JP2549136B2 - Thermal head - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION [Industrial Application] The present invention forms a polyimide resin layer on a metal support, and forms a large number of heating resistors on the polyimide resin layer. Related to thermal head.

(Prior Art) In recent years, thermal heads have come to be widely used in various recording devices such as facsimiles and word processor printers by taking advantage of low noise, low maintenance, low running cost and the like. On the other hand, these devices are downsized,
There is a demand for low price and low power consumption, so that a thermal head that is small, inexpensive, and highly efficient is also desired.

As such a thermal head, conventionally, a glaze glass layer is formed on an alumina ceramic substrate having an Al ₂ O ₃ purity of 90% or more, and a large number of heating resistors are connected to the glaze glass layer, respectively. The above-mentioned conductors are often used. Here, the glaze glass layer plays a role as a heat retaining layer that controls heat dissipation and heat storage.

However, the thermal head using this glaze glass layer as a heat retaining layer has the following drawbacks.

Since the glaze glass has a limited thermal response characteristic as a heat insulating layer, the efficiency is low.

Ceramic substrates require many steps in their manufacture, such as treatment for removing alkali metal components from the raw material powder, high temperature firing, and finish polishing to remove the warp of the substrate generated during high temperature firing. Also, since it is necessary to remove the alkali metal component from the raw material powder, the production cost is high.

As a method for solving such a problem, for example, as described in JP-A-52-100245 and JP-A-56-164876, as a heat insulating layer of a thermal head, a heat-resistant material having a small thermal diffusivity is used. It is known that a resin such as a polyimide resin may be used.

In addition, recently, a heat insulating layer made of an aromatic polyimide resin was formed on a thin metal plate, and a large number of heating resistors were formed on this heat insulating layer to temporarily produce a flat thermal head, which was used as a base. A vertical thermal head that can be downsized by bending and adhering so that the heat generating part is located on the top of a metal member has also been proposed. ), 1-125 and 5-1
28).

In this way, for example, polyimide resin has a low thermal diffusivity of 1/3 to 1/6 as compared with glaze glass, so it is possible to greatly improve the thermal efficiency of the thermal head and bend it. Therefore, it is attracting attention as a heat insulating layer for forming a small-sized and inexpensive high-performance thermal head.

However, a thermal head using such a heat-resistant resin as a heat retaining layer has not yet reached the level of practical application, and has a problem that stable printing operation cannot be performed for a long period of time.

This is a high heat resistance that can withstand long-term stable operation under the operating conditions of a thermal head that operates instantaneously at 400 ° C to 500 ° C and regular 250 ° C to 350 ° C, and also adheres by repeated application of heat. This is because no heat-resistant resin that does not cause deterioration in strength and satisfies at the same time excellent adhesiveness to a metal support or a thin film formed on a polyimide resin layer has been found. If the heat-resistant temperature is low, of course, thermal deterioration will occur during use, leading to a decline in performance.
"Peeling" of the heat-resistant resin layer is likely to occur during use, and both reduce the reliability of the thermal head.

For example, a polyamic acid solution called Treney's (trade name) described in the examples of JP-A-56-164876 is applied on an aluminum substrate, and the temperature is 50 ° C. × 60 minutes at 80 ° C.
× 30 minutes, 120 ℃ × 30 minutes, 250 ℃ × 60 minutes, by firing under the conditions of 450 ℃ × 60 minutes to form a polyimide resin layer, the thermal decomposition start temperature of this polyimide resin layer by thermogravimetry is Although it has a considerable heat resistance of about 510 ° C., sufficient adhesive strength was not obtained, and many peeled off already at this stage, and it was not possible to endure the use of the thermal head. Furthermore, Pyre-NL with relatively good adhesion was obtained.
A thermal head is manufactured using an aluminum substrate on which a polyimide resin layer (commercial name, manufactured by DuPont) is formed, and pulsed 10 ⁸ times under the conditions of applied energy of 0.26 mJ / dot, pulse width of 1.7 ms and pulse period of 5.0 ms. Applying voltage,
When the surface of the polyimide resin layer after this was observed with an ultrasonic microscope, it became clear that irregularities were formed on the surface and that the quality was altered during operation. Further, the thermal decomposition temperature of this polyimide resin layer was measured by a thermogravimetric method, and it was as low as about 420 ° C., which was not enough to withstand the operation of the thermistor.

(Problems to be solved by the invention) As described above, in the conventional heat-resistant resin, for example, in the thermal head using the polyimide resin as the heat retaining layer, the thermal efficiency is excellent due to the low thermal diffusivity of the polyimide resin, and bending is possible and the size is reduced. On the other hand, it has the advantage that it is easy, but it does not have long-term stable heat resistance under severe operating temperature conditions, and lacks the adhesive strength between the heat-resistant resin layer and the metal support and the thin film formed on the heat-resistant resin layer. However, there was a problem that reliability could not be obtained for a long time.

The present invention has been made to address such a conventional problem, and further improves the heat resistance of a heat-resistant resin layer provided as a heat-retaining layer for controlling heat dissipation and heat storage on a metal support, and a heat-resistant resin. Improved adhesion between the layer and the thin film formed on the metal support and heat-resistant resin layer, excellent thermal efficiency, bendable and easy to miniaturize,
It is an object of the present invention to provide a thermal head that is inexpensive and can obtain excellent reliability over a long period of time.

[Structure of the Invention] (Means for Solving the Problems) A thermal head according to the present invention includes a metal support, a heat-resistant resin layer formed on the metal support, and a large number of layers formed on the heat-resistant resin layer. In a thermal head comprising a heating resistor and a conductor connected to each heating resistor, the heat resistant resin layer is formed by a ring-opening polyaddition reaction of biphenyltetracarboxylic dianhydride and aromatic diamine. It is characterized by being substantially composed of an aromatic polyimide resin layer having a biphenyl structure in the main chain formed by the dehydration cyclization reaction of the obtained polyamic acid.

Biphenyltetracarboxylic dianhydride, which is one of the starting materials for the polyamic acid that is the precursor of the aromatic polyimide resin in the present invention, is represented by the following general formula.

General formula Examples of the biphenyltetracarboxylic acid dianhydride represented by the above general formula include, for example, 3,3 ′, 4,4′-biphenyltetracarboxylic acid dianhydride and 2,2 ′, 3,3′-biphenyltetracarboxylic acid dianhydride. An anhydrous substance etc. are illustrated.

Examples of the aromatic diamine as the other starting material include p-phenylenediamine, m-phenylenediamine, diaminodiphenyl sulfone, diaminodiphenylmethane, diaminodiphenyl ether and the like. Further, it is also possible to use a substitution product of these aromatic diamines. Examples of this substituent include a lower alkyl group such as a methyl group and an ethyl group. Specific examples of the substituted aromatic diamine include 2,4-dimethyl-p-
Examples thereof include phenylenediamine and 2,4-dimethyl-m-phenylenediamine tetramethyl-p-phenylenediamine.

The aromatic polyimide resin layer having a biphenyl structure in the main chain of the present invention is formed, for example, by the following method.

First, biphenyltetracarboxylic dianhydride and an aromatic diamine are subjected to a ring-opening polyaddition reaction to prepare a polyamic acid, and the polyamic acid is dissolved in an appropriate organic solvent to prepare a varnish having an arbitrary concentration. The use ratio of biphenyltetracarboxylic dianhydride and aromatic diamine is usually equimolar, but the use ratio can be changed within the allowable range of heat resistance and viscosity of varnish. The organic solvent used is N-methyl-2-pyrrolidone, N.N'-dimethylacetamide, N.N'-
A polar organic solvent such as dimethylformamide is suitable. Next, the polyamic acid varnish thus obtained is coated on a metal support, baked and subjected to a dehydration cyclization reaction to form an aromatic polyimide resin layer.

Further, in the heat resistant resin layer of the thermal head of the present invention, it is preferable to perform any of the following items (1) to (3) because the adhesion between the heat resistant resin layer and the metal support can be further improved.

An Si group is introduced into the molecular structure of an aromatic polyimide resin. Aromatic polyimide resin introduced with this Si group, for example, at the time of synthesizing the above-mentioned polyamic acid, a part of the aromatic diamine in an arbitrary molar ratio, desirably in the range of about 0.05 mol% to 10 mol% of the aromatic diamine component. Can be formed by using a polyamic acid obtained by substituting a diamine having a Si group for ring-opening polyaddition reaction.

Examples of the diamine having a Si group include those represented by the general formula (Wherein R is an alkylene group such as an ethylene group or a propylene group; a polymethylene group such as a trimethylene group or a tetramethylene group; a divalent organic group such as a phenylene group is represented by R ′
Represents a monovalent organic group such as an alkyl group such as a methyl group and an ethyl group, and n represents a positive number. ) Is exemplified by bisaminosiloxane. Typical examples of the bisaminosiloxane are as follows.

At least one of a silane compound having an amino bond and a silane compound having a urea bond is contained in the aromatic polyimide resin as a silane coupling agent component. This silane coupling agent is used, for example, in the above polyamic acid varnish in an amount of approximately 0.05% by weight to 10% by weight of solid content.
It can be contained by adding in the range of and using.

Examples of the silane compound having an amino bond added as the silane coupling agent component include γ-aminopropyltriethoxysilane and N-phenyl-γ-aminopropyltrimethoxysilane. , For example, γ-ureidopropyltrimethoxysilane.

Approximately 0.05 μm between the heat-resistant resin layer and the metal support
An active metal layer made of Cr or Ti having a thickness of 1 μm is interposed.

Incidentally, the introduction of a Si group into the molecular structure of the aromatic polyimide resin and the addition of the silane coupling agent into the aromatic polyimide resin, it is necessary to increase the manufacturing process of the thermal head as in Not only that, but also the adhesion between the heat resistant resin layer and the thin film formed on the heat resistant resin layer can be greatly improved.

(Operation) The aromatic polyimide resin formed by using biphenyltetracarboxylic dianhydride and aromatic diamine, which is used as the heat resistant resin layer in the thermal head of the present invention, has a biphenyl structure in the main chain. Due to the high thermal decomposition temperature, stable printing operation can be performed for a long time, the heat shrinkage rate is small, and the difference in the coefficient of thermal expansion from the metal support is also small, so it occurs due to the difference in the thermal contraction and coefficient of thermal expansion It is possible to effectively prevent peeling due to interface stress or the like. Further, by forming this aromatic polyimide resin layer by coating and firing a polyamic acid varnish, it is adhered to the metal support at the same time as imidization, so that it exhibits excellent adhesion to the metal support.

Furthermore, a metal support by containing a silane coupling agent component in the aromatic polyimide resin, or by introducing a Si group in the main chain, and further a thin film formed on the aromatic polyimide resin layer The adhesive strength of is further enhanced and reliability is improved.

(Example) Hereinafter, an example of the present invention will be described with reference to the drawings.

FIG. 1 is a partially exploded perspective view showing a main part of a thermal head according to an embodiment of the present invention.

In the figure, reference numeral 1 indicates a metal substrate made of Fe-Cr alloy or the like and having a thickness of about 0.5 mm. This metal substrate 1
Above, a polyamic acid represented by the following formula (I-1) obtained by ring-opening polyaddition reaction of an equimolar mixture of biphenyltetracarboxylic dianhydride and p-phenylenediamine as an aromatic diamine. Was dissolved in an organic solvent, or when the polyamic acid was synthesized, it was synthesized by replacing the range of 0.05 mol% to 10 mol% of the aromatic diamine component with the bisaminodisiloxane represented by the formula (II) below. A polyamic acid varnish using a polyamic acid having a Si group introduced into the molecular structure represented by the following formula (III-1), or a polyamic acid varnish using the polyamic acid represented by formula (I-1) The γ-ureidopropyltrimethoxysilane represented by the following formula (IV) is added to the solid content in the polyamic acid varnish at 0.
An aromatic compound whose main skeleton is represented by the following formula (I-2) or (III-2) by coating and baking one of the components added and dispersed in the range of 05 wt% to 10 wt% Polyimide resin thickness 5 to 50 μm, preferably
A heat resistant resin layer 2 having a thickness of 10 μm to 30 μm is formed.

On the heat-resistant resin layer 2, a base layer 3 made of SiO ₂ , β-SiAlON or the like and having a thickness of about 0.05 μm to 1 μm is formed. The underlayer 3 serves as a protective layer of an aromatic polyimide resin when the heating resistor 4 layer is formed into a predetermined shape by etching. Further, this on the underlying layer _{3, Ta-SiO 2, Ti-} SiO 2 and the like thickness 0.1
A large number of heating resistors 4 having a predetermined interval of about μm are formed, and a thickness of Al, Al-Si-Cu, etc. is formed so as to form an opening serving as the heating portion 5 on each heating resistor 4. Individual electrode 6 and common electrode 7 of about 0.7 μm to 1 μm
Are formed. Then, a thermal head is configured by forming a Si—O—N based anti-oxidation film / wear resistant film 8 having a thickness of about 3 μm to 5 μm so as to cover at least the heat generating portion 5.

In the formula, l, m, and n represent positive numbers (the same applies hereinafter).

According to this thermal head, a pulse voltage is applied at a predetermined time interval between each individual electrode 6 and the common electrode 7, and the heat generating resistor 4 corresponding to the heat generating portion 5 generates heat to perform print recording. .

This thermal head is manufactured, for example, as follows.

First, a metal substrate made of an Fe alloy having a thickness of about 0.5 mm and containing, for example, 18% by weight of Cr is subjected to leveling treatment, and then cut to a predetermined size and deburred. Then
After degreasing the metal substrate processed to have a predetermined size in an organic solvent, the metal substrate 1 is manufactured by performing a dipping treatment in dilute sulfuric acid at a temperature of about 50 ° C to 70 ° C. The dipping treatment in dilute sulfuric acid is carried out for the purpose of removing the oxide formed on the surface of the metal substrate and micro-roughening the surface to activate it.

Next, the above-mentioned polyamic acid varnish, namely (I
-1) a polyamic acid varnish whose main component is represented by the formula, or a polyamic acid varnish whose main component is represented by the formula (III-1), and further the main component is represented by the formula (I-1). The polyamic acid varnish obtained by adding a silane coupling agent component to N-methyl-2
-Adjusting to a predetermined viscosity using an organic solvent such as pyrrolidone, applying to a predetermined film thickness on the metal substrate 1 by a roller coater or a spion coater, and using a firing furnace in a nitrogen gas atmosphere, for example, 50 ° C x 60 minutes + 80 ° C x
30 minutes + 120 ° C x 30 minutes + 250 ° C x 60 minutes + 450 ° C x 60 minutes to remove the organic solvent and to promote the dehydration cyclization reaction to form an imidized film while forming a heat-resistant resin layer Two
To form. In the case of using a polyamic acid to which no silane coupling agent component is added or a polyamic acid having no Si group introduced into the molecular structure when forming this aromatic polyimide resin layer, the surface of the metal substrate 1 It is desirable that an active metal layer made of Cr, Ti or the like having a thickness of about 0.05 μm to 1 μm is formed by a vapor deposition method or the like, and an aromatic polyimide resin layer is formed thereon.

Next, an underlayer 3 made of SiO ₂ , β-SiAlON and the like and 4 layers of heating resistors made of Ta-SiO ₂ , Ti-SiO ₂ etc. are formed on the heat resistant resin layer 2 by sputtering or other known thin film forming method. Form in order. Furthermore, this heating resistor 4
On the layer, a conductor layer such as Al or Al—Si—Cu, which will be the individual electrode 6 and the common electrode 7, is formed by the same method.
Next, the heating resistor 4 layer and the conductor layer are subjected to patterning processing to form a large number of heating resistors 4 having a predetermined interval, the individual electrodes 6 and the common electrode 7. In this patterning process, first, a masking film is formed on the conductor layer so that the heating resistor 4 having a predetermined shape is formed, and unnecessary portions are removed by wet etching or chemical dry etching, and a large number of masks having predetermined intervals are formed. A conductor layer having the same shape as that of the heating resistor 4 is formed. Next, a masking film is formed on the conductor layer except for the portion to be the heat generating portion 5,
By a similar method, only the conductor layer is removed to form the heating portion 5, and at the same time, the individual electrodes 6 and the common electrode 7 are formed.
After that, an anti-oxidation film / abrasion resistant film 8 made of Si—O—N is formed so as to cover the heat generating portion 5 by, for example, a sputtering method.

Next, the results of evaluation of characteristics such as adhesion and heat resistance of the aromatic polyimide resin having a biphenyl structure in the main chain according to the present invention in the manufacturing process of this thermal head will be described.

First, using a varnish containing a polyamic acid as a main component obtained by a ring-opening polyaddition reaction of biphenyltetracarboxylic dianhydride and an aromatic diamine of this example, a Cr vapor deposition film Fe-18 formed Repeat 10 cycles by forming an aromatic polyimide resin layer having a biphenyl structure in the main chain on a wt% Cr alloy substrate and setting it as one cycle at room temperature x 30 minutes + 450 ° C x 30 minutes in nitrogen gas. A thermal stress test was conducted by using the above, and the presence or absence of peeling of the aromatic polyimide resin layer at that time was examined. Further, the thermal decomposition initiation temperature, the heat shrinkage ratio, and the thermal expansion coefficient were also measured by thermogravimetry. The results are shown in the table below. The heat shrinkage rate is measured under heating conditions of 400 ° C. × 30 minutes, and the thermal expansion coefficient is a value measured under conditions of a temperature increase rate of 5 ° C./minute using a fine linear dilatometer.

Further, for comparison with the present invention, p-phenylenediamine used in this example was used to prepare pyromellitic dianhydride (Comparative Example 1) and benzophenonetetracarboxylic dianhydride as tetracarboxylic acid components, respectively. (Comparative Example 2) was used to synthesize polyamic acid,
An aromatic polyimide resin layer was formed under the same conditions as in the example. Then, a polyimide resin layer was formed. The characteristics of these were also evaluated in the same manner. Furthermore, Comparative Example 3
Is the one using Treney (trade name) described in the example of JP-A-56-164876, and Comparative Example 4
Is an aromatic polyimide resin layer called Pyre-NL (trade name, manufactured by DuPont), and these were also evaluated in the same manner. The results of these evaluations are also shown in the following table.

As is clear from the above table, peeling of the polyimide resin layer was observed except for the aromatic polyimide resin having a biphenyl structure in the main chain of this example. It is considered that this was caused by a large heat shrinkage ratio and a difference in thermal expansion coefficient between the metal substrate and the polyimide resin layer. Also, the aromatic polyimide resin having a biphenyl structure has the highest thermal decomposition initiation temperature determined by thermogravimetric measurement, and it is found that it is suitable as a heat-resistant resin layer for a thermal head.

In the same manner as in the above example, the aromatic polyimide resin formed using 2,2 ', 3,3'-biphenyltetracarboxylic dianhydride as a tetracarboxylic acid component has a thermal decomposition starting temperature of 20. Although it decreased by about 0 ° C., no difference was observed in other characteristics, and it was also effective as a heat-resistant resin layer of the thermal head. In addition, similar to the above-mentioned example, regarding the one using the aromatic diamine having a substituent such as a methyl group or an ethyl group, no difference in characteristics was observed with the one using the unsubstituted aromatic diamine. ,
Similarly, it was suitable as a heat resistant resin layer for a thermal head.

Next, as a silane coupling agent component in the aromatic polyimide resin represented by the formula (III-2) in which a Si group is introduced into the molecular structure and the aromatic polyimide resin represented by the formula (I-2) ( The adhesion strength and heat resistance of the aromatic polyimide resin containing γ-ureidopropyltrimethoxysilane represented by the formula IV) were evaluated.

FIG. 2 is a diagram showing the relationship between the substitution ratio of the above-mentioned bisaminodisiloxane in the aromatic diamine component, the adhesion strength to the metal substrate (without Cr vapor deposition film) and the SiO ₂ layer, and the thermal decomposition start temperature. Is. Similarly, FIG. 3 shows the addition amount of the above-mentioned silane coupling agent (% by weight relative to the solid content in the polyamic acid varnish) and the metal substrate (Cr
FIG. 6 is a diagram showing the relationship between the adhesion strength and the thermal decomposition start temperature for each of the SiO ₂ layer (without vapor deposition film). The adhesive strength between the aromatic polyimide resin layer and the metal substrate was measured according to JIS standard 06481, 5, 7 "Peeling strength". On the other hand, the adhesion strength between the aromatic polyimide resin layer and the SiO ₂ layer was measured as follows. Al1μm, Cr0.1μ on the SiO ₂ layer formed on the aromatic polyimide resin layer
m, Cu 3 μm, Au 1 μm are continuously formed by mask sputtering, and then SiO _{2 in a} portion not covered with these layers is formed.
Was removed by chemical dry etching. After this,
Solder a 0.8mm diameter Sn-plated Cu wire on Cu,
The measurement was carried out by a tensile test.

In any case, it can be seen that the adhesion strength is greatly improved by the introduction of the Si component.

The heating resistor of the thermal head is instantaneously 400 ℃ -500 ℃,
Although it operates at a temperature of 250 ℃ to 350 ℃ continuously, the substitution ratio by bisaminosiloxane is about 0.05mo from the result of Fig. 2.
It is clear that a range of l% to 10 mol% is desirable. This is because the substitution ratio by bisaminosiloxane is about 0.05.
If it is less than mol%, the effect of improving the adhesive strength is not recognized, and
This is because if it exceeds 0 mol%, not only the effect of improving the adhesive strength is saturated, but also the heat resistance is significantly deteriorated. From the results shown in FIG. 3, it is understood that the addition amount of the silane coupling agent is preferably in the range of approximately 0.05% by weight to 10% by weight. This is because when the amount of the silane coupling agent added is less than approximately 0.05% by weight, the effect of improving the adhesive strength is not observed, and when it exceeds approximately 10% by weight, the effect of improving the adhesive strength is saturated.

As the silane coupling agent component, in addition to the aforementioned γ-ureidopropyltrimethoxysilane, the following (V)
Similar effects were obtained when γ-aminopropyltrimethoxysilane represented by the formula or N-phenyl-γ-aminopropyltrimethoxysilane represented by the formula (VI) was used.

_{H 2 N-C 3 H 6} -Si (OC 2 H 5) 3 ...... (V) Thus, the Si in the molecular structure of the aromatic polyimide resin
By introducing a group or containing a silane coupling agent component, the adhesive force with the inorganic insulating material serving as the metal substrate or the underlayer is further improved. Therefore, a thermal head having excellent reliability can be obtained. In particular, by introducing a Si group in a specific amount in the molecular structure of the aromatic polyimide resin, the adhesive strength is improved substantially without impairing the heat resistance, and it is suitable as a heat-resistant resin layer for a thermal head. Become.

 Next, the efficiency of the thermal head was evaluated.

_{First, SiO 2 -BaO-CaO-Al} 2 O 3 -B 2 O 3 -Z as a conventional example
A thermal head was formed by forming an underlayer, a heating resistor, an electrode and a protective film on a material obtained by forming a glaze glass layer of nO having a thickness of about 70 μm on an alumina ceramic substrate in the same manner as in this example. And print with the thermal head using this glaze glass,
Based on the input power at which a certain color density was obtained,
In this example, an aromatic polyimide resin layer represented by the above formula (I-2), an aromatic polyimide resin layer represented by the above formula (III-2), or an aromatic polyimide resin layer represented by the above formula (I-2). The applied power for obtaining the same color density was obtained as a ratio by the thermal head using each of the aromatic polyimide resins containing the silane coupling agent component. The results are graphed as a relationship between the input power ratio (ratio when the input power by the thermal head using glaze glass is 1) and the film thickness of the polyimide resin layer, and are shown in FIG.

As is clear from FIG. 4, when an aromatic polyimide resin having a biphenyl structure in the main chain according to the present invention is used as the heat-resistant resin layer, in order to obtain a color density equivalent to that when glaze glass is used, It can be seen that the low input power is sufficient, that is, the thermal efficiency is excellent. From the results shown in FIG. 4, it is also understood that the thickness of the aromatic polyimide resin layer is preferably in the range of approximately 5 μm to 50 μm. This is because if the thickness of the aromatic polyimide resin layer is less than about 5 μm, a sufficient efficiency improving effect cannot be expected, and if it exceeds about 50 μm, this effect is saturated.

Further, in FIG. 5, in order to obtain the basic knowledge resulting from the improvement in efficiency, the same 3 as that used for the above efficiency measurement was obtained.
The thermal diffusivity in the thickness direction measured by the laser flash method is shown for various types of aromatic polyimide resins and glaze glass. The aromatic polyimide resin having a biphenyl structure in the main chain according to the present invention has a low thermal diffusivity of about 1/3 to 1/6 that of conventional glaze glass, which makes it possible to construct a highly efficient thermal head. It is clear that In addition, when a Si group is introduced into the molecular structure, the thermal diffusivity is slightly reduced, and further improvement in efficiency can be expected.

Further, using the thermal head in this example, the applied voltage was applied 10 ⁸ times under the conditions of applied energy of 0.26 mJ / dot, pulse width of 1.7 ms and pulse period of 5.0 ms. When the surface was observed with an ultrasonic microscope, no alteration was observed.

In this example, the use ratios of biphenyltetracarboxylic dianhydride and aromatic diamine were equimolar, but the present invention is not limited to this, and the use of heat resistance and viscosity during synthesis is used. Within the allowable range, the mixing ratio is ± 7 mol
You may change and use it in the range of about%.

Further, in the present invention, since the metal member is used as the support, this metal support can be used as the common electrode to further reduce the production cost. Further, the anti-oxidation film / anti-wear film does not necessarily have to be provided on the entire surface, and if it is formed at least on the heat generating portion, its function is sufficiently exhibited.

[Effects of the Invention] As described above, in the thermal head of the present invention, the aromatic polyimide resin synthesized by the biphenyltetracarboxylic dianhydride and the aromatic diamine, which is used as the heat-resistant resin layer, has a main chain Has a high thermal decomposition initiation temperature and has heat resistance capable of withstanding severe operating temperature conditions, has a small difference in coefficient of linear expansion from the metal support, and has excellent adhesive strength. Therefore, the thermal head of the present invention using such an aromatic polyimide-based resin as the heat-resistant resin layer has excellent reliability, fully utilizes the characteristics of the polyimide resin, has excellent thermal efficiency, is inexpensive, and can be miniaturized. It is a thing.

[Brief description of drawings]

FIG. 1 is a partially exploded perspective view showing a main part of a thermal head according to an embodiment of the present invention, and FIG. 2 is a substitution ratio of an aromatic diamine component with diaminodisiloxane in a process of forming an aromatic polyimide resin according to the present invention. And a graph showing the relationship between the adhesion strength between the aromatic polyimide resin layer, the metal substrate and the underlying layer formed on the aromatic polyimide resin layer, and the thermal decomposition start temperature of the aromatic polyimide resin. The figure is the addition amount of the silane coupling agent in the formation process of the aromatic polyimide resin according to the present invention, the adhesion strength between the aromatic polyimide resin layer and the metal substrate and the underlying layer formed on the aromatic polyimide resin layer, And a graph showing the relationship with the thermal decomposition start temperature of this aromatic polyimide resin, and FIG. 4 is a thermal graph using a conventional glaze glass as a heat retaining layer. And head is a graph showing a graph showing a comparison of the efficiency of the thermal head, Fig. 5 a thermal diffusivity of the aromatic polyimide resin and the glaze glass according to the present invention in an embodiment of the present invention. 1 ... Metal substrate 2 ... Heat-resistant resin layer 3 ... Underlayer 4 ... Heating resistor 5 ... Heating part 6 ... Individual electrode 7 ... Common electrode 8 ... Antioxidant and abrasion resistant film

Front page continuation (72) Inventor Yoshiaki Ouchi 72 Horikawa-cho, Saiwai-ku, Kawasaki-shi, Kanagawa Toshiba Horikawa-cho factory (72) Inventor Tadayoshi Kinoshita 72 Horikawa-cho, Sai-ku, Kawasaki-shi, Kanagawa Toshiba Horikawa-cho, Ltd. (72) Inventor Teru Okunoyama 9-2 Chidori-cho, Kawasaki-ku, Kawasaki-shi, Kanagawa Inside the Chidori-cho Plant, Toshiba Chemical Co., Ltd. (56) Reference JP-A-60-32827 (JP, A) JP-A-59- 182850 (JP, A) JP-A-61-238809 (JP, A)

Claims (3)

(57) [Claims] 1. A metal support, a heat-resistant resin layer formed on the metal support, a large number of heat-generating resistors formed on the heat-resistant resin layer, and a conductive material connected to each of the heat-generating resistors. In a thermal head comprising a body, the heat-resistant resin layer is formed by a dehydration cyclization reaction of a polyamic acid obtained by a ring-opening polyaddition reaction of biphenyltetracarboxylic dianhydride and an aromatic diamine. A thermal head, which is essentially composed of an aromatic polyimide resin layer having a biphenyl structure in the chain. 2. The aromatic polyimide resin having a biphenyl structure in the main chain has a molecular structure in which a part of the aromatic diamine is replaced with a diamine having a Si group during the synthesis of the polyamic acid. The thermal head according to claim 1, wherein Si groups are introduced into the thermal head. 3. The aromatic polyimide resin having a biphenyl structure in the main chain contains at least one of a silane compound having an amino bond and a silane compound having a urea bond as a silane coupling agent component. The thermal head according to claim 1, which is characterized in that.