JP2022066512A - 粘着フィルム、それが用いられた表面保護フィルム、及び光学フィルム - Google Patents
粘着フィルム、それが用いられた表面保護フィルム、及び光学フィルム Download PDFInfo
- Publication number
- JP2022066512A JP2022066512A JP2022036041A JP2022036041A JP2022066512A JP 2022066512 A JP2022066512 A JP 2022066512A JP 2022036041 A JP2022036041 A JP 2022036041A JP 2022036041 A JP2022036041 A JP 2022036041A JP 2022066512 A JP2022066512 A JP 2022066512A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- meth
- film
- pressure
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
例えば、液晶ディスプレイを構成する部材である偏光板、位相差板などの光学部材を製造する工程において使用される表面保護フィルムは、光学的に透明性を有するポリエチレンテレフタレート(PET)樹脂フィルムの片面に粘着剤層が形成されているが、光学部材に貼り合わせるまで、その粘着剤層を保護するための剥離処理された離形フィルムが、粘着剤層の上に貼り合わされている。
また、近年では、偏光板、位相差板などの光学部材から表面保護フィルムを剥がすときに、粘着剤層を被着体が剥がす時に発生する静電気に伴って生じる剥離帯電が、液晶ディスプレイの電気制御回路の故障に影響することが懸念され、粘着剤層に対して優れた帯電防止性能が求められている。
このように、近年においては、表面保護フィルムを構成する粘着剤層に対する要求性能として、優れた帯電防止性能、及び汚染防止性能などが、表面保護フィルムを使用するに当たっての使い易さの点から求められている。
また、近年では、このような帯電防止剤を基材フィルムに含有させたり、あるいは基材フィルムの表面に塗布するのではなく、直接に粘着剤層に含有させたりすることが提案されている(特許文献2)。
このため、LR偏光板やAG-LR偏光板などの光学フィルムに使用する表面保護フィルム用の粘着剤組成物においては、光学フィルムの表面がシリコーン化合物やフッ素化合物などで防汚処理や低反射表面処理が施されている場合でも、表面保護フィルムを光学フィルムから剥離する時の、剥離帯電圧を低く抑え、且つ、被着体の汚染が少ない粘着剤組成物が求められている。
特に、本発明に係わる表面保護フィルムは、被着体が、光学フィルムの表面に積層された、フッ素化合物を含有する防汚層、又は、フッ素化合物を含有する低屈折率形成用の組成物を用いて形成された低屈折率層を有する被着体である場合において、従来技術に比べて、優れた耐汚染性を有し、且つ、経時劣化しないで優れた剥離帯電防止性能を有することから、帯電防止性能と、耐汚染性との両立に効果があることが判明した。
アクリル系ポリマーと、帯電防止剤と、架橋剤とを含有する粘着剤組成物であって、
前記アクリル系ポリマーが、
(a1)アルキル基の炭素数がC1~C4の(メタ)アクリル酸エステルモノマーの少なくとも1種を1~50重量部と、(a2)アルキル基の炭素数がC5~C18の(メタ)アクリル酸エステルモノマーの少なくとも1種を50~99重量部との割合で含有してなり、前記(a1)と前記(a2)との合計が100重量部である(A)アルキル基の炭素数C1~18の(メタ)アクリル酸エステルモノマーの少なくとも2種以上と、
(B)水酸基を含有する共重合性ビニルモノマーの少なくとも1種以上と、
(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマーの少なくとも1種以上と、
を共重合させた共重合体のアクリル系ポリマー(但し、水酸基を含有しない窒素含有ビニルモノマーまたはアルコキシ基含有アルキル(メタ)アクリレートモノマーの少なくとも1種以上を共重合させたものを除く。)であり、
前記(a2)のうち、イソオクチル(メタ)アクリレート、イソノニル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレートからなる群から選択した少なくとも1種を50重量部以上の割合で含有してなり、
前記アクリル系ポリマーが、0℃以下のガラス転移温度を有してなり、
前記(D)架橋剤が、3官能以上のイソシアネート化合物であり、
前記帯電防止剤が、カチオンとアニオンとからなる融点25℃以上のイオン性化合物であり、前記アニオンが、トリフルオロメタンスルホナートアニオン、ペンタフルオロエタンスルホナートアニオン、ヘプタフルオロプロパンスルホナートアニオン、ノナフルオロブタンスルホナートアニオン、からなる群から選択された1種であり、
前記粘着剤組成物が、さらに、(E)金属キレート化合物の架橋促進剤と、(F)ケトエノール互変異性体化合物とを含有してなり、
前記粘着剤組成物が、前記アクリル系ポリマーの100重量部に対して、前記帯電防止剤を0.01~10重量部の割合で必須成分として含有してなることを特徴とする粘着剤組成物を提供する。
(a1)アルキル基の炭素数がC1~C4の(メタ)アクリル酸エステルモノマーの少なくとも1種を1~50重量部と、(a2)アルキル基の炭素数がC5~C18の(メタ)アクリル酸エステルモノマーの少なくとも1種を50~99重量部との割合で含有してなり、前記(a1)と前記(a2)との合計が100重量部である(A)アルキル基の炭素数C1~18の(メタ)アクリル酸エステルモノマーの少なくとも2種以上と、
(B)水酸基及び/又はカルボキシル基を含有する共重合性ビニルモノマーの少なくとも1種以上と、
(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマーの少なくとも1種以上と、
を共重合させた共重合体のアクリル系ポリマーであり、
前記(a2)のうち、イソオクチル(メタ)アクリレート、イソノニル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレートからなる群から選択した少なくとも1種を50重量部以上の割合で含有してなり、
前記粘着剤組成物が、さらに、(E)金属キレート化合物の架橋促進剤と、(F)ケトエノール互変異性体化合物とを含有してなることが好ましい。
前記水酸基を含有する共重合可能なモノマーが、8-ヒドロキシオクチル(メタ)アクリレート、6-ヒドロキシヘキシル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート、2-ヒドロキシエチル(メタ)アクリレート、N-ヒドロキシ(メタ)アクリルアミド、N-ヒドロキシメチル(メタ)アクリルアミド、N-ヒドロキシエチル(メタ)アクリルアミドからなる化合物群の中から選択された少なくとも1種以上であり、
前記カルボキシル基を含有する共重合可能なモノマーが、(メタ)アクリル酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート、2-(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、2-(メタ)アクリロイロキシプロピルヘキサヒドロフタル酸、2-(メタ)アクリロイロキシエチルフタル酸、2-(メタ)アクリロイロキシエチルコハク酸、2-(メタ)アクリロイロキシエチルマレイン酸、カルボキシポリカプロラクトンモノ(メタ)アクリレート、2-(メタ)アクリロイロキシエチルテトラヒドロフタル酸からなる化合物群の中から選択された少なくとも1種以上であることが好ましい。
前記(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマー中のジエステル分が0.2%以下であり、
前記(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマーとして、ポリアルキレングリコールモノ(メタ)アクリレート、メトキシポリアルキレングリコール(メタ)アクリレート、エトキシポリアルキレングリコール(メタ)アクリレートからなる群の中から選択された少なくとも1種以上を、前記(A)アルキル基の炭素数C1~18の(メタ)アクリル酸エステルモノマーの少なくとも2種以上の合計100重量部に対して、1~50重量部の割合で含有することが好ましい。
前記アクリル系ポリマーの100重量部に対して、前記(E)架橋促進剤を0.001~0.5重量部と、前記(F)ケトエノール互変異性体化合物を0.1~300重量部との割合で含有してなり、前記(F)/前記(E)の重量部比率が、70~1000であることが好ましい。
本発明に係わる粘着剤組成物、及びそれを用いた表面保護フィルムは、被着体が、光学フィルムの表面に積層された、フッ素化合物を含有する防汚層、又は、フッ素化合物を含有する低屈折率層形成用の組成物を用いて形成された低屈折率層を有する被着体である場合において、従来技術に比べて、優れた耐汚染性を有し、且つ、経時劣化しないで優れた剥離帯電防止性能を有する。
すなわち、本発明に係わる粘着剤組成物、及びそれを用いた表面保護フィルムは、優れた帯電防止性能と、耐汚染性とを備えているため、産業上の利用価値が極めて大である。
本実施形態の粘着剤組成物は、アクリル系ポリマーと、帯電防止剤と、架橋剤とを含有する粘着剤組成物であって、前記アクリル系ポリマーが、0℃以下のガラス転移温度を有してなり、前記(D)架橋剤が、3官能以上のイソシアネート化合物であり、前記帯電防止剤が、カチオンとアニオンとからなる融点25℃以上のイオン性化合物であり、前記アニオンが、トリフルオロメタンスルホナートアニオン、ペンタフルオロエタンスルホナートアニオン、ヘプタフルオロプロパンスルホナートアニオン、ノナフルオロブタンスルホナートアニオン、からなる群から選択された1種であり、前記アクリル系ポリマーの100重量部に対して、前記帯電防止剤を0.01~10重量部の割合で必須成分として含有してなる。
また、前記帯電防止剤は、温度25℃において固体の融点25℃以上のイオン性化合物であることが好ましく、さらに、前記帯電防止剤の融点が450℃以下であることが好ましい。
本実施形態に係わる粘着剤組成物における(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマーの割合は、(A)アルキル基の炭素数C1~18の(メタ)アクリル酸エステルモノマーの少なくとも2種以上の合計100重量部に対して、1~50重量部の割合が好ましく、1~30重量部の割合がより好ましく、2~25重量部の割合が特に好ましい。
また、(G)帯電防止剤の具体例としては、トリフルオロメタンスルホン酸リチウム、ノナフルオロブタンスルホン酸リチウム、1-メチル-3-オクチルピリジニウム トリフルオロメタンスルホナート塩、3-メチル-1-オクチルピリジニウム トリフルオロメタンスルホナート塩、1-メチル-4-オクチルピリジニウム ノナフルオロブタンスルホナート塩、4-メチル-1-オクチルピリジニウム ノナフルオロブタンスルホナート塩、ジメチルジオクチルアンモニウム ペンタフルオロエタンスルホナート塩、1-メチル-3-オクチルピリジニウム ヘプタフルオロプロパンスルホナート塩、3-メチル-1-オクチルピリジニウム ヘプタフルオロプロパンスルホナート塩、1-メチル-3-オクチルピリジニウム ノナフルオロブタンスルホナート塩、3-メチル-1-オクチルピリジニウム ノナフルオロブタンスルホナート塩、1-オクチル-3-メチルイミダゾリウム ノナフルオロブタンスルホナート塩などが挙げられる。
3官能以上のイソシアネート化合物としては、例えば、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート、キシリレンジイソシアネート等のジイソシアネート類のビュレット変性体やイソシアヌレート変性体、トリメチロールプロパンや、グリセリン等の3価以上のポリオールとのアダクト体などが挙げられる。
(D)架橋剤の割合としては、例えば、アクリル系ポリマーの100重量部に対して0.01~5重量部の割合が挙げられる。
多座配位子Lとしては、アセト酢酸メチル、アセト酢酸エチル、アセト酢酸オクチル、アセト酢酸オレイル、アセト酢酸ラウリル、アセト酢酸ステアリル等のβ-ケトエステルや、アセチルアセトン(別名2,4-ペンタンジオン)、2,4-ヘキサンジオン、ベンゾイルアセトン等のβ-ジケトンが挙げられる。これらは、ケトエノール互変異性体化合物であり、多座配位子Lにおいてはエノールが脱プロトンしたエノラート(例えばアセチルアセトネート)であってもよい。
単座配位子Xとしては、塩素原子、臭素原子等のハロゲン原子、ペンタノイル基、ヘキサノイル基、2-エチルヘキサノイル基、オクタノイル基、ノナノイル基、デカノイル基、ドデカノイル基、オクタデカノイル基等のアシルオキシ基、メトキシ基、エトキシ基、n-プロポキシ基、イソプロポキシ基、ブトキシ基等のアルコキシ基などが挙げられる。
本実施形態に係わる粘着剤組成物は、アクリル系ポリマーの100重量部に対して、(F)ケトエノール互変異性体化合物を0.1~300重量部との割合で含有することが好ましい。
基材フィルムには、樹脂フィルムの粘着剤層が形成された側とは反対面に、シリコーン系、フッ素系の離形剤やコート剤、シリカ微粒子等による防汚処理、帯電防止剤の塗布や練り込み等による帯電防止処理を施すことができる。
離形フィルムには、粘着剤層の粘着面と合わされる側の面に、シリコーン系、フッ素系の離形剤などにより離形処理が施される。
偏光板用の表面保護フィルムなどの光学用の表面保護フィルムの場合は、基材フィルム及び粘着剤層は、十分な透明性を有することが好ましい。
[実施例1]
撹拌機、温度計、還流冷却器及び窒素導入管を備えた反応装置に、窒素ガスを導入して、反応装置内の空気を窒素ガスで置換した。その後、反応装置にメチルアクリレート12重量部、2-エチルヘキシルアクリレート88重量部、8-ヒドロキシオクチルアクリレート12.0重量部、アクリル酸0.1重量部、ポリプロピレングリコールモノアクリレート(アルキレンオキサイドの平均繰り返し数n=12)20重量部とともに、溶剤(酢酸エチル)を100部加えた。その後、重合開始剤としてアゾビスイソブチロニトリル0.1重量部を2時間かけて滴下させ、65℃で8時間反応させ、実施例1のアクリル系ポリマー溶液を得た。
[実施例2~6及び比較例1~3]
モノマーの組成を各々、表1の記載のようにする以外は、上記の実施例1に用いるアクリル系ポリマー溶液と同様にして、実施例2~6及び比較例1~3に用いるアクリル系ポリマー溶液を得た。
[実施例1]
上記のとおり製造した実施例1のアクリル系ポリマー溶液に対して、架橋剤(コロネートHX)2.0重量部、帯電防止剤(ノナフルオロブタンスルホン酸リチウム)1.0重量部、架橋促進剤(チタニウムトリスアセチルアセトネート)0.1重量部、ケトエノール互変異性体化合物(アセチルアセトン)9重量部を加えて撹拌混合して実施例1の粘着剤組成物を得た。この粘着剤組成物をシリコーン樹脂コートされたポリエチレンテレフタレート(PET)フィルムからなる離形フィルムの上に塗布後、90℃で乾燥することによって溶剤を除去し、厚みが20μmの粘着剤層を得た。その後、一方の面に帯電防止及び防汚処理されたポリエチレンテレフタレート(PET)からなる基材フィルムの、帯電防止及び防汚処理された面とは反対の面に、離形フィルム付き粘着剤層を転写させ、基材フィルム/粘着剤層/離形フィルムの積層構成を有する実施例1の表面保護フィルムを得た。
[実施例2~6及び比較例1~3]
添加剤の組成を各々、表1の記載のようにする以外は、上記の実施例1の表面保護フィルムと同様にして、実施例2~6及び比較例1~3の表面保護フィルムを得た。
なお、表1において、(D)、(G)、(E)、(F)の各欄では、アクリル系ポリマーを100重量部として、各成分の含有割合(重量部)を括弧( )内の数値で示した。
また、表1に用いた各成分の略記号の化合物名を、表2に示す。(C)ポリアルキレングリコール鎖含有モノ(メタ)アクリル酸エステルモノマーのうち、C-1~C-5はモノマー中のジエステル分が0.2%以下であり、C-6はモノマー中のジエステル分が0.8%である。G-1~G-6はすべて融点が25℃以上で、25℃において固体のイオン性化合物であり、G-7は融点が15℃で、25℃において液体のイオン性化合物である。
実施例1~6及び比較例1~3における表面保護フィルムを、それぞれ23℃、50%RHの雰囲気下で7日間エージングしてから、以下の試験方法により評価した。
離形フィルムを剥がして、粘着剤層を表出させた表面保護フィルムを、粘着剤層を介して偏光板(偏光子の保護層がTACである偏光板を使用)の表面に貼り合わせ、1日放置した後、50℃、5気圧、20分間オートクレーブ処理し、室温でさらに12時間放置したものを、粘着力の測定試料とした。被着体の前記偏光板は、LR偏光板、又はAG-LR偏光板である。上記で得られた測定試料を、180°方向に引張試験機を用いて低速度(0.3m/min)又は高速度(30m/min)において剥がして測定した剥離強度を粘着力とした。
ここで、上記のLR偏光板、及びAG-LR偏光板は、前記偏光板の表面が、フッ素化合物を含有する組成物で低反射表面処理が施されている。
表面保護フィルムをエージングした後、被着体に貼り合わせる前に、離形フィルムを剥がして粘着剤層を表出し、抵抗率計ハイレスタUP-HT450(三菱化学アナリテック製)を用いて粘着剤層の表面抵抗率を測定した。
離形フィルムを剥がして、粘着剤層を表出させた表面保護フィルムを、被着面にフッ素化合物を含有する低屈折率層形成用の組成物を用いて形成された低屈折率層を有する被着体に貼合した。表面保護フィルムを、30m/minの引張速度で180°剥離した際に、被着体が帯電して発生する電圧(帯電圧)を高精度静電気センサSK-035、SK-200(株式会社キーエンス製)を用いて測定し、測定値の最大値を剥離帯電圧とした。
ガラス板の片面上に、前記低反射表面処理を施したLR偏光板、又は前記低反射表面処理を施したAG-LR偏光板(偏光子の保護層がTACである偏光板を使用)を、貼合機を用いて、粘着剤層(両面粘着テープ)を介して貼合した。その後、前記偏光板の表面に、表面保護フィルムを、貼合機を用いて貼合した。23℃、50%RHの環境下で3日および30日の期間に渡って保管した後に、前記表面保護フィルムを剥がし、前記偏光板の表面の汚染状態を目視にて観察した。耐汚染性の判断基準は、前記偏光板の表面に対して汚染なしの場合を「○」、わずかに汚染ありの場合を「△」、汚染ありの場合を「×」と評価した。
また、実施例1~6の表面保護フィルムは、粘着剤層の表面抵抗率が1.0×10+12Ω/□以下であり、フッ素化合物を含有する低屈折率層形成用の組成物を用いて形成された低屈折率層に対する、粘着剤層の剥離帯電圧が-0.3~+0.3kVの範囲内であり、帯電防止性能が優れていた。
さらに、実施例1~6の表面保護フィルムは、3日および30日の期間に渡って保管した後にも被着体である偏光板に対する汚染がなく、耐汚染性にも優れていた。
すなわち、実施例1~6の表面保護フィルムについての、表3に示された評価結果では、本発明の課題を解決できたことが実証されている。
また、比較例1~2の表面保護フィルムは、粘着剤層の表面抵抗率が高いために、剥離帯電圧が高かった。比較例3の表面保護フィルムについては、剥離帯電圧を測定していないが、粘着剤層の表面抵抗率が高いことから、剥離帯電圧は高いと推測される。
さらに、比較例2の表面保護フィルムは、粘着剤組成物に含有されているアクリル系ポリマーのガラス転移温度が0℃超過(計算値では、+2℃)となった。このため、粘着性能が悪く、粘着力が過大となった。なお、比較例2に用いたアクリル系ポリマーでは、ホモポリマーのガラス転移温度が高い値(0℃超過)であるメチルアクリレート及びアクリル酸の割合が多くされている。
このように、比較例1~3の表面保護フィルムでは、本発明の課題を解決することができなかった。
Claims (3)
- 樹脂フィルムの少なくとも片面に、アクリル系ポリマーと、帯電防止剤と、架橋剤とを含有する粘着剤層を有する粘着フィルムであって、
前記アクリル系ポリマーが、0℃以下のガラス転移温度を有してなり、
前記架橋剤が、3官能以上のイソシアネート化合物であり、
前記帯電防止剤が、カチオンとアニオンとからなる融点25℃以上のイオン性化合物であり、
前記カチオンが、ピリジニウム、イミダゾリウム、ホスホニウム、スルホニウム、ピロリジニウム、グアニジニウム、アンモニウム、イソウロニウム、チオウロニウム、ピペリジニウム、ピラゾリウム、メチリウム、リチウム、モルホリニウムからなる群から選択された1種であり、
前記アニオンが、トリフルオロメタンスルホナートアニオン、ペンタフルオロエタンスルホナートアニオン、ヘプタフルオロプロパンスルホナートアニオン、ノナフルオロブタンスルホナートアニオン、からなる群から選択された1種であり、
前記アクリル系ポリマーの100重量部に対して、前記帯電防止剤を0.01~10重量部の割合で必須成分として含有し、
前記粘着剤層の、表面抵抗率が1.0×10+12Ω/□以下であり、フッ素化合物を含有する低屈折率層形成用の組成物を用いて形成された低屈折率層に対する、前記粘着剤層の剥離帯電圧が-0.3~+0.3kVの範囲内である
ことを特徴とする粘着フィルム。 - 請求項1に記載の粘着フィルムが用いられた、表面保護フィルム。
- 請求項1に記載の粘着フィルムが用いられた、光学フィルム。