JP2020165040A - 防湿性紙およびその製造方法 - Google Patents
防湿性紙およびその製造方法 Download PDFInfo
- Publication number
- JP2020165040A JP2020165040A JP2019066898A JP2019066898A JP2020165040A JP 2020165040 A JP2020165040 A JP 2020165040A JP 2019066898 A JP2019066898 A JP 2019066898A JP 2019066898 A JP2019066898 A JP 2019066898A JP 2020165040 A JP2020165040 A JP 2020165040A
- Authority
- JP
- Japan
- Prior art keywords
- moisture
- paper
- coating layer
- proof
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明に係る防湿性紙は、紙基材と、該紙基材の少なくとも一方の面に位置する塗工層と、を備え、透湿度が50g/m2・24h以下、好ましくは20g/m2・24h以下、より好ましくは10g/m2・24h以下であり、塗工層は合成樹脂およびワックスを含有し、塗工層表面の白色度が20%以上、より好ましくは30%以上、より好ましくは45%以上、更に好ましくは55%以上である。
本発明の防湿性紙を構成する紙基材は、防湿性紙の用途に応じて最適な坪量のものを使用することができる。紙基材が単層紙である場合、その坪量の下限は10g/m2以上、上限は250g/m2以下の範囲で適宜設定することができ、例えば、紙基材がクラフト紙の場合、坪量の下限は30g/m2以上、上限は250g/m2以下の範囲で設定することができる。また、紙基材が2層以上の紙層を有する多層抄き板紙である場合、その坪量の下限は100g/m2以上、上限は750g/m2以下の範囲で適宜設定することができ、例えば、段ボールのライナの場合、坪量の下限は100g/m2以上、上限は550g/m2以下の範囲で設定することができる。
本発明の防湿性紙を構成する塗工層は、上記のように、合成樹脂およびワックスを含有し、塗工層表面の白色度が20%以上、より好ましくは30%以上、より好ましくは45%以上、更に好ましくは55%以上である。
本発明を構成する塗工層が含有することのできるスチレン系樹脂とは、構造中にスチレン骨格を有するスチレン系単量体の共重合割合が50質量%以上である樹脂であり、スチレン系単量体の重合体のみからなるものであってもよい。
本発明を構成する塗工層が含有することのできるアクリル系樹脂とは、アクリル酸、メタクリル酸及びこれらの誘導体であるアクリル系単量体の共重合割合が50質量%以上である樹脂であり、アクリル系単量体の重合体のみからなるものであってもよい。
塗工層が含有するワックスとしては、例えば、ポリエチレン系ワックス、フィッシャートロプシュワックス、油脂系合成ワックス(脂肪酸エステル系、脂肪酸アミド、ケトン・アミン類)、水素硬化油等の合成ワックス、蜜蝋、木蝋、パラフィン系ワックス、マイクロクリスタリンワックス等の天然ワックス等を挙げることができる。これらのワックスは、1種単独、あるいは、2種以上の組み合わせで使用することができ、特に、パラフィンを含む炭化水素系ワックスが好適である。
本発明の防湿性紙の製造方法は、紙基材の少なくとも一方の面に、合成樹脂およびワックスを含有する塗工剤をブレード塗工方式により塗工し、塗工された塗工剤を乾燥して塗工層とすることにより防湿性紙を製造するものである。
(紙基材の準備)
針葉樹未晒クラフトパルプ(NUKP)を63質量%、古紙パルプを37質量%の割合で使用し、表面に耐水剤、粘性改良剤、保水剤、防腐剤、着色剤を塗工することにより、3層抄きで坪量280g/m2となるようライナ用の板紙を抄造して紙基材(参考試料1)とした。
溶媒中にスチレン系樹脂およびアクリル系樹脂とパラフィンを含む炭化水素系ワックスが混合分散された防湿剤(マイケルマン社製 VAPORCOAT2200.S)100質量部に、消泡剤0.46質量部を添加して塗工剤Aを調製した。この塗工剤Aを使用し、下記の表1に示すような5種の塗工量となるように、上記の紙基材(参考試料1)の片面にブレード塗工方式により塗工し、塗工層温度が90℃となるように乾燥して塗工層を形成した。これにより、3種の防湿性紙(試料1−1〜試料1−3)を作製した。
上記のように作製した7種の防湿性紙(試料1−1〜試料1−7)、および、紙基材(参考試料1)について、透湿度、塗工層表面の平滑度、白色度、吸水度、防湿性紙の防水性を以下のように測定、評価し、結果を下記の表1に示した。
JIS Z 0208に準拠して測定する。尚、防湿性紙においては、塗工層側から測定する。
JIS P8155に準拠して、旭精工(株)製デジタル型王研式透気度平滑度試験機にて、王研式平滑度を測定する。
JIS P8148に準拠して、(株)村上色彩技術研究所ISO白色度対応光測色システムCMS−35SPXMにて測定する。
JIS P8140(コッブ法)に準拠して、100mlの蒸留水を塗工層に接触させ、120秒後に吸収された水の単位面積あたりの重量を測定する。
防湿性紙を用いて縦28cm、横22cm、深さ13cmの容器を作製(塗工層は内面側に位置する)し、この容器に1.0Lの水を入れ、温度40℃、湿度80%の環境下で3週間放置した後の水の染み出し状況を観察して、下記の基準で判定する。
(防水性の判定基準)
○:水が容器外面や水面より上の容器内面に染み出していない。
△:水が容器外面には染み出していないが、水面より上の容器内面に染み出している。
×:水が容器外面や水面より上の容器内面に染み出している。
Claims (8)
- 紙基材と、該紙基材の少なくとも一方の面に位置する塗工層と、を備え、透湿度が50g/m2・24h以下であり、前記塗工層は合成樹脂およびワックスを含有し、前記塗工層表面の白色度が20%以上であることを特徴とする防湿性紙。
- 前記塗工層は、顔料を含有することを特徴とする請求項1に記載の防湿性紙。
- 前記顔料は、少なくとも無機顔料を含むことを特徴とする請求項1または請求項2に記載の防湿性紙。
- 前記塗工層の表面の平滑度は、25秒以上であることを特徴とする請求項1乃至請求項3のいずれかに記載の防湿性紙。
- 前記塗工層の塗工量は、20g/m2以下であることを特徴とする請求項1乃至4のいずれかに記載の防湿性紙。
- 前記紙基材の坪量は、10g/m2以上、750g/m2以下であることを特徴とする請求項1乃至5のいずれかに記載の防湿性紙。
- 紙基材の少なくとも一方の面に、合成樹脂およびワックスを含有する塗工剤をブレード塗工方式により塗工し、塗工された前記塗工剤を乾燥して塗工層とすることを特徴とする防湿性紙の製造方法。
- 前記塗工剤の塗工量が20g/m2以下となるように塗工することを特徴とする請求項7に記載の防湿性紙の製造方法。