JP2022014913A - 特に酸素還元(orr)触媒として有用な、金属ドーパントを有する多孔質の窒素含有カーボン材料の調製方法 - Google Patents
特に酸素還元(orr)触媒として有用な、金属ドーパントを有する多孔質の窒素含有カーボン材料の調製方法 Download PDFInfo
- Publication number
- JP2022014913A JP2022014913A JP2021112036A JP2021112036A JP2022014913A JP 2022014913 A JP2022014913 A JP 2022014913A JP 2021112036 A JP2021112036 A JP 2021112036A JP 2021112036 A JP2021112036 A JP 2021112036A JP 2022014913 A JP2022014913 A JP 2022014913A
- Authority
- JP
- Japan
- Prior art keywords
- nitrogen
- containing carbon
- core
- metal
- solvent medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の窒素含有カーボン材料の調製方法であって、少なくとも、(a)少なくともアルデヒド、置換もしくは無置換のヒドロキシベンゼン誘導体、及び窒素原子の供給源である重合性炭化水素化合物、さらに前記金属ドーパントの少なくとも1つの金属前駆体を溶解して含む溶媒媒体を提供する工程であって、前記金属前駆体は、少なくとも1つの窒素含有芳香族大環状化合物に配位した少なくとも1つの遷移金属を有する工程;(b)工程(a)の前記溶媒媒体内でゾル-ゲル重合を活性化して、少なくともコアに前記金属前駆体を含む窒素含有カーボンハイドロゲルを形成する工程;(c)工程(b)で形成された前記窒素含有カーボンハイドロゲルの乾燥形態を提供する工程;及び(d)工程(c)の前記乾燥形態を非酸化性雰囲気中で熱分解して、少なくともコアに少なくとも1つの金属ドーパントを担持した、前記多孔質の窒素含有カーボン材料を形成し、これを回収する工程を含む方法を提供する。
【選択図】なし
Description
しかるに、本発明は、優れた有効性を示す、酸素還元のための触媒を、白金を使用せずに供給する方法を提供することを目的とする。
本発明はまた、多孔質材料中に高密度の活性部位を有する触媒を供給する方法の提供も目的とする。
さらに、炭素、窒素、及び白金以外の金属を含む触媒の合成のための、簡便、効果的、且つ低コストの方法を提供することを目的とする。
これはまた、金属のドーピングと窒素のドーピングとを単一工程で行うことのできる方法を提供することも目的とする。
本発明はまた、コアにおいて1つ以上の触媒金属種で有利にドープされた、新たな多孔質の窒素含有カーボン材料を提供することを目的とする。
また、本発明は、白金を使用せずにPEMFCの出力向上を可能にする、触媒部位を含む材料を提供することを目的とする。
(a)少なくともアルデヒド、置換もしくは無置換のヒドロキシベンゼン誘導体、及び窒素原子の供給源である重合性炭化水素化合物を溶解状態で含み、また前記金属ドーパントの少なくとも1つの金属前駆体をさらに含む溶媒媒体を提供する工程であって、前記金属前駆体は、少なくとも1つの窒素含有芳香族大環状化合物に配位した少なくとも1つの遷移金属を有する工程、
(b)工程(a)の前記溶媒媒体内でゾル-ゲル重合を活性化して、少なくともコアに前記金属前駆体を含む窒素含有カーボンハイドロゲルを形成する工程、
(c)工程(b)で形成された前記窒素含有カーボンハイドロゲルの乾燥形態を提供する工程、
(d)工程(c)の前記乾燥形態を非酸化性雰囲気中で熱分解して、少なくともコアに少なくとも1つの金属ドーパントを担持した、前記多孔質の窒素含有カーボン材料を形成し、これを回収する工程を含む方法に関する。
少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の窒素含有カーボン材料は、有利にはエアロゲル、クリオゲル、またはキセロゲルであり、好ましくはエアロゲルまたはクリオゲルである。
より詳細には、本発明による方法は、遷移金属が白金とは異なる金属前駆体を使用する。
より詳細には、少なくともコアに少なくとも1つの金属ドーパントを担持した、この多孔質の窒素含有カーボン材料は、エアロゲル、クライオゲル、またはキセロゲルの形態をとり、好ましくはエアロゲルまたはクライオゲルである。好ましくは、BET法で評価して、300m2/g以上、特に300m2/gから800m2/g、さらには555m2/gから800m2/gの範囲内の比表面積を有する。
この材料は、その窒素含量によっても特徴付けられ、この窒素含量は、前記材料の全質量に対して、有利には少なくとも2質量%、特に5から15質量%、さらには6から10質量%である。
さらに別の主題によれば、本発明は、プロトン交換膜燃料電池(PEMFC)システムにおける正極材料としての、本発明による、少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の窒素含有カーボン材料の使用に関する。この材料は、有利には、燃料電池システムにおける活性部位への効果的なアクセスを可能にする。
本発明による材料は、特にプロトン交換膜燃料電池の正極触媒として、例えば自動車タイプの軽輸送における使用のために採用してよい。
このゾル-ゲル重合、あるいは重縮合反応は、少なくともアルデヒド、ヒドロキシベンゼン誘導体、及び窒素原子の供給源である炭化水素化合物を、反応の誘発を促進する条件下で一緒にすることによって実施される。
1つ以上のヒドロキシベンゼン誘導体及び1つ以上のアルデヒドは、有利には、ヒドロキシベンゼン誘導体のアルデヒドに対するモル比にして0.05から2.0、好ましくは0.1から1.0、より好ましくは0.2から0.4で一緒にされる。
好ましい一実施態様では、ゾル-ゲル重合により、ホルムアルデヒド、メラミン、及びレゾルシノールが一緒にされる。
より詳細には、本方法で使用される芳香族メタロ大環状化合物は、窒素原子が遷移金属に配位した、窒素含有芳香族大環状化合物を含む。
金属原子を含まない窒素含有芳香族大環状化合物中に存在する窒素の質量割合は、3から80質量%、好ましくは5から50質量%、より好ましくは8から40質量%である。
窒素含有芳香族大環状化合物は、有利には水溶性または水分散性であり、好ましくは水溶性である。
遷移金属は、マンガン(Mn)、コバルト(Co)、チタン(Ti)、鉄(Fe)、ルテニウム(Ru)、オスミウム(Os)、ニッケル(Ni)、銅(Cu)、及び亜鉛(Zn)から、好ましくはマンガン(Mn)、コバルト(Co)、及び鉄(Fe)から選択することができ、より好ましくは鉄(Fe)である。
金属は、採用する遷移金属の選択に応じて、いかなる所望の酸化状態で存在してもよい。例えば、使用する遷移金属が鉄原子である場合、これはメタロ大環状化合物中に、0、+2、または+3の酸化状態で存在してよい。
また、金属は、共有結合または別の方法で、窒素含有芳香族大環状化合物とは異なる1つ以上の化学成分、例えば、少なくとも1つの二原子酸素分子、ハロゲン原子、または、チオール、ピロリジン、ピペリジン、アルコールもしくはエーテル誘導体のヘテロ原子に、配位していてもよい。
この溶媒は、好ましくは水性媒体である。これは、特に、水または水性-アルコール性媒体であってよい。水性-アルコール性媒体は、特に、水と1つ以上のアルコールとの混合物であり、様々な割合のものである。
溶媒媒体への、ヒドロキシベンゼン及び窒素原子の供給源である炭化水素化合物の溶解、あるいはアルデヒドの溶解、並びに1つ以上の窒素含有芳香族メタロ大環状化合物の分散または溶解は、これらを含むこの溶媒媒体の、特に60℃から80℃の温度での加熱によってもたらすことができる。
ゾル-ゲル重合は、有利には、約85℃の温度で行われる。工程(b)における活性化は、特に、工程(a)からの前記溶媒媒体を、60℃から95℃、好ましくは80℃から90℃の温度に暴露することによって実施してもよい。
重合の生成物は、窒素含有芳香族メタロ大環状化合物が組み込まれた炭素/窒素ハイドロゲルである。ハイドロゲル中のこれらメタロ大環状化合物の存在は、有利には、高活性の触媒部位の形成を促進する。
採用した乾燥技術に応じて、工程(b)で得られたハイドロゲルは、クライオゲル、エアロゲル、またはキセロゲルに変換される。
第1の変形によれば、工程(c)の乾燥形態は、工程(b)で得られたハイドロゲルをその溶媒媒体から分離し、かくして単離されたハイドロゲルを、超臨界流体、特に水または二酸化炭素、特に二酸化炭素と接触させて乾燥させることによって得られる。この変形によれば、乾燥によって、工程(b)で得られたハイドロゲルは、上述のようにメタロ大環状化合物の形態で活性部位前駆体を含む窒素含有有機エアロゲルに変換される。次いで、工程(c)からの乾燥形態は、本プロセスの終わりに、少なくともコアに少なくとも1つの金属ドーパントを担持した窒素含有カーボンエアロゲルを生成させることに使用される。
熱分解は、有利には、750℃から1200℃、特に750℃から850℃、さらには約800℃の温度で行われる。
これは特に、不活性の、特に非酸化性の雰囲気下、例えば窒素またはアルゴン下、好ましくはアルゴン下で行われる。この雰囲気は、特に、アンモニア及び/または窒素含有化合物を含んでいてもよい。
この熱分解は、例えば、以下の実施例に記載される手順におけるような、段階的な温度の上昇と下降を適用することによって行ってもよい。温度プロファイルは、特に、2時間から6時間続く温度上昇と、これに次ぐ1時間から4時間、好ましくは2時間から3時間の温度安定化と、その後のオーブンの惰性による温度低下とを含んでいてよい。
直接的には、とりわけ、エアロゲル、クライオゲル、またはキセロゲルの形態の、少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の、特にメソポーラスな窒素含有カーボン材料に関する。一般に、その細孔の平均径が2~50nmである場合に物質がメソポーラスであると呼称される。
本発明による材料における金属ドーパントの質量負荷は、有利には、前記材料の全質量に対する金属原子の質量で表して、0.001%から7%、好ましくは0.01%から5%であってよい。金属ドーパントの担持は、例えば、原子吸光法によって特徴付けてよい。
少なくともコアに担持された多孔質の窒素含有カーボン材料は、特に少なくとも1nmの直径を有する金属ナノ粒子、特に鉄ナノ粒子を含まないことが好ましい。
これらの多孔質カーボン材料は、さらに、高い細孔容積を有し、特に2~20nmのピークで特徴付けられる細孔径分布を有する。
これらは、マンガン(Mn)、コバルト(Co)、チタン(Ti)、鉄(Fe)、ルテニウム(Ru)、オスミウム(Os)、ニッケル(Ni)、銅(Cu)、及び亜鉛(Zn)、好ましくはマンガン(Mn)、コバルト(Co)、及び鉄(Fe)の遷移金属から選択される少なくとも1つの金属ドーパントをコアに担持する。
好ましい一実施態様によれば、これらは鉄II及び/または鉄IIIの原子でドープされている。
特に、本発明による少なくともコアに担持した多孔質の窒素含有カーボン材料は、白金を含まない。
実施例に示されるように、本発明による多孔質の窒素含有カーボン材料は、鉄が金属大環状化合物の形態で導入されていない場合、例えば鉄が塩形態で導入されている場合に得られるものよりも、高い触媒性能レベルを示す。
これらの材料はまた、吸着剤、先進触媒担体、及びスーパーキャパシタ、二次電池、燃料電池などの電極材料としても使用することができる。
特に、これらは、プロトン交換膜燃料電池(PEMFC)システムにおける正極材料として使用してよい。また、プロトン交換膜燃料電池(PEMFC)システムにおける正極として使用してもよい。
材料の多孔性は、当該材料の77Kでの窒素吸収等温線に基づき、Brunauer-Emmet-Teller(BET)法によって比表面積を測定することによって特徴付けられる。
材料の電気化学的性能は、酸性電解液(0.1M H2SO4)中の回転電極への適用(0.3mg/cm2の触媒担持)により、チタン対電極及び硫酸水銀電極を基準として評価する。
0.630gのメラミンと0.550gのレゾルシノールを、0.010gの炭酸ナトリウムと共に52mLの蒸留水に一緒に加える。この混合物を、70℃で、粉末が完全に溶解するまで撹拌する。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、撹拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで60分間磁気撹拌しておく。その後撹拌を止めて、加熱を23時間継続する。生成したゲルを脱イオン水で2回洗浄する。
上澄み水溶液を除去し、ゲルのブロックを液体窒素に浸す。ゲルの水分が凍結したところで、ゲルを凍結乾燥瓶に入れ、凍結乾燥器(0.01mbar、-88℃で凝結)に5日間接続する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
0.630gのメラミンと0.550gのレゾルシノールを、0.010gの炭酸ナトリウムと共に52mLの蒸留水に一緒に加える。この混合物を、70℃で、粉末が完全に溶解するまで撹拌する。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、撹拌しつつ混合する。次いで、この溶液を、0.646gのFe(NO3)3と、撹拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで60分間磁気撹拌しておく。その後撹拌を止めて、加熱を23時間継続する。生成したゲルを脱イオン水で2回洗浄する。
上澄み水溶液を除去し、ゲルのブロックを液体窒素に浸す。ゲルの水分が凍結したところで、ゲルを凍結乾燥瓶に入れ、凍結乾燥器(0.01mbar、-88℃で凝結)に5日間接続する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
0.630gのメラミンと0.550gのレゾルシノールを、0.010gの炭酸ナトリウム及び0.094gの下記式2で示される4つのスルホン酸基を含む鉄(III)フタロシアニンと共に52mLの蒸留水に一緒に加える。この混合物を、70℃で1時間に亘り激しく撹拌し、メラミンを溶解させ、フタロシアニンを分散させる。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、撹拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで24時間磁気撹拌しておく。生成したゲルを脱イオン水で2回洗浄する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
0.630gのメラミンと0.550gのレゾルシノールを、0.010gの炭酸ナトリウム及び0.170gの下記式3で示される鉄(II)フタロシアニンと共に52mLの蒸留水に一緒に加える。この混合物を、70℃で1時間に亘り激しく撹拌し、メラミンを溶解させ、フタロシアニンを分散させる。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、撹拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで24時間磁気撹拌しておく。生成したゲルを脱イオン水で2回洗浄する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
0.630gのメラミンと0.550gのレゾルシノールを、0.010gの炭酸ナトリウム及び0.070gの下記式4で示されるテトラフェニルポルフィリンと共に52mLの蒸留水に一緒に加える。この混合物を、70℃で1時間に亘り激しく撹拌し、メラミンを溶解させ、ポルフィリンを分散させる。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、撹拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで24時間磁気撹拌しておく。生成したゲルを脱イオン水で2回洗浄する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
1.260gのレゾルシノールを、0.010gの炭酸ナトリウム及び0.030gの上記式3で示される鉄(II)フタロシアニンと共に52mLの蒸留水に加える。この混合物を70℃で1時間に亘り激しく撹拌して、フタロシアニンを分散させる。次いで、この溶液を、37質量%のホルムアルデヒド溶液1.622gと、攪拌しつつ混合する。オイルバスを85℃に加熱し、700rpmで24時間磁気撹拌しておく。生成したゲルを脱イオン水で2回洗浄する。
上澄み水溶液を除去し、ゲルのブロックを液体窒素に浸す。ゲルの水分が凍結したところで、ゲルを凍結乾燥瓶に入れ、凍結乾燥器(0.01mbar、-88℃で凝結)に5日間接続する。
有機クライオゲルを回収して石英ボートに入れ、次いで管状炉にてアルゴン流(80NL/h)中、800℃まで3.3K/minの勾配で熱分解し、さらに温度を2時間に亘って800℃に維持した後、周囲温度に戻す。
a)その多孔性の特性評価
実施例1から6で得られたクライオゲルのそれぞれの比表面積を、装置及び方法の項に記載した方法に従って特徴付け、表1に報告する。
表1から明らかなように、本発明によるクライオゲル(実施例3から5)の多孔性は、窒素含有芳香族大環状化合物なしに金属前駆体を用いて得られたクライオゲル(実施例2)または窒素原子の供給源である炭化水素化合物を用いずに得られたクライオゲル(実施例6)の多孔性よりも高い。したがって、本発明によるクライオゲルは、その反応部位へのアクセス性により優れている。
実施例1から6で得られたクライオゲルの電気化学的性能を、装置及び方法の項に記載した方法で評価し、その結果を図1に示す。
実施例3、4、5で得られた本発明によるクライオゲルは、実施例2、1、及び6で得られた本発明外のクライオゲルよりも優れた性能を有する。
[1] Zhang et al., Electrochimica Acta, 2018, 262, 326-336
[2] Hong et al., Journal of Materials Chemistry A, 2019, 7, 25557
[3] Jiang et al., ACS Catalysis, 2013, 3, 1263-1271
[4] CN 109659569
[5] Zion et al., Angewandte Chemie, 2020. 59, 2483-2489
Claims (24)
- 少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の窒素含有カーボン材料の調製方法であって、少なくとも、
(a)溶解状態の、少なくともアルデヒド、置換もしくは無置換のヒドロキシベンゼン誘導体、及び窒素原子の供給源である重合性炭化水素化合物、またさらに前記金属ドーパントの少なくとも1つの金属前駆体を含む溶媒媒体を提供する工程であって、前記金属前駆体は、少なくとも1つの窒素含有芳香族大環状化合物に配位した少なくとも1つの遷移金属を有する工程、
(b)工程(a)の前記溶媒媒体内でゾル-ゲル重合を活性化して、少なくともコアに前記金属前駆体を含む窒素含有カーボンハイドロゲルを形成する工程、
(c)工程(b)で形成された前記窒素含有カーボンハイドロゲルの乾燥形態を提供する工程、
(d)工程(c)の前記乾燥形態を非酸化性雰囲気中で熱分解して、少なくともコアに少なくとも1つの金属ドーパントを担持した、前記多孔質の窒素含有カーボン材料を形成し、これを回収する工程
を含む方法。 - 少なくともコアに少なくとも1つの金属ドーパントを担持した、前記多孔質の窒素含有カーボン材料が、エアロゲル、クリオゲル、またはキセロゲルである、請求項1に記載の方法。
- 少なくともコアに少なくとも1つの金属ドーパントを担持した、前記多孔質の窒素含有カーボン材料が、白金を含まない、請求項1または2に記載の方法。
- 前記窒素含有芳香族大環状化合物が、置換もしくは無置換のフタロシアニン、ポルフィリン、クロリン、及びコリンから選択される、請求項1から3のいずれか一項に記載の方法。
- 前記窒素含有芳香族大環状化合物が、水溶性または水分散性である、請求項1から4のいずれか一項に記載の方法。
- 前記窒素含有芳香族大環状化合物が、電気的に中性の親水性、カチオン性、及びアニオン性官能から選択される少なくとも1つの官能によって置換されている、請求項1から5のいずれか一項に記載の方法。
- 前記遷移金属が、マンガン(Mn)、コバルト(Co)、チタン(Ti)、鉄(Fe)、ルテニウム(Ru)、オスミウム(Os)、ニッケル(Ni)、銅(Cu)、及び亜鉛(Zn)から選択される、請求項1から6のいずれか一項に記載の方法。
- 金属前駆体と、窒素原子の供給源である1つ以上の重合性炭化水素化合物とが、窒素含有芳香族大環状化合物の炭化水素化合物に対する0.001から1.0のモル比で一緒にされる、請求項1から7のいずれか一項に記載の方法。
- 工程(a)の前記溶媒媒体が、直鎖状アルデヒド、例えば、ホルムアルデヒド、エタナール、及びプロパナール、環状アルデヒド、例えば、フルフラール、1つ以上のアミン官能を含むアルデヒド、例えば、ピロリジン及びアミノアセトアルデヒド、並びにこれらの混合物から選択される少なくとも1つのアルデヒドを含む、請求項1から8のいずれか一項に記載の方法。
- 工程(a)の前記溶媒媒体が、フェノール、レゾルシノール、カテコール、ジヒドロキシ-4-メチル安息香酸、2,6-ジヒドロキシベンズアミン、ジヒドロキシ安息香酸、及びこれらの誘導体、並びにこれらの混合物から選択される、少なくとも1つのヒドロキシベンゼン誘導体を含む、請求項1から9のいずれか一項に記載の方法。
- 窒素原子の供給源である重合性炭化水素化合物が、少なくとも2つの第1級及び/または第2級アミン官能を含む、請求項1から10のいずれか一項に記載の方法。
- 工程(a)の前記溶媒媒体が、窒素原子の供給源であって、且つ、第1級または第2級アミン官能で置換された脂肪族及び/または芳香族化合物、並びにこれらの誘導体から選択される、少なくとも1つの重合性炭化水素化合物を含む、請求項1から11のいずれか一項に記載の方法。
- 工程(a)の前記溶媒媒体が、窒素原子の供給源であって、且つ、トリアジン誘導体、フェナントロリン誘導体、ピリジン誘導体、及びピラジン誘導体から選択される、少なくとも1つの重合性炭化水素化合物を含む、請求項1から12のいずれか一項に記載の方法。
- 前記ゾル-ゲル重合により、ホルムアルデヒド、メラミン、及びレゾルシノールが一緒にされる、請求項1から13のいずれか一項に記載の方法。
- 工程(b)の活性化が、工程(a)の前記溶媒媒体を60℃から95℃の温度にさらすことによって行われる、請求項1から14のいずれか一項に記載の方法。
- 工程(c)による乾燥形態が、少なくともコアに少なくとも1つの金属ドーパントを担持した窒素含有カーボンエアロゲルの形成に使用され、また、工程(b)で得られたハイドロゲルをその溶媒媒体から分離し、次いで、かくして単離されたハイドロゲルを超臨界流体と接触させて乾燥させることによって得られる、請求項1から15のいずれか一項に記載の方法。
- 工程(c)による前記乾燥形態が、少なくともコアに少なくとも1つの金属ドーパントを担持した窒素含有カーボンクリオゲルの形成に使用され、また、工程(b)で得られたハイドロゲルをその溶媒媒体から分離し、かくして単離されたゲルを冷凍し、さらに前記の冷凍されたゲルを凍結乾燥させることによって得られる、請求項1から15のいずれか一項に記載の方法。
- 工程(c)による前記乾燥形態が、少なくともコアに少なくとも1つの金属ドーパントを担持した窒素含有カーボンキセロゲルの形成に使用され、また、工程(b)で得られたハイドロゲルから、制御された温度及び制御された圧力下で溶媒を蒸発させることによって形成される、請求項1から15のいずれか一項に記載の方法。
- 熱分解が、750℃から1200℃の温度で行われる、請求項1から18のいずれか一項に記載の方法。
- 請求項1から19のいずれか一項に規定の方法で得られ、BET法で評価して300m2/g以上の比表面積を有する、少なくともコアに少なくとも1つの金属ドーパントを担持した、多孔質の窒素含有カーボン材料。
- 請求項20に記載の材料であって、前記材料の総質量に対する金属原子の質量で表される、0.001%から7%の金属ドーパントの質量負荷を有する材料。
- コアに、遷移金属マンガン(Mn)、コバルト(Co)、チタン(Ti)、鉄(Fe)、ルテニウム(Ru)、オスミウム(Os)、ニッケル(Ni)、銅(Cu)、及び亜鉛(Zn)から選択された少なくとも1つの金属ドーパントを担持した、請求項20または21に記載の材料。
- 酸化還元用触媒としての、請求項20から22のいずれか一項に記載の材料の使用。
- プロトン交換膜燃料電池(PEMFC)システムにおける正極材料としての、請求項20から22のいずれか一項に記載の材料の使用。