が８０％以上とするのが好ましく、本実施例に おける上記平行光線平均透過率は約８５％、全光線平均透過率は約９０％となっ ている。このようにすることで、フィルム全体としての光線透過が良好となり、 ハウス内の環境を作物の成育により適したものとするとともに、ハウス内外の様 子がフィルムを通して判別することができ、農作業の効率化につながる。The non-fine concavo-convex portion 11 having no fine concavities and convexities is preferably 10% or more, and more preferably 30% or more of the entire surface of the film. In this example, it is about 75% of the total surface of the film. When the formation ratio of the non-fine concavo-convex portion 11 is small, sufficient light transmission cannot be obtained, which adversely affects the growth of the cultivated crop. Further, it is preferable that the non-fine concavo-convex portion 11 has an average transmittance of parallel rays at a wavelength of 500 to 600 nm of 60% or more and an average transmittance of all rays of 80% or more. The transmittance is about 85% and the average transmittance of all rays is about 90%. By doing so, the light transmission of the film as a whole will be good, making the environment in the house more suitable for the growth of crops, and the elements inside and outside the house can be discriminated through the film, thus improving the efficiency of agricultural work. Lead to
【００３３】 本実施例では、微細凹凸部１２と非微細凹凸部１１を、斜めのストライプ状に 交互に配置してなるが、これに限定されず、フィルムの少なくとも一端部から１ ｍ幅の範囲内で、微細凹凸を設けた微細凹凸部１２の形成比率が１０〜９０％で 、かつ微細凹凸部１２または非微細凹凸部１１の少なくとも一方が不連続であれ ば、いかなる配置をとってもよく、例えば微細凹凸部１２または非微細凹凸部１ １を縦あるいは横のストライプ状、格子状、水玉状に配置してもよい。In this embodiment, the fine concavo-convex portions 12 and the non-fine concavo-convex portions 11 are alternately arranged in a diagonal stripe shape. However, the present invention is not limited to this, and a range of 1 m width from at least one end portion of the film. Among them, any arrangement may be adopted as long as the formation ratio of the fine unevenness portion 12 provided with fine unevenness is 10 to 90% and at least one of the fine unevenness portion 12 and the non-fine unevenness portion 11 is discontinuous, for example, The fine concavo-convex portion 12 or the non-fine concavo-convex portion 11 may be arranged in a vertical or horizontal stripe shape, a lattice shape, or a polka dot shape.
【００３４】 また、本実施例においては、フィルム全表面を微細凹凸部１２の形成領域とし たが、本考案の農業用フィルムは、必ずしもフィルム全面を微細凹凸部１２の形 成領域とする必要はなく、フィルムの少なくとも一端部から１ｍ幅の範囲内を上 記の微細凹凸部１２の形成領域とすれば、本考案の目的とする光線透過率を悪化 させることなく、巻き上げ作業なども容易である農業用フィルムを得ることがで きる。 なお、微細凹凸部１２の形成領域以外の部分については、いかなる状態であっ てよく、例えば全域にわたって微細凹凸を設けてもよいし、全く微細凹凸を設け なくてもよいが、充分な光線を透過させるためには、全域にわたって微細凹凸を 設けないか、本実施例のように微細凹凸部１２と非微細凹凸部１１が混然となる ように微細凹凸を設けるのが望ましい。Further, in the present embodiment, the entire surface of the film is used as the formation area of the fine unevenness portion 12, but the agricultural film of the present invention does not necessarily need to have the entire surface of the film as the formation area of the fine unevenness portion 12. If the area within 1 m width from at least one end of the film is used as the formation area of the above-mentioned fine concavo-convex portion 12, the light-transmitting rate, which is the object of the present invention, is not deteriorated, and the winding operation is easy. Agricultural film can be obtained. It should be noted that the portion other than the formation region of the fine concavo-convex portion 12 may be in any state. In order to do so, it is desirable not to provide fine unevenness over the entire region, or to provide fine unevenness so that the fine unevenness portion 12 and the non-fine unevenness portion 11 are mixed as in this embodiment.
【００３５】 また、本考案の農業用フィルムは、微細凹凸が設けられていない面に、水系、 溶剤系または紫外線硬化系の塗料からなる塗膜１３が設けられている。この塗膜 １３により、塵埃などの付着が抑止され、またフィルムに防曇剤を配合した場合 には、防曇持続性も良好になるという効果が得られる。Further, the agricultural film of the present invention is provided with a coating film 13 made of a water-based, solvent-based or ultraviolet-curable coating material on the surface on which the fine irregularities are not provided. The coating film 13 has an effect of suppressing the adhesion of dust and the like, and when the film is mixed with an antifogging agent, the antifogging sustainability is also improved.
【００３６】 水系、溶剤系または紫外線硬化系の塗料として、具体的には下記のようなもの が挙げられる。 水系としては、アクリル樹脂系、ポリエステル樹脂系、ポリウレタン樹脂系、 エポキシ樹脂系などが使用できる。 また、溶剤系としては、アクリル樹脂系、セルロース樹脂系、塩化ビニル樹脂 系、フッ素樹脂系、ポリアミド樹脂系、ポリウレタン樹脂系、エポキシ樹脂系、 シリコーン樹脂系などが挙げられる。 さらに、紫外線硬化系としては、ポリエステルアクリレート系、エポキシアク リレート系、ポリウレタンアクリレート系などが挙げられる。Specific examples of the water-based, solvent-based or ultraviolet-curable coating materials include the following. As the water system, acrylic resin system, polyester resin system, polyurethane resin system, epoxy resin system and the like can be used. Examples of the solvent system include acrylic resin system, cellulose resin system, vinyl chloride resin system, fluororesin system, polyamide resin system, polyurethane resin system, epoxy resin system and silicone resin system. Further, examples of the ultraviolet curing system include polyester acrylate system, epoxy acrylate system and polyurethane acrylate system.
【００３７】 本実施例の農業用フィルムの使用にあっては、図外のビニルハウスの骨組を外 方から被うように微細凹凸部１２が形成された面を内側にし、かつ微細凹凸部１ ２の形成領域が巻き上げる部分となるようにして取りつける。このようにして取 り付け、例えば夏期の日差しが強い日に、ビニルハウス内の換気を良くするため に、ハウスの側面を被う農業用フィルム１０を外側に巻き上げれば、密着しにく い微細凹凸部１２が、密着し易い非微細凹凸部１１の表面に点接着状態で巻き上 げられる。このような点接着は、面接着に比べて剥がし易いので、フィルム１０ を巻き戻してビニルハウスの開口された側面を閉じる際に、フィルムどうしが密 着することなく、スムーズに巻き戻しの作業が行える。 また、塵埃などの付着し易い外側には、水系、溶剤系または紫外線硬化系の塗 料からなる塗膜が設けてあるので、塵埃が付着し難く、塵埃付着による光線透過 率の低下を抑制することができる。 なお、本考案の農業用フィルムをビニルハウスの天窓に使用する場合にも、同 様である。In the use of the agricultural film of the present embodiment, the surface on which the fine concavo-convex portion 12 is formed so that the frame of the vinyl house (not shown) is covered from the outside, and the fine concavo-convex portion 1 is formed. Attach so that the formation area of 2 becomes the part to be rolled up. In this way, if the agricultural film 10 covering the sides of the greenhouse is rolled up to improve ventilation in the greenhouse, for example, on a day with strong sunlight in the summer, it will be difficult to adhere. The fine concavo-convex portion 12 is wound on the surface of the non-fine concavo-convex portion 11 which is easily adhered in a point-bonded state. Since such point adhesion is easier to peel off than surface adhesion, when the film 10 is rewound to close the open side surface of the vinyl house, the films do not stick to each other and the rewinding operation is smooth. You can do it. In addition, a coating film made of water-based, solvent-based, or UV-curable coating is provided on the outside where dust is likely to adhere, so it is difficult for dust to adhere, and the decrease in light transmittance due to dust adhesion is suppressed. be able to. The same applies when the agricultural film of the present invention is used for a skylight of a vinyl house.
【００３８】 以上、本考案の実施例を具体的に説明したが、本考案はこの実施例に限定され るものではなく、要旨を逸脱しない範囲での設計変更などがあっても本考案に含 まれる。 例えば、本考案の農業用フィルムは、ビニルハウスの外装材としてのみでなく 、例えばカーテン、トンネルなどにも適用できる。Although the embodiment of the present invention has been specifically described above, the present invention is not limited to this embodiment, and even if there are design changes and the like without departing from the scope of the invention, the present invention is not limited thereto. Get caught For example, the agricultural film of the present invention can be applied not only as an exterior material for vinyl houses, but also for curtains, tunnels, and the like.
【００３９】[0039]
本考案の農業用フィルムは、農業用フィルムに要求される透光性を確保しつつ 、フィルムどうしの密着を防止することができる。従って、ビニルハウス内など で栽培する作物の成育に適した環境を作り、かつ巻き上げ作業なども容易に行え るという効果を奏するものである。しかも、一方の面に、水系、溶剤系または紫 外線硬化系の塗料からなる塗膜が設けてあるので、塵埃が付着し難く、長期にわ たって使用しても塵埃付着による光線透過率の低下が生じない。 INDUSTRIAL APPLICABILITY The agricultural film of the present invention can prevent the films from sticking to each other while ensuring the translucency required for the agricultural film. Therefore, it is possible to create an environment suitable for growing crops cultivated in a vinyl house and to easily perform winding work. Moreover, since a coating film made of water-based, solvent-based, or UV-curing paint is provided on one surface, it is difficult for dust to adhere, and the light transmittance decreases due to dust adhesion even after long-term use. Does not occur.
【図１】本考案の一実施例に係る農業用フィルムの平面
図である。FIG. 1 is a plan view of an agricultural film according to an embodiment of the present invention.
【図２】実施例の農業用フィルムの一部拡大断面図であ
る。FIG. 2 is a partially enlarged cross-sectional view of an agricultural film of an example.
１０ 農業用フィルム １１ 非微細凹凸部 １２ 微細凹凸部 １３ 塗膜 10 Agricultural film 11 Non-fine irregularities 12 Fine irregularities 13 Coating film
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成６年９月１３日[Submission date] September 13, 1994
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Correction target item name] Full text
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【書類名】 明細書[Document name] Statement
【考案の名称】 農業用フィルム[Name of device] Agricultural film
【実用新案登録請求の範囲】[Scope of utility model registration request]
【図面の簡単な説明】[Brief description of drawings]
【図１】本考案の一実施例に係る農業用フィルムの平面
図である。FIG. 1 is a plan view of an agricultural film according to an embodiment of the present invention.
【図２】実施例の農業用フィルムの一部拡大断面図であ
る。FIG. 2 is a partially enlarged cross-sectional view of an agricultural film of an example.
【符号の説明】 １０ 農業用フィルム １１ 非微細凹凸部 １２ 微細凹凸部 １３ 塗膜[Explanation of Codes] 10 Agricultural film 11 Non-fine irregularities 12 Fine irregularities 13 Coating film
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 7/02 １０３ 9268−4Ｆ 27/08 8413−4Ｆ 27/30 １０１ 8115−4Ｆ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location B32B 7/02 103 9268-4F 27/08 8413-4F 27/30 101 8115-4F
Claims (15)
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が１０〜９０％になる
ように微細凹凸を形成したことを特徴とする農業用フィ
ルム。1. A water-based film having a main surface of which a vinyl chloride resin is a main component and having a fine unevenness portion having fine unevenness on one surface and a non-fine unevenness portion having no fine unevenness on the surface on which the fine unevenness is not provided. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. A film for agriculture, characterized in that the fine irregularities are discontinuous, and the fine irregularities are formed so that the formation ratio of the fine irregularities is 10 to 90%.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が２０〜７０％になる
ように微細凹凸を形成したことを特徴とする農業用フィ
ルム。2. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having fine irregularities having fine irregularities on one surface and non-fine irregularities having no fine irregularities on the side not having the fine irregularities. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. A film for agriculture, characterized in that the fine irregularities are discontinuous, and the fine irregularities are formed so that the formation rate of the fine irregularities is 20 to 70%.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が１０〜９０％になる
とともに、該フィルム端部のいずれか１つに沿った１ｍ
幅の範囲内で任意の箇所に選定した１ｍ四方の正方形内
における微細凹凸部の形成比率が１０〜９０％となるよ
うに微細凹凸を形成したことを特徴とする農業用フィル
ム。3. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having a fine unevenness portion having fine unevenness on one surface and a non-fine unevenness portion having no fine unevenness on the side not having the fine unevenness. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. The fine concavo-convex portion is discontinuous, the formation rate of the fine concavo-convex portion is 10 to 90%, and 1 m along any one of the edge portions of the film.
A film for agriculture, characterized in that the fine irregularities are formed so that the formation rate of the fine irregularities within a square of 1 m square selected at any position within the width range is 10 to 90%.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が２０〜７０％になる
とともに、該フィルム端部のいずれか１つに沿った１ｍ
幅の範囲内で任意の箇所に選定した１ｍ四方の正方形内
における微細凹凸部の形成比率が２０〜７０％となるよ
うに微細凹凸を形成したことを特徴とする農業用フィル
ム。4. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having a fine unevenness portion having fine unevenness on one surface and a non-fine unevenness portion having no fine unevenness on the side not having the fine unevenness. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. The fine concavo-convex portion is discontinuous, the formation rate of the fine concavo-convex portion becomes 20 to 70%, and 1 m along any one of the edge portions of the film.
A film for agriculture, characterized in that fine irregularities are formed such that the formation rate of the fine irregularities within a square of 1 m square selected at any location within the width range is 20 to 70%.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が１０〜９０％になる
とともに、該フィルム端部のいずれか１つに沿った１ｍ
幅の範囲外には微細凹凸が設けられていないことを特徴
とする農業用フィルム。5. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having fine irregularities having fine irregularities on one surface and non-fine irregularities having no fine irregularities on the side not having the fine irregularities. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. The fine concavo-convex portion is discontinuous, the formation rate of the fine concavo-convex portion is 10 to 90%, and 1 m along any one of the edge portions of the film.
Agricultural film characterized by not having fine irregularities outside the width range.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、少なくともフ
ィルム端部のいずれか１つに沿った１ｍ幅の範囲内にお
いては、微細凹凸部および／または非微細凹凸部が不連
続で、かつ微細凹凸部の形成比率が２０〜７０％になる
とともに、該フィルム端部のいずれか１つに沿った１ｍ
幅の範囲外には微細凹凸が設けられていないことを特徴
とする農業用フィルム。6. A water-based film on the side not provided with fine irregularities of a film containing a vinyl chloride resin as a main component and having fine irregularities having fine irregularities on one surface and non-fine irregularities having no fine irregularities. , An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, and within a range of 1 m width along at least one of the film edge portions, fine irregularities and / or non-concave portions. The fine concavo-convex portion is discontinuous, the formation rate of the fine concavo-convex portion becomes 20 to 70%, and 1 m along any one of the edge portions of the film.
Agricultural film characterized by not having fine irregularities outside the width range.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、フィルム表面
全域にわたって微細凹凸部と非微細凹凸部が混然とな
り、かつ少なくともフィルム端部のいずれか１つに沿っ
た１ｍ幅の範囲内においては、微細凹凸部および／また
は非微細凹凸部が不連続で、かつ微細凹凸部の形成比率
が１０〜９０％になるように微細凹凸を形成したことを
特徴とする農業用フィルム。7. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having fine irregularities on one surface of which fine irregularities and non-fine irregularities do not have fine irregularities, on the side on which the fine irregularities are not provided. An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, in which fine irregularities and non-fine irregularities are mixed over the entire surface of the film, and at least one of the film edges is formed. Within the range of 1 m width along the line, the fine concavo-convex portion and / or the non-fine concavo-convex portion are discontinuous, and the fine concavo-convex portion is formed so that the formation ratio of the fine concavo-convex portion is 10 to 90%. Agricultural film.
微細凹凸を設けた微細凹凸部と微細凹凸を設けない非微
細凹凸部を有するフィルムの微細凹凸を設けていない側
の面に、水系、溶剤系または紫外線硬化系の塗料からな
る塗膜を設けた農業用フィルムであって、フィルム表面
全域にわたって微細凹凸部と非微細凹凸部が混然とな
り、かつ少なくともフィルム端部のいずれか１つに沿っ
た１ｍ幅の範囲内においては、微細凹凸部および／また
は非微細凹凸部が不連続で、かつ微細凹凸部の形成比率
が２０〜７０％になるように微細凹凸を形成したことを
特徴とする農業用フィルム。8. A water-based film is formed on a surface of a film containing a vinyl chloride-based resin as a main component and having fine irregularities on one surface of which fine irregularities are provided and non-fine irregularities on which no fine irregularities are provided, on the side not provided with fine irregularities. An agricultural film provided with a coating film composed of a solvent-based or ultraviolet-curable coating material, in which fine irregularities and non-fine irregularities are mixed over the entire surface of the film, and at least one of the film edges is formed. Within the range of 1 m width along the line, the fine concavo-convex portion and / or the non-fine concavo-convex portion are discontinuous, and the fine concavo-convex portion is formed so that the formation ratio of the fine concavo-convex portion is 20 to 70%. Agricultural film.
凸部が、フィルム表面中の１０％以上である請求項１〜
８いずれか１項記載の農業用フィルム。9. The non-fine concavo-convex portion not provided with fine concavities and convexities accounts for 10% or more of the film surface.
8. The agricultural film according to any one of 8 above.
凹凸部が、フィルム表面中の３０％以上である請求項１
〜８いずれか１項記載の農業用フィルム。10. The non-fine concavo-convex portion having no fine concavity and convexity is 30% or more of the film surface.
The agricultural film according to any one of 8 to 8.
に微細凹凸を設けた微細凹凸部と微細凹凸を設けない非
微細凹凸部を有するフィルムの微細凹凸を設けていない
側の面に、水系、溶剤系または紫外線硬化系の塗料から
なる塗膜を設けた農業用フィルムであって、フィルム全
表面に、縦のストライプ状、横のストライプ状、斜めの
ストライプ状、格子状、あるいは水玉状の微細凹凸部を
略一定間隔に形成し、かつ微細凹凸部の形成比率が１０
〜９０％になるように微細凹凸を形成したことを特徴と
する農業用フィルム。11. A water-based film, which is a main component of a vinyl chloride resin and has a fine uneven portion having fine unevenness on one surface and a non-fine uneven portion having no fine unevenness, on the surface on which the fine unevenness is not provided. A film for agriculture provided with a coating film composed of a solvent-based or UV-curable paint, which has a vertical stripe shape, a horizontal stripe shape, an oblique stripe shape, a grid shape, or a polka dot shape on the entire surface of the film. The fine concavo-convex portions are formed at substantially constant intervals, and the formation ratio of the fine concavo-convex portions is 10
A film for agriculture, characterized in that fine irregularities are formed so as to be up to 90%.
に微細凹凸を設けた微細凹凸部と微細凹凸を設けない非
微細凹凸部を有するフィルムの微細凹凸を設けていない
側の面に、水系、溶剤系または紫外線硬化系の塗料から
なる塗膜を設けた農業用フィルムであって、フィルム全
表面に、縦のストライプ状、横のストライプ状、斜めの
ストライプ状、格子状、あるいは水玉状の微細凹凸部を
略一定間隔に形成し、かつ微細凹凸部の形成比率が２０
〜７０％になるように微細凹凸を形成したことを特徴と
する農業用フィルム。12. A water-based film having a main surface of which a vinyl chloride resin is a main component and having a fine uneven portion having fine unevenness on one surface and a non-fine uneven portion having no fine unevenness, on a surface on which no fine unevenness is provided. A film for agriculture provided with a coating film composed of a solvent-based or UV-curable paint, which has a vertical stripe shape, a horizontal stripe shape, an oblique stripe shape, a grid shape, or a polka dot shape on the entire surface of the film. The fine concavo-convex portions are formed at substantially constant intervals, and the formation ratio of the fine concavo-convex portions is 20.
A film for agriculture, characterized in that fine irregularities are formed so as to be up to 70%.
長の平行光線平均透過率が４０％以下、全光線平均透過
率が７５％以上で、非微細凹凸部が５００〜６００ｎｍ
の波長の平行光線平均透過率が６０％以上、全光線平均
透過率が８０％以上である請求項１〜１２いずれか１項
記載の農業用フィルム。13. The fine concavo-convex portion has a parallel light beam average transmittance of 40% or less at a wavelength of 500 to 600 nm, the total light beam average transmissivity is 75% or more, and the non-fine concavo-convex portion is 500 to 600 nm.
The parallel film average transmittance of the wavelength of 60% or more and the total light average transmittance of 80% or more are the agricultural films according to any one of claims 1 to 12.
れている請求項１〜１３いずれか１項記載の農業用フィ
ルム。14. The agricultural film according to claim 1, wherein fine irregularities are provided by a satin finish.
配合されていることを特徴とする請求項１〜１４いずれ
か１項記載の農業用フィルム。15. The agricultural film according to claim 1, wherein the vinyl chloride resin film is blended with a drip-proofing agent.