JP2528937B2 - 低反射性被覆物品 - Google Patents
低反射性被覆物品Info
- Publication number
- JP2528937B2 JP2528937B2 JP63116789A JP11678988A JP2528937B2 JP 2528937 B2 JP2528937 B2 JP 2528937B2 JP 63116789 A JP63116789 A JP 63116789A JP 11678988 A JP11678988 A JP 11678988A JP 2528937 B2 JP2528937 B2 JP 2528937B2
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- low
- visible light
- film
- metal alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 産業上の利用分野 本発明は、透明被覆の分野に関し、特に、建築用のガ
ラス製品に使用するための多層着色透明被覆に関する。
ラス製品に使用するための多層着色透明被覆に関する。
従来の技術 金属及び(又は)金属酸化物膜を有する建築用ガラス
製品は、加熱及び冷却のために必要なエネルギーが次第
に高価になってきているので、重要性を増してきてい
る。被覆された建築用ガラス製品は、一般に二つの範
疇、太陽エネルギー調節製品と可視光高透過性で、かつ
低放射性被覆製品とに分類される。太陽エネルギー調節
ガラス製品は、一般に、屡々着色されているガラス基体
に、高反射性で可視光透過率の低い着色フィルムを被覆
したものであり、そのフィルムは、窓を通って建物の内
部へ入る太陽エネルギー(赤外線)の透過率を減じ、そ
れによって空調費を少なくする。これらの製品は暖かい
気候の処で最も有効であり、最も屡々商業的に製造され
ているのが見られる。暖房費が一層大きな関心事になる
地方では、特に居住用建造物中では、建物内部に熱を保
持するため赤外線を反射しながら、内部への可視光の透
過率を大きくするため、可視光高透過性で熱低放射性の
被覆が望ましい。可視光高透過性熱低放射性被覆は、典
型的には多層フィルムであり、この場合、銀、金、又は
銅の如き赤外線反射性金属が、ビスマス、インジウム及
び(又は)錫の酸化物の如き非反射性金属酸化物層の間
に挟まれている。一方、太陽エネルギー調節フィルム
は、コバルト、鉄、クロム、ニッケル、銅等の如き金属
又はそれら金属の酸化物の一種類以上の可視光の高反射
性単一層フィルムであるのが典型的である。
製品は、加熱及び冷却のために必要なエネルギーが次第
に高価になってきているので、重要性を増してきてい
る。被覆された建築用ガラス製品は、一般に二つの範
疇、太陽エネルギー調節製品と可視光高透過性で、かつ
低放射性被覆製品とに分類される。太陽エネルギー調節
ガラス製品は、一般に、屡々着色されているガラス基体
に、高反射性で可視光透過率の低い着色フィルムを被覆
したものであり、そのフィルムは、窓を通って建物の内
部へ入る太陽エネルギー(赤外線)の透過率を減じ、そ
れによって空調費を少なくする。これらの製品は暖かい
気候の処で最も有効であり、最も屡々商業的に製造され
ているのが見られる。暖房費が一層大きな関心事になる
地方では、特に居住用建造物中では、建物内部に熱を保
持するため赤外線を反射しながら、内部への可視光の透
過率を大きくするため、可視光高透過性で熱低放射性の
被覆が望ましい。可視光高透過性熱低放射性被覆は、典
型的には多層フィルムであり、この場合、銀、金、又は
銅の如き赤外線反射性金属が、ビスマス、インジウム及
び(又は)錫の酸化物の如き非反射性金属酸化物層の間
に挟まれている。一方、太陽エネルギー調節フィルム
は、コバルト、鉄、クロム、ニッケル、銅等の如き金属
又はそれら金属の酸化物の一種類以上の可視光の高反射
性単一層フィルムであるのが典型的である。
太陽エネルギー調節のための金属フィルムを製造する
ための化学的湿式法は、米国特許第3,846,152号;4,091,
172号;第3,723,158号及び第3,457,138号により良く知
られている。太陽エネルギー調節のための金属酸化物フ
ィルムを製造するための熱分解法は、米国特許第3,660,
061号;第3,658,568号;第3,978,272号及び第4,100,330
号により良く知られている。
ための化学的湿式法は、米国特許第3,846,152号;4,091,
172号;第3,723,158号及び第3,457,138号により良く知
られている。太陽エネルギー調節のための金属酸化物フ
ィルムを製造するための熱分解法は、米国特許第3,660,
061号;第3,658,568号;第3,978,272号及び第4,100,330
号により良く知られている。
可視光高透過性熱低放射性多層被覆のスパッタリング
による製造方法は、米国特許第4,462,884号及び第4,50
8,789号に記載されている。太陽エネルギー調節のため
のフィルムを製造するためのスパッタリング法は、米国
特許第4,512,863号及び第4,594,137号に記載されてい
る。
による製造方法は、米国特許第4,462,884号及び第4,50
8,789号に記載されている。太陽エネルギー調節のため
のフィルムを製造するためのスパッタリング法は、米国
特許第4,512,863号及び第4,594,137号に記載されてい
る。
グラブ(Grubb)その他による米国特許第4,022,947号
には、入射太陽光の大部分を反射しながら、可視光の希
望の部分を透過することができる透明板が記載されてお
り、又透明金属フィルムを得るために鉄、ニッケル及び
クロム合金をスパッターし、そしてそれらを又は同様な
合金を酸素の存在下で反応的にスパッターして酸化物フ
ィルムを形成させることによりその板を製造する方法が
記載されている。一つの好ましい態様として、金属フィ
ルムが基体と金属酸化物フィルムとの間に入れてある。
他の好ましい態様として、金属酸化物フィルムが基体と
金属フィルムとの間に入っている。
には、入射太陽光の大部分を反射しながら、可視光の希
望の部分を透過することができる透明板が記載されてお
り、又透明金属フィルムを得るために鉄、ニッケル及び
クロム合金をスパッターし、そしてそれらを又は同様な
合金を酸素の存在下で反応的にスパッターして酸化物フ
ィルムを形成させることによりその板を製造する方法が
記載されている。一つの好ましい態様として、金属フィ
ルムが基体と金属酸化物フィルムとの間に入れてある。
他の好ましい態様として、金属酸化物フィルムが基体と
金属フィルムとの間に入っている。
特開昭61−151045号明細書には、吸収及び干渉効果の
両方により色を示す金属化合物の層と組み合わさって高
度に反射性の金属の層を有する強く着色した被覆が記載
されている。
両方により色を示す金属化合物の層と組み合わさって高
度に反射性の金属の層を有する強く着色した被覆が記載
されている。
解決課題および解決手段 本発明は、陰極スパッタリング、好ましくはマグネト
ロンスパッタリングによりガラスの如き基体上に付着さ
せた可視光低反射性、赤外線低透過性ブロンズ色の太陽
エネルギー調節フィルムに関する。そのフィルムは、可
視光低反射性着色金属合金酸化物の層と灰色(neutra
l)金属合金の層とからなる。ここで、「仮反射性」の
語は、典型的には20〜25%以下の反射性を意味する。金
属合金酸化物層は、色及び可視光低反射性を与え、金属
合金層は灰色を与え、かつ赤外線低透過性を与える。
ロンスパッタリングによりガラスの如き基体上に付着さ
せた可視光低反射性、赤外線低透過性ブロンズ色の太陽
エネルギー調節フィルムに関する。そのフィルムは、可
視光低反射性着色金属合金酸化物の層と灰色(neutra
l)金属合金の層とからなる。ここで、「仮反射性」の
語は、典型的には20〜25%以下の反射性を意味する。金
属合金酸化物層は、色及び可視光低反射性を与え、金属
合金層は灰色を与え、かつ赤外線低透過性を与える。
透明基体、好ましくはガラスを陰極スパッタリング、
好ましくはマグネトロンスパッタリングにより被覆し、
従来の太陽エネルギー調節製品では達成されなかったよ
り効率の良い太陽エネルギー調節製品を与える。被覆
は、ステンレス鋼酸化物の如き着色金属合金酸化物の少
なくとも一つの層と、灰色を与え、かつ赤外線の低透過
性を与えるニッケル及びクロムを含有する金属合金(以
下ニッケル合金と称することもある)の少なくとも一つ
の層とからなる。好ましいニッケル合金としてはインコ
ネル(Inconel)が挙げられる。
好ましくはマグネトロンスパッタリングにより被覆し、
従来の太陽エネルギー調節製品では達成されなかったよ
り効率の良い太陽エネルギー調節製品を与える。被覆
は、ステンレス鋼酸化物の如き着色金属合金酸化物の少
なくとも一つの層と、灰色を与え、かつ赤外線の低透過
性を与えるニッケル及びクロムを含有する金属合金(以
下ニッケル合金と称することもある)の少なくとも一つ
の層とからなる。好ましいニッケル合金としてはインコ
ネル(Inconel)が挙げられる。
本発明の好ましい具体例として、ガラス表面をまず、
酸化性反応性雰囲気中でステンレス鋼陰極ターゲットを
スパッターすることにより、ステンレス鋼酸化物の層で
被覆する。ステンレス鋼酸化物で被覆された表面を次
に、アルゴンの如き非反応性雰囲気中でニッケル合金タ
ーゲットをスパッターすることにより、灰色金属合金の
層で更に被覆する。それら被覆層の相対的厚さは、種々
の視覚的効果を生ずるように変えることができる。特
に、灰色金属層の厚さは、ガラス側からの可視光の反射
又は色を実質的に変えることなく、可視光の透過性を増
加したり或は低下したりするように変えることができ
る。
酸化性反応性雰囲気中でステンレス鋼陰極ターゲットを
スパッターすることにより、ステンレス鋼酸化物の層で
被覆する。ステンレス鋼酸化物で被覆された表面を次
に、アルゴンの如き非反応性雰囲気中でニッケル合金タ
ーゲットをスパッターすることにより、灰色金属合金の
層で更に被覆する。それら被覆層の相対的厚さは、種々
の視覚的効果を生ずるように変えることができる。特
に、灰色金属層の厚さは、ガラス側からの可視光の反射
又は色を実質的に変えることなく、可視光の透過性を増
加したり或は低下したりするように変えることができ
る。
本願発明に係る低反射性被覆を設けたガラス製品は二
重絶縁ガラスユニットとして用いるのが好ましく、その
場合は被覆面が二枚のガラスに挟まれるようにするのが
よい。
重絶縁ガラスユニットとして用いるのが好ましく、その
場合は被覆面が二枚のガラスに挟まれるようにするのが
よい。
実施例 最も好ましい態様として、ステンレス鋼酸化物とイン
コネル金属合金層を一緒にしてブロンズ色の被覆を生成
させる。本発明は次の特別の実施例についての記載から
一層よく理解することができるであろう。
コネル金属合金層を一緒にしてブロンズ色の被覆を生成
させる。本発明は次の特別の実施例についての記載から
一層よく理解することができるであろう。
実施例1 ステンレス鋼酸化物とニッケル金属合金の多層被覆を
次の条件でガラス基体上に、連続した多段陰極の下を一
度通すことにより付着させた。正常なガラス基体は、真
空室中、3ミリトールの圧力の50%酸素及び50%アルガ
ンからなる雰囲気中に維持された。約2.74×0.4m(106
×15in)の大きさのターゲット表面積をもつステンレス
鋼陰極に98kWの電力を加えた。2.36m(93in)/分の線
速度で、ステンレス鋼酸化物被覆を、約6mm(1/4in)厚
の透明フロートガラス基体に対し可視光透過率を90%か
ら59%へ低下させる厚さ(おおよそ120〜150Åの厚さに
相当)に付着させた。この例で用いられたステンレス鋼
組成物は、68%の鉄、17%のクロム、12%のニッケル及
び2.25%のモリブデンを含む316合金であった。次にニ
ッケル合金陰極を3ミリトールの不活性アルゴン雰囲気
中でスパッターした。同じ線速度及び7kWの電力を用い
て、ニッケル合金被覆をステンレス鋼酸化物被覆の上に
付着させ、更に可視光透過率を16.8%(おおよそ50Åの
厚さに相当)へ低下させた。この例で用いられたニッケ
ル合金は、62.6%のニッケル、20%のクロム、6.85%の
鉄、3.95%のニオブと、タンタル、炭素、マンガン、
鉄、硫黄、珪素、銅、アルミニウム及びチタンを微量
(1%より少ない)含むインコネル625であった。被覆
物品を外囲条件に曝すと、ニッケル合金被覆表面は酸化
して、わずかに可視光透過率が増大した。被覆した物品
は、ガラス側から見て可視光低反射性ブロンズ色の外観
をもっていた。被覆した物品の光(可視光)透過率は約
20%で、可視光反射率はガラス側から約14%であった。
反射色はブロンズで、色度座標はx=0.3401、y=0.35
18であった。
次の条件でガラス基体上に、連続した多段陰極の下を一
度通すことにより付着させた。正常なガラス基体は、真
空室中、3ミリトールの圧力の50%酸素及び50%アルガ
ンからなる雰囲気中に維持された。約2.74×0.4m(106
×15in)の大きさのターゲット表面積をもつステンレス
鋼陰極に98kWの電力を加えた。2.36m(93in)/分の線
速度で、ステンレス鋼酸化物被覆を、約6mm(1/4in)厚
の透明フロートガラス基体に対し可視光透過率を90%か
ら59%へ低下させる厚さ(おおよそ120〜150Åの厚さに
相当)に付着させた。この例で用いられたステンレス鋼
組成物は、68%の鉄、17%のクロム、12%のニッケル及
び2.25%のモリブデンを含む316合金であった。次にニ
ッケル合金陰極を3ミリトールの不活性アルゴン雰囲気
中でスパッターした。同じ線速度及び7kWの電力を用い
て、ニッケル合金被覆をステンレス鋼酸化物被覆の上に
付着させ、更に可視光透過率を16.8%(おおよそ50Åの
厚さに相当)へ低下させた。この例で用いられたニッケ
ル合金は、62.6%のニッケル、20%のクロム、6.85%の
鉄、3.95%のニオブと、タンタル、炭素、マンガン、
鉄、硫黄、珪素、銅、アルミニウム及びチタンを微量
(1%より少ない)含むインコネル625であった。被覆
物品を外囲条件に曝すと、ニッケル合金被覆表面は酸化
して、わずかに可視光透過率が増大した。被覆した物品
は、ガラス側から見て可視光低反射性ブロンズ色の外観
をもっていた。被覆した物品の光(可視光)透過率は約
20%で、可視光反射率はガラス側から約14%であった。
反射色はブロンズで、色度座標はx=0.3401、y=0.35
18であった。
上記実施例は本発明を例示するためにのみ与えられて
いる。クロム合金の如き他の灰色低可視光反射性金属と
共に、種々の他の着色金属合金酸化物を用いてもよい。
どんな適当な透明保護基体が用いられてもよい。本発明
の範囲は、特許請求の範囲によって定められるものであ
る。
いる。クロム合金の如き他の灰色低可視光反射性金属と
共に、種々の他の着色金属合金酸化物を用いてもよい。
どんな適当な透明保護基体が用いられてもよい。本発明
の範囲は、特許請求の範囲によって定められるものであ
る。
Claims (3)
- 【請求項1】a.透明なガラス基体、 b.前記基体の表面上に付着された色を与える可視光低反
射性ステンレス鋼酸化物の透明なフィルム、及び c.前記酸化物フィルム上に付着されたニッケル及びクロ
ムを含有する金属合金からなる灰色で、赤外線低透過性
の透明金属合金フィルム、 からなる可視光低反射性太陽エネルギー調節用でかつブ
ロンズ色を呈した被覆物品。 - 【請求項2】前記酸化物の透明フィルム及び前記赤外線
低透過性合金フィルムがスパッターされたフィルムであ
る請求項(1)に記載の物品。 - 【請求項3】a.ガラス基体の表面上に色を与えるステン
レス鋼酸化物の第一透明被覆をスパッターし、そして b.前記酸化物フィルムの上にニッケル及びクロムを含有
する金属合金からなる灰色で、赤外線低透過性の透明金
属合金フィルムをスパッターする、諸工程からなる可視
光低反射性太陽エネルギー調節用でかつブロンズ色を呈
した被覆物品の製造方法。