JP2022529410A - 平面状材料及びその製造方法 - Google Patents
平面状材料及びその製造方法 Download PDFInfo
- Publication number
- JP2022529410A JP2022529410A JP2021559130A JP2021559130A JP2022529410A JP 2022529410 A JP2022529410 A JP 2022529410A JP 2021559130 A JP2021559130 A JP 2021559130A JP 2021559130 A JP2021559130 A JP 2021559130A JP 2022529410 A JP2022529410 A JP 2022529410A
- Authority
- JP
- Japan
- Prior art keywords
- fibers
- binder
- planar material
- fiber
- planar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
-繊維を供給し、
-結合剤を、好ましくは液体の形で供給し、
-繊維に結合剤を適用し、
-繊維ケーキを形成し、
結合剤を硬化させながら繊維ケーキをプレス機でプレスして、平面状材料を形成する、
ステップを有する。
結果を以下の表1に示す実験では、リグノセルロース繊維、この場合は針葉樹繊維を使用した。繊維は、リファイナー(精製機)での解繊を通して、蒸した木材チップから製造された。代わりになるものとして、他のリグノセルロース繊維又はそのような繊維の混合物を使用することができる。針葉樹繊維は、接着する前に、水分120%で使用され、プレスする前に、それらはその上に配置された結合剤と共に8%の残留水分まで乾燥され、つまり、1トンの繊維には80kgの水が含まれる。
例示的な実施形態2における平面状材料の繊維割合については、50:50の異なる繊維の混合物、この場合、例えば、木質繊維と炭素繊維、あるいは例えば再生紙繊維とガラス繊維、あるいは鉱物繊維とセルロース繊維が、使用される。ここで、天然繊維(木材、再生紙、セルロース繊維)は、好ましくは接着する前に乾燥され、繊維は、接着及び接着剤の随意の乾燥の前又は後に混合されることができる。どちらのバリエーションも、接着された繊維の均一な混合物を生成することを可能にし、それを散乱させて繊維ケーキを形成することができる。他の点では、例示的な実施形態2は、結合剤の使用及びパラフィンの使用に関して、例示的な実施形態1と同一である。
例示的な実施形態3は、50部のポリエチレン繊維、及び20部の炭素繊維、及び10部の骨材,例えばガラス,鉱物又はセラミック粒子が、繊維割合を形成し、115重量%の接着剤で、この場合例えばMF樹脂で接着される、繊維と結合剤の混合物に関する。繊維/骨材/結合剤の混合物は、他の点では、例示的な実施形態1のように処理される。
繊維と結合剤で形成されたボードは、床の敷物(フロアカバー)の製造に使用でき、又、装飾的な表面で、特に合成樹脂を含浸させた紙又は塗装のいずれかでコーティングできるものが製造されるべきである。密度が約550kg/m3の40重量%の繊維と55重量%の結合剤この場合メラミンの割合が60%を超えるMF樹脂が、使用される。さらに、5重量%の他の材料、この場合は1.5重量%のパラフィンと3.5重量%の灰色染料が使用される。染料は、平面状材料に均一な色を与えるために使用される。
-繊維を供給し、
-結合剤を、好ましくは液体の形で供給し、
-繊維に結合剤を適用し、
-繊維ケーキを形成し、
結合剤を硬化させながら繊維ケーキをプレス機でプレスして、平面状材料を形成する、
ステップを有する。
結果を以下の表1に示す実験では、リグノセルロース繊維、この場合は針葉樹繊維を使用した。繊維は、リファイナー(精製機)での解繊を通して、蒸した木材チップから製造された。代わりになるものとして、他のリグノセルロース繊維又はそのような繊維の混合物を使用することができる。針葉樹繊維は、接着する前に、水分120%で使用され、プレスする前に、それらはその上に配置された結合剤と共に8%の残留水分まで乾燥され、つまり、1トンの繊維には80kgの水が含まれる。
例示的な実施形態2における平面状材料の繊維割合については、50:50の異なる繊維の混合物、この場合、例えば、木質繊維と炭素繊維、あるいは例えば再生紙繊維とガラス繊維、あるいは鉱物繊維とセルロース繊維が、使用される。ここで、天然繊維(木材、再生紙、セルロース繊維)は、好ましくは接着する前に乾燥され、繊維は、接着及び接着剤の随意の乾燥の前又は後に混合されることができる。どちらのバリエーションも、接着された繊維の均一な混合物を生成することを可能にし、それを散乱させて繊維ケーキを形成することができる。他の点では、例示的な実施形態2は、結合剤の使用及びパラフィンの使用に関して、例示的な実施形態1と同一である。
例示的な実施形態3は、50部のポリエチレン繊維、及び20部の炭素繊維、及び10部の骨材,例えばガラス,鉱物又はセラミック粒子が、繊維割合を形成し、115重量%の接着剤で、この場合例えばMF樹脂で接着される、繊維と結合剤の混合物に関する。繊維/骨材/結合剤の混合物は、他の点では、例示的な実施形態1のように処理される。
繊維と結合剤で形成されたボードは、床の敷物(フロアカバー)の製造に使用でき、又、装飾的な表面で、特に合成樹脂を含浸させた紙又は塗装のいずれかでコーティングできるものが製造されるべきである。密度が約550kg/m3の40重量%の繊維と55重量%の結合剤この場合メラミンの割合が60%を超えるMF樹脂が、使用される。さらに、5重量%の他の材料、この場合は1.5重量%のパラフィンと3.5重量%の灰色染料が使用される。染料は、平面状材料に均一な色を与えるために使用される。
Claims (20)
- リグノセルロース繊維(5)及び結合剤を含む、平面状材料を製造する方法であって、
前記結合剤ならびに任意に使用される可塑化添加剤の割合が平面状材料(1)の50%を超え、前記可塑化添加剤が、前記結合剤の主成分として使用されておらず、
リグノセルロース繊維(5)を供給し、以下の
前記結合剤を、好ましくは液体形態で供給し、ここで、前記結合剤は、メラミン樹脂、ホルムアルデヒド樹脂、フェノール樹脂、メチレンジフェニルイソシアネート(MDI)又eMDIとして乳化された形態のもの、高分子ジフェニルメタンジイソシアネート(PDMI)、ポリウレタン、又は前述の結合剤の混合物を有し、液体可塑化添加剤が任意に使用され、
前記結合剤と任意に使用される前記可塑化添加剤を前記繊維(5)に適用し、
前記結合剤及び任意に前記可塑化添加剤を備えた繊維から繊維ケーキを形成し、
前記結合剤を硬化させながら前記繊維ケーキをプレス機でプレスして平面状材料(1)を形成する、
ステップを有する、ことを特徴とする方法。 - 前記平面状材料の前記可塑化添加剤として、アクリレート、スチレンアクリレート、ポリウレタン、ポリ酢酸ビニル、エチレン酢酸ビニル、モノ又はジエチレングリコールが添加される、
ことを特徴とする請求項1に記載の方法。 - 前記可塑化添加剤は、前記結合剤の固形物に対して、最大1:1、好ましくは0.7:1、特に0.2:1、有利には少なくとも0.01:1の比率で固形物として使用される、
ことを特徴とする請求項2に記載の方法。 - 前記可塑化添加剤は、前記結合剤の前又は後に前記繊維に適用されるか、又は、前記繊維に適用される前に前記結合剤と混合され、そして前記繊維に適用される、
ことを特徴とする請求項2又は3に記載の方法。 - 前記平面状材料を製造するために、連続又は不連続プレス、特にホットプレスが使用される、
ことを特徴とする請求項1ないし4いずれか一つに記載の方法。 - プレス温度が、140℃から220℃、好ましくは160℃から180℃である、
ことを特徴とする請求項1ないし5いずれか一つに記載の方法。 - プレス圧力が、0.3N/mm2から5.5N/mm2、好ましくは1N/mm2から3N/mm2である、
ことを特徴とする請求項1ないし6いずれか一つに記載の方法。 - プレス時間が、6秒/mm(板厚)から60秒/mm(板厚)、好ましくは10秒/mm(板厚)から20秒/mm(板厚)である、
ことを特徴とする請求項1ないし7いずれか一つに記載の方法。 - 前記繊維は、前記結合剤と任意に前記可塑化剤を用いて、湿潤、部分乾燥又は乾燥で提供され、前記結合剤及び任意に前記可塑化剤を適用するとき、前記繊維は、好ましくはその後に乾燥される、
ことを特徴とする請求項1ないし8いずれか一つに記載の方法。 - リグノセルロース繊維(5)及び結合剤を含み、プレス機において、請求項1ないし9いずれか一つの方法に従って製造される平面状材料であって、
前記結合剤は、メラミン樹脂、ホルムアルデヒド樹脂、フェノール樹脂、メチレンジフェニルイソシアネート(MDI)、又eMDIとして乳化された形態のもの、高分子ジフェニルメタンジイソシアネート(PDMI)、ポリウレタン、又は前述の結合剤の混合物を有し、前記結合剤の割合は、前記平面状材料の50重量%を超える、
ことを特徴とする平面状材料。 - 前記材料(1)は、天然繊維、合成繊維、無機繊維又は有機繊維、又は繊維の混合物を含む、
ことを特徴とする請求項10に記載の平面状材料。 - 前記有機,天然繊維は、再生可能な原料からのリグノセルロース繊維、特に針葉樹木繊維、落葉樹木繊維、一年生植物からの繊維、又は竹繊維を含む、
ことを特徴とする請求項11に記載の平面状材料。 - 前記合成繊維は、熱可塑性材料、特にポリエチレン又はポリプロピレンから形成された、又、ポリカーボネート、ポリアクリル、ポリメタクリル、又はポリウレタンから形成された繊維を含む、
ことを特徴とする請求項11に記載の平面状材料。 - 前記無機繊維は、鉱物、セラミック、又はガラス材料から形成された繊維を含む、
ことを特徴とする請求項11に記載の平面状材料。 - アトロウッドに対する前記結合剤の割合が、101重量%を超え、120重量%を超え、150重量%を超え、200重量%を超える、
ことを特徴とする請求項10ないし14いずれか一つに記載の平面状材料。 - 前記平面状材料(1)は、骨材、特に非吸湿性又は非膨潤性の充填剤を有する、
ことを特徴とする請求項10ないし16いずれか一つに記載の平面状材料。 - 前記骨材として、鉱物、セラミック、合成物、又はガラス粒子が使用される、
ことを特徴とする請求項16に記載の平面状材料。 - 前記平面状材料(1)は、疎水剤、例えばパラフィン又はワックスを有する、
ことを特徴とする請求項10ないし17いずれか一つに記載の平面状材料。 - リグノセルロース繊維(5)及び結合剤を含む前記平面状材料(1)は、最大3%、好ましくは最大2%、好ましくは1%未満の厚さの膨潤を有する、
ことを特徴とする請求項10ないし18いずれか一つに記載の平面状材料。 - 請求項10ないし19の少なくとも一つに記載の平面状材料の使用であって、
前記平面状材料(1)が、湿った部屋及び濡れた部屋のとき、内装仕上げとして、特に床板又は床ラミネートとして、壁又は天井板として、家具ボードとして使用され、屋外構造において、ファサードボード又は屋根として、厩舎のため、デッキ又は屋外床を含むテラス構造のため、及び屋外建造物、特に屋外家具として使用される、
ことを特徴とする平面状材料の使用。