JP2021155551A - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JP2021155551A JP2021155551A JP2020056957A JP2020056957A JP2021155551A JP 2021155551 A JP2021155551 A JP 2021155551A JP 2020056957 A JP2020056957 A JP 2020056957A JP 2020056957 A JP2020056957 A JP 2020056957A JP 2021155551 A JP2021155551 A JP 2021155551A
- Authority
- JP
- Japan
- Prior art keywords
- fatty acid
- acid amide
- protective film
- surface protective
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記粘着剤層がスチレン系ブロック共重合体と、脂肪酸アマイドと、を含み、
前記脂肪酸アマイドの融点が、220℃以上270℃以下であることを特徴とする。
図1は、本発明に係る表面保護フィルムの構成例を示す断面図である。
基材層1の厚みは、20μm以上100μm以下とすることができる。
スチレン系ブロック共重合体は、一般に、A−B−Aで表されるブロック共重合体、又はA−B−Aで表されるブロック共重合体とA−Bで表されるブロック共重合体との混合物であって、Aがスチレン重合体ブロック、Bが他の重合体ブロックである。他の重合体ブロックとしては、エチレン重合体ブロック、プロピレン重合体ブロック、ブチレン重合体ブロック等のオレフィン系重合体ブロック;ブタジエン重合体ブロック、イソプレン重合体ブロック等のジエン系重合体ブロック;ジエン系重合体ブロックの少なくとも一部を水素添加して得られる水素添加ブロックが挙げられる。AとBの重量比は、A/B=5/95〜50/50である。
また、粘着剤層中における前記脂肪酸アマイドの含有量は、0.025質量%以上であることが好ましく、0.05質量%以上であることがより好ましい。脂肪酸アマイドの含有量が少なすぎると、粘着剤層2の厚みやスチレン系ブロック共重合体の種類等によっては、脂肪酸アマイドの添加による効果が十分に得られない場合がある。
さらに、粘着剤層2には、基材層1との密着性を向上させるために、低密度ポリエチレンなどのポリオレフィン系樹脂が含まれていてもよい。
粘着剤層2の厚みは、2μm以上50μm以下とすることができる。
表面保護フィルムには、必要に応じて、ロール状に巻かれた表面保護フィルムを展開しやすくするための離型層等の他の層が形成されていてもよい。
まず、所定の濃度(例えば、0.5〜20質量%)で脂肪酸アマイドを含むマスターバッチを作成する。マスターバッチの主剤は、例えば、スチレン系ブロック共重合体、低密度ポリエチレンなどのポリオレフィン系樹脂を用いることができる。
次に、粘着剤層2中における脂肪酸アマイドの配合量が所定の濃度となるように、粘着剤層を構成する主剤であるスチレン系ブロック共重合体とマスターバッチとを混合し、粘着剤層形成材料を作成する。
次に、粘着剤層形成材料を粘着剤層用押出機に供給し、基材層1を形成するための材料を基材層用押出機に供給する。
その後、2台の押出機から各々の材料を一つのダイスから共押出しする二層共押出法により一体に成形する。こうすることで、基材層1上に粘着剤層2が形成された表面保護フィルムが得られる。
前述した実施形態では、表面保護フィルムが基材層と粘着剤層とを有する構成について説明したが、基材層と粘着剤層との間に中間層を有する構成であってもよい。
<脂肪酸アマイドA>
撹拌器、分水器付き還流冷却管及び温度計を備えた反応容器に、ステアリン酸852質量部と、アジピン酸2190質量部とを仕込み、100℃まで昇温して溶融させた。そこに、ヘキサメチレンジアミン1914質量部を加え、窒素雰囲気下、230〜260℃で4〜6時間、脱水縮合反応を行ってアミド化させ、脂肪酸アマイドAを得た。
脂肪酸アマイドAの酸価は7.3、アミン価は6.5であった。また、DSC測定(示差走査熱量測定)の結果、融点は257℃であった。
脂肪酸アマイドAの製造方法において、アジピン酸をセバシン酸909質量部に、ヘキサメチレンジアミンを696質量部にしたこと以外は脂肪酸アマイドAと同様にして、脂肪酸アマイドDを得た。
脂肪酸アマイドDの酸価は4.3、アミン価は3.6であった。また、DSC測定の結果、融点は212℃であった。
<マスターバッチA>
低密度ポリエチレン(東ソー(株)製ニポロン(登録商標)−Z、ZF260、MFR(メルトフローレート)=2.0g/10min、密度=920kg/m3)を94.7質量部と、脂肪酸アマイドAを5質量部と、フェノール系酸化防止剤(BASFジャパン(株)製、イルガノックス1076)0.3質量部、リン酸系酸化防止剤(BASFジャパン(株)製、イルガホス168)0.2質量部とを配合し、混合機を使用して均一に混合した。押出機を使用して、得られた混合物を160〜200℃で混練造粒し、ペレット状のマスターバッチAを製造した。
脂肪酸アマイドとして、脂肪酸アマイドAに代えて脂肪酸アマイドDを使用したこと以外はマスターバッチAと同様にして、マスターバッチDを製造した。
(実施例1)
基材層形成材料として、ポリプロピレン(日本ポリプロ社製、FW4B)を用意した。
スチレン系ブロック共重合体を主剤とした組成物A(ポリワンVersaflex PF MD6748N)に、上記マスターバッチAを粘着剤層全体の0.5質量%の添加量となるように配合し、粘着剤層形成材料とした。
基材層形成材料と粘着剤層形成材料とを共押出Tダイ法にてダイ温度230℃で製膜し、表面保護フィルムを得た。基材層の厚みは50μm、粘着剤層の厚みは、10μmであった。
マスターバッチAを粘着剤層全体の1質量%の添加量となるように配合した以外は、前記実施例1と同様にして表面保護フィルムを製造した。
マスターバッチAを粘着剤層全体の3質量%の添加量となるように配合した以外は、前記実施例1と同様にして表面保護フィルムを製造した。
マスターバッチAを粘着剤層全体の7質量%の添加量となるように配合した以外は、前記実施例1と同様にして表面保護フィルムを製造した。
マスターバッチAを粘着剤層全体の10質量%の添加量となるように配合した以外は、前記実施例1と同様にして表面保護フィルムを製造した。
組成物Aの代わりに、スチレン系ブロック共重合体(JSR製、ダイナロン1321P)80質量%と石油樹脂(荒川化学社製、アルコンP140)20質量%との混合物(組成物B)を用いた以外は、前記実施例3と同様にして表面保護フィルムを製造した。
マスターバッチAを配合しなかった以外は、前記実施例1と同様にして表面保護フィルムを製造した。
マスターバッチAの代わりに、マスターバッチDを配合した以外は、前記実施例3と同様にして表面保護フィルムを製造した。
マスターバッチAの代わりに、マスターバッチDを配合した以外は、前記実施例5と同様にして表面保護フィルムを製造した。
マスターバッチAを配合しなかった以外は、前記実施例6と同様にして表面保護フィルムを製造した。
(粘着力の測定)
評価用のSUS板は、SUS304HLを#280研磨紙で研磨して表面を調整した。
次に、SUS板に、25mm巾にカットした各実施例及び各比較例の表面保護フィルムを2kgローラーで貼り合わせ、23℃及び80℃で1日保管し、サンプルとした。
保管後のサンプルから表面保護フィルムをテンシロンで180°剥離での粘着力(剥離力)を測定した。なお、剥離速度は0.3m/min、30m/minとした。
上記粘着力の測定において、80℃で1日保管したサンプルから表面保護フィルムを剥離速度:0.3m/minで180°剥離した後のSUS板表面を目視で観察し、汚染の有無を確認した。
これらの結果を、粘着剤の構成、脂肪酸アマイドの含有量とともに、表1に示した。
2 粘着剤層
Claims (5)
- 基材層と、粘着剤層とを有し、
前記粘着剤層がスチレン系ブロック共重合体と、脂肪酸アマイドと、を含み、
前記脂肪酸アマイドの融点が、220℃以上270℃以下であることを特徴とする表面保護フィルム。 - 前記脂肪酸アマイドの酸価は、4.3以上10.0以下である請求項1に記載の表面保護フィルム。
- 前記脂肪酸アマイドのアミン価は、3.6以上9.0以下である請求項1または2に記載の表面保護フィルム。
- 前記粘着剤層中における前記脂肪酸アマイドの含有量は、0.5質量%以下である請求項1ないし3のいずれか1項に記載の表面保護フィルム。
- 前記粘着剤層中における前記脂肪酸アマイドの含有量は、0.4質量%以下である請求項1ないし4のいずれか1項に記載の表面保護フィルム。