JP2022036169A - Paint material made of cosmetic material, diluent for paint material, paint material and paint set - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a paint material made of a cosmetic capable of using similarly with a commercially available conventional water color paint material, a diluent for a paint material, a paint material and a paint material set.

SOLUTION: The paint material comprising a cosmetic material according to the present invention is used in combination with a diluent for a paint material, and has a minimum characteristic as the paint material, and can be used in the same manner as ordinary paint materials, thereby enabling the effective use of the cosmetic material to be discarded. In particular, in combination with such a diluent, it is possible to expect a good characteristic of the paint material based on the cosmetic material in the transparency, the quick drying, and the smell of a film when extending to drawing paper than the ordinary paint. The paint materials and the paint sets according to the present invention are made of a paint material made of such a cosmetic material and a diluent for a paint material, and are provided as a paint set which can be used in the same manner as ordinary paints, and a paint set with a dedicated diluent and a set.

SELECTED DRAWING: Figure 1

COPYRIGHT: (C)2022,JPO&INPIT

Description

The present invention relates to paint materials made of cosmetics, diluents for paint materials, paints and paint sets. More specifically, the present invention relates to a paint material composed of a cosmetic that can be used as a cosmetic to be discarded, a diluent for the paint material, a paint, and a paint set.

Cosmetics such as powdered cosmetics are distributed and used mainly by women. General powdered cosmetics include base makeup such as foundation and face powder, and point makeup such as eye shadow and cheek, all of which are used for the purpose of smearing on human skin. In addition, most of the powders such as constitutional powders constituting powdered cosmetics are derived from minerals (see, for example, Patent Document 1 and the like), but some minerals are called for depletion. ing.

On the other hand, individual consumers often dispose of powdered cosmetics without using them up, and even companies that manufacture and sell cosmetics do not meet a certain level of quality in bulk powdered cosmetics. (Contents) are discarded in large quantities annually. Considering the recent situation in which we should aim for a sustainable society, we should consider the effective use of powdered cosmetics to be discarded, and it is desired to establish the technology to deal with them.

Japanese Patent Application Laid-Open No. 2003-102450

Here, cosmetics such as powdered cosmetics often contain pigments or brilliant powders, and in that case, there is a characteristic that various colors can be visually enjoyed. If the powdered cosmetics to be discarded can be converted into, for example, paints while maintaining such characteristics, it is possible to bring about a new method of using the powdered cosmetics to be discarded.

In general, powdered cosmetics include oily components (oil agents) such as silicone oil and hydrocarbon oil, constitutional powders such as mica, talc, silica, barium sulfate and synthetic gold mica, and coloring materials such as titanium oxide. If necessary, a surfactant or the like is blended, and in many cases, these are packed in a container such as a gold plate and pressed.

Therefore, the powder in the powdered cosmetic may be partially covered with a certain amount of oily component, and even if the powdered cosmetic is crushed and kneaded with a commercially available water-based liquid, it may be mixed. It was difficult to make a paint-like slurry because the wetness did not proceed and the powder separated.

The present invention is made in view of the above, and provides a paint material made of a cosmetic, a diluent for the paint material, a paint, and a paint set, which can be used in the same manner as general watercolor paints on the market. There is something in it.

In order to solve the above-mentioned problems, the paint material made of the cosmetic according to the present invention is used.
Contains constitutional powder and coloring material, and
When the contained components are arranged in descending order of content, the fifth from the top is characterized by containing cosmetics having 3 or less oily components.

The paint material made of the cosmetic according to the present invention is characterized in that, in the above-mentioned invention, when the contained components are arranged in descending order of content, one or more constitutional powders are contained in the third order from the top. And.

In the above-mentioned invention, the constitutional powder contained in the third item from the top is selected from the group consisting of mica, talc, synthetic phlogopite, silica and barium sulfate. It is characterized by being at least one species.

The paint material made of the cosmetic according to the present invention is characterized in that, in the above-mentioned invention, when the contained components are arranged in descending order of content, the pearl powder is not contained in the third order from the top. ..

The paint material comprising the cosmetic according to the present invention is the group in which the cosmetic comprises eye shadow, teak, body powder, face powder, whitening powder, skin care powder, loose powder, pressed powder and foundation in the present invention. It is characterized by being at least one selected from.

The diluent for paint materials according to the present invention is a diluent for diluting paint materials made of cosmetics, and has the following components;
Water: 49.5-89.0% by weight based on the total diluent,
Lower alcohol: 10.0 to 35.0% by mass based on the total diluent,
Polyvinyl alcohol: 0.5 to 15.0% by mass based on the total diluent,
It is characterized by containing.

The diluent for paint materials according to the present invention is characterized in that, in the above-mentioned invention, the lower alcohol is ethanol.

The paint according to the present invention is
The above-mentioned paint material made of the cosmetic of the present invention and
The above-mentioned diluent for paint materials of the present invention and
It is characterized by containing a mixture of the above.

The paint set according to the present invention is
The above-mentioned paint material made of the cosmetic of the present invention and
The above-mentioned diluent for paint materials of the present invention and
It is characterized by including.

The paint material made of the cosmetic according to the present invention has the minimum characteristics as a paint when used in combination with a diluent for the paint material, and can be used in the same manner as general paints, and is subject to disposal. It makes it possible to make effective use of cosmetics. In particular, when used in combination with such a diluent, it is expected to have better properties peculiar to paint materials based on cosmetics, such as transparency, quick-drying, and fragrance of the film when spread on drawing paper compared to general paints. can do.

The diluent for paint materials according to the present invention can play a role of supplementing the components lacking as paint materials with respect to the paint materials for paint materials when used in combination with the paint materials made of cosmetics.

The paint and the paint set according to the present invention consist of a paint material made of the cosmetic according to the present invention and a diluent for the paint material according to the present invention, and can be used in the same manner as general paints, and paint materials. Can be provided as a paint set with a special diluent.

It is a figure which showed the evaluation standard used in the test example 1 and the test example 2.

Hereinafter, one aspect of the present invention will be described.

(I) Paint material consisting of cosmetics:
The present invention is a paint material made of cosmetics, and among commercially available cosmetics, various eye shadows such as powder eye shadows (eye colors) are considered to be applicable to the present invention. (Eye color), various teaks such as powder teak (cheek color), body powder, face powder, whitening powder, skin care powder, loose powder, pressed powder, foundation and other make-up (makeup) cosmetics and other powdered makeup Examples thereof include cosmetics containing a material and cosmetics containing powdered cosmetics such as a base cosmetic that serves as a base for make-up cosmetics such as a makeup base.

These cosmetics may be used alone or in combination of two or more. In addition, there is no problem with using these cosmetics that are to be discarded, and by using the cosmetics that were originally planned to be discarded, it is possible to make effective use of the cosmetics that are to be discarded. can.

Of these, eye shadow (eye color) is a cosmetic that is applied in order to form shadows by applying different tones of color to the eye holes on the eyelid side and around the eyes such as the lower eyelid and the outer corner of the eye. ..

Cheek (cheek color) is so-called blusher, which is a cosmetic that is applied to the cheeks to make the complexion look brighter, or to add shadows to the cheeks to give a three-dimensional effect. The dosage form may be solid, powder, cream, liquid, stick or the like, but the powder is suitable for the present invention.

Body powder is a cosmetic that is used to suppress oil glare and give a matte, natural finish.

Face powder is a cosmetic that is used to finish makeup and suppresses the so-called shine and stickiness of sebum and foundation. Whitening powder with whitening effect, skin care powder with skin care effect, and loose powder are also considered to be a kind of face powder and body powder.

Breast powder is a kind of face powder mentioned above, and is basically used after using the foundation described later. It is a cosmetic that prepares and coats the foundation to make the skin look more beautiful.

Foundation is a cosmetic that is used to adjust the color of the skin, cover freckles and age spots on the skin, and protect it from ultraviolet rays. It is a make-up cosmetic that is applied after applying the makeup base described later on the skin.

The makeup base is used as a base before applying make-up cosmetics such as foundation, and the color-developing property of the make-up cosmetics is improved in adhesion (attachment) and covering power (glue) to make up. It is a cosmetic that is used as a base material for the purpose of beautiful finish, prevention of makeup breakage, and maintenance of makeup effect.

The powdered cosmetics suitable for the paint material according to the present invention are generally considered to contain powder (powder component) as a main component (generally 60% by mass or more of the total amount of the cosmetics), and have a mass of 60 to 95%. %, But is not limited to this), and refers to cosmetics mixed with water-based components, oil-based components, etc. as appropriate. It is understood that each particle can freely flow under normal pressure, but the present invention is not particularly limited to this, and cosmetics generally called powdered cosmetics in the cosmetic industry can be widely used.

Examples of the components contained in the target cosmetics represented by the above include constitutional powders (for example, inorganic powders, organic powders, surfactant metal salt powders (metal soaps), etc.), and coloring materials. (For example, inorganic pigments, organic pigments, natural pigments, pearl powders, etc.), oily components (for example, naturally derived vegetable oils, animal oils, etc., hydrocarbon oils, ester oils (including glyceride oil), higher fatty acids, higher grades, etc.) Alcohol, silicone oil, wax, oily thickener, organic solvent, etc.) and other ingredients (eg, aqueous preservatives, powdered preservatives, preservatives, surfactants, surface treatments, antioxidants, beauty agents , Ultraviolet absorber, film forming agent, emollient component, aqueous component, etc.). One of these components may be used alone, or two or more thereof may be used in combination. Similarly, for each of the components listed below, one of them may be used alone, or two or more of them may be used in combination. Of these, constitutional powders and coloring materials are essential components for applying cosmetics as paint materials, but oily components and other components are not particularly such. As for the oily components, as will be described later, when the components contained in the cosmetics are arranged in descending order of content, the number of oily components is 3 or less from the top to the 5th.

In general, powders contained in powdered cosmetics include constitutional powders such as inorganic powders, organic powders, and surfactant metal salt powders (metal soaps), and inorganic pigments (including white pigments). ), Organic pigments, natural pigments, pearl powders and the like can be considered. Here, the powders listed below may or may not be subjected to various surface treatments.

Constitution powder (also called constitution pigment) is used as a bulking agent to maintain the dosage form of cosmetics, and in addition, it adjusts the extensibility, adhesion, gloss, etc. of cosmetics, and adjusts the color tone. It is understood that it is used as a regulator for regulation.

The components used as the constitutional powder are inorganic powders and crushed products of naturally occurring clay minerals. Other than that, for example, synthetic inorganic powder such as silicon dioxide (silica), organic powder such as organic polymer powder which is not an inorganic pigment, and surfactant metal salt powder (metal soap). Etc. may also be classified individually.

For cosmetics, constitutional powder prevents makeup from breaking due to absorption of sweat and sebum, improves the feel of use by adjusting the powder shape, particle size, hardness, and surface condition, and the extensibility and adhesiveness of cosmetics. It is also used for the purpose of adjusting the whiteness and color tone, adjusting the gloss of cosmetics by controlling the transparency, and is an indispensable ingredient as a base ingredient for, for example, foundations.

As the constitutional powder, as the inorganic powder, for example, zirconium oxide, cerium oxide, magnesium oxide, barium sulfate (Ba sulfate), calcium sulfate, magnesium sulfate, calcium carbonate, magnesium carbonate, talc, mica, kaolin, silicite, etc. White mica, synthetic mica, synthetic gold mica (synthetic fluorofrogo pite), gold mica, red mica, black mica, Lithia mica, silicic acid, anhydrous silicic acid, aluminum silicate, magnesium silicate, aluminum magnesium silicate, silicic acid Calcium acid, barium silicate, strontium silicate, silicic acid (Na / K / Al), metal tungstate, hydroxyapatite, vermiculite, hygilite, bentonite, montmorillonite, hectrite, disteardimonium hectrite, zeolite, Ceramic powder, dicalcium phosphate, alumina, aluminum hydroxide, boron nitride, boron nitride, silica, fine particle cerium oxide, dimethylsilylated silica, octenyl succinate corn starch aluminum (octenyl succinate corn starch Al), octenyl succinate starch aluminum (octenyl succinic acid) Distillate Al) and the like can be mentioned.

Examples of the organic powder include polyamide powder, polyester powder, polyethylene powder (which can also be wax), polypropylene powder, polystyrene powder, polyurethane powder, benzoguanamine powder, polymethylbenzoguanamine powder, polytetrafluoroethylene powder, and polymethylmethacrylate. Examples thereof include powder, cellulose powder, silk powder, nylon powder (12 nylon, 6 nylon, etc.). It should be noted that the description of these "-powder" is for convenience, and includes those without the description of "powder" (for example, "polyethylene", "polypropylene", etc.).

Examples of other organic powders include styrene / acrylic acid copolymer, divinylbenzene / styrene copolymer, vinyl resin, urea resin, phenol resin, fluororesin, silicon resin, acrylic resin, melamine resin, and epoxy resin. Polycarbonate resin, microcrystalline fiber powder, starch powder, lauroyl lysine (also a surface treatment agent), polymethylsilsesquioxane, (vinyldimethicone / methicone silsesquioxane) crosspolymer, (dimethicone / vinyldimethicone) Examples thereof include cross-polymers, (diphenyldimethicone / vinyldiphenyldimethicone / silsesquioxane) cross-polymers, polymethyl methacrylate, methyl methacrylate cross-polymers, corn starch, hydrolyzed hydrogenated starch and the like.

Examples of the surfactant metal salt powder (metal soap) include zinc stearate, aluminum stearate, aluminum distearate (Al distearate), calcium stearate, magnesium stearate (Mg stearate), zinc myristate, and myristin. Examples thereof include magnesium acid (Mg myristate), zinc cetyl phosphate, calcium cetyl phosphate, sodium zinc cetyl phosphate and the like.

The coloring material is a powder or the like for coloring a cosmetic into a desired color and developing a color. As a coloring material, examples of the inorganic pigment which is a pigment include fine particles and a pigment grade (titanium oxide (rutyl)). Inorganic substances such as titanium oxide (white pigment, which can also be a pearl powder), fine particles and pigment-grade zinc oxide (white pigment, which can also be a powder preservative), such as titanium oxide (anathase). Inorganic red pigments such as white pigments, iron oxide, iron hydroxide, iron titanate, inorganic brown pigments such as γ-iron oxide, inorganic yellow pigments such as yellow iron oxide and ocher, and inorganic substances such as black iron oxide and carbon black. Inorganic purple pigments such as black pigments, manganese violet and cobalt violet, inorganic green pigments such as chromium hydroxide, chromium oxide, cobalt oxide and cobalt titanate, and inorganic blue pigments such as konjo (dark blue) and gunjo (ultra blue). Can be mentioned.

As the organic pigment which is a pigment, for example, a raked tar-based dye, a raked natural dye, a synthetic resin powder in which these powders are combined, and the like can be used, for example. Red 2, Red 3, Red 102, Red 104, Red 105, Red 106, Yellow 4, Yellow 5, Green 3, Blue 1, Blue 2, Red 201, Red 202, Red 203, Red 204, Red 205, Red 206 , Red 207, Red 208, Red 213, Red 214, Red 215, Red 218, Red 219, Red 220, Red 221, Red 223, Red 225, Red 226, Red 227, Red 228, Red 230 (1), Red 230 (2), red 231 and red 232, orange 201, orange 203, orange 204, orange 205, orange 206, orange 207, yellow 201, yellow 202 (1), yellow 202 (2), yellow 203, yellow 204, Yellow 205, Green 201, Green 202, Green 204, Green 205, Blue 201, Blue 202, Blue 203, Blue 204, Blue 205, Brown 201, Purple 201, Red 401, Red 404, Red 405, Red 501, Red 502 , Red 504, Red 505, Red 506, Orange 401, Orange 402, Orange 403, Yellow 401, Yellow 402, Yellow 403, Yellow 404, Yellow 405, Yellow 406, Yellow 407, Green 401, Green 402, Blue 403, Blue Examples thereof include 404, purple 401, and black 401.

Examples of the natural pigment as a coloring material include carmine, carmic acid, laccinic acid, carthamin, brazilin, crocin, salol yellow, β-carotene, hibiscus pigment, capsinetin, laccinic acid, glucmin, riboflavin, ciconin and the like. ..

The pearl powder as a coloring material may be any powder having a pearl luster that is generally used. For example, in addition to ordinary mica titanium having a pearl luster, iron oxide-coated mica titanium and iron oxide-coated mica , Black Iron Oxide Coated Mica Titanium, Iron Oxide / Black Iron Oxide Coated Mica Titanium, Carmine Coated Mica Titanium, Carmine / Conjo Coated Mica Titanium, Iron Oxide / Carmine Treated Mica Titanium, Conjo Treated Mica Titanium, Iron Oxide / Conjo Treated Mica Titanium , Chromium oxide treated mica titanium, black titanium oxide treated mica titanium, synthetic gold mica, titanium oxide coated synthetic gold mica, glass powder, titanium oxide coated glass powder, polyethylene terephthalate / polyester film laminated powder, mica piece, acrylic resin coated aluminum powder (May contain coloring material), iron oxide coated mica, iron oxide coated bismuth oxide, titanium oxide coated talc, colored titanium oxide coated mica, bismuth oxychloride, fish scale foil, aluminum flakes, stainless flakes, titanium oxide coating Examples thereof include plate-shaped alumina, iron oxide (tin), pearl husks, gold foil, gold-deposited resin film, and metal-deposited resin film.

Other pearl powders include, for example, titanium oxide (which can also be a white pigment), borosilicate (Ca / Al), borosilicate (Ca / Na), (PET / polymethyl methacrylate) laminate, and the like. Examples thereof include (PET / Al) laminating and (PET / Al / epoxy resin) laminating.

The oily component (also called an oil agent) contains an oil content and is useful for smoothing the formulation. For example, naturally derived vegetable oils, animal oils and the like, hydrocarbon oils and ester oils (including glyceride oils). , Higher fatty acids, higher alcohols, silicone oils, waxes, oily thickeners, organic solvents and the like.

As oily components, naturally derived vegetable oils, animal oils and the like include, for example, avocado oil, flaxseed oil, almond oil, sardine oil, eno oil, olive oil, cacao butter, capoc wax, kaya oil, carnauba wax, liver oil, candelilla wax and kyonin oil. , Hardened oil, wheat germ oil, sesame oil, rice germ oil, rice bran oil, sugar cane, southern ka oil, safflower oil, shea butter, cinnamon oil, cinnamon oil, jojobaro, celaclow, turtle oil, soybean oil, brown seed oil , Camellia oil, evening primrose oil, corn oil, rapeseed oil, Japanese millet oil, nukarou, germ oil, persic oil, palm oil, palm kernel oil, sunflower oil, hardened sunflower oil, sunflower oil fatty acid methyl ester, sunflower oil, grape oil , Bayberry wax, jojoba oil, macadamia nut oil, mink oil, cotton seed oil, cotton wax, mokuro, mokuro kernel oil, montan wax, palm oil, hardened palm oil, tri-palm oil fatty acid glyceride, peanut oil, lanolin, liquid lanolin, reduced lanolin, lanolin alcohol , Hard lanolin, lanolin acetate, lanolin fatty acid isopropyl, POE lanolin alcohol ether, POE lanolin alcohol acetate, lanolin fatty acid polyethylene glycol, POE hydrogenated lanolin alcohol ether, hydrogenated vegetable oil, egg yolk oil and the like.

Examples of the hydrocarbon oil include squalane, squalane, paraffin, paraffin wax, liquid paraffin (mineral oil), pristane, polyisobutylene, petrolatum, polyisobutene, polybutene and the like.

Examples of the ester oil (including glyceride oil) include diisobutyl adipate, 2-hexyldecyl adipate, di-2-heptylundecyl adipate, N-alkylglycol monoisostearate, isosetyl isostearate, and triisostearic acid. Trimethylol propane, di-2-ethylhexanoate ethylene glycol, 2-ethylhexanoate cetyl, tri-2-ethylhexanoate glyceryl (triethylhexanoin), tri-2-ethylhexanoate trimethylolpropane, tetra-2- Pentaerythritol ethylhexanate, cetyl octanate, octyldodecyl gum ester, oleyl oleate, octyldodecyl oleate, decyl oleate, neopentyl glycol dicaprate, triethyl citrate, 2-ethylhexyl succinate, amyl acetate, ethyl acetate, Butyl acetate, isocetyl stearate, butyl stearate, diisopropyl sebacate, di-2-ethylhexyl sebacate, cetyl lactate, myristyl lactate, isopropyl palmitate, 2-ethylhexyl palmitate (ethylhexyl palmitate), 2-hexyldecyl palmitate , 2-Heptylundecyl palmitate, Cholesteryl 12-hydroxystearyl (cholesteryl hydroxystearate), Dipentaerythritol fatty acid ester, isopropyl myristate, octyldodecyl myristate, 2-hexyldecyl myristate, myristyl myristate, dimethyloctane Hexyldecyl acid, ethyl laurate, hexyl laurate, N-lauroyl-L-glutamate-2-octyldodecyl ester, diisostearyl malate, acetoglyceryl, glyceryl triisooctanoate, polyglyceryl-2 triisostearate-2 (triisostearic acid) Glyceryl) (also used as a surface active agent), glyceryl triisopalmitate, glyceryl monostearate, glyceryl di-2-heptylundecanoate, glyceryl trimyristate, diglyceryl triisostearate, tridecyltricate trimeritate, Hexa (hydroxystearic acid / stearic acid / logonic acid) dipentaerythrityl, propylene glycol dicaprate (PG dicapric acid), isotridecyl isononanoate, tri (capric acid / capric acid) glyceryl, isononyl isononanoate, bisdig Examples thereof include lyceryl polyacyl adipate-2, neopentyl glycol diethylhexanate, octyldodecyl stearoyloxystearate, isostearyl neopentate, hydrogenated castor oil isostearate, hydrogenated trifatty acid (C12-18) glyceryl and the like.

Examples of higher fatty acids include lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, undecylenic acid, oleic acid, linoleic acid, linolenic acid, arachidonic acid, eicosapentaenoic acid (EPA), docosahexaenoic acid (DHA), and the like. Examples thereof include isostearic acid and 12-hydroxystearic acid (hydroxystearic acid).

Examples of higher alcohols include lauryl alcohol, myristyl alcohol, palmityl alcohol, stearyl alcohol, behenyl alcohol, hexadecyl alcohol, oleyl alcohol, isostearyl alcohol, hexyldodecanol, octyldodecanol, cetostearyl alcohol and 2-decyltetradecy. Examples thereof include noll, cholesterol, phytosterol, POE cholesterol ether, monostearyl glycerin ether (bacyl alcohol), monooleyl glyceryl ether (ceracyl alcohol) and the like.

Examples of the silicone oil include dimethylsilicone oil, cyclic dimethylsilicone oil, methylhydrogen silicone oil, polyether-modified silicone oil, methylphenylsilicone oil, fluorine-modified silicone oil, dimethicone, hydrogendimethicone, cyclopentasiloxane, methicone, and diphenyl. Examples thereof include siloxyphenyltrimethicone and phenyltrimethicone.

Examples of the wax include candelilla wax, microcrystalline wax, polyethylene (which can also be an constitutional powder), selecin, zokerite, beeswax, synthetic wax, hydrogenated palm oil fatty acid, stearyl stearate and the like.

Examples of the oil-based thickener include (ethylene / propylene / styrene) copolymer, (butylene / ethylene / styrene) copolymer, (ethylene / propylene) copolymer, dextrin palmitate and the like.

Examples of the organic solvent include isododecane and the like.

Regarding other components, examples of the aqueous preservative include phenoxyethanol and caprylyl glycol. Examples of the powdered preservative include zinc oxide (which can also be a white pigment). Examples of preservatives include butylene glycol (BG, which is also an aqueous component) methylparaben, ethylparaben, propylparaben, butylparaben, caprylyl glycol, ethylhexylglycerin, propanediol, sodium dehydroacetate (Na dehydroacetate), and silver. And so on.

Examples of the surfactant include sorbitan sesquiisostearate, polyglyceryl-2 triisostearate (also used as an oily component), sorbitan stearate, polyhydroxystearic acid, and polyglyceryl-3 polylysinoreate (also used as an oily component). ), Etc. can be mentioned.

Examples of the surface treatment agent include perfluorohexylethyltriethoxysilane, isostearic acid, stearic acid, aluminum hydroxide (Al hydroxide), triethoxycaprylylsilane, palmitic acid, and lauroylricin (which can also be constitutional powders). ) Etc. can be mentioned.

Examples of the antioxidant include dibutylhydroxytoluene (BHT), tocopherol, tocopherol acetate, diethylhexylcyringidene malonic acid and the like.

Examples of beauty agents include lecithin, chamomile extract, strawberry fruit extract, lavender flower extract, magwa root bark extract, water-soluble collagen, chitosan, lactic acid rod fungus / hibiscus flower fermented liquid, tenninka fruit extract, camellia seed oil, and hydrolyzed conchiolin. , Di (phytosteryl / octyldodecyl) lauroyl glutamate (ceramide) and the like.

Examples of the ultraviolet absorber include ethylhexyl methoxycinnamate, t-butylmethoxydibenzoylmethane, ethylhexyl methoxycinnamate and the like.

Examples of the film forming agent include trimethylsiloxysilicic acid and the like.

Examples of the emollient component include tri (caprylic acid / capric acid) glyceryl and the like.

Examples of the aqueous component include butylene glycol (BG, which also serves as a preservative), water and the like.

The cosmetics applicable to the present invention may contain one or more constitutional powders in the third order from the top when they contain a coloring material and the contained components are arranged in descending order of content. preferable. Coloring materials contained in cosmetics often have brilliant properties, and constitutional powder is also a base material for paint materials and often helps color development, so it is more visually appealing than making it an essential ingredient. You can enjoy a variety of colors and it is suitable for use as a paint material. In addition, the constitutional powder has a function of adjusting the hiding power, coloring power, covering power, ductility, adhesiveness, etc. when spread on drawing paper as a paint.

The coloring material is generally preferably contained in an amount of 0.05% by mass or more, particularly preferably in the range of 2.0 to 30.0% by mass, as a paint material. The range is not particularly limited as long as it has enough color to be used. Further, when the cosmetic material is applied as a paint material and a lack of color development is felt, a coloring material may be added separately to obtain the above-mentioned content.

While the constitutional powder contained in cosmetics is suitable as a paint material in this way, when the contained components are arranged in descending order of content, one or more constitutional powders should be contained from the top to the third. For example, it can be expected that the constitutional powder is appropriately contained in the cosmetics, and it is considered that the cosmetics as a whole can be effectively used as a paint material.

Further, it is more preferable that the constitutional powder occupies two kinds of the third component from the top when the contained components are arranged in descending order of the content, and all three of the third from the top are included. It is especially preferable to occupy. Further, it is more preferable that the constitutional powder contains the constitutional powder from the top to the second when the contained components are arranged in descending order of the content, and the constitutional powder is the first from the top. Is particularly preferable.

In addition, when the contained components are arranged in descending order of content, the constitutional powders contained in the third order from the top include mica, talc, silica, synthetic phlogopite (synthetic fluorophlogopite), and barium sulfate. It is preferably at least one selected from the group consisting of (sulfate Ba). These constitutional powders are bulky powders with a large amount of refueling, and are suitable as paint materials. When used as paint materials, they have hiding power, coloring power, covering power, and spreading power when spread on paper. The sex, adhesiveness, etc. can be adjusted. That is, it is possible to impart uniformity of adhesion to the paper surface, smoothness of the finished paint film, visual transparency, and the like.

In the target cosmetics, when the contained components are arranged in descending order of content, the number of oily components is 3 or less from the top to the 5th. When four or more oily ingredients are contained in the fifth from the top, it is considered that the ratio of the oily ingredients to the cosmetics is high, and the diluent for paint materials to be used together ((II) described later). Even if it is mixed with (explained), the diluent will not be compatible with the cosmetics and will separate, and it will not be possible to obtain the same state as general watercolor paints on the market, which is not preferable. In addition, even if the cosmetic and the diluent are likely to be mixed, slight separation from the diluent is observed, and it may be difficult to use it as a paint if it is dissolved in water and smeared on drawing paper. Not preferred. As for the oily components, when the components contained in the cosmetics are arranged in descending order of content, the number of oily components is preferably 2 or less, and more preferably 1 or less, from the top to the 5th. , It is particularly preferable that it does not contain an oily component (it becomes 0 kinds).

Further, when the contained components are arranged in descending order of content, it is preferable that the pearl powder is not contained in the third order from the top. Since pearl powders such as pearl luster pigments (pearl agents) and brilliant pigments (lame agents) are formed from powders with a relatively large particle size, the third from the top contains pearl powder as a coloring material. Then, the ratio of pearl powder to cosmetics may increase, and when it is made into a paint, it spreads and spreads on the drawing paper, is overcoated on the drawing paper, and the smoothness of the film formed on the drawing paper. It may adversely affect the fixability of the film formed on the drawing paper, and may also reduce the secondary adhesion. When the contained components are arranged in descending order of content, it is more preferable that the pearl powder is not contained in the second order from the top, and it is particularly preferable that the pearl powder is not the most abundant component. Regarding the present invention, "secondary adhesion" is not a phenomenon but an evaluation item, and the high and low levels and superiority or inferiority of the evaluation items are described. In other words, low secondary adhesion and inferior secondary adhesion mean that secondary adhesion is likely to occur when viewed as an event.

The contained component preferably contains at least one selected from the group consisting of titanium oxide, zinc oxide and boron nitride. Since these ingredients are usually blended in make-up cosmetics and the like, they are considered to be general-purpose ingredients.

In addition to the above-mentioned ingredients, the cosmetics used in the present invention include ingredients generally used in cosmetics, such as drugs, moisturizers, and bactericides, as long as the purpose and effect of the present invention are not impaired. , Resins and the like, desired ingredients generally used in cosmetics can be added.

In order to use the paint material made of the cosmetic according to the present invention as a watercolor paint, for example, it is mixed (as a mixture) with a diluent for the paint material described later to be made into a paint. Here, "painting" means that the state (paint-like) is similar to that of general watercolor paints on the market (the same applies hereinafter). In addition, after being made into a paint, it is dissolved in an appropriate amount of water and smeared on drawing paper with a brush, similar to general watercolor paints on the market (hereinafter, may be simply referred to as "general paints"). Will be used.

When such a paint material made of a cosmetic according to the present invention is used in combination with a diluent for paint materials, it has the minimum characteristics as a paint material and can be used in the same manner as general paints. , It is possible to make effective use of cosmetics to be discarded. In particular, when used in combination with such a diluent, it is expected to have better properties peculiar to paint materials based on cosmetics, such as transparency, quick-drying, and fragrance of the film when spread on drawing paper compared to general paints. can do.

When the cosmetic is made into a paint as in the present invention (hereinafter, may be referred to as "cosmetic paint" for convenience), the cosmetic paint is a general paint in terms of color development (easiness of color appearance). It may be slightly inferior to that. This is because the concentration of the pigment contained in the powdered cosmetic itself produced for the purpose of smearing on human skin is lower than that of general paints.

In addition, depending on the type of cosmetic used as a paint, it is also generally available on the market in terms of secondary adhesiveness (for example, it can be confirmed by tracing a dry locus on drawing paper with a hand and checking whether it adheres to the hand). May be slightly lower than the watercolor paints in. It is considered that this is because the powder such as the constitutional powder contained in the cosmetic is relatively large as compared with the general paint composed of the powder having a pigment-grade particle size.

On the other hand, for example, the film of the depiction mark finished by the cosmetic paint has a transparent feeling peculiar to the cosmetic paint, and may also have a transparent touch feeling peculiar to the cosmetic paint which is not found in general paint. be. In addition, since it is originally a cosmetic, it has a good scent, and it is considered that quick-drying and the like are also good by mixing it with a diluent described later.

(II) Diluent for paint materials:
Next, a diluent for paint materials used in combination with paint materials made of cosmetics (hereinafter, may be simply referred to as “diluent”) will be described. The diluent is suitable for use in combination with the above-mentioned paint material made of the cosmetic according to the present invention, and contains water, lower alcohol, and polyvinyl alcohol having a specific content and a specific range. When the above-mentioned cosmetics and the like are applied as paint materials (base materials for paints), the diluents for paint materials are insufficient as paint materials for cosmetics because they are used in combination with such paints. It plays a role of supplementing the ingredients.

That is, since cosmetics such as powdered cosmetics are not originally manufactured assuming paint materials, it is natural that there are components that are insufficient for general paints. When the paint material composed of the above components is used by dissolving it in water as it is, the dispersibility in water and the wettability in water are insufficient, and even if it is dissolved in water, the paper It is expected that there will be insufficient adhesion to water, film properties, quick-drying properties, etc. Diluents for paint materials can supplement such deficient properties by containing the above-mentioned components in a specific amount.

The water serves as a solvent for dispersing each component constituting the diluent, and commonly used water such as tap water, purified water, ion-exchanged water and the like can be used. The content of such water may be, for example, the balance excluding the essential component and the optional component in the diluent (referring to the portion other than the essential component and the optional component in the diluent), but is generally the entire diluent. On the other hand, it is preferably 49.5 to 89.0% by mass, more preferably 60.5 to 86.0% by mass, and more preferably 66.5 to 83.5% by mass.

The lower alcohol plays a role of a volatile agent when used in combination with cosmetics, and can impart volatility and quick-drying property. As the lower alcohol, for example, lower alcohols (monohydric alcohols having 5 or less carbon atoms) such as methanol (methyl alcohol), ethanol (ethyl alcohol), propanol (propyl alcohol), isopropyl alcohol, butanol, and propanol shall be used. It is preferable to use ethanol in terms of versatility, safety, compatibility with cosmetics, and the like.

The total content of the lower alcohol is 10.0 to 35.0% by mass with respect to the total amount of the diluent. If the content of the lower alcohol is less than 10.0% by mass, the quick-drying property is impaired, the film formation on the paper is delayed, and color unevenness may occur. On the other hand, if the content exceeds 35.0% by mass, the quick-drying property is too strong, and the film is formed without being fully stretched, which may also cause color unevenness. Furthermore, when the lower alcohol is ethanol, excess ethanol may cause pigment aggregation. The total content of the lower alcohol is preferably 12.5 to 30.0% by mass, more preferably 15.0 to 30.0% by mass, based on the total amount of the diluent.

Polyvinyl alcohol is useful for film formation when used in combination with cosmetics (it becomes a film component), and imparts good riding (glue) to drawing paper, smoothness, etc. to the formed film. Can be done.

The content of polyvinyl alcohol is 0.5 to 15.0% by mass with respect to the total amount of the diluent. When the content of polyvinyl alcohol is less than 0.5% by mass, the formed film becomes thin, and the smoothness of the film and the uniformity of the film are lost. On the other hand, if the content exceeds 15.0% by mass, the film becomes thick, the uniform film is damaged, and the finished film may be damaged due to friction. That is, if the content is low, the forming film formed on the drawing paper becomes thin, and the unevenness of the powder becomes conspicuous, and the uniformity of the film may be lost. Pigment dispersibility on the paint itself or on the drawing paper at the time of drawing may deteriorate, resulting in color unevenness. On the other hand, if the content is high, the film formed on the drawing paper becomes too thick, and the uniformity of the film may be lost. The content of polyvinyl alcohol is more preferably 1.0 to 9.0% by mass, and particularly preferably 1.0 to 3.0% by mass, based on the total amount of the diluent.

In addition to the above-mentioned essential components, the diluent for paint materials is water-soluble, for example, phenoxyethanol, triethanolamine, polyhydric alcohol, acrylic acid polymer (carbomer), etc., as long as it does not interfere with the object and effect of the present invention. Polymer, sodium hydroxide (NaOH), potassium hydroxide (KOH) (the above-mentioned triethanolamine, sodium hydroxide, potassium hydroxide serve as a neutralizing agent for the acrylic acid polymer), nonionic synthetic resin, nonion. Arbitrary components such as a water-soluble film-forming agent and other water-soluble materials such as a sex-synthesized polymer, an acrylic acid-based water-soluble polymer, a polysaccharide, and a surfactant can be appropriately added.

Here, it is preferable to solve the problem by using a surfactant to supplement the dispersibility and wetness (wetting) of the paint material made of cosmetics, but powdered makeup which is considered to be the target of the paint material. Since cosmetics such as cosmetics often contain a surfactant, they are diluted in consideration of the environmental impact when used as a paint and the safety when they adhere to human skin. As an agent, it is listed as an optional ingredient. When added, the optional component may be contained, for example, in an amount of, for example, about 1.0% by mass or less with respect to the entire diluent, but the present invention is not limited thereto.

The diluent for paint materials can be prepared by mixing and stirring the above-mentioned essential components and optional components (essential components and the like). As an example, each component may be added to water as a solvent, mixed and stirred to disperse the essential components and the like in the water.

The diluent for paint materials according to the present invention described above can play a role of supplementing the components lacking as paint materials in the paint materials for paint materials when used in combination with the paint materials made of cosmetics. ..

(III) Paints and paint sets:
The paint according to the present invention comprises a mixture of a paint material consisting of the cosmetics described in (I) and a diluent for the paint material described in (II), and similarly, the paint set according to the present invention is: It contains a paint material consisting of the cosmetics described in (I) and a diluent for the paint material described in (II). As the paint set, the paint material and the diluent made of cosmetics may each have one kind of composition, or two or more kinds of each may have its composition.

The paint material composed of cosmetics is diluted with a diluent for the paint material to form a mixture, so that the paint material is in the same state as general watercolor paints on the market (this is the present invention). It will be the paint of.). The mixing ratio of the paint material and the diluent is not particularly limited, and can be appropriately determined depending on the type of cosmetic, the mixing ratio of the components constituting the diluent, the color finally desired by the user, and the like. As a mass ratio, it is preferable to mix the diluent as 0.5 to 2 with respect to the cosmetic 1, and it is particularly preferable to mix the diluent as 0.7 to 1.5, but this range is not particularly limited.

The paint material diluted with the diluent (paint which is a mixture) is used by being dissolved in water on a palette or the like, for example, like a general watercolor paint on the market. As for the amount of water used, as a mass ratio, 1 is a diluted paint material (a paint-ized cosmetic made of a mixture of a cosmetic and a diluent), and water is used. However, the mixing ratio is not limited to 0.5 to 3, and the mixture may be appropriately determined according to the preference of the user and the like.

The paint according to the present invention and the paint set described above are made of a paint material made of the cosmetic according to the present invention and a diluent for the paint material according to the present invention, and can be used in the same manner as general paints. And can be provided as a paint set in which the paint material is set with a special diluent.

(V) Modification of embodiment:
It should be noted that the embodiments described above show one aspect of the present invention, and the present invention is not limited to the above-described embodiment, but includes the configuration of the present invention and can achieve the object and the effect. Needless to say, modifications and improvements within the scope are included in the content of the present invention. Further, the specific structure, shape, etc. in carrying out the present invention may be any other structure, shape, etc. within the range in which the object and effect of the present invention can be achieved. The present invention is not limited to the above-described embodiments, and modifications and improvements to the extent that the object of the present invention can be achieved are included in the present invention.

For example, in the above-described embodiment, certain types of cosmetics that can be used as paint materials are given as an example, but the cosmetics that can be used as paint materials are not limited to this, and powders other than those mentioned as examples are given. It does not limit the application of cosmetics such as cosmetics. Similarly, in the above-described embodiment, specific examples of each component are given, but these are merely examples, and there is no problem even if the components not listed are blended in the paint material made of cosmetics.
In addition, the specific structure, shape, etc. at the time of carrying out the present invention may be other structures, etc. as long as the object of the present invention can be achieved.

Hereinafter, the present invention will be described in more detail based on test examples and the like, but the present invention is not limited thereto.

16 kinds of commercially available cosmetics A to P having the compositions shown in Tables 1 to 9 were prepared (Table 1 shows the product name and type, etc., and Tables 2 to 9 show all the ingredient information such as the composition, etc.). Shows.). Cosmetics A to P have a coloring material as an ingredient and have sufficient color development to be suitable for use as a paint material (also evaluated in Test Example 2 (4) described later).

Further, cosmetics A to P contain constitutional powder, oily components, etc., cosmetics A to cosmetics G, cosmetics M to cosmetics P are eye shadows, cosmetics H are teak, and cosmetics I to. Cosmetic K is classified into face powder, and cosmetic L is classified into foundation. Further, the cosmetic A, the cosmetic B, the cosmetic D, and the cosmetics H to P are generally distributed and sold as so-called powdered cosmetics.

(Product name and manufacturer / distributor)

(Information on all ingredients such as composition: Cosmetic A, Cosmetic B)

(Information on all ingredients such as composition: Cosmetic C, Cosmetic D)

(Information on all ingredients such as composition: Cosmetic E, Cosmetic F)

(Information on all ingredients such as composition: Cosmetic G, Cosmetic H)

(Information on all ingredients such as composition: Cosmetic I, Cosmetic J)

(Information on all ingredients such as composition: cosmetics K, cosmetics L)

(Information on all ingredients such as composition: Cosmetic M, Cosmetic N)

(Information on all ingredients such as composition: Cosmetic O, Cosmetic P)

Here, the compositions shown in Table 2 and the like are listed in descending order of the amount of ingredients with respect to the total cosmetics. Further, in the composition of Table 2 and the like, the indication of "+/-" is an indication used in series products having many different colors such as cosmetics for make-up, and the components (coloring materials) displayed after that. Etc.) indicates that it is used in the series products. Therefore, there are cases where ingredients that are not necessarily blended are displayed in the cosmetics with the listed product names (however, at least one kind of coloring material shown below "+/-" is used). ..

Then, with respect to these 16 types of cosmetics, various properties as paint materials are compared and evaluated by the method described in [Test Example 2] using the diluent for paint materials selected in [Test Example 1] below. did.

[Test Example 1]
Evaluation of Diluents for Paint Materials:
With respect to the diluent (diluent) for paint materials obtained by the following method, the suitability as a diluent for paint materials was evaluated using Cosmetic A as a control.

(Manufacturing of diluent for paint materials)
Water, ethanol as a lower alcohol, polyvinyl alcohol and phenoxyethanol are added as the components of the diluent for the paint material as the contents shown in Table 10 (% by mass with respect to the total amount of the diluent), and other components are added to the solvent water. Then, the mixture was mixed and stirred and dispersed in water to produce Diluent 1 to Diluent 3.

(Composition of diluent)

The diluents 1 to 3 thus obtained are made into paints by the following method using the cosmetics A shown in Tables 1 and 2 (in the same state as general watercolor paints on the market (similar to commercially available general watercolor paints). After making it a general paint)), an evaluation sample was prepared, and the suitability as a diluent for paint materials was evaluated by the following method.

(Painting and preparation of evaluation samples)
3 g of the cosmetic and 3 g of the diluent were kneaded with a spatula for 5 minutes to form a mixture, and the cosmetic was made into a paint. Then, 0.2 g of the paint-made cosmetic and 0.2 g of water (tap water) were dissolved on a palette to prepare an evaluation sample.

(Evaluation methods)
Of the 14 evaluation items (1) to (14) below, (1) spreading and spreading (on paper), (2) good riding (on paper), (3) quick-drying, etc. Using the five items of (5) transparency and (8) smoothness of the film (made on paper), the criteria shown in FIG. 1 by 12 panelists (3 points of general watercolor paints on the market (commercially available watercolor paints) It is a standard of 5 grades of 5, 4, 3, 2 and 1 point when it is normal), and 5 points are the best and 1 point is the worst.) The average score (average value) of was calculated. FIG. 1 is a diagram showing the evaluation criteria used in Test Example 1 and Test Example 2, and this criterion is also used in Test Example 2 described later.

Then, the calculated average score was compared and evaluated using the following evaluation criteria. The results are shown in Table 11 (Table 11 and Table 12 below show the average score of the results and the evaluations of "◎", "○", "Δ", and "×" below). In addition, in FIG. 1 and the following contents, the "drawing paper" to be smeared may be simply described as "paper". In addition, the average values in Table 11 and Table 12 to be described later are rounded off to the third decimal place.

(Evaluation criteria)
Rating contents ◎: Average score is 3.5 points or more 〇: Average score is 2.5 points or more and less than 3.5 points △: Average score is 1.5 points or more and less than 2.5 points ×: Average score is 1 . Less than 5 points

(Evaluation item)
(1) Spread (on paper):
We confirmed how easy it is to spread on the paper when it is applied to the drawing paper with a brush.

(2) Good ride (on paper):
I checked whether it could be smeared on paper in the same way as ordinary paints without fading.

(3) Quick-drying:
I confirmed how fast it dries.

(4) Color development:
I confirmed the ease of color appearance.

(5) Transparency:
We confirmed the degree to which the drawing paper can be seen through.

(6) Overcoating (on paper):
Immediately after smearing, it was smeared again from above, and it was confirmed that the first smear was not twisted or taken to the second smear.

(7) Detachability after drying:
After putting the paint on the palette and letting it harden for a few days, I checked if it fell off or peeled off the palette.

(8) Smoothness of film (made of paper):
I smeared it on drawing paper and traced the dry trajectory by hand to check if it was rough or uneven.

(9) Secondary adhesion:
I smeared it on drawing paper and traced the dry trajectory with my hand to check if it adhered to my hand.

(10) Film fixability (made of paper):
After smearing and drying, it was confirmed whether the film was twisted when traced by hand.

(11) Fragrance:
It was confirmed whether or not it had a good scent against the unique scent of general paints.

(12) Toning:
I checked if the color was as expected when I mixed other cosmetic paints on the palette (for example, if I expected it to be purple when red and blue were mixed, would it be so?).

(13) Solubility in water:
It was confirmed whether it was easy to mix when mixing with water on the pallet.

(14) Solubility in water after solidification:
As in (7), the paint was placed on a palette, dried and solidified, and then it was confirmed whether it could be redissolved with water.

(result)

As shown in Table 11, depending on the content of lower alcohol (ethanol) considered to be a volatile agent and the content of polyvinyl alcohol (PVA) considered to be a membrane component, (2) riding (on paper) The results showed that the evaluation scores of goodness, (3) quick-drying property, and (8) film smoothness were high (diluent 3 was the highest). Regarding (5) transparency, the average score of all three diluents was 5 (full score).

On the other hand, regarding (1) the evaluation of elongation and spread, the average score of the diluent 3 having the highest content of ethanol and polyvinyl alcohol is 1 although it is higher than the standard score (3 points) of general paints. It was the lowest. In this respect, from the viewpoint of combining volatility and film forming property, when the diluent 3 is used, there is an advantage that it spreads and spreads moderately to the extent of general paints, and a clean and uniform film can be quickly formed. You might also say that.

Based on the above results, in each of Diluent 1 to Diluent 3, the film of the paint does not spread too much when smeared on drawing paper, and it spreads as much as general paint, and it is faint than general paint. Relative evaluations were made on the fact that the paint was applied cleanly without being damaged, and that the film of the finished paint was uniform and had few irregularities, and it was confirmed that the paint had good characteristics equal to or better than those of general paint.

Then, among the three diluents, it was judged that the diluent 3 having these characteristics in a well-balanced manner was the most preferable, and in the following [Test Example 2], the diluent 3 was used as the diluent. ..

[Test Example 2]
Evaluation as a paint material for cosmetics:
With respect to the cosmetics A to P shown in Tables 1 to 9 above, various properties of the paint material were compared and evaluated using the diluent 3 selected in Test Example 1 as the diluent.

First, as in Test Example 1, 3 g of the cosmetic and 3 g of the diluent were kneaded with a spatula for 5 minutes to form a mixture, and the cosmetic was made into a paint. Further, 0.2 g of paint-based cosmetics and 0.2 g of water (tap water) were dissolved on a palette to prepare an evaluation sample.

As a result of performing the above operation, the cosmetic C, the cosmetic E, and the cosmetic F were separated from the diluent, and the diluent did not fit into the cosmetic and could not be made into a paint (hence,). It dissolved in water and could not be applied to drawing paper.) In addition, the cosmetic G was also found to be slightly separated from the diluent, and it was difficult to use it as a paint when it was dissolved in water and smeared on drawing paper. Therefore, these cosmetics C, cosmetics E, cosmetics F, and cosmetics G were judged to be unsuitable as paint materials, and subsequent evaluations were not performed.

Regarding the possibility of making paints, from the information on all the ingredients of the cosmetics shown in Tables 2 to 9, if 4 or more oily ingredients are contained from the top to the 5th, the constitutional powder etc. may be determined by the oily ingredients. It is considered that the powder contains so many oily components that the entire surface area of the powder is covered, which makes it difficult to make a paint. In addition, all the cosmetics that were difficult to paint were in a creamy dosage form, and were soft enough to be recognized as a slurry when touched with a finger.

On the other hand, when the contained components are arranged in descending order of content, the oily component is 3 or less from the top, and the constitutional powder is 1 from the top. Regarding the cosmetics A, B, D, H to P, which are the cosmetics including the above, there was no problem in making them into paints. Based on the above, the 14 evaluation items (see above for the contents of the evaluation items) of the following (1) to (14) for the evaluation samples of cosmetic A, cosmetic B, cosmetic D, and cosmetic H to cosmetic P. The evaluation was made according to the criteria shown in FIG. 1 (when 3 points were used for general paints). The results are shown in Table 12 (for cosmetic A, the results when Diluent 1 and Diluent 2 are used are also included for reference).

(Evaluation item)
(1) Spreading (on paper) (2) Good riding (on paper) (3) Quick-drying (4) Color development (5) Transparency (6) Overcoating (on paper) (7) After drying (8) Smoothness of the film (made on paper) (9) Secondary adhesion (10) Fixability of the film (made on paper) (11) Fragrance (12) Toning (13) To water Solubility (14) Solubility in water after solidification

(result)

As shown in Table 12, some of the evaluated cosmetics were evaluated as "△" for (4) color development and (9) secondary adhesion ((1)). Spreading (on paper), (6) recoating (on paper), (8) smoothness of film (made on paper), (10) fixability of film (made on paper) are "△" (9) Cosmetic N with "x" in "secondary adhesiveness" will be described later), and the overall evaluation results are generally good. As a result, this cosmetic paint is generally used. It can be judged that it has characteristics that are not much different from those of watercolor paints.

It should be noted that the items (1) to (14) are not essential characteristics as paints, but merely confirm the points that are relatively superior and inferior to general paints, and (4) color development and (9) Just because the evaluation results of these items, including items such as secondary adhesion, are inferior to those of general paints does not mean that they cannot be applied as paints.

Here, in (4) color development, some of the cosmetics (cosmetic paints) evaluated as paints this time are slightly inferior to the general watercolor paints (general paints) on the market. This is because the content of the pigment contained in the powdered cosmetic itself produced for the purpose of smearing on human skin may be lower than that of general paints.

However, regarding (3) quick-drying and (5) transparency, the film of the depiction trace finished with the cosmetic paint has the transparency peculiar to the cosmetic paint, and when the panelists' comments are put together, the makeup that is not found in general paints. It was said that it had a favorable impression because it had a touch feeling peculiar to paints. From the above, it is considered that although there is some inferiority in color development, it can be regarded as a paint, and it is possible to produce a unique depiction feeling with a transparent touch instead of color development.

In addition, (9) some of them were slightly inferior to general paints in secondary adhesiveness. It is considered that this is because the powder such as the constitutional powder contained in the cosmetic is relatively large as compared with the general paint composed of the powder having a pigment-grade particle size.

This is different from general paints that penetrate into the unevenness of the drawing paper surface, and the large powder contained in the cosmetic paint cannot penetrate the unevenness of the paper surface and adheres to the surface of the drawing paper. It is expected to be in a state of being fixed by the membrane component. As a result, it is easy to be entangled by the physical frictional force, and it is considered that the secondary adhesiveness is lowered.

In addition, as mentioned above, it has a better evaluation than general paints in (3) quick-drying and (5) transparency, and the transparency makes it possible to express a delicate design with a light touch. It was also confirmed that it is easy to draw because it dries quickly like acrylic paint, and has the advantage of being able to continue drawing without waiting for the time to dry.

Furthermore, the (11) scent was also generally better than that of general paints. This is because there are unscented and scented products in cosmetics, but the diluent itself does not have the odor peculiar to watercolor paints, and moreover, the cosmetic paints formed by the scented cosmetics have no scent. It was confirmed that the scent derived from cosmetics was given, and that there was a merit that there was a good scent unique to cosmetics that did not cause discomfort.

Cosmetic N, which has the highest content of pearl powder among all the components, can be spread and spread (1) (on paper), (6) overcoated (on paper), and (8) (on paper). The score was relatively low in each of the items of () smoothness of the film and (10) film fixability (made on paper), and (9) the average score of the secondary adhesion was 1 point, which was low. rice field.

It is considered that this result is caused by the fact that the pearl powder having a large particle size is contained in the largest amount among the components constituting the cosmetic, and the powder is caught on the brush tip. When the brush tip touches the paper, the large powder attached to the outer surface of the brush tip adheres to the paper, and in the initial stage of spreading and spreading, the large powder gets stuck between the brush tips, and the small powder is also entangled with it. It becomes clogged at the ends of the hair.

After that, only the liquid component spreads and spreads so as to be sucked into the drawing paper, and the fluidity of the liquid component of the brush tip also decreases, so that it is considered that the spread and spread seems to have decreased. From the above, there is a bias in the localization of the powder in the depiction trace that spreads on the drawing paper, making it difficult to recoat (6) (on paper), and the unevenness of the film of the depiction trace after drying. I think that will also occur. As a result, (8) it also affects the smoothness of the film (made on paper), and (9) secondary adhesion is reduced due to the localized powder lumps of the depiction trace after drying, and (10) ( It is thought that the fixability of the film (made of paper) is also reduced.

In addition, general paints are usually used by putting the paints on a palette, drying them, and solidifying them. In order to verify whether it is possible to use cosmetic paints in the same way as general paints, (7) exfoliation after drying and (14) solubility in water after solidification were evaluated. went. As a result, as shown in Table 12, it was confirmed that it was comparable to general paints, and that it could be used at the same level without peeling off from the palette or being sparingly soluble in water. ..

INDUSTRIAL APPLICABILITY The present invention can be advantageously used as a paint material or a means for applying a cosmetic to be discarded as a paint material, and has high industrial applicability.

Claims (9)

Contains constitutional powder and coloring material, and
A paint material comprising cosmetics, characterized in that, when the contained components are arranged in descending order of content, the fifth from the top contains cosmetics having three or less oily components. The paint material comprising a cosmetic according to claim 1, wherein when the contained components are arranged in descending order of content, one or more constitutional powders are contained from the top to the third. The cosmetic according to claim 2, wherein the constitutional powder contained in the third item from the top is at least one selected from the group consisting of mica, talc, synthetic phlogopite, silica and barium sulfate. Paint material consisting of materials. The paint comprising the cosmetic according to any one of claims 1 to 3, wherein when the contained components are arranged in descending order of content, the pearl powder is not contained in the third order from the top. material. Claim 1 to claim 1, wherein the cosmetic is at least one selected from the group consisting of eye shadow, teak, body powder, face powder, whitening powder, skin care powder, loose powder, pressed powder and foundation. A paint material comprising the cosmetic according to any one of claim 4. A diluent for diluting paint materials consisting of cosmetics, and the following components;
Water: 49.5-89.0% by weight based on the total diluent,
Lower alcohol: 10.0 to 35.0% by mass based on the total diluent,
Polyvinyl alcohol: 0.5 to 15.0% by mass based on the total diluent,
Diluent for paint materials, characterized by containing. The diluent for paint materials according to claim 6, wherein the lower alcohol is ethanol. The paint material comprising the cosmetic according to any one of claims 1 to 5.
The diluent for paint material according to claim 6 or 7.
A paint characterized by containing a mixture of. The paint material comprising the cosmetic according to any one of claims 1 to 5.
The diluent for paint material according to claim 6 or 7.
A set of paints characterized by including.