JP2020515641A - 歯科用セメント組成物および使用法 - Google Patents
歯科用セメント組成物および使用法 Download PDFInfo
- Publication number
- JP2020515641A JP2020515641A JP2020502554A JP2020502554A JP2020515641A JP 2020515641 A JP2020515641 A JP 2020515641A JP 2020502554 A JP2020502554 A JP 2020502554A JP 2020502554 A JP2020502554 A JP 2020502554A JP 2020515641 A JP2020515641 A JP 2020515641A
- Authority
- JP
- Japan
- Prior art keywords
- dental
- thiourea
- phosphate
- meth
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
PTU:1−(2−ピリジル)−2−チオ尿素
CHP:クメンヒドロペルオキシド
CuPD:アセチルアセトン銅(II)MDP:10−メタクリロイルオキシデシル二水素ホスフェート
R202:AEROSIL(商標)ヒュームドシリカR812S:AEROSIL(商標)ヒュームドシリカ
GM27884−K6:Schott GM27884歯科用ガラス、3μm
YbF3:フッ化イッテルビウム
BYK W9010:湿潤分散添加剤(流動改質剤)
CQ:カンファーキノン
EDMAB:エチル−4−ジメチルアミノベンゾエート
UDMA:ウレタンジメタクリレート
E6BAD:エトキシル化(6)ビスフェノールAジメタクリレートEBPADM:エトキシル化(3)ビスフェノールAジメタクリレート
BisGMA:ビスフェノールA−グリシジルメタクリレート
TEGDM:トリエチレングリコールジメタクリレート
BHT:ブチル化ヒドロキシトルエン
HDK N−20P:ヒュームドシリカ
Pluronic L−44:界面活性剤
DI水:蒸留水
DHEPT:N−N−ビス(2−ヒドロキシエチル)−P−トルイジン
BPO:過酸化ベンゾイル
実施例1および実施例2は、化学物質を添加および混合することにより調製した。化学物質は、ヒュームドシリカを除くすべての固体が溶解するまで混合し、結果として低粘性の液体となった。
実施例2は、実施例1および2を比率で混合することにより調製した。
例1および2は、化学物質を添加および混合することにより調製した。すべての化学物質はヒュームドシリカを除くすべての固体が溶解するまで混合し、低粘性の液体が生成された。
実施例3は、化学物質を添加および混合することにより調製した。樹脂化学物質は、すべての固体が溶解するまで、CQ、EDMAB、およびBHTなどの溶解可能な固体と混合した。次いで、R812S、YbF3およびGM27884を含む固体フィラーを添加し、スピードミキサーで混合し、続けて3本ロールミルで混合し、ペースト状の半固体を得た。
実施例4は、化学物質を添加および混合することにより調製した。樹脂化学物質は、すべての固体が溶解するまで、CQ、EDMAB、PTU、およびBHTを含む溶解可能な固体と混合した。CuPDをTEGDMAのミキサーに追加し、スピードミキサーで混合した。次に、R812S、YbF3、およびGM27884を含む固体フィラーを添加し、スピードミキサーで混合した後、3本ロールミルで混合して、ペースト状の半固体を得た。
実施例5は、実施例3(CHP共開始剤含有)および実施例4(PTU共開始剤含有)をデュアルバレルシリンジに充填することにより調製され、各筒では第1の部分および第2の部分として、それぞれ1つのペーストが収容された。このペーストの組み合わせを使用する場合は、両方のペーストが混合筒を通過して好適に混合できるように、混合チップが取り付けられる。混合が行われると、材料は約4〜8分間で硬化した。
ジルコニア基材をポリマー樹脂に埋め込み、最上層を切り落とすことにより露出させた。基材を露出させ、600グリットのSiC紙で研磨した。ジルコニア表面に、60psiの圧力で50nmの酸化アルミニウム粉末をさらにサンドブラストした。その後、すべての試験片を徹底的にすすいだ。実施例1または実施例2または比較例Aのいずれかからの接着剤の層を軽くブラッシングして適用し、続いて約10秒間空気により薄くした。次に、試験片をISO29022−2013に記載されている接着ジグに入れた。実施例5のペースト混合物を窩洞に注入し、35℃の湿度室に1時間保持した後、ジグから外した。次に、試験片を水に入れ、37℃のオーブンで20時間保持した。次に、試験片の接着強度をISO29022−2013に従って記録した。各グループの10個の試験片について、平均接着強度と標準偏差を表1に記録した。結果は、16%(実施例1)または8%(実施例2)の接着剤を含有しているMDPは、それぞれ19.8MPaおよび19.1MPaで15MPaを超える接着強度を提供することが示され、一方ではMDPを欠く比較例Aの接着剤は、11.6MPaで15MPa未満の劣った接着強度を有していた。
比較例Cは、実施例3で行ったように化学物質を添加および混合することにより調製した。樹脂化学物質は、すべての固体が溶解するまで、CQ、EDMAB、BPO、およびBHTなどの溶解可能な固体と混合した。次いで、R812S、YbF3およびGM27884を含む固体フィラーを添加し、スピードミキサーで混合し、続いて3本ロールミルにより、ペースト状の半固体を得た。
比較例Dは、実施例4で行われたように化学物質を添加および混合することにより調製した。樹脂化学物質は、すべての固体が溶解するまで、CQ、EDMAB、DHEPT、およびBHTなどの溶解可能な固体と混合した。次いで、R812S、YbF3およびGM27884を含む固体フィラーを添加し、スピードミキサーで混合し、続いて3本ロールミルにより、ペースト状の半固体を得た。
比較例Eは、比較例Cおよび比較例Dをデュアルバレルシリンジに、各筒に1つのペーストを収容して充填することにより、実施例5で行われたように調製した。このペーストの組み合わせを使用する場合は、両方のペーストが混合筒を通過して適切に混合できるように、混合チップが取り付けられる。混合が行われると、材料は約4〜8分間で硬化した。
実施例7および実施例8で行われたように、ジルコニア基材をポリマー樹脂に埋め込み、最上層を切り落とすことにより露出させた。基材を露出させ、600グリットのSiC紙で研磨した。ジルコニア表面に、60psiの圧力で50nmの酸化アルミニウム粉末をさらにサンドブラストした。その後、すべての試験片を徹底的にすすいだ。実施例1または実施例2の層を軽くブラッシングして適用し、続いて約10秒間空気により薄くした。次に、試験片をISO29022−2013に記載されている接着ジグに入れた。比較例Eのペースト混合物を窩洞に注入し、35℃の湿度室に1時間保持した後、ジグから外した。次に、試験片を水に入れ、37℃のオーブンで20時間保持した。次に、試験片の接着強度をISO29022−2013に従って記録した。各グループの10個の試験片について、平均接着強度と標準偏差を表2に記録した。表2で示される結果は、BPO(例C)およびDHEPT(例D)がセメントペーストを調製するための第1の部分および第2の部分の共開始剤含有ペーストにおいて共開始剤として使用される場合、接着強度は、8.1MPaおよび11.4Mpaにおいて、それぞれ19.8MPaおよび19.1MPaにてのCHP(例3)およびPTU(例4)が第1の部分および第2の部分において共開始剤として使用される場合よりもはるかに低く、弱いことを示すものであった。
Claims (22)
- 歯科用基材の表面上で、
接着剤および
ペースト混合物を含んでなる歯科用組成物であって、
該接着剤が、少なくとも1種のリン酸含有(メタ)アクリルモノマーを含んでなり、該ペースト混合物が、少なくとも1種の重合可能なモノマー、少なくとも1種のヒドロペルオキシドおよび少なくとも1種のチオ尿素化合物を含んでなる、歯科用組成物。 - 前記リン酸含有(メタ)アクリルモノマーが、GPDM(グリセロールホスフェートジ(メタ)アクリレート{(メタ)アクリレート=アクリレートまたはメタクリレート})、フェニル−P(フェニルメタクリルオキシエチルホスフェート)、PENTA−P(ジペンタエリスリトールペンタアクリレートホスフェート)、10−MDP(メタクリロイルオキシデシルホスフェート)、HEMA−P(ヒドロキシエチルメタクリレートホスフェート)、HEA−P(ヒドロキシエチルアクリレートホスフェート)、ビス(HEMA)−P(ビス(ヒドロキシエチルメタクリレート)ホスフェート)、ビス(HEA)−P{ビス(ヒドロキシエチルアクリレート)ホスフェート)、ビス((メタ)アクリルオキシプロピル)ホスフェート、およびそれらの組み合わせからなる群から選択される、請求項1に記載の歯科用組成物。
- 前記リン酸含有(メタ)アクリルモノマーが、10−メタクリロイルオキシデシル二水素ホスフェート(10−MDP)である、請求項1または2に記載の歯科用組成物。
- 前記チオ尿素が、1−(2−ピリジル)−2−チオ尿素(PTU)、1−ベンゾイル−2−チオ尿素(BTU)、1−アセチル−2−チオ尿素(ATU)、1−(2−テトラヒドロフルフリル)−2−チオ尿素(TTU)、またはそれらの組み合わせからなる群から選択される、請求項1〜3のいずれか一項に記載の歯科用組成物。
- 前記チオ尿素が、1−(2−ピリジル)−2−チオ尿素(PTU)である、請求項1〜4のいずれか一項に記載の歯科用組成物。
- 前記ヒドロペルオキシドが第三級ヒドロペルオキシドである、請求項1〜5のいずれか一項に記載の歯科用組成物。
- 前記ペースト混合物の第1の部分または第2の部分のいずれかが、銅(II)化合物をさらに含んでなる、請求項1〜6のいずれか一項に記載の歯科用組成物。
- 前記歯科用基材がジルコニアである、請求項1〜7のいずれか一項に記載の歯科用組成物。
- 前記接着剤が、単一ボトルの接着剤である、請求項1〜8のいずれか一項に記載の歯科用組成物。
- 歯科修復方法であって、
歯科用基材上に歯科用接着剤を適用する第一工程であって、該接着剤が、少なくとも1種のリン酸含有(メタ)アクリルモノマーを含むものである、工程;および第1の部分と第2の部分が互いに分離した装置からペースト混合物を適用する第二工程であって、該第1の部分および第2の部分がペースト混合物を形成するものであり、かつ該装置からのペースト混合物が、第1の部分において少なくとも1種の重合可能モノマーおよび少なくとも1種のヒドロペルオキシドを含んでなり、かつ第2の部分において少なくとも1種のチオ尿素化合物を含むものである、工程
を含んでなる方法。 - 前記リン酸含有(メタ)アクリルモノマーが、GPDM(グリセロールホスフェートジ(メタ)アクリレート{(メタ)アクリレート=アクリレートまたはメタクリレート})、フェニル−P(フェニルメタクリルオキシエチルホスフェート)、PENTA−P(ジペンタエリスリトールペンタアクリレートホスフェート)、10−MDP(メタクリロイルオキシデシルホスフェート)、HEMA−P(ヒドロキシエチルメタクリレートホスフェート)、HEA−P(ヒドロキシエチルアクリレートホスフェート)、ビス(HEMA)−P(ビス(ヒドロキシエチルメタクリレート)ホスフェート)、ビス(HEA)−P{ビス(ヒドロキシエチルアクリレート)ホスフェート)、ビス((メタ)アクリルオキシプロピル)ホスフェート、およびそれらの組み合わせからなる群から選択される、請求項10に記載の方法。
- 前記リン酸含有(メタ)アクリルモノマーが、10−メタクリロイルオキシデシル二水素ホスフェート(10−MDP)である、請求項10または11に記載の方法。
- 前記チオ尿素が、1−(2−ピリジル)−2−チオ尿素(PTU)、1−ベンゾイル−2−チオ尿素(BTU)、1−アセチル−2−チオ尿素(ATU)、1−(2−テトラヒドロフルフリル)−2−チオ尿素(TTU)、またはそれらの組み合わせからなる群から選択される、請求項10〜12のいずれか一項に記載の方法。
- 前記チオ尿素が、1−(2−ピリジル)−2−チオ尿素(PTU)である、請求項10〜13のいずれか一項に記載の方法。
- 前記ヒドロペルオキシドが第三級ヒドロペルオキシドである、請求項10〜14のいずれか一項に記載の方法。
- 前記ペースト混合物の第1の部分または第2の部分のいずれかが、銅(II)化合物をさらに含んでなる、請求項10〜15のいずれか一項に記載の方法。
- 前記接着剤が歯科用基材に効果的に接着する、請求項10〜16のいずれか一項に記載の方法。
- 前記歯科用基材がジルコニアである、請求項10〜17のいずれか一項に記載の方法。
- 歯科用基材上の前記歯科用接着剤の接着強度が15MPa超である、請求項10〜18のいずれか一項に記載の方法。
- 前記装置がデュアルバレルシリンジである、請求項10〜19のいずれか一項に記載の方法。
- 歯科用基材の表面上で、
接着剤および
ペースト混合物を含んでなる歯科用組成物であって、
該接着剤が、少なくとも1種のリン酸含有(メタ)アクリルモノマーを含んでなり、該ペースト混合物が、事前に分離させた第1の部分および第2の部分を一緒に混合することによって形成されるものであり、該第1の部分が、少なくとも1種の重合可能なモノマーおよび少なくとも1種のヒドロペルオキシドを含んでなり、かつ該第2の部分が少なくとも1種のチオ尿素化合物を含んでなる、歯科用組成物。 - 前記の事前に分離させた第1の部分および第2の部分が、デュアルバレルシリンジで分離される、請求項21に記載の歯科用組成物。