JP2021006683A - 地盤改良体補強用繊維 - Google Patents
地盤改良体補強用繊維 Download PDFInfo
- Publication number
- JP2021006683A JP2021006683A JP2019120815A JP2019120815A JP2021006683A JP 2021006683 A JP2021006683 A JP 2021006683A JP 2019120815 A JP2019120815 A JP 2019120815A JP 2019120815 A JP2019120815 A JP 2019120815A JP 2021006683 A JP2021006683 A JP 2021006683A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- fibers
- reinforcing
- cement
- ground improvement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
〔1〕平均繊維径が50〜650μmであり、平均繊維長が1〜30mmである繊維を含んでなる地盤改良体補強用繊維。
〔2〕前記繊維が、ポリビニルアルコール繊維、ポリオレフィン繊維、ポリアミド繊維、エポキシ繊維、アクリル繊維、ポリベンゾオキサゾール繊維、ポリエステル繊維、ポリエーテル繊維、セルロース繊維、ポリウレタン繊維、レーヨン繊維、金属繊維、ガラス繊維からなる群から選択される少なくとも1種である、前記〔1〕の地盤改良体補強用繊維。
〔3〕前記繊維が耐アルカリ性繊維である、前記〔1〕の地盤改良体補強用繊維。
〔4〕前記耐アルカリ性繊維がポリビニルアルコール繊維である、前記〔3〕の地盤改良体補強用繊維。
〔5〕前記繊維の比重が0.5〜5である、前記〔1〕〜〔4〕の地盤改良体補強用繊維。
P=([η]×104/8.29)(1/0.62)
<繊維の平均繊維径>
平均繊維径については、無作為に繊維を100本取り出し、それぞれの繊維の長さ方向の中央部における繊維径を光学顕微鏡により測定し、その平均値を平均繊維径とした。
平均繊維長については、無作為に繊維を100本取り出し、それぞれの繊維の最も長い辺の繊維長を光学顕微鏡により測定し、その平均値を平均繊維長とした。
下記の実施例及び比較例で得られたセメントスラリーにおける地盤改良体補強用繊維の分散性を、触感及び目視による下記の項目に従って評価した。
A:ファイバーボールが無く、さらに繊維がセメントスラリー中に均一に分散された状態
B:ファイバーボールが少しあり、さらに繊維の一部がセメントスラリーの表面に浮き上がり、または底に沈殿状態
C:ファイバーボールが多数発生し、ファイバーボールが沈殿し相分離状態
下記の実施例及び比較例で得られた成形体について曲げ強度を測定した。曲げ強度の測定は、JIS A 1106に準じ、(株)島津製作所製のオートグラフAG5000−Bにて、試験速度(載荷ヘッドスピード)2mm/分、3等分点載荷方式で、曲げスパン120mmの条件で行った。
<地盤改良体補強用繊維の作製>
ポリマー重合度1750、ケン化度99.9モル%のPVAを用い、PVA濃度が21
質量%となるようにDMSOに溶解し紡糸原液とし、メタノールとDMSOの混合溶媒を
固化浴に用いて湿式紡糸にて紡糸した。さらにメタノールでDMSOを抽出しながら、湿
延伸、乾燥後、乾熱延伸(延伸温度230℃、総延伸倍率13倍)を実施した。
その結果、地盤改良体補強用繊維として、平均繊維径100μm、平均繊維長12mm、比重が1.3のPVA繊維を得た。
得られたPVA繊維ついて、次の方法に従い、セメントスラリーを調製した。水/セメント比(W/C)60体積%、セメント添加量は250kg/m3とした地盤改良スラリー配合により、最終的に得られる成形体の体積に対して、PVA繊維が0.5体積%となるようにPVA繊維、普通ポルトランドセメント(太平洋セメント株式会社製)および水を、モルタルミキサー(丸菱化学機械製作所社製)に投入し、公転62rpm、自転140rpmの条件下で、2分間混練してセメントスラリーを得た。得られたセメントスラリーについて、上述の方法により繊維の分散性を評価した。評価結果を表1に示す。
得られたセメントスラリーについて、次の方法に従い、成形体を得た。上記方法によって得られたセメントスラリーに、珪砂6号(トーヨーマテラン株式会社製)をセメントスラリー/珪砂6号を体積比1/4の割合で、モルタルミキサーで1分間混練した後に、混練物を鋼製型枠に流し込んで4cm角、長さ16cmの水硬性硬化体を作製し、鋼製型枠ごと室温20℃、湿度60%の部屋でラッピングを施し、7日間静置養生して成形体を得た。得られた成形体について、上述の方法により曲げ強度を測定した。測定結果を表1に示す。
地盤改良体補強用繊維として用いたPVA繊維の平均繊維径、平均繊維長及び最終的に得られる成形体の体積に対するPVA繊維の添加量を表1に示す通りに変更した以外は、実施例1と同様にしてセメントスラリーおよび成形体を作製した。得られたセメントスラリーについて、上述の方法により、繊維の分散性を評価した、また、成形体について、上述の方法により曲げ強度を測定した。評価及び測定結果を表1に示す。
平均繊維径65μm、平均繊維長12mmのポリプロピレン(PP)繊維(萩原工業社製 PW−jr)を、地盤改良体補強用繊維として用いて、実施例1と同様にしてセメントスラリーおよび成形体を作製した。得られたセメントスラリーについて、上述の方法により、繊維の分散性を評価した、また、成形体について、上述の方法により曲げ強度を測定した。評価及び測定結果を表1に示す。
Claims (5)
- 平均繊維径が50〜650μmであり、平均繊維長が1〜30mmである繊維を含んでなる地盤改良体補強用繊維。
- 前記繊維が、ポリビニルアルコール繊維、ポリオレフィン繊維、ポリアミド繊維、エポキシ繊維、アクリル繊維、ポリベンゾオキサゾール繊維、ポリエステル繊維、ポリエーテル繊維、セルロース繊維、ポリウレタン繊維、レーヨン繊維、金属繊維、ガラス繊維からなる群から選択される少なくとも1種である、請求項1に記載の地盤改良体補強用繊維。
- 前記繊維が耐アルカリ性繊維である、請求項1に記載の地盤改良体補強用繊維。
- 前記耐アルカリ性繊維がポリビニルアルコール繊維である、請求項3に記載の地盤改良体補強用繊維。
- 前記繊維の比重が0.5〜5である、請求項1〜4のいずれかに記載の地盤改良体補強用繊維。